JP7456793B2 - 樹脂組成物および積層体 - Google Patents
樹脂組成物および積層体 Download PDFInfo
- Publication number
- JP7456793B2 JP7456793B2 JP2020017930A JP2020017930A JP7456793B2 JP 7456793 B2 JP7456793 B2 JP 7456793B2 JP 2020017930 A JP2020017930 A JP 2020017930A JP 2020017930 A JP2020017930 A JP 2020017930A JP 7456793 B2 JP7456793 B2 JP 7456793B2
- Authority
- JP
- Japan
- Prior art keywords
- polyethylene
- resin
- resin composition
- mass
- molecular weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記ポリエチレン(A)が下記要件(a-1)を満たし、
前記ポリエチレン(B)が下記要件(b-1)を満たし、
前記ポリエチレン樹脂(C)が下記要件(c-1)を満たし、
前記変性ポリオレフィン樹脂(D)の含有量が、前記ポリエチレン樹脂(C)100質量部に対して0.01~1.5質量部の範囲である、樹脂組成物(E):
(a-1)135℃のデカリン溶媒中で測定した極限粘度[η]が10~40dl/gである;
(b-1)135℃のデカリン溶媒中で測定した極限粘度[η]が0.1~5dl/gである;
(c-1)密度が920~970kg/m3である。
[3] 前記オルガノポリシロキサンの含有量が、前記ポリエチレン樹脂(C)100質量部に対して0.1~20質量部である、項[1]または[2]に記載の樹脂組成物(E)。
[5] JIS B0601-1994に準拠して測定された、前記第2の層の表面粗さが0.5~4.0μmである、項[4]に記載の積層体。
[6] 温度23℃および湿度50%の条件で測定された、前記第2の層の表面の動摩擦係数が0.4以下である、項[4]または[5]に記載の積層体。
本発明の樹脂組成物(E)は、特定のポリエチレン樹脂(C)、変性ポリオレフィン樹脂(D)およびオルガノポリシロキサンを含有し、前記変性ポリオレフィン樹脂(D)の含有量が、前記ポリエチレン樹脂(C)100質量部に対して0.01~1.5質量部である。
前記ポリエチレン樹脂(C)は、特定の超高分子量ポリエチレン(A)(以下、単に「ポリエチレン(A)」ともいう。)0.1~5質量%、好ましくは0.5~4.8質量%、より好ましくは1.0~4.5質量%と、特定の低分子量ないし高分子量ポリエチレン(B)(以下、単に「ポリエチレン(B)」ともいう。)99.9~95質量%、好ましくは99.5~95.2質量%、より好ましくは99.0~95.5質量%(ただし、ポリエチレン(A)とポリエチレン(B)の合計量を100質量%とする。)とを含み、かつ、下記要件(c-1)を満たす。なお、ポリエチレン(A)およびポリエチレン(B)は、後述する変性ポリオレフィン樹脂(D)とは異なる。
前記ポリエチレン(A)は、下記要件(a-1)を満たす。
要件(a-1):135℃のデカリン溶媒中で測定した極限粘度[η]が10~40dl/g、好ましくは10~35dl/g、より好ましくは12.5~35dl/gである。
前記ポリエチレン(B)は、下記要件(b-1)を満たす。また、前記ポリエチレン(B))は、下記要件(b-2)をさらに満たすことが好ましい。
要件(b-2):密度(ASTM D1505に準拠)が915~966kg/m3、好ましくは915~953kg/m3、より好ましくは920~953kg/m3である。
前記ポリエチレン(B)を使用することにより、超高分子量ポリエチレンの性質を持ち、かつ、柔軟性を合わせ持つ樹脂組成物(E)を得ることができる。
前記変性ポリオレフィン樹脂(D)は、オレフィン由来の構造単位を主成分として含み、かつヘテロ原子を含む官能基(以下、単に「官能基」ともいう。)を有する構造単位を、好ましくは0.1~10質量%、より好ましくは0.5~5質量%の割合で含む重合体である。この割合は、たとえば国際公開第2015/011935号の[0067]~[0071]に記載の方法で特定することができる。
変性ポリオレフィン樹脂(D)の製造方法の一例として、未変性のオレフィン重合体を変性剤(たとえば、不飽和カルボン酸およびその誘導体)でグラフト変性させる方法が挙げられる。
本発明において用いられるオルガノポリシロキサンとしては、具体的には、ジメチルポリシロキサン、メチルフェニルポリシロキサン、フルオロポリシロキサン、テトラメチルテトラフェニルポリシロキサン、メチルハイドロジェンポリシロキサンなど、あるいはエポキシ変性、アルキル変性、アミノ変性、カルボキシル変性、アルコール変性、フッ素変性、アルキルアラルキルポリエーテル変性、エポキシポリエーテル変性などの変性ポリシロキサンなどが挙げられる。これらの中ではジメチルポリシロキサンが好ましく用いられる。
本発明の樹脂組成物(E)は、本発明の目的を損ねない範囲であれば、他のポリオレフィン系樹脂などの熱可塑性樹脂や、樹脂用添加剤(例えば、耐熱安定剤、耐候安定剤などの安定剤、架橋剤、架橋助剤、帯電防止剤、スリップ剤、アンチブロッキング剤、防曇剤、滑剤、染料、顔料、フィラー、鉱物油系軟化剤、石油樹脂、ワックスなど)などを含有してもよい。
前記ポリエチレン樹脂(C)の製造方法は、ポリエチレン(A)およびポリエチレン(B)がポリエチレン樹脂(C)中に存在する製造方法であれば特に制限はないが、好ましい態様として以下の方法(M-1)および(M-2)を例示することができる。
(M-2)公知のオレフィン重合用触媒の存在下、第1工程としてポリエチレン(A)を生成させる工程と、第2工程としてポリエチレン(B)を生成させる工程との少なくとも2段階の工程を含む多段重合法により製造する方法。
なお、当該多段階で重合させる方法については、例えば、特開平1-129047号公報に記載の重合方法と同様な方法で行うことができる。
本発明の樹脂組成物(E)は、ポリエチレン樹脂(C)と変性ポリオレフィン樹脂(E)とオルガノポリシロキサンとを溶融ブレンドまたはドライブレンドすることによって製造することができる。オルガノポリシロキサンはマスターバッチの形状でポリエチレン樹脂(C)と混合することができる。溶融ブレンドまたはドライブレンドは公知の方法で行うことができる。
本発明の積層体は、熱硬化性樹脂および加硫剤を含む第1の層と、上述した本発明の樹脂組成物(E)を含む第2の層とを有することを特徴とする。第1の層と第2の層は接していることが好ましい。
前記第1の層の厚さは、特に限定されず、用途に応じて適宜決定することができる。また、前記第2の層の厚さは、好ましくは1~500μm、より好ましくは10~300μmである。
下記実施例および比較例で得られた各種ポリマーおよび樹脂組成物の各物性は、以下の方法にて求めた。
135℃、デカリン溶媒中で測定した。
ASTM D1505に準拠して測定した。
ASTM D638に準拠して、試験片形状をASTM 4号及び引張速度を50mm/minとし、引張弾性応力(YM:MPa)を求めた。
プレス成形によって、2mm厚みのプレス板を作製した。
ASTM D2240に準拠して、デュロメータ硬度計を使用して23℃で、作製した2mm厚みのプレス板を4枚重ねて測定した(5秒後)。
後述の方法で得られた二層積層体における樹脂組成物(E)層側の表面をガラスに当てて、5000回までの往復摺動を行い、1回往復から5000往復までの動摩擦係数を測定し、平均値を算出した。試験条件は速度:150mm/秒、荷重:1kg、測定環境温度:23℃とした。
後述の方法で得られた二層積層体における樹脂組成物(E)層側の表面粗さを、表面粗さ測定機(ミツトヨ製サーフテストSV-3200S4)を用いて、JIS B0601-1994に準拠して、評価長さ:4mm、測定速度:0.5mm/secで測定した。
<触媒調製>
充分に窒素置換された10Lの撹拌機付反応器に4.0Lの精製ヘキサンおよび95gの無水塩化マグネシウムを加え、撹拌下に室温で350mlのエタノールを2時間かけて滴下した後、約1時間室温で混合した。次いで330mlのジエチルアルミニウムクロライドを2時間かけて滴下した後、約1時間室温で混合した。次いで1.3Lの四塩化チタンを1時間かけて滴下した後、80℃で1時間の反応を行なった。
充分に窒素置換された24Lのオートクレーブに12Lの精製n-デカンを添加した後、50℃に昇温し、同温度で12mmolのトリエチルアルミニウムおよび上記固体状チタン触媒成分をチタン原子換算で0.12mmol添加した。次いで触媒装入口を閉じ、オートクレーブの内圧が3.1kg/cm2・Gになるようにエチレンを導入して重合を行なった。重合温度は45~46℃に維持した。エチレンを導入してから45分後に降温し、固体状白色ポリマーを分離して乾燥した。得られた超高分子量ポリエチレン(A1)の極限粘度は28.1dl/gであった。
ポリプロピレン(プライムポリマー製J106G)100質量部、無水マレイン酸4.0質量部、および有機過酸化物[日本油脂(株)製、商品名パーヘキシン-25B]0.35質量部をヘキシェルミキサーで混合し、得られた混合物を270℃に設定した100mmφの二軸押出機で、混練時間1分30秒程で溶融グラフト変性することによって、変性ポリオレフィン樹脂(D1)を得た。この変性ポリオレフィン樹脂(D1)の無水マレイン酸グラフト量をIR分析で測定したところ、3.0質量%であった。
<ポリエチレン樹脂組成物(E1)の製造>
上記で得られたポリエチレン樹脂(C1)100質量部に対して、変性ポリオレフィン樹脂(D1)および東レダウコーニング社製の超高分子量シリコーンポリマーマスターバッチ(製品名:BY27-001、ベース樹脂:ポリプロピレン、オルガノポリシロキサン含有量:50質量%、オルガノポリシロキサンの粘度:1×105cSt以上)を表2に示す量で添加してドライブレンドを実施した。次いで2軸押出機(池貝社製、φ=43mm、L/D=32、シリンダ温度:230℃)で溶融混練を行い、ポリエチレン樹脂組成物(E1)を得た。得られたポリエチレン樹脂組成物(E1)の各物性を測定した結果を表2に示す。
上記で得られたポリエチレン樹脂組成物(E1)と、熱硬化性加硫物を含んでいるEPDMとを二層押出成形することにより、長さ20cm、幅5mm、厚み2mmの試験片を作製し、これを230℃、5分間の条件で加硫することで二層積層体を得た。トータル厚みは2mmで、EPDM層が1.9mm、ポリエチレン樹脂組成物(E1)層が0.1mmであった。得られた二層積層体におけるポリエチレン樹脂組成物(E1)層側の表面について、表面粗さおよび動摩擦係数を測定した。結果を表2に示す。
表2に示す組成となるように各成分のドライブレンドを実施したこと以外は、実施例1と同様にしてポリエチレン樹脂組成物および二層積層体を製造し、各物性を測定した。結果を表2に示す。
Claims (8)
- 超高分子量ポリエチレン(A)0.1~4.8質量%と、低分子量ないし高分子量ポリエチレン(B)99.9~95.2質量%(ただし、ポリエチレン(A)とポリエチレン(B)の合計量を100質量%とする。)とを含むポリエチレン樹脂(C)、
変性ポリオレフィン樹脂(D)、および
オルガノポリシロキサン
を含有し、
前記ポリエチレン(A)が下記要件(a-1)を満たし、
前記ポリエチレン(B)が下記要件(b-1)を満たし、
前記ポリエチレン樹脂(C)が下記要件(c-1)を満たし、
前記変性ポリオレフィン樹脂(D)の含有量が、前記ポリエチレン樹脂(C)100質量部に対して0.01~1.5質量部の範囲である、樹脂組成物(E):
(a-1)135℃のデカリン溶媒中で測定した極限粘度[η]が10~40dl/gである;
(b-1)135℃のデカリン溶媒中で測定した極限粘度[η]が0.1~5dl/gである;
(c-1)密度が920~970kg/m3である。 - 前記変性ポリオレフィン樹脂(D)が、カルボキシル基および酸無水物基から選ばれる少なくとも1種の基を有する不飽和化合物により変性したポリオレフィン樹脂を含む、請求項1に記載の樹脂組成物(E)。
- 前記オルガノポリシロキサンが、ジメチルポリシロキサン、メチルフェニルポリシロキサン、フルオロポリシロキサン、テトラメチルテトラフェニルポリシロキサン、およびメチルハイドロジェンポリシロキサンからなる群より選ばれる少なくとも1種である、請求項1または2に記載の樹脂組成物(E)。
- 前記オルガノポリシロキサンの含有量が、前記ポリエチレン樹脂(C)100質量部に対して0.1~20質量部である、請求項1~3のいずれか1項に記載の樹脂組成物(E)。
- 熱硬化性樹脂および加硫剤を含む第1の層と、請求項1~4のいずれか1項に記載の樹脂組成物(E)を含む第2の層とを有する積層体。
- JIS B0601-1994に準拠して測定された、前記第2の層の表面粗さが0.5~4.0μmである、請求項5に記載の積層体。
- 温度23℃および湿度50%の条件で測定された、前記第2の層の表面の動摩擦係数が0.4以下である、請求項5または6に記載の積層体。
- 請求項5~7のいずれか1項に記載の積層体を製造する方法であって、
前記樹脂組成物(E)と、加硫剤を含む熱硬化性樹脂とを共押出する工程、および
前記共押出工程後、200~250℃および1~10分間の条件で加硫する工程
を含む、積層体の製造方法。