JP7392916B2 - キャリアガラス及びその製造方法 - Google Patents
キャリアガラス及びその製造方法 Download PDFInfo
- Publication number
- JP7392916B2 JP7392916B2 JP2022173042A JP2022173042A JP7392916B2 JP 7392916 B2 JP7392916 B2 JP 7392916B2 JP 2022173042 A JP2022173042 A JP 2022173042A JP 2022173042 A JP2022173042 A JP 2022173042A JP 7392916 B2 JP7392916 B2 JP 7392916B2
- Authority
- JP
- Japan
- Prior art keywords
- glass
- less
- carrier
- carrier glass
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)熱処理工程で成膜された半導体膜中にアルカリイオンが拡散する事態を防止するため、アルカリ金属酸化物の含有量が少ないこと、
(2)生産性に優れること、例えば溶融性、清澄性、耐失透性に優れること。
logTin=log(I1/I0)-logR
logTin:内部透過率(%)
I0:入射した光の強度(%)
I1:特定の光路長を透過した後の光の強度(%)
R:反射による光の減衰率(%)
β-OH値 = (1/X)log(T1/T2)
X:板厚(mm)
T1:参照波長3846cm-1における透過率(%)
T2:水酸基吸収波長3600cm-1付近における最小透過率(%)
Claims (9)
- 有機樹脂基板を搬送するためのキャリアガラスであって、
板厚0.1~1.2mmの平板形状であり、
ガラス中の鉄含有量が、Fe2O3換算で45~130質量ppmであり、
且つ波長308nmにおける板厚方向の透過率が71~81%であり、
ガラス組成として、下記酸化物換算の質量%で、SiO2 55~65%、Al2O3 15~23%、B2O3 0~3%、Li2O+Na2O+K2O 0~0.20%未満、MgO 2.5~6%、CaO 0.1~10%、SrO 0.3~3.16%、BaO 0.1~13%を含有することを特徴とするキャリアガラス。 - ガラス組成中のLi2O+Na2O+K2Oの含有量が0.20質量%未満であることを特徴とする請求項1に記載のキャリアガラス。
- β-OH値が0.20/mm以下であることを特徴とする請求項1又は2に記載のキャリアガラス。
- 常温から5℃/分の速度で昇温し、500℃で1時間保持し、5℃/分の速度で降温した時の熱収縮率が20ppm以下であることを特徴とする請求項1~3の何れかに記載のキャリアガラス。
- 液相温度が1300℃以下であることを特徴とする請求項1~4の何れかに記載のキャリアガラス。
- 高温粘度102.5dPa・sの粘度における温度が1700℃以下であることを特徴とする請求項1~5の何れかに記載のキャリアガラス。
- キャリアガラスと有機樹脂基板とを積層させたガラス樹脂積層体であって、
キャリアガラスが、請求項1~6の何れかに記載のキャリアガラスであることを特徴とするガラス樹脂積層体。 - 有機樹脂基板を搬送するためのキャリアガラスの製造方法であって、
ガラス組成として、下記酸化物換算の質量%で、SiO2 55~65%、Al2O3 15~23%、B2O3 0~3%、Li2O+Na2O+K2O 0~0.20%未満、MgO 2.5~6%、CaO 0.1~10%、SrO 0.3~3.16%、BaO 0.1~13%、Fe2O3 45~130質量ppm、As2O3 0~0.010%未満、Sb2O3 0~0.010%未満を含有し、且つ波長308nmにおける板厚方向の透過率が71~81%であるガラスが得られるように、ガラスバッチを調合する調合工程と、調合されたガラスバッチに対して、加熱電極による通電加熱を行うことにより、溶融ガラスを得る溶融工程と、得られた溶融ガラスをオーバーフローダウンドロー法により板厚0.1~1.2mmの平板形状に成形する成形工程と、を有することを特徴とするキャリアガラスの製造方法。 - MgO導入原料とCaO導入原料由来の鉄含有量が、Fe2O3換算で30~70質量ppmになるように、ガラスバッチを調合することを特徴とする請求項8に記載のキャリアガラスの製造方法。