JP3327354B2 - Hologram layer-enclosed laminated glass and laminate used for its production - Google Patents
Hologram layer-enclosed laminated glass and laminate used for its productionInfo
- Publication number
- JP3327354B2 JP3327354B2 JP21585393A JP21585393A JP3327354B2 JP 3327354 B2 JP3327354 B2 JP 3327354B2 JP 21585393 A JP21585393 A JP 21585393A JP 21585393 A JP21585393 A JP 21585393A JP 3327354 B2 JP3327354 B2 JP 3327354B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- hologram
- laminated
- silicon oxide
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ホログラム層が封入さ
れた合わせガラス及びその製造に使用される積層体に関
し、特に、自動車用のヘッドアップディスプレーのコン
バイナー、自動車または建築物の窓ガラス用の熱線反射
膜等への用途に有用な、ホログラム層封入合わせガラス
及びその製造に使用される積層体に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a laminated glass in which a hologram layer is encapsulated and a laminate used for the production thereof, and more particularly to a combiner for a head-up display for automobiles and a window glass for automobiles or buildings. The present invention relates to a hologram layer-enclosed laminated glass useful for application to a heat ray reflection film or the like, and a laminate used for producing the same.
【０００２】[0002]
【従来の技術】近年、ホログラムは、装飾用、偽造防止
用、光学素子用等に広く利用されるようになってきてお
り、特に最近では波長選択性に優れ、立体感も優れる体
積位相型（リップマン型）のホログラムが注目されてい
る。2. Description of the Related Art In recent years, holograms have been widely used for decoration, forgery prevention, optical elements, and the like. In particular, recently, holograms are excellent in wavelength selectivity and three-dimensional appearance. A hologram of the Lippmann type is drawing attention.
【０００３】例えば、ホログラムコンバイナーは１つの
光学素子であり、その機能は半透過性結像素子と言うこ
とができる。図７（ａ）はその撮影方法を説明するため
の図であり、レーザー２０から発振された光をハーフミ
ラー２１で２分し、それぞれのレーザー光をレンズ２
２、２３で１点からでる発散光に変え、フォトポリマー
等の体積位相型ホログラム記録材料３′の両側からこれ
ら２つの発散光を入射させてリップマンホログラムとし
て干渉させたものがホログラムコンバイナーである。For example, a hologram combiner is one optical element, and its function can be called a semi-transmissive imaging element. FIG. 7A is a diagram for explaining the image capturing method. The light oscillated from the laser 20 is split into two by a half mirror 21 and each laser light is
The hologram combiner converts the divergent light emitted from one point at 2 and 23, and makes these two divergent lights incident from both sides of the volume phase hologram recording material 3 'such as a photopolymer to cause interference as a Lippmann hologram.
【０００４】このようなホログラムコンバイナー３は、
同図（ｂ）に示すように、撮影の際の一方の発散点近傍
に設置した表示体２５から出た光を反射方向に回折し、
その回折像をあたかも撮影の際の他方の発散点近傍に設
置された表示体の像２５’から出たように行うもので、
その結像倍率及び像位置は、撮影時の発散点と記録材料
との相対距離Ｌ，Ｌ’によって決まり、しかも、記録の
際の波長またはそれと特定の関係がある波長の光しか回
折せず、他の波長の光は透過するので、像を重畳または
合成できるものである。このようなホログラムコンバイ
ナーに代表される光学素子として、ヘッドアップディス
プレー用のコンバイナー等があげられる。[0004] Such a hologram combiner 3 comprises:
As shown in FIG. 2B, light emitted from the display body 25 installed near one of the divergence points at the time of shooting is diffracted in the reflection direction.
The diffraction image is performed as if it came out of an image 25 ′ of a display body installed near the other divergence point at the time of shooting,
The imaging magnification and the image position are determined by the relative distances L and L 'between the divergence point and the recording material at the time of photographing, and furthermore, only the wavelength at the time of recording or a light having a specific relation to the wavelength diffracts. Since light of other wavelengths is transmitted, an image can be superimposed or synthesized. An optical element represented by such a hologram combiner includes a combiner for a head-up display.
【０００５】特に、自動車用途として合わせガラス形態
で用いられる場合には、日本工業規格の自動車用安全ガ
ラスの規格（ＪＩＳ３２１１、３２１２）を満足しなく
てはならない。ＪＩＳの用語では、「合わせガラスと
は、２枚以上の板ガラスをプラスチックを中間膜として
接着したもので、外力の作用によって破損しても中間膜
によって破片の大部分が飛び散らないようにしたもの」
と定義され、プラスチックの中間膜としては、通常、ポ
リビニルブチラール膜が用いられている。[0005] In particular, when used in the form of a laminated glass for automotive applications, it must satisfy the Japanese Industrial Standards for automotive safety glass (JIS 3211, 3212). According to JIS terms, "Laminated glass is a laminate of two or more plate glasses made of plastic as an interlayer, so that even if it is damaged by the action of an external force, most of the shards are not scattered by the interlayer."
In general, a polyvinyl butyral film is used as a plastic intermediate film.
【０００６】このような合わせガラス中に、ヘッドアッ
プディスプレー用のコンバイナーとしてのホログラムを
封入する場合は、板ガラス／ホログラム／ポリビニルブ
チラール膜／板ガラスの構成とされ、ローラによる加圧
等により予備圧着させた後、１３０℃程度に加熱、加圧
して本圧着して製造され、ホログラム積層側を車内方
向、ポリビニルブチラール膜積層側を車外方向として使
用される。[0006] When a hologram as a combiner for a head-up display is sealed in such a laminated glass, the laminated glass has a configuration of plate glass / hologram / polyvinyl butyral film / plate glass, and is preliminarily pressed by a roller or the like. Thereafter, it is manufactured by heating and pressurizing it to about 130 ° C. and performing full pressure bonding, and the hologram lamination side is used as the vehicle interior direction, and the polyvinyl butyral film lamination side is used as the vehicle exterior direction.
【０００７】しかしながら、この層構成では、ホログラ
ムとポリビニルブチラール膜とが直接接触しているた
め、ポリビニルブチラール中に含有しているテトラエチ
レングリコール・ｎ−ヘプタネート、ジ−（ｎ−ヘキシ
ル）アジペート、トリエチレングリコール・ジ−（２−
エチルブチレート）等の可塑剤がホログラムの構造中に
浸透することにより干渉縞の構造を乱され、特性の経時
変化が生じ、像品質が劣化するという問題があり、その
ため、ポリビニルアルコール等の可塑剤バリア層をホロ
グラム層とポリビニルブチラール層との間に介在させ
て、可塑剤のホログラムへの浸透を防止することが行な
われている。However, in this layer configuration, since the hologram is in direct contact with the polyvinyl butyral film, tetraethylene glycol / n-heptane, di- (n-hexyl) adipate, Ethylene glycol di- (2-
The plasticizer such as ethyl butyrate) penetrates into the hologram structure, disturbing the structure of the interference fringes, causing the characteristics to change over time, and deteriorating the image quality. An agent barrier layer is interposed between the hologram layer and the polyvinyl butyral layer to prevent the penetration of the plasticizer into the hologram.
【０００８】しかしながら、ポリビニルアルコールフイ
ルムを可塑剤バリア層として使用すると、可塑剤の浸透
性を防止するものの、透湿性や透気性を有し、合わせガ
ラスの作製時での状況により、ホログラム特性に影響を
与えるという問題を有している。また、従来は、ホログ
ラム層や可塑剤バリア層の積層作業が見当合わせして手
作業で行なわれているが、ホログラムフイルムや可塑剤
バリアフィルムは、いずれも極めて薄膜であり、また、
高い積層精度が要求されるという問題がある。However, when a polyvinyl alcohol film is used as a plasticizer barrier layer, the hologram characteristics are affected by the situation at the time of manufacturing a laminated glass, although it has moisture permeability and air permeability although it prevents penetration of the plasticizer. Has the problem of giving Conventionally, the lamination work of the hologram layer and the plasticizer barrier layer is manually performed in register, but the hologram film and the plasticizer barrier film are both extremely thin,
There is a problem that high lamination accuracy is required.
【０００９】[0009]
【発明が解決しようとする課題】本発明は、積層精度に
優れ、かつ作業効率に優れるとともに、透明性に優れ、
可塑剤、透湿性、透気性に対する高度なバリア性を有す
るホログラム層封入合わせガラスの製造に使用される積
層体、及びその積層体を使用して製造されるホログラム
層封入合わせガラスの提供を課題とする。DISCLOSURE OF THE INVENTION The present invention is excellent in lamination accuracy, excellent in work efficiency, excellent in transparency,
An object of the present invention is to provide a laminated body used for producing a hologram layer-enclosed laminated glass having a high barrier property against a plasticizer, moisture permeability, and air permeability, and to provide a hologram layer-enclosed laminated glass produced using the laminated body. I do.
【００１０】[0010]
【課題を解決するための手段】本発明の第１のホログラ
ム層封入合わせガラスは、ガラス／ホログラム層／珪素
酸化物層／可塑剤を含む合成樹脂膜／ガラスの順に積層
されたことを特徴とする。A first hologram layer-sealed laminated glass of the present invention is characterized in that it is laminated in the order of glass / hologram layer / silicon oxide layer / synthetic resin film containing a plasticizer / glass. I do.
【００１１】本発明の第２のホログラム層封入合わせガ
ラスは、ガラス／可塑剤を含む合成樹脂膜／珪素酸化物
層／ホログラム層／珪素酸化物層／可塑剤を含む合成樹
脂膜／ガラスの順に積層されたことを特徴とする。The second hologram layer-encapsulated laminated glass of the present invention comprises glass / a synthetic resin film containing a plasticizer / a silicon oxide layer / a hologram layer / a silicon oxide layer / a synthetic resin film containing a plasticizer / glass. It is characterized by being laminated.
【００１２】また、上記の第１〜第２のホログラム層封
入合わせガラスにおいて、珪素酸化物層が、接着剤との
混合層、若しくはその両面或いは片面に接着剤層を有す
るものであることを特徴とする。Further, in the above-mentioned first and second hologram layer-sealed laminated glasses, the silicon oxide layer is characterized by having a mixed layer with an adhesive or having an adhesive layer on both surfaces or one surface thereof. And
【００１３】更に、上記の第１〜第２のホログラム層封
入合わせガラスにおいて、ホログラム層が、接着剤との
混合層、若しくはその両面或いは片面に接着剤層を有す
るものであることを特徴とする。Further, in the first and second hologram layer-enclosed laminated glasses, the hologram layer is characterized by having a mixed layer with an adhesive or having an adhesive layer on both surfaces or one surface thereof. .
【００１４】更に、上記の第１〜第２のホログラム層封
入合わせガラスにおいて、珪素酸化物層の積層面積が、
合わせガラス作製時の加熱圧着操作により、ホログラム
層を、その積層面を除いた表面の全周にわたって被覆可
能とする大きさとされたものであることを特徴とする。Further, in the above-mentioned first and second hologram layer-sealed laminated glasses, the lamination area of the silicon oxide layer is as follows:
It is characterized in that the hologram layer is sized so as to be able to cover the entire periphery of the surface excluding the lamination surface by a heat-pressing operation at the time of producing a laminated glass.
【００１５】本発明の第１のホログラム層封入合わせガ
ラスの製造に使用される積層体（以下、第１の積層体と
いう）は、カバーフィルム／ホログラム層／珪素酸化物
層／カバーフィルムを順次積層してなるものであり、両
カバーフィルムが剥離除去されて使用されるものである
ことを特徴とする。The laminated body (hereinafter referred to as the first laminated body) used for producing the first hologram layer-enclosed laminated glass of the present invention comprises a cover film / hologram layer / silicon oxide layer / cover film laminated in order. Wherein both cover films are used after being peeled off.
【００１６】また、本発明の第１のホログラム層封入合
わせガラスの製造に使用される積層体（以下、第２の積
層体という）は、カバーフィルム／ホログラム層／珪素
酸化物層／可塑剤を含む合成樹脂膜／カバーフィルムを
順次積層してなるものであり、両カバーフィルムが剥離
除去されて使用されるものであることを特徴とする。The laminate (hereinafter, referred to as a second laminate) used for manufacturing the first hologram layer-sealed laminated glass of the present invention comprises a cover film / hologram layer / silicon oxide layer / plasticizer. A synthetic resin film / cover film is sequentially laminated, and both cover films are used after being peeled off.
【００１７】本発明の第２のホログラム層封入合わせガ
ラスの製造に使用される積層体（以下、第３の積層体と
いう）は、カバーフィルム／珪素酸化物層／ホログラム
層／珪素酸化物層／カバーフィルムを順次積層してなる
ものであり、両カバーフィルムが剥離除去されて使用さ
れるものであることを特徴とする。The laminate (hereinafter, referred to as a third laminate) used for manufacturing the second hologram layer-enclosed laminated glass of the present invention is a cover film / silicon oxide layer / hologram layer / silicon oxide layer / A cover film is sequentially laminated, and both cover films are used after being peeled off.
【００１８】本発明の第２のホログラム層封入合わせガ
ラスの製造に使用される積層体（以下、第４の積層体と
いう）は、カバーフィルム／可塑剤を含む合成樹脂膜／
珪素酸化物層／ホログラム層／珪素酸化物層／可塑剤を
含む合成樹脂膜／カバーフィルムを順次積層してなるも
のであり、両カバーフィルムが剥離除去されて使用され
るものであることを特徴とする。A laminate (hereinafter, referred to as a fourth laminate) used for producing the second hologram layer-enclosed laminated glass of the present invention comprises a cover film / a synthetic resin film containing a plasticizer /
It is obtained by sequentially laminating a silicon oxide layer / hologram layer / silicon oxide layer / synthetic resin film containing a plasticizer / cover film, wherein both cover films are peeled off and used. And
【００１９】また、上記の第１〜第４の積層体におい
て、珪素酸化物層が、接着剤との混合層、若しくはその
両面或いは片面に接着剤層を有するものであることを特
徴とする。Further, in the above-mentioned first to fourth laminates, the silicon oxide layer is characterized in that it has a mixed layer with an adhesive or has an adhesive layer on both surfaces or one surface thereof.
【００２０】更に、上記の第１〜第４の積層体におい
て、ホログラム層が、接着剤との混合層、若しくはその
両面或いは片面に接着剤層を有するものであることを特
徴とする。Further, in the above-mentioned first to fourth laminates, the hologram layer is characterized in that the hologram layer has a mixed layer with an adhesive or has an adhesive layer on both surfaces or one surface thereof.
【００２１】更に、上記の第１〜第４の積層体におい
て、珪素酸化物層の積層面積が、合わせガラス作製時の
加熱圧着操作により、ホログラム層を、その積層面を除
いた表面の全周にわたって被覆可能とする大きさとされ
たものであることを特徴とする。Further, in the above-described first to fourth laminates, the lamination area of the silicon oxide layer is set such that the hologram layer is formed around the entire surface excluding the lamination surface by a heat-pressing operation at the time of manufacturing a laminated glass. Characterized in that it is sized so that it can be covered over a wide area.
【００２２】まず、本発明における第１の積層体及び本
発明の第１〜第４の積層体において共通する積層物につ
いて、図１により説明する。図１は、本発明の第１の積
層体を断面により説明するための図で、図中、１はカバ
ーフィルム、２は接着剤層、３はホログラム、４は珪素
酸化物層を示す。First, a laminate common to the first laminate of the present invention and the first to fourth laminates of the present invention will be described with reference to FIG. FIG. 1 is a diagram for explaining a first laminate of the present invention by a cross section. In the drawing, 1 indicates a cover film, 2 indicates an adhesive layer, 3 indicates a hologram, and 4 indicates a silicon oxide layer.
【００２３】カバーフィルムとしては、ポリエチレン
（ＰＥ）フィルム、一軸延伸ポリエチレンフィルム、二
軸延伸ポリエチレンフィルム、延伸ポリプロピレン（Ｏ
ＰＰ）フィルム、無延伸ポリプロピレン（ＣＰＰ）フィ
ルム、エチレン・酢酸ビニル共重合体（ＥＶＡ）フィル
ム、アイオノマーフィルム、エチレン・エチルアクリレ
ート共重合体（ＥＥＡ）フィルム、エチレン・アクリル
酸共重合体（ＥＡＡ）フィルム、エチレン・メタクリル
酸共重合体（ＥＭＡＡ）フィルム、エチレン・メチルメ
タクリレート共重合体（ＥＭＭＡ）フィルム、エチレン
・アクリル酸メチル共重合体（ＥＭＡ）フィルム、ポリ
エステルフィルム、ナイロンフィルム、トリアセチルセ
ルロースフィルム、エチレン・ビニルアルコール共重合
体（ＥＶＯＨ）フィルム、ポリ塩化ビニリデン（ＰＶＤ
Ｃ）フィルム、二軸延伸ポリ塩化ビニリデンフィルム、
ポリフッ化ビニリデンフィルム、ポリアクリロニトリル
（ＰＡＮ）フィルム、ポリブチレンテレフタレート（Ｐ
ＢＴ）フィルム、ポリエチレンテレフタレート（ＰＥ
Ｔ）フィルム、ポリエチレンナフタレート（ＰＥＮ）フ
ィルム、アモルファスポリエチレンテレフタレート（Ａ
−ＰＥＴ）フィルム、ポリスチレンフィルム、ポリ塩化
ビニルフィルム、ポリビニルアルコールフィルム、ポリ
カーボネート（ＰＣ）フィルム、ポリメチルメタクリレ
ート（ＰＭＭＡ）フィルム、ポリウレタンフィルム、フ
ッ素樹脂フィルム、ポリメチルペンテンフィルム、ポリ
ブテンフィルム、ポリイミドフィルム、ポリアリレート
フィルム等が挙げられる。また各種共押出しフィルムも
使用できる。これらのカバーフィルムは、積層体への支
持性が要求され、膜厚１μｍ〜５００μｍ、好ましくは
１０μｍ〜１００μｍとするとよい。また、カバーフィ
ルムはホログラム層封入合わせガラスの作製時に際し
て、剥離除去される。As the cover film, polyethylene (PE) film, uniaxially stretched polyethylene film, biaxially stretched polyethylene film, stretched polypropylene (O
PP) film, unstretched polypropylene (CPP) film, ethylene / vinyl acetate copolymer (EVA) film, ionomer film, ethylene / ethyl acrylate copolymer (EEA) film, ethylene / acrylic acid copolymer (EAA) film , Ethylene-methacrylic acid copolymer (EMAA) film, ethylene-methyl methacrylate copolymer (EMMA) film, ethylene-methyl acrylate copolymer (EMA) film, polyester film, nylon film, triacetyl cellulose film, ethylene・ Vinyl alcohol copolymer (EVOH) film, polyvinylidene chloride (PVD)
C) film, biaxially oriented polyvinylidene chloride film,
Polyvinylidene fluoride film, polyacrylonitrile (PAN) film, polybutylene terephthalate (P
BT) film, polyethylene terephthalate (PE)
T) film, polyethylene naphthalate (PEN) film, amorphous polyethylene terephthalate (A
-PET) film, polystyrene film, polyvinyl chloride film, polyvinyl alcohol film, polycarbonate (PC) film, polymethyl methacrylate (PMMA) film, polyurethane film, fluororesin film, polymethylpentene film, polybutene film, polyimide film, poly Arylate film and the like can be mentioned. Various coextruded films can also be used. These cover films are required to have support for the laminate, and have a thickness of 1 μm to 500 μm, preferably 10 μm to 100 μm. In addition, the cover film is peeled and removed at the time of producing the hologram layer-enclosed laminated glass.
【００２４】次に、ホログラム層３としては、記録材料
として銀塩、重クロム酸ゼラチン、フォトポリマー等の
公知のホログラム記録材料を使用することができるが、
本発明の合わせガラスに封入される場合には、体積型で
位相型のホログラムとするとよく、特に、湿式の現像工
程を必要としないフォトポリマーが好ましい。フォトポ
リマーとしてはアクリル樹脂系のフォトポリマー等が挙
げられる。Next, as the hologram layer 3, known hologram recording materials such as silver salt, gelatin dichromate, and photopolymer can be used as recording materials.
When enclosed in the laminated glass of the present invention, a volume type and phase type hologram may be used, and a photopolymer which does not require a wet developing step is particularly preferable. Examples of the photopolymer include an acrylic resin-based photopolymer.
【００２５】また、ホログラム層は、記録材料層にホロ
グラムを記録した後に積層されてもよいが、ホログラム
記録は未記録の記録材料層を使用して本発明における積
層体とした後でもよく、或いは積層過程のいずれかの段
階で記録材料層にホログラム記録し、ホログラム層を形
成してもよい。The hologram layer may be laminated after recording the hologram on the recording material layer. The hologram recording may be performed after the unrecorded recording material layer is used to form the laminate in the present invention, or Hologram recording may be performed on the recording material layer at any stage of the lamination process to form a hologram layer.
【００２６】ホログラム層の大きさはその用途に応じて
適宜のものとできるが、本発明における第１〜第４の積
層体においては、ホログラム層の周辺に１ｃｍ〜５ｃｍ
の巾の未記録部分を形成しておくと、その端部からの可
塑剤の浸透によるホログラムの劣化を防止することがで
きる。The size of the hologram layer can be appropriately determined according to its use. In the first to fourth laminates of the present invention, the size of the hologram layer is 1 cm to 5 cm around the hologram layer.
By forming an unrecorded portion having a width of, it is possible to prevent the hologram from deteriorating due to the penetration of the plasticizer from its end.
【００２７】次に、珪素酸化物層４について説明する。
珪素酸化物層は、透明性、可塑剤のホログラム層への浸
透防止性に優れ、また、合わせガラス作製時の加熱程度
ではその熱収縮性は殆どないので、従来の珪素酸化物層
に比してホログラム特性に影響を与えることがないもの
である。特に、積層体においては、透湿性、透気性に対
するバリア性に優れるので、ホログラム特性への影響を
与えることがなく、保存性の優れたものとすることがで
きる。Next, the silicon oxide layer 4 will be described.
The silicon oxide layer is excellent in transparency and in preventing the penetration of the plasticizer into the hologram layer, and has almost no heat shrinkage when heated during the production of laminated glass. This does not affect the hologram characteristics. In particular, since the laminate has excellent barrier properties against moisture permeability and air permeability, it can have excellent storage stability without affecting the hologram characteristics.
【００２８】珪素酸化物層は、接着剤を介して蒸着法に
より積層されるか、または塗布法により積層される。蒸
着法としては、接着層上に珪素酸化物を蒸着源として真
空蒸着するか、または硅素を母材とし、酸素を含有する
不活性ガス雰囲気下でスパッタリングして珪素酸化物を
１００Å〜３０００Åの膜厚で積層するとよく、その組
成としてはＳｉＯx （０＜ｘ≦２）で示されるものであ
る。The silicon oxide layer is laminated by a vapor deposition method via an adhesive or laminated by a coating method. As a vapor deposition method, silicon oxide is deposited on the adhesive layer by vacuum deposition using silicon oxide as a deposition source, or silicon oxide is sputtered in an inert gas atmosphere containing oxygen to form a silicon oxide film having a thickness of 100 to 3000 mm. The layers may be stacked in a thickness, and the composition is represented by SiO x (0 <x ≦ 2).
【００２９】また、塗布法としては、珪素酸化物微粒
子、例えばＳｉＯ2 粒子を樹脂、例えばフェノール−ノ
ボラック樹脂中に分散させた樹脂溶融物、またはＳｉＯ
2 コーティング用金属アルコキシド溶液を、直接ロール
コート法、スプレーコート法等により塗布し、１０００
Å〜３０００Åの乾燥後膜厚に形成される。また、塗布
液自体が接着性を有する場合には接着剤は不用であり、
また塗布液中に後述する接着剤を上述したバリア性を損
なわない程度に混入し、珪素酸化物層自体に接着性を付
与することができる。As a coating method, a resin melt in which silicon oxide fine particles, for example, SiO 2 particles are dispersed in a resin, for example, a phenol-novolak resin, or SiO 2 particles,
2 Apply the metal alkoxide solution for coating directly by roll coating, spray coating, etc.
It is formed to a film thickness after drying of {3000}. In addition, when the coating liquid itself has adhesiveness, the adhesive is unnecessary,
In addition, an adhesive described later can be mixed into the coating liquid to such an extent that the above-described barrier property is not impaired, so that the silicon oxide layer itself can be provided with adhesiveness.
【００３０】次に、層間の積層にあたって接着剤を使用
する場合について説明する。接着剤は、特に、ホログラ
ム層の接着に使用される場合、可塑剤を含有しないこと
が必要である。また、接着剤層は、通常、膜厚は０．１
μｍ〜１０μｍとされ、その光学特性としては、４００
〜７８０ｎｍの可視光透過率が９０％以上で、曇り度が
１％以下のものが好ましい。なお、ホログラム層、珪素
酸化物層がそれ自体で接着性を有する場合には、接着剤
層を省略することができる。Next, a case where an adhesive is used for lamination between layers will be described. The adhesive must not contain a plasticizer, especially when used for bonding the hologram layer. The adhesive layer usually has a thickness of 0.1.
μm to 10 μm, and the optical characteristics are 400 μm.
Those having a visible light transmittance of 90% or more and a haze of 1% or less are preferable. When the hologram layer and the silicon oxide layer have adhesiveness by themselves, the adhesive layer can be omitted.
【００３１】接着剤としては、天然ゴム系、再生ゴム
系、クロロプレンゴム系、ニトリルゴム系、スチレン・
ブタジエンゴム系、熱可塑性エラストマー系等のエラス
トマー系接着剤、また、エポキシ樹脂系、ポリウレタン
系等の合成樹脂系接着剤、反応型アクリル系、シアノア
クリレート系等の化学反応型接着剤、その他、ＵＶ硬化
型接着剤、ＥＢ硬化型接着剤、更に、エチレン・酢酸ビ
ニル共重合樹脂系ホットメルト系、ポリアミド系、ポリ
エステル系、熱可塑性エラストマー系、反応ホットメル
ト系等のホットメルト系接着剤、また、水性接着剤であ
る水溶性接着剤、エマルジョン系接着剤、ラテックス系
接着剤、更に無機系接着剤等が挙げられる。また、その
接着方法としては、熱可塑系のものは積層物間に挟んで
軟化点以上の温度に加熱すればよく、ＵＶ、ＥＢ硬化型
のものは積層物間に挟んで紫外線照射、電子線照射して
硬化させるとよく、粘着型のものは単に積層物間に挟ん
で硬化させるとよい。As the adhesive, natural rubber, recycled rubber, chloroprene rubber, nitrile rubber, styrene
Elastomer adhesives such as butadiene rubber and thermoplastic elastomers, synthetic resin adhesives such as epoxy resin and polyurethane, chemical acrylic adhesives such as reactive acrylic and cyanoacrylate, and other UV Curable adhesives, EB-curable adhesives, hot-melt adhesives such as ethylene-vinyl acetate copolymer resin-based hot melt-based, polyamide-based, polyester-based, thermoplastic elastomer-based, and reaction hot-melt-based adhesives, Examples of the aqueous adhesive include a water-soluble adhesive, an emulsion adhesive, a latex adhesive, and an inorganic adhesive. As for the bonding method, a thermoplastic resin may be sandwiched between laminates and heated to a temperature equal to or higher than its softening point. It is preferable to cure by irradiating, and it is better to cure the adhesive type simply by sandwiching it between laminates.
【００３２】第１の積層体の作製方法としては、例え
ば、ホログラムを記録済か又は未記録の記録材料フイル
ムの両面に接着剤を塗布した後、その一方の面にカバー
フィルムを剥離可能に積層する一方、他方の面に珪素酸
化物層を積層し、更にその層上に接着層を設けた後、カ
バーフィルムを剥離可能に積層して作製される。The first laminate may be produced, for example, by applying an adhesive to both sides of a recording material film on which a hologram has been recorded or not, and then laminating a cover film on one of the surfaces so that the cover film can be peeled off. On the other hand, a silicon oxide layer is laminated on the other surface, an adhesive layer is further provided on the layer, and a cover film is laminated so as to be peelable.
【００３３】次に、本発明における第２の積層体は、図
２に示すように、第１の積層体における珪素酸化物層上
に、上述した接着層を介して可塑剤を含む合成樹脂膜５
を積層し、更にその膜上にカバーフィルム１を積層した
構造を有する。なお、図では可塑剤を含む合成樹脂膜を
珪素酸化物層と同一の積層面積で図示しているが、例え
ばホログラム層を合わせガラスにおける一部に封入する
ような場合には、可塑剤を含む合成樹脂膜の積層面積を
珪素酸化物層、ホログラム層の積層面積より十分な大き
さとしておくとよい。また、可塑剤を含む合成樹脂膜に
カバーフィルムを積層するには、上述した接着剤を使用
して剥離可能に積層してもよいが、単に物理的に積層し
てよい。可塑剤を含む合成樹脂膜は、ポリビニルブチラ
ール膜が好ましく、膜厚１００μｍ〜２０００μｍ、好
ましくは５００μｍ〜１０００μｍのものである。Next, as shown in FIG. 2, the second laminate of the present invention comprises a synthetic resin film containing a plasticizer via the above-mentioned adhesive layer on the silicon oxide layer of the first laminate. 5
Are laminated, and the cover film 1 is further laminated on the film. In the drawings, the synthetic resin film containing a plasticizer is shown with the same lamination area as the silicon oxide layer. However, for example, when the hologram layer is encapsulated in a part of the laminated glass, the synthetic resin film contains the plasticizer. It is preferable that the lamination area of the synthetic resin film is sufficiently larger than the lamination area of the silicon oxide layer and the hologram layer. Further, in order to laminate the cover film on the synthetic resin film containing the plasticizer, the cover film may be laminated so as to be releasable using the above-mentioned adhesive, but may be simply physically laminated. The synthetic resin film containing a plasticizer is preferably a polyvinyl butyral film, and has a thickness of 100 μm to 2000 μm, preferably 500 μm to 1000 μm.
【００３４】作製方法としては、例えば、ホログラムを
記録済か又は未記録の記録材料フイルムの両面に接着剤
を塗布した後、その一方の面にカバーフィルムを剥離可
能に積層する一方、他方の面に珪素酸化物層を積層し、
更にその層上に接着層を設けた後、ポリビニルブチラー
ル膜、更にカバーフィルムを剥離可能に積層して形成さ
れる。各層の形成方法、膜厚等はポリビニルブチラール
膜以外は第１の積層体と同様である。As a manufacturing method, for example, an adhesive is applied to both surfaces of a recording material film on which a hologram is recorded or unrecorded, and a cover film is laminated on one of the surfaces so that the cover film can be peeled off, and the other surface is laminated. A silicon oxide layer on the
Furthermore, after providing an adhesive layer on the layer, a polyvinyl butyral film and a cover film are further laminated so as to be peelable. Except for the polyvinyl butyral film, the method of forming each layer, the film thickness, and the like are the same as those of the first laminate.
【００３５】本発明の第２のホログラム層封入合わせガ
ラスの製造に使用される第３〜第４の積層体について説
明する。第３の積層体は、図３に示すように、第１の積
層体におけるホログラム層の両面に珪素酸化物層３を有
するものである。作製方法としては、例えばホログラム
を記録済か又は未記録の記録材料フイルムの両面に接着
剤を塗布した後、その一方の面にカバーフィルムを剥離
可能に積層する一方、他方の面に珪素酸化物層を積層
し、更にその層上に接着層を設けた後、カバーフィルム
を剥離可能に積層し、次いで他方の面のカバーフィルム
を剥離し、その接着剤層上に上記と同様にして珪素酸化
物層、接着層、カバーフィルムを積層して形成される。
各層の形成方法、膜厚等は第１の積層体と同様である。The third and fourth laminates used for producing the second hologram layer-sealed laminated glass of the present invention will be described. As shown in FIG. 3, the third laminate has a silicon oxide layer 3 on both surfaces of the hologram layer in the first laminate. As a manufacturing method, for example, after applying an adhesive to both sides of a recording material film on which a hologram is recorded or unrecorded, a cover film is releasably laminated on one surface thereof, and a silicon oxide film is formed on the other surface. After laminating the layers and further providing an adhesive layer on the layer, the cover film is laminated so that it can be peeled off, and then the cover film on the other surface is peeled off. It is formed by laminating a material layer, an adhesive layer, and a cover film.
The method of forming each layer, the film thickness, and the like are the same as those of the first laminate.
【００３６】また、第４の積層体は、図４に示すよう
に、第３の積層体におけるそれぞれの珪素酸化物層とカ
バーフィルム１との間にそれぞれ可塑剤を含む合成樹脂
膜５を積層した構造を有するものである。なお、図では
可塑剤を含む合成樹脂膜を珪素酸化物層と同一の積層面
積で図示しているが、例えばホログラム層を合わせガラ
スにおける一部に封入するような場合には可塑剤を含む
合成樹脂膜の積層面積を珪素酸化物層、ホログラム層の
積層面積より十分な大きさとしておくとよい。As shown in FIG. 4, the fourth laminate has a synthetic resin film 5 containing a plasticizer laminated between each silicon oxide layer and the cover film 1 in the third laminate. It has the following structure. Although the figure shows the synthetic resin film containing a plasticizer with the same lamination area as the silicon oxide layer, the synthetic resin film containing the plasticizer is used, for example, when the hologram layer is encapsulated in a part of the laminated glass. The lamination area of the resin film is preferably larger than the lamination area of the silicon oxide layer and the hologram layer.
【００３７】作製方法としては、例えばホログラムを記
録済か又は未記録の記録材料フイルムの両面に接着剤を
塗布した後、その一方の面にカバーフィルムを剥離可能
に積層する一方、他方の面に珪素酸化物層を積層し、更
にその層上に接着層を設けた後、ポリビニルブチラール
膜、更にカバーフィルムを積層する。ついで、他方のカ
バーフィルムを剥離した後、上記同様に珪素酸化物層を
積層し、更にその層上に接着層を設けた後、ポリビニル
ブチラール膜、更にカバーフィルムを積層して作製され
る。各層の形成方法、膜厚等は第２の積層体と同様であ
る。As a manufacturing method, for example, an adhesive is applied to both sides of a recording material film on which a hologram is recorded or unrecorded, and a cover film is laminated on one of the surfaces so as to be peelable, and the other is coated on the other surface. After stacking a silicon oxide layer and further providing an adhesive layer on the silicon oxide layer, a polyvinyl butyral film and a cover film are further stacked. Then, after the other cover film is peeled off, a silicon oxide layer is laminated in the same manner as described above, an adhesive layer is further provided thereon, and then a polyvinyl butyral film and a cover film are further laminated. The method of forming each layer, the film thickness, and the like are the same as those of the second laminate.
【００３８】次に、上述した第１〜第４の積層体の他の
実施態様について、図５により説明する。図５（ａ）に
その断面、同図（ｂ）によりその平面を示すように、第
１の積層体におけるホログラム層３の積層面積を、珪素
酸化物層４の積層面積より小さく形成するものである。
なお、同図（ｂ）における３はホログラム層の積層位置
を示す。珪素酸化物層４とホログラム層３との積層面積
の関係は、図６（ｂ）に示すように、カバーフィルム１
を剥離して合わせガラス中に封入された時、珪素酸化物
層４の積層面積を、ホログラム層３の表面全周にわたっ
てホログラム層を被覆可能なものとするものである。Next, another embodiment of the above-described first to fourth laminates will be described with reference to FIG. The lamination area of the hologram layer 3 in the first laminate is formed to be smaller than the lamination area of the silicon oxide layer 4 as shown in the cross section in FIG. 5A and the plane in FIG. is there.
In addition, 3 in the same figure (b) shows the lamination position of the hologram layer. As shown in FIG. 6B, the relationship between the lamination areas of the silicon oxide layer 4 and the hologram layer 3 is as follows.
When the film is peeled off and sealed in a laminated glass, the lamination area of the silicon oxide layer 4 is such that the hologram layer can be covered over the entire surface of the hologram layer 3.
【００３９】この積層体を使用すると、ホログラム層３
がその端部も含めて珪素酸化物層５により被覆されるの
で、可塑剤を含む合成樹脂膜からの可塑剤の浸透を防止
することができ、第１〜第４の積層体において必要とし
たホログラム層３の周辺部に設けられる未記録部を不要
とできる。一般に、ホログラム周辺部に未記録部が存在
すると、白化現象（ヘイズ）、黄変現象（イエローネ
ス）が生じ、合わせガラスとした時にホログラム部、未
記録部、ガラス部の３重構成となり、好ましくない問題
が生じるが、この積層体においては未記録部を残す必要
がないので、例えば自動車等のフロントガラス中に封入
されるものとして、ノイズのないものとできる。また、
積層体として保存する場合においても、積層体を脱気
し、珪素酸化物層によりホログラム層の全表面を被覆し
ておくことにより、湿気や空気を遮断し、ホログラム層
を安定した状態で保存することができる。When this laminate is used, the hologram layer 3
Is covered with the silicon oxide layer 5 including its ends, so that penetration of the plasticizer from the synthetic resin film containing the plasticizer can be prevented, which is required in the first to fourth laminates. Unrecorded portions provided around the hologram layer 3 can be made unnecessary. In general, when an unrecorded portion exists around the hologram, a whitening phenomenon (haze) and a yellowing phenomenon (yellowness) occur, and when a laminated glass is formed, the hologram portion, the unrecorded portion, and the glass portion have a triple structure, which is preferable. However, there is no need to leave an unrecorded portion in this laminate, so that the laminate can be sealed in a windshield of an automobile or the like, for example, and can be free of noise. Also,
Even in the case of storing as a laminate, the laminate is degassed, and the entire surface of the hologram layer is covered with a silicon oxide layer, so that moisture and air are shut off and the hologram layer is stored in a stable state. be able to.
【００４０】この積層体の作製方法を説明する。まず、
カバーフィルムの表面に接着剤を塗布した後、ホログラ
ム記録材料層を積層し、ホログラム記録されたか或いは
ホログラム記録予定部を、上述した積層面積となるよう
にカバーフィルム１を残してハーフカットし、それ以外
の部分を剥離除去することにより、まず積層面積の小さ
なホログラム層を積層した積層体（Ａ）を得る。ハーフ
カットは、鋭利な刃を使用するとよく、公知の切断装置
により行なってもよい。一方、これとは別に、表面が剥
離処理されたカバーフィルム面に接着剤を塗布した後、
上述のホログラム層の積層面積より広い珪素酸化物層を
積層し、次いで、その層上に接着剤を塗布して積層体
（Ｂ）を得る。次いで、得られた積層体（Ｂ）の珪素酸
化物層上に、上記で作製した積層体（Ａ）をそのホログ
ラム層側から図５（ｂ）に示す積層位置で積層すること
により、図５に示す積層体を作製することができる。な
お、図５に示す積層体は第１の積層体に対応するもので
あるが、第２〜第４の積層体においても、それぞれのホ
ログラム層の積層面積と珪素酸化物層の積層面積との関
係を上記同様の関係に設定することにより、図５に対応
した同様の積層体とすることができる。A method for producing this laminate will be described. First,
After applying an adhesive to the surface of the cover film, the hologram recording material layer is laminated, and the hologram recorded or the hologram recording scheduled portion is half-cut while leaving the cover film 1 so as to have the above-described laminated area. First, a laminate (A) in which hologram layers having a small lamination area are laminated is obtained by peeling and removing portions other than the above. The half cut may use a sharp blade, and may be performed by a known cutting device. On the other hand, separately, after applying an adhesive to the cover film surface whose surface has been peeled,
A silicon oxide layer having a larger area than the above-mentioned hologram layer is laminated, and then an adhesive is applied on the layer to obtain a laminate (B). Next, on the silicon oxide layer of the obtained laminate (B), the laminate (A) produced above is laminated from the hologram layer side at the lamination position shown in FIG. Can be produced. Although the laminate shown in FIG. 5 corresponds to the first laminate, also in the second to fourth laminates, the stack area of each hologram layer and the stack area of the silicon oxide layer are different. By setting the relationship to the same relationship as described above, a similar laminate corresponding to FIG. 5 can be obtained.
【００４１】次に、各積層体を使用した合わせガラスの
作製方法について説明する。図６（ａ）は、本発明の第
１のホログラム層封入合わせガラスをその断面により、
また同図（ｂ）はその平面により説明するための図であ
り、図中、５は可塑剤を含む合成樹脂膜、１０はガラ
ス、１１は合わせガラスを自動車用とする場合の車外方
向を示し、又、図１、図５と同一符号は同一内容を示
す。なお、図６においては、可塑剤を含む合成樹脂膜５
の積層面積が、ホログラム層３、珪素酸化物層４の積層
面積より広い場合を示している。Next, a method of manufacturing a laminated glass using each laminated body will be described. FIG. 6A is a cross-sectional view of the first hologram layer-enclosed laminated glass of the present invention.
FIG. 2B is a view for explaining the plane, in which 5 is a synthetic resin film containing a plasticizer, 10 is glass, and 11 is an exterior direction when a laminated glass is used for an automobile. 1 and FIG. 5 indicate the same contents. In FIG. 6, the synthetic resin film 5 containing a plasticizer is used.
Is larger than the hologram layer 3 and the silicon oxide layer 4.
【００４２】図６（ａ）に示す合わせガラスを作製する
には、第１の積層体におけるカバーフィルムの一方、ま
たは両方を剥離して、一方のガラス１０上にホログラム
層３側から接着した後、可塑剤を含む合成樹脂膜５、他
方のガラス１０を順次重ね、オートクレーブ中で１３０
℃〜１５０℃、圧力１Ｋｇ／ｃｍ2 以上、３０〜６０分
間の条件で積層するとよい。In order to produce the laminated glass shown in FIG. 6A, one or both of the cover films in the first laminate are peeled off and bonded to one glass 10 from the hologram layer 3 side. , A synthetic resin film 5 containing a plasticizer, and the other glass 10 in order, and
It is preferable that the layers are laminated under the conditions of a temperature of 150 to 150 ° C., a pressure of 1 kg / cm 2 or more and a period of 30 to 60 minutes.
【００４３】また、図５に示す積層体を使用して作製し
た合わせガラスについて、図６（ｂ）に示す。図５に示
す積層体を使用する場合も第１の積層体同様にして合わ
せガラスの製造に使用されるが、合わせガラス作製時の
加圧加熱操作により、珪素酸化物層４によりホログラム
層３はその表面が全周にわたり被覆される。FIG. 6B shows a laminated glass manufactured using the laminate shown in FIG. When the laminated body shown in FIG. 5 is used, the hologram layer 3 is used by the silicon oxide layer 4 due to the silicon oxide layer 4 due to the pressure and heating operation at the time of producing the laminated glass, similarly to the first laminated body. The surface is covered all around.
【００４４】次に、第２の積層体の場合には、カバーフ
ィルムの一方、または両方を剥離して、一方のガラス１
０上にホログラム層３側から接着した後、他方のガラス
１０を順次重ね、上記と同様にして合わせガラスとされ
るが、その積層構造中に可塑剤を含む合成樹脂膜５を有
しているので、第１のホログラム層封入合わせガラスを
より効率的に作製できる。Next, in the case of the second laminate, one or both of the cover films are peeled off, and one of the glass sheets 1 is removed.
After adhering onto the hologram layer 3 from the side of the hologram layer 3, the other glass 10 is successively layered to form a laminated glass in the same manner as described above, but has a synthetic resin film 5 containing a plasticizer in its laminated structure. Therefore, the first hologram layer-enclosed laminated glass can be produced more efficiently.
【００４５】次に、第３〜第４の積層体を使用すること
により、本発明の第２のホログラム層封入合わせガラス
を容易に作製することができる。まず、第３の積層体
は、ホログラム層３の両面に珪素酸化物層４を積層して
いるので、可塑剤を含む合成樹脂膜と共に使用され、本
発明の第２のホログラム層封入合わせガラスとされる。Next, by using the third and fourth laminates, the second hologram layer-sealed laminated glass of the present invention can be easily produced. First, since the third laminate has the silicon oxide layer 4 laminated on both sides of the hologram layer 3, it is used together with a synthetic resin film containing a plasticizer, and the second hologram layer-sealed laminated glass of the present invention Is done.
【００４６】更に、第４の積層体の場合には、第３の積
層体中に可塑剤を含む合成樹脂膜５を有しているので、
第２のホログラム層封入合わせガラスをより効率的に作
製できる。Further, in the case of the fourth laminate, since the third laminate has the synthetic resin film 5 containing a plasticizer,
The second hologram layer-sealed laminated glass can be more efficiently produced.
【００４７】上述した第１〜第４の積層体及び図５に示
す積層体は、いずれも両カバーフィルム間にホログラム
層と珪素酸化物層等をワンセットで積層しているので、
可塑剤を含む合成樹脂膜を有する合わせガラス中にホロ
グラムを封入する際、位置決め等の必要がなく、簡便に
貼着させることができる。In each of the above-described first to fourth laminates and the laminate shown in FIG. 5, a hologram layer and a silicon oxide layer are laminated in one set between both cover films.
When enclosing the hologram in a laminated glass having a synthetic resin film containing a plasticizer, there is no need for positioning or the like, and the hologram can be easily attached.
【００４８】なお、第１、第３の積層体及び図５に示す
積層体を合わせガラス中ではなく、ガラス板上に一方の
カバーフィルムを剥離して貼着して使用することもでき
る。この場合には、これらの積層体における一方のカバ
ーフィルムを剥離不能に接着すると共に、ガラス板に貼
着すべき側のカバーフィルムを剥離可能に接着しておく
とよく、通常の合わせガラスの車内側に貼着され、合わ
せガラス同様の用途に使用できる。The first and third laminates and the laminate shown in FIG. 5 can be used by peeling one of the cover films on a glass plate instead of in the laminated glass. In this case, it is preferable that one of the cover films in these laminates is adhered in a non-peelable manner, and the cover film on the side to be attached to the glass plate is detachably adhered. It is stuck on the inside and can be used for applications similar to laminated glass.
【００４９】[0049]
【作用及び発明の効果】本発明における積層体または合
わせガラスにおいて、ホログラム層を珪素酸化物層によ
り保護することにより、透明性に優れ、また可塑剤のホ
ログラム層への浸透を防止できると共に、合わせガラス
作製時の加熱程度ではその熱収縮性は殆どないものであ
り、従来の可塑剤バリア層に比してホログラム特性に影
響を与えることがないものである。In the laminated body or laminated glass according to the present invention, the hologram layer is protected by a silicon oxide layer, whereby the transparency is excellent, and the penetration of the plasticizer into the hologram layer can be prevented. The heat shrinkage is almost non-existent when heated at the time of glass production, and the hologram characteristics are not affected as compared with the conventional plasticizer barrier layer.
【００５０】また、積層体として、図５に示す積層構造
とすると、可塑剤を含む合成樹脂膜からの可塑剤の浸透
をその端部においても防止することができ、また、ホロ
グラム層の周辺部に設けられる未記録部を不要とでき、
例えば自動車等のフロントガラス中に封入される場合
に、ホログラム周辺でのノイズのないものとできる。ま
た、積層体として保存する場合においても、珪素酸化物
層によりホログラム層の端部も含めて被覆するものとし
ておくことができ、ホログラム層を湿気や空気から遮断
することができ、ホログラム特性に影響を与えることな
く保存することができる。When the laminated body has the laminated structure shown in FIG. 5, the penetration of the plasticizer from the synthetic resin film containing the plasticizer can be prevented even at the end thereof, and the periphery of the hologram layer can be prevented. The unrecorded part provided in the
For example, when enclosed in a windshield of an automobile or the like, noise around the hologram can be eliminated. In addition, even when the hologram layer is stored as a laminate, the hologram layer can be covered with the silicon oxide layer, including the ends thereof, and the hologram layer can be shielded from moisture and air, which affects the hologram characteristics. Can be saved without giving.
【００５１】また、本発明における積層体は、いずれも
両カバーフィルム間にホログラム層と珪素酸化物層等を
ワンセットで積層しているので、可塑剤を含む合成樹脂
膜を有する合わせガラス中にホログラムを封入する際、
位置決め等の必要がなく、簡便に貼着させることができ
る。以下、本発明を実施例により説明するが、本発明
は、これにより限定はされない。Further, in the laminate of the present invention, the hologram layer and the silicon oxide layer are laminated in one set between both cover films, so that the laminated glass having a synthetic resin film containing a plasticizer can be used. When enclosing a hologram,
There is no need for positioning or the like, and it can be simply attached. Hereinafter, the present invention will be described with reference to examples, but the present invention is not limited thereto.
【００５２】[0052]
【実施例１】周辺２０ｍｍに未記録部が残るようにホロ
グラム記録したホログラフィック記録フイルム（デュポ
ン社製、商標名「Omnidex 352 」膜厚２０μｍ）の両面
に、光学接着剤Ｎｏ．６１（ノーランドプロダクツ社
製）をロールコートし、乾燥後膜厚１μｍの接着剤層を
それぞれ設けた後、一方の面にカバーフィルムとしてポ
リエチレンテレフタレートフイルム（米国デュポン社
製、商品名Ｍｙｌａｒ９０Ｄ、膜厚２５μｍ）をラミネ
ートした。Example 1 Optical adhesive No. 1 was applied to both sides of a holographic recording film (trade name "Omnidex 352", manufactured by DuPont, having a film thickness of 20 μm) in which a hologram was recorded such that an unrecorded portion was left around 20 mm. 61 (manufactured by Norland Products Co., Ltd.), and after drying, an adhesive layer having a film thickness of 1 μm was provided. Then, a polyethylene terephthalate film (manufactured by DuPont USA, product name: Mylar 90D, film thickness: 25 μm) was provided as a cover film on one surface. ) Was laminated.
【００５３】次いで、このホログラム記録フイルムをフ
イルム用高周波誘導加熱方式の真空蒸着装置にセット
し、カバーフィルムをラミネートしていない接着剤層面
に、ＳｉＯを蒸着源とし、１０-4 Torr の真空下で珪素
酸化物層を膜厚５０００Åで積層し、珪素酸化物層を設
けた。次いで、その珪素酸化物層上に、光学接着剤Ｎ
ｏ．６１（ノーランドプロダクツ社製）を乾燥膜厚１μ
ｍで塗布した後、上記と同じその表面を剥離処理したカ
バーフィルムを貼着し、本発明の第１の積層体を得た。Next, this hologram recording film was set in a high-frequency induction heating type vacuum evaporation apparatus for film, and the surface of the adhesive layer on which the cover film was not laminated was formed using SiO as an evaporation source under a vacuum of 10 -4 Torr. A silicon oxide layer was laminated at a thickness of 5000 ° to provide a silicon oxide layer. Then, on the silicon oxide layer, an optical adhesive N
o. 61 (manufactured by Norland Products) with a dry film thickness of 1μ
After coating with m, a cover film having the same surface as that described above, which had been subjected to release treatment, was adhered to obtain a first laminate of the present invention.
【００５４】この第１の積層体におけるホログラム層上
のカバーフィルムを剥離した後、２ｍｍ厚のクリアガラ
ス板上に積層し、次いで、珪素酸化物層上のカバーフィ
ルムを剥離した後、７５０μｍ厚のポリビニルブチラー
ルフイルムをその上に積層し、更に２ｍｍ厚のクリアガ
ラス板を載置した。この積層物を、オートクレーブ中に
入れ、１３０℃、５Ｋｇ／ｃｍ2 圧で加熱圧着し、本発
明の第１のホログラム層封入合わせガラスを作製した。After the cover film on the hologram layer in the first laminate was peeled off, it was laminated on a clear glass plate having a thickness of 2 mm, and then the cover film on the silicon oxide layer was peeled off. A polyvinyl butyral film was laminated thereon, and a clear glass plate having a thickness of 2 mm was placed thereon. The laminate was placed in an autoclave and heated and pressed at 130 ° C. and a pressure of 5 kg / cm 2 to produce a first hologram layer-sealed laminated glass of the present invention.
【００５５】これにより、効率よく合わせガラスを作製
でき、また、得られた合わせガラスは、ホログラムの経
時変化のない良好な合わせガラスとなしえた。As a result, a laminated glass could be produced efficiently, and the obtained laminated glass was a good laminated glass having no change in the hologram with time.
【００５６】[0056]
【実施例２】実施例１の第１の積層体の作製における、
蒸着法による珪素酸化物層に代えて、接着剤層上に、組
成 ・メタノールシリカゾル（日産化学工業（株）製） ・・・・２重量部 ・フェノールノボラック樹脂 ・・・・１重量部 からなる二酸化珪素微粒子分散液を、ロールコート法
で、乾燥後膜厚２μｍとなるように塗布して珪素酸化物
層を形成した以外は、実施例１と同様にして本発明の第
１の積層体を作製した。Example 2 In the production of the first laminate of Example 1,
Instead of a silicon oxide layer formed by a vapor deposition method, a composition comprising methanol silica sol (manufactured by Nissan Chemical Industries, Ltd.) 2 parts by weight phenol novolak resin 1 part by weight on the adhesive layer A first laminate of the present invention was prepared in the same manner as in Example 1 except that a silicon dioxide fine particle dispersion was applied by a roll coating method so as to have a thickness of 2 μm after drying to form a silicon oxide layer. Produced.
【００５７】実施例１と同様にして合わせガラスを作製
したところ、同様の合わせガラスが得られた。When a laminated glass was produced in the same manner as in Example 1, a similar laminated glass was obtained.
【００５８】[0058]
【実施例３】実施例１の第１の積層体の作製における、
蒸着法による珪素酸化物層に代えて、接着剤層上に、組
成 ・Ｓｉ（ＯＣ2 Ｈ5 ）4 ・・・ ２５ 重量部 ・エタノール ・・・ ３７．６重量部 ・水 ・・・ ２３．５重量部 ・塩酸 ・・・ ０．３重量部 からなる二酸化珪素コーティング用金属アルコキシド溶
液を、ロールコート法で、乾燥後膜厚５０００Åとなる
ように塗布して珪素酸化物層を形成した以外は、実施例
１と同様にして本発明の第１の積層体を作製した。Embodiment 3 In the production of the first laminate of Embodiment 1,
Instead of the silicon oxide layer by vapor deposition, on the adhesive layer, the composition · Si (OC 2 H 5) 4 ··· 25 parts by weight of ethanol.. 37.6 parts • water 23. 5 parts by weight ・ Hydrochloric acid ・ ・ ・ except that a silicon oxide layer was formed by applying a metal alkoxide solution for silicon dioxide coating consisting of 0.3 parts by weight to a film thickness of 5,000 mm after drying by a roll coating method. In the same manner as in Example 1, a first laminate of the present invention was produced.
【００５９】実施例１と同様にして合わせガラスを作製
したところ、同様の合わせガラスが得られた。When a laminated glass was produced in the same manner as in Example 1, a similar laminated glass was obtained.
【００６０】[0060]
【実施例４】実施例１の第１の積層体の作製において、
ホログラム両面に接着剤を塗布しないで、直接、組成 ・メタノールシリカゾル（日産化学工業（株）製） ・・ ２重量部 ・フェノールノボラック樹脂 ・・０．５重量部 ・光学接着剤Ｎｏ．６１（ノーランドプロダクツ社製）・０．５重量部 からなる二酸化珪素微粒子分散液を、ロールコート法
で、乾燥後膜厚２μｍとなるように塗布して珪素酸化物
層を形成し、カバーフィルムを積層した以外、実施例１
と同様にして本発明の第１の積層体を作製した。Embodiment 4 In the fabrication of the first laminate of Embodiment 1,
The composition was directly applied without applying an adhesive to both sides of the hologram. ・ Methanol silica sol (manufactured by Nissan Chemical Industries, Ltd.) ・ 2 parts by weight ・ Phenol novolak resin ・ ・ 0.5 parts by weight ・ Optical adhesive No. 61 (manufactured by Norland Products) and 0.5 parts by weight of a silicon dioxide fine particle dispersion were applied by a roll coating method to a thickness of 2 μm after drying to form a silicon oxide layer, and a cover film was formed. Example 1 except for lamination
In the same manner as in the above, a first laminate of the present invention was produced.
【００６１】実施例１と同様にして合わせガラスを作製
したところ、同様の合わせガラスが得られた。When a laminated glass was produced in the same manner as in Example 1, a similar laminated glass was obtained.
【００６２】[0062]
【実施例５】実施例１における第１の積層体の作製時に
おいて、珪素酸化物層上に実施例１同様に接着剤層を設
けた後、７５０μｍ厚のポリビニルブチラールフイルム
を積層し、次いでカバーフィルムを積層して、本発明の
第２の積層体を作製した。Embodiment 5 At the time of manufacturing the first laminate in Embodiment 1, after providing an adhesive layer on the silicon oxide layer in the same manner as in Embodiment 1, a 750 μm-thick polyvinyl butyral film is laminated, and then the cover is formed. The films were laminated to produce a second laminate of the present invention.
【００６３】この積層体におけるホログラム層側のカバ
ーフィルムを剥離した後、２ｍｍ厚のクリアガラス板上
に積層し、次いで、ポリビニルブチラール層上のカバー
フィルムを剥離した後、２ｍｍ厚のクリアガラス板を載
置した。この積層物を、オートクレーブ中に入れ、１３
０℃、５Ｋｇ／ｃｍ2 圧で加熱圧着し、本発明の第１の
ホログラム層封入合わせガラスを作製した。After the cover film on the hologram layer side of this laminate was peeled off, it was laminated on a clear glass plate having a thickness of 2 mm. Then, after the cover film on the polyvinyl butyral layer was peeled off, the clear glass plate having a thickness of 2 mm was peeled off. Placed. This laminate is placed in an autoclave and
It was heated and pressed at 0 ° C. and a pressure of 5 kg / cm 2 to produce a first hologram layer-sealed laminated glass of the present invention.
【００６４】これにより、より効率よく合わせガラスを
作製でき、また、得られた合わせガラスは、ホログラム
の経時変化のない良好な合わせガラスとなしえた。As a result, a laminated glass could be produced more efficiently, and the obtained laminated glass could be a good laminated glass having no change in the hologram with time.
【００６５】[0065]
【実施例６】全面にホログラム記録したホログラフィッ
ク記録フイルム（２００ｍｍ×２００ｍｍ、デュポン社
製、商標名「Omnidex 352 」膜厚２０μｍ）の両面に、
光学接着剤Ｎｏ．６１（ノーランドプロダクツ社製）を
ロールコートし、乾燥後膜厚１μｍの接着剤層をそれぞ
れ設けた後、一方の面に、巾３００ｍｍの、ポリエチレ
ンテレフタレートフイルム（米国デュポン社製、商品名
Ｍｙｌａｒ９０Ｄ、膜厚２５μｍ）をラミネートした。Embodiment 6 A holographic recording film (200 mm × 200 mm, manufactured by DuPont, trade name “Omnidex 352”, film thickness: 20 μm) having a hologram recorded on the entire surface is provided on both surfaces.
Optical adhesive No. 61 (manufactured by Norland Products Co., Ltd.), and after drying, an adhesive layer having a film thickness of 1 μm was provided. On one side, a 300 mm wide polyethylene terephthalate film (manufactured by DuPont, product name: Mylar 90D, film) (Thickness: 25 μm) was laminated.
【００６６】次いで、このホログラム記録フイルムをフ
イルム用高周波誘導加熱方式の真空蒸着装置にセット
し、カバーフィルムをラミネートしていない接着剤層面
に、ＳｉＯを蒸着源とし、１０-4 Torr の真空下で、２
２０ｍｍ×２２０ｍｍの積層範囲で、図５（ａ）（ｂ）
に示す積層範囲となるように膜厚５０００Åに積層し、
珪素酸化物層を設けた。次いで、その珪素酸化物層上
に、光学接着剤Ｎｏ．６１（ノーランドプロダクツ社
製）を乾燥膜厚１μｍで塗布した後、上記と同じその表
面を剥離処理したカバーフィルムを貼着し、図５に示す
本発明の積層体を得た。Next, this hologram recording film was set in a high frequency induction heating type vacuum evaporation apparatus for film, and the surface of the adhesive layer on which the cover film was not laminated was formed using SiO as an evaporation source under a vacuum of 10 -4 Torr. , 2
5 (a) and 5 (b) in a stacking range of 20 mm × 220 mm.
Is laminated to a film thickness of 5000 mm so as to have a lamination range shown in
A silicon oxide layer was provided. Next, on the silicon oxide layer, an optical adhesive No. After applying 61 (manufactured by Norland Products) at a dry film thickness of 1 μm, a cover film having the same surface as that described above and having been subjected to a release treatment was adhered to obtain a laminate of the present invention shown in FIG.
【００６７】この積層体におけるホログラム層上のカバ
ーフィルムを剥離した後、２ｍｍ厚のクリアガラス板上
に積層し、次いで、珪素酸化物層上のカバーフィルムを
剥離した後、７５０μｍ厚のポリビニルブチラールフイ
ルムをその上に積層し、更に２ｍｍ厚のクリアガラス板
を載置した。この積層物を、オートクレーブ中に入れ、
１３０℃、５Ｋｇ／ｃｍ2 圧で加熱圧着し、図６（ｂ）
に示すホログラム層封入合わせガラスを作製した。After the cover film on the hologram layer in this laminate was peeled off, it was laminated on a clear glass plate having a thickness of 2 mm, then the cover film on the silicon oxide layer was peeled off, and then a polyvinyl butyral film having a thickness of 750 μm was peeled off. Was laminated thereon, and a clear glass plate having a thickness of 2 mm was further placed thereon. Put this laminate in an autoclave,
FIG. 6 (b) is obtained by thermocompression bonding at 130 ° C. and 5 kg / cm 2 pressure.
The hologram layer-sealed laminated glass shown in (1) was produced.
【００６８】これにより、効率よく合わせガラスを作製
でき、また、ホログラムの経時変化のない良好な合わせ
ガラスとなしえると共に、実施例１で得られた合わせガ
ラスと比較してホログラム未記録層によるヘイズ、イエ
ローネス等のノイズのないものとできた。As a result, a laminated glass can be efficiently produced, a good laminated glass without aging of the hologram can be obtained, and the haze due to the hologram unrecorded layer is smaller than that of the laminated glass obtained in Example 1. And no noise such as yellowness.
【００６９】[0069]
【実施例７】実施例１で作製した第１の積層体における
ホログラム層側のカバーフィルムを剥離した後、フイル
ム用高周波誘導加熱方式の真空蒸着装置にセットし、そ
の接着剤層上に、ＳｉＯを蒸着源とし、１０-4 Torr の
真空下で珪素酸化物層を膜厚５０００Åで積層し、珪素
酸化物層を設けた。次いで、その珪素酸化物層上に、光
学接着剤Ｎｏ．６１（ノーランドプロダクツ社製）を乾
燥膜厚１μｍで塗布した後、上記と同じその表面を剥離
処理したカバーフィルムを貼着し、本発明の第３の積層
体を作製した。Example 7 After the cover film on the hologram layer side of the first laminate produced in Example 1 was peeled off, the film was set in a high-frequency induction heating type vacuum evaporation apparatus for film, and SiO 2 was adhered on the adhesive layer. Was used as an evaporation source, and a silicon oxide layer was laminated at a thickness of 5000 ° under a vacuum of 10 -4 Torr to provide a silicon oxide layer. Next, on the silicon oxide layer, an optical adhesive No. After applying 61 (manufactured by Norland Products) at a dry film thickness of 1 μm, a cover film having the same surface as that described above, whose surface was subjected to a release treatment, was adhered to produce a third laminate of the present invention.
【００７０】この積層体における一方のカバーフィルム
を剥離した後、７５０μｍ厚のポリビニルブチラールフ
イルムをその上に積層すると共に、他方のカバーフィル
ムを剥離した後、同様に７５０μｍ厚のポリビニルブチ
ラールフイルムを積層し、その積層体を２枚の２ｍｍ厚
のクリアガラス板間に挟持させた。この積層物を、オー
トクレーブ中に入れ、１３０℃、５Ｋｇ／ｃｍ2 圧で加
熱圧着し、本発明の第２のホログラム層封入合わせガラ
スを作製した。After peeling off one cover film in this laminate, a 750 μm thick polyvinyl butyral film was laminated thereon, and after peeling off the other cover film, a 750 μm thick polyvinyl butyral film was similarly laminated. The laminate was sandwiched between two 2 mm-thick clear glass plates. The laminate was placed in an autoclave and heated and pressed at 130 ° C. and a pressure of 5 kg / cm 2 to produce a second hologram layer-sealed laminated glass of the present invention.
【００７１】これにより、より効率よく合わせガラスを
作製でき、また、得られた合わせガラスは、ホログラム
の経時変化のない良好な合わせガラスとなしえた。As a result, a laminated glass could be produced more efficiently, and the obtained laminated glass was a good laminated glass having no hologram change with time.
【００７２】[0072]
【実施例８】実施例７で作製した第３の積層体の作製時
において、各珪素酸化物層上に実施例１同様に接着剤層
を設けた後、７５０μｍ厚のポリビニルブチラールフイ
ルムをそれぞれ積層し、次いで表裏両面にカバーフィル
ムを積層して、本発明の第４の積層体を作製した。[Embodiment 8] At the time of producing the third laminate produced in Embodiment 7, an adhesive layer was provided on each silicon oxide layer in the same manner as in Embodiment 1, and then a 750 μm thick polyvinyl butyral film was laminated. Then, a cover film was laminated on both the front and back surfaces to produce a fourth laminate of the present invention.
【００７３】この積層体における一方のカバーフィルム
を剥離した後、２ｍｍ厚のクリアガラス板上に積層し、
次いで、ポリビニルブチラール層上のカバーフィルムを
剥離した後、２ｍｍ厚のクリアガラス板を載置した。こ
の積層物を、オートクレーブ中に入れ、１３０℃、５Ｋ
ｇ／ｃｍ2 圧で加熱圧着し、本発明の第２のホログラム
層封入合わせガラスを作製した。After peeling off one cover film in the laminate, the laminate was laminated on a clear glass plate having a thickness of 2 mm,
Next, after the cover film on the polyvinyl butyral layer was peeled off, a clear glass plate having a thickness of 2 mm was placed. This laminate is placed in an autoclave, at 130 ° C., 5K
The resultant was heated and pressed at a pressure of g / cm 2 to produce a second hologram layer-sealed laminated glass of the present invention.
【００７４】これにより、より効率よく合わせガラスを
作製でき、また、得られた合わせガラスは、ホログラム
の経時変化のない良好な合わせガラスとなしえた。As a result, a laminated glass could be produced more efficiently, and the obtained laminated glass could be a good laminated glass having no change over time of the hologram.
【図１】 図１は、本発明の第１のホログラム封入合わ
せガラスを製造するために使用される第１の積層体を説
明するための図である。FIG. 1 is a diagram for explaining a first laminate used for manufacturing a first hologram-enclosed laminated glass of the present invention.
【図２】 図２は、本発明の第１のホログラム封入合わ
せガラスを製造するために使用される第２の積層体を説
明するための図である。FIG. 2 is a diagram for explaining a second laminate used to manufacture the first hologram-enclosed laminated glass of the present invention.
【図３】 図３は、本発明の第２のホログラム封入合わ
せガラスを製造するために使用される第３の積層体を説
明するための図である。FIG. 3 is a view for explaining a third laminate used for manufacturing the second hologram-enclosed laminated glass of the present invention.
【図４】 図４は、本発明の第２のホログラム封入合わ
せガラスを製造するために使用される第４の積層体を説
明するための図である。FIG. 4 is a view for explaining a fourth laminate used for manufacturing the second hologram-enclosed laminated glass of the present invention.
【図５】 図５は、本発明の第１の積層体の他の実施態
様を説明するための図であり、同図（ａ）はその断面に
より、同図（ｂ）はその平面により説明するための図で
ある。FIGS. 5A and 5B are diagrams for explaining another embodiment of the first laminate of the present invention, wherein FIG. 5A is a sectional view and FIG. 5B is a plan view. FIG.
【図６】 図６（ａ）は、本発明の第１のホログラム封
入合わせガラスをその断面により説明するための図であ
り、同図（ｂ）は第１の積層体の他の実施態様である図
５に示す積層体を使用して製造したホログラム層封入合
わせガラスをその断面により説明するための図である。FIG. 6 (a) is a view for explaining the first hologram-enclosed laminated glass of the present invention by its cross section, and FIG. 6 (b) is another embodiment of the first laminate. FIG. 6 is a view for explaining a hologram layer-enclosed laminated glass manufactured using the laminated body shown in FIG. 5 by using a cross section thereof.
【図７】 図７は、ホログラム記録方法及びその記録再
生原理を説明するための図である。FIG. 7 is a diagram for explaining a hologram recording method and a recording / reproducing principle thereof.
１はカバーフィルム、３はホログラム、４は珪素酸化物
層、５は可塑剤を含む合成樹脂膜、１０はガラス、１１
は車外方向、２０はレーザー、２１はハーフミラー、２
２、２３はレンズ、２５は表示体である。1 is a cover film, 3 is a hologram, 4 is a silicon oxide layer, 5 is a synthetic resin film containing a plasticizer, 10 is glass, 11
Is outside the vehicle, 20 is a laser, 21 is a half mirror, 2
Reference numerals 2 and 23 are lenses, and 25 is a display.
フロントページの続き (56)参考文献 特開 平６−56484（ＪＰ，Ａ) 特開 平５−279090（ＪＰ，Ａ) 特開 平５−85784（ＪＰ，Ａ) 特開 平５−24889（ＪＰ，Ａ) 特開 平４−130035（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) B32B 17/00 B60J 1/00 E04C 2/54 C03C 27/12 Continuation of the front page (56) References JP-A-6-56484 (JP, A) JP-A-5-279090 (JP, A) JP-A-5-85784 (JP, A) JP-A-5-24889 (JP, A) (A) JP-A-4-130035 (JP, A) (58) Fields investigated (Int. Cl. 7 , DB name) B32B 17/00 B60J 1/00 E04C 2/54 C03C 27/12
Claims (12)
可塑剤を含む合成樹脂膜／ガラスの順に積層されたこと
を特徴とするホログラム層封入合わせガラス。1. Glass / hologram layer / silicon oxide layer /
A laminated glass enclosing a hologram layer, which is laminated in the order of a synthetic resin film containing a plasticizer / glass.
酸化物層／ホログラム層／珪素酸化物層／可塑剤を含む
合成樹脂膜／ガラスの順に積層されたことを特徴とする
ホログラム層封入合わせガラス。2. A hologram layer encapsulation characterized by being laminated in the order of glass / synthetic resin film containing a plasticizer / silicon oxide layer / hologram layer / silicon oxide layer / synthetic resin film containing a plasticizer / glass. Laminated glass.
しくはその両面或いは片面に接着剤層を有するものであ
る請求項１、または請求項２記載のホログラム層封入合
わせガラス。3. The laminated glass enclosing a hologram layer according to claim 1, wherein the silicon oxide layer has a mixed layer with an adhesive or an adhesive layer on both surfaces or one surface thereof.
しくはその両面或いは片面に接着剤層を有するものであ
る請求項１、または請求項２記載のホログラム層封入合
わせガラス。4. The laminated hologram layer-enclosed glass according to claim 1, wherein the hologram layer has a mixed layer with an adhesive, or has an adhesive layer on both surfaces or one surface thereof.
ス作製時の加熱圧着操作により、ホログラム層を、その
積層面を除いた表面の全周にわたって被覆可能とする大
きさとされたものである請求項１〜請求項２の何れか一
つに記載のホログラム層封入合わせガラス。5. The lamination area of the silicon oxide layer is set to a size such that the hologram layer can be covered over the entire surface excluding the lamination surface by a heat-pressing operation at the time of manufacturing a laminated glass. The hologram layer-enclosed laminated glass according to any one of claims 1 to 2.
可塑剤を含む合成樹脂層／ガラスの順で積層されたホロ
グラム層封入合わせガラスの製造にあたって使用される
積層体であって、該積層体が、カバーフィルム／ホログ
ラム層／珪素酸化物層／カバーフィルムを順次積層して
なるものであり、両カバーフィルムが剥離除去されて使
用されるものであることを特徴とするホログラム層封入
合わせガラスの製造に使用される積層体。6. A glass / hologram layer / silicon oxide layer /
A laminated body used in the production of a laminated glass enclosing a hologram layer in which a synthetic resin layer containing a plasticizer / glass is laminated in this order, wherein the laminated body is a cover film / hologram layer / silicon oxide layer / cover film Wherein the two cover films are peeled off and used to produce a hologram layer-enclosed laminated glass.
可塑剤を含む合成樹脂層／ガラスの順で積層されたホロ
グラム層封入合わせガラスの製造にあたって使用される
積層体であって、該積層体が、カバーフィルム／ホログ
ラム層／珪素酸化物層／可塑剤を含む合成樹脂膜／カバ
ーフィルムを順次積層してなるものであり、両カバーフ
ィルムが剥離除去されて使用されるものであることを特
徴とするホログラム層封入合わせガラスの製造に使用さ
れる積層体。7. Glass / hologram layer / silicon oxide layer /
A laminated body used for producing a laminated glass enclosing a hologram layer in which a synthetic resin layer containing a plasticizer / glass is laminated in this order, wherein the laminated body is a cover film / hologram layer / silicon oxide layer / plasticizer A laminated body used in the production of a hologram-layer-enclosed laminated glass, comprising a laminate of a synthetic resin film and a cover film containing, in order, both cover films being peeled and removed. .
酸化物層／ホログラム層／珪素酸化物層／可塑剤を含む
合成樹脂膜／ガラスの順で積層されたホログラム層封入
合わせガラスの製造にあたって使用される積層体であっ
て、該積層体が、カバーフィルム／珪素酸化物層／ホロ
グラム層／珪素酸化物層／カバーフィルムを順次積層し
てなるものであり、両カバーフィルムが剥離除去されて
使用されるものであることを特徴とするホログラム層封
入合わせガラスの製造に使用される積層体。8. Production of a hologram layer-enclosed laminated glass laminated in the order of glass / synthetic resin film containing plasticizer / silicon oxide layer / hologram layer / silicon oxide layer / synthetic resin film containing plasticizer / glass The laminate used in this case is a laminate in which a cover film / a silicon oxide layer / a hologram layer / a silicon oxide layer / a cover film are sequentially laminated, and both cover films are peeled and removed. A laminate used for producing a hologram layer-enclosed laminated glass, characterized in that the laminate is used.
酸化物層／ホログラム層／珪素酸化物層／可塑剤を含む
合成樹脂膜／ガラスの順で積層されたホログラム層封入
合わせガラスの製造にあたって使用される積層体であっ
て、該積層体が、カバーフィルム／可塑剤を含む合成樹
脂膜／珪素酸化物層／ホログラム層／珪素酸化物層／可
塑剤を含む合成樹脂膜／カバーフィルムを順次積層して
なるものであり、両カバーフィルムが剥離除去されて使
用されるものであることを特徴とするホログラム層封入
合わせガラスの製造に使用される積層体。9. Production of laminated glass in which hologram layer is laminated in the order of glass / synthetic resin film containing plasticizer / silicon oxide layer / hologram layer / silicon oxide layer / plastic film containing plasticizer / glass. Wherein the laminate comprises a cover film / a synthetic resin film containing a plasticizer / a silicon oxide layer / a hologram layer / a silicon oxide layer / a synthetic resin film containing a plasticizer / a cover film. A laminate for use in the production of a hologram-layer-enclosed laminated glass, which is formed by sequentially laminating, and used by peeling and removing both cover films.
若しくはその両面或いは片面に接着剤層を有するもので
ある請求項６から請求項９の何れか一つに記載のホログ
ラム層封入合わせガラスの製造に使用される積層体。10. A silicon oxide layer comprising a mixed layer with an adhesive,
10. A laminated body used for producing a hologram layer-enclosed laminated glass according to claim 6, wherein the laminated glass has an adhesive layer on both surfaces or one surface thereof.
若しくはその両面或いは片面に接着剤層を有するもので
ある請求項６から請求項９の何れか一つに記載のホログ
ラム層封入合わせガラスの製造に使用される積層体。11. The hologram layer is a mixed layer with an adhesive,
10. A laminated body used for producing a hologram layer-enclosed laminated glass according to claim 6, wherein the laminated glass has an adhesive layer on both surfaces or one surface thereof.
ラス作製時の加熱圧着操作により、ホログラム層を、そ
の積層面を除いた表面の全周にわたって被覆可能とする
大きさとされたものである請求項６から請求項９の何れ
か一つに記載のホログラム層封入合わせガラスの製造に
使用される積層体。12. The lamination area of the silicon oxide layer is set to a size such that the hologram layer can be covered over the entire surface excluding the lamination surface by a heat-pressing operation at the time of manufacturing a laminated glass. A laminate used for manufacturing the hologram layer-enclosed laminated glass according to any one of claims 6 to 9.