JP7311724B1 - 積層体 - Google Patents
積層体 Download PDFInfo
- Publication number
- JP7311724B1 JP7311724B1 JP2023030908A JP2023030908A JP7311724B1 JP 7311724 B1 JP7311724 B1 JP 7311724B1 JP 2023030908 A JP2023030908 A JP 2023030908A JP 2023030908 A JP2023030908 A JP 2023030908A JP 7311724 B1 JP7311724 B1 JP 7311724B1
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- melt adhesive
- hot
- mass
- hot melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
項1.
セルロース系繊維を含む不織布αにより構成される不織布層(I)及び任意の不織布により構成される不織布層(II)をこの順に有し、前記不織布層(I)と前記不織布層(II)とはホットメルト接着剤βを介して接着しており、
前記不織布αにおける前記ホットメルト接着剤βを介し前記不織布層(II)と接する側の表面の表面粗さの平均偏差(SMD)は2.3以下又は3.0以上であり、
前記ホットメルト接着剤βは成分(A)熱可塑性エラストマー、及び成分(B)粘着付与剤を含み、
前記ホットメルト接着剤βは、温度50℃、周波数0.05Hz、ひずみ0.05%での損失正接が0.21以上であり、且つ、温度50℃、周波数1.00Hz、ひずみ0.05%での損失正接0.35以上であることを特徴とする、積層体。
項2.
前記ホットメルト接着剤βは、温度50℃、周波数1.00Hz、ひずみ0.05%での損失弾性率が10,000Pa以上である、項1に記載の積層体。
項3.
前記ホットメルト接着剤βは、
温度23℃、周波数1.00Hz、ひずみ0.05%での損失弾性率が200,000Pa以上であり、且つ。
温度23℃、周波数1.00Hz、ひずみ0.05%での損失正接が1.40以上である、項1又は2に記載の積層体。
項4.
前記不織布αの目付は15~40g/m2である、項1に記載の積層体。
項5.
前記不織布αに含まれるセルロース系繊維がコットン又はレーヨンである、項1又は4に記載の積層体。
項6.
前記ホットメルト接着剤βは吸収性物品用ホットメルト接着剤である、項1又は4に記載の積層体。
本発明の積層体は、セルロース系繊維を含む不織布αにより構成される不織布層(I)及び任意の不織布により構成される不織布層(II)をこの順に有し、前記不織布層(I)と前記不織布層(II)とはホットメルト接着剤βを介して接着しており、前記不織布αにおける前記ホットメルト接着剤βを介し前記不織布層(II)と接する側の表面の表面粗さの平均偏差(SMD)は2.3以下又は3.0以上であり、前記ホットメルト接着剤βは成分(A)熱可塑性エラストマー、及び成分(B)粘着付与剤を含み、前記ホットメルト接着剤βは、温度50℃、周波数0.05Hz、ひずみ0.05%での損失正接が0.21以上であり、且つ、温度50℃、周波数1.00Hz、ひずみ0.05%での損失正接0.40以上であることを特徴とするものである。
不織布層(I)は、セルロース系繊維を含む不織布αにより構成される。不織布αにおけるセルロース系繊維の含有量は、不織布α100質量中に5質量%以上であることが好ましく、20質量%以上であることがより好ましく、50質量%以上であることがさらに好ましい。また、セルロース系繊維の含有量は、不織布α100質量%中に100質量%以下であることが好ましい。また、不織布αがセルロース系繊維のみから構成される態様であってもよい。
不織布層(II)は、任意の不織布により構成される。かかる不織布としては、公知の不織布を広く採用することができ、中でもセルロース系繊維を含む不織布又はセルロース系繊維のみから構成される不織布であることが好ましい。もちろん、上述した不織布αと同様の不織布であってもよい。
ホットメルト接着剤βは、成分(A)熱可塑性エラストマー、及び成分(B)粘着付与剤を含む。
成分(A)熱可塑性エラストマーは、特に限定されず、例えば、スチレン系ブロック共重合体、オレフィン系ブロック共重合体、ポリウレタン系ブロック共重合体、ポリエステル系ブロック共重合体等が挙げられる。これらの中でも、ホットメルト接着剤の剥離強度をより一層向上させる点から、スチレン系ブロック共重合体が好ましい。
成分(B)粘着付与剤は、成分(B1)及び成分(B2)を含んで構成されることが好ましい。成分(B)粘着付与剤は、成分(B1)及び成分(B2)のみからなる態様あってもよい。
ホットメルト接着剤βは、本発明の目的を本質的に妨げない範囲で、必要に応じて各種添加剤を含んでいてもよい。各種添加剤としては、可塑剤、酸化防止剤、紫外線吸収剤、液状ゴム、ワックス、及び微粒子充填剤等が挙げられる。
本発明で使用するホットメルト接着剤βの動的粘弾性は、所定の温度及び所定のひずみの条件下において、当該ホットメルト接着剤βにかける周波数(ひずみを与える頻度)を変更した際の粘弾性測定を行った際に算出される損失正接が所定の範囲内となる。
<50℃の動的粘弾性測定の測定条件>
・周波数範囲:0.01Hz~10.00Hz
・測定温度:50℃
・ひずみ:0.05%
・下部プレート:直径25mmのパラレルプレート
・上部プレート:直径8mmのクロスハッチプレート
<23℃の動的粘弾性測定の測定条件>
・測定温度範囲:-20℃~130℃
・周波数:1.00Hz
・昇温速度:5℃/分
・ひずみ:0.05%
・下部プレート:直径25mmのパラレルプレート
・上部プレート:直径8mmのクロスハッチプレート
下記表1及び2に示す通りの熱可塑性エラストマー、粘着付与剤、可塑剤、酸化防止剤及び各種添加剤を、加熱装置を備えた撹拌混錬機中に投入し、145℃で加熱、90分間に亘って混錬してホットメルト接着剤の製造例1~11を得た。
コットン不織布I~III、レーヨン不織布及びポリエチレンおよびポリプロピレン系繊維で構成されるエアスルー不織布を準備した。各不織布における表面粗さの平均偏差(SMD)については、表面試験機(例えば、カトーテック社製 KES-FB4-A)を用いて計測を行った結果、コットン不織布Iが1.623、コットン不織布IIが3.179、コットン不織布IIIが6.931、レーヨン不織布が4.857、エアスルー不織布が2.676と計測された。
図1に示す通り、上記不織布I~III及びレーヨン不織布を、MD方向に70mm、CD方向に50mmのサイズに切り抜き(基材A)、上記した各種の接着シートの離型紙をはがして不織布のSMD測定を実施した面に貼り付け、その上に500gのロールを置いて5mm/secの速度で一往復させた。更に、接着シートの離型フィルムをはがし、むき出しになった接着面に対し、もう一枚用意した不織布(基材B)を、SMD測定を実施した面を貼り付けた。各実施例及び比較例共に、接着シートを挟む2つの不織布は、同一の素材の不織布の組み合わせとした。得られた積層体の上に、100gのロールを置き、5mm/secの速度で一往復させた。
上記した方法に基づき、上記製造例1~11のホットメルト接着剤の動的粘弾性の測定を実施した。得られた値は、下記表3の通りであった。
図1に示すように引張試験機(島津製作所社製 AGS-X)を使用し、各実施例及び比較例の積層体における不織布を、基材Bを固定し、基材AをMD方向に引張強度100mm/minでT型剥離試験を実施し、凸最大試験力を計測した。計測は3回実施し、その平均値を凸最大試験力の試験結果として採用した。当該計測は、各実施例及び比較例を製造後、温度23℃、湿度50%環境下で24時間静置後、50℃環境下で2週間静置後の2ポイントで実施した。尚、本明細書ではこれ以降、上記24時間静置後の測定結果を「初期強度」、2週間静置後の測定結果を、「2W強度」というものとする。また、評価基準としては、上記凸最大試験力測定を3回実施して得られる平均値に関して、下記の基準で評価した。下記評価基準で〇又は◎となった場合に、十分な接着性が得られていると判断した。
<評価基準>
2.00N未満 ×
2.00N以上2.50N未満 △
2.50N以上3.00N未満 〇
3.00N以上 ◎
下記表4~18に示す通り、各実施例1~40の積層体では、2週間経過後においても優れた接着性が確認できたのに対し、各比較例1~15の積層体ではそのような優れた接着性が確認されなかった。
Claims (5)
- セルロース系繊維を含む不織布αにより構成される不織布層(I)及び任意の不織布により構成される不織布層(II)をこの順に有し、前記不織布層(I)と前記不織布層(II)とはホットメルト接着剤βを介して接着しており、
前記不織布αにおける前記ホットメルト接着剤βを介し前記不織布層(II)と接する側の表面の表面粗さの平均偏差(SMD)は2.3以下又は3.0以上であり、
前記ホットメルト接着剤βは成分(A)熱可塑性エラストマー、及び成分(B)粘着付与剤を含み、
前記ホットメルト接着剤βは、温度50℃、周波数0.05Hz、ひずみ0.05%での損失正接が0.21以上であり、且つ、温度50℃、周波数1.00Hz、ひずみ0.05%での損失正接0.35以上であることを特徴とする、積層体。 - 前記ホットメルト接着剤βは、温度50℃、周波数1.00Hz、ひずみ0.05%での損失弾性率が10,000Pa以上である、請求項1に記載の積層体。
- 前記ホットメルト接着剤βは、
温度23℃、周波数1.00Hz、ひずみ0.05%での損失弾性率が200,000Pa以上であり、且つ、
温度23℃、周波数1.00Hz、ひずみ0.05%での損失正接が1.40以上である、請求項1又は2に記載の積層体。 - 前記不織布αの目付は15~40g/m2である、請求項1に記載の積層体。
- 前記不織布αに含まれるセルロース系繊維がコットン又はレーヨンである、請求項1又は4に記載の積層体。