JPH04500089A - high performance tape - Google Patents

high performance tape

Info

Publication number
JPH04500089A
JPH04500089A JP1508829A JP50882989A JPH04500089A JP H04500089 A JPH04500089 A JP H04500089A JP 1508829 A JP1508829 A JP 1508829A JP 50882989 A JP50882989 A JP 50882989A JP H04500089 A JPH04500089 A JP H04500089A
Authority
JP
Japan
Prior art keywords
tape
adhesive
film
tape according
adhesive layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP1508829A
Other languages
Japanese (ja)
Inventor
ラマール，ジョージア，エル
ビジャヤクマール，プレマ
Original Assignee
オーコン・コーポレイション
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by オーコン・コーポレイション filed Critical オーコン・コーポレイション
Publication of JPH04500089A publication Critical patent/JPH04500089A/en
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるため要約のデータは記録されません。 (57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.

Description

【発明の詳細な説明】 高性能テープ Ｕ列１」 本発明は布類を他の表面に接着するのに使用される種類のテープに関するもので ある。[Detailed description of the invention] high performance tape U row 1” The present invention relates to tapes of the type used to adhere fabrics to other surfaces. be.

本発明は、特に運輸関係の用途などに使用されるテープであって、布類例えば床 カーペットやキッチンマントなどを床表面又は床上のパッド又はその他の表面に 接着すべき用途に向けたテープに関するものである。The present invention is a tape used particularly for transportation-related applications, and is suitable for use on fabrics such as floors. Place carpets, kitchen cloaks, etc. on floor surfaces or pads on floors or other surfaces. It relates to tapes for adhesive applications.

本発明はまた特に運輸用途（例えば航空機用途など）のためのテープであって、 耐炎性及び低発煙性、軽量及び耐湿性、並びに通常使用中は所望の接着力を維持 しつつ取付は及び剥離が容易であるという能力が重要な特質性能とされるような 分野のためのテープに関するものである。The invention also relates to a tape particularly for transportation applications, such as aircraft applications, comprising: Flame resistant and low smoke emitting, lightweight and moisture resistant, and maintains desired adhesion during normal use However, the ability to attach and remove easily is considered to be an important characteristic performance. Concerning tape for the field.

ｉｔ政監 航空機関係でこれまで使用されている上記のような種類の１つのテープは、綿織 物テープにゴムのベースをっけ、感圧性接着剤をテープの上面及び下面につけた テープであった。IT political supervisor One type of tape previously used in aircraft applications is cotton woven tape. A rubber base is attached to the material tape, and pressure sensitive adhesive is applied to the top and bottom of the tape. It was a tape.

このテープはいろいろな問題を提起し、航空機関係で使用するには全面的には満 足でなかった。This tape poses a number of problems and is not completely satisfactory for use in aircraft applications. It wasn't a leg.

綿布は比較的重い材料なので、適当な強さにしようとすると過剰な重量を要する 。綿布はまた湿気にさらされると水分を吸収しやすい。Cotton fabric is a relatively heavy material, so it would require excessive weight to achieve adequate strength. . Cotton fabrics also tend to absorb moisture when exposed to moisture.

ゴムをベースとした感圧性接着剤の成るものも不満足な材料である。ゴムベース 接着剤は、それ自体が問題を起こし得る多数の物質から合成される複合材料であ る。ゴムベース接着剤はゴムに加えて、粘着剤、抗酸化剤及び増量剤を含有して いることがある。これら成分の１つ又はそれ以上も湿気を吸収しやすい。また別 の問題は（長期間の後に）酸化によって起こり、これにより粘着性を失い、その 結果脆くなる。Compositions of rubber-based pressure sensitive adhesives are also unsatisfactory materials. rubber base Adhesives are composite materials made from a number of substances that can themselves pose problems. Ru. Rubber-based adhesives contain, in addition to rubber, adhesives, antioxidants, and fillers. Sometimes there are. One or more of these components also tend to absorb moisture. Another thing The problem arises (after a long period of time) due to oxidation, which causes it to lose its stickiness and its The result is brittleness.

綿布裏打材とゴムベース接着剤とはまた、あまり永くなると、これを剥がそうと しても飛行機の床に接着剤のカスを残すという問題を生じる。ゴムベース接着剤 は、綿布の表面がゴムベース接着剤にとってはや）接着しにくい表面であるので 、テープを剥がす時に綿布から層剥離する傾向がある。The cotton cloth backing and rubber-based adhesive are also difficult to remove if they get too long. However, this creates the problem of leaving adhesive residue on the floor of the airplane. rubber based adhesive This is because the surface of cotton cloth is a difficult surface for rubber-based adhesives to adhere to. , the tape tends to delaminate from the cotton fabric when removed.

綿布テープはまた湿気を吸収しやすい。このためテープが水を吸収すると重量増 加（テープの３２％の重量）の問題を起こし、接着剤が水の吸収によりその粘着 性を失うため接着性能を失うという問題も起こしている。Cotton cloth tape also tends to absorb moisture. Therefore, when the tape absorbs water, it increases in weight. (32% of the weight of the tape) and the adhesive loses its tack due to water absorption. This also causes the problem of loss of adhesive performance due to loss of adhesiveness.

成るゴムベース接着剤のその他の問題は、この種の接着剤が異種のカーペットを 結合するのには十分粘着性でないことが多いということであった。Another problem with rubber-based adhesives is that this type of adhesive can It was found that they were often not sticky enough to bond.

澄」Ｂ針園示一 本発明の第１の目的は、運輸関係、特に航空機用途に従来使用されていたテープ の諸問題及び限界を克服したテープを構成することである。Sumi” B Harizono Shikazu The first object of the present invention is to solve the problem of tapes conventionally used in transportation-related applications, particularly aircraft applications. The objective is to construct a tape that overcomes the problems and limitations of the prior art.

本発明のテープは、床カーペット及びキッチンマットなどのような布類を床表面 に、又は床上のパッドに、又はその他の機材の表面に接着すべき種類の用途向け に特に構成されたテープである０本発明のテープは、テープが耐炎性・低発煙性 の特質、軽量及び耐湿性の特質、並びに取付は及び除去が容易であって、取付は 中、使用中及び除去に際し所望の接着性を維持する能力を持たなければならない ような用途向けに構成されるものである。The tape of the present invention can be used to cover fabrics such as floor carpets and kitchen mats on floor surfaces. For applications of the type that must be adhered to the surface of the material, or to a pad on the floor, or to the surface of other materials. The tape of the present invention, which is a tape specially constructed to characteristics, lightweight and moisture resistant characteristics, and easy installation and removal; Must be capable of maintaining the desired adhesion during use, during use, and upon removal. It is designed for such uses.

本発明のテープは、水分を吸収しない非−織布基質から成っている。非−織布基 質がフィルムである好適実施例において、このフィルムは湿気障壁を構成し、軽 量で高強度、耐炎性・低発煙性をもたらすと共に、滑らかな外表面をもたらして 、組合わされる感圧性接着剤に接着するのに良好な排湿性（ｗｅｔ　ｏｕｔ）を もっている。The tape of the present invention is comprised of a non-woven matrix that does not absorb moisture. non-woven base In a preferred embodiment where the material is a film, the film constitutes a moisture barrier and is lightweight. It provides high strength, flame resistance and low smoke emission, as well as a smooth outer surface. , good wet out properties for adhesion to pressure sensitive adhesives to be combined with I have it.

本発明のテープはまた好適に、軽量で高強度の補強をもたらすため基質に接着さ れる糸（ストランド）状補強物をも含んでいる。The tape of the invention is also preferably adhered to a substrate to provide lightweight, high strength reinforcement. It also includes strand-like reinforcement.

本発明のテープは、感圧性で耐湿性の第１の接着剤層をもっている。この第１の 接着剤層は、カーペット又はその他の布類の下側に面する糸状補強物と同じ側で フィルムの表面にあって、高い粘着力をもっている。The tape of the present invention has a first adhesive layer that is pressure sensitive and moisture resistant. This first The adhesive layer should be on the same side as the thread reinforcement facing the underside of the carpet or other fabric. It is on the surface of the film and has high adhesive strength.

本発明のテープは感圧性の第２の接着剤層をもっている。The tape of the present invention has a pressure sensitive second adhesive layer.

この第２接着剤層はテープの床に面する側にある比較的薄い接着剤層であって、 テープとこれに一体になっている接着剤を床上に接着剤の残滓を残すことなく床 から除去することを可能にするように組成されている。This second adhesive layer is a relatively thin adhesive layer on the floor-facing side of the tape, The tape and its integrated adhesive can be applied to the floor without leaving any adhesive residue on the floor. The composition is such that it can be removed from the

本発明の好適実施例において、接着剤はアクリル系接着剤であり、耐炎性接着剤 である。In a preferred embodiment of the invention, the adhesive is an acrylic adhesive and a flame resistant adhesive. It is.

他の実施例において、接着剤はゴムベース接着剤に適当な添加剤を加えたもので ある。In other embodiments, the adhesive is a rubber-based adhesive with suitable additives. be.

好適実施例において、基質はプラスチックフィルム、好適にポリエステル又はポ リビニルフルオライドフィルムであり、これは全方向で高い寸法安定性と、低い 湿気蒸気透過性と低い吸湿性をもち、それ自身又は特に添加剤の配合により耐炎 性をもつものである。フィルムの１面又は両面を感圧性接着剤に接着するように 表面改質処理してもよい。In a preferred embodiment, the substrate is a plastic film, preferably polyester or polyester. ribinyl fluoride film, which has high dimensional stability in all directions and low Has moisture vapor permeability and low hygroscopicity, and is flame resistant by itself or especially with additives. It has a nature. By adhering one or both sides of the film to a pressure sensitive adhesive. Surface modification treatment may be performed.

成る用途向けとして基質はフィルム以外の非−織布基質であり、所要の特質、特 に全方向での寸法安定性と低吸湿性と難燃性をもつように構成される。For applications in which the substrate is a non-woven substrate other than a film and has the required characteristics It is constructed to have dimensional stability in all directions, low moisture absorption, and flame retardancy.

基質の厚さと、その結果の重量とは、問題とする特定用途に対し最小限に保たれ る。Substrate thickness and resulting weight are kept to a minimum for the particular application in question. Ru.

例えばフィルム基質の場合、通路におけるフィルムの厚さは１／４ミルから１ミ ル（０，０００６〜０．００２５ｍｍ）の範囲であり得る。他の領域、特にカー ベントが湿気に曝される所、例えば入口通路、キッチン、トイレなどにおいては 、フィルムはより厚くて、ｌ／２ミルから１０ミル（０，００１２’−０，０２ ５ｍｍ）の範囲とし、耐湿性を増加させ、刺通に対する抵抗を増大させるように することができる。For example, in the case of film substrates, the thickness of the film in the passageway may range from 1/4 mil to 1 mil. (0,0006 to 0.0025 mm). other areas, especially car In areas where the vent is exposed to moisture, such as entrance passages, kitchens, and toilets. , the film is thicker, l/2 mil to 10 mil (0,0012'-0,02 5mm) to increase moisture resistance and resistance to puncture. can do.

テープの糸状補強物は最小の重量で増大した強度をもたらす。糸状補強物を使用 することにより、より薄い基質を使用することができ、その場合の全体重量は１ 強度を追加するため必要な大きさだけ基質の厚さを増加させることにより増加強 度を得ようとする場合より小さくてすむ。The thread reinforcement of the tape provides increased strength with minimal weight. using filamentous reinforcement This allows the use of thinner substrates, with a total weight of 1 Increase strength by increasing substrate thickness by the amount needed to add strength. It is smaller than when trying to obtain degrees.

糸状補強物に使用される材料はそれ自身耐炎性で低発煙性の材料である。The material used for the filament reinforcement is itself flame resistant and low smoke emitting material.

好適な１実施例において、糸状補強物はポリエステル糸である。この糸のデニー ルと本数は、縦横両方向の強度と通行流れ方向の強度との両者をもたらすと共に テープの長さ方向の有効な割れ又は引き裂き抵抗を維持するように選択される。In one preferred embodiment, the thread reinforcement is a polyester thread. Denny of this thread The number of rods provides both vertical and horizontal strength as well as strength in the flow direction. It is selected to maintain effective cracking or tearing resistance along the length of the tape.

糸状補強物の本数とデニールはまた、補強強度の必要に応じた分布をもたらし、 且つ必要なら切断工具を用いることなく手でテープを裂くことができるように選 択される。糸の本数どデニール、特にテープの長さ方向に走る糸の本数とデニー ルは、また、カーペットとそれに付けたテープを除去する時にテープを引き裂き から守ると共に、テープの除去を容易にするように選択される。The number and denier of the filamentary reinforcements also provides a tailored distribution of reinforcement strength, And, if necessary, the tape should be chosen so that it can be torn by hand without the use of cutting tools. selected. The number of threads and denier, especially the number of threads running in the length direction of the tape and the denier. The tape may also tear when removing the carpet and the tape attached to it. The tape is selected to protect it from damage and to facilitate removal of the tape.

テープに使用される感圧性接着剤の両層は好適に、実質的に酸化に耐性あるアク リル系感圧性接着剤である。Both layers of pressure sensitive adhesive used in the tape are preferably adhesives that are substantially oxidation resistant. It is a rill-based pressure-sensitive adhesive.

本発明のこの特定実施例において、接着剤の上層は５ミル（０，０１ｍｍ）、好 適に３ミル（０，００７ｍｍ）以下の厚さである。In this particular embodiment of the invention, the top layer of adhesive is 5 mil (0.01 mm), preferably Suitably, the thickness is 3 mils (0,007 mm) or less.

下層の接着剤はより薄く、５ミル以下、通常３ミル以下、好適に１ミル（０，０ ０２５ｍｍ）以下の厚さである。この薄い第２接着剤層は比較的低い範囲の剥離 値（０，５ボンド／インチ幅から２．０ポンド／インチ＠）　（２５，４ｍ＋ｎ 幅当り０．２７〜０．９ｋｇ）をもつから、テープとこれに組合せた布は接着表 面にテープ又は残滓を残すことなく容易に除去することができる。The lower layer adhesive is thinner, less than 5 mils, usually less than 3 mils, preferably 1 mil (0,0 025 mm) or less. This thin second adhesive layer has a relatively low range of peeling. Value (0.5 bond/inch width to 2.0 lb/inch@) (25.4m+n 0.27 to 0.9 kg per width), so the tape and the cloth combined with it have an adhesive surface. Can be easily removed without leaving any tape or residue on surfaces.

本発明の好適実施例において、下方の接着剤層は上方の接着剤層はど強くない。In a preferred embodiment of the invention, the lower adhesive layer is not as strong as the upper adhesive layer.

下方層の強力性が小さいことはテープを床から容易に剥離できるようにさせる。The lower tenacity of the lower layer allows the tape to be easily peeled off from the floor.

これは、接着剤が除去可能に、全面的に架橋しているからである。This is because the adhesive is fully crosslinked in a removable manner.

上方層の高い・強力性は、上方層をより粘着性にし、カーペットの下側の不規則 面によく接着できるようにし、最初の取付は及び使用中の所望の安定性の両方を 容易にする。この接着剤は自己架橋式であり、長期間にわたり剥離性を改良する 。The higher strength of the upper layer makes the upper layer more sticky and the irregularities of the underside of the carpet. Allows for good adhesion to surfaces, both during initial installation and for desired stability during use. make it easier. This adhesive is self-crosslinking, improving long-term release properties .

しかし上方層は、テープを剥がしつつある時にタフトパイルを引きちぎってカー ペットを傷つけるほど強力ではない。However, the upper layer may tear off the tuft pile while removing the tape. Not strong enough to hurt your pet.

シリコーン処理紙の剥離ライナーが第１接着剤層に適用され、テープをロールか ら直接床表面に適用できるようにする。A release liner of silicone-treated paper is applied to the first adhesive layer and the tape is rolled. It can be applied directly to the floor surface.

上記した特徴を具現し、上記のように有効に機能するテープは１本発明のさらに 他の具体的目的を構成する。A tape that embodies the above-mentioned characteristics and functions effectively as described above is a further aspect of the present invention. Constitute other specific objectives.

本発明のその他の目的は図面を参照して以下本発明の原理を具体化した好適実施 例について説明するところから明らかとなるであろう。同−又は均等な原理を具 体化したその他の本発明の実施例も本発明から逸脱することなく当業者によりな され得るものである。Other objects of the present invention will be described below with reference to the drawings, in which preferred embodiments embodying the principles of the present invention will be described. This will become clear from the discussion of examples. with the same or equivalent principle. Other embodiments of the present invention may be devised by those skilled in the art without departing from the present invention. It can be done.

図」しΔｍ男− 第１［は飛行機の通路の斜視図であって１本発明のテープがどのように通路カー ペットを飛行機の床に接着するかをカーペットの一部をめくって３本のテープに ついて示すものである。Figure" Δm man- The first figure is a perspective view of an airplane aisle and shows how the tape of the present invention can be applied to an aisle car. Glue your pet to the floor of the airplane by flipping up a section of the carpet and using three strips of tape. This is what is shown here.

第２図は本発明の１実施例に従って構成されたテープ（第１図の３本のテープの １本）の上層の接着剤層を一部剥がし、下の糸状補強物とフィルム基質とを示す 拡大平面図である。FIG. 2 shows a tape (of the three tapes in FIG. 1) constructed in accordance with one embodiment of the present invention. 1) Part of the upper adhesive layer is peeled off to reveal the filamentous reinforcement and film substrate underneath. FIG.

第３図は第２図に示したテープの一部の拡大分解斜視図をカーペット及び床と共 に示す図である。Figure 3 is an enlarged exploded perspective view of a portion of the tape shown in Figure 2, along with the carpet and floor. FIG.

第４図は第２図４−４線に沿うテープ断面の一部を示す拡大断面図である。FIG. 4 is an enlarged sectional view showing a part of the tape cross section taken along the line 4--4 in FIG.

第５図は、フィルム基質の上に紗織物を糸状補強物として用いる本発明の他の実 施例に従って構成されたテープを示す第４図と同様な断面図である。FIG. 5 shows another implementation of the invention using a gauze fabric as a thread reinforcement on a film substrate. 5 is a cross-sectional view similar to FIG. 4 showing a tape constructed in accordance with an embodiment; FIG.

第６図はカーペットと床の間にカーペットパッド又はクッションが追加クッショ ンとして用いられる場合に本発明に係る２本のテープがどのようにカーペットを 床に固着するのに使用されるかを示す拡大立面図である。Figure 6 shows that a carpet pad or cushion is added between the carpet and the floor. How two tapes according to the present invention cover a carpet when used as a carpet. FIG. 6 is an enlarged elevational view showing how it is used to secure to the floor.

第７図は本発明の１実施例に従い作られたテープを、飛行機床表面に容易に適用 できるように剥離ライナーと共にロール状に巻いた斜視図である。FIG. 7 illustrates the ease of application of a tape made in accordance with one embodiment of the present invention to an airplane floor surface. FIG. 3 is a perspective view of the product being rolled up with a release liner so that it can be used.

第８図は非織布基質の他の実施例を示す第３図と同様な分解図である。FIG. 8 is an exploded view similar to FIG. 3 showing another embodiment of the non-woven substrate.

本　ｎ（ｙ）　＠ 第１図では本発明に従って構成された３本の別々のテープ１１が１通路カーペッ ト１３を航空機の座席の間の通路で航空機の床１５に接着するのに使用されてい る。Book n(y) @ In FIG. 1, three separate tapes 11 constructed in accordance with the present invention are shown in a single passage carpet. 13 to the aircraft floor 15 in the aisle between aircraft seats. Ru.

第１図で、カーペット１３の下端はめくり上げら九、個々のテープ１１が配置さ れている様子と、カーペラ１−の裏面１７が３本のテープ１１の各々の表面に接 触している様子が示されている。In Figure 1, the lower end of the carpet 13 has been turned up and the individual tapes 11 are placed. The back side 17 of the carpeller 1- is in contact with the surface of each of the three tapes 11. It is shown touching.

テープ１１の構造の詳細は第２，３及び４図に示されている。Details of the construction of tape 11 are shown in FIGS. 2, 3 and 4.

第３図の分解図に最もよく示されるように、テープ１１は非織布基質としてのフ ィルム２１、縦糸２３と横糸２５から成る糸状補強物、上方の接着剤層２７、及 び下方の接着剤層２９から成り立っている。As best shown in the exploded view of FIG. film 21, a thread-like reinforcement consisting of warp threads 23 and weft threads 25, an upper adhesive layer 27, and and an adhesive layer 29 below.

横糸２５は横糸接着剤３１により縦糸に接着されている。The weft threads 25 are adhered to the warp threads by weft thread adhesive 31.

横糸接着剤３１は第４図に示されているが、第３図では簡単のため省略されてい る。The weft adhesive 31 is shown in FIG. 4, but is omitted in FIG. 3 for simplicity. Ru.

剥離ライナー４３が第４．５．７図に示されている。A release liner 43 is shown in Figure 4.5.7.

運輸関係用途、特に航空機用のテープは、運輸環境で非常に重要な多くの特性を 備えていなければならない。Tapes for transportation applications, particularly aircraft, exhibit many properties that are very important in transportation environments. Must be prepared.

重量は航空機用途に使用する製品には重要な考察点である。Weight is an important consideration for products used in aircraft applications.

耐炎性及び低発煙性も航空機用途では全く重要である。強度対重量特性が高いこ とも重要である。そして航空機の成る領域、例えば通路の入口領域、キッチン領 域及びトイレで使用するには耐湿特性がテープの非常に重要な特性である。テー プが高度の耐湿性をもつことは重要である。同様に、航空機の入口１通路及びそ の他の領域では多数の足の通過があるから、テープはカーペットがカールしたり 滑ったりシワにならないように所定位置に保持することがきわめて重要である。Flame resistance and low smoke emission are also of great importance in aircraft applications. High strength-to-weight characteristics Both are important. and areas of the aircraft, such as aisle entrance areas, kitchen areas, etc. Moisture resistance is a very important characteristic of tapes for use in areas and toilets. Tae It is important that the pool has a high degree of moisture resistance. Similarly, aircraft entrance aisles and In other areas of the carpet where there is a lot of foot traffic, the tape will prevent the carpet from curling. It is extremely important to hold it in place to prevent it from slipping or wrinkling.

キッチンカートは、通路を行き来する時、そのの車輪がカーペット及び下にある テープに非常に大きい荷重の集中を作用させるから、テープはこのような用途に おいてカーペットを定位値にしっかり保持しなければならない。投資額と航空機 の完全利用の必要から見て、航空機の着陸時間は最短に保たれなければならず、 これはカーペットの取付は及び除去の時間もまた最短にしなければならないこと を意味する。従って本発明のテープは古いカーベントを除いて新しいのを取り付 けることが必要又は望まれるような場合にカーペットの容易で迅速なな除去と取 付けを可能にするものでなければならない。When moving the kitchen cart up and down the aisle, make sure the wheels are on the carpet and underneath. Tapes are not suitable for such applications because they are subjected to extremely large concentrations of loads. The carpet must be held firmly in position. Investment amount and aircraft In view of the need for full utilization of aircraft, landing times of aircraft must be kept to a minimum; This means that carpet installation and removal times must also be minimized. means. Therefore, the tape of the present invention can be used to remove old car vents and install new ones. Easy and quick removal and removal of carpet when necessary or desired. must be able to be attached.

航空機の床は航空機の構造部材であり、従ってテープ１１に使われた接着剤がテ ープの除去に際し少しも床に残らないことが重要である。なぜなら、このような 残滓は構造床を削り取ることを要するからである。テープ１１は航空機の床から きれいに除去可能でなければならない。The aircraft floor is a structural member of the aircraft, so the adhesive used in tape 11 It is important that no residue be left on the floor when removing the pipe. Because something like this This is because the residue requires scraping away from the structural floor. Tape 11 is from the floor of the aircraft Must be cleanly removable.

成る場合に航空機の床はガラス繊維パネルを使用するから、テープ１１はこのよ うなパネルを剥がしたり、その他何らの損傷も起こさないことが必要である。従 ってテープはカーペットを所定場所に保持するのに十分大きな接着幅をもたなけ ればならないと共に、テープをパネルから除去する必要がある時には残滓を残し たり、パネル構造を損傷したりするほど過剰でないことが必要である。Since fiberglass panels are used for the floor of aircraft in this case, the tape 11 is It is necessary that the panels do not peel off or cause any other damage. subordinate The tape must have a large enough adhesive width to hold the carpet in place. The tape must be removed from the panel, leaving no residue behind when the tape needs to be removed from the panel. It should not be so excessive as to cause damage to the panel structure.

本発明のテープ１１及びその構成分の組成及び機能性は相当な重要性をもち、航 空機用途に満足な製品となるような成る要件に合致するものでなければならない 。The composition and functionality of the tape 11 of the present invention and its components are of considerable importance and The product must meet the requirements for a product that is satisfactory for aircraft applications. .

本発明の１つの特定実施例によれば、非織布基質２１はプラスチックフィルムか ら成る。According to one particular embodiment of the invention, the non-woven substrate 21 is a plastic film. It consists of

１つの好適実施例において、このフィルムはポリエステルフィルムであり、その 床１５に面する側の表面はその接着特性を改良するように処理された表面である 。In one preferred embodiment, the film is a polyester film; The surface facing the floor 15 is a treated surface to improve its adhesive properties. .

本発明の他の実施例において、フィルムはポリビニルフルオライドフィルムから 成り、このフィルムはフィルム自体に耐炎剤を添加するよう改質した配合物であ る。In another embodiment of the invention, the film is made of polyvinyl fluoride film. This film is a modified formulation that adds a flame retardant to the film itself. Ru.

本発明の好適な実施例においては、プラスチックフィルムの創外表面が接着剤へ の接着性を改良するように処理されている。In a preferred embodiment of the invention, the external surface of the plastic film is attached to the adhesive. treated to improve adhesion.

本発明の他の実施例において、非織布基質は、軽量で丈夫で難燃性で、吸湿性が 低い、多方向繊維の不織布から成る。In another embodiment of the invention, the nonwoven substrate is lightweight, durable, flame retardant, and non-absorbent. Consisting of low, multi-directional fiber non-woven fabric.

本発明のすべての実施例において、基質は、全方向に高い寸法安定性があって最 大の強さと歪みに対する抵抗があり、テープの成分として最小の重量をもつ材料 から作られる。In all embodiments of the invention, the substrate has high dimensional stability in all directions and A material that has the greatest strength and resistance to distortion and has the lowest weight as a component of the tape. made from.

プラスチックフィルムは、連邦航空機規則例えば規則節２５．８５３（ｂ）によ る自己消火性をもつことができる離燃性ある材料から作られる。Plastic films may be made from combustible materials that can be self-extinguishing.

テープ１１が使用されるべき航空機の多くの領域用としてテープは２０ミル（０ ，０５＋＋＋ｍ）以下、通常５ミル（０，０１２１１１ｍ）以下、好適に１７２ ミル（０，００１２ｍｍ）の厚さをもつフィルムから成ることができる。例えば 通常は高温又は高摩耗にさらされないような航空機の領域、すなわち通路とかシ ートの下、又は湿気シールをしである領域などで使用されるテープは１／４ミル （０，００６ｍｍ）から１ミル（０，００２５ｍｍ）厚のものでよい。The tape is 20 mil (0 mil) for many areas of the aircraft where tape 11 is to be used. ,05+++m) or less, usually 5 mils (0,012111m) or less, preferably 172 It can consist of a film with a thickness of mil (0,0012 mm). for example Areas of the aircraft that are not normally exposed to high temperatures or high wear, such as aisles and 1/4 mil tape is used under floors or in areas where moisture seals are needed. (0,006 mm) to 1 mil (0,0025 mm) thick.

他方、入口領域、キッチン、　トイレなど湿気の防止と刺通耐性が重要であるそ の他の領域でのフィルムは具体的要件に応じて２０ミル（０，０５ｍｍ）以下、 通常１０ミル（０，０２５功ｍ）以下の厚さとする。On the other hand, areas where moisture prevention and puncture resistance are important, such as entrance areas, kitchens, and toilets. Films in other areas may be 20 mils (0.05 mm) or less depending on specific requirements; Usually less than 10 mils (0,025 mm) thick.

本発明のテープ１１は好適に基質と共に糸状補強物を含む。The tape 11 of the present invention preferably includes a filamentous reinforcement along with a matrix.

これは糸状補強物が、基質の厚さを増すだけで達成するよりも一層大きい強度増 加をより軽量においてもたらし得るからである。This is because filamentous reinforcement provides a greater strength increase than could be achieved by simply increasing the thickness of the matrix. This is because it can provide additional weight with a lighter weight.

本発明の好適実施例において糸状補強物は縦糸横糸二方向の糸から成る。特定実 施例においては第２．３．４図に示すように、二方向糸条は不織布であって、横 糸２５は縦糸２３とその下にあるフィルム２１とに横糸接着剤３１により接着さ れ、横糸接着剤３１は第４図に示すように横糸２５を取り巻いている。In a preferred embodiment of the invention, the filamentous reinforcement consists of yarns in two directions: warp and weft. specific fruit In the example, as shown in Figure 2.3.4, the bidirectional yarn is a nonwoven fabric, and the horizontal The threads 25 are bonded to the warp threads 23 and the film 21 underneath with a weft thread adhesive 31. The weft thread adhesive 31 surrounds the weft thread 25 as shown in FIG.

１つの実施例において、横糸接着剤３１は難燃性接着剤である。In one embodiment, weft adhesive 31 is a flame retardant adhesive.

好適実施例において縦糸は、フィルムに比較的均一な補強を与えると共にフィル ムを縦に引き裂くことができ、なお比較的均一な補強を保持するようなデニール 及び本数をもつように選定される。すなわち、例えばテープの幅全部にわたって 多数の長さ方向位置に補強を与えるように十分な縦糸が使用され、これは太い糸 を少量用いると不均一な補強となり、特にテープを裂くこととが必要な時そのよ うな不均一を起こすのと違って好ましい。In a preferred embodiment, the warp threads provide relatively uniform reinforcement to the film and A denier that allows the material to be torn lengthwise and still retain relatively uniform reinforcement. and the number of pieces. i.e. across the entire width of the tape, e.g. Sufficient warp threads are used to provide reinforcement at multiple longitudinal locations; Using small amounts of tape can result in uneven reinforcement, especially when tearing the tape is necessary. This is preferable since it causes non-uniformity.

他の実施例においては、第８図に示すように非職基質２２は多方向繊維の不織布 から成る。不織布２２はフィルム２１の代りに第８図に示すように使用され得る し、また不織布２２はテープの所要強度に応じて紗織物２３．２５及びフィルム ２１の代りに使用することもできる。In another embodiment, as shown in FIG. Consists of. Non-woven fabric 22 can be used instead of film 21 as shown in FIG. In addition, the nonwoven fabric 22 may be a gauze fabric 23, 25 or a film depending on the required strength of the tape. It can also be used in place of 21.

本発明の１つの実施例においてテープ１１の幅は約２インチ（５０ｍｍ）で、縦 糸は実質的εこ均等に分配され、縦糸の本数は実質的にインチ（２５，４＋ｌ１ ｍ）当り縦糸６本である。この例で縦糸は約２２０デニールである。このデニー ルは、縦糸方向すなわち通路における通行の流れ方向に所望の強度をもたらすの に十分であり、他方必要であれば、工具によらなければ切れないというのではな く、手で引き裂くことができるものである。縦糸の本数が比較的多いことはまた 、カーペットとテープを除去することが必要な場合などに破壊に対する耐性を増 加させるものである。In one embodiment of the invention, tape 11 is approximately 2 inches (50 mm) wide and vertically The threads are distributed substantially evenly and the number of warp threads is substantially equal to inches (25,4+l1 m) There are 6 warp threads per piece. In this example, the warp yarns are approximately 220 denier. this denny to provide the desired strength in the warp direction, i.e. in the flow direction of the passageway. On the other hand, if necessary, it does not mean that it cannot be cut without using a tool. It is small and can be torn apart by hand. The fact that the number of warp threads is relatively large is also Increased resistance to vandalism, such as when carpet and tape removal is required. It is something to add.

第２図に示す本発明の実施例において、横糸は実質的にインチ当り２本で、約７ ０デニールである。この小寸法で比較的少本数の横糸は、テープの長さ方向に沿 う引き裂き又は分割に十分な抵抗をもたらすものと認められた。In the embodiment of the invention shown in FIG. 2, the weft threads are substantially two threads per inch, about seven It is 0 denier. This small size and relatively small number of weft threads run along the length of the tape. It was found to provide sufficient resistance to tearing or splitting.

縦糸及び横糸に好適な材料はポリエステル材料である。糸状補強物は耐炎性で発 煙耐性があり、火炎にさらされた時も自己消火性があって、引張り強さが高く、 吸湿耐性がある材料から作られる。A preferred material for the warp and weft threads is a polyester material. Filiform reinforcement is flame resistant and It is smoke resistant, self-extinguishing when exposed to flame, and has high tensile strength. Made from moisture resistant material.

織ってない砂状補強物は重量と強度につき好適であるが、第５図に示すような紗 織物も成る用途では使用できる。Non-woven sand-like reinforcements are suitable for weight and strength, but gauze reinforcements as shown in Figure 5 are preferred. It can also be used in applications involving textiles.

第５図に示すように縦糸２３は横糸２５と共に織られている。また、糸状補強物 をフィルム２１に接着するための接着剤は、第４図に示したような横糸接着剤３ １の代りに接着剤３１の表面コーティングである。As shown in FIG. 5, the warp threads 23 are woven together with the weft threads 25. Also, filamentous reinforcement The adhesive for bonding the film 21 to the film 21 is a weft adhesive 3 as shown in FIG. 1 is replaced by a surface coating of adhesive 31.

本発明のテープのその他の重要な成分は、テープをこの上に横たわる布類又はパ ッドに接着する第１の接着剤２７と。Another important component of the tape of the present invention is that the tape and a first adhesive 27 that adheres to the pad.

テープを機体の床又は床上のパッド（第６図参照）に接着する第２の接着剤２９ である。A second adhesive 29 that adheres the tape to the fuselage floor or pad on the floor (see Figure 6) It is.

第４図に明示するように第１の接着剤層２７はやＳ不規則な上表面を有し、これ は下の糸状補強物の輪郭に従ったものである。As clearly shown in FIG. 4, the first adhesive layer 27 has a slightly irregular upper surface, which follows the contour of the filamentous reinforcement below.

この接着剤の層がもたなければならない性状には、感圧性であること、高度の粘 着性、高度の耐湿性、高度の引き裂き強さをもつことがある。この接着剤層２７ 　（又はフィルム２１）は好適に光学的に黒色とするとよい。Properties that this adhesive layer must have include being pressure sensitive and having a high degree of viscosity. May have adhesion properties, high moisture resistance, and high tear strength. This adhesive layer 27 (or the film 21) is preferably optically black.

感圧性接着剤の高粘着性は、不規則表面、例えば布の裏面などへの接着力を改良 し、カーペットがロールから引出される時はとんど瞬間的に取付は完了するよう 瞬間接着力をもつようにするため重要である。The high tackiness of pressure-sensitive adhesives improves adhesion to irregular surfaces, such as the back side of fabrics The installation is completed almost instantaneously when the carpet is pulled from the roll. This is important in order to have instant adhesive strength.

この接着剤層２７は、カーペットがテープ上でズして滑らないよう、そして接着 された布類がシワになる傾向が最小化されるよう、高い剪断強さをもつように配 合される。この層の接着剤（アクリル系か、ゴムベースかを問わず）は１％以下 の吸湿性となるように配合されるから、湿った時も粘着性を保ち、この接着剤層 がフィルム２１と組合わさって湿気に対しきわめて有効な障壁となるようにされ る。この接着剤Ｎ２７は、カーペットを外して交換すべき時にカーペットを容易 に剥がす（カーペットの毛を引きちぎらずに）ことができるように、しかし取付 は中及び使用中はカーペットが定位値からズレないように、はどよい剥離強さを もつように配合される。This adhesive layer 27 prevents the carpet from slipping on the tape and fabrics with high shear strength to minimize their tendency to wrinkle. will be combined. This layer contains less than 1% adhesive (whether acrylic or rubber-based) Because it is formulated to be hygroscopic, it remains sticky even when wet, and this adhesive layer in combination with the film 21 to provide a highly effective barrier against moisture. Ru. This adhesive N27 makes it easier to attach carpets when they need to be removed and replaced. so that it can be removed (without tearing the carpet hair), but installed During use and during use, the carpet should have good peel strength so that it does not deviate from its normal position. It is blended so that it lasts.

本発明の特定実施例において接着剤２７は２〜３ミル（０゜０Ｏ５〜０．００７ ５ｍｍ）の範囲の厚さであり、自己架橋したアクリル接着剤である。In certain embodiments of the invention, the adhesive 27 is 2-3 mils (0°005-0.007 5 mm) and is a self-crosslinking acrylic adhesive.

第２接着剤層２９は好適に透明接着剤である。これも感圧性の特質をもたなけれ ばならない。特定実施例において、この接着剤層２９は、長期にわたり粘稠を保 ち、テープを布類及び床表面に接着するのに使用されている間実質的に増えも減 りもしない剥離強さをもたらす接着剤から組成される。接着剤２９は、テープと これに組合わされた布類が容易に航空機の床表面から剥がせるように低い範囲の 剥離値をもつ。特定実施例において接着剤２９の厚さは０．７ミル〜１．５ミル （０，００１７〜０．００３７ｍ＋ａ）である。The second adhesive layer 29 is preferably a transparent adhesive. This must also have pressure-sensitive properties. Must be. In certain embodiments, the adhesive layer 29 remains viscous over long periods of time. However, while the tape is used to adhere to fabrics and floor surfaces, it increases or decreases substantially. Composed of adhesives that provide exceptional peel strength. The adhesive 29 is a tape and A low range so that the associated fabric can be easily removed from the aircraft floor surface. Has a peel value. In certain embodiments, the thickness of adhesive 29 is between 0.7 mil and 1.5 mil. (0,0017 to 0.0037 m+a).

接着剤２７及び２９は両方とも、上に敷いた布３１が濡れた場合も粘着性を保持 するよう十分な耐湿性がある。Both adhesives 27 and 29 remain tacky even when the overlying cloth 31 gets wet. It has sufficient moisture resistance.

成る航空機設備ではカーペットの下にパッドが使用される。Pads are used under carpets in aircraft equipment.

しかし本発明のテープ１１はパッドが必要とされるような設備でも使用可能であ り、そのような例を第６図に示す。第６図では２枚のテープ１１がカーペット布 １３をパッド１４が望まれる床１５に接着するのに使用されている。１つのテー プ１１はカーペット１３とパッド４１の間に挾まれ、もう１つのテープ１１はパ ッド４１と床１５の間に挾まれている。However, the tape 11 of the present invention can also be used in equipment that requires a pad. An example of this is shown in FIG. In Figure 6, two tapes 11 are made of carpet cloth. 13 is used to adhere the pad 14 to the floor 15 where it is desired. one table The tape 11 is sandwiched between the carpet 13 and the pad 41, and the other tape 11 is sandwiched between the carpet 13 and the pad 41. It is sandwiched between the pad 41 and the floor 15.

このパッドはファブリックメツシュ（布がフオーム上に使用されているパッド） 又はフオームなしの布パッドであり得る。This pad is a fabric mesh (pad where cloth is used on the foam) Or it can be a cloth pad without foam.

テープ１１の接着剤はいずれの場合もカーペットを所定位置に保持するのに十分 な粘着性をもたらす。The adhesive in tape 11 is sufficient to hold the carpet in place in both cases. Provides good stickiness.

以上説明し、図示したテープの実際例をさらに以下の例で説明する。これらの例 は好適なものであるが、本発明を限定するものではなく、本発明の範囲内で種々 変更修正をなし得るものである。Practical examples of the tapes described and illustrated above will be further explained in the following examples. These examples Although these are preferred, they do not limit the present invention, and various modifications may be made within the scope of the present invention. Changes and modifications may be made.

且−−−よ この例は第２，３．４．７図に関連して記述されるもので。And---yo This example is described in conjunction with Figures 2, 3.4.7.

構造と成分は以下の通りである。The structure and components are as follows.

シリコーンコーティングした剥離紙４３（第４図）は両面をシリコーンコーティ ングしたクラフト紙で、どちらの面に付いた接着剤に対しても等しい剥がれ方を するようになっている。このシリコーン処理紙は多くの供給源から入手できる標 準品である。Silicone-coated release paper 43 (Figure 4) is coated with silicone on both sides. Make sure the adhesive peels off equally well on either side of the kraft paper. It is supposed to be done. This silicone-treated paper is a standard material available from many sources. It is a quasi-quality product.

第１の接着剤Ｎ２’ｌは、黒に着色され、難燃性添加物が接着剤層の配合に加え られているアクリル系接着剤である。この接着剤層の厚さは２．５ミル（０，０ ０６３ｍｍ）で、接着剤は自己架橋しているのでカーペットの裏面に瞬間接着す る。この接着剤層の上表面は不規則面で、カーペットの裏面の不規則面への接着 を増強する。このアクリル系接着剤は例えばモートンケミカル社から取引糸Ａｄ ｃｏｔｅ　７３Ａ２０７で入手し得るタイプのものである。The first adhesive N2'l is colored black and a flame retardant additive is added to the formulation of the adhesive layer. It is an acrylic adhesive. The thickness of this adhesive layer is 2.5 mils (0,0 063mm), and the adhesive is self-crosslinking, so it can be instantly bonded to the back of the carpet. Ru. The top surface of this adhesive layer is irregular and will adhere to the irregular surface on the back of the carpet. strengthen. This acrylic adhesive is available from Morton Chemical Co., Ltd. It is of the type available from Cote 73A207.

難燃性添加物は例えばストウファーケミカル社から取引糸Ｆｙｒｏｌ　ＣＥＦで 入手可能なタイプのものである。Flame retardant additives are available, for example, from Stouffer Chemical Co. in the trade thread Fyrol CEF. of the type available.

糸状補強物２３．２５はポリエステルで、糸２３は２２Ｑデニール、インチ（２ ５，４ｍｍ）当り６本の糸間隔である。The thread reinforcement 23.25 is polyester and the thread 23 is 22Q denier, inch (2 The spacing is 6 threads per 5.4 mm).

糸２５は７０デニールのポリエステル糸で、インチ当り２本の糸間隔である。Thread 25 is a 70 denier polyester thread with a spacing of 2 threads per inch.

接着剤３１はポリエステル糸をプラスチックフィルム基質に接着するのに適した 難燃性接着剤で、第１接着剤層２７のアクリル系接着剤と相容性がある。Adhesive 31 is suitable for bonding polyester threads to plastic film substrates. It is a flame retardant adhesive and is compatible with the acrylic adhesive of the first adhesive layer 27.

非織布基質２１は、ポリエステルフィルムの接着剤２９に面する側をコロナ処理 したものである。このフィルムは１／２ミル（０，００１５ｍｍ）厚である。こ のフィルムは多くの入手源から購入できる。The non-woven substrate 21 is corona treated on the side facing the adhesive 29 of the polyester film. This is what I did. This film is 1/2 mil (0,0015 mm) thick. child films can be purchased from many sources.

第２接着剤Ｎ２９は難燃性添加剤を有している透明アクリル系接着剤から成る。The second adhesive N29 consists of a transparent acrylic adhesive with flame retardant additives.

この接着剤は十分に架橋しているから、機体の床から除去が可能である。層２９ の厚さは１ミル（０゜００２５ｍｍ）である。このアクリル系接着剤は例えばＢ 、Ｆ、グツドリッチ社から取引名ＨＹＣＡＲ２６１４６で、又はモートンケミカ ルからＡｄｃｏｔｅ　７３Ａ２２４で入手可能なタイプのものである。This adhesive is sufficiently cross-linked that it can be removed from the fuselage floor. layer 29 The thickness is 1 mil (0°0025 mm). This acrylic adhesive is, for example, B , F. Gutdrich under trade name HYCAR26146, or Morton Chemica. It is of the type available from Adcote 73A224 from Le.

この例で製作されたテープは航空機でカーペットを通路の床及び座席下の床に接 着する用途に特に適している。The tape produced in this example is used to attach carpet to the aisle floor and the floor under seats on aircraft. Particularly suitable for wearing.

籠−一−１ 基質２１が１０ミル（０，０２５ｍｍ）厚のポリエステルフィルムで、糸状補強 物２５が２２０デニール、インチ当り６本のポリエステル糸であることを除いて １例１と同じことを繰り返した。第１接着剤層２７は透明接着剤として、テープ を通して床表面が見えるようにする。Basket-1-1 Substrate 21 is a 10 mil (0.025 mm) thick polyester film with thread reinforcement. Except item 25 is 220 denier, 6 threads per inch polyester thread The same procedure as in Example 1 was repeated. The first adhesive layer 27 is made of tape as a transparent adhesive. Make sure the floor surface is visible through.

より厚いフィルムは耐久性と刺通抵抗、並びに有効な湿気シールをもたらす。糸 状補強物２３．２５は同じタイプで、両方向とも同じ密度とし、縦横両方向に均 一な強度をもたらす。Thicker films provide durability and puncture resistance as well as an effective moisture seal. thread The shaped reinforcements 23.25 are of the same type, have the same density in both directions, and are uniform in both length and width. Brings uniform strength.

この例で製造されるタイプは航空機のキッチンで床にキッチンマットを貼りつけ る用途に特に適している。The type manufactured in this example is an aircraft kitchen with a kitchen mat attached to the floor. Particularly suitable for applications where

匠−３ 糸状補強物２３．２５が第５図に示すような紗織物であることを除いて、例１と 同じことを繰り返した。補強物を基質２１に結合するのに使った接着剤３１は、 横糸２５のコーティングではなく基質にコーティングとして適用される、例−４ − 基質２１が第８図に示すような多方向繊維の不織布であることを除いて例１を繰 り返す。Takumi-3 Example 1 except that the thread reinforcement 23.25 is a gauze fabric as shown in FIG. I repeated the same thing. The adhesive 31 used to bond the reinforcement to the substrate 21 was Example-4 applied as a coating to the substrate rather than coating the weft 25 − Example 1 is repeated except that substrate 21 is a nonwoven fabric of multidirectional fibers as shown in FIG. Go back.

不織布基質は全方向に均一な強度をもたらす。適当な材料は吸湿耐性があり、難 燃性である。The nonwoven matrix provides uniform strength in all directions. Suitable materials are resistant to moisture absorption and difficult to It is flammable.

匠−一一旦 糸状補強物２３．２５と接着剤３１を省いたことを除いて例４を繰り返す、基質 ２１はテープに引き裂くことなく剥がし得るように長さ方向に適当な強さをもつ べきである。Takumi - once Example 4 repeated except that thread reinforcement 23.25 and adhesive 31 were omitted; substrate 21 has appropriate strength in the length direction so that the tape can be peeled off without tearing. Should.

億ニーー−」− 第１接着剤層２７がゴムをベースとした接着剤で、第２接着剤層２９が同じくゴ ムをベースとした接着剤であることを除いて例１を繰り返す、このタイプのゴム ベース接着剤は例えばモートンケミカルから取引名Ａ　ｄｃｏｔｅ　７２Ａ２０ ９　（第１層２７について）、及びＡ　ｄｃｏｔｅ　７２Ａ１２５　（第２層２ ９について）で入手し得る。100,000,000,000,000,000,000,000-”- The first adhesive layer 27 is a rubber-based adhesive, and the second adhesive layer 29 is also rubber-based. Repeat Example 1 except that the adhesive is based on this type of rubber. The base adhesive is manufactured by Morton Chemical under trade name A dcote 72A20. 9 (for the first layer 27), and A dcote 72A125 (for the second layer 2 9).

以上、本発明の好適実施例を説明し図示したが、これら実施例は変更修正が可能 なものであるから、本発明をこれらの詳細に限定する意図はなく、次の請求の範 囲に包含される変形や改良も本発明により支配されるものである。Although preferred embodiments of the present invention have been described and illustrated above, these embodiments can be modified and modified. As such, it is not intended to limit the invention to these details, but rather the scope of the following claims. It is intended that the present invention covers all modifications and improvements within the scope of the foregoing.

Ｒ６２ ＦＩＧ、３ ＦＩＧ、５ ／’７Ｇ、６ 国際調査報告 １＝１Ｇ、ＢR62 FIG.3 FIG.5 /’7G, 6 international search report 1=1G,B

Claims (34)

【特許請求の範囲】[Claims] １．布カーペット及びキッチンマットなどの布類を床表面又は床上のパッド又は その他の機材表面に接着するような用途で、難炎性及び低発煙性、軽量性、耐湿 性の特性、並びに取付け中及び使用中に所望の接着性を維持しつつ取付けと除去 を容易になし得る能力が重要な特性及び能力であるような運輸関係用途に使用さ れるテープであって、吸湿に対する抵抗、全方向での寸法安定性、火炎発生抵抗 をもたらし、接着剤に接着する良好な排湿性をもつ表面を呈するための非織基質 と、 該非織基質の第１の表面上にあって、テープを布又は床被覆材若しくはキッチン マットなどのような被覆用の布に接着するため、感圧性、耐湿性、難炎性である 接着剤から成る第１の接着剤層と、 前記非織基質の第２の表面上にあって、テープを床表面又は床上のパッド又はそ の他の機材表面に接着するため、感圧性、耐湿性、難炎性である接着剤の薄い層 から成り、前記布を剥がし且つ（又は）交換すべき時はテープが貼り付けられて いる床又はパッドから実質的に全部剥がされ得る厚さに配合され適用される第２ の接着剤層とから成るテープ。1. Place cloth such as cloth carpets and kitchen mats on floor surfaces or pads on the floor. Flame retardant, low smoke emitting, lightweight, and moisture resistant for applications such as adhesion to other material surfaces. properties, as well as installation and removal while maintaining the desired adhesion during installation and use. used in transportation-related applications where an important characteristic and capability is the ability to easily A tape with excellent resistance to moisture absorption, dimensional stability in all directions, and resistance to flame formation. non-woven substrates to provide a surface with good moisture wicking properties that will adhere to the adhesive. and, The tape is placed on the first surface of the non-woven substrate and is attached to a fabric or floor covering or kitchen. It is pressure sensitive, moisture resistant and flame retardant as it adheres to covering fabrics such as mats. a first adhesive layer consisting of an adhesive; On the second surface of the non-woven substrate, the tape is placed on a floor surface or a pad on the floor or the like. A thin layer of adhesive that is pressure sensitive, moisture resistant, and flame retardant for bonding to other substrate surfaces. and a tape is attached when the cloth is to be removed and/or replaced. The second layer is formulated and applied to a thickness that allows it to be peeled off substantially completely from the floor or pad in which it is located. A tape consisting of an adhesive layer. ２．前記非織基質が、湿気障壁を形成し、軽量で高強度と発煙抵抗をもたすフィ ルムから成る請求の範囲第１項に記載のテープ。2. The non-woven matrix forms a moisture barrier and is a lightweight, high-strength, smoke-resistant fiber. 2. A tape according to claim 1, comprising a lumen. ３．前記非織基質が、多方向繊維の不織布から成る請求の範囲第１項に記載のテ ープ。3. 2. A method according to claim 1, wherein the non-woven substrate comprises a non-woven fabric of multi-directional fibers. -P. ４．前記フィルムがプラスチックフィルムであり、且つこのフィルムに軽量で高 強度の補強をもたらすため接着された糸状条補強物を含んでいる請求の範囲第２ 項に記載のテープ。4. The film is a plastic film, and the film is lightweight and high-quality. Claim 2 includes glued filament reinforcement to provide strength reinforcement. Tape described in section. ５．前記フィルム基質が２０ミル（０．０５ｍｍ）以下、通常５ミル（０．０１ ２５ｍｍ）以下、好適に１／２ミル（０．００１２５ｍｍ）の厚さのフィルムで 、航空機用カーペットを通常高湿や摩耗にさらされない通路や座席下の領域など のような航空機の床に接着するため使用される請求の範囲第４項に記載のテープ 。5. The film substrate is 20 mils (0.05 mm) or less, typically 5 mils (0.01 mm) or less. 25 mm) or less, preferably with a film thickness of 1/2 mil (0.00125 mm). , such as aisles and under-seat areas where aircraft carpet is not normally exposed to high humidity or abrasion. A tape according to claim 4 used for adhering to the floor of an aircraft such as . ６．前記フィルム基質が２０ミル（０．０５ｍｍ）以下、通常１０ミル（０．０ ２５ｍｍ）以下の厚さのフィルムで、航空機用キッチンマットをきわめて高い湿 気シールと刺通抵抗とが重要である場所で航空機の床パネルに接着するため使用 される請求の範囲第４項に記載のテープ。6. If the film substrate is 20 mils (0.05 mm) or less, typically 10 mils (0.05 mm) or less, Aircraft kitchen mats with a film thickness of up to 25 mm) Used for adhesion to aircraft floor panels where air seal and puncture resistance are important The tape according to claim 4. ７．前記フィルム基質がポリエステルフィルムである請求の範囲第４項に記載の テープ。7. Claim 4, wherein the film substrate is a polyester film. tape. ８．前記フィルム基質が光学的性質として黒のコーティングを付されていて、第 １の接着剤層が透明接着剤である請求の範囲第４項に記載のテープ。8. the film substrate is coated with an optically black coating; 5. The tape according to claim 4, wherein one adhesive layer is a transparent adhesive. ９．前記フィルムの少なくとも第２の表面がその面で接着剤に接着するため相容 性を改質する処理をされている請求の範囲第７項に記載のテープ。9. At least a second surface of the film is compatible for adhering to the adhesive on that side. 8. The tape according to claim 7, which has been treated to modify its properties. １０．前記フィルムがそれ自身に難燃性添加剤をもつように配合を変えられたポ リビニルフルオライドフィルムである請求の範囲第４項に記載のテープ。10. The film is formulated to have flame retardant additives of its own. The tape according to claim 4, which is a ribinyl fluoride film. １１．前記フィルムの両面が接着剤に接着するための相容性を改質する処理をさ れている請求の範囲第１０項に記載のテープ。11. Both sides of the film are treated to modify their compatibility to adhere to the adhesive. 11. The tape according to claim 10. １２．前記フィルム基質が低湿気蒸気透過性をもつようメタライズコーティング をされているフィルムから成る請求の範囲第４項に記載のテープ。12. Metallized coating so that the film substrate has low moisture vapor permeability 5. The tape according to claim 4, comprising a film having the following properties. １３．前記フィルム基質が連邦航空機規則による自己消火性をもち得る難燃性状 をもつ材料から作られたフィルムを含む請求の範囲第４項に記載のテープ。13. Flame retardant properties that allow the film substrate to be self-extinguishing according to Federal Aviation Regulations. 5. A tape according to claim 4, comprising a film made of a material having a . １４．前記フィルム基質が軽量で高強度をもたらし、吸湿に抵抗性があるプラス チックフィルム又は不織布を含む請求の範囲第４項に記載のテープ。14. Plus the film matrix provides high strength at low weight and is resistant to moisture absorption 5. The tape according to claim 4, comprising a tick film or a nonwoven fabric. １５．前記糸状補強物がポリエステル又はその他の高強度、低発炎性、高吸湿性 糸状を含む請求の範囲第４項に記載のテープ。15. The filamentous reinforcement is made of polyester or other high strength, low flammability, high moisture absorption material. The tape according to claim 4, which includes a thread-like tape. １６．前記糸状補強物が縦横二方向の糸から成り、縦糸は約２２０デニール、横 糸は約７０デニールである請求の範囲第４項に記載のテープ。16. The filament-like reinforcement is made of yarns in two directions, the warp being about 220 denier and the weft being about 220 5. The tape of claim 4, wherein the thread is about 70 denier. １７．前記糸状補強物が縦横二方向の糸から成り、縦糸はインチ当り実質的に６ 本、横糸はインチ当り実質的に２本であり、テープは縦糸が航空機内の主たる通 行流れ方向に沿うように貼られ、縦糸本数を多くしてカーペット及びテープを剥 がす時の破損に対する抵抗を強めた請求の範囲第１０項に記載のテープ。17. The filamentous reinforcement is comprised of yarns in both warp and width directions, the warp being substantially 6 per inch. There are essentially two threads per inch, and the warp threads of the tape are the main threads in the aircraft. It is pasted along the direction of the grain, and the number of warp threads is increased so that the carpet and tape can be removed. 11. A tape according to claim 10 having increased resistance to breakage during peeling. １８．縦糸が実質的に２２０デニールで、比較的多数の縦糸がテープ幅にわたっ て分配され、テープの縦裂きに自由度をもたせると共に裂かれた後どの部分にも 比較的均一な強度を保つようにし、前記デニールば必要な時は切断工具なしに手 でテープを引き裂くことができるのに十分な低い大きさである請求の範囲第１７ 項に記載のテープ。18. The warp threads are substantially 220 denier and a relatively large number of warp threads span the width of the tape. This allows the tape to be torn vertically with greater flexibility and can be distributed at any part after being torn. It maintains relatively uniform strength and the denier can be cut by hand without cutting tools when necessary. Claim 17 Tape as described in Section. １９．前記糸状補強物が難炎性及び低発煙性があって、火炎にさらされた場合も 自己消火性をもつ材料製である請求の範囲第４項に記載のテープ。19. The filamentous reinforcement is flame retardant and has low smoke emitting properties, even when exposed to flame. 5. A tape according to claim 4, which is made of a material with self-extinguishing properties. ２０．前記糸状補強物が、接着剤に難燃性を与えるよう処理されたポリウレタン 接着剤でフィルムに接着され、テープ重量を最小に保つために横糸に最少量の接 着剤が付着されている請求の範囲第４項に記載のテープ。20. The filamentous reinforcement is polyurethane treated to impart flame retardancy to the adhesive. Bonded to the film with an adhesive and has a minimum amount of contact with the weft threads to keep tape weight to a minimum. 5. The tape according to claim 4, to which an adhesive is attached. ２１．前記第１の接着剤層が光学的に黒い色を含んでいる請求の範囲第１項に記 載のテープ。21. Claim 1, wherein the first adhesive layer includes an optically black color. The tape included. ２２．前記第１の接着剤層の接着剤が、布の裏面などのような不規則表面に対し 改良された接着力と、カーペットをロールからほどいていく時にほとんど瞬間的 に貼り付けができるような良好な瞬間的粘着力とをもつようにきわめて粘着性と なるよう配合されている請求の範囲第１項に記載のテープ。22. The adhesive of the first adhesive layer may be applied to an irregular surface such as the back side of a cloth. Improved adhesion and almost instantaneous unwinding of carpet from rolls Extremely sticky and has good instantaneous adhesion so that it can be pasted on The tape according to claim 1, wherein the tape is formulated so as to have the following properties. ２３．前記第１の接着剤層の接着剤が、テープ上でカーペットが滑らないように 且つ付着した布がシワになる傾向が最小化されるように高い剪断強さをもつよう に配合されている請求の範囲第１項に記載のテープ。23. The adhesive in the first adhesive layer prevents the carpet from slipping on the tape. and to have high shear strength so that the tendency of attached fabrics to wrinkle is minimized. The tape according to claim 1, wherein the tape is blended with. ２４．前記第１の接着剤層の接着剤が、カーペットを容易に剥がすことができて 損傷させないが、貼り付け中及び使用中は所定位置にとどまらせるのにほど良い 剥離強さをもっている請求の範囲第１項に記載のテープ。24. The adhesive of the first adhesive layer allows the carpet to be easily removed. Good enough to not cause damage but stay in place during application and use The tape according to claim 1, which has peel strength. ２５．前記第１の接着剤層の接着剤が、１％以下の吸湿性をもつように配合され ている請求の範囲第１項に記載のテープ。25. The adhesive of the first adhesive layer is formulated to have a hygroscopicity of 1% or less. The tape according to claim 1. ２６．前記第１の接着剤層の接着剤が、酸化に対し実質的耐性があり、難燃性添 加物を含んでいるアクリルから配合されている請求の範囲第１項に記載のテープ 。26. The adhesive of the first adhesive layer is substantially resistant to oxidation and includes flame retardant additives. The tape according to claim 1, which is formulated from acrylic containing additives. . ２７．前記第１の接着剤層の接着剤が、５ミル（０．０１２５ｍｍ）以下、好適 に３ミル（０．００７５ｍｍ）以下の厚さである請求の範囲第１項に記載のテー プ。27. The adhesive of the first adhesive layer is preferably 5 mils (0.0125 mm) or less. The tape according to claim 1, which has a thickness of 3 mils (0.0075 mm) or less. P. ２８．前記第２の接着剤層の接着剤が、長期にわたり粘稠であり、テープとこれ に組合わされた布とを航空機内の表面に接着させるため使用している間に実質的 に増減しない剥離強さをその完全架橋によって有する接着剤から形成される請求 の範囲第１項に記載のテープ。28. The adhesive of the second adhesive layer is viscous over time and the tape and during use to adhere the combined fabric to surfaces within the aircraft. Claims formed from adhesives that have a peel strength that does not increase or decrease due to their complete crosslinking. The tape according to item 1 of the scope. ２９．前記第２の接着剤層の接着剤が、テープとこれに組合わされた布とを接着 剤残滓を残すことなく容易に航空機部材の表面から除去することができる低い範 囲の剥離強さをもっている請求の範囲第１項に記載のテープ。29. The adhesive of the second adhesive layer bonds the tape and the fabric combined therewith. Low range that can be easily removed from the surface of aircraft components without leaving any chemical residue. 2. The tape according to claim 1, having a peel strength of ３０．前記第２の接着剤層の接着剤が、５ミル（０．０１２５ｍｍ）以下、通常 ３ミル（０．００７５ｍｍ）以下、好適に１ミル（０．００２５ｍｍ）以下の厚 さである請求の範囲第１項に記載のテープ。30. The adhesive of the second adhesive layer is typically less than or equal to 5 mils (0.0125 mm). Thickness of 3 mils (0.0075 mm) or less, preferably 1 mil (0.0025 mm) or less The tape according to claim 1, which is ３１．前記第１及び第２の接着剤層とも、上に敷いた布が濡れた場合でも粘着性 を保つように十分な耐湿性をもっている請求の範囲第１項に記載のテープ。31. Both the first and second adhesive layers are sticky even when the cloth placed on top gets wet. 2. The tape according to claim 1, having sufficient moisture resistance so as to maintain the temperature of the tape. ３２．前記糸状補強物が、一方向に高い強度をもつように仕上げられており、所 要の性状を発揮するように材料の選択により仕上げられている請求の範囲第１項 に記載のテープ。32. The filament reinforcement is finished to have high strength in one direction, and Claim 1: The product is finished by selecting materials so as to exhibit the essential properties. The tape described in . ３３．前記第１及び第２の接着剤層がアクリル系接着剤から成る請求の範囲第１ 項に記載のテープ。33. Claim 1, wherein the first and second adhesive layers are comprised of an acrylic adhesive. Tape as described in Section. ３４．前記第１及び第２の接着剤層がゴムをベースとした接着剤から成る請求の 範囲第１項に記載のテープ。34. 3. The method of claim 1, wherein said first and second adhesive layers are comprised of a rubber-based adhesive. The tape according to scope 1.
JP1508829A 1988-08-08 1989-08-07 high performance tape Pending JPH04500089A (en)