JPH05288910A - Diffraction grating - Google Patents
Diffraction gratingInfo
- Publication number
- JPH05288910A JPH05288910A JP9435292A JP9435292A JPH05288910A JP H05288910 A JPH05288910 A JP H05288910A JP 9435292 A JP9435292 A JP 9435292A JP 9435292 A JP9435292 A JP 9435292A JP H05288910 A JPH05288910 A JP H05288910A
- Authority
- JP
- Japan
- Prior art keywords
- poly
- methacrylate
- diffraction grating
- layers
- refractive index
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、回折格子に関し、特
に、熱線反射膜のように広い波長範囲の回折をする回折
格子に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a diffraction grating, and more particularly to a diffraction grating that diffracts in a wide wavelength range such as a heat ray reflective film.
【０００２】[0002]
【従来の技術】従来の回折格子としては、フォトポリマ
ー、重クロム酸ゼラチン、銀塩等の膜に光の干渉縞を記
録して形成したブラグ回折格子がよく知られている。し
かし、これらは何れも回折波長の範囲が狭く、広い波長
範囲の回折が可能なものは得られていない。As a conventional diffraction grating, a Bragg diffraction grating formed by recording light interference fringes on a film of photopolymer, dichromated gelatin, silver salt or the like is well known. However, all of them have a narrow range of diffraction wavelengths, and no one capable of diffracting a wide wavelength range has been obtained.
【０００３】このようなブラグ回折格子を熱線反射膜等
の用途に用いるには、回折波長が数百ｎｍ以上の範囲に
わたる必要がある。In order to use such a Bragg diffraction grating for applications such as a heat ray reflection film, it is necessary that the diffraction wavelength is in the range of several hundreds nm or more.
【０００４】[0004]
【発明が解決しようとする課題】本発明はこのような状
況に鑑みてなされたものであり、その目的は、屈折率差
のある２種類以上のフィルムを厚さを変化させて積層す
ることにより、広い波長範囲の回折が可能なブラグ回折
格子を提供することである。SUMMARY OF THE INVENTION The present invention has been made in view of such circumstances, and an object thereof is to laminate two or more kinds of films having different refractive indexes by changing the thickness. The purpose is to provide a Bragg diffraction grating capable of diffracting a wide wavelength range.
【０００５】[0005]
【課題を解決するための手段】一般に、回折格子の格子
間ピッチｄと回折波長λは、入射角をθとすると、 ２ｄｓｉｎθ＝ｎλ （ｎ＝１，２，３，・・・） で与えられる。したがって、屈折率の高い層と低い層を
交互に積層し回折格子を構成し、その際、格子間ピッチ
ｄを層間で異なるように変化させることにより、種々の
波長の光を回折するようにすることができ、１つの回折
格子の回折波長範囲を広げることができる。Generally, the inter-grating pitch d of the diffraction grating and the diffraction wavelength λ are given by 2d sin θ = nλ (n = 1, 2, 3, ...) When the incident angle is θ. .. Therefore, a layer having a high refractive index and a layer having a low refractive index are alternately laminated to form a diffraction grating, and at this time, by varying the inter-grating pitch d so as to be different between the layers, light of various wavelengths is diffracted. Therefore, the diffraction wavelength range of one diffraction grating can be expanded.
【０００６】具体的な例について説明すると、図１に断
面図を示すように、例えば、厚さ０．４０μｍの高屈折
率フィルム１、０．４１μｍの高屈折率フィルム３、・
・・、１．００μｍの高屈折率フィルム５と、同じ厚さ
の低屈折率フィルム２、４、・・・、６とを交互に積層
して回折格子を作成する。特定の厚さの層について、積
層する層数は、図の場合、４層であるが、これに限定さ
れず何層であってもよい。A specific example will be described. As shown in the sectional view of FIG. 1, for example, a high refractive index film 1 having a thickness of 0.40 μm, a high refractive index film 3 having a thickness of 0.41 μm ,.
The diffraction grating is formed by alternately laminating the high-refractive index film 5 having a thickness of 1.00 μm and the low-refractive index films 2, 4, ..., 6 having the same thickness. Regarding the layer having a specific thickness, the number of layers to be laminated is four layers in the figure, but the number is not limited to this and may be any number.
【０００７】この回折格子により、図２に示すように、
第１の厚さの層では垂直入射時に８００ｎｍの波長の光
を回折し、順次増加する厚さの層で、８２０ｎｍ、・・
・、２０００ｎｍの光を回折し、全体として８００〜２
０００ｎｍの幅広い光を回折するようになる。With this diffraction grating, as shown in FIG.
The first thickness layer diffracts light having a wavelength of 800 nm at the time of vertical incidence, and the thickness gradually increases to 820 nm, ...
.. Diffracts light of 2000 nm, 800 to 2 as a whole
Diffracts a wide light of 000 nm.
【０００８】しかし、このような層厚が順次変化するフ
ィルムの入手と積層は容易でないので、現実には、これ
らのフィルムの数倍〜数十倍の厚さのフィルムを積層
し、その後、延伸法、プレス法等の機械的方法により所
定の厚みに減じる方法がとられる。また、コーティング
により所定の膜厚の各層を構成し、これを順次繰り返す
ことにより所定の積層体を形成してもよい。さらに、上
記機械的方法とコーティング法を組み合わせてもよい。
また、高屈折率の材料と低屈折率の材料は、それぞれ１
種に限る必要はなく、より多くの高屈折率、低屈折率の
材料を組み合わせてもよい。なお、層の厚さの変化は、
積層体の一方の面から他方の面に順に増加するような変
化であっても、また、異なる厚さの層がランダムに分布
するような変化であってもよく、特に限定されない。However, since it is not easy to obtain and laminate such a film whose layer thickness changes sequentially, in reality, a film having a thickness of several times to several tens of times that of these films is laminated and then stretched. The thickness may be reduced to a predetermined value by a mechanical method such as a press method or a pressing method. Further, each layer having a predetermined film thickness may be formed by coating, and a predetermined laminated body may be formed by sequentially repeating this. Further, the mechanical method and the coating method may be combined.
In addition, the material of high refractive index and the material of low refractive index are 1
It is not necessary to limit the number of seeds, and more high refractive index materials and low refractive index materials may be combined. The change in layer thickness is
The change may be such that it sequentially increases from one surface to the other surface of the laminate, or it may be a change in which layers having different thicknesses are randomly distributed, and is not particularly limited.
【０００９】このような高屈折率及び低屈折率の層の材
料としては、例えば次に示すようなものがあげられ、こ
れらの何れかを組み合わせて積層する。なお、以下には
ｄ線での屈折率も併せて示す。Examples of the material of such a high refractive index layer and a low refractive index layer are as follows, and any one of them may be combined and laminated. The refractive index at the d-line is also shown below.
【００１０】 ポリビニリデンフルオライド 1.42 ポリジメチルシリレン（ポリジメチルシロキサン） 1.43 ポリトリフルオロエチルメタクリレート 1.437 ポリオキシプロピレン 1.4495 ポリビニルイソブチルエーテル 1.4507 ポリビニルエチルエーテル 1.4540 ポリオキシエチレン 1.4563 ポリビニルブチルエーテル 1.4563 ポリビニルペンチルエーテル 1.4581 ポリビニルヘキシルエーテル 1.4591 ポリ（４−メチル−１−ペンテン） 1.459 -1.465 セルロースアセテートブチレート 1.46 -1.49 ポリ（４−フルオロ−２−トリフルオロメチルスチレン） 1.46 ポリビニルオクチルエーテル 1.4613
ポリ（ビニル２−エチルヘキシルエーテル） 1.4626 ポリビニルデシルエーテル 1.4628 ポリ（２−メトキシエチルアクリレート） 1.463 ポリブチルアクリレート 1.4631 ポリブチルアクリレート 1.466 ポリ（ｔ−ブチルメタクリレート） 1.4638 ポリビニルドデシルエーテル 1.4640 ポリ（３−エトキシプロピルアクリレート） 1.465 ポリオキシカルボニルテトラメチレン 1.465 ポリビニルプロピオネート 1.4665 ポリビニルアセテート 1.4665 ポリビニルメチルエーテル 1.467 ポリエチルアクリレート 1.4685 エチレン−ビニルアセテート共重合体 1.47 -1.50 （８０％−２０％ビニルアセテート） セルロースプロピオネート 1.47 -1.49 セルロースアセテートプロピオネート 1.47 ベンジルセルロース 1.47 -1.58 フェノール−フォルムアルデヒド樹脂 1.47 -1.70 セルローストリアセテート 1.47 -1.48 ポリビニルメチルエーテル（アイソタクティック） 1.4700 ポリ（３−メトキシプロピルアクリレート） 1.471 ポリ（２−エトキシエチルアクリレート） 1.471 ポリメチルアクリレート 1.472 -1.480 ポリイソプロピルメタクリレート 1.4728 ポリ（１−デセン） 1.4730 ポリプロピレン（アタクティック，密度0.8575ｇ／ｃｍ3 ） 1.4735 ポリ（ビニルｓｅｃ−ブチルエーテル）（アイソタクティック） 1.4740 ポリドデシルメタクリレート 1.4740
ポリオキシエチレンオキシスクシノイル 1.4744 （ポリエチレンスクシネート） ポリテトラデシルメタクリレート 1.4746 エチレン−プロピレン共重合体（ＥＰＲ−ゴム） 1.4748-1.48 ポリヘキサデシルメタクリレート 1.4750 ポリビニルフォルメート 1.4757 ポリ（２−フルオロエチルメタクリレート） 1.4768 ポリイソブチルメタクリレート 1.477 エチルセルロース 1.479 ポリビニルアセタール 1.48 -1.50 セルロースアセテート 1.48 -1.50 セルローストリプロピオネート 1.48 -1.49 ポリオキシメチレン 1.48 ポリビニルブチラール 1.48 -1.49 ポリ（ｎ−ヘキシルメタクリレート） 1.4813 ポリ（ｎ−ブチルメタクリレート） 1.483 ポリエチリデンジメタクリレート 1.4831 ポリ（２−エトキシエチルメタクリレート） 1.4833 ポリオキシエチレンオキシマレオイル 1.4840 （ポリエチレンマレート） ポリ（ｎ−プロピルメタクリレート） 1.484 ポリ（３，３，５−トリメチルシクロヘキシルメタクリレート） 1.485 ポリエチルメタクリレート 1.485 ポリ（２−ニトロ−２−メチルプロピルメタクリレート） 1.4868 ポリトリエチルカルビニルメタクリレート 1.4889 ポリ（１，１−ジエチルプロピルメタクリレート） 1.4889 ポリメチルメタクリレート 1.4893 1.490 ポリ（２−デシル−１，３−ブタジエン） 1.4899
ポリビニルアルコール 1.49 -1.53 ポリエチルグリコレートメタクリレート 1.4903 ポリ（３−メチルシクロヘキシルメタクリレート） 1.4947 ポリ（シクロヘキシルα−エトキシアクリレート） 1.4969 メチルセルロース（低粘度） 1.497 ポリ（４−メチルシクロヘキシルメタクリレート） 1.4975 ポリデカメチレングリコールジメタクリレート 1.4990 ポリウレタン 1.5 -1.6 ポリ（１，２−ブタジエン） 1.5000 ポリビニルフォルマール 1.50 ポリ（２−ブロモ−４−トリフルオロメチルスチレン） 1.5 セルロースニトレート 1.50 -1.514 ポリ（ｓｅｃ−ブチルα−クロロアクリレート） 1.500 ポリ（２−ヘプチル−１，３−ブタジエン） 1.5000 ポリ（エチルα−クロロアクリレート） 1.502 ポリ（２−イソプロピル−１，３ブタジエン） 1.5028 ポリ（２−メチルシクロヘキシルメタクリレート） 1.5028 ポリプロピレン（密度0.9075ｇ／ｃｍ3 ） 1.5030 ポリイソブテン 1.505 -1.51 ポリボルニルメタクリレート 1.5059 ポリ（２−ｔ−ブチル−１，３−ブタジエン） 1.5060 ポリエチレングリコールジメタクリレート 1.5063 ポリシクロヘキシルメタクリレート 1.5066 ポリ（シクロヘキサンジオール−１，４−ジメタクリレート） 1.5067 ブチルゴム（未加硫） 1.508 ポリテトラハイドロフルフリルメタクリレート） 1.5096 グッタペルカ（β） 1.509 ポリエチレンアイオノマー 1.51 ポリオキシエチレン（高分子量） 1.51 -1.54 ポリエチレン（密度0.914 ｇ／ｃｍ3 ） 1.51 （密度0.94-0.945ｇ／ｃｍ3 ） 1.52 -1.53 （密度0.965 ｇ／ｃｍ3 ） 1.545 ポリ（１−メチルシクロヘキシルメタクリレート） 1.5111 ポリ（２−ヒドロキシエチルメタクリレート） 1.5119 ポリビニルクロロアセテート 1.512 ポリブテン（アイソタクティック） 1.5125 ポリビニルメタクリレート 1.5129 ポリ（Ｎ−ブチル−メタクリルアミド） 1.5135 グッタペルカ（α） 1.514 テルペン樹脂 1.515 ポリ（１，３−ブタジエン） 1.5154 セラック 1.51 -1.53 ポリ（メチルα−クロロアクリレート） 1.517 ポリ（２−クロロエチルメタクリレート） 1.517 ポリ（２−ジエチルアミノエチルメタクリレート） 1.5174 ポリ（２−クロロシクロヘキシルメタクリレート） 1.5179 ポリ（１，３−ブタジエン）（３５％ｃｉｓ；５６％ｔｒａｎｓ 1.5180 ；７％１，２−ｃｏｎｔｅｔ） 天然ゴム 1.519 -1.52 ポリアリルメタクリレート 1.5196 ポリビニルクロライド＋４０％ジオクチルフタテート 1.52 ポリアクリロニトリル 1.52 1.5187 ポリメタクリロニトリル 1.52 ポリ（１，３−ブタジエン）（ｓｉｃ型リッチ） 1.52 ブタジエン−アクリロニトリル共重合体 1.52 ポリメチルイソプロペニルケトン 1.5200 ポリイソプレン 1.521 ポリエステル樹脂 リジッド（約５０％スチレン） 1.523 -1.54 ポリ（Ｎ−（２−メトキシエチル）メタクリルアミド） 1.5246 ポリ（２，３−ジメチルブタジエン）（メチルゴム） 1.525 ビニルクロライド−ビニルアセテート共重合体（95/5-90/10） 1.525 -1.535 ポリアクリックアシド 1.527 ポリ（１，３−ジクロロプロピルメタクリレート） 1.5270 ポリ（２−クロロ−１−（クロロメチル）エチルメタクリレート） 1.5270 ポリアクロレイン 1.529 ポリ（１−ビニル−２−ピロリドン） 1.53 塩酸化ゴム 1.53 -1.55 ナイロン６；ナイロン６，６；ナイロン６，１０（成型体） 1.53 （ナイロン−６−ファイバ：1.515 横断方向 1.565 ファイバ方向） ブタジエン−スチレン共重合体（約３０％スチレン） 1.53 ブロック共重合体 ポリ（シクロヘキシルα−クロロアクリレート） 1.532 ポリ（２−クロロエチルα−クロロアクリレート） 1.533 ブタジエン−スチレン共重合体（約７５／２５） 1.535 ポリ（２−アミノエチルメタクリレート） 1.537 ポリフルフリルメタクリレート 1.5381 プロテイン 1.539 -1.541 ポリブチルメルカプチルメタクリレート 1.5390 ポリ（１−フェニル−ｎ−アミルメタクリレート） 1.5396 ポリ（Ｎ−メチル−メタクリルアミド） 1.5398 セルロース 1.54 ポリビニルクロライド 1.54 -1.55 ウレアフォルムアルデヒド樹脂 1.54 -1.56 ポリ（ｓｅｃ−ブチルα−ブロモアクリレート） 1.542 ポリ（シクロヘキシルα−ブロモアクリレート） 1.542 ポリ（２−ブロモエチルメタクリレート） 1.5426 ポリジヒドロアビエチックアシド 1.544 ポリアビエチックアシド 1.546 ポリエチルメルカプチルメタクリレート 1.547 ポリ（Ｎ−アリルメタクリルアミド） 1.5476 ポリ（１−フェニルエチルメタクリレート） 1.5487 ポリビニルフラン 1.55 ポリ（２−ビニルテトラヒドロフラン） 1.55 ポリ（ビニルクロライド）＋４０％トリクレジルフォスフェート 1.55 エポキシ樹脂 1.55 -1.60 ポリ（ｐ−メトキシベンジルメタクリレート） 1.552 ポリイソプロピルメタクリレート 1.552 ポリ（ｐ−イソプロピルスチレン） 1.554 ポリクロロプレン 1.554 -1.558 ポリ（オキシエチレン−α−ベンゾエート−ω−メタクリレート） 1.555 ポリ（ｐ，ｐ’−キシリレニルジメタクリレート） 1.5559 ポリ（１−フェニルアリルメタクリレート） 1.5573 ポリ（ｐ−シクロヘキシルフェニルメタクリレート） 1.5575 ポリ（２−フェニルエチルメタクリレート） 1.5592 ポリ（オキシカルボニロキシ−１，４−フェニレン−１−プロピル 1.5602 −ブチリデン−１，４−フェニレン） ポリ（１−（ｏ−クロロフェニル）エチルメタクリレート） 1.5624 スチレン−無水マレイン酸共重合体 1.564 ポリ（１−フェニルシクロヘキシルメタクリレート） 1.5645 ポリ（オキシカルボニロキシ−１，４−フェニレン−１，３ 1.5671 −ジメチル−ブチリデン−１，４−フェニレン） ポリ（メチルα−ブロモアクリレート） 1.5672 ポリベンジルメタクリレート 1.5680 ポリ（２−（フェニルスルフォニル）エチルメタクリレート） 1.5682
ポリ（ｍ−クレジルメタクリレート） 1.5683 スチレン−アクリロニトリル共重合体（約７５／２５） 1.57 ポリ（オキシカルボニロキシ−１，４−フェニレンイソブチリデン 1.5702 −１，４−フェニレン） ポリ（ｏ−メトキシフェニルメタクリレート） 1.5705 ポリフェニルメタクリレート 1.5706 ポリ（ｏ−クレジルメタクリレート） 1.5707 ポリジアリルフタレート 1.572 ポリ（２，３−ジブロモプロピルメタクリレート） 1.5739 ポリ（オキシカルボニロキシ−１，４−フェニレン−１−メチル 1.5745 −ブチリデン−１，４−フェニレン） ポリ（オキシ−２，６−ジメチルフェニレン） 1.575 ポリオキシエチレンオキシテレフタロイル（アモルファス） 1.5750 （ポリエチレンテレフタレート） （結晶性ファイバ：1.51横断方向 1.64ファイバ方向） ポリビニルベンゾエート 1.5775 ポリ（オキシカルボニロキシ−１，４−フェニレンブチリデン 1.5792 −１，４−フェニレン） ポリ（１，２−ジフェニルエチルメタクリレート） 1.5816 ポリ（ｏ−クロロベンジルメタクリレート） 1.5823 ポリ（オキシカルボニロキシ−１，４−フェニレン−ｓｅｃ− 1.5827 ブチリデン−１，４−フェニレン） ポリオキシペンタエリスリトロキシフタロイル） 1.584 ポリ（ｍ−ニトロベンジルメタクリレート） 1.5845 ポリ（オキシカルボニロキシ−１，４−フェニレンイソプロピリデン 1.5850 −１，４−フェニレン） ポリ（Ｎ−（２−フェニルエチル）メタクリルアミド） 1.5857 ポリ（４−メトキシ−２−メチルスチレン） 1.5868
ポリ（ｏ−メチルスチレン） 1.5874 ポリスチレン 1.59 -1.592 ポリ（オキシカルボニロキシ−１，４−フェニレンシクロヘキシリデン 1.5900 −１，４−フェニレン） ポリ（ｏ−メトキシスチレン） 1.5932 ポリジフェニルメチルメタクリレート 1.5933 ポリ（オキシカルボニロキシ−１，４−フェニレンエチリデン 1.5937 −１，４−フェニレン） ポリ（ｐ−ブロモフェニルメタクリレート） 1.5964 ポリ（Ｎ−ベンジルメタクリルアミド） 1.5965 ポリ（ｐ−メトキシスチレン） 1.5967 硬化ゴム（３２％Ｓ） 1.6 ポリビニリデンクロライド 1.60 -1.63 ポリスルフィド（“Ｔｈｉｏｋｏｌ”） 1.6 -1.7 ポリ（ｏ−クロロジフェニルメチルメタクリレート） 1.6040 ポリ（オキシカルボニロキシ−１，４−（２，６−ジクロロ） 1.6056 フェニレン−イソプロピリデン−１，４− （２，６−ジクロロ）フェニレン） ポリ（オキシカルボニロキシビス（１，４−（３，５− 1.6056 ジクロロフェニレン））） ポリペンタクロロフェニルメタクリレート 1.608 ポリ（ｏ−クロロスチレン） 1.6098 ポリ（フェニルα−ブロモアクリレート） 1.612 ポリ（ｐ−ジビニルベンゼン） 1.6150 ポリ（Ｎ−ビニルフタルイミド） 1.6200 ポリ（２，６−ジクロロスチレン） 1.6248 ポリ（β−ナフチルメタクリレート） 1.6298 ポリ（α−ナフチルカルビニルメタクリレート） 1.63 ポリサルホン 1.633 ポリ（２−ビニルチオフェン） 1.6376 ポリ（α−ナフチルメタクリレート） 1.6410 ポリ（オキシカルボニロキシ−１，４−フェニレンジフェニル 1.6539 −メチレン−１，４−フェニレン） ポリビニルフェニルスルフィド 1.6568 ブチルフェノールフォルムアルデヒド樹脂 1.66 ウレア−チオウレア−フォルムアルデヒド樹脂 1.660 ポリビニルナフタレン 1.6818 ポリビニルカルバゾール 1.683 ナフタレン−フォルムアルデヒド樹脂 1.696 フェノール−フォルムアルデヒド樹脂 1.70 ポリペンタブロモフェニルメタクリレート 1.71 。Polyvinylidene fluoride 1.42 Polydimethylsilylene (polydimethylsiloxane) 1.43 Polytrifluoroethyl methacrylate 1.437 Polyoxypropylene 1.4495 Polyvinyl isobutyl ether 1.4507 Polyvinyl ethyl ether 1.4540 Polyoxyethylene 1.4563 Polyvinyl butyl ether 1.4563 Polyvinyl pentyl ether 1.4581 Polyvinyl hexyl ether 1.4591 Poly (4-methyl-1-pentene) 1.459 -1.465 Cellulose acetate butyrate 1.46 -1.49 Poly (4-fluoro-2-trifluoromethylstyrene) 1.46 Polyvinyl octyl ether 1.4613
Poly (vinyl 2-ethylhexyl ether) 1.4626 Polyvinyl decyl ether 1.4628 Poly (2-methoxyethyl acrylate) 1.463 Polybutyl acrylate 1.4631 Polybutyl acrylate 1.466 Poly (t-butyl methacrylate) 1.4638 Polyvinyl dodecyl ether 1.4640 Poly (3-ethoxypropyl acrylate) 1.465 Polyoxycarbonyltetramethylene 1.465 Polyvinyl propionate 1.4665 Polyvinyl acetate 1.4665 Polyvinyl methyl ether 1.467 Polyethyl acrylate 1.4685 Ethylene-vinyl acetate copolymer 1.47 -1.50 (80% -20% vinyl acetate) Cellulose propionate 1.47 -1.49 Cellulose Acetate propionate 1.47 Benzyl cellulose 1.47 -1.58 Phenol-formaldehyde resin 1.47 -1.70 Cellulose triase Tate 1.47 -1.48 Polyvinyl methyl ether (isotactic) 1.4700 Poly (3-methoxypropyl acrylate) 1.471 Poly (2-ethoxyethyl acrylate) 1.471 Polymethyl acrylate 1.472 -1.480 Polyisopropyl methacrylate 1.4728 Poly (1-decene) 1.4730 Polypropylene ( Atactic, density 0.8575 g / cm 3 ) 1.4735 poly (vinyl sec-butyl ether) (isotactic) 1.4740 polydodecyl methacrylate 1.4740
Polyoxyethylene oxysuccinoyl 1.4744 (Polyethylene succinate) Polytetradecyl methacrylate 1.4746 Ethylene-propylene copolymer (EPR-rubber) 1.4748-1.48 Polyhexadecyl methacrylate 1.4750 Polyvinyl formate 1.4757 Poly (2-fluoroethyl methacrylate) 1.4768 Polyisobutyl methacrylate 1.477 Ethylcellulose 1.479 Polyvinyl acetal 1.48 -1.50 Cellulose acetate 1.48 -1.50 Cellulose tripropionate 1.48 -1.49 Polyoxymethylene 1.48 Polyvinyl butyral 1.48 -1.49 Poly (n-hexyl methacrylate) 1.4813 Poly (n-butyl methacrylate) 1.483 Poly Ethylidene dimethacrylate 1.4831 Poly (2-ethoxyethyl methacrylate) 1.4833 Polyoxyethylene oxymale oil 1.4840 Remmalate) Poly (n-propyl methacrylate) 1.484 Poly (3,3,5-trimethylcyclohexyl methacrylate) 1.485 Polyethyl methacrylate 1.485 Poly (2-nitro-2-methylpropyl methacrylate) 1.4868 Polytriethylcarbinyl methacrylate 1.4889 Poly (1, 1-diethylpropylmethacrylate) 1.4889 polymethylmethacrylate 1.4893 1.490 poly (2-decyl-1,3-butadiene) 1.4899
Polyvinyl alcohol 1.49 -1.53 Polyethyl glycolate methacrylate 1.4903 Poly (3-methylcyclohexyl methacrylate) 1.4947 Poly (cyclohexyl α-ethoxy acrylate) 1.4969 Methyl cellulose (low viscosity) 1.497 Poly (4-methylcyclohexyl methacrylate) 1.4975 Polydecamethylene glycol dimethacrylate 1.4990 Polyurethane 1.5 -1.6 Poly (1,2-butadiene) 1.5000 Polyvinyl formal 1.50 Poly (2-bromo-4-trifluoromethylstyrene) 1.5 Cellulose nitrate 1.50 -1.514 Poly (sec-butyl α-chloroacrylate) 1.500 Poly (2-heptyl-1,3-butadiene) 1.5000 poly (ethyl α-chloroacrylate) 1.502 poly (2-isopropyl-1,3 butadiene) 1.5028 poly (2-methylcyclohexyl) Methacrylate) 1.5028 polypropylene (density 0.9075g / cm 3) 1.5030 polyisobutene 1.505 -1.51 poly isobornyl methacrylate 1.5059 poly (2-t-butyl-1,3-butadiene) 1.5060 Polyethylene glycol dimethacrylate 1.5063 poly cyclohexyl methacrylate 1.5066 poly (cyclohexane Diol-1,4-dimethacrylate) 1.5067 Butyl rubber (unvulcanized) 1.508 Polytetrahydrofurfuryl methacrylate) 1.5096 Guttapercha (β) 1.509 Polyethylene ionomer 1.51 Polyoxyethylene (high molecular weight) 1.51 -1.54 Polyethylene (density 0.914 g / cm 3 ) 1.51 (Density 0.94-0.945 g / cm 3 ) 1.52-1.53 (Density 0.965 g / cm 3 ) 1.545 Poly (1-methylcyclohexyl methacrylate) 1.5111 Poly (2-hydroxyethyl methacrylate) 1.5119 Polyvinyl chloroacetate 1.512 Polybutene (isotactic) 1.5125 Polyvinyl methacrylate 1.5129 Poly (N-butyl-methacrylamide) 1.5135 Guttaperca (α) 1.514 Terpene resin 1.515 Poly (1,3-butadiene) 1.5154 Shellac 1.51 -1.53 Poly (methyl α-) Chloroacrylate) 1.517 Poly (2-chloroethylmethacrylate) 1.517 Poly (2-diethylaminoethylmethacrylate) 1.5174 Poly (2-chlorocyclohexylmethacrylate) 1.5179 Poly (1,3-butadiene) (35% cis; 56% trans 1.5180; 7 % 1,2-contet) Natural rubber 1.519 -1.52 Polyallyl methacrylate 1.5196 Polyvinyl chloride + 40% Dioctyl phthalate 1.52 Polyacrylonitrile 1.52 1.5187 Polymethacrylonitrile 1.52 Poly (1,3 -Butadiene) (sic type rich) 1.52 Butadiene-acrylonitrile copolymer 1.52 Polymethyl isopropenyl ketone 1.5200 Polyisoprene 1.521 Polyester resin rigid (about 50% styrene) 1.523 -1.54 Poly (N- (2-methoxyethyl) methacrylamide) 1.5246 Poly (2,3-dimethyl butadiene) (methyl rubber) 1.525 Vinyl chloride-vinyl acetate copolymer (95 / 5-90 / 10) 1.525 -1.535 Polyacrydacid 1.527 Poly (1,3-dichloropropylmethacrylate) 1.5270 Poly (2-chloro-1- (chloromethyl) ethyl methacrylate) 1.5270 Polyacrolein 1.529 Poly (1-vinyl-2-pyrrolidone) 1.53 Hydrochlorinated rubber 1.53 -1.55 Nylon 6; Nylon 6,6; Nylon 6,10 (molded product) ) 1.53 (nylon-6-fiber: 1.515 crossing direction) 1.565 Fiber direction) Butadiene-styrene copolymer (about 30% styrene) 1.53 Block copolymer Poly (cyclohexyl α-chloroacrylate) 1.532 Poly (2-chloroethyl α-chloroacrylate) 1.533 Butadiene-styrene copolymer (about 75) / 25) 1.535 Poly (2-aminoethyl methacrylate) 1.537 Polyfurfuryl methacrylate 1.5381 Protein 1.539 -1.541 Polybutyl mercaptyl methacrylate 1.5390 Poly (1-phenyl-n-amyl methacrylate) 1.5396 Poly (N-methyl-methacrylamide) 1.5398 Cellulose 1.54 Polyvinyl chloride 1.54 -1.55 Ureaformaldehyde resin 1.54 -1.56 Poly (sec-butyl α-bromoacrylate) 1.542 Poly (cyclohexyl α-bromoacrylate) 1.542 Poly (2-bromoethylmethacryl) Relate) 1.5426 Polydihydroabietic acid 1.544 Polyavitic acid 1.546 Polyethylmercaptyl methacrylate 1.547 Poly (N-allylmethacrylamide) 1.5476 Poly (1-phenylethylmethacrylate) 1.5487 Polyvinylfuran 1.55 Poly (2-vinyltetrahydrofuran) 1.55 Poly (Vinyl chloride) + 40% tricresyl phosphate 1.55 Epoxy resin 1.55-1.60 Poly (p-methoxybenzyl methacrylate) 1.552 Polyisopropyl methacrylate 1.552 Poly (p-isopropylstyrene) 1.554 Polychloroprene 1.554 -1.558 Poly (oxyethylene-α-) Benzoate-ω-methacrylate) 1.555 poly (p, p'-xylylenyl dimethacrylate) 1.5559 poly (1-phenylallyl methacrylate) 1.5573 poly (p-cyclohexyl) Luphenyl methacrylate) 1.5575 Poly (2-phenylethyl methacrylate) 1.5592 Poly (oxycarbonyloxy-1,4-phenylene-1-propyl 1.5602-Butylidene-1,4-phenylene) poly (1- (o-chlorophenyl) ethyl Methacrylate) 1.5624 Styrene-maleic anhydride copolymer 1.564 Poly (1-phenylcyclohexyl methacrylate) 1.5645 Poly (oxycarbonyloxy-1,4-phenylene-1,3 1.5671-Dimethyl-butylidene-1,4-phenylene) Poly (Methyl α-bromoacrylate) 1.5672 Polybenzyl methacrylate 1.5680 Poly (2- (phenylsulfonyl) ethyl methacrylate) 1.5682
Poly (m-cresyl methacrylate) 1.5683 Styrene-acrylonitrile copolymer (about 75/25) 1.57 Poly (oxycarbonyloxy-1,4-phenylene isobutylidene 1.5702-1,4-phenylene) Poly (o-methoxy) Phenylmethacrylate) 1.5705 Polyphenylmethacrylate 1.5706 Poly (o-cresylmethacrylate) 1.5707 Polydiallylphthalate 1.572 Poly (2,3-dibromopropylmethacrylate) 1.5739 Poly (oxycarbonyloxy-1,4-phenylene-1-methyl 1.5745- Butylidene-1,4-phenylene) Poly (oxy-2,6-dimethylphenylene) 1.575 Polyoxyethylene oxyterephthaloyl (amorphous) 1.5750 (Polyethylene terephthalate) (Crystalline fiber: 1.51 Transverse direction 1.64 Fiber direction) Polyvinyl Rubenzoate 1.5775 Poly (oxycarbonyloxy-1,4-phenylene butylidene 1.5792-1,4-phenylene) Poly (1,2-diphenylethyl methacrylate) 1.5816 Poly (o-chlorobenzyl methacrylate) 1.5823 Poly (oxycarbonyl) Roxy-1,4-phenylene-sec-1.5827 Butylidene-1,4-phenylene) Polyoxypentaerythritoloxyphthaloyl) 1.584 Poly (m-nitrobenzyl methacrylate) 1.5845 Poly (oxycarbonyloxy-1,4-phenylene) Isopropylidene 1.5850-1,4-phenylene) Poly (N- (2-phenylethyl) methacrylamide) 1.5857 Poly (4-methoxy-2-methylstyrene) 1.5868
Poly (o-methylstyrene) 1.5874 Polystyrene 1.59 -1.592 Poly (oxycarbonyloxy-1,4-phenylenecyclohexylidene 1.5900-1,4-phenylene) Poly (o-methoxystyrene) 1.5932 Polydiphenylmethylmethacrylate 1.5933 Poly ( Oxycarbonyloxy-1,4-phenylene ethylidene 1.5937-1,4-phenylene) Poly (p-bromophenyl methacrylate) 1.5964 Poly (N-benzylmethacrylamide) 1.5965 Poly (p-methoxystyrene) 1.5967 Cured rubber (32% S) 1.6 Polyvinylidene chloride 1.60 -1.63 Polysulfide ("Thiokol") 1.6 -1.7 Poly (o-chlorodiphenylmethylmethacrylate) 1.6040 Poly (oxycarbonyloxy-1,4- (2,6-dichloro) 1.6056 Phenylene-isopropyi Reden-1 4- (2,6-dichloro) phenylene) poly (oxycarbonyloxybis (1,4- (3,5-1.6056 dichlorophenylene))) polypentachlorophenyl methacrylate 1.608 poly (o-chlorostyrene) 1.6098 poly (phenyl α-bromoacrylate) 1.612 Poly (p-divinylbenzene) 1.6150 Poly (N-vinylphthalimide) 1.6200 Poly (2,6-dichlorostyrene) 1.6248 Poly (β-naphthylmethacrylate) 1.6298 Poly (α-naphthylcarbylmethacrylate) 1.63 Polysulfone 1.633 Poly (2-vinylthiophene) 1.6376 Poly (α-naphthylmethacrylate) 1.6410 Poly (oxycarbonyloxy-1,4-phenylenediphenyl) 1.6539-Methylene-1,4-phenylene) Polyvinylphenyl sulfide 1.6568 Butylphenolform Aldehyde resin 1.66 urea - thiourea - formaldehyde resin 1.660 polyvinylnaphthalene 1.6818 polyvinylcarbazole 1.683 naphthalene - formaldehyde resin 1.696 phenol - formaldehyde resin 1.70 Poly pentabromophenyl methacrylate 1.71.
【００１１】以上の説明から明らかなように、本発明の
回折格子は、屈折率の異なる２種以上の材料からなる層
を屈折率が相対的に高・低と繰り返すように交互に積層
させて構成したことを特徴とするものである。As is clear from the above description, in the diffraction grating of the present invention, layers made of two or more kinds of materials having different refractive indexes are alternately laminated so that the refractive indexes are relatively high and low. It is characterized by being configured.
【００１２】この場合、層の厚さが少なくとも一部の異
なる層間で異なるようにすることが、広い波長範囲の回
折を行わせるために必要である。In this case, it is necessary that the layers have different thicknesses between at least some different layers in order to perform diffraction in a wide wavelength range.
【００１３】実際にこのような回折格子を作成するに
は、屈折率の異なる２種以上の材料からなるフィルム状
シートを交互に積層して構成するか、各層をコーティン
グにより積層して構成するのが望ましく、また、各層の
厚さの制御には、積層体を延伸法、プレス法等の機械的
手段により変形して行うのが望ましい。なお、この変形
は、厚みを薄くする方向だけではなく、厚くする方向の
変形も考えられる。In order to actually form such a diffraction grating, film-like sheets made of two or more kinds of materials having different refractive indexes are alternately laminated, or each layer is laminated by coating. It is desirable to control the thickness of each layer by deforming the laminate by a mechanical means such as a stretching method or a pressing method. It should be noted that this deformation can be considered not only in the direction of decreasing the thickness but also in the direction of increasing the thickness.
【００１４】また、このような回折格子は例えば熱線反
射膜として用いることができる。Further, such a diffraction grating can be used as, for example, a heat ray reflective film.
【００１５】[0015]
【作用】本発明においては、屈折率の異なる２種以上の
材料からなる層を屈折率が相対的に高・低と繰り返すよ
うに交互に積層させて構成しているので、層間の厚さを
異ならせることにより、回折波長が広い回折格子を得る
ことができる。In the present invention, since the layers made of two or more kinds of materials having different refractive indexes are alternately laminated so that the refractive index is relatively high and low, the thickness between the layers can be reduced. By making them different, it is possible to obtain a diffraction grating having a wide diffraction wavelength.
【００１６】[0016]
【実施例】以下、本発明の１実施例について説明する。
ポリビニリデンクロライドフィルム（２５μｍ厚、屈折
率１．６２）とポリビニリデンフルオライドフィルム
（２５μｍ厚、屈折率１．４２）を、加熱雰囲気中で延
伸処理をし、それぞれについて、１０μｍ、１１．２５
μｍ、１２μｍ、・・・、２３．７５μｍ、２５μｍの
膜厚を持つ１３種類の膜厚に変化させたフィルムを得
た。EXAMPLE One example of the present invention will be described below.
A polyvinylidene chloride film (25 μm thick, refractive index 1.62) and a polyvinylidene fluoride film (25 μm thick, refractive index 1.42) were stretched in a heating atmosphere, and 10 μm and 11.25 respectively.
Films having various thicknesses of 13 μm, 12 μm, ..., 23.75 μm, and 25 μm were obtained.
【００１７】まず、それぞれの１０μｍ厚のフィルムを
４枚ずつ計８枚を交互に屈折率が高・低・高・低・・・
となるように積層し、加熱しつつドライラミネーション
を行った。First, four films each having a thickness of 10 μm, eight films in total, are alternately arranged so that the refractive index is high / low / high / low ...
The layers were laminated so as to be the same, and dry lamination was performed while heating.
【００１８】順次、１１．２５μｍ、１２μｍ、・・
・、２３．７５μｍ、２５μｍ厚のフィルムを用いて、
同様にラミネーションを行った。Sequentially 11.25 μm, 12 μm, ...
., Using a 23.75 μm, 25 μm thick film,
Lamination was performed in the same manner.
【００１９】できあがった１３枚のラミネーションフィ
ルムをさらに延伸処理し、２５倍に引き伸ばしてそれぞ
れの厚みを２５分の１にした。これら延伸処理した１３
枚のフィルムは、それぞれ、図４に示すような回折特性
を有しており、これら１３枚を積層してドライラミネー
ションすることにより、図３に示したように、ほぼ８０
０ｎｍから２０００ｎｍの波長範囲で平滑な回折特性を
持つ回折格子を作成することができた。The 13 laminated films thus prepared were further stretched and stretched 25 times to reduce the thickness to 1/25. These stretched 13
Each of the films has diffractive characteristics as shown in FIG. 4, and when these 13 films are laminated and dry laminated, as shown in FIG.
It was possible to create a diffraction grating having a smooth diffraction characteristic in the wavelength range of 0 nm to 2000 nm.
【００２０】[0020]
【発明の効果】以上の説明から明らかなように、本発明
の回折格子によると、屈折率の異なる２種以上の材料か
らなる層を屈折率が相対的に高・低と繰り返すように交
互に積層させて構成しているので、層間の厚さを異なら
せることにより、回折波長が広い回折格子を得ることが
できる。As is clear from the above description, according to the diffraction grating of the present invention, layers made of two or more kinds of materials having different refractive indexes are alternately arranged so that the refractive index is relatively high and low. Since the layers are laminated, it is possible to obtain a diffraction grating having a wide diffraction wavelength by making the thicknesses of the layers different.
【００２１】具体的には、回折波長範囲を例えば８００
〜２０００ｎｍにすることができ、この場合は、可視光
を通過し熱線を反射する良好な熱線反射膜になる。この
熱線反射膜を自動車や建物の窓に用いるのことにより、
車内及び室内の温度上昇を低減することができる。Specifically, the diffraction wavelength range is set to, for example, 800
The thickness can be up to 2000 nm, and in this case, a good heat ray reflective film that transmits visible light and reflects heat rays is obtained. By using this heat ray reflective film for windows of automobiles and buildings,
It is possible to reduce the temperature rise inside and inside the vehicle.
【図１】本発明の回折格子の１つの具体例の断面図であ
る。1 is a cross-sectional view of one embodiment of the diffraction grating of the present invention.
【図２】図１の回折格子の回折特性を示す図である。FIG. 2 is a diagram showing diffraction characteristics of the diffraction grating of FIG.
【図３】実施例の回折格子の回折特性を示す図である。FIG. 3 is a diagram showing diffraction characteristics of the diffraction grating of the example.
【図４】実施例の各ラミネーションフィルムの回折特性
を示す図である。FIG. 4 is a diagram showing the diffraction characteristics of each lamination film of the example.
１、３、５…高屈折率フィルム ２、４、６…低屈折率フィルム 1, 3, 5 ... High refractive index film 2, 4, 6 ... Low refractive index film
Claims (6)
層を屈折率が相対的に高・低と繰り返すように交互に積
層させて構成したことを特徴とする回折格子。1. A diffraction grating characterized by being constituted by alternately laminating layers made of two or more kinds of materials having different refractive indexes so as to repeat relatively high and low refractive indexes.
で異なるようにしたことを特徴とする請求項１記載の回
折格子。2. The diffraction grating according to claim 1, wherein the layers have different thicknesses among at least some different layers.
フィルム状シートを交互に積層して構成したことを特徴
とする請求項１又は２記載の回折格子。3. The diffraction grating according to claim 1, wherein film-like sheets made of two or more kinds of materials having different refractive indexes are alternately laminated.
したことを特徴とする請求項１又は２記載の回折格子。4. The diffraction grating according to claim 1, wherein each layer is formed by laminating coating layers.
段により変形して各層の厚みを変化させて作成したこと
を特徴とする請求項１から４の何れか１項記載の回折格
子。5. The diffraction grating according to claim 1, wherein the laminated body is formed by deforming the laminated body by a mechanical means such as a stretching method or a pressing method to change the thickness of each layer. ..
する請求項１から５の何れか１項記載の回折格子。6. The diffraction grating according to claim 1, which is configured as a heat ray reflective film.