JP6845869B2 - リチウム二次電池正極活物質の製造方法及びこれにより製造されたリチウム二次電池正極活物質 - Google Patents
リチウム二次電池正極活物質の製造方法及びこれにより製造されたリチウム二次電池正極活物質 Download PDFInfo
- Publication number
- JP6845869B2 JP6845869B2 JP2018550462A JP2018550462A JP6845869B2 JP 6845869 B2 JP6845869 B2 JP 6845869B2 JP 2018550462 A JP2018550462 A JP 2018550462A JP 2018550462 A JP2018550462 A JP 2018550462A JP 6845869 B2 JP6845869 B2 JP 6845869B2
- Authority
- JP
- Japan
- Prior art keywords
- compound
- producing
- compound containing
- lithium
- active material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記正極活物質のうち、LiCoO2は、寿命特性及び充放電効率に優れ、最も多く使用されているが、容量が小さく、原料として使用されるコバルトの資源的限界により高価であるため、電気自動車などのような中大型電池分野の動力源として大量使用するには価格競争力に限界があるという短所がある。LiMnO2、LiMn2O4などのリチウムマンガン酸化物は、原料として使用されるマンガン資源が豊富で値段が安く、環境親和的であり、熱的安定性に優れるという長所があるが、容量が小さく、高温特性及びサイクル特性等が劣悪であるという問題がある。
本発明はさらに、本発明の製造方法により製造されたリチウム二次電池正極活物質を提供することを目的とする。
i)下記の化学式1で表されるニッケル複合水酸化物を製造するステップと、
[化1]Ni1−x−yM1xM2y(OH)2
(M1は、Co、Mnからなる群より選ばれた1つ以上の元素であり、
M2は、Al、Mn、Mg、Si、P、及びGaからなる群より選ばれた1つ以上の元素であり、
0≦a≦0.3であり、0≦x≦0.03、0≦y≦0.03
である)
ii)前記i)ステップで得られた化合物を水洗溶液に添加して水洗するステップと、
iii)前記ii)ステップで水洗された化合物を乾燥させるステップと、
iv)前記iii)ステップで乾燥された化合物をリチウム化合物及びM3を含む化合物(M3は、Al、B、Ba、Mg、Ce、Cr、F、Li、Mo、P、Sr、Ti、及びZrからなる群より選ばれた1つ以上の元素であり、M1、M2、及びM3は、全て同一でない)と混合するステップと、
v)熱処理するステップと、を含む
下記の化学式2で表されるリチウムニッケル複合酸化物の製造方法を提供する
(前記化学式2においてM1は、Co、Mnからなる群より選ばれた1つ以上の元素であり、M2は、Al、Mn、Mg、Si、P、及びGaからなる群より選ばれた1つ以上の元素であり、0≦a≦0.3であり、0≦x≦0.03、0≦y≦0.03、0≦z≦0.03である)
本発明に係る製造方法において、前記ii)ステップの水洗溶液は、蒸留水、メタノール、エタノール、2−プロパノール、1−ブタノール、エチレングリコール、ポリビニルアルコール(PVA)、アセトン、アセチルアセトン、ベンゾフェノン、NaOH、NH4OH、LiOH、KOH、Mg(OH)2、及びBa(OH)2からなる群より選ばれた1つ以上を含むことを特徴とする。
本発明に係る製造方法において、前記M3は、セリウムであり、前記M3を含む化合物は、CeO2であることを特徴とする。
本発明に係る製造方法において、前記M3はMgであり、前記M3を含む化合物は、Mg(OH) 2 であることを特徴とする。
本発明に係る製造方法において、前記iii)ステップで乾燥された粒子、リチウム化合物、及びM3を含む化合物と混合するiv)ステップにおいて、前記iii)ステップで乾燥された粒子100重量部当たり前記M3を含む化合物は、0.001〜10重量部の割合で混合されることを特徴とする。
本発明に係る製造方法において、前記M4は、Mgであり、前記M4を含む表面コーティング用化合物は、MgOであることを特徴とする。
本発明はさらに、本発明の製造方法により製造されたリチウムニッケル複合酸化物を提供する。
本発明はさらに、本発明の製造方法により製造されたリチウムニッケル複合酸化物を含むリチウム二次電池を提供する。
NCA系の正極活物質を製造するために、まず、共沈反応によってNiCoAl(OH)2で表される前駆体を製造した。
製造された前駆体にリチウム化合物としてLiOH及びドーパントM3を含む化合物としてAl2O3、Mg(OH)2を各々1.4モル、0.125モル添加し、第1の温度で熱処理してリチウム二次電池用正極活物質を製造した。
蒸留水を用意し、温度を一定に維持した後、前記製造されたリチウム二次電池用正極活物質を蒸留水に投入して温度を維持させながら水洗した。
水洗された正極活物質にコーティングのためのM4を含有する化合物としてCeO2を0.005モル混合し、その後、第2の温度で熱処理した。
共沈反応によってNiCoAl(OH)2で表される前駆体を製造した。
製造された前駆体にリチウム化合物としてLiOH及びドーパントM3を含む化合物としてAl2O3、Mg(OH)2、及びCeO2を各々1.4モル、0.125モル、及び0.05モル添加し、第1の温度で熱処理してリチウム二次電池用正極活物質を製造した。
蒸留水を用意し、温度を一定に維持した後、前記製造されたリチウム二次電池用正極活物質を蒸留水に投入して温度を維持させながら水洗した。
その後、第2の温度で熱処理して実施例5の正極活物質を製造した。
共沈反応によってNiCoAl(OH)2で表される前駆体を製造した。
製造された前駆体にリチウム化合物としてLiOH及びドーパントM3を含む化合物としてAl2O3、Mg(OH)2、及びCeO2を各々1.4モル、0.125モル、及び0.05モル添加し、第1の温度で熱処理してリチウム二次電池用正極活物質を製造した。
蒸留水を用意し、温度を一定に維持した後、前記製造されたリチウム二次電池用正極活物質を蒸留水に投入して温度を維持させながら水洗した。
水洗された正極活物質にコーティングのためのM4を含有する化合物としてTiO2を0.005モル混合し、その後、第2の温度で熱処理した。
共沈反応によってNiCoAl(OH)2で表される前駆体を製造した。
製造された前駆体にリチウム化合物としてLiOH及びドーパントM3を含む化合物としてAl2O3、Mg(OH)2、及びCeO2を各々1.4モル、0.125モル、及び0.05モル添加し、第1の温度で熱処理してリチウム二次電池用正極活物質を製造した。
蒸留水を用意し、温度を一定に維持した後、前記製造されたリチウム二次電池用正極活物質を蒸留水に投入して温度を維持させながら水洗した。
水洗された正極活物質にコーティングのためのM4を含有する化合物としてCeO2を0.005モル混合し、その後、第2の温度で熱処理した。
共沈反応によってNiCoAl(OH)2で表される前駆体を製造した。製造された前駆体にリチウム化合物としてLiOH及びドーパントM3を含む化合物としてAl2O3、Mg(OH)2を各々1.4モル、0.125モル添加し、第1の温度で熱処理してリチウム二次電池用正極活物質を製造した。蒸留水を用意し、温度を一定に維持した後、前記製造されたリチウム二次電池用正極活物質を蒸留水に投入して温度を維持させながら水洗した。その後、第2の温度で熱処理して比較例1の正極活物質を製造した。
共沈反応によってNiCoAl(OH)2で表される前駆体を製造した。製造された前駆体にリチウム化合物としてLiOH及びドーパントM3を含む化合物としてAl2O3、Mg(OH)2、TiO2を各々1.4モル、0.125モル、0.1モル添加し、第1の温度で熱処理してリチウム二次電池用正極活物質を製造した。蒸留水を用意し、温度を一定に維持した後、前記製造されたリチウム二次電池用正極活物質を蒸留水に投入して温度を維持させながら水洗した。その後、第2の温度で熱処理して比較例2の正極活物質を製造した。
上記実施例1〜5、及び比較例1、2において製造された正極活物質のSEM写真を測定し、図1及び図2に示した。
上記実施例1〜5、及び比較例1、2において製造された正極活物質のXRDを測定し、図3及び図4に示した。
図3及び図4において、本発明の実施例によって製造された正極活物質の場合、2θが28゜〜29゜、45゜〜50゜、55゜〜60゜の範囲で特徴的なピークが検出され、特に、2θが28゜〜29゜の範囲では、リチウム源とCeO2とを同時に投入するより、焼成後にCeO2を投入する場合、検出されるピークの強度が高く測定されることが分かる。
上記実施例及び比較例において製造されたリチウム−ニッケル複合酸化物の残留リチウムを測定し、その結果を表2に示した。
残留リチウムを測定するために、活物質1gを蒸留水5gに浸漬させた後、5分間攪拌し、濾過液を取って0.1M HClに滴定し、前記濾過液のpHが5になるまで投入されたHClの体積を測定することにより、活物質の残留リチウムを分析した。
Mgのみをドーピングした比較例1に比べて、本発明の実施例によってセリウムをドーピングした場合、残留リチウムが大きく減少することが確認できる
上記実施例及び比較例の各々によって製造されたリチウム二次電池用正極活物質と、導電材として人造黒鉛、結合材ではポリビニリデンフルオライド(PVdF)を85:10:75の重量比で混合してスラリを製造した。前記スラリを15μm厚さのアルミニウム箔に均一に塗布し、135℃で真空乾燥してリチウム二次電池用正極を製造した。
前記正極と、リチウムホイールを相対電極とし、厚さが20μmである多孔性ポリプロピレン膜をセパレータとし、エチレンカーボネート、ジエチルカーボネート、及びエチルメチルカーボネートが3:1:6の体積比で混合された溶媒にLiPF6を1.15M濃度で溶かした電解液を使用して、通常の方法にてコイン電池を製造した。
上記製造例において製造された電池に対して充放電特性を測定し、その結果を表2及び図5に示した。
上記実施例及び比較例の正極活物質を含むコインセルに対してc−rateを測定し、その結果を表2及び図6に示した。
Mgのみをドーピングした比較例1に比べて、本発明の実施例によってセリウムをドーピングした場合、c−rate特性が大きく改善されることが確認できる。
上記実施例及び比較例の正極活物質を含むコインセルに対して寿命特性を測定し、その結果を上記表2及び図7に示した。
セリウム酸化物を熱処理後、コーティングの際に導入した実施例1の場合、セリウムを導入していない比較例1より寿命特性が大きく改善されることが確認できる。
上記実施例及び比較例の活物質を含む電池に対して60℃高温で7日間保管した後、保存前後のインピーダンスの変化を測定し、その結果を表2及び図8に示した。
表2及び図8において、本発明によってセリウムをリチウムソースとともにドーピングする実施例5の正極活物質を含む電池の場合、保存前に測定されたインピーダンスが小さいだけでなく、保存後のインピーダンス増加量が最も小さいということが分かる。
上記実施例及び比較例の活物質を含む電池に対して熱安全性を評価するために、DSCピーク温度を測定し、その結果を上記表2及び図9に示した。
図9において、セリウム酸化物をドーピングしたり、コーティングしていない比較例1に比べて、セリウム酸化物をリチウムソースとともにドーピングする実施例5の正極活物質を含む電池の場合、ピーク温度がより高く、優れた熱安定性を表することが確認でき、セリウム酸化物を熱処理後、コーティングの際に導入した実施例1の場合、優れた熱的安定性を見せることと確認された。
本発明に係るリチウム二次電池正極活物質の製造方法は、リチウム化合物と前駆体とを反応させた後、表面水洗し、金属酸化物をさらにドーピングし、熱処理することにより、金属酸化物をリチウム源とともにドーピングしたり、活物質製造後、金属酸化物の表面をコーティングさせることにより、本発明に係るリチウム二次電池正極活物質の製造方法により製造されたリチウム二次電池正極活物質は、表面未反応リチウムの量を減少させながらも高容量特性を表す。
Claims (10)
- i)下記の化学式1で表されるニッケル複合水酸化物を製造するステップと、
[化1]Ni1−x−yM1xM2y(OH)2
(M1は、Co、Mnからなる群より選ばれた1つ以上の元素であり、
M2は、Al、Mn、Mg、Si、P、及びGaからなる群より選ばれた1つ以上の元素であり、
0≦x≦0.03、0≦y≦0.03である)
ii)前記i)ステップで得られた化合物を水洗溶液に添加して水洗するステップと、
iii)前記ii)ステップで水洗された化合物を乾燥させるステップと、
iv)前記iii)ステップで乾燥された化合物を、LiOHおよびLi 2 CO 3 の内少なくとも1種を含むリチウム化合物、Alを含む化合物、Mgを含む化合物、およびCeを含む化合物と混合するステップと、
v)前記iv)ステップで混合された化合物を熱処理するステップと、
vi)前記v)ステップで熱処理された化合物を水洗溶液に添加して水洗するステップと、
vii)前記vi)ステップで水洗された化合物とM4を含む表面コーティング用化合物(M4は Al、B、Ba、Mg、Ce、Cr、F、Li、Mo、P、Sr、Ti、及びZrからなる群より選ばれた1つ以上の元素である)とを混合するステップと、
viii)前記vii)ステップで混合された化合物を熱処理するステップと、
を含む下記の化学式2で表されるリチウムニッケル複合酸化物の製造方法であって、
[化2]Li1+aNi1−x−yM1xM2yM3zO2
(前記化学式2においてM1は、Co、Mnからなる群より選ばれた1つ以上の元素であり、M2は、Al、Mn、Mg、Si、P、及びGaからなる群より選ばれた1つ以上の元素であり、M3は、Al、Mn及びCeからなり、0≦a≦0.3、0≦x≦0.03、0≦y≦0.03、0≦z≦0.03である)
リチウムニッケル複合酸化物の製造方法。 - 前記ii)ステップの水洗溶液は、蒸留水、メタノール、エタノール、2−プロパノール、1−ブタノール、エチレングリコール、ポリビニルアルコール(PVA)、アセトン、アセチルアセトン、ベンゾフェノン、NaOH、NH4OH、LiOH、KOH、Mg(OH)2、及びBa(OH)2からなる群より選ばれた1つ以上を含む請求項1に記載のリチウムニッケル複合酸化物の製造方法。
- iii)前記ii)ステップで水洗された化合物を乾燥させるステップでは、50〜300℃にて減圧雰囲気で乾燥させる請求項1に記載のリチウムニッケル複合酸化物の製造方法。
- 前記iv)ステップにおいて、前記iii)ステップで乾燥された粒子、リチウム化合物、及びM3を含む化合物と混合するステップで前記M3を含む化合物は、粒径が5μm以下である請求項1に記載のリチウムニッケル複合酸化物の製造方法。
- 前記Ceを含む化合物は、CeO2である請求項1に記載のリチウムニッケル複合酸化物の製造方法。
- 前記Mgを含む化合物は、Mg(OH)2である請求項1に記載のリチウムニッケル複合酸化物の製造方法。
- 前記iv)ステップにおいて、Alを含む化合物、Mgを含む化合物、およびCeを含む化合物の合計0.001〜10重量部が、前記iii)ステップで乾燥された化合物100重量部と混合される、請求項1に記載のリチウムニッケル複合酸化物の製造方法。
- 前記vi)ステップにおいて、前記水洗溶液は、蒸留水、メタノール、エタノール、2−プロパノール、1−ブタノール、エチレングリコール、ポリビニルアルコール(PVA)、アセトン、アセチルアセトン、ベンゾフェノン、NaOH、NH4OH、LiOH、KOH、Mg(OH)2、及びBa(OH)2からなる群より選ばれた1つ以上を含む請求項1に記載のリチウムニッケル複合酸化物の製造方法。
- 前記M4を含む表面コーティング用化合物は、粒径が5μm以下である請求項1に記載のリチウムニッケル複合酸化物の製造方法。
- 前記M4を含む表面コーティング用化合物は、CeO2である請求項1に記載のリチウムニッケル複合酸化物の製造方法。