JPH04272978A - コーティング用樹脂組成物およびこれを用いたカラーフィルタ保護膜用樹脂組成物 - Google Patents
コーティング用樹脂組成物およびこれを用いたカラーフィルタ保護膜用樹脂組成物Info
- Publication number
- JPH04272978A JPH04272978A JP3034164A JP3416491A JPH04272978A JP H04272978 A JPH04272978 A JP H04272978A JP 3034164 A JP3034164 A JP 3034164A JP 3416491 A JP3416491 A JP 3416491A JP H04272978 A JPH04272978 A JP H04272978A
- Authority
- JP
- Japan
- Prior art keywords
- resin composition
- weight
- coating
- parts
- color filter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【0001】
【産業上の利用分野】本発明は、コーティング用樹脂組
成物およびこれを用いたカラーフィルタ保護膜用樹脂組
成物に関する。
成物およびこれを用いたカラーフィルタ保護膜用樹脂組
成物に関する。
【0002】
【従来の技術】各種物品の表面の劣化や損傷を防止する
目的でコーティング膜を形成することがしばしば行われ
ている。このようなコーティング膜においては、平滑な
塗膜が得られること、基体との密着性が高いこと、強靱
であること、耐水性及び耐薬品性、耐溶剤性が優れてい
ること、耐熱性及び耐光性が高くて長期間変質を起こさ
ないこと等の性能が要求される。
目的でコーティング膜を形成することがしばしば行われ
ている。このようなコーティング膜においては、平滑な
塗膜が得られること、基体との密着性が高いこと、強靱
であること、耐水性及び耐薬品性、耐溶剤性が優れてい
ること、耐熱性及び耐光性が高くて長期間変質を起こさ
ないこと等の性能が要求される。
【0003】また、近年では液晶表示素子、太陽電池、
光ディスク等に用いられるコーティング膜として前述の
性能に加えて透明性等の要求される用途が増加している
。
光ディスク等に用いられるコーティング膜として前述の
性能に加えて透明性等の要求される用途が増加している
。
【0004】例えば、近年、カラーフィルタを内蔵した
カラー液晶表示素子が種々発表されている。このカラー
液晶表示素子の作製にあたっては、ガラス等の透明基板
上にカラーフィルタを設け、この上にインジウムチンオ
キシド(ITO)等からなる無機薄膜を蒸着し、フォト
リソグラフィー法によってパターニングして透明電極を
形成した後、さらにこの上に液晶を配置する方法が主流
となりつつある。この場合、カラーフィルタには、この
上にITOを蒸着して、フォトリソグラフィー法で透明
電極を形成するプロセスに耐え得るだけの耐熱性、耐薬
品性が備わっていないため、ITOを蒸着する前にカラ
ーフィルタ上に保護膜を形成しておく必要がある。
カラー液晶表示素子が種々発表されている。このカラー
液晶表示素子の作製にあたっては、ガラス等の透明基板
上にカラーフィルタを設け、この上にインジウムチンオ
キシド(ITO)等からなる無機薄膜を蒸着し、フォト
リソグラフィー法によってパターニングして透明電極を
形成した後、さらにこの上に液晶を配置する方法が主流
となりつつある。この場合、カラーフィルタには、この
上にITOを蒸着して、フォトリソグラフィー法で透明
電極を形成するプロセスに耐え得るだけの耐熱性、耐薬
品性が備わっていないため、ITOを蒸着する前にカラ
ーフィルタ上に保護膜を形成しておく必要がある。
【0005】このカラーフィルタ保護膜に要求される特
性としては耐熱性、耐薬品性の他にガラス基板やカラー
フィルタとの密着性、コーティング性、透明性、耐傷性
等が挙げられる。このうち耐熱性は保護膜上にITO等
の透明電極を蒸着によって形成する際に保護膜表面が、
通常200℃以上に加熱されるため、この条件下で安定
であることが必要である。
性としては耐熱性、耐薬品性の他にガラス基板やカラー
フィルタとの密着性、コーティング性、透明性、耐傷性
等が挙げられる。このうち耐熱性は保護膜上にITO等
の透明電極を蒸着によって形成する際に保護膜表面が、
通常200℃以上に加熱されるため、この条件下で安定
であることが必要である。
【0006】このような耐熱性、耐薬品性等に優れたコ
ーティング材料としては、特開昭58−196506号
公報や特開昭62−119501号公報記載のアクリル
系樹脂、特開昭60−216307号公報記載のポリグ
リシジルメタクリレート樹脂、特開昭63−13110
3号公報記載のメラミン樹脂、エポキシ樹脂、その他ポ
リイミド樹脂等が提案されている。
ーティング材料としては、特開昭58−196506号
公報や特開昭62−119501号公報記載のアクリル
系樹脂、特開昭60−216307号公報記載のポリグ
リシジルメタクリレート樹脂、特開昭63−13110
3号公報記載のメラミン樹脂、エポキシ樹脂、その他ポ
リイミド樹脂等が提案されている。
【0007】
【発明が解決しようとする課題】しかしながら、従来提
案されている材料ではそれぞれ欠点があり、全ての要求
特性を満足するバランスのとれた材料は無い。
案されている材料ではそれぞれ欠点があり、全ての要求
特性を満足するバランスのとれた材料は無い。
【0008】例えば、アクリル系樹脂では耐熱性が不十
分であり、ITO等の蒸着時に膜の表面にシワやクラッ
クを生じるという問題がある。
分であり、ITO等の蒸着時に膜の表面にシワやクラッ
クを生じるという問題がある。
【0009】ポリグリシジルメタクリレート系樹脂では
、ガラス基板等との密着性が不十分であり、液晶素子組
立てプロセス中にハガレを生じたり、カラーフィルタ層
に薬品等が侵入することを十分に阻止することができな
い。
、ガラス基板等との密着性が不十分であり、液晶素子組
立てプロセス中にハガレを生じたり、カラーフィルタ層
に薬品等が侵入することを十分に阻止することができな
い。
【0010】メラミン樹脂は、比較的耐熱性は高いもの
のガラス基板やカラーフィルタとの密着性が極端に悪く
、基板やフィルタ上でハジキを生じ易い。
のガラス基板やカラーフィルタとの密着性が極端に悪く
、基板やフィルタ上でハジキを生じ易い。
【0011】エポキシ樹脂は密着性の良いものは耐熱性
が不十分であり、耐熱性の高いものは密着性やコーティ
ング性が劣るため要求特性のバランスをとることができ
ない。また、ポリイミド樹脂は、透明性が不十分な上に
、ワニスの保存安定性に欠ける点や、カラーフィルタを
浸すような溶剤しか使用できないというような問題点が
ある。
が不十分であり、耐熱性の高いものは密着性やコーティ
ング性が劣るため要求特性のバランスをとることができ
ない。また、ポリイミド樹脂は、透明性が不十分な上に
、ワニスの保存安定性に欠ける点や、カラーフィルタを
浸すような溶剤しか使用できないというような問題点が
ある。
【0012】本発明の目的は上記従来材料の欠点を解決
し耐熱性、耐薬品性、密着性、コーティング性、透明性
、耐傷性等の全ての要求特性を満足し得るバランスのと
れた新規なコーティング用樹脂組成物およびこれを用い
たカラーフィルタ保護膜用樹脂組成物を提供するもので
ある。
し耐熱性、耐薬品性、密着性、コーティング性、透明性
、耐傷性等の全ての要求特性を満足し得るバランスのと
れた新規なコーティング用樹脂組成物およびこれを用い
たカラーフィルタ保護膜用樹脂組成物を提供するもので
ある。
【0013】
【課題を解決するための手段】すなわち、本発明は、A
.(1)N置換マレイミド、(2)炭素数6〜20の脂
環式構造を有する脂環式アクリル酸エステルおよび/ま
たは脂環式メタクリル酸エステル、(3)アクリル酸お
よび/またはメタクリル酸ならびに(4)必要により(
1)および/または(3)と共重合可能な不飽和単量体
を共重合してなる共重合樹脂と B.分子内にエポキシ基を2以上有するエポキシ樹脂と
を含有してなるコーティング用樹脂組成物およびこれを
用いたカラーフィルタ保護膜用樹脂組成物に関する。
.(1)N置換マレイミド、(2)炭素数6〜20の脂
環式構造を有する脂環式アクリル酸エステルおよび/ま
たは脂環式メタクリル酸エステル、(3)アクリル酸お
よび/またはメタクリル酸ならびに(4)必要により(
1)および/または(3)と共重合可能な不飽和単量体
を共重合してなる共重合樹脂と B.分子内にエポキシ基を2以上有するエポキシ樹脂と
を含有してなるコーティング用樹脂組成物およびこれを
用いたカラーフィルタ保護膜用樹脂組成物に関する。
【0014】本発明におけるA成分である共重合樹脂を
構成するモノマー成分としての(1)N置換マレイミド
としては、公知のものが使用できるが、Nメチルマレイ
ミド、Nエチルマレイミド、Nプロピルマレイミド、N
ブチルマレイミドNシクロヘキシルマレイミド、Nフェ
ニルマレイミドおよびNアルキル基置換フェニルマレイ
ミドからなる群より選ばれる少なくとも1種の化合物を
使用することが、耐熱性および基材との密着性の観点か
ら好ましい。これらのうちでもNシクロヘキシルマレイ
ミドおよびNフェニルマレイミドが特に好ましい。A成
分である共重合樹脂中における
構成するモノマー成分としての(1)N置換マレイミド
としては、公知のものが使用できるが、Nメチルマレイ
ミド、Nエチルマレイミド、Nプロピルマレイミド、N
ブチルマレイミドNシクロヘキシルマレイミド、Nフェ
ニルマレイミドおよびNアルキル基置換フェニルマレイ
ミドからなる群より選ばれる少なくとも1種の化合物を
使用することが、耐熱性および基材との密着性の観点か
ら好ましい。これらのうちでもNシクロヘキシルマレイ
ミドおよびNフェニルマレイミドが特に好ましい。A成
分である共重合樹脂中における
【0015】(1)N置換マレイミドの配合量は20〜
70重量%((1)、(2)、(3)および(4)の総
量基準)であることが好ましい。これより少ないと得ら
れるコーティング膜の耐熱性が不十分となる傾向があり
、またこれより多い場合は密着性やコーティング性に不
都合を生じる傾向がある。
70重量%((1)、(2)、(3)および(4)の総
量基準)であることが好ましい。これより少ないと得ら
れるコーティング膜の耐熱性が不十分となる傾向があり
、またこれより多い場合は密着性やコーティング性に不
都合を生じる傾向がある。
【0016】(2)の炭素数6〜20の脂環式構造を有
する脂環式アクリル酸エステル、脂環式メタクリル酸エ
ステルとしては、例えばアクリル酸シクロヘキシル、ア
クリル酸シクロヘキシルメチル、アクリル酸2,2,5
−トリメチルシクロヘキシル、アクリル酸ノルボルニル
、アクリル酸ノルボルニルメチル、アクリル酸アダマン
チル、アクリル酸トリシクロ〔5,2,1,02′6〕
デカン−8−イル、アクリル酸トリシクロ〔5,2,1
,02′6〕デカン−3(又は4)−イルメチル、アク
リル酸ボルニル、アクリル酸イソボルニル、アクリル酸
フェンチル、アクリル酸メンチル等のアクリル酸シクロ
アルキル、メタクリル酸シクロヘキシル、メタクリル酸
シクロヘキシルメチル、メタクリル酸2,2,5−トリ
メチルシクロヘキシル、メタクリル酸ノルボルニル、メ
タクリル酸ノルボルニルメチル、メタクリル酸アダマン
チル、メタクリル酸トリシクロ〔5,2,1,02′6
〕デカン−8−イル、メタクリル酸トリシクロ〔5,2
,1,02′6〕デカン−3(又は4)−イルメチル、
メタクリル酸ボルニル、メタクリル酸イソボルニル、メ
タクリル酸フェンチル、メタクリル酸メンチル等のメタ
クリル酸シクロアルキルエステルなどが挙げられ、これ
らの1種以上が使用される。なかでも、耐熱性の点から
メタクリル酸ノルボルニルメタクリル酸アダマンチル、
メタクリル酸トリシクロ〔5,2,1,02′6〕デカ
ン−8−イル、メタクリル酸イソボルニル等の縮合環を
含むメタクリル酸シクロアルキルエステルが好ましい。
する脂環式アクリル酸エステル、脂環式メタクリル酸エ
ステルとしては、例えばアクリル酸シクロヘキシル、ア
クリル酸シクロヘキシルメチル、アクリル酸2,2,5
−トリメチルシクロヘキシル、アクリル酸ノルボルニル
、アクリル酸ノルボルニルメチル、アクリル酸アダマン
チル、アクリル酸トリシクロ〔5,2,1,02′6〕
デカン−8−イル、アクリル酸トリシクロ〔5,2,1
,02′6〕デカン−3(又は4)−イルメチル、アク
リル酸ボルニル、アクリル酸イソボルニル、アクリル酸
フェンチル、アクリル酸メンチル等のアクリル酸シクロ
アルキル、メタクリル酸シクロヘキシル、メタクリル酸
シクロヘキシルメチル、メタクリル酸2,2,5−トリ
メチルシクロヘキシル、メタクリル酸ノルボルニル、メ
タクリル酸ノルボルニルメチル、メタクリル酸アダマン
チル、メタクリル酸トリシクロ〔5,2,1,02′6
〕デカン−8−イル、メタクリル酸トリシクロ〔5,2
,1,02′6〕デカン−3(又は4)−イルメチル、
メタクリル酸ボルニル、メタクリル酸イソボルニル、メ
タクリル酸フェンチル、メタクリル酸メンチル等のメタ
クリル酸シクロアルキルエステルなどが挙げられ、これ
らの1種以上が使用される。なかでも、耐熱性の点から
メタクリル酸ノルボルニルメタクリル酸アダマンチル、
メタクリル酸トリシクロ〔5,2,1,02′6〕デカ
ン−8−イル、メタクリル酸イソボルニル等の縮合環を
含むメタクリル酸シクロアルキルエステルが好ましい。
【0017】A成分である共重合樹脂中における(1)
脂環式アクリル酸エステルおよび/またはメタクリル酸
エステルの使用量は20〜70重量%((1)、(2)
、(3)および(4)の総量基準)であることが好まし
い。これより少ないと得られる硬化被覆膜の耐熱性が不
十分となる傾向があり、これより多い場合は、密着性や
コーティング性に不都合を生じる傾向がある。
脂環式アクリル酸エステルおよび/またはメタクリル酸
エステルの使用量は20〜70重量%((1)、(2)
、(3)および(4)の総量基準)であることが好まし
い。これより少ないと得られる硬化被覆膜の耐熱性が不
十分となる傾向があり、これより多い場合は、密着性や
コーティング性に不都合を生じる傾向がある。
【0018】(3)のアクリル酸および/またはメタク
リル酸の配合量は、共重合樹脂中の5〜30重量%((
1)、(2)、(3)および(4)の総量基準)である
ことが好ましい。これより少ないと、得られる硬化物の
耐熱性、耐傷性が不十分となる傾向があり、これより多
い場合は、コーティング性や硬化物の耐薬品性等が低下
する傾向がある。
リル酸の配合量は、共重合樹脂中の5〜30重量%((
1)、(2)、(3)および(4)の総量基準)である
ことが好ましい。これより少ないと、得られる硬化物の
耐熱性、耐傷性が不十分となる傾向があり、これより多
い場合は、コーティング性や硬化物の耐薬品性等が低下
する傾向がある。
【0019】(4)の(1)、(2)および/または(
3)と共重合可能な不飽和単量体としては(2)以外の
不飽和脂肪酸エステル、芳香族ビニル化合物、シアン化
ビニル化合物等がある。(2)以外の不飽和脂肪酸エス
テルとしては、アクリル酸メチル、アクリル酸エチル、
アクリル酸ブチル、アクリル酸2−エチルヘキシル等の
アクリル酸アルキルエステル、アクリル酸フェニル、ア
クリル酸ベンジル等のアクリル酸芳香族エステル、アク
リル酸グリシジルアクリル酸2−ヒドロキシエチル等の
アクリル酸エステル、メタクリル酸メチル、メタクリル
酸エチル、メタクリル酸ブチル、メタクリル酸2−エチ
ルヘキシル等のメタクリル酸アルキルエステル、メタク
リル酸フェニル、メタクリル酸ベンジル等のメタクリル
酸芳香族エステル、メタクリル酸グリシジル、メタクリ
ル酸2−ヒドロキシエチル等のメタクリル酸エステルな
どがある。芳香族ビニル化合物としては、スチレン又は
α−メチルスチレン、α−エチルスチレン等の置換スチ
レン、クロロスチレン、ビニルトルエン、t−ブチルス
チレン等の核置換スチレン等がある。シアン化ビニル化
合物としては、アクリロニトリル、メタクリロニトリル
等がある。
3)と共重合可能な不飽和単量体としては(2)以外の
不飽和脂肪酸エステル、芳香族ビニル化合物、シアン化
ビニル化合物等がある。(2)以外の不飽和脂肪酸エス
テルとしては、アクリル酸メチル、アクリル酸エチル、
アクリル酸ブチル、アクリル酸2−エチルヘキシル等の
アクリル酸アルキルエステル、アクリル酸フェニル、ア
クリル酸ベンジル等のアクリル酸芳香族エステル、アク
リル酸グリシジルアクリル酸2−ヒドロキシエチル等の
アクリル酸エステル、メタクリル酸メチル、メタクリル
酸エチル、メタクリル酸ブチル、メタクリル酸2−エチ
ルヘキシル等のメタクリル酸アルキルエステル、メタク
リル酸フェニル、メタクリル酸ベンジル等のメタクリル
酸芳香族エステル、メタクリル酸グリシジル、メタクリ
ル酸2−ヒドロキシエチル等のメタクリル酸エステルな
どがある。芳香族ビニル化合物としては、スチレン又は
α−メチルスチレン、α−エチルスチレン等の置換スチ
レン、クロロスチレン、ビニルトルエン、t−ブチルス
チレン等の核置換スチレン等がある。シアン化ビニル化
合物としては、アクリロニトリル、メタクリロニトリル
等がある。
【0020】これらの(4)の(1)、(2)および/
または(3)と共重合可能な不飽和単量体はA成分の共
重合樹脂中0〜50重量%((1)、(2)、(3)お
よび(4)の総量基準)使用される。50重量%以上の
場合は本発明の効果が不十分となりやすい。
または(3)と共重合可能な不飽和単量体はA成分の共
重合樹脂中0〜50重量%((1)、(2)、(3)お
よび(4)の総量基準)使用される。50重量%以上の
場合は本発明の効果が不十分となりやすい。
【0021】これらの(1)、(2)、(3)および(
4)を共重合するにあたってはラジカル重合やイオン重
合等の公知の方法を適用できる。例えば重合開始剤の存
在下で塊状重合法、溶液重合法、懸濁重合法、乳化重合
法等の方法で製造できる。
4)を共重合するにあたってはラジカル重合やイオン重
合等の公知の方法を適用できる。例えば重合開始剤の存
在下で塊状重合法、溶液重合法、懸濁重合法、乳化重合
法等の方法で製造できる。
【0022】重合開始剤としては例えば、過酸化ベンゾ
イル、過酸化ラウロイル、ジ−t−ブチルペルオキシヘ
キサヒドロフタレート、t−ブチルペルオキシ−2−エ
チルヘキサノエート、1,1−ジ−t−ブチルペルオキ
シ−3,3,5−トリメチルシクロヘキサン等の有機過
酸化物、アゾビスイソブチロニトリル、アゾビス−4−
メトキシ−2,4−ジメチルバレロニトリル、アゾビス
シクロヘキサノン−1−カルボニトリル、アゾジベンゾ
イル等のアゾ化合物、過硫酸カリウム、過硫酸アンモニ
ウムに代表される水溶性触媒及び過酸化物あるいは過硫
酸塩と還元剤の組み合わせによるレドックス触媒等、通
常のラジカル重合に使用できるものはいずれも使用する
ことができる。重合触媒は(1)、(2)、(3)およ
び(4)の総量に対して0.01〜10重量%の範囲で
使用するのが好ましい。
イル、過酸化ラウロイル、ジ−t−ブチルペルオキシヘ
キサヒドロフタレート、t−ブチルペルオキシ−2−エ
チルヘキサノエート、1,1−ジ−t−ブチルペルオキ
シ−3,3,5−トリメチルシクロヘキサン等の有機過
酸化物、アゾビスイソブチロニトリル、アゾビス−4−
メトキシ−2,4−ジメチルバレロニトリル、アゾビス
シクロヘキサノン−1−カルボニトリル、アゾジベンゾ
イル等のアゾ化合物、過硫酸カリウム、過硫酸アンモニ
ウムに代表される水溶性触媒及び過酸化物あるいは過硫
酸塩と還元剤の組み合わせによるレドックス触媒等、通
常のラジカル重合に使用できるものはいずれも使用する
ことができる。重合触媒は(1)、(2)、(3)およ
び(4)の総量に対して0.01〜10重量%の範囲で
使用するのが好ましい。
【0023】また、重合調節剤として、メルカプタン系
化合物、チオグリコール、四臭化炭素、α−メチルスチ
レンダイマー等が分子量調節のために必要に応じて添加
し得る。
化合物、チオグリコール、四臭化炭素、α−メチルスチ
レンダイマー等が分子量調節のために必要に応じて添加
し得る。
【0024】重合温度は、0〜200℃の範囲で適宜選
択するのが好ましく、特に50〜120℃であるのが好
ましい。
択するのが好ましく、特に50〜120℃であるのが好
ましい。
【0025】溶液重合における溶媒としては、通常のラ
ジカル重合に使用される溶媒が使用できる。具体例とし
てはベンゼン、トルエン、キシレン等の芳香族系溶剤;
アセトン、メチルエチルケトン、メチルイソブチルケト
ン、シクロヘキサノン等のケトン系溶剤;ジエチルエー
テル、イソプロピルエーテル、テトラヒドロフラン、ジ
オキサン、エチレングリコールジメチルエーテル、エチ
レングリコールジエチルエーテル、ジエチレングリコー
ルジメチルエーテル、ジエチレングリコールジエチルエ
ーテル等のエーテル系溶剤;酢酸エチル、酢酸−n−プ
ロピル、酢酸イソプロピル、酢酸−n−ブチル、エチレ
ングリコールモノメチルエーテルアセタート、エチレン
グリコールモノエチルエーテルアセタート、エチレング
リコールモノブチルエーテルアセタート、ジエチレング
リコールモノメチルエーテルアセタート、ジエチレング
リコールモノエチルエーテルアセタート、プロピレング
リコールモノメチルエーテルアセタート、プロピレング
リコールモノエチルエーテルアセタート、γ−ブチロラ
クトン等のエステル系溶剤;ジメチルホルムアミド、ジ
メチルアセトアミド、N−メチルピロリドン等のアミド
系溶剤などが挙げられる。これらの溶剤のうち、エステ
ル系溶剤及びケトン系溶剤が好ましく、単独で、または
2種類以上を混合して使用することができる。なお、通
常、コーティング用樹脂組成物として用いる場合は溶剤
を含有しているので同じ溶剤を用いて溶液重合法によっ
て重合するのが好ましいが、重合体製造後、メタノール
再沈法等の方法によりポリマを単離し、他の溶剤に溶解
して使用に供することも可能である。
ジカル重合に使用される溶媒が使用できる。具体例とし
てはベンゼン、トルエン、キシレン等の芳香族系溶剤;
アセトン、メチルエチルケトン、メチルイソブチルケト
ン、シクロヘキサノン等のケトン系溶剤;ジエチルエー
テル、イソプロピルエーテル、テトラヒドロフラン、ジ
オキサン、エチレングリコールジメチルエーテル、エチ
レングリコールジエチルエーテル、ジエチレングリコー
ルジメチルエーテル、ジエチレングリコールジエチルエ
ーテル等のエーテル系溶剤;酢酸エチル、酢酸−n−プ
ロピル、酢酸イソプロピル、酢酸−n−ブチル、エチレ
ングリコールモノメチルエーテルアセタート、エチレン
グリコールモノエチルエーテルアセタート、エチレング
リコールモノブチルエーテルアセタート、ジエチレング
リコールモノメチルエーテルアセタート、ジエチレング
リコールモノエチルエーテルアセタート、プロピレング
リコールモノメチルエーテルアセタート、プロピレング
リコールモノエチルエーテルアセタート、γ−ブチロラ
クトン等のエステル系溶剤;ジメチルホルムアミド、ジ
メチルアセトアミド、N−メチルピロリドン等のアミド
系溶剤などが挙げられる。これらの溶剤のうち、エステ
ル系溶剤及びケトン系溶剤が好ましく、単独で、または
2種類以上を混合して使用することができる。なお、通
常、コーティング用樹脂組成物として用いる場合は溶剤
を含有しているので同じ溶剤を用いて溶液重合法によっ
て重合するのが好ましいが、重合体製造後、メタノール
再沈法等の方法によりポリマを単離し、他の溶剤に溶解
して使用に供することも可能である。
【0026】本発明におけるB成分である分子内にエポ
キシ基を2以上有するエポキシ樹脂としては、ビスフェ
ノールA型液状エポキシ樹脂、ビスフェノールA型固型
エポキシ樹脂、ビスフェノールF型エポキシ樹脂、フェ
ノールノボラックエポキシ樹脂、クレゾールノボラック
エポキシ樹脂、脂環式エポキシ樹脂、グリシジルエステ
ル系エポキシ樹脂、グリシジルアミン系エポキシ樹脂、
複素環式エポキシ樹脂などがあるが、耐熱性及び密着性
の点からフェノールノボラックエポキシ樹脂およびクレ
ゾールノボラックエポキシ樹脂が特に好ましい。
キシ基を2以上有するエポキシ樹脂としては、ビスフェ
ノールA型液状エポキシ樹脂、ビスフェノールA型固型
エポキシ樹脂、ビスフェノールF型エポキシ樹脂、フェ
ノールノボラックエポキシ樹脂、クレゾールノボラック
エポキシ樹脂、脂環式エポキシ樹脂、グリシジルエステ
ル系エポキシ樹脂、グリシジルアミン系エポキシ樹脂、
複素環式エポキシ樹脂などがあるが、耐熱性及び密着性
の点からフェノールノボラックエポキシ樹脂およびクレ
ゾールノボラックエポキシ樹脂が特に好ましい。
【0027】本発明の組成物におけるA成分とB成分と
の混合比率は、A成分の共重合樹脂100重量部に対し
てB成分のエポキシ樹脂30〜300重量部を配合する
ことが好ましい。B成分のエポキシ樹脂が少な過ぎると
、耐薬品性が不十分となる傾向があり、多過ぎる場合は
密着性が低下する傾向がある。
の混合比率は、A成分の共重合樹脂100重量部に対し
てB成分のエポキシ樹脂30〜300重量部を配合する
ことが好ましい。B成分のエポキシ樹脂が少な過ぎると
、耐薬品性が不十分となる傾向があり、多過ぎる場合は
密着性が低下する傾向がある。
【0028】本発明のコーティング用樹脂組成物には、
必要に応じて、A、B成分以外にも種々の成分(C成分
)を使用することができる。C成分としては、多価カル
ボン酸無水物および多価カルボン酸からなる群より選ば
れる少なくとも1種の化合物の使用することが、耐熱性
、耐傷性向上の点から好ましい。
必要に応じて、A、B成分以外にも種々の成分(C成分
)を使用することができる。C成分としては、多価カル
ボン酸無水物および多価カルボン酸からなる群より選ば
れる少なくとも1種の化合物の使用することが、耐熱性
、耐傷性向上の点から好ましい。
【0029】多価カルボン酸無水物としては、無水イタ
コン酸、無水マレイン酸、無水コハク酸、無水シトラコ
ン酸、無水ドデセニルコハク酸、無水テトラヒドロフタ
ル酸、無水ヘキサヒドロフタル酸、無水メチルテトラヒ
ドロフタル酸、無水メチルヘキサヒドロフタル酸、無水
エンドメチレンテトラヒドロフタル酸、無水メチルエン
ドメチレンテトラヒドロフタル酸等の脂肪族ジカルボン
酸無水物;シクロペンタンテトラカルボン酸二無水物、
1,2,3,4−ブタンテトラカルボン酸二無水物等の
脂肪族多価カルボン酸二無水物;無水フタル酸、無水ト
リメリット酸、無水ピロメリット酸、無水ベンゾフェノ
ンテトラカルボン酸、3,3′,4,4′−ジフェニル
スルホンテトラカルボン酸二無水物等の芳香族多価カル
ボン酸無水物;エチレングリコールビストリメリテート
、グリセリントリストリメリテート等のエステル基含有
酸無水物などを挙げることができる。また多価カルボン
酸としては、イタコン酸、マレイン酸、コハク酸、シト
ラコン酸、テトラヒドロフタル酸、ヘキサヒドロフタル
酸、メチルテトラヒドロフタル酸、シクロペンタンテト
ラカルボン酸等の脂肪族多価カルボン酸;フタル酸、テ
レフタル酸、イソフタル酸、トリメリット酸、ピロメリ
ット酸、ベンゾフェノンテトラカルボン酸等の芳香族多
価カルボン酸などを挙げることができる。
コン酸、無水マレイン酸、無水コハク酸、無水シトラコ
ン酸、無水ドデセニルコハク酸、無水テトラヒドロフタ
ル酸、無水ヘキサヒドロフタル酸、無水メチルテトラヒ
ドロフタル酸、無水メチルヘキサヒドロフタル酸、無水
エンドメチレンテトラヒドロフタル酸、無水メチルエン
ドメチレンテトラヒドロフタル酸等の脂肪族ジカルボン
酸無水物;シクロペンタンテトラカルボン酸二無水物、
1,2,3,4−ブタンテトラカルボン酸二無水物等の
脂肪族多価カルボン酸二無水物;無水フタル酸、無水ト
リメリット酸、無水ピロメリット酸、無水ベンゾフェノ
ンテトラカルボン酸、3,3′,4,4′−ジフェニル
スルホンテトラカルボン酸二無水物等の芳香族多価カル
ボン酸無水物;エチレングリコールビストリメリテート
、グリセリントリストリメリテート等のエステル基含有
酸無水物などを挙げることができる。また多価カルボン
酸としては、イタコン酸、マレイン酸、コハク酸、シト
ラコン酸、テトラヒドロフタル酸、ヘキサヒドロフタル
酸、メチルテトラヒドロフタル酸、シクロペンタンテト
ラカルボン酸等の脂肪族多価カルボン酸;フタル酸、テ
レフタル酸、イソフタル酸、トリメリット酸、ピロメリ
ット酸、ベンゾフェノンテトラカルボン酸等の芳香族多
価カルボン酸などを挙げることができる。
【0030】これらの多価カルボン酸無水物および多価
カルボン酸は1種類ので用いて、2種類以上を組み合わ
せても良いが、芳香族多価カルボン酸無水物、芳香族多
価カルボン酸が耐熱性の点から好ましく、耐熱性と溶剤
に対する溶解性のバランスの点から無水トリメリット酸
が特に好ましい。
カルボン酸は1種類ので用いて、2種類以上を組み合わ
せても良いが、芳香族多価カルボン酸無水物、芳香族多
価カルボン酸が耐熱性の点から好ましく、耐熱性と溶剤
に対する溶解性のバランスの点から無水トリメリット酸
が特に好ましい。
【0031】多価カルボン酸無水物および多価カルボン
酸からなる群より選ばれる少なくとも1種の化合物等の
C成分を使用する場合は、A成分である共重合樹脂10
0重量部に対して5〜50重量部の範囲で使用すること
が好ましい。これより少ない場合は使用の十分な効果が
得にくく、多い場合はコーティング性、耐薬品性等が低
下する。
酸からなる群より選ばれる少なくとも1種の化合物等の
C成分を使用する場合は、A成分である共重合樹脂10
0重量部に対して5〜50重量部の範囲で使用すること
が好ましい。これより少ない場合は使用の十分な効果が
得にくく、多い場合はコーティング性、耐薬品性等が低
下する。
【0032】また、本発明の組成物に密着性を向上させ
るためにカップリング剤を添加することができる。カッ
プリング剤としては、官能性シランカップリング剤が好
ましくビニル基、メタクリロイル基、水酸基、カルボキ
シル基、アミノ基、イソシアネート基、エポキシ基等の
反応性置換基を有するシランカップリング剤、具体的に
はビニルトリメトキシシラン、ビニルトリエトキシシラ
ン、γ−メタクリロキシプロピルトリメトキシシラン、
γ−イソシアナートプロピルトリエトキシシラン、γ−
グリシドキシプロピルトリメトキシシラン等が挙げられ
、特にエポキシ基を有するシランカップリング剤が接着
性、耐溶剤性等に優れているため好ましい。これらの官
能性シランカップリング剤は、1種類のみで用いても、
2種類以上を組み合わせても良い。官能性シランカップ
リング剤の使用量は、A成分の共重合樹脂とB成分のエ
ポキシ樹脂との合計量を100重量部とした場合、0.
1〜10重量部の範囲が好ましく、これより少ないと使
用の効果が不十分となる傾向があり、多いと耐薬品性等
が低下する傾向がある。
るためにカップリング剤を添加することができる。カッ
プリング剤としては、官能性シランカップリング剤が好
ましくビニル基、メタクリロイル基、水酸基、カルボキ
シル基、アミノ基、イソシアネート基、エポキシ基等の
反応性置換基を有するシランカップリング剤、具体的に
はビニルトリメトキシシラン、ビニルトリエトキシシラ
ン、γ−メタクリロキシプロピルトリメトキシシラン、
γ−イソシアナートプロピルトリエトキシシラン、γ−
グリシドキシプロピルトリメトキシシラン等が挙げられ
、特にエポキシ基を有するシランカップリング剤が接着
性、耐溶剤性等に優れているため好ましい。これらの官
能性シランカップリング剤は、1種類のみで用いても、
2種類以上を組み合わせても良い。官能性シランカップ
リング剤の使用量は、A成分の共重合樹脂とB成分のエ
ポキシ樹脂との合計量を100重量部とした場合、0.
1〜10重量部の範囲が好ましく、これより少ないと使
用の効果が不十分となる傾向があり、多いと耐薬品性等
が低下する傾向がある。
【0033】本発明の組成物は、通常、溶剤に溶解して
塗布し、加熱硬化させることによって塗膜を形成させる
ことができる。溶剤としては、本発明の組成物を溶解し
、かつこれらの成分と反応しないものであれば、特に限
定されるものではない。具体的には、本発明のA成分で
ある共重合樹脂を、溶液重合させる際の溶媒として例示
した溶剤が挙げられる。これらの溶剤のうちエステル系
溶剤及びケトン系溶剤が好ましく、単独でまたは2種類
以上を混合して使用することができる。
塗布し、加熱硬化させることによって塗膜を形成させる
ことができる。溶剤としては、本発明の組成物を溶解し
、かつこれらの成分と反応しないものであれば、特に限
定されるものではない。具体的には、本発明のA成分で
ある共重合樹脂を、溶液重合させる際の溶媒として例示
した溶剤が挙げられる。これらの溶剤のうちエステル系
溶剤及びケトン系溶剤が好ましく、単独でまたは2種類
以上を混合して使用することができる。
【0034】本発明の組成物を溶剤に溶解して、組成物
溶液を調整する方法は特に限定されるものではなく、全
成分を同時に溶剤に溶解して組成物溶液を調整しても良
いし、必要に応じて各成分を適宜2つ以上の溶液として
おいて、使用時にこれらを混合して組成物溶液としても
よい。このようにして組成物溶液を調整する場合の溶剤
の使用量は、塗布に供せられる最終的な組成物溶液全量
のうちの50〜95重量%とすることが好ましい。50
重量%未満では固形分濃度が高すぎて塗膜のレベリング
性が低下したり、塗膜の透明性が低下したりする場合が
あり、一方95重量%を超える場合は固形分濃度が低す
ぎて塗膜の耐薬品性等が不十分となる場合がある。また
、本発明の組成物には必要に応じて、一般のエポキシ樹
脂の硬化に使用される硬化促進剤、酸化防止剤や紫外線
吸収剤等の安定剤等を透明性を損なわない程度に添加し
ても良い。
溶液を調整する方法は特に限定されるものではなく、全
成分を同時に溶剤に溶解して組成物溶液を調整しても良
いし、必要に応じて各成分を適宜2つ以上の溶液として
おいて、使用時にこれらを混合して組成物溶液としても
よい。このようにして組成物溶液を調整する場合の溶剤
の使用量は、塗布に供せられる最終的な組成物溶液全量
のうちの50〜95重量%とすることが好ましい。50
重量%未満では固形分濃度が高すぎて塗膜のレベリング
性が低下したり、塗膜の透明性が低下したりする場合が
あり、一方95重量%を超える場合は固形分濃度が低す
ぎて塗膜の耐薬品性等が不十分となる場合がある。また
、本発明の組成物には必要に応じて、一般のエポキシ樹
脂の硬化に使用される硬化促進剤、酸化防止剤や紫外線
吸収剤等の安定剤等を透明性を損なわない程度に添加し
ても良い。
【0035】本発明の組成物溶液を塗布する方法は特に
限定されず、浸漬法、スプレー法、ロールコート法、回
転塗布法等の他、スクリーン印刷、オフセット印刷等の
印刷による塗布方法等がある。本発明の組成物の加熱硬
化条件は組成物の各成分の具体的種類、配合割合等によ
って適宜選択されるが、通常50〜300℃で0.1〜
10時間、好ましくは100〜250℃で1〜5時間程
度である。
限定されず、浸漬法、スプレー法、ロールコート法、回
転塗布法等の他、スクリーン印刷、オフセット印刷等の
印刷による塗布方法等がある。本発明の組成物の加熱硬
化条件は組成物の各成分の具体的種類、配合割合等によ
って適宜選択されるが、通常50〜300℃で0.1〜
10時間、好ましくは100〜250℃で1〜5時間程
度である。
【0036】このようにして得られる本発明の組成物に
より形成されるコーティング膜はガラス、金属、プラス
チック等の種々の材料に対して優れた密着性を示し、平
滑、強靱で耐光性、耐熱性、耐水性、耐溶剤性、透明性
の優れているため、各種物品のコーティング膜として有
用である。特にカラーフィルタ保護膜としてゼラチン、
グリュー、ポリビニルアルコール、アクリル系樹脂等の
種々のバインダー樹脂を染料による染色や、顔料分散に
よって着色して得られる種々のカラーフィルタの表面保
護層、防染保護層として有用である。カラーフィルタ保
護膜として用いる場合は加熱硬化後の膜厚が0.05〜
30μm、好ましくは0.1〜10μm程度となるよう
に、適宜、塗布して用いることができる。
より形成されるコーティング膜はガラス、金属、プラス
チック等の種々の材料に対して優れた密着性を示し、平
滑、強靱で耐光性、耐熱性、耐水性、耐溶剤性、透明性
の優れているため、各種物品のコーティング膜として有
用である。特にカラーフィルタ保護膜としてゼラチン、
グリュー、ポリビニルアルコール、アクリル系樹脂等の
種々のバインダー樹脂を染料による染色や、顔料分散に
よって着色して得られる種々のカラーフィルタの表面保
護層、防染保護層として有用である。カラーフィルタ保
護膜として用いる場合は加熱硬化後の膜厚が0.05〜
30μm、好ましくは0.1〜10μm程度となるよう
に、適宜、塗布して用いることができる。
【0037】従来技術では、コーティング性、密着性、
耐熱性等の全ての要求特性を満足させるものは無かった
が、本発明の特定の構造の化合物の組み合わせにより、
これらの各要求特性をバランス良く満足させることが可
能となった。
耐熱性等の全ての要求特性を満足させるものは無かった
が、本発明の特定の構造の化合物の組み合わせにより、
これらの各要求特性をバランス良く満足させることが可
能となった。
【0038】
【実施例】以下実施例により本発明を具体的に説明する
が、本発明はこれら実施例によって限定されるものでは
ない。 実施例1 撹拌機、温度計、窒素導入管、還流冷却器、滴下ロート
の備わった1lフラスコにセロソルブアセテート(アセ
トキシエトキシエタン)100重量部を仕込みフラスコ
内を窒素置換した。N−フェニルマレイミド75重量部
、メタクリル酸イソボルニルエステル45重量部、メタ
クリル酸30重量部、アゾビスイソブチロニトリル0.
6重量部をセロソルブアセテート350重量部に溶解し
、前述の1lフラスコに窒素気流中80℃で3時間かけ
て滴下した。さらに80℃で5時間撹拌した後、120
℃に昇温して2時間保った。得られた共重合樹脂溶液は
粘度が33ポアズ(25℃)であり、不揮発分が25.
2重量%(180℃・1h、JIS C−2103に
準拠)、酸価32.5(mgKOH/g)であった。
が、本発明はこれら実施例によって限定されるものでは
ない。 実施例1 撹拌機、温度計、窒素導入管、還流冷却器、滴下ロート
の備わった1lフラスコにセロソルブアセテート(アセ
トキシエトキシエタン)100重量部を仕込みフラスコ
内を窒素置換した。N−フェニルマレイミド75重量部
、メタクリル酸イソボルニルエステル45重量部、メタ
クリル酸30重量部、アゾビスイソブチロニトリル0.
6重量部をセロソルブアセテート350重量部に溶解し
、前述の1lフラスコに窒素気流中80℃で3時間かけ
て滴下した。さらに80℃で5時間撹拌した後、120
℃に昇温して2時間保った。得られた共重合樹脂溶液は
粘度が33ポアズ(25℃)であり、不揮発分が25.
2重量%(180℃・1h、JIS C−2103に
準拠)、酸価32.5(mgKOH/g)であった。
【0039】この共重合樹脂溶液400重量部にクレゾ
ールノボラックエポキシ樹脂(日本化薬(株);EOC
N−102S,エポキシ当量214(g/eq)、軟化
点75℃)50重量部、無水トリメリット酸10重量部
、γ−グリシドキシプロピルトリメトキシシラン(東レ
・ダウコーニング・シリコーン(株);SH−6040
)1.6重量部、セロソルブアセテート375重量部を
加えて室温で均一に混合、溶解させた。得られた溶液は
粘度が40センチポアズ(25℃)であり不揮発分20
.2重量%(180℃・1h)であった。
ールノボラックエポキシ樹脂(日本化薬(株);EOC
N−102S,エポキシ当量214(g/eq)、軟化
点75℃)50重量部、無水トリメリット酸10重量部
、γ−グリシドキシプロピルトリメトキシシラン(東レ
・ダウコーニング・シリコーン(株);SH−6040
)1.6重量部、セロソルブアセテート375重量部を
加えて室温で均一に混合、溶解させた。得られた溶液は
粘度が40センチポアズ(25℃)であり不揮発分20
.2重量%(180℃・1h)であった。
【0040】この溶液を、孔径0.2μmのメンブラン
フィルターで濾過した後、スピンコーターを用いてガラ
ス板(ダウコーニング社 7059材、無アルカリガ
ラス)上に回転数2000rpmで回転塗布した。塗布
後ガラス板を180℃の恒温槽にて1時間加熱処理し、
塗膜を硬化させた。得られた塗膜の表面は極めて平滑で
あり、ピンホール等は全く見られなかった。二光速干渉
顕微鏡によって測定した膜厚は1.2μmであった。
フィルターで濾過した後、スピンコーターを用いてガラ
ス板(ダウコーニング社 7059材、無アルカリガ
ラス)上に回転数2000rpmで回転塗布した。塗布
後ガラス板を180℃の恒温槽にて1時間加熱処理し、
塗膜を硬化させた。得られた塗膜の表面は極めて平滑で
あり、ピンホール等は全く見られなかった。二光速干渉
顕微鏡によって測定した膜厚は1.2μmであった。
【0041】このようにして作製した塗膜について以下
の試験を行った。塗膜のガラス板との接着性を調べるた
めにテープ剥離によるゴバン目試験(JIS−K−54
00)を行った。その結果、残存数100/100であ
り、剥離は全く見られなかった。次に塗膜の400nm
〜800nmにおける吸収スペクトルを塗布したものと
同じガラス板をリファレンスとして測定したところ、光
線透過率は全領域で90%以上であった。
の試験を行った。塗膜のガラス板との接着性を調べるた
めにテープ剥離によるゴバン目試験(JIS−K−54
00)を行った。その結果、残存数100/100であ
り、剥離は全く見られなかった。次に塗膜の400nm
〜800nmにおける吸収スペクトルを塗布したものと
同じガラス板をリファレンスとして測定したところ、光
線透過率は全領域で90%以上であった。
【0042】また、この塗膜をつけたガラス板をプレッ
シャークッカーテスト(120℃2気圧)10時間後、
N−メチルピロリドン中に室温で30分浸漬後、5%水
酸化ナトリウム水溶液に室温で30分浸漬後、250℃
のギヤオーブン中に1時間放置後、それぞれ上記のゴバ
ン目試験及び光線透過率の測定を行ったが、いずれの場
合も接着性や光線透過率の低下は認められなかった。な
お、試験結果をまとめて表1に示す。
シャークッカーテスト(120℃2気圧)10時間後、
N−メチルピロリドン中に室温で30分浸漬後、5%水
酸化ナトリウム水溶液に室温で30分浸漬後、250℃
のギヤオーブン中に1時間放置後、それぞれ上記のゴバ
ン目試験及び光線透過率の測定を行ったが、いずれの場
合も接着性や光線透過率の低下は認められなかった。な
お、試験結果をまとめて表1に示す。
【0043】実施例2
撹拌機、温度計、窒素導入管、還流冷却器、滴下ロート
の備わった1lフラスコにセロソルブアセテート100
重量部を仕込みフラスコ内を窒素置換した。N−シクロ
ヘキシルマレイミド75重量部、メタクリル酸ノルボル
ニルエステル(メタクリル酸ビシクロ〔2.2.1〕ヘ
プト−2−イルエステル)45重量部、メタクリル酸3
0重量部、アゾビスイソブチロニトリル0.6重量部を
セロソルブアセテート350重量部に溶解し前述の1l
フラスコに窒素気流中80℃で3時間かけて滴下した。 さらに80℃で5時間撹拌した後、120℃に昇温して
2時間保った。
の備わった1lフラスコにセロソルブアセテート100
重量部を仕込みフラスコ内を窒素置換した。N−シクロ
ヘキシルマレイミド75重量部、メタクリル酸ノルボル
ニルエステル(メタクリル酸ビシクロ〔2.2.1〕ヘ
プト−2−イルエステル)45重量部、メタクリル酸3
0重量部、アゾビスイソブチロニトリル0.6重量部を
セロソルブアセテート350重量部に溶解し前述の1l
フラスコに窒素気流中80℃で3時間かけて滴下した。 さらに80℃で5時間撹拌した後、120℃に昇温して
2時間保った。
【0044】得られた共重合樹脂溶液400重量部にク
レゾールノボラックエポキシ樹脂(日本化薬(株)、E
OCN−102S)50重量部、無水トリメリット酸1
0重量部、γ−グリシドキシプロピルトリメトキシシラ
ン(東レ・ダウコーニング・シリコーン(株);SH−
6040)1.6重量部、セロソルブアセテート375
重量部を加えて室温で均一に混合溶解させた。得られた
溶液は粘度が48センチポアズ(25℃),不揮発分2
0.3重量%(180℃・1h)であった。得られた溶
液を実施例1と同様にしてガラス上に塗布、加熱硬化し
て塗膜の各種特性試験を行った。結果を表1に示す。
レゾールノボラックエポキシ樹脂(日本化薬(株)、E
OCN−102S)50重量部、無水トリメリット酸1
0重量部、γ−グリシドキシプロピルトリメトキシシラ
ン(東レ・ダウコーニング・シリコーン(株);SH−
6040)1.6重量部、セロソルブアセテート375
重量部を加えて室温で均一に混合溶解させた。得られた
溶液は粘度が48センチポアズ(25℃),不揮発分2
0.3重量%(180℃・1h)であった。得られた溶
液を実施例1と同様にしてガラス上に塗布、加熱硬化し
て塗膜の各種特性試験を行った。結果を表1に示す。
【0045】実施例3
撹拌機、温度計、窒素導入管、還流冷却器、滴下ロート
の備わった1lフラスコにセロソルブアセテート100
重量部を仕込みフラスコ内を窒素置換した。N−フェニ
ルマレイミド60重量部、メタクリル酸トリシクロ[5
,2,1,02′6]デカ−8−イルエステル(日立化
成工業(株)、FA−513M)60重量部、メタクリ
ル酸30重量部、アゾビスイソブチロニトリル0.6重
量部をセロソルブアセテート350重量部に溶解し前述
の1lフラスコに窒素気流中80℃で3時間かけて滴下
した。さらに80℃で5時間撹拌した後、120℃に昇
温して2時間保った。
の備わった1lフラスコにセロソルブアセテート100
重量部を仕込みフラスコ内を窒素置換した。N−フェニ
ルマレイミド60重量部、メタクリル酸トリシクロ[5
,2,1,02′6]デカ−8−イルエステル(日立化
成工業(株)、FA−513M)60重量部、メタクリ
ル酸30重量部、アゾビスイソブチロニトリル0.6重
量部をセロソルブアセテート350重量部に溶解し前述
の1lフラスコに窒素気流中80℃で3時間かけて滴下
した。さらに80℃で5時間撹拌した後、120℃に昇
温して2時間保った。
【0046】得られた共重合樹脂溶液400重量部にク
レゾールノボラックエポキシ樹脂(日本化薬(株)、E
OCN−102S)70重量部、無水トリメリット酸1
7.5重量部、γ−グリシドキシプロピルトリメトキシ
シラン(東レ・ダウコーニング・シリコーン(株)SH
−6040)1.9重量部、セロソルブアセテート45
0重量部を加えて室温で均一に混合溶解させた。得られ
た溶液は粘度が38センチポアズ(25℃),不揮発分
20.8重量%(180℃・1h)であった。得られた
溶液を実施例1と同様にしてガラス上に塗布、加熱硬化
して塗膜の各種特性試験を行った。結果を表1に示す。
レゾールノボラックエポキシ樹脂(日本化薬(株)、E
OCN−102S)70重量部、無水トリメリット酸1
7.5重量部、γ−グリシドキシプロピルトリメトキシ
シラン(東レ・ダウコーニング・シリコーン(株)SH
−6040)1.9重量部、セロソルブアセテート45
0重量部を加えて室温で均一に混合溶解させた。得られ
た溶液は粘度が38センチポアズ(25℃),不揮発分
20.8重量%(180℃・1h)であった。得られた
溶液を実施例1と同様にしてガラス上に塗布、加熱硬化
して塗膜の各種特性試験を行った。結果を表1に示す。
【0047】実施例4
撹拌機、温度計、窒素導入管、還流冷却器、滴下ロート
の備わった1lフラスコにセロソルブアセテート100
重量部を仕込みフラスコ内を窒素置換した。N−フェニ
ルマレイミド75重量部、メタクリル酸トリシクロ[5
,2,1,02′6]デカ−8−イルエステル(日立化
成工業(株)、FA−513M)45重量部、メタクリ
ル酸30重量部、アゾビスイソブチロニトリル0.6重
量部をセロソルブアセテート350重量部に溶解し前述
の1lフラスコに窒素気流中80℃で3時間かけて滴下
した。さらに80℃で5時間撹拌した後、120℃に昇
温して2時間保った。
の備わった1lフラスコにセロソルブアセテート100
重量部を仕込みフラスコ内を窒素置換した。N−フェニ
ルマレイミド75重量部、メタクリル酸トリシクロ[5
,2,1,02′6]デカ−8−イルエステル(日立化
成工業(株)、FA−513M)45重量部、メタクリ
ル酸30重量部、アゾビスイソブチロニトリル0.6重
量部をセロソルブアセテート350重量部に溶解し前述
の1lフラスコに窒素気流中80℃で3時間かけて滴下
した。さらに80℃で5時間撹拌した後、120℃に昇
温して2時間保った。
【0048】得られた共重合樹脂溶液400重量部にク
レゾールノボラックエポキシ樹脂(日本化薬(株)、E
OCN−102S)50重量部、無水トリメリット酸1
0重量部、γ−グリシドキシプロピルトリメトキシシラ
ン(東レ・ダウコーニング・シリコーン(株)SH−6
040)1.6重量部、セロソルブアセテート375重
量部を加えて室温で均一に混合溶解させた。得られた溶
液は粘度が43センチポアズ(25℃),不揮発分20
.1重量%(180℃・1h)であった。得られた溶液
を実施例1と同様にしてガラス上に塗布、加熱硬化して
塗膜の各種特性試験を行った。結果を表1に示す。
レゾールノボラックエポキシ樹脂(日本化薬(株)、E
OCN−102S)50重量部、無水トリメリット酸1
0重量部、γ−グリシドキシプロピルトリメトキシシラ
ン(東レ・ダウコーニング・シリコーン(株)SH−6
040)1.6重量部、セロソルブアセテート375重
量部を加えて室温で均一に混合溶解させた。得られた溶
液は粘度が43センチポアズ(25℃),不揮発分20
.1重量%(180℃・1h)であった。得られた溶液
を実施例1と同様にしてガラス上に塗布、加熱硬化して
塗膜の各種特性試験を行った。結果を表1に示す。
【0049】比較例1
クレゾールノボラックエポキシ樹脂(日本化薬(株)、
EOCN−102S)10重量部、無水トリメリット酸
3重量部、γ−グリシドキシプロピルトリメトキシシラ
ン(東レ・ダウコーニング・シリコーン(株)SH−6
040)0.1重量部、セロソルブアセテート40重量
部を室温で均一に混合溶解し、得られた溶液を実施例1
と同様にしてガラス上に塗布、加熱硬化して塗膜の各種
特性試験を行った。結果を表1に示す。
EOCN−102S)10重量部、無水トリメリット酸
3重量部、γ−グリシドキシプロピルトリメトキシシラ
ン(東レ・ダウコーニング・シリコーン(株)SH−6
040)0.1重量部、セロソルブアセテート40重量
部を室温で均一に混合溶解し、得られた溶液を実施例1
と同様にしてガラス上に塗布、加熱硬化して塗膜の各種
特性試験を行った。結果を表1に示す。
【0050】比較例2
ポリメタクリル酸グリシジル(ポリスチレン換算重量平
均分子量約80,000)6g、無水トリメリット酸0
.6g、γ−グリシドキシプロピルトリメトキシシラン
(東レ・ダウコーニング・シリコーン(株)SH−60
40)0.3g、セロソルブアセテート35重量部を加
えて室温で均一に混合溶解し、得られた溶液を実施例1
と同様にしてガラス上に塗布、加熱硬化して塗膜の各種
特性試験を行った。結果を表1に示す。
均分子量約80,000)6g、無水トリメリット酸0
.6g、γ−グリシドキシプロピルトリメトキシシラン
(東レ・ダウコーニング・シリコーン(株)SH−60
40)0.3g、セロソルブアセテート35重量部を加
えて室温で均一に混合溶解し、得られた溶液を実施例1
と同様にしてガラス上に塗布、加熱硬化して塗膜の各種
特性試験を行った。結果を表1に示す。
【0051】
【表1】
【0052】実施例5
実施例1〜4で形成した塗膜の表面硬度を鉛筆硬さ(J
IS K−5400)により測定した。結果を表2に
示す。
IS K−5400)により測定した。結果を表2に
示す。
【0053】
【表2】
【0054】実施例6
実施例1〜4で調製した組成物溶液を用いてカラーフィ
ルタ基材への適性を調べた。試験法としては一般的に知
られている方法でカラーフィルタ基材を作製し、この基
材上への塗布性と耐熱性を調べた。カラーフィルタ基材
の作製はまず透明ガラス基板上にゼラチン−重クロムア
ンモニウム(10:1、重量比)の水溶液を乾燥後の膜
厚が1μmとなるように回転塗布した後、80℃で10
分間乾燥し、得られた塗膜に紫外線を照射した後、純水
で現像することにより、染色基質層を得た。これを下記
の赤色染色浴に浸漬し、水洗後、150℃で30分間乾
燥することにより、赤色に染色されたカラーフィルタ基
材を形成した。 染色浴 スミノール・ミリングレッドRS(住友化学(株)
製) 2g 酢酸
3g 蒸留水
100g
ルタ基材への適性を調べた。試験法としては一般的に知
られている方法でカラーフィルタ基材を作製し、この基
材上への塗布性と耐熱性を調べた。カラーフィルタ基材
の作製はまず透明ガラス基板上にゼラチン−重クロムア
ンモニウム(10:1、重量比)の水溶液を乾燥後の膜
厚が1μmとなるように回転塗布した後、80℃で10
分間乾燥し、得られた塗膜に紫外線を照射した後、純水
で現像することにより、染色基質層を得た。これを下記
の赤色染色浴に浸漬し、水洗後、150℃で30分間乾
燥することにより、赤色に染色されたカラーフィルタ基
材を形成した。 染色浴 スミノール・ミリングレッドRS(住友化学(株)
製) 2g 酢酸
3g 蒸留水
100g
【0055】次に
、このカラーフィルター基材上に前記組成物溶液を2,
000rpmで回転塗布し、180℃で1時間乾燥する
ことにより保護層を形成した。このようにして作製され
た保護層つきカラーフィルタ上に、インジウムチンオキ
シド(ITO)を常法に従い蒸着した後、ホトリソグラ
フィーによりパターニングした。このITOのパターン
を有するカラーフィルタを光学顕微鏡で詳細に観察した
が、カラーフィルターや保護膜にシワやクラック等は全
く認められず、カラーフィルターと保護膜との接着性、
密着性も良好であった。
、このカラーフィルター基材上に前記組成物溶液を2,
000rpmで回転塗布し、180℃で1時間乾燥する
ことにより保護層を形成した。このようにして作製され
た保護層つきカラーフィルタ上に、インジウムチンオキ
シド(ITO)を常法に従い蒸着した後、ホトリソグラ
フィーによりパターニングした。このITOのパターン
を有するカラーフィルタを光学顕微鏡で詳細に観察した
が、カラーフィルターや保護膜にシワやクラック等は全
く認められず、カラーフィルターと保護膜との接着性、
密着性も良好であった。
【0056】
【発明の効果】実施例から明らかなように本発明のコー
ティング用樹脂組成物により形成される塗膜は、平滑で
あり、透明性、接着性、耐水性、耐薬品性、耐熱性、耐
傷性等に極めて優れており、各種物品のコーティング材
、特にカラーフィルタ保護膜材として有用である。
ティング用樹脂組成物により形成される塗膜は、平滑で
あり、透明性、接着性、耐水性、耐薬品性、耐熱性、耐
傷性等に極めて優れており、各種物品のコーティング材
、特にカラーフィルタ保護膜材として有用である。
Claims (5)
- 【請求項1】 A.(1)N置換マレイミド、(2)
炭素数6〜20の脂環式構造を有する脂環式アクリル酸
エステルおよび/または脂環式メタクリル酸エステル、
(3)アクリル酸および/またはメタクリル酸ならびに
(4)必要により(1)、(2)および/または(3)
と共重合可能な不飽和単量体を共重合してなる共重合樹
脂と B.分子内にエポキシ基を2以上有するエポキシ樹脂と
を含有してなるコーティング用樹脂組成物。 - 【請求項2】 さらに、C.多価カルボン酸無水物お
よび多価カルボン酸からなる群より選ばれる少なくとも
1種の化合物を含有してなる請求項1記載のコーティン
グ用樹脂組成物。 - 【請求項3】 N置換マレイミドが、Nメチルマレイ
ミド、Nエチルマレイミド、Nプロピルマレイミド、N
ブチルマレイミド、Nシクロヘキシルマレイミド、Nフ
ェニルマレイミドおよびNアルキル基置換フェニルマレ
イミドからなる群より選ばれる少なくとも1種の化合物
である請求項1または2記載のコーティング樹脂組成物
。 - 【請求項4】 エポキシ樹脂が、フェノールノボラッ
クエポキシ樹脂およびクレゾールノボラックエポキシ樹
脂からなる群より選ばれる少なくとも1種の化合物であ
る請求項1、2または3記載のコーティング用樹脂組成
物。 - 【請求項5】 請求項1、2、3または4記載のコー
ティング用樹脂組成物を含有してなるカラーフィルタ保
護膜用樹脂組成物。