JP6887719B2 - ホットメルト組成物 - Google Patents
ホットメルト組成物 Download PDFInfo
- Publication number
- JP6887719B2 JP6887719B2 JP2019138491A JP2019138491A JP6887719B2 JP 6887719 B2 JP6887719 B2 JP 6887719B2 JP 2019138491 A JP2019138491 A JP 2019138491A JP 2019138491 A JP2019138491 A JP 2019138491A JP 6887719 B2 JP6887719 B2 JP 6887719B2
- Authority
- JP
- Japan
- Prior art keywords
- mpa
- product name
- wax
- hot melt
- manufactured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明では、非結晶性ポリアルファオレフィン(A)を用いる。当該(A)成分は、本発明にかかるホットメルト組成物のベースポリマーとして用いられる。
本発明では、スチレン系熱可塑性エラストマー(B)を用いる。当該(B)成分の25℃における25%トルエン溶液粘度としては、50〜5,000mPa・sであることが好ましく、80〜4,000mPa・sであることがより好ましく、100〜3,000mPa・sであることが特に好ましい。
本発明では、粘着付与剤(C)を用いる。当該(C)成分を用いることにより、被着体表面の濡れ性が高くなることから、層間の密着性を向上させることができる。
などが挙げられる。
表1に示す配合において、190℃に設定したニーダーにより十分に混練し、実施例及び比較例のホットメルト組成物を得た。ここで、表1における数値は、重量部を表すものとする。以下に、使用した原材料を示す。
非結晶性ポリアルファオレフィン1:VESTOPLAST 888(製品名、エボニック社製、溶融粘度(190℃):120,000mPa・s、引張強度:2.5MPa)
非結晶性ポリアルファオレフィン2:VESTOPLAST EP807(製品名、エボニック社製、溶融粘度(190℃):7,000mPa・s、引張強度:4.0MPa)
非結晶性ポリアルファオレフィン3:VESTOPLAST 703(製品名、エボニック社製、溶融粘度(190℃):2,700mPa・s、引張強度:2.1MPa)
非結晶性ポリアルファオレフィン4:VESTOPLAST 508(製品名、エボニック社製、溶融粘度(190℃):8,000mPa・s、引張強度:1.5MPa)
非結晶性ポリアルファオレフィン5:VESTOPLAST 828(製品名、エボニック社製、溶融粘度(190℃):25,000mPa・s、引張強度:1.0MPa)
非結晶性ポリアルファオレフィン6:VESTOPLAST 891(製品名、エボニック社製、溶融粘度(190℃):115,000mPa・s、引張強度:2.0MPa)
スチレン系熱可塑性エラストマー:クレイトン G1726(製品名、クレイトン社製、SEBS、25%トルエン溶液粘度(25℃):200mPa・s)
粘着付与剤1:T−REZ HA125(製品名、JXTGエネルギー社製、水添脂環族系炭化水素、軟化点:120℃〜130℃)
粘着付与剤2:Endex 155(製品名、イーストマン社製、α−メチルスチレン系樹脂、軟化点:152℃)
ワックス1:ユーメックス 1010(製品名、三洋化成工業社製、無水マレイン酸変性ポリプロピレンワックス、酸価:52)
ワックス2:H−501(製品名、QINGDAO SINOPLAS社製、無変性ポリプロピレンワックス、融点:160℃)
軟化剤:PB1300(製品名、大林産業社製、ポリブテン)
老化防止剤:Irganox 1010(製品名、BASF社製)
当該ホットメルトを厚み2mmのシート状に加工し、JIS K 6251に規定する3号形ダンベル状に打ち抜いたものを試験片とし、万能引張試験機にてC.H.S.=500mm/minで引張試験を行って、破断した際の強度(MPa)を測定した。
180℃に設定したホットメルトガンに、ホットメルト組成物を投入し、1時間保持することにより完全に溶融させた。そして、表面材(ガラス繊維不織布:100mm×100mm×7mmt)の中心部分において、1点ごとに塗布量100mg/cm2となるように、円状に2点塗布し、その塗布部の隙間に針金を置き、10秒間養生した。その後、2種類の基材(PP:25mm×70mm×2mmt、鋼板(SECC):25mm×60mm×1mmt)のいずれかを貼り合わせ、5kgの重りを載せて圧締し、室温にて24時間養生することにより試験片を作製した。作製した試験片は、90℃に調温した恒温機内に30分間静置した後、表面材が上部となるよう支え、針金の両端を結び、その結び目に1.8kgの重りを吊るして、重りが落下するまでの時間を測定した。
Claims (1)
- 非結晶性ポリアルファオレフィン(A)と、スチレン系熱可塑性エラストマー(B)と、粘着付与剤(C)と、不飽和カルボン酸及び/又はその無水物で変性されたワックスと、を含み、
非結晶性ポリアルファオレフィン(A)は、溶融粘度(190℃)が22,000〜300,000mPa・sであり、引張強度が2.3〜6.0MPaであることを特徴とする自動車内装材用ホットメルト組成物。