JPH04109137U - 複合基材 - Google Patents
複合基材Info
- Publication number
- JPH04109137U JPH04109137U JP1975191U JP1975191U JPH04109137U JP H04109137 U JPH04109137 U JP H04109137U JP 1975191 U JP1975191 U JP 1975191U JP 1975191 U JP1975191 U JP 1975191U JP H04109137 U JPH04109137 U JP H04109137U
- Authority
- JP
- Japan
- Prior art keywords
- base material
- resin
- fiberboard
- impregnated
- composite base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【目的】 低密度のファイバーボードの表面を樹脂含浸
処理と樹脂含浸紙の被覆により表面強度の向上を図る。 【構成】 密度０．２５〜０．４０のファイバーボード
２の片面又は両面に、フェノール樹脂初期縮合物などの
熱硬化性樹脂３を含浸処理及び含浸紙の積層被覆をした
複合基材。
処理と樹脂含浸紙の被覆により表面強度の向上を図る。 【構成】 密度０．２５〜０．４０のファイバーボード
２の片面又は両面に、フェノール樹脂初期縮合物などの
熱硬化性樹脂３を含浸処理及び含浸紙の積層被覆をした
複合基材。
Description
【０００１】
本考案は、軽量で表面強度が優れている木質系の複合基材に関する。
【０００２】
ファイバーボードは断熱材、家具芯材、吸着材等、多用途に広く利用されてい
る。しかし、特に密着０．４５ｇ／cm3未満の軽量なファイバーボードにあって
は、強度が弱く、表面あれが生じやすい。塗料の吸収が不均一であり、塗装性が
悪い等の欠点がある。
【０００３】
本考案が解決しようとする問題点は、軽量な基材でかつ、表面強度が強く、表
面あれがなく、塗料を吸収しないボードを提供するものである。
【０００４】
本考案では、密度０．２５〜０．４０ｇ／cm3のファイバーボードの片面また
は両面に、熱硬化性樹脂が含浸処理してあると共に、該含浸処理面に樹脂含浸処
理紙が積層被覆してあることを特徴とする複合基材である。
【０００５】
本考案で使用するファイバーボード（２）からなる基材は木材チップ、パルプ
くず、稲ワラ、綿くず、このくず等の原材料を蒸煮解繊し、ワックス系サイズ剤
、ロジン系サイズ剤等を添加した後、抄造し、連続乾燥装置で乾燥して調整され
たもので、一般にインシュレーションボードと称されるものをいう。適合する材
質としては密度０．２５ｇ／cm3以上、０．４０ｇ／cm3未満のものが好ましい。
密度０．２５ｇ／cm3未満の材質では強度が弱く、密度０．４０ｇ／cm3以上の材
質では初期縮合物の該基材への浸透が不十分になり好ましくない。
【０００６】
該ファイバーボード（２）の片面または両面に含浸処理される熱硬化性樹脂と
しては、メラミン樹脂、フェノール樹脂、尿素樹脂、ウレタン樹脂、エポキシ樹
脂、不飽和ポリエステル等の初期縮合物ないしはプレポリマーが使用される。こ
れらは単独もしくは硬化剤とともに使用される。
【０００７】
該基材に対し熱硬化性樹脂を含浸処理するには、熱硬化性樹脂又はその溶液に
該基材を浸漬したのち、乾燥機中において水、有機溶剤等の溶媒を揮発して得ら
れた処理基材の片面又は両面に樹脂含浸紙を所要枚数積層し、離型フィルム、鏡
面板等を用いて常法により、加熱、加圧して成型する。
【０００８】
本考案で用いられる樹脂含浸紙（３）としては、紙、布、不織布等の多孔質シ
ート基材に前述の如き、熱硬化性樹脂を塗布あるいは含浸し、乾燥したものであ
る。
【０００９】
なお、樹脂含浸率としては、基材（ファイバーボード（２））に対して２０重
量％以上、樹脂含浸紙（３）は多孔質シート基材に対して１００重量％以上が適
当で、少なすぎると成形素材相互の密着性が劣り、層間の剥離の原因になり、表
面強度が低下する。
【００１０】
本考案による複合基材はファイバーボードの表面及び繊維間に熱硬化性樹脂が
固着して仕上げられているため、軽量で、なおかつ強度が著しく向上し、塗料の
吸い込みもないので、塗装性も改善されている。また、熱圧で一体成型されてい
るため、表面は平滑に仕上げられている。
以下に実施例と比較例をあげて説明する。
【００１１】
実施例１
密度０．２８ｇ／cm3のＪＩＳ Ａ−５９０５Ａ級インシュレーションボードに
相当するファイバーボードを、ホルマリンとフェノールのモル比率１．２：１の
割合で、苛性ソーダでＰＨ＝８に調整し反応した樹脂分５３％フェノール樹脂初
期縮合物の満たされた開放容器中に２０秒間浸漬したのち取りだし、１００℃で
３０分間乾燥させた基材に、さらしクラフトパルプ（坪量１２５ｇ／m2、密度０
．５ｇ／cm3）にフェノール樹脂初期縮合物を樹脂量１２０％となるように含浸
・乾燥した樹脂含浸紙を表面と裏面にそれぞれ１枚ずつ被覆し、１４０℃、圧力
４．５kgt／cm2で３０分間加熱圧締して硬化させた複合基材とした。
【００１２】
比較例１
密度０．２８ｇ／cm3のＪＩＳ Ａ−５９０５Ａ級インシュレーションボードに
相当するファイバーボードとした。
【００１３】
次に、実施例１と比較例１のボードの曲げ強さ、表面あれ、塗料の吸収を試験
した。
試験方法の概略は次のごとくである。
【００１４】
［曲げ強さ］ＪＩＳ Ａ−５９０５「曲げ強さ試験方法」に準ずる。２支点間
（Ｌcm）に幅（ｂcm）、厚さ（ｔcm）の試片を置き、２支点間の中央に荷重を加
え、破断時の最大荷重（Ｐkgf）を測定し、数式１により曲げ強さを求める。
【００１５】
【数式１】
【００１６】
［表面あれ］試片の表面に粘着テープを圧着後、粘着テープをゆっくり剥離し
、剥離後の試片の表面あれ状況を観察する。
【００１７】
［塗料の吸収］試片の表面にラッカースプレーで塗装を行ない、乾燥後の塗料
の吸収状況を観察する。測定結果を表１に示す。
【００１８】
【表１】
【図面の簡単な説明】
【図１】本考案による複合基材の斜視断面図である。
１ 複合基材
２ ファイバーボード
３ 熱硬化性樹脂層
Claims (1)
- 【請求項１】 密度０．２５〜０．４０ｇ／cm3のファ
イバーボードの片面または両面に、熱硬化性樹脂が含浸
処理してあると共に、該含浸処理面に樹脂含浸紙が積層
被覆してあることを特徴とする複合基材。