JP7512647B2 - 加飾フィルム及び加飾成形体 - Google Patents
加飾フィルム及び加飾成形体 Download PDFInfo
- Publication number
- JP7512647B2 JP7512647B2 JP2020062892A JP2020062892A JP7512647B2 JP 7512647 B2 JP7512647 B2 JP 7512647B2 JP 2020062892 A JP2020062892 A JP 2020062892A JP 2020062892 A JP2020062892 A JP 2020062892A JP 7512647 B2 JP7512647 B2 JP 7512647B2
- Authority
- JP
- Japan
- Prior art keywords
- decorative
- layer
- resin
- decorative film
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
具体的に、本発明は、以下の構成を有する。
接着層は、イソペンタン由来構造から構成されるブロックを含むブロック共重合体と、テルペンフェノール系樹脂と、スチレン系樹脂と、を含有する加飾フィルム。
[2] 23℃、相対湿度50%、かつ下記測定条件で測定されるプローブタックのピーク値が1.0N/5mmφ以下である、[1]に記載の加飾フィルム;
(プローブタック値の測定条件)
測定機器:タッキング試験機 TAC1000(株式会社レスカ製)
プローブ直径:5mmφ
プローブ材質:SUS304
プローブ温度:50℃
ステージ温度:50℃
プローブ押付け荷重:200gf
プローブ押付けおよび引き剥がし速度:1mm/秒
プローブ押付け保持時間:60秒。
[3] ブロック共重合体は、
イソペンタン由来構造から構成されるブロック及びスチレン系ポリマーから構成されるブロックを含むブロック共重合体である、[1]又は[2]に記載の加飾フィルム。
[4] テルペンフェノール系樹脂の軟化点は125~170℃であり、
テルペンフェノール系樹脂の数平均分子量は800~1500である、[1]~[3]のいずれかに記載の加飾フィルム。
[5] テルペンフェノール系樹脂の含有量は、ブロック共重合体100質量部に対して、40~200質量部である、[1]~[4]のいずれかに記載の加飾フィルム。
[6] 接着層の厚みは、0.5~20μmである、[1]~[5]のいずれかに記載の加飾フィルム。
[7] 加飾フィルムは、フィルムインサート成形法又はインモールド成形法による被着体加飾用である、[1]~[6]のいずれかに記載の加飾フィルム。
[8] [1]~[7]のいずれかに記載の加飾フィルムを、ポリプロピレン樹脂を含む被着体に貼合してなる加飾成形体。
[9] 自動車部材、電子機器又は建材用である、[8]に記載の加飾成形体。
本発明は、加飾層と、接着層とを有する加飾フィルムに関する。ここで、接着層は、イソペンタン由来構造から構成されるブロックを含むブロック共重合体と、テルペンフェノール系樹脂と、スチレン系樹脂と、を含有する。本発明の加飾フィルムは、上記構成を有するため、ポリプロピレン樹脂を含む被着体に対して優れた密着性を発揮する。このため、本発明の加飾フィルムは、ポリプロピレン樹脂を主成分として含む被着体への貼合用として好ましく用いられる。また、本発明の加飾フィルムは、上記構成を有するため、耐ブロッキング性にも優れている。このため、本発明の加飾フィルム同士を剥離フィルムを介さずに積層したり、加飾フィルムをロール状の巻回体とした場合であっても、使用時には各加飾フィルムを容易に引き剥がすことができる。
(プローブタック値の測定条件)
測定機器:タッキング試験機 TAC1000(株式会社レスカ製)
プローブ直径:5mmφ
プローブ材質:SUS304
プローブ温度:50℃
ステージ温度:50℃
プローブ押付け荷重:200gf
プローブ押付けおよび引き剥がし速度:1mm/秒
プローブ押付け保持時間:60秒
プローブタックのピーク値が上記範囲内であれば、加飾フィルム同士を剥離フィルムを介さずに積層したり、ロール状に巻回した場合の耐ブロッキング性をより効果的に高めることができる。
なお、本発明の加飾フィルムをフィルムインサート成形に用いる場合は、加飾層21の最表層(接着層11と接する逆面)には加飾性層とは別にハードコート層や反射防止層などの機能層を設けていてもよい。
一方で、本発明の加飾フィルムをインモールド成形に用いる場合は、加飾層21の加飾性層は必ず接着層11と接する面に設けられ、成形後に基材と加飾性層が容易に剥がれるように離型性を有する基材を用いるか、もしくは、基材と加飾性層の間に離型層を設けることで、基材(離型層)と加飾性層とが接するように構成されていることが好ましい。
加飾フィルムは、接着層を有する。本発明において、接着層は、加飾層の両面に設けられていてもよいが、加飾層のいずれか一方の面に一層設けられていることが好ましい。
加飾フィルムは、加飾層を有する。ここで、加飾層は、基材に顔料や染料が練りこまれた単層の着色フィルムであってもよい。また、加飾層は、基材と加飾性層を含む多層フィルムであってもよい。
(1)基材層のみからなる構成(着色フィルムなど基材に顔料や染料が練りこまれている)(一般的にこの構成はフィルムインサート成形に用いられインモールド成形には用いられない)
(2)基材層、印刷層、印刷保護層がこの順で設けられた構成
(3)表面保護層、印刷層、基材層がこの順で設けられた構成
(4)基材層、印刷層がこの順で設けられた構成
(5)機能層、基材層、印刷層がこの順で設けられた構成
(一般的にこの構成はフィルムインサート成形に用いられインモールド成形には用いられない)
(6)基材層、離型層、印刷保護層、印刷層がこの順で設けられた構成
(一般的にこの構成はインモールド成形に用いられフィルムインサート成形には用いられない)
(7)上述した(1)~(6)の構成の最表面にさらにプロテクトフィルムが設けられた構成
(8)上述した(1)~(6)の構成の最表面にさらに粘着剤層及びセパレーター層が設けられた構成
本発明の加飾フィルムの製造方法は、加飾層上に、接着剤組成物を塗工し、乾燥又は硬化させることで、接着層を形成する工程を含む。
本発明は、加飾フィルムを、ポリプロピレン樹脂を含む被着体に貼合してなる加飾成形体に関するものでもある。なお、加飾成形体においては、被着体と、少なくとも加飾フィルム(又はインモールド成形の場合は加飾層)が接着層を介して一体化した状態であり、被着体の表面の少なくとも一部が加飾フィルム(又は加飾層)によって被覆された状態である。
加飾成形体の製造方法は、加飾フィルムを被着体に貼合する工程を含むことが好ましい。加飾成形体の製造方法としては、例えば、熱プレス成形、インモールド成形、フィルムインサート成形、真空条件下又は減圧条件下における成形等を挙げることができる。中でも、加飾成形体の製造方法は、フィルムインサート成形法又はインモールド成形法であることが好ましく、上述した加飾フィルムは、フィルムインサート成形法又はインモールド成形法における加飾成形用に適した加飾フィルムである。
接着剤組成物(A-1)
下記構造式で表される構造を有するブロック共重合体(クラレ社製、セプトン1020)100質量部、テルペンフェノール樹脂(ヤスハラケミカル社製、YS ポリスター T130、軟化点130℃、分子量900)60質量部、ポリスチレン樹脂(三井化学社製、FTR8100、分子量800)30質量部、酸化防止剤(BASF社製、IRGANOX1010)0.6質量部を、固形分濃度が30質量%になるようにトルエンに溶解して接着剤組成物(A-1)を得た。
ブロック共重合体として下記構造式で表される構造を有する樹脂(クラレ社製、セプトン2002)を使用した以外は接着剤組成物(A-1)の作製方法と同様にして固形分濃度30質量%の接着剤組成物(A-2)を得た。
ブロック共重合体として下記構造式で表される構造を有する樹脂(クラレ社製、セプトン4033)を使用した以外は接着剤組成物(A-1)の作製方法と同様にして固形分濃度30質量%の接着剤組成物(A-3)を得た。
テルペンフェノール樹脂(ヤスハラケミカル社製、YS ポリスター T130、軟化点130℃、分子量900)の添加量を160質量部に変更した以外は接着剤組成物(A-3)の作製方法と同様にして固形分濃度30質量%の接着剤組成物(A-4)を得た。
テルペンフェノール樹脂(ヤスハラケミカル社製、YS ポリスター T130、軟化点130℃、分子量900)を、テルペンフェノール系樹脂(ヤスハラケミカル社製、YS ポリスター T160、軟化点160℃、分子量1300)に変更した以外は接着剤組成物(A-3)の作製方法と同様にして固形分濃度30質量%の接着剤組成物(A-5)を得た。
ポリスチレン樹脂(三井化学社製、FTR8100、分子量800)を、ポリスチレン樹脂(三井化学社製、FTR2140 分子量1900)に変更した以外は接着剤組成物(A-3)の作製方法と同様にして固形分濃度30質量%の接着剤組成物(A-6)を得た。
イソペンタン由来構造を有するブロック共重合体の代わりに、イソペンタン由来構造を有さない下記構造式で表される水添ポリブタジエン系樹脂(クラレ社製、セプトン8004)を使用した以外は接着剤組成物(A-1)の作製方法と同様にして固形分濃度30質量%の接着剤組成物(B-1)を得た。
テルペンフェノール系樹脂を添加しなかった以外は接着剤組成物(A-3)の作製方法と同様にして固形分濃度30質量%の接着剤組成物(B-2)を得た。
スチレン系樹脂を添加しなかった以外は接着剤組成物(A-3)の作製方法と同様にして固形分濃度30質量%の接着剤組成物(B-3)を得た。
テルペンフェノール系樹脂の代わりにテルペン樹脂(ヤスハラケミカル社製、YS レジンPX1250 、軟化点125℃、分子量1100)に変更した以外は接着剤組成物(A-3)の作製方法と同様にして固形分濃度30質量%の接着剤組成物(B-4)を得た。
(実施例1)
上記で作製した接着剤組成物(A-1)を、ナイフコーターを用いてアクリルフィルム(クラレ社製、パラピュア HIグレード 75μm)に、乾燥後の接着層の厚みが5μmとなるように塗工した後、100℃で3分間乾燥して溶剤のトルエンを揮発乾燥させた。このようにして、接着層を有する加飾フィルムを得た。
接着剤組成物(A-1)を接着剤組成物(A-2)に変更した以外は、実施例1と同様にして加飾フィルムを得た。
接着剤組成物(A-1)を接着剤組成物(A-3)に変更した以外は、実施例1と同様にして加飾フィルムを得た。
接着剤組成物(A-1)を接着剤組成物(A-4)に変更した以外は、実施例1と同様にして加飾フィルムを得た。
接着剤組成物(A-1)を接着剤組成物(A-5)に変更した以外は、実施例1と同様にして加飾フィルムを得た。
接着剤組成物(A-1)を接着剤組成物(A-6)に変更した以外は、実施例1と同様にして加飾フィルムを得た。
乾燥後の接着層の厚みを1μmに変更した以外は、実施例3と同様にして加飾フィルムを得た。
乾燥後の接着層の厚みを20μmに変更した以外は、実施例3と同様にして加飾フィルムを得た。
接着剤組成物(A-1)を接着剤組成物(B-1)に変更した以外は、実施例1と同様にして加飾フィルムを得た。
接着剤組成物(A-1)を接着剤組成物(B-2)に変更した以外は、実施例1と同様にして加飾フィルムを得た。
接着剤組成物(A-1)を接着剤組成物(B-3)に変更した以外は、実施例1と同様にして加飾フィルムを得た。
接着剤組成物(A-1)を接着剤組成物(B-4)に変更した以外は、比較例1と同様にして加飾フィルムを得た。
各実施例及び比較例で得た加飾フィルムを用いて、以下の方法で評価した。
まず加飾フィルムを50mm×50mmのサイズに切り出したものをタッキング試験機TAC1000(株式会社レスカ製)のステージの上に接着剤層が上(プローブ側)になるようにセットして以下の条件で位置を変えて5回測定して、平均値を算出した
<測定条件>
プローブ直径:5mmφ
プローブ材質:SUS304
プローブ温度:50℃
ステージ温度:50℃
プローブ押付け荷重:200gf
プローブ押付けおよび引き剥がし速度:1mm/秒
プローブ押付け保持時間:60秒
<加飾成形体の作製>
各実施例及び比較例で得た加飾フィルムを用いてフィルムインサート成形法により加飾成形体を作製した。まず、成形品の大きさが100mm×100mm×2mmの板状となる金型の内側に、接着層が射出樹脂側になるように加飾フィルムをセットした。続いて加飾フィルムをセットした金型を60℃に加温した後、200℃に加熱溶融したポリプロピレン(三菱ケミカル社製、ノバテックTMPP)を金型に流し込み、室温まで冷却してから加飾成形体を金型より取り出すことで加飾成形体を得た。
<評価>
上記で作製した加飾成形体を23℃、相対湿度50%の環境下で24時間養生した後、加飾フィルムとポリプロピレン樹脂被着体の密着性をJIS K 5600-5-6に準拠し評価した。具体的には、以下のようにしてクロスカット法による密着試験を行った。
まず、加飾フィルム側からかみそりを用いて1mm×1mmの碁盤目が100マスできるように切込みを入れた後、セロハンテープ(ニチバン社製、CT28)を指で上から押し付けるようにして加飾フィルムに密着させた後に剥離した。100マスの内、全てのマス目で加飾フィルムが剥離していない場合を100/100、全てのマス目で剥離している場合を0/100とし、加飾フィルムが剥離していないマス目を数え、以下の評価基準にて加飾フィルムの密着性を評価した。
A:80/100~100/100
B:50/100~79/100
C:0/100~49/100
各実施例及び比較例で得た加飾フィルムを用いて、以下の方法で評価した。まず加飾フィルムを20mm×20mmのサイズに切り出したもの10枚作製した。この加飾フィルムを加飾層と接着層が接するように10枚重ね、50mm×50mm×2mm厚のソーダガラス2枚の間に挟み1kgの錘を乗せて、50℃の恒温層で24時間処理した。
次いで恒温層から取り出して錘を乗せた状態で23℃、相対湿度50%の環境下に24時間静置した後、錘とガラス板を除去して10枚の加飾フィルム同士がブロッキングしていないか以下の基準で評価した。
A:全ての加飾フィルムが問題なく剥がれる
B:10枚中1枚以上剥がれないものがある
11 接着層
30 加飾フィルム
50 被着体
100 加飾成形体
Claims (8)
- 加飾層と、接着層とを有する加飾フィルムであって、
前記接着層は、イソペンタン由来構造から構成されるブロックを含むブロック共重合体と、粘着付与剤と、を含有し、
前記粘着付与剤は、テルペンフェノール系樹脂及びスチレン系樹脂を含み、
前記テルペンフェノール系樹脂の含有量は、前記ブロック共重合体100質量部に対して、40~200質量部であり、
前記スチレン系樹脂の含有量は、ブロック共重合体100質量部に対して、10~60質量部である、加飾フィルム。 - 23℃、相対湿度50%、かつ下記測定条件で測定されるプローブタックのピーク値が1.0N/5mmφ以下である、請求項1に記載の加飾フィルム;
(プローブタック値の測定条件)
測定機器:タッキング試験機 TAC1000(株式会社レスカ製)
プローブ直径:5mmφ
プローブ材質:SUS304
プローブ温度:50℃
ステージ温度:50℃
プローブ押付け荷重:200gf
プローブ押付けおよび引き剥がし速度:1mm/秒
プローブ押付け保持時間:60秒。 - 前記ブロック共重合体は、
イソペンタン由来構造から構成されるブロック及びスチレン系ポリマーから構成されるブロックを含むブロック共重合体である、請求項1又は2に記載の加飾フィルム。 - 前記テルペンフェノール系樹脂の軟化点は125~170℃であり、
前記テルペンフェノール系樹脂の数平均分子量は800~1500である、請求項1~3のいずれか1項に記載の加飾フィルム。 - 前記接着層の厚みは、0.5~20μmである、請求項1~4のいずれか1項に記載の加飾フィルム。
- 前記加飾フィルムは、フィルムインサート成形法又はインモールド成形法による被着体加飾用である、請求項1~5のいずれか1項に記載の加飾フィルム。
- 請求項1~6のいずれか1項に記載の加飾フィルムを、ポリプロピレン樹脂を含む被着体に貼合してなる加飾成形体。
- 自動車部材、電子機器又は建材用である、請求項7に記載の加飾成形体。