JPH05210840A - Magnetic recording medium - Google Patents

Abstract

PURPOSE:To obtain a magnetic recording medium excellent in traveling property, wear resistance, durability, etc. CONSTITUTION:A lubricant formed by adding a hydrocarbon compound having a hydroxy group in the molecule at 5-80 % content in wt. to perfluoropolyether is applied on the magnetic layer surface of the magnetic recording medium such as magnetic tape, hard disk. Consequently, since the magnetic recording medium is extremely excellent in lubricity and can keep its lubricity in any using condition, the magnetic recording medium excellent in traveling property, wear resistance and durability is obtained.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】この発明は、磁気テープ、磁気デ
ィスク等の磁気記録媒体に関するものであり、特にパー
フルオロポリエーテルに分子内に水酸基を持つ炭化水素
を加えた潤滑剤を塗布した磁気記録媒体に関するもので
ある。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a magnetic recording medium such as a magnetic tape or a magnetic disk, and more particularly to a magnetic recording obtained by coating a lubricant containing perfluoropolyether with a hydrocarbon having a hydroxyl group in the molecule. It is about the medium.

【０００２】[0002]

【従来の技術】例えば、強磁性金属材料を蒸着等の手法
により非磁性支持体上に被着し、これを磁性層とした、
いわゆる金属薄膜型の磁気記録媒体では、磁性層表面の
平滑性が極めて良好であるため、磁気ヘッドやガイドロ
ーラー等の摺動部材に対する実質的な接触面積が大き
く、従って摩擦係数が大きくなり凝着現象（いわゆる張
り付き）が起き易く走行性や耐久性に欠ける等問題点が
多い。2. Description of the Related Art For example, a ferromagnetic metal material is deposited on a non-magnetic support by a method such as vapor deposition to form a magnetic layer.
In a so-called metal thin film type magnetic recording medium, the smoothness of the magnetic layer surface is extremely good, so that the substantial contact area with a sliding member such as a magnetic head or a guide roller is large, and therefore the friction coefficient is large and the adhesion is large. Phenomena (so-called sticking) are likely to occur and there are many problems such as lack of running performance and durability.

【０００３】そこで、これら問題点を改善するために各
種の潤滑剤を使用することが検討されており、従来より
高級脂肪酸やそのエステル或いはパーフルオロポリエー
テル等を前記磁気記録媒体の磁性層にトップコートする
ことにより摩擦係数を抑えようとする試みがされてい
る。Therefore, use of various kinds of lubricants has been studied in order to improve these problems, and higher fatty acids, their esters, perfluoropolyethers and the like have been conventionally used for the magnetic layer of the magnetic recording medium. Attempts have been made to suppress the coefficient of friction by coating.

【０００４】ところで、磁気記録媒体に使用される潤滑
剤には、その性質上非常に厳しい特性が要求され、従来
用いられている潤滑剤では対応することが難しいのが現
状である。By the way, the lubricant used in the magnetic recording medium is required to have very strict characteristics, and it is difficult at present to deal with the conventional lubricant.

【０００５】即ち、磁気記録媒体に使用される潤滑剤に
は、 １． 寒冷地での使用に際して所定の潤滑効果が確保さ
れるように低温特性に優れること ２． 磁気ヘッドとのスペーシングが問題となるので、
極めて薄く塗布できること、その場合にも十分な潤滑特
性が発揮されること ３． 長時間の使用に耐え、潤滑効果が持続すること 等が要求される。That is, the lubricants used for magnetic recording media are: Excellent low-temperature characteristics to ensure the desired lubrication effect when used in cold regions. Since the spacing with the magnetic head becomes a problem,
2. It can be applied extremely thinly, and in that case, sufficient lubrication characteristics can be exhibited. It is required to withstand long-term use and to maintain the lubricating effect.

【０００６】[0006]

【問題点を解決するための手段】ところが、従来より使
用されていた高級脂肪酸やそのエステル等は、０℃以下
のような低温条件上では凍結して固化し、潤滑剤として
の機能が損なわれたり、長時間の耐久性に欠ける傾向に
ある。[Means for Solving the Problems] However, higher fatty acids and their esters, which have been conventionally used, are frozen and solidified under low temperature conditions such as 0 ° C. or lower, impairing the function as a lubricant. Or, it tends to lack long-term durability.

【０００７】以上のように、磁気録媒体の分野において
は、使用される潤滑剤の能力不足に起因して、走行性、
耐久性等の実用特性に不満を残している。そのためこの
発明は、各種使用条件下において優れた潤滑性が保たれ
るとともに、長時間にわたり潤滑効果が持続され、走行
性、耐摩耗性、耐久性等に優れた磁気記録媒体を提供し
ようとするものである。As described above, in the field of magnetic recording media, runnability,
I am still dissatisfied with practical characteristics such as durability. Therefore, the present invention intends to provide a magnetic recording medium which has excellent lubricity under various conditions of use, has a long-lasting lubrication effect, and is excellent in running property, wear resistance, durability and the like. It is a thing.

【０００８】[0008]

【問題点を解決するための手段】この発明は、前記の問
題点を解決するために鋭意研究を重ねた結果、次の〔化
１〕の一般式で表されるパーフルオロポリエーテルに分
子内に水酸基を持つ炭化水素を加えた潤滑剤が、好適で
あることを見出し、磁気記録媒体の磁性層の表面にこの
潤滑剤を被着することによって、前記の課題を解決し
た。As a result of intensive studies to solve the above-mentioned problems, the present invention provides a perfluoropolyether represented by the following general formula It has been found that a lubricant containing a hydrocarbon having a hydroxyl group is suitable, and the above-mentioned problems have been solved by coating this lubricant on the surface of the magnetic layer of the magnetic recording medium.

【０００９】[0009]

【化１】 [Chemical 1]

【００１０】[0010]

【作用】パーフルオロポリエーテルに分子内に水酸基を
持つ炭化水素を加えた潤滑剤は、良好な潤滑作用を発揮
して摩擦係数を低減する。また、この潤滑作用は低温下
等の厳しい条件下においても損なわれることはない。従
って、この持つパーフルオロポリエーテルに分子内に水
酸基を持つ炭化水素を加えた潤滑剤を保有する磁気記録
媒体は、パーフルオロポリエーテルに分子内に水酸基を
持つ炭化水素を加えた潤滑剤の前記潤滑効果により走行
性の改善が図られ、耐久性が向上する。[Function] A lubricant obtained by adding a hydrocarbon having a hydroxyl group in the molecule to perfluoropolyether exhibits a good lubricating effect and reduces the friction coefficient. Further, this lubricating action is not impaired even under severe conditions such as low temperature. Therefore, the magnetic recording medium having a lubricant containing a hydrocarbon having a hydroxyl group in the molecule in this perfluoropolyether has the above-mentioned properties of a lubricant containing a hydrocarbon having a hydroxyl group in the molecule in a perfluoropolyether. The lubrication effect improves runnability and improves durability.

【００１１】[0011]

【実施例】以下、この発明の具体的な実施例について説
明するが、この発明はこの実施例に限定されるものでは
ないことは言うまでもない。EXAMPLES Specific examples of the present invention will be described below, but it goes without saying that the present invention is not limited to these examples.

【００１２】この発明の分子内に水酸基を持つ炭化水素
は、分子量、分岐構造、不飽和結合、異性体構造、脂環
構造によらず選択することができる。またヘテロ原子を
含んでいても構わない。具体的には、〔表１〕にその構
造を示す。The hydrocarbon having a hydroxyl group in the molecule of the present invention can be selected regardless of the molecular weight, branched structure, unsaturated bond, isomer structure or alicyclic structure. Further, it may contain a hetero atom. Specifically, its structure is shown in [Table 1].

【００１３】パーフルオロポリエーテルとしては単官能
の、及び多官能のパーフルオロポリエーテルを使用する
ことが可能で、例えば、その例として、単官能としては
次の〔化２〕で表されるもの、即ち、As the perfluoropolyether, monofunctional and polyfunctional perfluoropolyethers can be used. For example, as the monofunctional ones, those represented by the following [Chemical Formula 2] can be used. , That is,

【００１４】[0014]

【化２】 また、多官能としては次の〔化３〕で表されるもの、即
ち、[Chemical 2] Further, as the polyfunctional, those represented by the following [Chemical Formula 3],

【００１５】[0015]

【化３】 があるが、何等これらに限定されるものではない。[Chemical 3] However, the present invention is not limited to these.

【００１６】ここで、前記パーフルオロポリエーテルの
化学構造式中のｋ、ｌ、ｍ、ｎ、ｐ、ｑ、は１以上の整
数を示す。また、X としてはヒドロキシメチル基、カル
ボキシル基、アルコキシカルボニル基、カルボン酸アミ
ン塩、アミド等があるが何等これに限ったことではな
い。Here, k, l, m, n, p and q in the chemical structural formula of the perfluoropolyether represent integers of 1 or more. Examples of X include a hydroxymethyl group, a carboxyl group, an alkoxycarbonyl group, a carboxylic acid amine salt, and an amide, but are not limited thereto.

【００１７】その分子量としては特に限定はしないが、
６００から５０００程度が好ましい。分子量が大きくな
り過ぎると吸着基の効果が小さくなり、小さいとフッ素
の効果が薄れる。分子内に水酸基を持つ炭化水素の場合
にその炭化水素の構造としては、アルキル基にすると効
果が大きく、アルキル基の炭素数が１０以上であるとそ
の効果が特に大きい。The molecular weight is not particularly limited,
It is preferably about 600 to 5000. If the molecular weight is too high, the effect of the adsorbing group will be small, and if it is small, the effect of fluorine will be weak. In the case of a hydrocarbon having a hydroxyl group in the molecule, an alkyl group has a large effect on the structure of the hydrocarbon, and an alkyl group having 10 or more carbon atoms has a particularly large effect.

【００１８】また、その塗布方法であるが、分子内に水
酸基を持つ炭化水素化合物の融点以上に加熱してパーフ
ルオロポリエーテルと攪拌した後、フレオン等の溶媒に
溶解させて塗布してもよいし、或いはフレオン等の溶媒
に炭化水素化合物とパーフルオロポリエーテルとを溶解
させて塗布してもよい。The coating method may be such that it is heated to a temperature higher than the melting point of the hydrocarbon compound having a hydroxyl group in the molecule, stirred with perfluoropolyether, and then dissolved in a solvent such as Freon for coating. Alternatively, the hydrocarbon compound and perfluoropolyether may be dissolved and applied in a solvent such as Freon.

【００１９】前記のパーフルオロポリエーテルに分子内
に水酸基を持つ炭化水素を加えた潤滑剤の組成を〔表
１〕に示す。また〔表２〕には比較として用いたパーフ
ルオロポリエーテルをまとめた。The composition of the lubricant obtained by adding a hydrocarbon having a hydroxyl group in the molecule to the above-mentioned perfluoropolyether is shown in Table 1. In addition, Table 2 shows the perfluoropolyethers used for comparison.

【００２０】〔表１〕に示す潤滑剤を使用して、以下に
示す磁気記録媒体を作成した。金属薄膜型磁気記録媒体
（蒸着テープ）に適用した実施例について説明する。Using the lubricants shown in [Table 1], magnetic recording media shown below were prepared. An example applied to a metal thin film type magnetic recording medium (vapor deposition tape) will be described.

【００２１】１．実施例１ １４μ厚のポリエチレンテレフタレートフィルムに斜方
蒸着法によりＣｏを被着させ、膜厚２００ｎｍの強磁性
金属薄膜を形成した。次に、この金属磁性薄膜表面に、
〔表１〕中の合成物１をフレオン溶媒に溶解したものを
塗布量が５ｍｇ／ｍ² となるように塗布し、８ミリ幅に
裁断してサンプルテープを作製した。1. Example 1 Co was deposited on a 14 μm-thick polyethylene terephthalate film by the oblique evaporation method to form a ferromagnetic metal thin film having a thickness of 200 nm. Next, on this metal magnetic thin film surface,
A solution obtained by dissolving the synthetic compound 1 in [Table 1] in a Freon solvent was applied so that the application amount was 5 mg / m ^2, and cut into 8 mm width to prepare a sample tape.

【００２２】２．実施例２〜実施例１２ 実施例１において、潤滑剤として使用した〔表１〕中の
合成物１を合成物２乃至合成物１４に変えて、他は実施
例１と同様の方法によりサンプルテープを作製した。2. Examples 2 to 12 Sample tapes were prepared in the same manner as in Example 1 except that the compound 1 in Table 1 used as the lubricant in Example 1 was replaced with the compounds 2 to 14. Was produced.

【００２３】前記のようにして作製された各サンプルテ
ープについて、温度２５℃湿度６０％の時、温度ー５℃
の時、温度４０℃湿度８０％の時の摩擦係数、スチル耐
久性、シャトル耐久性について測定を行った。スチル耐
久性はポーズ状態での出力のー３ｄＢまでの減衰時間を
評価した。シャトル耐久性は、１回に付き２分間のシャ
トル走行を行い、出力が３ｄＢ低下するまでのシャトル
回数で評価した。なお、比較例として、全く潤滑剤を使
用していないブランクテープ、パーフルオロポリエーテ
ルを単独で潤滑剤として使用した場合についても測定し
た。その結果を〔表３〕に示した。For each sample tape prepared as described above, when the temperature is 25 ° C. and the humidity is 60%, the temperature is −5 ° C.
At that time, the friction coefficient, the still durability, and the shuttle durability at a temperature of 40 ° C. and a humidity of 80% were measured. For the still durability, the decay time of the output in the pause state up to -3 dB was evaluated. The shuttle durability was evaluated by performing shuttle travel for 2 minutes each time and counting the number of shuttles until the output decreased by 3 dB. In addition, as a comparative example, a blank tape containing no lubricant and a case of using perfluoropolyether alone as a lubricant were also measured. The results are shown in [Table 3].

【００２４】〔表３〕から明らかなように、潤滑剤とし
てパーフルオロポリエーテルを単独で用いた場合より
も、パーフルオロポリエーテルに分子内に水酸基を持つ
炭化水素を加えて使用することにより、摩擦係数、スチ
ル耐久性、シャトル耐久性等は、各種条件でも劣化する
ことなく非常に良好な結果が得られた。As is clear from [Table 3], by using perfluoropolyether with a hydrocarbon having a hydroxyl group in the molecule, as compared with the case of using perfluoropolyether alone as the lubricant, The friction coefficient, still durability, shuttle durability, etc. did not deteriorate under various conditions, and very good results were obtained.

【００２５】次に、添加する分子内に水酸基を持つ炭化
水素の量を変化させてその摩擦係数を調べた。その結果
を〔表４〕にまとめた。Next, the friction coefficient was investigated by changing the amount of the hydrocarbon having a hydroxyl group in the molecule to be added. The results are summarized in [Table 4].

【００２６】〔表４〕から明らかなように、分子内に水
酸基を持つ炭化水素の添加量を好ましくは５から９０重
量％とすることによって、単独で使用した時より良好な
結果が得られた。As is apparent from [Table 4], by adding the amount of the hydrocarbon having a hydroxyl group in the molecule to preferably 5 to 90% by weight, better results can be obtained when used alone. ..

【００２７】所で、前記の実施例では、磁気録媒体とし
て、非磁性支持体表面に蒸着により磁性材を磁性層とし
て形成した、いわゆる金属薄膜型磁気記録媒体に適用し
て説明したが、非磁性支持体と磁性層との間に下地層を
介した構成の磁気記録媒体にも適用することができる。Incidentally, in the above-described embodiment, the magnetic recording medium is described as being applied to a so-called metal thin film type magnetic recording medium in which a magnetic material is formed as a magnetic layer on the surface of a non-magnetic support by vapor deposition. It can also be applied to a magnetic recording medium having a structure in which an underlayer is interposed between a magnetic support and a magnetic layer.

【００２８】また、適用可能な金属薄膜型磁気記録媒体
の非磁性支持体、金属磁性薄膜は何等限定されるもので
はなく、従来より知られるものが何でも使用できる。例
示するならば、非磁性支持体としては先の塗布型の磁気
記録媒体と同様のものが使用可能である。この場合、非
磁性支持体にＡｌ合金板やガラス板等の剛性を有する基
板を使用した場合には、基板表面にアルマイト処理等の
酸化皮膜やＮｉ−Ｐ皮膜等を形成してその表面を硬くす
るようにしてもよい。The non-magnetic support and the metal magnetic thin film of the applicable metal thin film type magnetic recording medium are not particularly limited, and any conventionally known one can be used. For example, as the non-magnetic support, the same one as the above-mentioned coating type magnetic recording medium can be used. In this case, when a rigid substrate such as an Al alloy plate or a glass plate is used as the non-magnetic support, an oxide film such as an alumite treatment or a Ni-P film is formed on the surface of the substrate to harden the surface. You may do so.

【００２９】金属磁性薄膜は、メッキやスパッタリン
グ、真空蒸着等のＰＶＤの手法により連続膜として形成
されるもので、Ｆｅ、Ｃｏ、Ｎｉ等の金属やＣｏ−Ｎｉ
系合金、Ｃｏ−Ｐｔ系合金、Ｃｏ−Ｐｔ−Ｎｉ系合金、
Ｆｅ−Ｃｏ系合金、Ｆｅ−Ｎｉ系合金、Ｆｅ−Ｃｏ−Ｎ
ｉ系合金、Ｆｅ−Ｎｉ−Ｂ系合金、Ｆｅ−Ｃｏ−Ｂ系合
金、Ｆｅ−Ｃｏ−Ｎｉ−Ｂ系合金等からなる面内磁化記
録金属磁性膜やＣｏ−Ｃｒ系合金薄膜を列挙できる。The metal magnetic thin film is formed as a continuous film by a PVD method such as plating, sputtering or vacuum deposition, and is made of a metal such as Fe, Co or Ni, or Co-Ni.
Alloys, Co-Pt alloys, Co-Pt-Ni alloys,
Fe-Co based alloy, Fe-Ni based alloy, Fe-Co-N
In-plane magnetization recording metal magnetic films and Co-Cr alloy thin films made of i-based alloys, Fe-Ni-B-based alloys, Fe-Co-B-based alloys, Fe-Co-Ni-B-based alloys, etc. can be listed.

【００３０】特に、面内磁化記録金属磁性薄膜の場合、
予め非磁性支持体上にＢｉ、Ｓｂ、Ｐｂ、Ｓｎ、Ｇａ、
Ｉｎ、Ｇｅ、Ｓｉ、Ｔｌ等の低融点非磁性材料の下地層
を形成しておき、金属磁性材料を垂直方向から蒸着ある
いはスパッタし、金属磁性薄膜中にこれら低融点非磁性
材料を拡散せしめ、配向性を解消して面内等方性を確保
するとともに、抗磁性を向上するようにするとよい。Particularly, in the case of in-plane magnetization recording metal magnetic thin film,
Bi, Sb, Pb, Sn, Ga, on the non-magnetic support in advance
An underlayer of a low melting point non-magnetic material such as In, Ge, Si, Tl is formed in advance, and a metal magnetic material is vapor-deposited or sputtered from the vertical direction to diffuse the low melting point non-magnetic material in the metal magnetic thin film. It is advisable to eliminate the orientation to secure the in-plane isotropic property and to improve the anti-magnetism.

【００３１】また、ハードディスクとする場合には、金
属磁性薄膜表面に、カーボン膜、ダイヤモンド状或いは
アモルファス状カーボン膜、酸化クロム膜、ＳｉＯ2膜
等の硬質保護膜を形成するようにするとよい。In the case of a hard disk, it is advisable to form a hard protective film such as a carbon film, a diamond-like or amorphous carbon film, a chromium oxide film and a SiO2 film on the surface of the metal magnetic thin film.

【００３２】このような属薄膜型磁気記録媒体に前記パ
ーフルオロポリエーテルに分子内に水酸基を持つ炭化水
素を加えた潤滑剤を保有せしめる方法としては、金属磁
性薄膜表面や前記保護膜表面に潤滑剤層をトップコート
する方法が挙げられる。この場合、パーフルオロポリエ
ーテルに分子内に水酸基を持つ炭化水素を加えた潤滑剤
の塗布量としては、０．５ー１００ｍｇ／ｍ²であるこ
とが望ましく、１ー２０ｍｇ／ｍ²であることがより好
ましい。As a method of retaining a lubricant in which a hydrocarbon having a hydroxyl group in the molecule is added to the perfluoropolyether in such a metal thin film magnetic recording medium, the surface of the metal magnetic thin film or the surface of the protective film is lubricated. A method of topcoating the agent layer may be mentioned. In this case, the coating amount of the lubricant in which hydrocarbon having a hydroxyl group in the molecule is added to perfluoropolyether is preferably 0.5-100 mg / m ² , and 1-20 mg / m ^2. Is more preferable.

【００３３】前記のパーフルオロポリエーテルに分子内
に水酸基を持つ炭化水素を加えた潤滑剤は、単独で磁気
記録媒体の潤滑剤として用いてもよいが、従来公知の潤
滑剤と組み合わせて用いてもよい。The lubricant obtained by adding a hydrocarbon having a hydroxyl group in the molecule to the above-mentioned perfluoropolyether may be used alone as a lubricant for a magnetic recording medium, but it may be used in combination with a conventionally known lubricant. Good.

【００３４】更に、より厳しい条件に対処し潤滑効果を
持続させるために重量比３０：７０ー７０：３０程度の
配合比で極圧剤を併用するとよい。Further, in order to cope with more severe conditions and to maintain the lubricating effect, it is preferable to use an extreme pressure agent together with a compounding ratio of about 30:70 to 70:30 by weight.

【００３５】極圧剤は、境界潤滑領域において部分的に
金属接触を生じた時に、これに伴う摩擦熱によって金属
面と反応し、反応生成物皮膜を形成することにより摩
擦、摩耗防止作用を行うものであって、リン系極圧剤、
硫黄系極圧剤、ハロゲン系極圧剤、有機金属系極圧剤、
複合系極圧剤等のいずれも使用することができる。The extreme pressure agent reacts with the metal surface by frictional heat generated when a metal contact is partially generated in the boundary lubrication region, and forms a reaction product film, thereby performing a friction and wear preventing action. Which is a phosphorus-based extreme pressure agent,
Sulfur-based extreme pressure agent, halogen-based extreme pressure agent, organometallic extreme pressure agent,
Any of the composite extreme pressure agents can be used.

【００３６】また、前記の潤滑剤、極圧剤の他、必要に
応じて、防錆剤を併用してもよい。防錆剤としては、通
常この種の磁気記録媒体の防錆剤として使用されるもの
であればいずれも使用でき、例えばフェノール類、ナフ
トール類、キノン類、窒素原子を含む複素環化合物、酸
素原子を含む複素環化合物、硫黄原子を含む複素環化合
物等である。In addition to the above lubricant and extreme pressure agent, a rust preventive agent may be used in combination, if necessary. As the rust preventive, any rust preventive commonly used as a rust preventive for magnetic recording media of this type can be used, and examples thereof include phenols, naphthols, quinones, nitrogen atom-containing heterocyclic compounds, and oxygen atoms. And a heterocyclic compound containing a sulfur atom.

【００３７】所で、前記の金属薄膜型の磁気録媒体にお
いて、磁性層である金属磁性薄膜の他に、バックコート
層や下塗層等が必要に応じて形成されていてもよい。例
えば、バックコート層は磁性塗膜と同様の樹脂結合剤に
導電性を付与するためのカーボン系微粉末や表面粗度を
コントールするための無機顔料を添加し塗布形成される
ものである。Incidentally, in the above-mentioned metal thin film type magnetic recording medium, a back coat layer, an undercoat layer and the like may be formed, if necessary, in addition to the metal magnetic thin film which is the magnetic layer. For example, the back coat layer is formed by coating a resin binder similar to that of the magnetic coating film with a carbon-based fine powder for imparting conductivity and an inorganic pigment for controlling the surface roughness.

【００３８】この発明においては、このバックコート層
に前記のパーフルオロポリエーテルに長鎖炭化水素を加
えた化合物を潤滑剤として内添、或いはトップコートに
より含有せしめてもよい。或いは、磁性塗膜、金属磁性
薄膜とバックコート層にいずれもパーフルオロポリエー
テルに分子内に水酸基を持つ炭化水素を加えた潤滑剤と
して内添、トップコートする等、種々の組み合わせも可
能である。In the present invention, a compound obtained by adding a long-chain hydrocarbon to the above-mentioned perfluoropolyether may be internally added as a lubricant to the back coat layer, or may be contained by a top coat. Alternatively, various combinations such as magnetic coating, metal magnetic thin film and back coat layer can be internally added as a lubricant in which hydrocarbon having a hydroxyl group in the molecule is added to perfluoropolyether and top coated. ..

【００３９】[0039]

【発明の効果】以上の説明から明らかなように、この発
明の磁気記録媒体は、非常に優れた潤滑性を有するパー
フルオロポリエーテルに分子内に水酸基を持つ炭化水素
を重量比で５から９０％加えた潤滑剤を被着したので、
如何なる使用条件下でも、即ち高温高湿或いは低温低湿
等の過酷な条件下で使用した場合にでも良好な潤滑性を
保つことができ、また長期にわたりその潤滑性を保つこ
とができる。従って、この発明の磁気記録媒体は走行
性、耐摩耗性、耐久性に優れたものである。As is clear from the above description, the magnetic recording medium of the present invention has a weight ratio of hydrocarbons having hydroxyl groups in the molecule to perfluoropolyether having very excellent lubricity in a range of 5 to 90. % I added the added lubricant, so
Good lubricity can be maintained under any conditions of use, that is, even under severe conditions such as high temperature and high humidity or low temperature and low humidity, and the lubricity can be maintained for a long period of time. Therefore, the magnetic recording medium of the present invention is excellent in running property, wear resistance and durability.

【００４０】[0040]

【表１】 [Table 1]

【００４１】[0041]

【表２】 [Table 2]

【００４２】[0042]

【表３】 耐久性の測定結果 条件 摩擦係数 スチル シャトル 耐久性（分） 耐久性（回） 実施例１ 25℃,60%RH ０．１９ ＞１２０ ＞１５０ 40℃,80%RH ０．２３ ＞１２０ ＞１５０ -5℃ ０．２０ ＞１２０ ＞１５０ 実施例２ 25℃,60%RH ０．２１ ＞１２０ ＞１５０ 40℃,80%RH ０．２４ ＞１２０ ＞１５０ -5℃ ０．２０ ＞１２０ ＞１５０ 実施例３ 25℃,60%RH ０．１９ ＞１２０ ＞１５０ 40℃,80%RH ０．２３ ＞１２０ ＞１５０ -5℃ ０．２０ ＞１２０ ＞１５０ 実施例４ 25℃,60%RH ０．２０ ＞１２０ ＞１５０ 40℃,80%RH ０．２４ ＞１２０ ＞１５０ -5℃ ０．１９ ＞１２０ ＞１５０ 実施例５ 25℃,60%RH ０．２１ ＞１２０ ＞１５０ 40℃,80%RH ０．２５ ＞１２０ ＞１５０ -5℃ ０．２０ ＞１２０ ＞１５０ 実施例６ 25℃,60%RH ０．２２ ＞１２０ ＞１５０ 40℃,80%RH ０．２４ ＞１２０ ＞１５０ -5℃ ０．２０ ＞１２０ ＞１５０ 実施例７ 25℃,60%RH ０．２０ ＞１２０ ＞１５０ 40℃,80%RH ０．２３ ＞１２０ ＞１５０ -5℃ ０．２０ ＞１２０ ＞１５０ 実施例８ 25℃,60%RH ０．１８ ＞１２０ ＞１５０ 40℃,80%RH ０．２１ ＞１２０ ＞１５０ -5℃ ０．１９ ＞１２０ ＞１５０ 実施例９ 25℃,60%RH ０．１９ ＞１２０ ＞１５０ 40℃,80%RH ０．２３ ＞１２０ ＞１５０ -5℃ ０．２０ ＞１２０ ＞１５０ 実施例１０ 25℃,60%RH ０．１９ ＞１２０ ＞１５０ 40℃,80%RH ０．２３ ＞１２０ ＞１５０ -5℃ ０．２０ ＞１２０ ＞１５０ 実施例１１ 25℃,60%RH ０．２１ ＞１２０ ＞１５０ 40℃,80%RH ０．２４ ＞１２０ ＞１５０ -5℃ ０．２２ ＞１２０ ＞１５０ 実施例１２ 25℃,60%RH ０．１９ ＞１２０ ＞１５０ 40℃,80%RH ０．２３ ＞１２０ ＞１５０ -5℃ ０．１９ ＞１２０ ＞１５０ 実施例１３ 25℃,60%RH ０．１９ ＞１２０ ＞１５０ 40℃,80%RH ０．２１ ＞１２０ ＞１５０ -5℃ ０．１８ ＞１２０ ＞１５０ 実施例１４ 25℃,60%RH ０．２０ ＞１２０ ＞１５０ 40℃,80%RH ０．２５ ＞１２０ ＞１５０ -5℃ ０．２０ ＞１２０ ＞１５０ 比較例１ 25℃,60%RH ０．９ ２ ３ 40℃,80%RH ー ー ー -5℃ ー ー ー 比較例２ 25℃,60%RH ０．３３ １０４ １３０ 40℃,80%RH ０．３７ ９１ ５５ -5℃ ０．３４ ５１ ６０ 比較例３ 25℃,60%RH ０．３４ ９５ １２０ 40℃,80%RH ０．４０ ７６ ４６ -5℃ ０．３２ ２９ ４０ 比較例４ 25℃,60%RH ０．３１ ９４ １２１ 40℃,80%RH ０．３９ ８５ ５４ -5℃ ０．３０ ４３ ４３ 比較例５ 25℃,60%RH ０．３１ ９７ １２４ 40℃,80%RH ０．３７ ８１ ６５ -5℃ ０．３２ ４５ ５４ 比較例６ 25℃,60%RH ０．３２ １０５ ９４ 40℃,80%RH ０．４０ ８６ ５６ -5℃ ０．３２ ３９ ５０ 比較例７ 25℃,60%RH ０．２９ １１４ １４１ 40℃,80%RH ０．３３ ９５ ８６ -5℃ ０．３０ ５４ ６５ 比較例８ 25℃,60%RH ０．３２ １１０ １２３ 40℃,80%RH ０．３７ １０２ ５６ -5℃ ０．３２ ６５ ７３ 比較例９ 25℃,60%RH ０．３４ ９８ １２６ 40℃,80%RH ０．４０ ７９ ７６ -5℃ ０．３５ ３９ ５０ 比較例１０ 25℃,60%RH ０．３１ １１１ １０１ 40℃,80%RH ０．３７ ９５ ７４ -5℃ ０．３０ ５３ ６３ 比較例１１ 25℃,60%RH ０．３２ １１０ １１５ 40℃,80%RH ０．３５ ９６ ６５ -5℃ ０．３３ ６７ ７１ 比較例１２ 25℃,60%RH ０．３０ ９１ １０７ 40℃,80%RH ０．３４ ７１ ５６ -5℃ ０．３２ ３１ ４６[Table 3] Durability measurement condition Conditions Friction coefficient Still shuttle Durability (min) Durability (times) Example 1 25 ° C, 60% RH 0.19>120> 150 40 ° C, 80% RH 0.23>120> 150 -5 ° C 0.20>120> 150 Example 2 25 ° C, 60% RH 0.21>120> 150 40 ° C, 80% RH 0.24>120> 150 -5 ° C 0.20> 120 > 150 Example 3 25 ° C, 60% RH 0.19>120> 150 40 ° C, 80% RH 0.23>120> 150 -5 ° C 0.20>120> 150 Example 4 25 ° C, 60% RH 0.20>120> 150 40 ° C, 80% RH 0.24>120> 150 -5 ° C 0.19>120> 150 Example 5 25 ° C, 60% RH 0.21>120> 150 40 ° C, 80 % RH 0.25>120> 150 -5 ° C 0.20>120> 150 Example 6 25 ° C, 60% RH 0.22>120> 150 40 ° C, 80% RH 0. 4>120> 150 -5 ° C 0.20>120> 150 Example 7 25 ° C, 60% RH 0.20>120> 150 40 ° C, 80% RH 0.23>120> 150 -5 ° C 0.20 >120> 150 Example 8 25 ° C, 60% RH 0.18>120> 150 40 ° C, 80% RH 0.21>120> 150 -5 ° C 0.19>120> 150 Example 9 25 ° C, 60 % RH 0.19>120> 150 40 ° C, 80% RH 0.23>120> 150 -5 ° C 0.20>120> 150 Example 10 25 ° C, 60% RH 0.19>120> 150 40 ° C , 80% RH 0.23>120> 150 −5 ° C. 0.20>120> 150 Example 11 25 ° C., 60% RH 0.21>120> 150 40 ° C., 80% RH 0.24>120> 150 -5 ° C 0.22>120> 150 Example 12 25 ° C, 60% RH 0.19>120> 150 40 ° C, 80% RH 0.23>120> 150 -5 ° C 0.19>120> 150 Example 13 25 ° C, 60% RH 0.19>120> 150 40 ° C, 80% RH 0.21>120> 150 -5 ° C 0.18>120> 150 Implementation Example 14 25 ° C, 60% RH 0.20>120> 150 40 ° C, 80% RH 0.25>120> 150 -5 ° C 0.20>120> 150 Comparative Example 1 25 ° C, 60% RH 0.9 2 3 40 ℃, 80% RH ー -5 ℃ ー ー Comparative Example 2 25 ℃, 60% RH 0.33 104 130 40 ℃, 80% RH 0.37 91 55 -5 ℃ 0.34 51 60 Comparative Example 3 25 ° C, 60% RH 0.34 95 120 40 ° C, 80% RH 0.40 76 46 -5 ° C 0.32 29 40 Comparative Example 4 25 ° C, 60% RH 0.31 94 121 40 ° C, 80% RH 0.39 85 54 -5 ° C 0.30 43 43 Comparative Example 5 25 ° C, 60% RH 0.31 97 124 40 ° C, 80% RH 0.37 81 65 -5 ° C 0.32 45 54 Comparison Example 6 25 ° C, 60% RH 0. 2 105 94 40 ° C, 80% RH 0.40 86 56 -5 ° C 0.32 39 50 Comparative Example 7 25 ° C, 60% RH 0.29 114 141 40 ° C, 80% RH 0.33 95 86 -5 ° C 0.30 54 65 Comparative Example 8 25 ° C, 60% RH 0.32 110 123 40 ° C, 80% RH 0.37 102 56 -5 ° C 0.32 65 73 Comparative Example 9 25 ° C, 60% RH 0.34 98 126 40 ° C, 80% RH 0.40 79 76 -5 ° C 0.35 39 50 Comparative Example 10 25 ° C, 60% RH 0.31 111 101 40 ° C, 80% RH 0.37 95 74 -5 ° C 0 30 53 63 Comparative Example 11 25 ° C, 60% RH 0.32 110 115 40 ° C, 80% RH 0.35 96 65 -5 ° C 0.33 67 71 Comparative Example 12 25 ° C, 60% RH 0.30 91 107 40 ° C, 80% RH 0.34 71 56 -5 ° C 0.32 31 46

【００４３】[0043]

【表４】 潤滑剤組成 モル比 摩擦係数 パーフルオロポリエーテル／炭化水素 ∞ 0.33 HOCH₂(CF₂CF₂O)p(CF₂O)qCF₂CH₂OH/C₁₈H₃₈ 95/5 0_.29 90/10 0.29 80/20 0.26 70/30 0.24 60/40 0.23 50/50 0.21 40/60 0.20 30/70 0.21 20/80 0.22 10/90 0.24 5/95 0.25[Table 4] Lubricant composition Molar ratio Friction coefficient Perfluoropolyether / hydrocarbon ∞ 0.33 HOCH ₂ (CF ₂ CF ₂ O) p (CF ₂ O) q CF ₂ CH ₂ OH / C ₁₈ H ₃₈ 95/5 _0.29 90/10 0.29 80/20 0.26 70/30 0.24 60/40 0.23 50/50 0.21 40/60 0.20 30/70 0.21 20/80 0.22 10/90 0.24 5/95 0.25

Claims (2)

【特許請求の範囲】[Claims] 【請求項１】非磁性支持体上に少なくとも磁性層を有し
てなる磁気記録媒体であって、その磁性層表面にパーフ
ルオロポリエーテルに分子内に水酸基を持つ炭化水素化
合物を加えて耐久性を改善したことを特徴とする磁気記
録媒体。1. A magnetic recording medium comprising at least a magnetic layer on a non-magnetic support, wherein the surface of the magnetic layer is made of perfluoropolyether to which a hydrocarbon compound having a hydroxyl group in the molecule is added. A magnetic recording medium characterized by improving. 【請求項２】請求項１において、その分子内に水酸基を
持つ炭化水素の含有量が５から９０重量％であることを
特徴とする磁気記録媒体。2. The magnetic recording medium according to claim 1, wherein the content of the hydrocarbon having a hydroxyl group in its molecule is 5 to 90% by weight.