JP7302115B2 - Hexagonal boron nitride powder and resin composition - Google Patents
Hexagonal boron nitride powder and resin composition Download PDFInfo
- Publication number
- JP7302115B2 JP7302115B2 JP2023501448A JP2023501448A JP7302115B2 JP 7302115 B2 JP7302115 B2 JP 7302115B2 JP 2023501448 A JP2023501448 A JP 2023501448A JP 2023501448 A JP2023501448 A JP 2023501448A JP 7302115 B2 JP7302115 B2 JP 7302115B2
- Authority
- JP
- Japan
- Prior art keywords
- boron nitride
- hexagonal boron
- nitride powder
- less
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本開示は、六方晶窒化ホウ素粉末、及び樹脂組成物に関する。 The present disclosure relates to hexagonal boron nitride powders and resin compositions.
トランジスタ、サイリスタ、及びＣＰＵ等の電子部品においては、使用時に発生する熱を効率良く放熱することが重要な問題となっている。そのため、このような電子部品と共に、高い熱伝導性を有する放熱部材が用いられる。一方、窒化ホウ素粒子は、高熱伝導性及び高絶縁性を有しているため、放熱部材における充填材として幅広く利用されている。 Efficiently dissipating heat generated during use of electronic components such as transistors, thyristors, and CPUs is an important issue. Therefore, heat dissipation members having high thermal conductivity are used together with such electronic components. On the other hand, boron nitride particles are widely used as fillers in heat dissipating members because of their high thermal conductivity and high insulating properties.
例えば、特許文献１では、樹脂等の絶縁性放熱材の充填材として用いた場合に、上記樹脂等の熱伝導率及び耐電圧（絶縁破壊電圧）を高めることができる六方晶窒化ホウ素粉末及びその製造方法が提案されている。 For example, in Patent Document 1, when used as a filler for an insulating heat dissipating material such as resin, hexagonal boron nitride powder and its A manufacturing method has been proposed.
近年、電子部品を搭載したデバイスでは信号の高速伝送化や大容量化が進んでいる。このため、放熱部材にも上述の傾向に対応できる特性が求められている。具体的には誘電正接の小さい放熱部材が望ましい。 2. Description of the Related Art In recent years, high-speed signal transmission and large-capacity transmission have been progressing in devices equipped with electronic components. For this reason, the heat dissipating member is also required to have characteristics capable of coping with the above-described tendency. Specifically, a heat radiating member having a small dielectric loss tangent is desirable.
放熱部材の誘電正接を低下させる方法としては、例えば、使用する樹脂として誘電正接の小さな樹脂を用いることが考えられる。しかし、低誘電正接の樹脂として知られる液晶性ポリマーやフッ素樹脂等は、低誘電正接であるものの、加工性、熱的特性、及び機械特性等が当該用途においては不足している。そこで熱的特性の向上の観点から、一般には充填材が使用されている。しかし、充填材の配合によっては樹脂の低誘電正接の特性が十分に発揮されない場合が生じ得る。 As a method for reducing the dielectric loss tangent of the heat radiating member, for example, it is conceivable to use a resin having a small dielectric loss tangent as the resin to be used. However, although liquid crystalline polymers and fluororesins known as low dielectric loss tangent resins have low dielectric loss tangents, they lack workability, thermal properties, mechanical properties, and the like for the intended use. Therefore, fillers are generally used from the viewpoint of improving thermal characteristics. However, depending on the blending of the filler, the low dielectric loss tangent characteristic of the resin may not be sufficiently exhibited.
本開示は、低誘電正接の放熱部材を製造可能な六方晶窒化ホウ素粉末、及び樹脂組成物を提供することを目的とする。 An object of the present disclosure is to provide a hexagonal boron nitride powder and a resin composition capable of producing a heat dissipation member with a low dielectric loss tangent.
本開示の一側面は、六方晶窒化ホウ素の一次粒子を含み、比表面積が２．５ｍ２／ｇ以下であり、黒鉛化指数が２．０以下であり、純度が９９質量％以上である、六方晶窒化ホウ素粉末を提供する。One aspect of the present disclosure includes primary particles of hexagonal boron nitride, having a specific surface area of 2.5 m 2 /g or less, a graphitization index of 2.0 or less, and a purity of 99% by mass or more. A hexagonal boron nitride powder is provided.
上記六方晶窒化ホウ素粉末は、比表面積が小さく、誘電正接の上昇を招くような水や不純物の吸着が抑制されており、更に、黒鉛化指数及び純度が所定範囲となることによって、六方晶窒化ホウ素自体から誘電正接を上昇させるような成分の発生が抑制されている。これによって、低誘電正接の放熱部材を製造する充填材として好適である。 The hexagonal boron nitride powder has a small specific surface area, suppresses adsorption of water and impurities that cause an increase in dielectric loss tangent, and further has a graphitization index and purity within a predetermined range. Generation of a component that increases the dielectric loss tangent from boron itself is suppressed. As a result, it is suitable as a filling material for producing a heat radiating member with a low dielectric loss tangent.
上記一次粒子の円形度が０．８以上であってよい。 The circularity of the primary particles may be 0.8 or more.
上記六方晶窒化ホウ素粉末は、５００℃に加熱した際の単位質量当たりの水分量が３００ｐｐｍ未満であってよい。 The hexagonal boron nitride powder may have a water content per unit mass of less than 300 ppm when heated to 500°C.
上記六方晶窒化ホウ素粉末は、２００℃に加熱した際の単位質量当たりの水分量が２５０ｐｐｍ未満であってよい。 The hexagonal boron nitride powder may have a water content per unit mass of less than 250 ppm when heated to 200°C.
上記六方晶窒化ホウ素粉末は、２０１～５００℃まで加熱した際の単位質量当たりの水分量が１００ｐｐｍ未満であってよい。 The hexagonal boron nitride powder may have a water content per unit mass of less than 100 ppm when heated to 201 to 500°C.
上記六方晶窒化ホウ素粉末において、一次粒子の平均粒子径が７．０μｍ以上であってよい。 In the hexagonal boron nitride powder, the average particle size of the primary particles may be 7.0 μm or more.
本開示の一側面は、樹脂と、上述の六方晶窒化ホウ素粉末と、を含有する樹脂組成物を提供する。 One aspect of the present disclosure provides a resin composition containing a resin and the hexagonal boron nitride powder described above.
上記樹脂組成物は、上述の六方晶窒化ホウ素粉末を含有することから、低誘電正接となり得る。 Since the resin composition contains the hexagonal boron nitride powder described above, it can have a low dielectric loss tangent.
本開示によれば、低誘電正接の放熱部材を製造可能な六方晶窒化ホウ素粉末、及び樹脂組成物を提供できる。 According to the present disclosure, it is possible to provide a hexagonal boron nitride powder and a resin composition capable of producing a heat dissipation member with a low dielectric loss tangent.
以下、本開示の実施形態について説明する。ただし、以下の実施形態は、本開示を説明するための例示であり、本開示を以下の内容に限定する趣旨ではない。 Embodiments of the present disclosure will be described below. However, the following embodiments are examples for explaining the present disclosure, and are not intended to limit the present disclosure to the following contents.
本明細書において例示する材料は特に断らない限り、１種を単独で又は２種以上を組み合わせて用いることができる。組成物中の各成分の含有量は、組成物中の各成分に該当する物質が複数存在する場合には、特に断らない限り、組成物中に存在する当該複数の物質の合計量を意味する。 The materials exemplified in this specification can be used singly or in combination of two or more unless otherwise specified. The content of each component in the composition means the total amount of the multiple substances present in the composition unless otherwise specified when there are multiple substances corresponding to each component in the composition. .
六方晶窒化ホウ素粉末の一実施形態は、六方晶窒化ホウ素の一次粒子を含み、比表面積が２．５ｍ２／ｇ以下であり、黒鉛化指数が２．０以下であり、純度が９９質量％以上である。六方晶窒化ホウ素粉末は、六方晶窒化ホウ素の一次粒子の集合物であってよい。One embodiment of the hexagonal boron nitride powder comprises primary particles of hexagonal boron nitride, has a specific surface area of 2.5 m 2 /g or less, a graphitization index of 2.0 or less, and a purity of 99% by mass. That's it. The hexagonal boron nitride powder may be an aggregate of primary particles of hexagonal boron nitride.
六方晶窒化ホウ素粉末の比表面積の上限値は２．５ｍ２／ｇ以下であるが、例えば、２．２ｍ２／ｇ以下、２．０ｍ２／ｇ以下、１．８ｍ２／ｇ以下、又は１．６ｍ２／ｇ以下であってよい。比表面積の上限値が上記範囲内であると、水分等の吸着を抑制し、誘電正接をより低下させ得る。六方晶窒化ホウ素粉末の比表面積の下限値は、例えば、０．５ｍ２／ｇ以上、０．８ｍ２／ｇ以上、１．０ｍ２／ｇ以上、１．２ｍ２／ｇ以上、又は１．４ｍ２／ｇ以上であってよい。比表面積の下限値が上記範囲内であると、六方晶窒化ホウ素粉末をより低誘電正接化することができる。六方晶窒化ホウ素粉末の比表面積は上述の範囲内で調整でき、例えば、０．５～２．５ｍ２／ｇ、又は１．０～２．２ｍ２／ｇであってよい。The upper limit of the specific surface area of the hexagonal boron nitride powder is 2.5 m 2 /g or less, for example, 2.2 m 2 /g or less, 2.0 m 2 /g or less, 1.8 m 2 /g or less, or It may be 1.6 m 2 /g or less. When the upper limit of the specific surface area is within the above range, the adsorption of moisture and the like can be suppressed, and the dielectric loss tangent can be further reduced. The lower limit of the specific surface area of the hexagonal boron nitride powder is, for example, 0.5 m 2 /g or more, 0.8 m 2 /g or more, 1.0 m 2 /g or more, 1.2 m 2 /g or more, or 1. It may be 4 m 2 /g or more. When the lower limit of the specific surface area is within the above range, the hexagonal boron nitride powder can have a lower dielectric loss tangent. The specific surface area of the hexagonal boron nitride powder can be adjusted within the above range, and can be, for example, 0.5-2.5 m 2 /g, or 1.0-2.2 m 2 /g.
本明細書における比表面積は、ＪＩＳ Ｚ ８８３０：２０１３「ガス吸着による粉体（固体）の比表面積測定方法」の記載に準拠し、比表面積測定装置を用いて測定される値を意味し、窒素ガスを使用したＢＥＴ一点法を適用して算出される値である。より具体的には、本明細書の実施例に記載の方法で測定する。 The specific surface area in this specification means a value measured using a specific surface area measuring device in accordance with the description of JIS Z 8830:2013 "Method for measuring specific surface area of powder (solid) by gas adsorption", nitrogen It is a value calculated by applying the BET one-point method using gas. More specifically, it is measured by the method described in the Examples of this specification.
六方晶窒化ホウ素は好ましくは結晶性が高いものである。本実施形態の窒化ホウ素粉末においては、上述の結晶性の指標として黒鉛化指数（Ｇｒａｐｈｉｔｉｚａｔｉｏｎ Ｉｎｄｅｘ（Ｇ．Ｉ．）ということもある）を用いる。すなわち、黒鉛化指数の低い六方晶窒化ホウ素を含む窒化ホウ素粉末は、不純物がより低減されており誘電正接の上昇が抑制され得る。六方晶窒化ホウ素粉末の黒鉛化指数の上限値は２．０以下であるが、例えば、１．９以下、１．５以下、又は１．３以下であってよい。六方晶窒化ホウ素粉末の黒鉛化指数の上限値が上記範囲内であることによって、誘電正接をより低下させ得る。六方晶窒化ホウ素粉末の黒鉛化指数の下限値は、特に制限されるものではないが、例えば、０．８以上、又は１．０以上であってよい。六方晶窒化ホウ素粉末の黒鉛化指数の下限値が上記範囲内であることによって、低誘電正接と高放熱性とをより高い水準で両立し得る。六方晶窒化ホウ素粉末の黒鉛化指数は上述の範囲内で調整でき、例えば、１．０～２．０であってよい。 The hexagonal boron nitride is preferably highly crystalline. In the boron nitride powder of the present embodiment, a graphitization index (G.I.) is used as an index of crystallinity. That is, the boron nitride powder containing hexagonal boron nitride with a low graphitization index has fewer impurities and can suppress an increase in dielectric loss tangent. The upper limit of the graphitization index of the hexagonal boron nitride powder is 2.0 or less, and may be, for example, 1.9 or less, 1.5 or less, or 1.3 or less. When the upper limit of the graphitization index of the hexagonal boron nitride powder is within the above range, the dielectric loss tangent can be further reduced. The lower limit of the graphitization index of the hexagonal boron nitride powder is not particularly limited, but may be, for example, 0.8 or more, or 1.0 or more. When the lower limit of the graphitization index of the hexagonal boron nitride powder is within the above range, both low dielectric loss tangent and high heat dissipation can be achieved at a higher level. The graphitization index of the hexagonal boron nitride powder can be adjusted within the range described above, and can be, for example, 1.0 to 2.0.
本明細書における黒鉛化指数は、黒鉛の結晶性の程度を示す指標値としても知られている指標である（例えば、Ｊ．Ｔｈｏｍａｓ，ｅｔ．ａｌ，Ｊ．Ａｍ．Ｃｈｅｍ．Ｓｏｃ．８４，４６１９（１９６２）等）。黒鉛化指数は、六方晶窒化ホウ素の一次粒子を粉末Ｘ線回折法で測定したスペクトルに基づき算出する。まず、Ｘ線回折スペクトルにおいて、六方晶窒化ホウ素の一次粒子の（１００）面、（１０１）面及び（１０２）面に対応する各回折ピークの積分強度（すなわち、各回折ピーク）とそのベースラインとで囲まれる面積値（単位は任意）を算出し、それぞれＳ１００、Ｓ１０１、及びＳ１０２とする。算出された面積値を用いて、［（Ｓ１００＋Ｓ１０１）／Ｓ１０２］の値を算出し、黒鉛化指数を決定する。より具体的には、本明細書の実施例に記載の方法によって決定する。 The graphitization index herein is an index also known as an index value indicating the degree of crystallinity of graphite (for example, J. Thomas, et. al, J. Am. Chem. Soc. 84, 4619 (1962) etc.). The graphitization index is calculated based on the spectrum of primary particles of hexagonal boron nitride measured by powder X-ray diffraction. First, in the X-ray diffraction spectrum, the integrated intensity of each diffraction peak corresponding to the (100) plane, (101) plane and (102) plane of the hexagonal boron nitride primary particles (that is, each diffraction peak) and its baseline and S100, S101, and S102, respectively. Using the calculated area value, the value of [(S100+S101)/S102] is calculated to determine the graphitization index. More specifically, it is determined by the method described in the Examples of this specification.
六方晶窒化ホウ素粉末の純度はより高いものであってよく、例えば、９９．５質量％以上、又は９９．８質量％以上であってよい。本明細書における窒化ホウ素粉末の純度は、滴定によって算出される値を意味する。より具体的には、本明細書の実施例に記載の方法で滴定を行い、決定する。 The purity of the hexagonal boron nitride powder may be higher, for example, 99.5 wt% or higher, or 99.8 wt% or higher. The purity of boron nitride powder herein means a value calculated by titration. More specifically, titration is performed and determined by the method described in the Examples of the present specification.
六方晶窒化ホウ素の一次粒子は、放熱部材等を調製する際の樹脂等への充填性を向上させ、放熱部材の熱伝導性及び誘電率といった特性を等方的にする観点から、好ましくは、球状又は球状に近い形状であってよい。一次粒子の円形度は、例えば、０．８０以上、０．８５以上、０．８８以上、又は０．９０以上であってよい。 The primary particles of hexagonal boron nitride improve the fillability in a resin or the like when preparing a heat dissipating member or the like, and from the viewpoint of isotropic properties such as thermal conductivity and dielectric constant of the heat dissipating member, preferably: It may be spherical or nearly spherical. The circularity of the primary particles may be, for example, 0.80 or greater, 0.85 or greater, 0.88 or greater, or 0.90 or greater.
本明細書における一次粒子の円形度とは以下の方法によって測定される平均円形度を意味する。具体的には、走査型電子顕微鏡（ＳＥＭ）を用いて撮影した窒化ホウ素粒子の像（倍率：１０，０００倍、画像解像度：１２８０×１０２４ピクセル）について、画像解析ソフトを用いた画像解析によって、窒化ホウ素粒子の投影面積（Ｓ）及び周囲長（Ｌ）を算出する。そして、得られた投影面積（Ｓ）及び周囲長（Ｌ）を用いて、以下の式：円形度＝４πＳ／Ｌ２に従って円形度を求める。任意に選ばれた１００個の窒化ホウ素粒子について求めた円形度の平均値を平均円形度と定義する。画像解析ソフトとしては、例えば、マウンテック社製の「ＭａｃＶｉｅｗ」（商品名）等を使用できる。The circularity of primary particles as used herein means the average circularity measured by the following method. Specifically, an image of boron nitride particles taken using a scanning electron microscope (SEM) (magnification: 10,000 times, image resolution: 1280 × 1024 pixels) was analyzed using image analysis software. Calculate the projected area (S) and perimeter (L) of the boron nitride particles. Then, using the obtained projected area (S) and perimeter (L), the circularity is obtained according to the following formula: circularity=4πS/ L2 . The average circularity obtained for 100 arbitrarily selected boron nitride particles is defined as the average circularity. As the image analysis software, for example, "MacView" (trade name) manufactured by Mountec Co., etc. can be used.
上記六方晶窒化ホウ素粉末において、一次粒子の平均粒子径の下限値は、例えば、７．０μｍ以上、７．５μｍ以上、８．０μｍ以上、８．５μｍ以上、又は９．０μｍ以上であってよい。平均粒子径の下限値が上記範囲内であると、充填性や放熱性の観点で好適に使用できる。上記一次粒子の平均粒子径の上限値は、例えば、４０μｍ以下、３０μｍ以下、２０μｍ以下、１５μｍ以下、又は１０μｍ以下であってよい。平均粒子径の上限値が上記範囲内であると、樹脂組成物の成形性を良好にすることができる。六方晶窒化ホウ素粉末における一次粒子の平均粒子径は上述の範囲内で調整してよく、例えば、７．０～４０μｍ、又は７．５～１５μｍであってよい。例えば、樹脂中に六方晶窒化ホウ素粉末を分散させシート状に成形して用いる場合には、シートの厚みに合わせて上記一次粒子の平均粒子径を選択してよい。 In the hexagonal boron nitride powder, the lower limit of the average particle size of the primary particles may be, for example, 7.0 μm or more, 7.5 μm or more, 8.0 μm or more, 8.5 μm or more, or 9.0 μm or more. . When the lower limit of the average particle size is within the above range, it can be suitably used from the viewpoint of filling properties and heat dissipation. The upper limit of the average particle size of the primary particles may be, for example, 40 μm or less, 30 μm or less, 20 μm or less, 15 μm or less, or 10 μm or less. When the upper limit of the average particle size is within the above range, the moldability of the resin composition can be improved. The average particle size of primary particles in the hexagonal boron nitride powder may be adjusted within the range described above, and may be, for example, 7.0 to 40 μm, or 7.5 to 15 μm. For example, when hexagonal boron nitride powder is dispersed in a resin and molded into a sheet for use, the average particle size of the primary particles may be selected according to the thickness of the sheet.
本明細書における平均粒子径は、六方晶窒化ホウ素粉末に対するホモジナイザー処理を行ったサンプルを対象として測定して得られる値であり、凝集粒子を含まない平均粒子径である。本明細書における平均粒子径はまた、累積粒度分布の累積値が５０％となる粒子径（メジアン径、ｄ５０）である。本明細書における平均粒子径は、ＩＳＯ １３３２０：２００９の記載に準拠し、レーザー回折散乱法粒度分布測定装置を用いて測定する。具体的には、本明細書の実施例に記載の方法で測定する。レーザー回折散乱法粒度分布測定装置としては、例えば、ベックマンコールター社製の「ＬＳ－１３ ３２０」（装置名）等を使用できる。 The average particle size in the present specification is a value obtained by measuring a sample of hexagonal boron nitride powder subjected to homogenizer treatment, and is an average particle size that does not contain agglomerated particles. The average particle size in this specification is also the particle size at which the cumulative value of the cumulative particle size distribution is 50% (median size, d50). The average particle size in this specification is measured using a laser diffraction scattering particle size distribution analyzer in accordance with ISO 13320:2009. Specifically, it is measured by the method described in the Examples of this specification. As a laser diffraction scattering particle size distribution analyzer, for example, "LS-13 320" (apparatus name) manufactured by Beckman Coulter can be used.
六方晶窒化ホウ素粉末はその表面に水分を吸着し得る。水分を吸着した六方晶窒化ホウ素粉末に対して周期的な電場を印加した際に、電気エネルギーの一部が熱エネルギーとして消費されることを促進し得ることから、誘電正接が上昇する傾向にある。六方晶窒化ホウ素粉末は誘電正接をより低下させる観点から、好ましくは水分量が低いものであってよい。六方晶窒化ホウ素粉末は、５００℃に加熱した際の単位質量当たりの水分量が、例えば、３００ｐｐｍ未満、２８０ｐｐｍ以下、２６０ｐｐｍ以下、２４０ｐｐｍ以下、又は２２０ｐｐｍ以下であってよい。 Hexagonal boron nitride powder can adsorb moisture on its surface. When a periodic electric field is applied to the hexagonal boron nitride powder that adsorbs moisture, a part of the electrical energy can be promoted to be consumed as thermal energy, so the dielectric loss tangent tends to increase. . The hexagonal boron nitride powder may preferably have a low water content from the viewpoint of further reducing the dielectric loss tangent. The hexagonal boron nitride powder may have a water content per unit mass when heated to 500° C., for example, less than 300 ppm, 280 ppm or less, 260 ppm or less, 240 ppm or less, or 220 ppm or less.
六方晶窒化ホウ素粉末の表面における水分は２００℃まで加熱することによって脱離し得る。六方晶窒化ホウ素粉末は、２００℃に加熱した際の単位質量当たりの水分量が、例えば、２５０ｐｐｍ未満、２００ｐｐｍ未満、１８０ｐｐｍ以下、１６０ｐｐｍ以下、又は１５０ｐｐｍ以下であってよい。 Moisture on the surface of hexagonal boron nitride powder can be desorbed by heating up to 200°C. The hexagonal boron nitride powder may have a water content per unit mass of less than 250 ppm, less than 200 ppm, 180 ppm or less, 160 ppm or less, or 150 ppm or less when heated to 200°C.
六方晶窒化ホウ素粉末の表面に水酸基（ＯＨ基）が存在する場合、例えば、２００℃を超える高温時に一部水分として脱離し得る。すなわち、高温使用時において水分が事後的に発生し得る。したがって、六方晶窒化ホウ素粉末としては、高温時の水分発生も抑制されていることが好ましい。六方晶窒化ホウ素粉末は、２０１～５００℃まで加熱した際の単位質量当たりの水分量が、例えば、１００ｐｐｍ未満、９０ｐｐｍ以下、８０ｐｐｍ以下、又は７０ｐｐｍ以下であってよい。２０１～５００℃まで加熱した際の単位質量当たりの水分量が上記範囲内である場合、六方晶窒化ホウ素粉末は水分の吸着性能が比較的低く抑制され、保管時の水分吸着をより抑制することができる。 When hydroxyl groups (OH groups) are present on the surface of the hexagonal boron nitride powder, they can partially desorb as moisture at high temperatures exceeding 200° C., for example. In other words, moisture may be generated afterward during use at high temperatures. Therefore, it is preferable that the hexagonal boron nitride powder also suppresses moisture generation at high temperatures. The hexagonal boron nitride powder may have a water content per unit mass of less than 100 ppm, less than 90 ppm, less than 80 ppm, or less than 70 ppm when heated to 201 to 500° C., for example. When the water content per unit mass when heated to 201 to 500° C. is within the above range, the hexagonal boron nitride powder has a relatively low water adsorption performance, and water adsorption during storage is further suppressed. can be done.
本明細書における水分量とは、ＪＩＳ Ｋ ００６８：２００１「化学製品の水分測定方法」の記載に準拠してカールフィッシャー法に基づいて測定される値を意味する。具体的には、まず、空焼きされたアルミナボードに上記測定サンプルを所定量だけ採取し、これを２５℃に恒温調整された炉内に静置し、キャリアガスとして窒素ガスを用い測定温度（２００℃又は５００℃）まで加熱した際に発生する水分を電量滴定法によって測定し、得られた結果を単位質量（１ｇ）あたりに換算することによって、水分量を決定することができる。測定装置としては、例えば、三菱化学製の「微量水分測定装置ＣＡ－０６」（製品名）等を使用できる。滴定溶液としては、例えば、陰極液として三菱化学製の「アクアミクロンＡＸ」（商品名）等を用い、陽極液として三菱化学製の「アクアミクロンＣＸＵ」（商品名）等を用いることができる。 The water content as used herein means a value measured based on the Karl Fischer method in accordance with the description of JIS K 0068:2001 "Method for measuring water content of chemical products". Specifically, first, a predetermined amount of the measurement sample is taken on a pre-fired alumina board, which is placed in a furnace whose temperature is adjusted to 25 ° C., and nitrogen gas is used as a carrier gas to measure the temperature ( The moisture content can be determined by measuring the moisture generated when heated to 200° C. or 500° C. by coulometric titration and converting the obtained results into per unit mass (1 g). As the measuring device, for example, "trace moisture measuring device CA-06" (product name) manufactured by Mitsubishi Chemical can be used. As the titrant solution, for example, "Aquamicron AX" (trade name) manufactured by Mitsubishi Chemical can be used as the catholyte, and "Aquamicron CXU" (trade name) manufactured by Mitsubishi Chemical can be used as the anolyte.
上述のような六方晶窒化ホウ素粉末は誘電正接が低く抑制されている。六方晶窒化ホウ素粉末の誘電正接は、例えば、０．００２０未満、０．００１５以下、０．００１２以下、又は０．００１０以下とすることができる。 The dielectric loss tangent of the hexagonal boron nitride powder as described above is kept low. The dielectric loss tangent of the hexagonal boron nitride powder can be, for example, less than 0.0020, 0.0015 or less, 0.0012 or less, or 0.0010 or less.
本明細書における誘電正接は、ＪＩＳ Ｃ ２１３８：２００７「電気絶縁材料－比誘電率及び誘電正接の測定方法」に記載の方法に準拠して測定される１ＧＨｚにおける値を意味する。具体的には、ホルダーに六方晶窒化ホウ素粉末で粉末を調整し、測定セルとする。空洞共振器法摂動法の測定装置としては、例えば、キーサイト社製の「ベクトルネットワークアナライザＥ５０６３Ａ」（製品名）等を用いることができる。 The dielectric loss tangent in this specification means a value at 1 GHz measured according to the method described in JIS C 2138:2007 "Electrical insulating materials--Methods for measuring relative permittivity and dielectric loss tangent." Specifically, hexagonal boron nitride powder is prepared in a holder to form a measurement cell. As a measurement device for the cavity resonator perturbation method, for example, Keysight's "Vector Network Analyzer E5063A" (product name) can be used.
上述の六方晶窒化ホウ素粉末は、例えば、以下のような方法で製造することができる。六方晶窒化ホウ素粉末の製造方法の一実施形態は、いわゆる炭素還元法を応用した製造方法であり、ホウ酸を含むホウ素含有化合物と、炭素含有化合物とを含む混合粉末を、窒素加圧雰囲気下で焼成して、窒化ホウ素を含む焼成物を得る工程（以下、低温焼成工程ともいう）と、上記工程よりも高く、２０５０℃未満の温度で上記焼成物を加熱処理し、六方晶窒化ホウ素（ｈＢＮ）の一次粒子を生成し、上記一次粒子の一部が凝集して構成される凝集粒子を含む粉末を得る工程（以下、焼成工程ともいう）と、を有する。 The hexagonal boron nitride powder described above can be produced, for example, by the following method. One embodiment of the method for producing hexagonal boron nitride powder is a production method applying a so-called carbon reduction method, in which a mixed powder containing a boron-containing compound containing boric acid and a carbon-containing compound is subjected to a pressurized nitrogen atmosphere. to obtain a fired product containing boron nitride (hereinafter also referred to as a low-temperature firing step); hBN), and obtaining a powder containing agglomerated particles formed by agglomeration of some of the primary particles (hereinafter also referred to as a sintering step).
ホウ素含有化合物は構成元素としてホウ素を有する化合物である。ホウ素含有化合物としては、純度が高く比較的安価な原料を用いることができる。このようなホウ素含有化合物としては、ホウ酸の他、例えば、酸化ホウ素などが挙げられる。ホウ素含有化合物はホウ酸を含むが、ホウ酸は加熱によって脱水し酸化ホウ素となり、原料粉末の加熱処理中に液相を形成すると共に粒成長を促す助剤としても働くことができる。 A boron-containing compound is a compound having boron as a constituent element. As the boron-containing compound, a raw material with high purity and relatively low cost can be used. Examples of such boron-containing compounds include boric acid as well as boron oxide. The boron-containing compound includes boric acid, which is dehydrated by heating to form boron oxide, which forms a liquid phase during the heat treatment of the raw material powder and can also serve as an aid for promoting grain growth.
炭素含有化合物は構成元素として炭素原子を有する化合物である。炭素含有化合物としては、純度が高く比較的安価な原料を用いることができる。このような炭素含有化合物としては、例えば、カーボンブラック及びアセチレンブラック等が挙げられる。 A carbon-containing compound is a compound having a carbon atom as a constituent element. As the carbon-containing compound, a raw material with high purity and relatively low cost can be used. Examples of such carbon-containing compounds include carbon black and acetylene black.
混合粉末において、ホウ素含有化合物を炭素含有化合物に対して過剰量となるように配合してよい。混合粉末は、炭素含有化合物及びホウ素含有化合物に加えて、その他の化合物を含有してもよい。その他の化合物としては、例えば、核剤としての窒化ホウ素等が挙げられる。混合粉末が核剤としての窒化ホウ素を含有することで、合成される六方晶窒化ホウ素粉末の平均粒径をより容易に制御することができる。混合粉末は、好ましくは核剤を含む。混合粉末が核剤を含む場合、比表面積の小さな六方晶窒化ホウ素粉末（例えば、比表面積が２．５ｍ２／ｇ以下である六方晶窒化ホウ素粉末）の調製がより容易となる。In the mixed powder, the boron-containing compound may be blended in an excess amount relative to the carbon-containing compound. The mixed powder may contain other compounds in addition to the carbon-containing compound and the boron-containing compound. Other compounds include, for example, boron nitride as a nucleating agent. By containing boron nitride as a nucleating agent in the mixed powder, the average particle size of the synthesized hexagonal boron nitride powder can be more easily controlled. The mixed powder preferably contains a nucleating agent. When the mixed powder contains a nucleating agent, it becomes easier to prepare a hexagonal boron nitride powder with a small specific surface area (for example, a hexagonal boron nitride powder with a specific surface area of 2.5 m 2 /g or less).
低温焼成工程は加圧下で行われる。低温焼成工程における圧力は、例えば、０．２５ＭＰａ以上５．０ＭＰａ未満、０．２５～３．０ＭＰａ、０．２５～２．０ＭＰａ、０．２５～１．０ＭＰａ、０．２５ＭＰａ以上１．０ＭＰａ未満、０．３０～２．０ＭＰａ、又は０．５０～２．０ＭＰａであってよい。低温焼成工程における圧力を高くすることで、ホウ素含有化合物等の原料の揮発をより抑制し、副生成物である炭化ホウ素の生成を抑制することができる。また低温焼成工程における圧力を高くすることで、窒化ホウ素粉末の比表面積の増加を抑制することができる。低温焼成工程の圧力の上限値を上記範囲内とすることで、窒化ホウ素の一次粒子の成長をより促進することができる。 The low temperature firing process is performed under pressure. The pressure in the low-temperature firing step is, for example, 0.25 MPa or more and less than 5.0 MPa, 0.25 to 3.0 MPa, 0.25 to 2.0 MPa, 0.25 to 1.0 MPa, 0.25 MPa or more and less than 1.0 MPa. , 0.30-2.0 MPa, or 0.50-2.0 MPa. By increasing the pressure in the low-temperature firing step, volatilization of raw materials such as boron-containing compounds can be further suppressed, and the formation of boron carbide, which is a by-product, can be suppressed. Also, by increasing the pressure in the low-temperature firing step, it is possible to suppress an increase in the specific surface area of the boron nitride powder. By setting the upper limit of the pressure in the low-temperature firing step within the above range, the growth of the primary particles of boron nitride can be further promoted.
低温焼成工程における加熱温度は、例えば、１６５０℃以上１８００℃未満、１６５０～１７５０℃、又は１６５０～１７００℃であってよい。低温焼成工程における加熱温度の下限値を上記範囲内とすることで、反応を促進させ、得られる窒化ホウ素の収量を向上させることができる。低温焼成工程における加熱温度の上限値を上記範囲内とすることで、副生成物の生成を十分に抑制することができる。 The heating temperature in the low-temperature firing step may be, for example, 1650°C or higher and lower than 1800°C, 1650 to 1750°C, or 1650 to 1700°C. By setting the lower limit of the heating temperature in the low-temperature firing step within the above range, the reaction can be promoted and the yield of boron nitride obtained can be improved. By setting the upper limit of the heating temperature in the low-temperature firing step within the above range, it is possible to sufficiently suppress the generation of by-products.
低温焼成工程における加熱時間は、例えば、１～１０時間、１～５時間、又は２～４時間であってよい。窒化ホウ素を合成する反応の序盤である工程において、比較的低温で所定時間の間、維持することで、反応系をより均質化することができ、ひいては形成される窒化ホウ素をより均質化できる。なお、本明細書において加熱時間とは、加熱対象物の周囲環境の温度が所定の温度に到達してから当該温度で維持する時間（保持時間）を意味する。 The heating time in the low temperature firing step may be, for example, 1 to 10 hours, 1 to 5 hours, or 2 to 4 hours. By maintaining a relatively low temperature for a predetermined time in the initial stage of the reaction for synthesizing boron nitride, the reaction system can be made more homogeneous, and thus the boron nitride to be formed can be made more homogeneous. In this specification, the term "heating time" refers to the time (holding time) during which the ambient temperature of the object to be heated reaches a predetermined temperature and is maintained at that temperature.
焼成工程は、低温焼成工程で得られた焼成物を、低温焼成工程よりも高い温度で加熱処理して六方晶窒化ホウ素（ｈＢＮ）の一次粒子を生成し、上記一次粒子が凝集して構成される凝集粒子を含む粉末を得る工程である。 In the firing step, the fired product obtained in the low-temperature firing step is heat-treated at a temperature higher than the low-temperature firing step to generate primary particles of hexagonal boron nitride (hBN), and the primary particles are aggregated. It is a step of obtaining a powder containing agglomerated particles.
焼成工程における加熱温度は、低温焼成工程よりも高く、２０５０℃未満の温度である。焼成工程における加熱温度を蒸気範囲内とすることで黒鉛化指数をより高め、結晶性に優れる六方晶窒化ホウ素を得ることができる。焼成工程の加熱温度は、２０００℃以下であってよい。焼成工程における加熱時間は、例えば、３～１５時間、５～１０時間、又は６～９時間であってよい。 The heating temperature in the firing step is higher than that in the low-temperature firing step and is less than 2050°C. By setting the heating temperature in the firing step within the steam range, the graphitization index can be further increased, and hexagonal boron nitride having excellent crystallinity can be obtained. The heating temperature in the firing step may be 2000° C. or lower. The heating time in the firing step may be, for example, 3-15 hours, 5-10 hours, or 6-9 hours.
焼成工程の圧力は、例えば、０．２５ＭＰａ以上５．０ＭＰａ未満、０．２５～３．０ＭＰａ、０．２５～２．０ＭＰａ、０．２５～１．０ＭＰａ、０．２５ＭＰａ以上１．０ＭＰａ未満、０．３０～２．０ＭＰａ、又は０．５０～２．０ＭＰａであってよい。焼成工程における圧力を高くすることで、得られる原料粉末の純度をより向上させることができる。焼成工程における圧力の上限値を上記範囲内とすることで、原料粉末の調製コストをより低減することができ、工業的に優位である。 The pressure of the firing step is, for example, 0.25 MPa or more and less than 5.0 MPa, 0.25 to 3.0 MPa, 0.25 to 2.0 MPa, 0.25 to 1.0 MPa, 0.25 MPa or more to less than 1.0 MPa, It may be 0.30-2.0 MPa, or 0.50-2.0 MPa. By increasing the pressure in the firing process, the purity of the obtained raw material powder can be further improved. By setting the upper limit of the pressure in the firing process within the above range, the preparation cost of the raw material powder can be further reduced, which is industrially advantageous.
以上の工程によって、六方晶窒化ホウ素粉末を得ることができる。低温焼成工程又は焼成工程の後に、粉砕工程を行ってもよい。粉砕工程においては、一般的な粉砕機又は解砕機を用いることができる。 A hexagonal boron nitride powder can be obtained by the above steps. A pulverization step may be performed after the low-temperature firing step or the firing step. In the pulverization step, a general pulverizer or pulverizer can be used.
本開示に係る六方晶窒化ホウ素粉末は低誘電正接であることから、高周波電圧が印加されるような用途にも使用可能である。本開示に係る六方晶窒化ホウ素粉末は、例えば、高周波回路を構成する電子部品に使用される樹脂組成物への充填材として好適である。樹脂組成物の一実施形態は、樹脂と、上述の六方晶窒化ホウ素粉末とを含有する。 Since the hexagonal boron nitride powder according to the present disclosure has a low dielectric loss tangent, it can be used in applications where high frequency voltage is applied. The hexagonal boron nitride powder according to the present disclosure is suitable, for example, as a filler for resin compositions used in electronic components that constitute high-frequency circuits. One embodiment of the resin composition contains a resin and the hexagonal boron nitride powder described above.
六方晶窒化ホウ素粉末の含有量の下限値は、樹脂組成物の全体積を基準として、例えば、３０体積％以上、４０体積％以上、５０体積％以上であってよい。六方晶窒化ホウ素粉末の含有量の下限値が上記範囲内であることで、樹脂組成物の熱伝導率を向上させ、優れた放熱性能が得られ得る。六方晶窒化ホウ素粉末の含有量の上限値は、樹脂組成物の全体積を基準として、例えば、８５体積％以下、８０体積％以下、又は７０体積％以下であってよい。六方晶窒化ホウ素粉末の含有量の上限値が上記範囲内であることで、樹脂組成物の成形時に内部に空隙が発生することをより抑制することができ、また絶縁性及び機械強度の低下を抑制することができる。 The lower limit of the content of the hexagonal boron nitride powder may be, for example, 30% by volume or more, 40% by volume or more, or 50% by volume or more based on the total volume of the resin composition. When the lower limit of the content of the hexagonal boron nitride powder is within the above range, the thermal conductivity of the resin composition can be improved, and excellent heat dissipation performance can be obtained. The upper limit of the content of the hexagonal boron nitride powder may be, for example, 85% by volume or less, 80% by volume or less, or 70% by volume or less based on the total volume of the resin composition. When the upper limit of the content of the hexagonal boron nitride powder is within the above range, it is possible to further suppress the generation of voids inside during molding of the resin composition, and to prevent deterioration of insulation and mechanical strength. can be suppressed.
樹脂は、例えば、液晶ポリマー、フッ素樹脂、シリコーン樹脂、シリコーンゴム、アクリル樹脂、ポリオレフィン（ポリエチレン等）、エポキシ樹脂、フェノール樹脂、メラミン樹脂、ユリア樹脂、不飽和ポリエステル、ポリイミド、ポリアミドイミド、ポリエーテルイミド、ポリブチレンテレフタレート、ポリエチレンテレフタレート、ポリフェニレンエーテル、ポリフェニレンスルフィド、全芳香族ポリエステル、ポリスルホン、ポリエーテルスルホン、ポリカーボネート、マレイミド変性樹脂、ＡＢＳ（アクリロニトリル－ブタジエン－スチレン）樹脂、ＡＡＳ（アクリロニトリル－アクリルゴム・スチレン）樹脂、及びＡＥＳ（アクリロニトリル・エチレン・プロピレン・ジエンゴム－スチレン）樹脂等が挙げられる。 Resins include, for example, liquid crystal polymers, fluororesins, silicone resins, silicone rubbers, acrylic resins, polyolefins (polyethylene, etc.), epoxy resins, phenolic resins, melamine resins, urea resins, unsaturated polyesters, polyimides, polyamideimides, and polyetherimides. , polybutylene terephthalate, polyethylene terephthalate, polyphenylene ether, polyphenylene sulfide, wholly aromatic polyester, polysulfone, polyethersulfone, polycarbonate, maleimide modified resin, ABS (acrylonitrile-butadiene-styrene) resin, AAS (acrylonitrile-acrylic rubber/styrene) resins, and AES (acrylonitrile-ethylene-propylene-diene rubber-styrene) resins.
樹脂の含有量は、樹脂組成物の全体積を基準として、例えば、１５体積％以上、２０体積％以上、又は３０体積％以上であってよい。樹脂の含有量は、樹脂組成物の全体積を基準として、例えば、７０体積％以下、６０体積％以下、又は５０体積％以下であってよい。 The resin content may be, for example, 15% by volume or more, 20% by volume or more, or 30% by volume or more based on the total volume of the resin composition. The resin content may be, for example, 70% by volume or less, 60% by volume or less, or 50% by volume or less based on the total volume of the resin composition.
樹脂組成物は、樹脂を硬化させる硬化剤を更に含有していてよい。硬化剤は、樹脂の種類によって適宜選択してよい。例えば、樹脂がエポキシ樹脂である場合、硬化剤としては、例えば、フェノールノボラック化合物、酸無水物、アミノ化合物、及びイミダゾール化合物等が挙げられる。硬化剤の含有量は、樹脂１００質量部に対して、例えば、０．５質量部以上又は１．０質量部以上であってよく、１５質量部以下又は１０質量部以下であってよい。 The resin composition may further contain a curing agent that cures the resin. The curing agent may be appropriately selected according to the type of resin. For example, when the resin is an epoxy resin, curing agents include, for example, phenol novolak compounds, acid anhydrides, amino compounds, imidazole compounds, and the like. The content of the curing agent may be, for example, 0.5 parts by mass or more or 1.0 parts by mass or more, and may be 15 parts by mass or less or 10 parts by mass or less with respect to 100 parts by mass of the resin.
以上、幾つかの実施形態について説明したが、本開示は上記実施形態に何ら限定されるものではない。また、上述した実施形態についての説明内容は、互いに適用することができる。 Although several embodiments have been described above, the present disclosure is not limited to the above embodiments. Also, the descriptions of the above-described embodiments can be applied to each other.
以下、本開示について、実施例及び比較例を用いてより詳細に説明する。なお、本開示は以下の実施例に限定されるものではない。 Hereinafter, the present disclosure will be described in more detail using examples and comparative examples. It should be noted that the present disclosure is not limited to the following examples.
（実施例１）
［六方晶窒化ホウ素粉末の調製］
ホウ酸（株式会社高純度化学研究所製）１００質量部と、アセチレンブラック（デンカ株式会社製、グレード名：Ｌｉ４００）２２質量部とをヘンシェルミキサーを用いて混合して混合粉末（原料粉末）を得た。得られた混合粉末を２５０℃の乾燥機に入れ、３時間保持することでホウ酸の脱水を行った。脱水後の混合粉末をプレス成型機の直径１００Φの型に入れ、加熱温度：２００℃及びプレス圧：３０ＭＰａの条件にて成型を行った。このようにして得られた原料粉末のペレットを以降の加熱処理に供した。(Example 1)
[Preparation of hexagonal boron nitride powder]
100 parts by mass of boric acid (manufactured by Kojundo Chemical Laboratory Co., Ltd.) and 22 parts by mass of acetylene black (manufactured by Denka Co., Ltd., grade name: Li400) are mixed using a Henschel mixer to obtain a mixed powder (raw material powder). Obtained. The obtained mixed powder was placed in a drier at 250° C. and held for 3 hours to dehydrate boric acid. The mixed powder after dehydration was placed in a mold with a diameter of 100Φ of a press molding machine, and molded under the conditions of heating temperature: 200°C and press pressure: 30 MPa. The raw material powder pellets thus obtained were subjected to subsequent heat treatment.
まず、上記ペレットをカーボン雰囲気炉内に静置し、０．８５ＭＰａに加圧された窒素雰囲気において昇温速度：５℃／分で１７５０℃まで昇温し、１７５０℃にて３時間保持して上記ペレットの加熱処理を行い、第一の加熱処理物を得た（第一工程）。次に、カーボン雰囲気炉内を昇温速度：２℃／分で１８００℃まで更に昇温し、１８００℃にて３時間保持して第一の加熱処理物を加熱処理し、第二の加熱処理物を得た（第二工程）。その後、カーボン雰囲気炉内を昇温速度：２℃／分で２０５０℃まで更に昇温し、２０５０℃にて７時間保持して第二の加熱処理物を高温で焼成した（第三工程）。焼成後の緩く凝集した窒化ホウ素をヘンシェルミキサーで解砕し、真空乾燥機を用いて解砕後の粉末を２５０℃で５時間乾燥した後、目開き：６３μｍの篩を通し、篩を通過した粉末を得た。このようにして、六方晶窒化ホウ素粉末を調製した。 First, the pellets were placed in a carbon atmosphere furnace, heated to 1750° C. at a rate of 5° C./min in a nitrogen atmosphere pressurized to 0.85 MPa, and held at 1750° C. for 3 hours. The pellets were heat-treated to obtain a first heat-treated product (first step). Next, the temperature in the carbon atmosphere furnace is further increased to 1800°C at a temperature increase rate of 2°C/min, and the first heat-treated product is heat-treated by holding at 1800°C for 3 hours, followed by the second heat-treatment. obtained (second step). Thereafter, the temperature in the carbon atmosphere furnace was further increased to 2050° C. at a rate of temperature increase of 2° C./min, and held at 2050° C. for 7 hours to sinter the second heat-treated product at a high temperature (third step). Loosely agglomerated boron nitride after firing was pulverized with a Henschel mixer, and the pulverized powder was dried at 250 ° C. for 5 hours using a vacuum dryer, and then passed through a sieve with an opening of 63 μm. A powder was obtained. Thus, a hexagonal boron nitride powder was prepared.
＜六方晶窒化ホウ素粉末の物性測定＞
得られた六方晶窒化ホウ素粉末に対して、後述する方法に沿って、比表面積、黒鉛化指数、純度、一次粒子の円形度及び平均粒子径、並びに、２５～２００℃まで加熱した際の水分量及び２０１～５００℃まで加熱した際の水分量を測定した。結果を表１に示す。<Measurement of physical properties of hexagonal boron nitride powder>
For the obtained hexagonal boron nitride powder, the specific surface area, graphitization index, purity, circularity and average particle size of primary particles, and moisture content when heated to 25 to 200 ° C. The amount of water and the moisture content when heated from 201 to 500° C. were measured. Table 1 shows the results.
［比表面積］
六方晶窒化ホウ素粉末の比表面積は、ＪＩＳ Ｚ ８８３０：２０１３「ガス吸着による粉体（固体）の比表面積測定方法」の記載に準拠し、窒素ガスを使用したＢＥＴ一点法を適用して算出した。比表面積測定装置としては、ユアサアイオニクス株式会社製の比表面積測定装置（装置名：カンターソーブ）を用いた。なお、測定は、窒化ホウ素粉末を、３００℃で、１５分間かけて、乾燥脱気した後に行った。[Specific surface area]
The specific surface area of the hexagonal boron nitride powder is based on the description of JIS Z 8830:2013 "Method for measuring the specific surface area of powder (solid) by gas adsorption", and was calculated by applying the BET one-point method using nitrogen gas. . As a specific surface area measuring device, a specific surface area measuring device manufactured by Yuasa Ionics Co., Ltd. (device name: Kantersorb) was used. The measurement was performed after the boron nitride powder was dried and degassed at 300° C. for 15 minutes.
［黒鉛化指数］
窒化ホウ素粉末の黒鉛化指数は粉末Ｘ線回折法による測定結果から算出した。得られたＸ線回折スペクトルにおいて、六方晶窒化ホウ素の一次粒子の（１００）面、（１０１）面及び（１０２）面に対応する各回折ピークの積分強度（すなわち、各回折ピーク）とそのベースラインとで囲まれる面積値（単位は任意）を算出し、それぞれＳ１００、Ｓ１０１、及びＳ１０２とした。こうして算出された面積値を用いて、以下の式（１）に基づき、黒鉛化指数を決定した。
ＧＩ＝（Ｓ１００＋Ｓ１０１）／Ｓ１０２・・・（１）[Graphitization index]
The graphitization index of the boron nitride powder was calculated from the measurement results by the powder X-ray diffraction method. In the obtained X-ray diffraction spectrum, the integrated intensity of each diffraction peak corresponding to the (100) plane, (101) plane and (102) plane of the hexagonal boron nitride primary particles (that is, each diffraction peak) and its base The area values (in arbitrary units) surrounded by the lines were calculated and designated as S100, S101, and S102, respectively. Using the area value thus calculated, the graphitization index was determined based on the following formula (1).
GI=(S100+S101)/S102 (1)
［純度］
六方晶窒化ホウ素粉末を水酸化ナトリウムでアルカリ分解させ、水蒸気蒸留法によって分解液からアンモニアを蒸留して、ホウ酸水溶液に捕集した。この捕集液を対象として、硫酸規定液で滴定行った。滴定の結果から窒化ホウ素粉末中の窒素原子（Ｎ）の含有量を算出した。得られた窒素原子の含有量から、式（２）に基づいて、窒化ホウ素粉末中の六方晶窒化ホウ素（ｈＢＮ）の含有量を決定し、六方晶窒化ホウ素粉末の純度を算出した。なお、六方晶窒化ホウ素の式量は２４．８１８ｇ／ｍｏｌ、窒素原子の原子量は１４．００６ｇ／ｍｏｌを用いた。
試料中の六方晶窒化ホウ素（ｈＢＮ）の含有量［質量％］＝窒素原子（Ｎ）の含有量［質量％］×１．７７２・・・（２）[purity]
Hexagonal boron nitride powder was alkali-decomposed with sodium hydroxide, ammonia was distilled from the decomposed solution by steam distillation, and collected in an aqueous boric acid solution. This collected liquid was subjected to titration with a normal sulfuric acid solution. The content of nitrogen atoms (N) in the boron nitride powder was calculated from the titration results. Based on the obtained nitrogen atom content, the content of hexagonal boron nitride (hBN) in the boron nitride powder was determined based on the formula (2), and the purity of the hexagonal boron nitride powder was calculated. The formula weight of hexagonal boron nitride was 24.818 g/mol, and the atomic weight of nitrogen atoms was 14.006 g/mol.
Hexagonal boron nitride (hBN) content [mass%] in the sample = nitrogen atom (N) content [mass%] x 1.772 (2)
［一次粒子の円形度］
六方晶窒化ホウ素粉末について、走査型電子顕微鏡（ＳＥＭ）を用いて一次粒子の像（倍率：１０，０００倍、画像解像度：１２８０×１０２４ピクセル）を撮影した。次に、画像解析ソフト（マウンテック社製、商品名「ＭａｃＶｉｅｗ」）を用いた画像解析によって、得られた像から、窒化ホウ素粒子の投影面積（Ｓ）及び周囲長（Ｌ）を算出した。そして、得られた投影面積（Ｓ）及び周囲長（Ｌ）を用いて、以下の式：円形度＝４πＳ／Ｌ２に従って円形度を求めた。一次粒子の全体が確認でき、板状の平面（ａｂ軸結晶平面）が確認できる粒子から任意に選ばれた１００個の窒化ホウ素粒子について求め、円形度の平均値を算出し、これを平均円形度として採用した。[Circularity of primary particles]
For the hexagonal boron nitride powder, images of primary particles (magnification: 10,000 times, image resolution: 1280×1024 pixels) were taken using a scanning electron microscope (SEM). Next, the projected area (S) and perimeter (L) of the boron nitride particles were calculated from the obtained image by image analysis using image analysis software (manufactured by Mountech, trade name "MacView"). Then, using the obtained projected area (S) and peripheral length (L), the circularity was obtained according to the following formula: circularity = 4πS/ L2 . Obtained for 100 boron nitride particles arbitrarily selected from particles in which the entire primary particles can be confirmed and plate-like planes (ab-axis crystal planes) can be confirmed, and the average circularity is calculated. adopted as a measure.
［一次粒子の平均粒子径］
六方晶窒化ホウ素粉末における一次粒子の平均粒子径は、ＩＳＯ １３３２０：２００９の記載に準拠し、レーザー回折散乱法粒度分布測定装置（ベックマンコールター社製、商品名「ＬＳ－１３ ３２０」）を用いて測定した。なお、六方晶窒化ホウ素粉末は測定に際して、超音波ホモジナイザー（日本精機製作所製、商品名「ＵＳ－３００Ｅ」）を用い、ＡＭＰＬＩＴＵＤＥ（振幅）８０％にて超音波分散を１分３０秒間で１回行うことで、六方晶窒化ホウ素粉末の分散液を調製し、これを測定対象とした。粒度分布の測定に際し、六方晶窒化ホウ素粉末を分散させる溶媒には水を用い、分散剤にはヘキサメタリン酸を用いた。この際、水の屈折率として１．３３の数値を用い、窒化ホウ素粉末の屈折率として１．８０の数値を用いた。[Average particle size of primary particles]
The average particle size of the primary particles in the hexagonal boron nitride powder is measured using a laser diffraction scattering method particle size distribution analyzer (Beckman Coulter, trade name "LS-13 320") in accordance with ISO 13320:2009. It was measured. In addition, when measuring the hexagonal boron nitride powder, an ultrasonic homogenizer (manufactured by Nippon Seiki Seisakusho, trade name "US-300E") is used, and AMPLITUDE (amplitude) is 80%. Ultrasonic dispersion is performed once for 1 minute and 30 seconds. By doing so, a dispersion liquid of hexagonal boron nitride powder was prepared, and this was used as a measurement target. In measuring the particle size distribution, water was used as a solvent for dispersing the hexagonal boron nitride powder, and hexametaphosphoric acid was used as a dispersant. At this time, a numerical value of 1.33 was used as the refractive index of water, and a numerical value of 1.80 was used as the refractive index of the boron nitride powder.
［水分量］
六方晶窒化ホウ素粉末の２５～２００℃まで加熱した際の水分量及び２０１～５００℃まで加熱した際の水分量をカールフィッシャー法に基づいて測定した。まず、空焼きされたアルミナボードに上記測定サンプルを所定量だけ採取し、これを２５℃に恒温調整された炉内に静置し、２５℃から測定温度（２００℃又は５００℃）まで加熱した際に発生する水分を電量滴定法によって測定し、得られた結果を単位質量（１ｇ）あたりに換算することによって、水分量（単位：ｐｐｍ）を決定した。[amount of water]
The water content when the hexagonal boron nitride powder was heated to 25 to 200° C. and the water content when heated to 201 to 500° C. were measured based on the Karl Fischer method. First, a predetermined amount of the measurement sample was taken on a pre-baked alumina board, placed in a furnace whose temperature was adjusted to 25 ° C., and heated from 25 ° C. to the measurement temperature (200 ° C. or 500 ° C.). The water content (unit: ppm) was determined by measuring the water content generated at the time by a coulometric titration method and converting the obtained result per unit mass (1 g).
＜六方晶窒化ホウ素粉末の充填材としての評価＞
得られた六方晶窒化ホウ素粉末を充填材として用いた際の誘電正接を測定した。具体的には、空洞共振器法の測定装置（キーコム製測定システム 摂動法 空洞共振器タイプ ＤＰＳ１８）を用いて、温度２５℃の条件で測定を行うことによって、六方晶窒化ホウ素粉末の１ＧＨｚにおける誘電正接を求めた。結果を表１に示す。<Evaluation of hexagonal boron nitride powder as filler>
The dielectric loss tangent was measured when the obtained hexagonal boron nitride powder was used as a filler. Specifically, using a cavity resonator method measurement device (measurement system perturbation method cavity resonator type DPS18 manufactured by Keycom), the dielectric of hexagonal boron nitride powder at 1 GHz was measured at a temperature of 25 ° C. Asked for tangent. Table 1 shows the results.
（実施例２）
原料であるアセチレンブラックをアセチレンブラック（デンカ株式会社製、グレード名：ＦＸ３５）に変更したこと以外は、実施例１と同様にして、六方晶窒化ホウ素粉末を調製した。(Example 2)
A hexagonal boron nitride powder was prepared in the same manner as in Example 1, except that the raw material acetylene black was changed to acetylene black (manufactured by Denka Co., Ltd., grade name: FX35).
（実施例３）
原料に、窒化ホウ素粉末（デンカ株式会社製、デンカボロンナイトライド粉末、グレード名：ＳＧＰ）を２質量％外割添加したこと以外は、実施例１と同様にして、六方晶窒化ホウ素粉末を調製した。(Example 3)
Hexagonal boron nitride powder was prepared in the same manner as in Example 1, except that 2% by mass of boron nitride powder (Denka boron nitride powder, grade name: SGP) was added to the raw material. bottom.
（実施例４）
第３工程の焼成温度を２０７０℃に変更したこと以外は、実施例１と同様にして、六方晶窒化ホウ素粉末を調製した。(Example 4)
A hexagonal boron nitride powder was prepared in the same manner as in Example 1, except that the firing temperature in the third step was changed to 2070°C.
（実施例５）
第３工程の焼成温度を１９７０℃に変更したこと以外は、実施例１と同様にして、六方晶窒化ホウ素粉末を調製した。(Example 5)
A hexagonal boron nitride powder was prepared in the same manner as in Example 1, except that the firing temperature in the third step was changed to 1970°C.
（実施例６）
アセチレンブラック（デンカ株式会社製、グレード名：Ｌｉ４００）の配合量を２０質量部に変更し、真空乾燥の温度を３００℃に変更したこと以外は、実施例１と同様にして、六方晶窒化ホウ素粉末を調製した。(Example 6)
Hexagonal boron nitride in the same manner as in Example 1, except that the amount of acetylene black (manufactured by Denka Co., Ltd., grade name: Li400) was changed to 20 parts by mass, and the vacuum drying temperature was changed to 300 ° C. A powder was prepared.
（実施例７）
アセチレンブラック（デンカ株式会社製、グレード名：Ｌｉ４００）の配合量を２７質量部に変更したこと以外は、実施例１と同様にして、六方晶窒化ホウ素粉末を調製した。(Example 7)
A hexagonal boron nitride powder was prepared in the same manner as in Example 1, except that the amount of acetylene black (manufactured by Denka Co., Ltd., grade name: Li400) was changed to 27 parts by mass.
（参考例）
原料に、窒化ホウ素粉末（デンカ株式会社製、デンカボロンナイトライド粉末、グレード名：ＭＧＰ）を１質量％外割添加したしたこと以外は、実施例１と同様にして、六方晶窒化ホウ素粉末を調製した。
( Reference example )
Hexagonal boron nitride powder was prepared in the same manner as in Example 1, except that 1% by mass of boron nitride powder (Denka boron nitride powder, grade name: MGP) was added to the raw material. prepared.
実施例１～７及び参考例で得られた六方晶窒化ホウ素粉末について、比表面積、黒鉛化指数、純度、一次粒子の円形度及び平均粒子径、並びに、２５～２００℃まで加熱した際の水分量及び２０１～５００℃まで加熱した際の水分量を、実施例１と同様に測定した。実施例１～７及び参考例で得られた六方晶窒化ホウ素粉末について、実施例１と同様に充填材としての評価を行った。結果を表１に示す。 For the hexagonal boron nitride powders obtained in Examples 1 to 7 and Reference Example , specific surface area, graphitization index, purity, circularity and average particle size of primary particles, and moisture content when heated to 25 to 200 ° C. The amount and moisture content when heated to 201 to 500° C. were measured in the same manner as in Example 1. The hexagonal boron nitride powders obtained in Examples 1 to 7 and Reference Example were evaluated as fillers in the same manner as in Example 1. Table 1 shows the results.
（比較例１）
ホウ酸粉末（純度９９．８質量％以上、関東化学株式会社製）１００質量部、メラミン粉末（純度９９．０質量％以上、富士フイルム和光純薬社製）９質量部、助剤として炭酸ナトリウム（純度９９．５質量％以上）１３質量部を添加し、アルミナ製乳鉢を用い１０分間混合して、混合粉末を得た。乾燥後の混合粉末を、六方晶窒化ホウ素製の容器に入れ、電気炉内に配置した。電気炉内に窒素ガスを流通させながら、１０℃／分の昇温速度で室温から１０００℃に昇温した。１０００℃で２時間保持した後、加熱を止めて自然冷却した。温度が１００℃以下になった時点で電気炉を開放した。このようにして、低結晶性の六方晶窒化ホウ素を含む仮焼物を得た。(Comparative example 1)
100 parts by mass of boric acid powder (purity of 99.8% by mass or more, manufactured by Kanto Chemical Co., Ltd.), 9 parts by mass of melamine powder (purity of 99.0% by mass or more, manufactured by Fujifilm Wako Pure Chemical Industries, Ltd.), sodium carbonate as an auxiliary agent 13 parts by mass (purity of 99.5% by mass or more) was added and mixed for 10 minutes using an alumina mortar to obtain a mixed powder. The mixed powder after drying was placed in a container made of hexagonal boron nitride and placed in an electric furnace. The temperature was raised from room temperature to 1000° C. at a rate of 10° C./min while nitrogen gas was circulated in the electric furnace. After holding at 1000° C. for 2 hours, the heating was stopped and the mixture was allowed to cool naturally. The electric furnace was opened when the temperature became 100° C. or lower. Thus, a calcined product containing low-crystalline hexagonal boron nitride was obtained.
上記仮焼物１００ｇを、上述の電気炉内に配置した。電気炉内に窒素ガスを流通させながら、１０℃／分の昇温速度で室温から１８００℃に昇温した。１８００℃の焼成温度で４時間保持した後、加熱を止めて自然冷却した。温度が１００℃以下になった時点で電気炉を開放した。得られた焼成物を回収し、アルミナ製乳鉢で１０分間粉砕して、六方晶窒化ホウ素を含む粗粉を得た。 100 g of the calcined product was placed in the above electric furnace. The temperature was raised from room temperature to 1800° C. at a rate of 10° C./min while nitrogen gas was circulated in the electric furnace. After holding the sintering temperature of 1800° C. for 4 hours, the heating was stopped and the product was allowed to cool naturally. The electric furnace was opened when the temperature became 100° C. or lower. The obtained fired product was recovered and ground in an alumina mortar for 10 minutes to obtain coarse powder containing hexagonal boron nitride.
次に、上記粗粉中に含まれる不純物を除くため、希硝酸（硝酸濃度：５質量％）５００ｇに、上記粗粉３０ｇを投入し、室温で６０分間攪拌した。攪拌後、吸引ろ過によって固液分離し、ろ液が中性になるまで、水を入れ替えて、最終的に洗浄液の電気伝導度が１ｍＳ／ｍ以下になるまで洗浄した。洗浄後、乾燥機を用いて１２０℃で３時間乾燥させることによって乾燥粉末を得た。当該乾燥粉末を比較例１の六方晶窒化ホウ素粉末とした。 Next, in order to remove impurities contained in the coarse powder, 30 g of the coarse powder was added to 500 g of dilute nitric acid (nitric acid concentration: 5% by mass) and stirred at room temperature for 60 minutes. After stirring, solid-liquid separation was carried out by suction filtration, water was replaced until the filtrate became neutral, and washing was carried out until the electric conductivity of the washing liquid finally became 1 mS/m or less. After washing, dry powder was obtained by drying at 120° C. for 3 hours using a dryer. The dry powder was used as the hexagonal boron nitride powder of Comparative Example 1.
（比較例２）
原料であるアセチレンブラックをアセチレンブラック（デンカ株式会社製、グレード名：ＦＸ３５）に変更し、配合量を２４質量部に変更したこと、プレス成形機の成形圧を５ＭＰａにしたこと、及び真空乾燥処理をしなかった以外は、実施例１と同様にして、六方晶窒化ホウ素粉末を調製した。(Comparative example 2)
The raw material acetylene black was changed to acetylene black (manufactured by Denka Co., Ltd., grade name: FX35), the blending amount was changed to 24 parts by mass, the molding pressure of the press molding machine was set to 5 MPa, and vacuum drying processing A hexagonal boron nitride powder was prepared in the same manner as in Example 1, except that the
（比較例３）
ホウ酸量の配合量を１５０質量部に変更し、原料に炭酸カルシウム（純度９９．５質量％以上）５質量部を添加したこと、及び焼成温度１９００℃に変更したこと以外は、比較例１と同様にして、六方晶窒化ホウ素粉末を調製した。(Comparative Example 3)
Comparative Example 1 except that the amount of boric acid was changed to 150 parts by mass, 5 parts by mass of calcium carbonate (purity of 99.5% by mass or more) was added to the raw material, and the firing temperature was changed to 1900 ° C. A hexagonal boron nitride powder was prepared in the same manner.
（比較例４）
第３工程の焼成条件を１７５０℃、２０時間に変更したこと、及び真空乾燥処理をしなかったこと以外は、比較例１と同様にして、六方晶窒化ホウ素粉末を調製した。(Comparative Example 4)
A hexagonal boron nitride powder was prepared in the same manner as in Comparative Example 1, except that the firing conditions in the third step were changed to 1750° C. for 20 hours and the vacuum drying treatment was not performed.
比較例１～４で得られた六方晶窒化ホウ素粉末について、比表面積、黒鉛化指数、純度、一次粒子の円形度及び平均粒子径、並びに、２５～２００℃まで加熱した際の水分量及び２０１～５００℃まで加熱した際の水分量を、実施例１と同様に測定した。比較例１～４で得られた六方晶窒化ホウ素粉末について、実施例１と同様に充填材としての評価を行った。結果を表２に示す。 Regarding the hexagonal boron nitride powders obtained in Comparative Examples 1 to 4, the specific surface area, graphitization index, purity, circularity and average particle size of primary particles, and water content and 201 when heated to 25 to 200 ° C. The water content when heated up to 500° C. was measured in the same manner as in Example 1. The hexagonal boron nitride powders obtained in Comparative Examples 1 to 4 were evaluated as fillers in the same manner as in Example 1. Table 2 shows the results.
本開示によれば、低誘電正接の放熱部材を製造するために有用な六方晶窒化ホウ素粉末を提供できる。
According to the present disclosure, it is possible to provide a hexagonal boron nitride powder that is useful for producing a heat dissipation member with a low dielectric loss tangent.
Claims (6)
比表面積が２．５ｍ２／ｇ以下であり、黒鉛化指数が２．０以下であり、純度が９９質量％以上であり、
５００℃に加熱した際の単位質量当たりの水分量が３００ｐｐｍ未満である、六方晶窒化ホウ素粉末。 comprising primary particles of hexagonal boron nitride,
a specific surface area of 2.5 m 2 /g or less, a graphitization index of 2.0 or less, and a purity of 99% by mass or more ;
A hexagonal boron nitride powder having a water content per unit mass of less than 300 ppm when heated to 500°C .