JP7371958B2 - ポリウレタン系複合材料の製造方法、ポリウレタン系複合材料および歯科切削加工用材料。 - Google Patents
ポリウレタン系複合材料の製造方法、ポリウレタン系複合材料および歯科切削加工用材料。 Download PDFInfo
- Publication number
- JP7371958B2 JP7371958B2 JP2021573990A JP2021573990A JP7371958B2 JP 7371958 B2 JP7371958 B2 JP 7371958B2 JP 2021573990 A JP2021573990 A JP 2021573990A JP 2021573990 A JP2021573990 A JP 2021573990A JP 7371958 B2 JP7371958 B2 JP 7371958B2
- Authority
- JP
- Japan
- Prior art keywords
- radically polymerizable
- raw material
- material composition
- polyurethane
- polyaddition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
条件I:BSA≧200(MPa)
条件II:1>BSW/BSA≧0.7
ここで、BSAは、ISO 6872による3点曲げ強さ(MPa)を表し、BSWはJDMAS 245:2017による水中浸漬後の3点曲げ強さ(MPa)を表す。
本発明のポリウレタン系複合材料の製造方法は、1つ以上のラジカル重合性基を有するジオール化合物(a1)と、ジイソシアネート化合物(a2)と、分子内に1つ以上のラジカル重合性基を有し、ジオール化合物(a1)およびジイソシアネート化合物(a2)の何れとも重付加反応を起こさない重合性単量体(B)と、を含む重付加反応性原料組成物中において、ジオール化合物(a1)とジイソシアネート化合物(a2)とを重付加反応させることにより、数平均分子量が1500~5000であり、かつ、ラジカル重合性基を有するポリウレタン成分(A)を形成する重付加反応工程と、ポリウレタン成分(A)と、重合性単量体(B)と、ラジカル重合開始剤(C)と、充填材(D)と、を含むラジカル重合性原料組成物を調製するラジカル重合性原料組成物調製工程と、重付加反応工程およびラジカル重合性原料組成物調製工程を完了した後に、ラジカル重合性原料組成物を用いてラジカル重合を行うことによりポリウレタン系複合材料を形成するラジカル重合工程とを含み、下式(1)に示す重合性単量体配合比率Rrが20質量%~80質量%であることを特徴とする。
・式(1) Rr=100×Br/〔a1r+a2r+Ar+Br〕
〔式(1)中、a1rは、ラジカル重合性原料組成物中に残存している未反応のジオール化合物(a1)の含有量(質量部)を表し、a2rは、ラジカル重合性原料組成物中に残存している未反応のジイソシアネート化合物(a2)の含有量(質量部)を表し、Arは、ラジカル重合性原料組成物に含まれるポリウレタン成分(A)の含有量(質量部)を表し、Brは、ラジカル重合性原料組成物に含まれる重合性単量体(B)の含有量(質量部)を表す。〕
・式(1) Rr=100×Br/〔a1r+a2r+Ar+Br〕
〔式(1)中、a1rは、ラジカル重合性原料組成物中に残存している未反応のジオール化合物(a1)の含有量(質量部)を表し、a2rは、ラジカル重合性原料組成物中に残存している未反応のジイソシアネート化合物(a2)の含有量(質量部)を表し、Arは、ラジカル重合性原料組成物に含まれるポリウレタン成分(A)の含有量(質量部)を表し、Brは、ラジカル重合性原料組成物に含まれる重合性単量体(B)の含有量(質量部)を表す。〕
・式(1) Rr=100×Br/〔a1r+a2r+Ar+Br〕
〔式(1)中、a1rは、ラジカル重合性原料組成物中に残存している未反応のジオール化合物(a1)の含有量(質量部)を表し、a2rは、ラジカル重合性原料組成物中に残存している未反応のジイソシアネート化合物(a2)の含有量(質量部)を表し、Arは、ラジカル重合性原料組成物に含まれるポリウレタン成分(A)の含有量(質量部)を表し、Brは、ラジカル重合性原料組成物に含まれる重合性単量体(B)の含有量(質量部)を表す。〕
本実施形態のポリウレタン系複合材料の製造方法は、1つ以上のラジカル重合性基を有するジオール化合物(a1)と、ジイソシアネート化合物(a2)と、分子内に1つ以上のラジカル重合性基を有し、ジオール化合物(a1)およびジイソシアネート化合物(a2)の何れとも重付加反応を起こさない重合性単量体(B)と、を含む重付加反応性原料組成物中において、ジオール化合物(a1)とジイソシアネート化合物(a2)とを重付加反応させることにより、数平均分子量が1500~5000であり、かつ、ラジカル重合性基を有するポリウレタン成分(A)を形成する重付加反応工程と、ポリウレタン成分(A)と、重合性単量体(B)と、ラジカル重合開始剤(C)と、充填材(D)と、を含むラジカル重合性原料組成物を調製するラジカル重合性原料組成物調製工程と、重付加反応工程およびラジカル重合性原料組成物調製工程を完了した後に、ラジカル重合性原料組成物を用いてラジカル重合を行うことによりポリウレタン系複合材料を形成するラジカル重合工程とを含み、下式(1)に示す重合性単量体配合比率Rrが20質量%~80質量%であることを特徴とする。
・式(1) Rr=100×Br/〔a1r+a2r+Ar+Br〕
〔式(1)中、a1rは、ラジカル重合性原料組成物中に残存している未反応のジオール化合物(a1)の含有量(質量部)を表し、a2rは、ラジカル重合性原料組成物中に残存している未反応のジイソシアネート化合物(a2)の含有量(質量部)を表し、Arは、ラジカル重合性原料組成物に含まれるポリウレタン成分(A)の含有量(質量部)を表し、Brは、ラジカル重合性原料組成物に含まれる重合性単量体(B)の含有量(質量部)を表す。〕
2-1.ラジカル重合性ジオール化合物(a1)
ラジカル重合性ジオール化合物(a1)は、ラジカル重合性ポリウレタン成分(A)を形成するための原料となる化合物である。そして、ラジカル重合性ジオール化合物(a1)が有する2つのヒドロキシル基と、もう一方のポリウレタン前駆体成分であるジイソシアネート化合物(a2)のイソシアネート基とが、重付加反応工程で重付加反応を起こすことにより、ラジカル重合性ポリウレタン成分(A)が形成される。
上記ジイソシアネート化合物(a2)は、ラジカル重合性ポリウレタン成分(A)を形成するためのもう一方のポリウレタン前駆体成分であり、1分子中に2個のイソシアネート基を有する公知の化合物が特に限定されず使用できる。
ラジカル重合性ポリウレタン成分(A)は、重付加反応工程においてラジカル重合性ジオール化合物(a1)とジイソシアネート化合物(a2)との重付加反応により形成される成分である。そして、ラジカル重合性ポリウレタン成分(A)の構造は、重付加反応工程において使用するラジカル重合性ジオール化合物(a1)およびジイソシアネート化合物(a2)によってほぼ一義的に決定される。
・カラム:ACQUITY APC TM XT 45 1.7μm
ACQUITY APC TM XT 125 2.5μm
・カラム温度:40℃
・展開溶媒:THF
・流量:0.5 ml/分
・検出器:フォトダイオードアレイ検出器 254nm(PDA検出器)
非重付加性ラジカル重合性単量体(B)は、分子内に、少なくとも1つのラジカル重合性基を有し、かつ、ラジカル重合性ジオール化合物(a1)およびジイソシアネート化合物(a2)の何れとも重付加反応を起こさない化合物である。ここで、「ラジカル重合性ジオール化合物(a1)およびジイソシアネート化合物(a2)の何れとも重付加反応を起こさない」とは、分子内に、ラジカルジオール化合物(a1)と重付加反応を起こす基、および、ジイソシアネート化合物(a2)と重付加反応を起こす基の双方が含まれないことを意味し、具体的にはヒドロキシル基、アミノ基、カルボキシ基、イソシアネート基およびメルカプト基が含まれないことを意味する。これらの官能基のうち、ラジカル重合性ジオール化合物(a1)と重付加反応を起こし得る基は、イソシアネート基が挙げられ、ジイソシアネート化合物(a2)と重付加反応を起こし得る基は、ヒドロキシル基、アミノ基、カルボキシル基、メルカプト基が挙げられる。したがって、非重付加性ラジカル重合性単量体(B)は、分子内にヒドロキシル基、アミノ基、カルボキシ基、イソシアネート基およびメルカプト基を有さない。また、ラジカル重合性基は、ラジカル重合性ジオール化合物(a1)が有するラジカル重合性基と同様の基が利用できる。好適なラジカル重合性基としては、(メタ)アクリレート基および/または(メタ)アクリルアミド基や、ラジカル重合性ジオール化合物(a1)が有するラジカル重合性基と同一の分子構造を持つ基が好ましい。非重付加性ラジカル重合性単量体(B)の分子内に含まれるラジカル重合性基の数は、架橋の形成し易さの観点から、2~6個であることが好ましく、2~4個であることがより好ましい。ラジカル重合性基の数を2個以上とすることにより、架橋密度をより大きくできるため、十分な強度を有する硬化体を得ることがより容易になる。また、ラジカル重合性基の数を6個以下とすることにより、硬化時の収縮を抑制することがより容易になる。また、非重付加性ラジカル重合性単量体(B)は室温(すなわち25℃)で液体であることが好ましい。
ラジカル重合開始剤(C)は、ラジカル重合工程におけるラジカル重合反応を開始する機能を有し、ラジカル重合性基同士を反応させて結合させることにより、ラジカル重合性原料組成物を重合硬化させると共に架橋点を形成させる機能を有する。ラジカル重合開始剤(C)としては、熱ラジカル重合開始剤および/または光ラジカル重合開始剤が使用できるが、ラジカル重合性原料組成物の内部まで均一に硬化させることができる点から、熱ラジカル重合開始剤を用いることが好ましい。熱重合開始剤としては、取り扱い易さや安定性の観点から、10時間半減期温度が40℃~150℃の範囲である熱重合開始剤が好ましく、10時間半減期温度が70℃~100℃の範囲である熱重合開始剤が特に好適である。ここで、10時間半減期温度とは、熱重合開始剤の存在量が、初期から10時間経過後に初期の半分に減ずる温度のことであり、熱重合開始剤の反応性を表す指標として用いられる。好適に使用できる熱ラジカル重合開始剤を具体的に例示すると、ベンゾイルパーオキサイドやtert-ブチルパーオキシラウレートなどのような過酸化物開始剤、アゾビスブチロニトリルやアゾビス(2,4-ジメチルバレロニトリル)などのようなアゾ系の開始剤などを挙げることができる。これら熱重合開始剤は、単独で用いても、2種以上を混合して使用してもよい。
充填材(D)は、ポリウレタン系樹脂マトリックス中に分散して、ポリウレタン系樹脂マトリックスと複合化することにより、ポリウレタン系複合材料の機械的強度、耐摩耗性および耐水性等の物性を向上させる機能を有する。
ラジカル重合性原料組成物あるいは重付加反応性原料組成物には以上に説明した必須成分の他に、その他の各種の添加剤を配合しても良い。各種添加剤としては、重合禁止剤、蛍光剤、紫外線吸収剤、酸化防止剤、顔料、抗菌材、X線造影剤など挙げることができ、その添加量は所望の目的に応じて適宜決定すればよい。
本実施形態のポリウレタン系複合材料の製造方法は、重付加反応工程と、ラジカル重合性原料組成物調製工程と、ラジカル重合工程とを含む。以下に各工程の詳細について説明する。
(1)重付加反応性原料組成物の調製
重付加反応工程では、まず、ラジカル重合性ジオール化合物(a1)と、ジイソシアネート化合物(a2)と、非重付加性ラジカル重合性単量体(B)と、を含む重付加反応性原料組成物を調製する。そして、重付加反応性原料組成物中にて、ラジカル重合性ジオール化合物(a1)と、ジイソシアネート化合物(a2)との重付加反応を実施し、ラジカル重合性ポリウレタン成分(A)を形成する。
・式(1’) Rp=100×Bp/〔a1p+a2p+Bp〕
〔式(1’)中、a1pは、重付加反応性原料組成物中に含まれるラジカル重合性ジオール化合物(a1)の含有量(質量部)を表し、a2pは、重付加反応性原料組成物中に含まれるジイソシアネート化合物(a2)の含有量(質量部)を表し、Bpは、重付加反応性原料組成物に含まれる非重付加性ラジカル重合性単量体(B)の含有量(質量部)を表す。〕
<1>重付加反応性原料組成物が、ラジカル重合性ジオール化合物(a1)、ジイソシアネート化合物(a2)、非重付加性ラジカル重合性単量体(B)および充填材(D)を少なくとも含む。
<2>ラジカル重合性原料組成物に含まれる充填材(D)の充填率が高い場合(たとえば充填率で60質量%程度以上の場合)。
重付加反応性原料組成物を調製した後は、重付加反応性原料組成物に含まれるラジカル重合性ジオール化合物(a1)と、ジイソシアネート化合物(a2)とを重付加反応させることでラジカル重合性ポリウレタン成分(A)を形成する。重付加反応は、重付加反応性原料組成物が調製されると同時に、あるいは、重付加反応性原料組成物を必要に応じて加熱することにより開始される。重付加反応は、重付加反応性原料組成物に含まれるラジカル重合性ジオール化合物(a1)およびジイソシアネート化合物(a2)の少なくとも一方が重付加反応により実質的に消費し尽くされるまで重付加反応を進行させるように、言い換えれば、重付加反応の進行度が最大値(飽和値)近傍となるまで、実施する。それゆえ、重付加反応性原料組成物を加熱する場合は、上述した点を踏まえて加熱温度および加熱時間を適宜選択することができる。この場合、加熱温度は30℃~100℃が好ましく、35℃~80℃がより好ましい。また、重付加反応の進行度が実質的に最大値(飽和値)近傍に到達できるという観点から、加熱時間は、(1)加熱温度が30℃以上35℃未満であれば約90時間以上が好ましく、約100時間以上がより好ましく、(2)加熱温度が35℃以上50℃未満であれば約65時間以上が好ましく、約72時間以上がより好ましく、約80時間以上がさらに好ましく、(3)加熱温度が50℃以上75℃未満であれば約45時間以上が好ましく、約55時間以上がより好ましく、約65時間以上がさらに好ましく、(4)加熱温度が75℃以上100℃以下であれば約24時間以上が好ましく、約35時間以上がより好ましく、約45時間以上がさらに好ましい。なお、上記(1)~(4)に示すケースにおいて、加熱時間の上限値は特に限定されるものではないが、生産性などの実用上の観点からは168時間以下が好ましい。
(1)ラジカル重合性原料組成物の調製手順
ラジカル重合性原料組成物調製工程では、ラジカル重合性ポリウレタン成分(A)と、非重付加性ラジカル重合性単量体(B)と、ラジカル重合開始剤(C)と、充填材(D)とを含むラジカル重合性原料組成物を調製する。
<1>ラジカル重合性ジオール化合物(a1)、ジイソシアネート化合物(a2)、非重付加性ラジカル重合性単量体(B)およびラジカル重合開始剤(C)
<2>ラジカル重合性ジオール化合物(a1)、ジイソシアネート化合物(a2)、非重付加性ラジカル重合性単量体(B)および充填材(D)
<3>ラジカル重合性ジオール化合物(a1)、ジイソシアネート化合物(a2)、非重付加性ラジカル重合性単量体(B)、ラジカル重合開始剤(C)および充填材(D)
<4>ラジカル重合性ジオール化合物(a1)、ジイソシアネート化合物(a2)、非重付加性ラジカル重合性単量体(B)
重付加反応性原料組成物が上記<1>に列挙する成分を含む場合には、まず、重付加反応性原料組成物中において、ラジカル重合性ジオール化合物(a1)とジイソシアネート化合物(a2)とを重付加反応させることでラジカル重合性ポリウレタン成分(A)を形成し、重付加反応工程を完了させる。その後、ラジカル重合性ポリウレタン成分(A)、非重付加性ラジカル重合性単量体(B)およびラジカル重合開始剤(C)を含む中間組成物に対して、充填材(D)を添加・混合することによりラジカル重合性原料組成物を調製することができる。なお、第1の調製手順では、重付加反応工程と、ラジカル重合性原料組成物調製工程とがこの順に実施されることになる。
重付加反応性原料組成物が上記<2>に列挙する成分を含む場合には、まず、重付加反応性原料組成物中において、ラジカル重合性ジオール化合物(a1)とジイソシアネート化合物(a2)とを重付加反応させることでラジカル重合性ポリウレタン成分(A)を形成し、重付加反応工程を完了させる。その後、ラジカル重合性ポリウレタン成分(A)、非重付加性ラジカル重合性単量体(B)および充填材(D)を含む中間組成物に対して、ラジカル重合開始剤(C)を添加・混合することによりラジカル重合性原料組成物を調製することができる。
重付加反応性原料組成物が上記<3>に列挙する成分を含む場合には、まず、重付加反応性原料組成物中において、ラジカル重合性ジオール化合物(a1)とジイソシアネート化合物(a2)とを重付加反応させることでラジカル重合性ポリウレタン成分(A)を形成し、重付加反応工程を完了させる。また、重付加反応工程の完了により、4つの必須成分の全てを含むラジカル重合性原料組成物の調製も完了する。すなわち、第3の調製手順では、重付加反応工程の完了と同時にラジカル重合性原料組成物調製工程も完了する。
重付加反応性原料組成物が上記<4>に列挙する成分を含む場合には、まず、重付加反応性原料組成物中において、ラジカル重合性ジオール化合物(a1)とジイソシアネート化合物(a2)とを重付加反応させることでラジカル重合性ポリウレタン成分(A)を形成し、重付加反応工程を完了させる。その後、ラジカル重合性ポリウレタン成分(A)および非重付加性ラジカル重合性単量体(B)を含む中間組成物に対して、ラジカル重合開始剤(C)および充填材(D)を添加・混合することによりラジカル重合性原料組成物を調製することができる。なお、第4の調製手順では、重付加反応工程と、ラジカル重合性原料組成物調製工程とがこの順に実施されることになる。
ラジカル重合性原料組成物を構成する4つの必須成分のうち、含有量の点で主成分となるのは、ラジカル重合性ポリウレタン成分(A)、非重付加性ラジカル重合性単量体(B)および充填材(D)である。ここで、非重付加性ラジカル重合性単量体(B)は常温では液状の低分子物質である。これに加えて、ラジカル重合性ポリウレタン成分(A)は高分子ではあるものの、その数平均分子量は1500~5000という比較的小さい値である(すなわち、分子サイズがかなり小さい)。それゆえ、ラジカル重合性ポリウレタン成分(A)は、非重付加性ラジカル重合性単量体(B)中に析出することなく溶解することが容易である。従って、充填材(D)の充填率が過剰に大きくない限り、本実施形態のポリウレタン系複合材料の製造方法において用いられるラジカル重合性原料組成物は、通常、ペースト状の組成物として存在する。また、ラジカル重合性原料組成物の相形態がペースト状である場合、重合性単量体配合比率Rrが20質量%~80質量%であるラジカル重合性原料組成物、言い換えれば、十分な量の低分子量成分(非重付加性ラジカル重合性単量体(B))を含むラジカル重合性原料組成物は操作性にも優れる。なお、ラジカル重合性原料組成物の相形態をより確実にペースト状とする観点からは、充填材(D)の充填率は、通常、85質量%以下が好ましく、80質量%以下がより好ましい。
ラジカル重合工程(硬化工程)は、重付加反応工程およびラジカル重合性原料組成物調製工程を完了した後に実施される。ラジカル重合工程では、ラジカル重合性原料組成物に含まれるラジカル重合開始剤(C)を活性化してラジカル重合を行うことにより、ラジカル重合性原料組成物を硬化させる。これにより、ポリウレタン系複合材料からなる硬化体を得る。ラジカル重合開始剤(C)として熱ラジカル重合開始剤を用いた場合にはラジカル重合性原料組成物を加熱することによりラジカル重合が進行し、ラジカル重合開始剤(C)として光ラジカル重合開始剤を用いた場合にはこれを活性化する光をラジカル重合性原料組成物に照射することによりラジカル重合が進行する。
(a1)加熱温度:ラジカル重合開始剤(C)として用いる熱ラジカル重合開始剤の10時間半減期温度の-10℃~+25℃の範囲
(b1)加熱時間:2時間~120時間
(a2)加熱温度:ラジカル重合開始剤(C)として用いる熱ラジカル重合開始剤の10時間半減期温度の+0℃~+25℃の範囲
(b2)加熱時間:5時間~72時間
(a3)加熱温度:ラジカル重合開始剤(C)として用いる熱ラジカル重合開始剤の10時間半減期温度の+10℃~+25℃の範囲
(b3)加熱時間:8時間~24時間
・式(3) ラジカル重合性基残存率(%)=(r1/r0)×100
〔式(3)中、r0は、ラジカル重合開始前のラジカル重合性原料組成物のFT-IR測定により得られた2つのピーク面積(ν6170およびν4920)について、ピーク面積(ν6170)をピーク面積(ν4920)で除することにより正規化して得られた正規化ピーク面積比(ν6170/ν4920)を意味し、r1は、ラジカル重合の終了後に得られた硬化体(ポリウレタン系複合材料)のFT-IR測定により得られた2つのピーク面積(ν6170およびν4920)について、ピーク面積(ν6170)をピーク面積(ν4920)で除することにより正規化して得られた正規化ピーク面積比(ν6170/ν4920)を意味する。
ここで、ピーク面積(ν6170)は、ラジカル重合性基の炭素-炭素二重結合に起因する6170cm-1付近に観察される吸収ピークのピーク面積を意味し、ピーク面積(ν4920)は、ウレタン結合のカルボニル基に起因する4920cm-1付近に観察される吸収ピークのピーク面積を意味する。〕
本実施形態のポリウレタン系複合材料の製造方法において使用するラジカル重合性原料組成物がペースト状の組成物である場合は、上述したようにラジカル重合性原料組成物を型枠に注入した後にラジカル重合工程(硬化工程)を実施することも可能である。また、得られる硬化体(ポリウレタン系複合材料)は、口腔内のような親水環境下においても高い強度を維持しつつ耐水性も有する。このように高い耐水性を有するために、本実施形態のポリウレタン系複合材料の製造方法は、特に歯科用CAD/CAMシステムを用いて歯科切削加工用材料を切削加工することにより歯科用補綴物を作製する場合において、当該歯科切削加工用材料の製造方法として好適に使用することができる。以下に、本実施形態のポリウレタン系複合材料の製造方法について、歯科切削加工用材料の製造に利用した場合の好適な具体例について説明する。
本実施形態のポリウレタン系複合材料の製造方法により製造されたポリウレタン系複合材料としては、本実施形態のポリウレタン系複合材料の製造方法においてさらに下記(a)~(c)に示す製造条件もさらに満たすことで製造されたものが好適である。この場合、下記(a)に示す製造条件に対応する充填材(D)の含有量と、下記(d)に示すラジカル重合性基残存率とを有する硬化体(第一の本実施形態のポリウレタン系複合材料)を得ることができる。なお、下記(d)に示すラジカル重合性基残存率は、10%~20%がより好適である。
(a)ラジカル重合性原料組成物中における充填材(D)の含有割合が60質量%~85質量%である。
(b)ラジカル重合開始剤(C)として熱ラジカル重合開始剤を使用する。
(c)ラジカル重合工程が前記熱ラジカル重合開始剤の10時間半減期温度の-10℃~+25℃の温度に加熱した状態で実施される。
(d)ラジカル重合工程において形成されたラジカル重合性ポリウレタン成分(A)と非重付加性ラジカル重合性単量体(B)との共重合体には、ラジカル重合性原料組成物に含まれるラジカル重合性ジオール化合物(a1)および非重付加性ラジカル重合性単量体(B)が有するラジカル重合性基の総量の10%~25%が残存している(すなわち、ラジカル重合性基残存率が10%~25%である)。
〔式(4)中、初期二重結合量は、下式(5)に基づいて決定される検量線作成用サンプル製造時のラジカル重合開始前の原料組成物(ラジカル重合性原料組成物の調製に用いた重付加反応性原料組成物)における未反応のラジカル重合性基の総量(mmol/g)を意味し、ラジカル重合性基残存率は、式(3)に基づいて決定されるラジカル重合性基残存率(%)を意味する。〕
また、Xaは、重付加反応工程で用いた重付加反応性原料組成物中に含まれるa番目のラジカル重合性ジオール化合物(a1)の含有量(mmol)を意味し、αaはa番目のラジカル重合性ジオール化合物(a1)の1分子当たりに含まれるラジカル重合性基の数を意味し、Ybは、重付加反応工程で用いた重付加反応性原料組成物中に含まれるb番目の非重付加性ラジカル重合性単量体(B)の含有量(mmol)を意味し、βbはb番目の非重付加性ラジカル重合性単量体(B)の1分子当たりに含まれるラジカル重合性基の数を意味する。
さらに、Mは、重付加反応工程で用いた重付加反応性原料組成物の質量(g)を意味する。但し、重付加反応工程で用いた重付加反応性原料組成物が、ラジカル重合性ジオール化合物(a1)、ジイソシアネート化合物(a2)および非重付加性ラジカル重合性単量体(B)のいずれにも溶解しない不溶性成分(たとえば、充填材(D)など)をさらに含む場合、Mは、重付加反応性原料組成物の質量(g)から当該重付加反応性原料組成物に含まれる不溶性成分の質量(g)を除外した後の質量(g)を意味する。〕
なお、第一および第二の本実施形態のポリウレタン系複合材料は、充填材(D)を必須成分として含むものであるが、充填材(D)が必須成分として含まれない態様でも利用できる。この態様を踏まえた好適なポリウレタン系樹脂材料としては、以下に説明する第一および第二の参考実施形態のポリウレタン系樹脂材料が挙げられる。
・式(1) Rr=100×Br/〔a1r+a2r+Ar+Br〕
〔式(1)中、a1rは、ラジカル重合性原料組成物中に残存している未反応のジオール化合物(a1)の含有量(質量部)を表し、a2rは、ラジカル重合性原料組成物中に残存している未反応のジイソシアネート化合物(a2)の含有量(質量部)を表し、Arは、ラジカル重合性原料組成物に含まれるポリウレタン成分(A)の含有量(質量部)を表し、Brは、ラジカル重合性原料組成物に含まれる重合性単量体(B)の含有量(質量部)を表す。〕
各実施例および比較例において用いた各成分とその略称を以下に示す。
(1)ラジカル重合性ジオール化合物(a1)
GLM:グリセロールモノメタクリレート(OH間距離:2)
bis-GMA:ビスフェノールAジグリシジルメタクリレート(OH間距離:19)
(2)非ラジカル重合性ポリオール化合物
PG:プロピレングリコール
GTP:グリセロールトリプロポキシレート(平均分子量=266)
(3)ジイソシアネート化合物(a2)
XDI:m-キシリレンジイソシアナート
(4)非重付加性ラジカル重合性単量体(B)
1G:エチレングリコールジメタクリレート
2G:ジエチレングリコールジメタクリレート
3G:トリエチレングリコールジメタクリレート
9G:ポリエチレングリコール#400ジメタクリレート
A-TMPT-3EO:EO変性トリメチロールプロパントリアクリレート
A-DOG:ジオキサングリコールジアクリレート
UDMA:1,6-ビス(メタクリルエチルオキシカルボニルアミノ)-2,2,4-トリメチルヘキサン
(5)ラジカル重合開始剤(C)
PBL:t-ブチルパーオキシラウレート(10時間半減期温度98℃)
V-65:2,2‘-アゾビス(2,4-ジメチルバレロニトリル)(10時間半減期温度51℃)
BPO:ベンゾイルパーオキサイド(10時間半減期温度74℃)
(6)充填材(D)
F1:シリカ-ジルコニア(平均粒径:0.4μm、メタクリル酸3-(トリメトキシシリル)プロピル表面処理物)
F2:シリカ-チタニア(平均粒径:0.08μm、メタクリル酸3-(トリメトキシシリル)プロピル表面処理物)
以下に本発明のポリウレタン系複合材料の製造方法の実施例を、比較例と共に示す。
(1)1次原料組成物調製工程
先ず、ラジカル重合性ジオール化合物(a1)であるGLM:10.63質量部、非重付加性ラジカル重合性単量体(B)である1G:5.79質量部、及びラジカル重合開始剤(C)であるPBL:0.08質量部を混合した混合組成物を調製した。次に、この混合物組成物に対して、充填材(D)であるF1:49.70質量部及びF2:21.30質量部を添加して混練することにより、1次原料組成物を調製した。
得られた1次原料組成物の全量を含む自転公転ミキサー内にジイソシアネート化合物(a2)であるXDI:12.50質量部を加えて混練することにより重付加反応性原料組成物を調製した。次に、得られた重付加反応性原料組成物を37℃で168時間インキュベーター内に静置して重付加反応を行い、ラジカル重合性ポリウレタン成分(A)を形成してラジカル重合性原料組成物を調製した。なお、重付加反応時の加熱条件(37℃・168時間)は、重付加反応の進行度が最大値(飽和値)に到達する上で十分な条件である。
(3-1)ポリウレタン成分(A)の数平均分子量測定(GPC測定)
得られたラジカル重合性原料組成物1gをスクリュー管瓶に秤取り、THFを3.5ml加え撹拌して得られたTHF溶液を遠心分離機(アズワン株式会社製)にて、10000rpmで10分間遠心分離を行った。次に遠心分離により得られた上澄み液をメンブレンフィルター(PORE SIZE 20μm,アドバンテック東洋株式会社製)で濾過することにより濾液を得た。そしてこの濾液について、下記に示すGPC測定条件にてGPC測定を行うことにより、重付加反応により得られたラジカル重合性ポリウレタン成分(A)のポリスチレン換算の数平均分子量を求めた。その結果、数平均分子量は3500であった。
測定装置:Advanced Polymer Chromatography(日本ウォーターズ社製)
・カラム:ACQUITY APC TM XT 45 1.7μm
ACQUITY APC TM XT 125 2.5μm
・カラム温度:40℃
・展開溶媒:THF(流量:0.5 ml/分)
・検出器:フォトダイオードアレイ検出器 254nm(PDA検出器)
ラジカル重合性原料組成物の操作性は、直径5mmのステンレス(SUS)製丸棒を所定の速度で所定の深さまで押し込んだときの最大荷重を測定することにより評価した。最大荷重は以下の手順で測定した。まず、ラジカル重合性原料組成物をSUS製ナット状型に填入して表面を平らにならし、2分間遮光下で放置した。次に、サンレオメーターCR-150(株式会社サン科学製)に、ラジカル重合性原料組成物を充填したSUS製ナット状型と、感圧軸として5mmSUS製棒と、を取り付けた。続いて、23℃において、感圧軸を120mm/分の速度でラジカル重合性原料組成物中に深さ2mmまで圧縮進入させた。そしてこの時の最大荷重[Kg]を測定した。その結果、最大荷重は6.0Kgであった。
ラジカル重合性原料組成物の相形態は、操作性評価のために測定した最大荷重を基準に判断した。ここで、最大荷重が10Kg以下の場合、ラジカル重合性原料組成物は、ラジカル重合性原料組成物を型枠に隙間なく注入して型成形を容易に行うことができる十分な流動性を有しているため、ラジカル重合性原料組成物の相形態をペースト状と判定した。一方、最大荷重が10Kgを超える場合、ラジカル重合性原料組成物は、ラジカル重合性原料組成物を型枠に隙間なく注入して型成形を実施できない程に著しく流動性を喪失するため、ラジカル重合性原料組成物の相形態を実質的に固体と判定した。その結果、得られたラジカル重合性原料組成物は、その最大荷重は6.0Kgであり、ペースト状であることが確認された。
得られたラジカル重合性原料組成物を型枠(縦12mm×横18mm×厚さ14mm)内に注入し、120℃で15時間、窒素加圧下(0.35MPa)にてラジカル重合することにより、ポリウレタン系樹脂マトリックス中に充填材が分散したポリウレタン系複合材料を得た。なお、得られたラジカル重合性原料組成物は調製直後から型成形およびラジカル重合を開始する直前までの数時間の間、粘度の上昇や液性の変化は特に観察されず、常温環境下において安定した組成物であることが確認された。また、ラジカル重合による硬化により得られた硬化体は、硬化が部分的に不十分な部分も存在しておらず、均一な硬化体が得られた。
得られたポリウレタン系複合材料について、曲げ強さ、水中曲げ強さ、維持率(耐水性)および均一性を評価した。評価方法と結果を以下に示す。
得られたポリウレタン系複合材料(硬化体)を低速のダイヤモンドカッター(Buehler社製)で切り出した後、#2000の耐水研磨紙を用いて研磨することにより、10本の角柱状の試験片(厚さ:約1.2mm×幅:約4.0mm×長さ:14.0mm)を作製した。次に、各試験片についてオートグラフ(島津製作所製)を用いて3点曲げ試験を行い、最大点の曲げ荷重を測定した。そして、下式(6)に基づき曲げ強さBSを求めた。最大点の曲げ荷重は、支点間距離は12.0mm、クロスヘッドスピードは1.0mm/minに設定して測定した。その結果、10個の試験片の曲げ強さBSの平均値(曲げ強さBSd)は、337MPaであった。
・式(6) BS=3PS/2WB2
〔式(6)中、BSは曲げ強さ(MPa)、Pは最大点の曲げ荷重(N)、Sは支点間距離(12.0mm)、Wは試験片の幅(実測値、mm)、Bは試験片の厚さ(実測値、mm)を意味する。〕
[曲げ強さ]の欄にて説明した場合と同様にして試験片10本を作製し、全ての試験片をイオン交換水中にて、37℃で1週間保管した。その後、イオン交換水から取り出した試験片について、表面に付着した水分を除去した後、[曲げ強さ]の欄にて説明した場合と同様の試験条件にて3点曲げ試験を行い、水中保管後の試験片の最大点の曲げ荷重を測定した。その後、個々の水中保管後の試験片について式(6)に基づき曲げ強さBSを求めた。その結果、10個の水中保管後の試験片の曲げ強さBSの平均値(水中曲げ強さBSw)は、283MPaであった。
硬化体の耐水性を示す指標となる維持率は、下式(7)に基づいて計算した。本実施例では、維持率は84%であり、高い耐水性を有することが確認された。
・式(7) 維持率(%)=100×BSW/BSd
〔式(7)中、BSWは、10個の水中保管後の試験片の曲げ強さBSの平均値(MPa)、BSdは、10個の試験片の曲げ強さBSの平均値(MPa)を表す。〕
得られた硬化体の外観および硬化体を略2等分して得た切断面を目視で観察することにより、硬化体の均一性を評価した。ここで、硬化体が均一性を有するか否かは、硬化体の表面および切断面において、硬化ムラが存在するか否かや亀裂が存在するか否かにより判断し、硬化ムラおよび亀裂共に確認されない場合は均一と判定し、硬化ムラおよび亀裂の少なくとも一方が確認された場合は不均一と判定した。実施例A1の硬化体については、硬化ムラおよび亀裂共に確認されず、均一であることが判った。
実施例A1と同様にして1次原料組成物を調製した。得られた1次原料組成物の全量を含む自転公転ミキサー内に、実施例A1と同量のジイソシアネート化合物(a2)〔XDI〕を加えて混練することで原料組成物を得た。なお、この原料組成物は、実施例A1において調製した重付加反応性原料組成物と同一の組成を有する組成物であり、比較例A1のポリウレタン系複合材料の製造プロセス上は、実施例A1において用いた重付加反応性原料組成物の機能およびラジカル重合性原料組成物の機能の双方を兼ねる組成物に相当する。
実施例A1において、使用する原料、a2/a1モル比、重合性単量体配合比率Rr及び充填率を表1に示すように変更した以外は実施例A1と同様にしてラジカル重合性原料組成物を調製した。得られたラジカル重合性原料組成物については、実施例A1と同様にして評価を行った。その結果を表2に示す。
使用する原料、a2/a1モル比、重合性単量体配合比率Rr及び充填率を表1に示すように変更した以外は実施例A1と同様にしてラジカル重合性原料組成物を調製した。得られたラジカル重合性原料組成物については、実施例A1と同様にして評価を行った。その結果を表2に示す。
以下に第一の本発明のポリウレタン系複合材料および第二の本発明のポリウレタン系複合材料の実施例を、比較例と共に示す。
実施例A2と同様にして各工程を実施して硬化体(ポリウレタン系複合材料)を作製した。なお、得られた硬化体および硬化体の製造に用いたラジカル重合性原料組成物についてはFT-IR測定を行うことにより、式(3)に示すラジカル重合性基残存率(%)を求めた。また、硬化体の製造に用いたラジカル重合性原料組成物について式(5)に基づき初期二重結合量を計算した上で、式(4)に基づき、硬化体の二重結合量(mmol/g)を求めた。さらに、硬化体については初期接着強さ、耐久接着強さ、曲げ強さ、水中曲げ強さおよび均一性を評価した。結果を表3-4に示す。
得られた硬化体および硬化体の製造に用いたラジカル重合性原料組成物のFT-IR測定は、フーリエ変換赤外分光光度計(Spectrum One、Perkin Elmer社製)を用いた透過法により行った。ラジカル重合性原料組成物のFT-IR測定は、ラジカル重合性原料組成物を円板モールド(直径15mm×厚さ1mm)に充填したものを測定サンプルとして用いて実施し、硬化体のFT-IR測定は、円板モールドに充填されたラジカル重合性原料組成物を当該硬化体を作製する場合と同様のラジカル重合条件にて硬化させたものを測定サンプルとして用いて実施した。そして、各々の測定サンプルにつき、式(3)に示すラジカル重合性基残存率(%)の計算に必要な2つのピーク面積、すなわち、ウレタン結合のカルボニル基に由来する吸収ピークのピーク面積(ν4920)と、ラジカル重合性基の炭素-炭素二重結合に由来する吸収ピークのピーク面積(ν6170)とを測定した。
得られた硬化体を低速のダイヤモンドカッター(Buehler社製)で切り出した後に#1500の耐水研磨紙を用いて研磨することにより試験片(縦12mm×横14mm×厚さ3mm)を得た。次に、試験片の表面にアルミナサンドブラスト処理を行い、イオン交換水にて超音波洗浄を行った後、乾燥空気を吹き付けて乾燥させた。続いて、試験片の表面に直径3mmの孔を有する両面テープを貼り付け、孔から露出する面を接着面とした。この接着面にエステセムII(トクヤマデンタル社製)を塗布した後に、接着面に対して円筒状のSUS製アタッチメント(直径8mm、長さ25mm)を接着することで接合体を得た。得られた接合体を37℃湿潤下に1時間静置してから、37℃の水中に24時間浸漬することにより、アタッチメント付き試験片(初期接着強さ評価用の測定サンプル)を得た。引張試験は、万能試験機(オートグラフ、株式会社島津製作所製)を用いて、クロスヘッドスピード2mm/minで行った。この際、5つの測定サンプルについて測定した引張接着強さの平均値を、初期接着強さとした。
[初期接着強さ評価]の欄にて説明した場合と同様にして作製したアタッチメント付き試験片を熱衝撃試験機に入れた後、5℃の水槽に30秒間浸漬後、55℃の水槽に移し30秒間浸漬し、再び5℃の水槽に戻す操作を3000回繰り返すことにより、熱衝撃試験後のアタッチメント付き試験片(耐久接着強さ評価用の測定サンプル)を得た。次に、[初期接着強さ評価]の欄にて説明した場合と同様にして、引張接着強さを測定した。この際、5つの測定サンプルについて測定した引張接着強さの平均値を耐久接着強さとした。
実施例A8と同様にして各工程を実施して硬化体(ポリウレタン系複合材料)を作製した。そして実施例B1と同様にして、ラジカル重合性基残存率(%)および二重結合量(mmol/g)を求めると共に、初期接着強さおよび耐久接着強さを評価した。結果を表3-4に示す。
実施例A10と同様にして各工程を実施して硬化体(ポリウレタン系複合材料)を作製した。そして実施例B1と同様にして、ラジカル重合性基残存率(%)および二重結合量(mmol/g)を求めると共に、初期接着強さおよび耐久接着強さを評価した。結果を表3-4に示す。
始めに、UDMA:19質量部、3G:6質量部、BPO:0.1質量部加え、マグネチックスターラーにより撹拌した。続いて、F1:53質量部及びF2:22質量部を投入し、自転公転ミキサー(クラボウ社製)にて混練することで原料組成物を得た。得られた原料組成物を型枠(縦12mm×横18mm×厚さ14mm)内に注入した後、窒素加圧下(0.3MPa)で、90℃に昇温し、15時間ラジカル重合を行った。その後、型枠内に形成された硬化体を型枠より取り出した。そして実施例B1と同様にして、ラジカル重合性基残存率(%)および二重結合量(mmol/g)を求めると共に、初期接着強さおよび耐久接着強さを評価した。結果を表3-4に示す。
以下に第一の本発明のポリウレタン系複合材料および第二の本発明のポリウレタン系複合材料を構成するポリウレタン系樹脂マトリックスに相当する樹脂材料の実験例を示す。
ラジカル重合性原料組成物の調製に際して充填材(D)を配合しなかった以外は実施例A2と同様にして硬化体を作製した(製造条件の詳細は表5参照)。続いて、得られた硬化体について、実施例A2に対応する実施例B1と同様にして、ラジカル重合性基残存率および二重結合量を求めると共に、初期接着強さおよび耐久接着強さを評価した。結果を表6に示す。
ラジカル重合性原料組成物の調製に際して充填材(D)を配合しなかった以外は実施例A10と同様にして硬化体を作製した(製造条件の詳細は表5参照)。続いて、得られた硬化体について、実施例A10に対応する実施例B3と同様にして、ラジカル重合性基残存率および二重結合量を求めると共に、初期接着強さおよび耐久接着強さを評価した。結果を表6に示す。
表3-4に示す実施例B1、B3と、表5-6に示す実験例A1、A2との対比結果から明らかなように、充填材(D)の配合の有無による二重結合量および接着耐久性への影響は殆ど無いことが確認された。それゆえ、ポリウレタン系樹脂マトリックスの違いは、ポリウレタン系樹脂マトリックスとポリウレタン系樹脂マトリックス中に分散含有された充填剤とを含むポリウレタン系複合材料の強度等の物性にも直接的に反映されることは明らかである。
Claims (8)
- 1つ以上のラジカル重合性基を有するジオール化合物(a1)と、ジイソシアネート化合物(a2)と、下記構造式(1)に示す重合性単量体、EO変性トリメチロールプロパントリアクリレート、および、ジオキサングリコールジアクリレートからなる群より選択される少なくとも1種を含む重合性単量体(B)と、を含む重付加反応性原料組成物中において、前記ジオール化合物(a1)と、前記ジイソシアネート化合物(a2)と、を重付加反応させることにより、数平均分子量が1500~5000であり、かつ、ラジカル重合性基を有するポリウレタン成分(A)を形成する重付加反応工程と、
前記ポリウレタン成分(A)と、前記重合性単量体(B)と、ラジカル重合開始剤(C)と、充填材(D)と、を含むラジカル重合性原料組成物を調製するラジカル重合性原料組成物調製工程と、
前記重付加反応工程および前記ラジカル重合性原料組成物調製工程を完了した後に、前記ラジカル重合性原料組成物を用いてラジカル重合を行うことによりポリウレタン系複合材料を形成するラジカル重合工程と、を含み、
下式(1)に示す重合性単量体配合比率Rrが20質量%~80質量%であることを特徴とするポリウレタン系複合材料の製造方法。
・式(1) Rr=100×Br/〔a1r+a2r+Ar+Br〕
〔前記式(1)中、a1rは、前記ラジカル重合性原料組成物中に残存している未反応の前記ジオール化合物(a1)の含有量(質量部)を表し、a2rは、前記ラジカル重合性原料組成物中に残存している未反応の前記ジイソシアネート化合物(a2)の含有量(質量部)を表し、Arは、前記ラジカル重合性原料組成物に含まれる前記ポリウレタン成分(A)の含有量(質量部)を表し、Brは、前記ラジカル重合性原料組成物に含まれる前記重合性単量体(B)の含有量(質量部)を表す。〕 - 前記ラジカル重合性原料組成物中における前記充填材(D)の含有割合が60質量%~85質量%であることを特徴とする請求項1に記載のポリウレタン系複合材料の製造方法。
- 前記ラジカル重合開始剤(C)として熱ラジカル重合開始剤を使用し、前記ラジカル重合工程が前記熱ラジカル重合開始剤の10時間半減期温度の-10℃~+25℃の温度に加熱した状態で実施されることを特徴とする請求項1または2に記載のポリウレタン系複合材料の製造方法。
- 前記重付加反応性原料組成物が、
前記ジオール化合物(a1)、前記重合性単量体(B)、および、前記充填材(D)を含む1次原料組成物を調製した後に、
前記1次原料組成物に前記ジイソシアネート化合物(a2)をさらに添加することにより調製されることを特徴とする請求項1~3のいずれか1つに記載のポリウレタン系複合材料の製造方法。 - 前記ラジカル重合性原料組成物がペースト状の組成物であることを特徴とする請求項1~4のいずれか1つに記載のポリウレタン系複合材料の製造方法。
- 前記ラジカル重合性原料組成物を型枠に注入した後に前記ラジカル重合工程を実施することを特徴とする請求項5に記載のポリウレタン系複合材料の製造方法。
- ポリウレタン系樹脂マトリックスと、
前記ポリウレタン系樹脂マトリックス中に分散含有される充填材とを含む複合材料からなり、
前記ポリウレタン系樹脂マトリックスは、数平均分子量が1500~5000であるラジカル重合性基を有するポリウレタンと、下記構造式(1)に示す重合性単量体、EO変性トリメチロールプロパントリアクリレート、および、ジオキサングリコールジアクリレートからなる群より選択される少なくとも1種を含むラジカル重合性単量体との共重合体からなり、
前記ポリウレタン系樹脂マトリックス1g当たりに含まれるラジカル重合性炭素-炭素二重結合の含有量が0.5mmol/g~1.0mmol/gであり、
前記複合材料に占める前記充填材の含有量は、60質量%~85質量%である、
ことを特徴とするポリウレタン系複合材料。
- 請求項7に記載のポリウレタン系複合材料からなる、
ことを特徴とする歯科切削加工用材料。