JP6825737B2 - セメント組成物及びその製造方法 - Google Patents
セメント組成物及びその製造方法 Download PDFInfo
- Publication number
- JP6825737B2 JP6825737B2 JP2020057575A JP2020057575A JP6825737B2 JP 6825737 B2 JP6825737 B2 JP 6825737B2 JP 2020057575 A JP2020057575 A JP 2020057575A JP 2020057575 A JP2020057575 A JP 2020057575A JP 6825737 B2 JP6825737 B2 JP 6825737B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- mixture
- cement
- content
- clinker
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
2 クリンカサイロ
3 仕上ミル
4 分級装置
5 混合装置
6 セメントサイロ
A 混合材
C クリンカ
D 破砕物
F 微粒側混合物
G 石膏
M 混合物
R 粗粒側混合物
Claims (6)
- セメントクリンカ、石膏及び混合材の混合物からなるセメント組成物であって、
前記セメントクリンカの鉱物組成としてのC 3 A含有率が10.1質量%以上12.2質量%以下であり、前記セメントクリンカの化学組成としてのSO3含有率が0.70質量%以上1.58質量%以下であり、前記セメントクリンカのTiO2含有率、MnO含有率、P2O5含有率、Na2O含有率及びK2O含有率をそれぞれT質量%、M質量%、P質量%、N質量%及びK質量%と定義した場合における前記セメントクリンカの物性値「(T+M+P)/(N+0.658×K)」が0.780以上1.141以下であり、
前記石膏は、前記混合物に対してSO 3 換算で1.0質量%以上2.4質量%以下の割合で前記混合物に含まれており、
前記混合材は、前記混合物に対して5.0質量%以上12.0質量%以下の割合で前記混合物に含まれており、かつ、石灰石及びフライアッシュを含んでいることを特徴とするセメント組成物。 - 前記セメントクリンカの化学組成としてのSO 3 含有率が0.94質量%以上であり、
前記混合材中の前記フライアッシュのブレーン比表面積が3500cm 2 /g以上6700cm 2 /g以下であることを特徴とする請求項1に記載のセメント組成物。 - 前記セメントクリンカの鉱物組成は、C3Sが48.0質量%以上70.0質量%以下、C2Sが9.0質量%以上22.0質量%以下、C 4 AFが7.0質量%以上12.0質量%以下であることを特徴とする請求項1又は2に記載のセメント組成物。
- 前記混合材中の前記石灰石は、前記混合物に対して3.0質量%以上5.0質量%以下の割合で前記混合物に含まれており、
前記混合材中の前記フライアッシュは、前記混合物に対して2.5質量%以上5.0質量%以下の割合で前記混合物に含まれていることを特徴とする請求項1乃至3のいずれか1項に記載のセメント組成物。 - 前記混合材は、さらに高炉スラグを含むことを特徴とする請求項1乃至4のいずれか1項に記載のセメント組成物。
- 請求項1乃至5のいずれか1項に記載のセメント組成物を製造する方法であって、
前記セメントクリンカ及び前記石膏を仕上ミルにおいて破砕し、
当該仕上ミルから排出された破砕物を前記混合材と共に混合装置において混合することを特徴とするセメント組成物の製造方法。