JP6888730B1 - 粘着シート、粘着部品、フレキシブル画像表示装置部材、積層体、画像表示装置 - Google Patents
粘着シート、粘着部品、フレキシブル画像表示装置部材、積層体、画像表示装置 Download PDFInfo
- Publication number
- JP6888730B1 JP6888730B1 JP2020189730A JP2020189730A JP6888730B1 JP 6888730 B1 JP6888730 B1 JP 6888730B1 JP 2020189730 A JP2020189730 A JP 2020189730A JP 2020189730 A JP2020189730 A JP 2020189730A JP 6888730 B1 JP6888730 B1 JP 6888730B1
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- sheet
- image display
- display device
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
このような画像表示装置では、複数の部材シートが透明な接着シートで貼り合された構造をしており、折り曲げに伴う部材シート間の歪を吸収できる柔らかさを備えつつ、強固に部材シートを粘着することができる粘着シートが求められている。
近年、屈曲用の画像表示装置に対応するためにアクリルポリマー組成を見直した、低いTg(ガラス転移温度)を有する粘着シートが提案されている。
しかし、このようなポリイミドフィルムは、極性が高いことから、従来の粘着シートでは、屈曲のストレスで剥がれたり、ディスプレイの使用者が保護フィルムの一部と勘違いして剥がされてしまったりする虞があった。
(I)周波数1Hzの剪断モードで動的粘弾性測定により得られる−20℃の貯蔵弾性率(G’(−20℃))が300kPa以下。
(II)周波数1Hzの剪断モードで動的粘弾性測定により得られる60℃の貯蔵弾性率(G’(60℃))が10kPa以上。
前記粘着層は、下記(I)及び(II)を満足する、フレキシブル画像表示装置部材を提案する。
(I)周波数1Hzの剪断モードで動的粘弾性測定により得られる−20℃の貯蔵弾性率(G’(−20℃))が300kPa以下。
(II)周波数1Hzの剪断モードで動的粘弾性測定により得られる60℃の貯蔵弾性率(G’(60℃))が10kPa以上。
なお、本粘着層は、その形態に制限はなく、予めシート状に成形されたシート状粘着製品が本フレキシブル画像表示装置部材に貼り合わされて形成されたものであっても、本フレキシブル画像表示装置部材に粘着層が直接形成されたものであってもよい。
よって、屈曲可能な画像表示装置に好適に使用することができる。
本発明の実施形態の一例に係る粘着シート(以下、「本粘着シート」と称する。)は、ポリエーテルポリオール成分及びイソシアネート成分由来のウレタン結合を有する分子鎖を有するウレタンポリマー鎖(以下、「ウレタン成分セグメント」と称する)と、(メタ)アクリル酸アルキルエステル成分由来の分子鎖を有するアクリルポリマー鎖(以下、「アクリル成分セグメント」と称する)と、を有する粘着剤(以下、「本粘着剤」と称する)を含む。
本発明の実施形態の一例に係るフレキシブル画像表示装置部材(以下、「本フレキシブル画像表示装置部材」と称することがある。)は、2つのフレキシブル部材が粘着層を介して貼り合わされた構成を有するフレキシブル画像表示装置部材であって、前記粘着層(以下、「本粘着層」と称することがある。)は、本粘着剤を含む。
一方、ウレタン成分セグメント、すなわち、「ポリエーテルポリオール成分及びイソシアネート成分由来のウレタン結合を有する分子鎖を有するウレタンポリマー鎖」とは、ポリエーテルポリオールとポリイソシアネートの反応よりウレタン結合を形成して重合された分子鎖構造を意味し、前記ウレタン成分セグメントは当該分子鎖構造をもつセグメントである。
本粘着剤は、ウレタン成分セグメントを含有することで、後述するように、アクリル重合体のみからなる粘着シート又は粘着層に比べて、表面のHSPにおいて、δpを大きくすることが可能となる。よって、δpが大きい各種ディスプレイフィルム(部材シート)との濡れ性が向上し、界面接着力が向上し、結果として剥離試験における粘着力の向上に寄与することができる。
ただし、本発明においては、アクリル成分との相溶性の観点から、ポリエーテル鎖を有するポリエーテル型のウレタン成分セグメントであることが好ましい。
前記ウレタン成分セグメントは、ポリオールと多官能イソシアネート化合物とから形成され、このポリオールはポリエーテルポリオールであることが好ましい。
さらにポリエーテルポリオールの中でも、ポリエーテルグリコール由来の成分を含むもの、中でも、ポリエーテルグリコールを主成分として選択することが好ましい。
さらに、アクリル成分セグメントとウレタン成分セグメントが共有結合で結合していることが好ましい。アクリル成分セグメントとウレタン成分セグメントが共有結合で結合するポリマーを含むことで、アクリル成分セグメントとウレタン成分セグメントが相溶しやすくなり、本粘着シート又は本粘着層の透明性が向上する。
(b)前記ウレタン成分セグメント又は前記アクリル成分セグメントが主鎖を構成し、他方のセグメントが側鎖を構成するグラフトポリマー
(c)前記ウレタン成分セグメント又は前記アクリル成分セグメントの一方と、他方のセグメントとが架橋している架橋ポリマー
前記の中でも本粘着シート又は本粘着層の好ましい一態様(以下「第1の態様」という)としては、本粘着剤が、アクリルポリマーからなる幹ポリマーと、ポリエーテル型ポリウレタンからなる枝ポリマー(「グラフト鎖」とも称する)とを有するグラフトポリマーを主成分樹脂として含有する態様を挙げることができる。
なお、前記ポリエーテル型ポリウレタンとは、ポリエーテルポリオール成分由来のウレタン結合を有する分子鎖を複数有するポリウレタンであり、詳細については下述する。
すなわち、アクリルポリマーからなる主鎖に、(メタ)アクリロイル基末端ポリウレタンが枝成分として結合したグラフトポリマーであることが好ましい。
このグラフトポリマーは、このポリマー単独でアクリル成分セグメントとウレタン成分セグメントとを有するものである。
ここで、質量平均分子量は、ポリスチレン換算でゲル浸透クロマトグラフィーを用いて測定した値である。
中でも、当該粘着剤組成物は、光又は熱硬化性粘着剤組成物であるのが好ましく、その場合には、開始剤及び/又は架橋剤を含有する場合が多い。
前記開始剤は特に限定されず、例えば熱により活性化するもの、活性エネルギー線により活性化するもの、いずれも使用できる。
また、ラジカルを発生し、ラジカル反応を引き起こすもの、カチオンやアニオンを発生し、付加反応を引き起こすものいずれも使用することができる。
前記有機過酸化物としては、例えばラウロイルパーオキシド、1,1−ビス(t−ヘキシルパーオキシ)−3,3,5−トリメチルシクロヘキサン、t−ヘキシルパーオキシピバレート、t−ブチルパーオキシピバレート、2,5−ジメチル−2,5−ビス(2−エチルヘキサノイルパーオキシ)ヘキサン、t−ヘキシルパーオキシ−2−エチルヘキサノエート、t−ブチルパーオキシ−2−エチルヘキサノエート、t−ブチルパーオキシイソブチレート、t−ブチルパーオキシ−3,5,5−トリメチルヘキサノエート、t−ブチルパーオキシラウレート等を挙げることができる。
また、水素引抜型光開始剤は、一度光硬化反応に用いた後であっても、再度光照射することで繰り返し活性種として機能し得る。
架橋構造形成のために、架橋剤を使用することができる。
水酸基などの活性水素基を含有した高分子量成分であれば、イソシアネートやカルボジイミドなどによって架橋することが可能である。
また、架橋反応の促進のために、遷移金属触媒などをさらに添加することも、粘着シート又は粘着層形成のプロセス上好ましい。
前記第1の態様において、本粘着剤は、前記の他に、必要に応じて、例えばポリエステル、ポリアミド、ポリオレフィン、オレフィン系モノマーなどの他の樹脂成分を含んでいてもよい。
前記第1の態様において、本粘着剤は、前記の他に、必要に応じて、その他の添加剤として、例えば粘着付与剤、硬化促進剤、充填剤、カップリング剤、紫外線吸収剤、紫外線安定剤、酸化防止剤、安定剤、顔料、防錆剤などのうちの一種又は二種以上を含んでいてもよい。
これら添加剤の量は、典型的には、粘着シート及び粘着層の硬化に悪影響を与えないように、又は粘着シート及び粘着層の物理的特性に悪影響を与えないように選択するのが好ましい。
粘着付与剤としては、特に限定されるものではなく、従来公知のものを使用することができる。例えば、テルペン系粘着付与剤、フェノール系粘着付与剤、ロジン系粘着付与剤、脂肪族系石油樹脂、芳香族系石油樹脂、共重合系石油樹脂、脂環族系石油樹脂、キシレン樹脂、エポキシ系粘着付与剤、ポリアミド系粘着付与剤、ケトン系粘着付与剤、エラストマー系粘着付与剤などが挙げられ、これらを1種又は2種以上を組み合わせて使用できる。
本粘着シート又は本粘着層の好ましい他の一態様(以下「第2の態様」という)としては、本粘着剤が、下記(d)及び(e)のうちのいずれか一種以上を含む粘着剤組成物から形成される態様を挙げることができる。
(e)アクリルポリマーを構成する単量体成分の混合物又はその部分重合物及びポリエーテル型ポリウレタン
前記粘着剤組成物は、光又は熱で硬化する、光又は熱硬化性粘着剤組成物であるのが好ましく、その場合には、開始剤及び/又は架橋剤を含有することが多い。
なお、これら開始剤、架橋剤、その他の樹脂成分及び添加剤の好ましい態様は上述と同じであるため省略する。
前記第1の態様及び第2の態様において、前記アクリルポリマーとしては、(メタ)アクリル酸アルキルエステルを単量体として含む重合体又は共重合体を挙げることができる。
前記アクリルポリマーの水酸基価は、前記(メタ)アクリル酸エステルの中から水酸基含有単量体成分の重合組成比率により制御できる。
水酸基価が上記範囲であることで、水酸基との反応を利用したウレタン成分セグメントの導入が可能となる。
前記アクリルポリマーの質量平均分子量(Mw)が40万以上であれば、粘着シート又は粘着層のベタツキが高くなり過ぎることがなく、打ち抜き加工性を維持できるとともに、粘着力と復元性の両立が可能となる。
他方、上記アクリルポリマーの質量平均分子量(Mw)が130万以下であれば、表面が平滑でヘイズの小さい粘着シート又は粘着層を成形することが可能である。
前記単量体成分をラジカル反応させる方法、即ち、重合方法としては、例えば溶液重合(沸点重合又は定温重合)、乳化重合、懸濁重合、塊状重合等を挙げることができる。なかでも、開始剤や重合温度等を調整することにより、分子量分布(Mw/Mn)を制御できることから、溶液重合が好ましい。
前記重合方法として溶液重合を用いる場合、重合温度としては、40〜90℃程度が好ましい。
前記第2の態様において、前記ポリエーテル型ポリウレタンは、ポリエーテルポリオールと多官能イソシアネート化合物を反応して得られるウレタン結合を有する分子鎖を複数有するポリウレタンである。
本発明において、前記ポリエーテル型ポリウレタンは、ウレタン結合を分子内に2以上有することが好ましい。
また、ゲル化防止やアクリル重合体との相溶性の観点から特に好ましくは、4,4’−メチレンビス(フェニルイソシアネート)(MDI);トルエンジイソシアネート(TDI);m−キシレンジイソシアネート(XDI);ヘキサメチレンジイソシアネート(HDI);メチレンビス(4−シクロヘキシルジイソシアネート)(HDMI(登録商標));ナフタレン−1,5−ジイソシアネート(NDI);3,3’−ジメチル−4,4’−ビフェニルジイソシアネート(TODI);1,4−ジ−イソシアナトベンゼン(PPDI);フェニル−1,4−4−ジイソシアネート;トリメチルヘキサメチルジイソシアネート(TDMI);イソフォロンジイソシアネート(IPDI);1,4ーシクロヘキシルジイソシアネート(CHDI);ジフェニルエーテル4,4’−ジイソシアネート;p,p’−ジフェニルジイソシアネート;リジンジイソシアネート(LDI);1,3−ビス(イソシアナトメチル)シクロヘキサン;ポリメチルポリフェニルイソシアネート(PMDI);及びそれらの異性体及び/又は混合物からなる群から選択される。
よって、ポリエーテルグリコール由来の成分の質量割合(質量%)が、前記イソシアネート由来の成分の質量割合(質量%)よりも大きいことが好ましい。
前記粘着剤組成物を硬化することで、本粘着シート又は本粘着層の接着力及び凝集力を高めることができる。
また、その他にも、一分子中に水酸基及び(メタ)アクリロイル基を有するポリエーテル型ポリウレタンであってもよく、また、一分子中にイソシアネート基及び(メタ)アクリロイル基を有するポリエーテル型ポリウレタンであってもよい。
前記1分子中に1個以上の水酸基を有するポリエーテル型ポリウレタンとしては、例えば片末端又は両末端に水酸基を有するポリエーテル型ポリウレタンを挙げることができる。
本粘着シート及び本粘着層は、周波数1Hzの剪断モードで動的粘弾性測定により得られる−20℃の貯蔵弾性率(G’(−20℃))が300kPa以下であることが好ましく、200kPa以下であることがさらに好ましい。
G’(−20℃)を上記範囲とすることで、本粘着シート又は本粘着層に後述する部材シートを貼り合わせて折り曲げ操作をした際、部材シートの割れを防止することができる。
屈曲可能な画像表示装置に使用される粘着シート及び本粘着層は、折り畳む速度(周波数)において柔らかくしてある必要があり、高周波数にて柔軟であるためには、動的粘弾性の温度−時間換算測により、低温域でG’が低いこと、つまり、粘着シート及び粘着層のガラス転移温度Tgが低いことが求められるため、−20℃の貯蔵弾性率(G’(−20℃))が300kPa以下であることが求められる。
本粘着シート及び本粘着層において、−20℃の貯蔵弾性率(G’(−20℃))を上記範囲に調整するには、ウレタン成分セグメント及びアクリル成分セグメントを有する粘着剤を使用して上記範囲に調整すればよく、とりわけ、上記第1の態様又は第2の態様で示した粘着剤を使用することが好ましい。但し、その方法に限定するものではない。
貯蔵剪断弾性率(G’(60℃))を上記範囲とすることで、例えば本粘着シート又は本粘着層を部材シートに貼着して積層シートを形成した際、常温から高温において、積層シートの折り曲げ時の層間応力を小さくすることができ、部材シートのデラミや割れを抑制することができる。
本粘着シート及び本粘着層は、周波数1Hzの剪断モードで動的粘弾性測定により得られる損失正接(tanδ)の極大値が−20℃以下にあることが好ましい。
この極大値は−30℃以下にあることがより好ましく、−40℃以下にあることがさらに好ましい。下限については特に定めないが通常−70℃以上である。
この極大値の温度は、粘着シートのガラス転移温度(Tg)の目安となるものであり、この値が−20℃以下であることで、低温での貯蔵弾性率が十分下がり、屈曲操作によるストレスを低減することが可能となる。
本粘着シート及び本粘着層は、周波数1Hzの剪断における損失正接(tanδ)の極大値0.1以上のピークが、−60〜−20℃の温度範囲に存在することが特に好ましい。
本粘着シート及び本粘着層は、粘着シート又は本粘着層の両端を反対方向に引っ張って初期長さの4倍の長さに伸長して、その状態を10分間保持し、その後、片端を放して20分間経過後の長さが、初期長さの1.0倍〜1.6倍であることが好ましい。
上記の操作は、粘着シート又は本粘着層を部材シートに貼り合わせた積層体、本フレキシブル画像表示装置部材及び画像表示装置の折り曲げ後に広げた際の復元性に関連しており、上記の範囲内にあることで、積層体や本フレキシブル画像表示装置部材や画像表示装置の折り目を目立たなくできる。
本粘着シート及び本粘着層は、ヘイズが1.0%未満であることが好ましく、0.7%未満であることがさらに好ましい。
本粘着シート及び本粘着層のヘイズが上記範囲にあることで、画像表示装置用の粘着シート及び粘着層として好適に用いることができる。
ここで、ヘイズはJIS K7136に準じてそれぞれ測定されるものである。
粘着シート又は本粘着層が部材シートと貼着された積層体になっている場合、積層体のヘイズを測定することで、粘着シート及び本粘着層のヘイズはその値以下であるとみなすことができる。
本粘着シート及び本粘着層は、厚み100μmの時の全光線透過率が85%以上であることが好ましく、88%以上であることがより好ましく、91%以上であることがより好ましい。
ここで、全光線透過率は、JIS K7361−1に準じて測定されるものである。
本粘着シート及び本粘着層は、粘着シート又は粘着層表面のハンセン溶解度パラメーター(δd,δp,δh)において、極性項δpが2.0MPa0.5以上であり、且つ、水素結合項δhが5.0MPa0.5以上であるのが好ましい。
本粘着シート及び本粘着層は、ウレタン成分セグメントを含有することで、アクリル成分セグメントのみからなる粘着シート又は粘着層よりも、表面のHSPにおいてδpを大きくすることが可能である。
よって、δpが大きい各種ディスプレイフィルム(部材シート)との濡れ性が向上し、界面接着力が向上し、結果として剥離試験における粘着力の向上に寄与することができる。
δd: 分子間のLondon分散力に由来するエネルギー
δp: 分子間の極性力に由来するエネルギー
δh: 分子間の水素結合力に由来するエネルギー
と、表記される。(ここで、それぞれの単位はMPa0.5である。)
Charles M. Hansen著、Hansen Solubility Parameters: A Users Handbook(CRCプレス、2007年)。
(式1)δd2+δp2+0.068δh2=13.9γSL(1/(VL 1/3))
また、水素結合項δhは、5.0MPa0.5以上が好ましく、6.0MPa0.5以上がさらに好ましい。
本粘着シート及び本粘着層のδp及びδhが上記範囲にあることで、ポリアミド、ポリイミド、エポキシ、ポリエステル、TACフィルムなどの高極性の(光学)部材シートへの濡れが良くなり、界面接着力が高まり、従来アクリル系の粘着シートよりも粘着力を向上することができる。
さらに表面のHSPにおけるδp,δhを大きくするためには、ウレタン成分セグメントが粘着シート表面に露出するように、配合量を調整したりするか、或いは、上記第1又は第2の態様で示した粘着剤を使用して本粘着シート及び本粘着層を形成するのが好ましい。
本粘着シート及び本粘着層のゲル分率は55%以上であることが好ましく、60%以上であることがさらに好ましく、65%以上であることがより好ましい。
本粘着シート及び本粘着層のゲル分率が55%以上であることにより、形状を十分に保持することができる。
本粘着シート及び本粘着層の厚みは、特に制限されるものではない。0.005mm以上であるのが好ましく、より好ましくは0.010mm以上、更に好ましくは0.150mm以上である。
一方、上限として、好ましくは1.000mm以下、より好ましくは0.700mm以下、更に好ましくは0.500mm以下である。
厚みが0.005mm以上であれば、ハンドリング性が良好であり、また、厚みが1.000mm以下であれば、部材シートを貼り合わせた積層体の薄型化に寄与することができる。
本粘着シートは、ディスプレイ部材を構成する部材(「ディスプレイ部材」とも称する)、とりわけ、ディスプレイを作製するのに用いるディスプレイ用のフレキシブル部材の貼合に使用することが好ましく、フレキシブルディスプレイを作製するのに用いるフレキシブルディスプレイ用の粘着部品として使用することが特に好ましい。
なお、フレキブル部材については、後述するものと同一のものを使用することができる。
次に、本フレキシブル画像表示装置部材の構成要素のうち、本粘着層以外の要素について説明する。
本フレキシブル画像表示装置部材を構成するフレキシブル部材としては、例えば有機エレクトロルミネッセンス(EL)ディスプレイ等のフレキシブルディスプレイ、カバーレンズ(カバーフィルム)、偏光板、偏光子、位相差フィルム、バリアフィルム、視野角補償フィルム、輝度向上フィルム、コントラスト向上フィルム、拡散フィルム、半透過反射フィルム、電極フィルム、透明導電性フィルム、金属メッシュフィルム、タッチセンサーフィルム等のディスプレイ用のフレキシブル部材を挙げることができる。これらのうちのいずれか1種又は2種のうちの2つを組み合わせて使用すればよい。例えばフレキシブルディスプレイと、その他のフレキシブル部材との組み合わせや、カバーレンズと、その他のフレキシブル部材との組み合わせを挙げることができる。
また、下述する理由から、上記2つのフレキブル部材のうち少なくとも1つのフレキブル部材の表面のHSPは、δpが10.0MPa0.5以上、20.0MPa0.5以下であることが好ましい。ポリアミド、ポリイミド、ポリエステル、エポキシ樹脂などは通常、この範囲にあることが多いが、コロナ処理やプラズマ処理、プライマー処理などで、上記範囲に調整することで、粘着層との界面接着力を高めることができる。
また、同じく下述する理由から、本フレキシブル画像表示装置部材においては、前記フレキシブル部材表面のハンセン溶解性パラメーターと、本粘着層表面のハンセン溶解性パラメーターのHSP距離(Ra)が17.0以下であることが好ましく、16.0以下であることがより好ましく、15.0以下であることがさらに好ましい。
また、HSP距離(Ra)の算出方法も下述するとおりである。
フレキシブル部材と本粘着層との粘着力が上記範囲であることで、屈曲時のストレスでフレキシブル部材が剥離することなく、画像表示装置の信頼性を向上させることができる。
本発明の実施態様の一例に係る粘着部品(以下「本部品」と称する)は、上述したウレタン成分セグメントとアクリル成分セグメントを有する粘着剤(上述した本粘着剤)を含むものであり、例えばウェアラブル電子機器、フォルダブルディスプレイ等のフレキシブルデバイスに好適に用いることができる。
中でも、とりわけ、本部品の表面のハンセン溶解度パラメーター(δd,δp,δh)において、極性項δpが2.0MPa0.5以上であり、且つ、水素結合項δhが5.0MPa0.5以上であるのが好ましい。
このような透明ポリイミドフィルムは、高温信頼性と透明性を両立するために、芳香族骨格とイミド基及び/又はアミド基を多く含有しており、種類によってはフッ素系の官能基を含有していることもある。
よって、極めて極性の高いフィルムとなっており、従来のディスプレイに使用されていた粘着部品では、フレキシブルデバイスに適用した際には、強固に粘着することができず、屈曲のストレスで剥がれたり、ディスプレイの使用者が保護フィルムの一部と勘違いして剥がされてしまったりするという課題がある。
本発明の実施形態の一例に係る積層体(以下、「本積層体」と称することがある)は、上述した本粘着シート又は本粘着層の少なくとも片面に部材シートを備えた積層体である。
この際、第1の部材シートと第2の部材シートは同じでもよいし、異なるものでもよい。
本粘着シート又は本粘着層の被着体となる部材シートの主成分としては、例えばポリシクロオレフィン、トリアセチルセルロース、ポリメチルメタクリレート、ポリエステル、エポキシ樹脂、ポリイミド、ポリアミドなどが挙げられ、これらのうちに一種の樹脂であっても、又は二種以上の樹脂であってもよい。
ここで、前記「主成分」とは、最も多い質量比率を占める成分であることをいい、具体的には部材シート又は該部材シートを形成する組成物の50質量%以上を占めるものであり、55質量%以上、中でも60質量%以上(100質量%包含する)を占めるのがさらに好ましい。
本積層体の厚みは、特に制限されるものではない。例えば画像表示装置に使用される場合の一例としては、本積層体はシート状であり、その厚みが0.01mm以上であれば、ハンドリング性が良好であり、また、厚みが1.0mm以下であれば、積層体の薄型化に寄与することができる。
よって、本積層体の厚みは、0.01mm以上であるのが好ましく、中でも0.03mm以上、特に0.05mm以上であるのがより好ましい。一方、上限に関しては、1.0mm以下であるのが好ましく、中でも0.7mm以下、特に0.5mm以下であるのがさらに好ましい。
本積層体において、部材シート表面のHSPはδpが10.0MPa0.5以上、20.0MPa0.5以下であることが好ましい。ポリアミド、ポリイミド、ポリエステル、エポキシ樹脂などは通常、この範囲にあることが多いが、コロナ処理やプラズマ処理、プライマー処理などで、上記範囲に調整することで、粘着シートとの界面接着力を高めることができる。
部材シートと粘着シート又は本粘着層との粘着力は、剥離周波数(速度)における損失弾性率(G’’)の大きさといった粘弾性的な要素と、濡れなどの界面接着力の要素などにより決まるのが通常である。
しかし、屈曲用の低Tgの粘着シート乃至粘着層は、粘弾性上の制約から大きな改善が見込めない可能性が高く、粘着シート乃至粘着層の表面HSPを制御し、界面接着力の向上を図った方が効果的に粘着力を高められることが分かってきた。
(式2)HSP距離(Ra)={4×(δdA−δdS)2+(δpA−δpS)2+(δhA−δhS)2}0.5
なお、式2中、δdA、δpA及びδhAはそれぞれ、本粘着シートのδd、δp及びδhを示し、δdS、δpS及びδhSはそれぞれ、本部材シートのδd、δp及びδhを示す。
粘着力の評価方法は様々であるが、例えば、部材シート、特に極性の高いフィルムからなる部材シートに対する本粘着シートの、60℃における300mm/min剥離速度での180度剥離強度(JIS Z 0237)を8N/25mm以上とすることができ、さらに好ましくは10N/25mm以上とすることができる。
部材シートと本粘着シート又は本粘着層との粘着力が上記範囲であることで、屈曲時のストレスで部材シートが剥離することなく、画像表示装置の信頼性を向上させることができる。
本積層体は、ヘイズが1.0%未満であることが好ましく、0.7%未満であることがさらに好ましい。
本積層体のヘイズが上記範囲にあることで、画像表示装置用の構成部材として好適に用いることができる。
ここで、ヘイズはJIS K7136に準じてそれぞれ測定されるものである。
本粘着シートの製造方法の一例として、「本粘着シート中のウレタン成分セグメントを形成するポリエーテル型ポリウレタン」と、「本粘着シート中のアクリル成分セグメントを形成するアクリルポリマー」とを含有する粘着剤組成物をシート状に成形した後、光又は熱などにより組成物を硬化させ、必要に応じて適宜加工を施すことにより、本粘着シートを製造する方法を挙げることができる。但し、かかる方法に限定するものではない。
粘着剤組成物を調製する際、上記原料を、温度調節可能な混練機(例えばディスパー、一軸押出機、二軸押出機、プラネタリーミキサー、二軸ミキサー、加圧ニーダー等)を用いて混練すればよい。
なお、種々の原料を混合する際、シランカップリング剤、酸化防止剤等の各種添加剤は、予め樹脂とともにブレンドしてから混練機に供給してもよいし、予め全ての材料を溶融混合してから供給してもよいし、添加剤のみを予め樹脂に濃縮したマスターバッチを作製し供給してもよい。
粘着剤組成物をシート状に成形する方法としては、公知の方法、例えばウェットラミネーション、ドライラミネート、Tダイを用いる押出キャスト法、押出ラミネート法、カレンダー法やインフレーション法、射出成型、注液硬化法等を採用することができる。中でも、シートを製造する場合は、ウェットラミネーション法、押出キャスト法、押出ラミネート法が好適である。
本粘着シート及び本粘着層を硬化させるためには、離型シートなどの部材シートに上記粘着剤組成物を塗布して重合させてもよいし、粘着剤組成物を重合させて硬化させた後に部材シートなどに貼着してもよい。
また、活性エネルギー線の照射エネルギー、照射時間、照射方法などに関しては特に限定されない。
本粘着シート及び本粘着層の製造方法の別の実施態様として、上記粘着剤組成物を適切な溶剤に溶解させ、各種コーティング手法を用いて実施することもできる。
コーティング手法を用いた場合、上記の活性エネルギー線照射硬化の他、熱硬化させることにより本粘着シートを得ることもできる。
本粘着シート又は本粘着層の少なくとも片面に、ブロッキング防止や異物付着防止の観点から、保護フィルムを積層させることが好ましい。
また、必要に応じて、本粘着シート又は本粘着層の少なくとも片面に、エンボス加工や種々の凹凸(円錐や角錐形状や半球形状など)加工を行ってもよい。
また、各種被着部材への接着性を向上させる目的で、本粘着シートの表面にコロナ処理、プラズマ処理及びプライマー処理などの各種表面処理を行ってもよい。
ここで、離型フィルムとしては、光透過性とコストの観点から、離型処理したポリエチレンテレフタレート(PET)フィルムを採用することが好ましい。
本フレキシブル画像表示装置部材の製造方法としては、特に制限されるものではなく、上述のように、本粘着層形成用の樹脂組成物をフレキブル部材上に塗布して形成してもよいし、予め当該樹脂組成物を用いてシート状に成形した後に、フレキブル部材と貼合してもよい。
本積層体を組み込むことで、例えば本積層体を他の画像表示装置構成部材に積層することで、本積層体を備えた画像表示装置(「本画像表示装置」とも称する)を形成することができる。
特に本積層体は、低温及び高温における環境下で折り畳み操作をしても、積層シートのデラミや割れを防止でき、復元性も良好であるから、フレキシブル画像表示装置を形成することができる。
本発明においては、「フィルム」と称する場合でも「シート」を含むものとし、「シート」と称する場合でも「フィルム」を含むものとする。
また、画像表示パネル、保護パネル等のように「パネル」と表現する場合、板体、シート及びフィルムを包含するものである。
また、「X以上」(Xは任意の数字)と記載した場合、特にことわらない限り「好ましくはXより大きい」の意を包含し、「Y以下」(Yは任意の数字)と記載した場合、特にことわらない限り「好ましくはYより小さい」の意も包含するものである。
(A−1):アクリル重合体 アクリット6HY-3030(大成ファインケミカル(株)商品名、ブチルアクリレートと2−ヒドロキシエチルアクリレートの共重合体、質量平均分子量:約60万、水酸基価24[KOH・mg/g])
(F):触媒 ナーセルアルミニウム;アセチルアセトン金属錯体、日本化学産業(株)製
表1に記載した配合(固形分)となるように均一に混合し、固形分が30wt%になるように酢酸エチルを添加して塗工液を調整した。
次に、離型処理されたポリエチレンテレフタレートフィルム(三菱ケミカル株式会社製、ダイアホイルMRV(V03)厚さ:100μm)上に、エルコメーター社製 バードフィルムアプリケーターを用いて液を展開し、90℃のオーブンで10分間乾燥させた。
(ゲル分率)
実施例及び比較例で作製した粘着シートから離型フィルムを取り除いたものについて、下記の測定を行った。
1)粘着シート約150mgを秤量し(W1)、予め重さを測った200メッシュのSUS(ステンレス製)メッシュ(W0)に包む。
2)上記SUSメッシュを100mLの酢酸エチルに24時間浸漬する。
3)SUSメッシュを取り出し、75℃で4時間半乾燥する。
4)乾燥後の質量(W2)を求め、下記式より粘着シートのゲル分率を測定する。
ゲル分率(%)=100×(W2−W0)/W1
粘着シートの表面のHSPは以下のように測定した。
粘着シートの離型PETフィルムを片面剥がして粘着シートを露出させ、そこにHSP既知の11種の溶媒2.0μLの液滴を滴下し、30秒後の接触角を記録し、接触角の値から、Young-Dupreの式及び、畑・北崎、拡張ホークスの式からγSLを算出し、ハンセン溶解度パラメーターと表面張力の関係(式1)(Hansen Solubility Parameters 50th anniversary conference,preprint 2017 PP.14-21(2017))から、Raと(γSL/(VL 1/3))1/2が最も相関するように決定される。
(式1)δd2+δp2+0.068δh2=13.9γSL(1/(VL 1/3))
さらに上記で測定された粘着シートの表面HSP及び部材シートの表面HSPの値から、HSP距離(Ra)を算出した。
実施例及び比較例で作製した粘着シートの両面の離型フィルムを剥がし、粘着シートを複数枚重ねることで、厚みが約0.8mmのシートを作製し、直径8mmの円形に打ち抜いたものを、レオメーター(ティー・エイ・インスツルメント・ジャパン株式会社製、DHR−2)を用いて、粘着治具:Φ8mmパラレルプレート、歪み:0.1%、周波数:1Hz、温度:−70〜100℃、昇温速度:3℃/minの条件で測定することで、粘着シートの貯蔵弾性率(G’)、損失弾性率(G”)、損失正接(tanδ)を得た。表1に結果を示す。
実施例及び比較例で得られた粘着シートを長さ70mm×幅10mmの短冊状に切り出し、両端の10mm×10mmの両面に紙を貼りつけ、持ち手とした。(持ち手のない部分は長さ50mm×幅10mm)
持ち手を掴み、持ち手間の距離4倍の長さ(200mm)になるまで長手方向に伸長して10分間保持し、その後片端を放して20分間後の長さを測定し、下記の様に判定した。
×:試験後の持ち手間の長さが、初期長さの1.6倍超である。
実施例及び比較例で作製した粘着シートの一方の離型フィルムを剥がし、該粘着シートをKOLON社製CPI(50μm)にロール貼合し、残る離型フィルムを剥がして、もう一枚のKOLON社製CPI(50μm)を該粘着シートに貼合した。この積層体を、オートクレーブ処理(60℃、ゲージ圧0.2MPa、20分)して仕上げ貼着し、積層体とした。
なお、実施例4では、部材シートとして、KOLON社製CPIの表面をO2プラズマ処理した部材シートを使用した。
得られた積層体を、40mm×100mmに裁断して屈曲保管性の評価用サンプルとした。評価サンプルをユアサシステム社製、DLDMLH−FSを用いて、IEC 63715に準拠して、U字曲げを繰り返し行った。試験条件は、−30℃、周波数1Hz、曲率半径r:3mm、10万サイクルであり、下記基準で折り曲げ性を評価した。
○:10万回折り曲げ後に、積層体に外観上の変化がみられない。
×:10万回折り曲げ後に、積層体に破断、剥離(デラミ)、気泡、発泡などの異常がみられる。
部材シートを両面に貼合して作製した積層体を評価用サンプルとした。ヘーズメータ(日本電色工業社製「NDH5000」)を用いて、JIS K7136に準拠して、ヘイズ値を測定した。結果を表1に示す。
SUS板に部材シートとしてKOLON社製CPI(50μm)を両面テープで貼り付け、粘着シートの離型PETフィルムを片面剥がして粘着シートを露出させ、粘着シートの一方の離型フィルムを剥がし、裏打ちフィルムとしてポリエチレンテレフタレートフィルム(三菱ケミカル社製「ダイアホイルS−100」、厚さ50μm)をハンドローラーにてロール圧着した。これを、25mm幅×150mm長の短冊状に裁断し、残る離型フィルムを剥がして露出した粘着面を、部材シートとしてKOLON社製CPI(50μm)にハンドローラーを用いてロール貼着して、部材シート面を両面テープでSUS板に貼り付け、SUS板/両面テープ/部材シート(CPI)/粘着シート/裏打ちフィルム(PET)からなる積層体を作成し、この積層体にオートクレーブ処理(60℃、ゲージ圧0.2MPa、20分)を施して仕上げ貼着し、粘着シート/部材シート間の粘着力測定サンプルを作製した。
また、ウレタン成分セグメントを含有した方が、δp、δhが大きくなり、部材シートとのHSP距離が小さくなる傾向が確認された。
60℃の粘着力は、G’(60℃)とHSP距離の両方の影響を受けていることが示唆された。特に実施例1〜3の光重合可能なウレタン成分を含んだものが、ヘイズも含めた性能のバランスがとれていることが分かった。
なお、別試験において、実施例3の(B−1)の代わりに、ポリカプロラクトン型ポリウレタン(ジシクロヘキシルメタンジイソシアネート47.8wt%、ポリカプロラクトン34.8wt%、ネオペンチルグリコール4.2wt%、1,4−ブタンジオール13.2wt%の組成からなるオリゴマー)を使用したところ、ポリカプロラクトン型などのウレタン成分セグメントと、アクリル成分セグメントは相溶せず、ヘイズを悪化させた。これに対し、ポリエーテル型のウレタン成分セグメントとアクリル成分セグメントは、一定の相溶性が認められ、上記の結果を踏まえると、画像表示装置に好適に使用できる粘着シート及び積層体であることが分かった。
Claims (4)
- 2つのフレキシブル部材が粘着層を介して貼り合わされた構成を有するフレキシブル画像表示装置部材であって、
前記粘着層は、ポリエーテルポリオール成分及びイソシアネート成分由来のウレタン結合を有する分子鎖を有するウレタンポリマー鎖(以下、「ウレタン成分セグメント」と称する)と、(メタ)アクリル酸アルキルエステル成分由来の分子鎖を有するアクリルポリマー鎖(以下、「アクリル成分セグメント」と称する)と、を有する粘着剤を含み、
接触角法により測定される、粘着層表面のハンセン溶解度パラメーター(δd,δp,δh)において、極性項δpが2.0MPa 0.5 以上であり、かつ、水素結合項δhが5.0MPa 0.5 以上であり、
前記粘着層は、周波数1Hzの剪断モードで動的粘弾性測定により得られる損失正接(tanδ)の極大値が−20℃以下にあり、かつ、下記(I)及び(II)を満足する、フレキシブル画像表示装置部材。
(I)周波数1Hzの剪断モードで動的粘弾性測定により得られる−20℃の貯蔵弾性率(G’(−20℃))が300kPa以下。
(II)周波数1Hzの剪断モードで動的粘弾性測定により得られる60℃の貯蔵弾性率(G’(60℃))が10kPa以上。 - 前記粘着剤は、前記ウレタン成分セグメント及び前記アクリル成分セグメントが共有結合により結合している請求項1に記載のフレキシブル画像表示装置部材。
- 前記粘着剤は、下記(a)〜(c)のいずれか1種以上のポリマーを含む請求項1又は2に記載のフレキシブル画像表示装置部材。
(a)前記ウレタン成分セグメント及び前記アクリル成分セグメントが主鎖を構成するブロックポリマー
(b)前記ウレタン成分セグメント又は前記アクリル成分セグメントが主鎖を構成し、他方のセグメントが側鎖を構成するグラフトポリマー
(c)前記ウレタン成分セグメント又は前記アクリル成分セグメントの一方と、他方のセグメントとが架橋している架橋ポリマー - 前記粘着剤は、下記(d)及び(e)のうちのいずれか1種以上を含む粘着剤組成物の硬化物からなる請求項1又は2に記載のレキシブル画像表示装置部材。
(d)アクリルポリマー及びポリエーテル型ポリウレタン
(e)アクリルポリマーを構成する単量体成分の混合物又はその部分重合物及びポリエーテル型ポリウレタン