JP6715915B2 - Film for laminating on metal plate - Google Patents
Film for laminating on metal plate Download PDFInfo
- Publication number
- JP6715915B2 JP6715915B2 JP2018229088A JP2018229088A JP6715915B2 JP 6715915 B2 JP6715915 B2 JP 6715915B2 JP 2018229088 A JP2018229088 A JP 2018229088A JP 2018229088 A JP2018229088 A JP 2018229088A JP 6715915 B2 JP6715915 B2 JP 6715915B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- laminating
- metal plate
- layer
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、飲料缶や食缶（以下、「飲食料缶」と称する）等の材料として用いられる金属板へのラミネート用フィルムに関する。本発明のラミネート用フィルムは、製缶に際して絞り加工やしごき加工（以下、「絞り加工等」と称する）が行われるＤＲ缶やＤＩ缶といった２ピース缶の缶胴材の為の金属板へのラミネート用フィルムとして特に適する。 The present invention relates to a film for laminating a metal plate used as a material for beverage cans, food cans (hereinafter referred to as “food and drink cans”) and the like. The laminating film of the present invention is applied to a metal plate for a can body of a two-piece can such as a DR can or a DI can, which is subjected to a drawing process and an ironing process (hereinafter, referred to as “drawing process”) during can making. Particularly suitable as a laminating film.
飲食料缶は、機械的強度、密閉性に優れる容器である。また内容物を高温で充填してそのまま密封することが可能で、レトルト処理などの殺菌処理も容易に行えるため、さまざまな飲食料の容器として使用されている。
飲食料缶に用いられる金属板には、従来、内容物の風味を保つと同時に、金属板の腐食を防止するため、あるいは缶外面の美粧性の向上、印刷面の保護等を目的として、熱硬化性樹脂を主成分とする溶剤型塗料が塗布されてきた。
しかしながらこのような塗装缶においては、以下のような問題がある。
（イ）塗膜中の残留溶剤等の低分子量物質が内容物中に移行し、内容物の風味が低下する恐れがある。
（ロ）有機溶剤を多量に使用する為、環境負荷が大きく、更に塗膜の乾燥、焼き付けにも多量の熱エネルギーが必要である。
The food and drink can is a container having excellent mechanical strength and airtightness. Further, since the contents can be filled at a high temperature and sealed as it is, and sterilization treatment such as retort treatment can be easily performed, it is used as a container for various foods and drinks.
Conventionally, metal plates used for food and drink cans have been heat-treated in order to maintain the flavor of the contents and at the same time prevent corrosion of the metal plates, improve the outer appearance of the can, and protect the printing surface. Solvent-based paints based on curable resins have been applied.
However, such a paint can has the following problems.
(A) A low molecular weight substance such as a residual solvent in the coating film may migrate into the contents, and the flavor of the contents may be deteriorated.
(B) Since a large amount of organic solvent is used, the environmental load is large, and a large amount of heat energy is required for drying and baking the coating film.
このような問題のない飲食料缶として、近年、ラミネート缶が注目されている。ラミネート缶とは、溶剤型塗料に代えてプラスチックフィルムをラミネートした金属板（以下、ラミネート金属板と称す）を成形加工した缶であり、内容物の風味を低下し難く、有機溶剤を使用しない為、環境負荷も小さい。
当該ラミネート金属板に用いられるプラスチックフィルム（以下、「ラミネート用フィルム」と称す）としては、二軸延伸ポリエチレンテレフタレートフィルムが広く用いられているが、近年、ポリエチレンテレフタレート（以下、「ＰＥＴ」と略称する）の短所を補うために、ＰＥＴにポリブチレンテレフタレート（以下、「ＰＢＴ」と略称する）をブレンドすることが提案されている。
In recent years, a laminated can has attracted attention as a food and drink can without such a problem. A laminated can is a can formed by molding a metal plate (hereinafter, referred to as a laminated metal plate) laminated with a plastic film instead of the solvent-based paint, because the flavor of the contents is not easily deteriorated and an organic solvent is not used. The environmental load is also small.
A biaxially stretched polyethylene terephthalate film is widely used as a plastic film (hereinafter referred to as a “laminating film”) used for the laminated metal plate, but in recent years, polyethylene terephthalate (hereinafter abbreviated as “PET”). It has been proposed to blend PET with polybutylene terephthalate (hereinafter abbreviated as "PBT") in order to make up for the disadvantages of (1).
特許文献１は、金属板との接着性、耐レトルト性、フレーバー性、耐衝撃性等に優れたラミネート用フィルムの提供を目的とした発明であり、該ラミネート用フィルムとして、ＰＥＴ又はこれを主体とする極限粘度が０．５０~０．９０のポリエステル（Ａ）１０~６０重量％と、ＰＢＴ又はこれを主体とする極限粘度が０．６０以上のポリエステル（Ｂ）９０~４０重量％とからなるポリエステル樹脂組成物で構成されたフィルムであり、更に熱特性が特定の条件を満足するフィルムが提案されている。
特許文献２は、金属板との熱ラミネート性、缶の成形性、特に絞り成形やしごき成形等の高次加工性に優れ、更に内容物の保味保香性にも優れたラミネート用フィルムの提供を目的とし、ＰＥＴ又はこれを主体とするポリエステル（Ｉ）９０〜４５質量％とＰＢＴ又はこれを主体とするポリエステル（ＩＩ）１０〜５５質量％とからなるポリエステルＡ層と、ポリエステル（Ｉ）５５〜２５質量％とポリエステル（ＩＩ）４５〜７５質量％とからなるＢ層とを積層してなる、少なくとも２層のラミネート用フィルムが提案されている。
Patent Document 1 is an invention aimed at providing a laminating film having excellent adhesiveness to a metal plate, retort resistance, flavor resistance, impact resistance, etc., and PET or a film mainly composed of PET is used as the laminating film. From 10 to 60% by weight of polyester (A) having an intrinsic viscosity of 0.50 to 0.90 and 90 to 40% by weight of PBT or a polyester (B) mainly composed of PBT having an intrinsic viscosity of 0.60 or more. There is proposed a film which is composed of the following polyester resin composition, and further has a thermal property satisfying specific conditions.
Patent Document 2 discloses a film for laminating which is excellent in thermal laminating property with a metal plate, moldability of a can, particularly high-order processability such as drawing and ironing, and also excellent in flavor and aroma of contents. For the purpose of providing, a polyester A layer comprising 90 to 45% by mass of PET or polyester (I) mainly composed of PET and 10 to 55% by mass of PBT or polyester (II) mainly composed thereof, and polyester (I) There has been proposed a laminating film having at least two layers, which is formed by laminating a layer B composed of 55 to 25% by mass and polyester (II) 45 to 75% by mass.
特許文献３には、ラミネート性、耐摩耗性、成形加工性に優れ、金属板と貼り合せて成形加工されたあとに、美麗性に優れたラミネート用フィルムとして、融点が２４６〜２７０℃のエチレンテレフタレートを主な繰り返し単位とするポリエステル１を８０〜２０重量％、融点が１８０〜２４０℃のブチレンテレフタレートを主な繰り返し単位とするポリエステル２を２０〜８０重量％混合して成るポリエステル層（Ａ層）の少なくとも片面に、エチレンテレフタレートおよび／またはブチレンテレフタレートを主な繰り返し単位とするポリエステル３よりなる層（Ｂ層）を積層して為るポリエステルフィルムであって、フィルムのＣＯＯＨ末端基量が特定範囲であり、かつＡ層および／またはＢ層に白色顔料を混合することを特徴とする白色のラミネート用フィルムが提案されている。
しかしながらこれらのフィルムはすべて延伸フィルムであるため、絞り加工等を行う際に均一に拡張し難い。近年、飲食料缶は大容量化、薄肉化の要求が進みつつあり、絞り加工等におけるラミネート用フィルムの変形加工割合が増大している。そのためラミネート用フィルムとして延伸フィルムを用いた場合は、絞り加工等により金属板から剥離する恐れがあった。
In Patent Document 3, ethylene having a melting point of 246 to 270° C. is used as a laminating film having excellent laminating properties, abrasion resistance and molding processability, and after being formed by laminating with a metal plate and processed. 80 to 20% by weight of polyester 1 having terephthalate as a main repeating unit, and 20 to 80% by weight of polyester 2 having a melting point of 180 to 240° C. butylene terephthalate as a main repeating unit. ) Is laminated on at least one side with a layer (layer B) made of polyester 3 having ethylene terephthalate and/or butylene terephthalate as a main repeating unit, the amount of COOH terminal groups of the film being within a specific range. And a white laminating film characterized by mixing a white pigment in the A layer and/or the B layer has been proposed.
However, since all of these films are stretched films, it is difficult to uniformly expand them when performing drawing processing or the like. In recent years, there has been an increasing demand for food and drink cans having a large capacity and a thin wall, and the deformation processing ratio of the laminating film in the drawing processing is increasing. Therefore, when a stretched film is used as the laminating film, it may be peeled off from the metal plate due to a drawing process or the like.
また飲食料缶はしばしばレトルト処理が行われるが、ラミネート用フィルムの種類によっては、レトルト処理時に白く変色（以下、「レトルト白化」と称する）することがあった。レトルト白化の問題は、主としてフィルムを着色し、白化を隠蔽するという手段により解決されている。特許文献４では、ラミネート用フィルム（皮膜構造）として金属板面に接する層がＰＢＴもしくはＰＢＴが９０ｍａｓｓ％以上のポリエステル層とすることを提案している。特許文献４には、レトルト白化はレトルト処理時にフィルム内に浸入してきた水蒸気に起因すること、このような水蒸気の浸入を防止するためには、金属板に接する層に結晶化速度の速いＰＢＴを用いるとよいことが記載されている。 Further, food and drink cans are often subjected to retort treatment, but depending on the type of laminating film, they may turn white during retort treatment (hereinafter referred to as "retort whitening"). The problem of retort whitening is solved primarily by the means of coloring the film and masking the whitening. Patent Document 4 proposes that the layer in contact with the metal plate surface is a PBT or a polyester layer having PBT of 90 mass% or more as a laminating film (coating structure). Patent Document 4 discloses that retort whitening is caused by water vapor that has penetrated into the film during retort treatment. It is described that it is good to use.
本発明者らは、レトルト処理適性、絞り加工性、しごき加工性に優れたラミネート用フィルムを鋭意検討する過程で、特許文献４記載のラミネート用フィルムは、レトルト白化は起こり難いものの、加工条件によっては金属板に対し密着不良となることを見出した。
ラミネート金属板における主な密着不良は以下の３つである。
（１）ラミネート用フィルムと金属板とを貼合した際の密着性（以下、「一次密着性」と称す）が不足し、貼合直後に金属板からラミネート用フィルムが剥離する。
（２）ラミネート用フィルムと金属板とを貼合した後、得られるラミネート金属板をレトルト処理した際の密着性（以下、「二次密着性」と称す）が低下し、レトルト処理直後に金属板からラミネート用フィルムが剥離する。
（３）ラミネート用フィルムと金属板とを貼合し、絞り加工等を行った後にレトルト処理を行った際の密着性（以下、「成形後密着性」と称す）が低下し、金属板からラミネート用フィルムが剥離する。
特許文献４記載のラミネート用フィルムは、一次密着性は良好であるが、二次密着性、成形後密着性が満足できるものではなかった。
本発明は、レトルト処理適性、絞り加工性、しごき加工性に優れたラミネート用フィルムの提供を目的とするもので、レトルト処理を行っても白化したり、金属板から剥離したりすることのないラミネート用フィルムであって、絞り加工後のレトルト処理等によっても剥離しないラミネート用フィルムの提供を課題とする。
In the process of diligently studying a laminating film having excellent retort treatment suitability, drawability, and ironing processability, the present inventors have found that the laminating film described in Patent Document 4 is unlikely to cause retort whitening, but depending on the processing conditions. Found that the adhesion to the metal plate was poor.
The three main adhesion defects in a laminated metal plate are as follows.
(1) Adhesiveness (hereinafter, referred to as “primary adhesiveness”) when the laminating film and the metal plate are bonded together is insufficient, and the laminating film is peeled off from the metal plate immediately after bonding.
(2) After laminating the laminating film and the metal plate, the adhesion (hereinafter, referred to as “secondary adhesion”) when the obtained laminated metal plate is subjected to retort treatment is deteriorated, and the metal is formed immediately after the retort treatment. The laminating film peels from the plate.
(3) Adhesion (hereinafter referred to as “adhesion after molding”) when a laminating film and a metal plate are bonded together and subjected to a retort treatment after performing drawing processing, etc. The laminating film peels off.
The laminating film described in Patent Document 4 has good primary adhesion, but is not satisfactory in secondary adhesion and adhesion after molding.
The present invention is intended to provide a laminating film excellent in retort processing suitability, drawability, and ironing workability, and does not whiten or peel from a metal plate even after retort processing. An object of the present invention is to provide a laminating film that is not peeled off even by a retort treatment after drawing.
本発明者らは上記課題を解決するための手段を鋭意検討した結果、ラミネート用フィルムの主たる層を結晶化速度が速くレトルト白化し難いＰＢＴ系樹脂が９０重量％以上である樹脂組成物から形成し、さらに接着層にＰＥＴ系樹脂を１５~４５重量％添加することにより、上記課題が解決できることを見出した。ＰＥＴ系樹脂の使用は、密着性の改善に寄与するがレトルト白化を誘発する恐れがある。しかしながら本発明者らは、当該樹脂の配合割合が４５重量％以下であればレトルト白化を顕著に抑制できることを見出したのである。 As a result of earnest studies on means for solving the above-mentioned problems, the present inventors formed a main layer of a laminating film from a resin composition containing 90% by weight or more of a PBT-based resin having a high crystallization rate and hardly retort whitening. It was found that the above problem can be solved by further adding 15 to 45% by weight of PET resin to the adhesive layer. The use of PET-based resin contributes to the improvement of adhesion, but may induce retort whitening. However, the present inventors have found that retort whitening can be significantly suppressed if the blending ratio of the resin is 45% by weight or less.
即ち、本発明によると上記課題を解決するための手段として、接着層と基材層とを備える未延伸フィルムであって、前記接着層はポリブチレンテレフタレート系樹脂８５〜５５重量％とポリエチレンテレフタレート系樹脂１５〜４５重量％とからなる樹脂組成物から形成され、前記基材層がポリブチレンテレフタレート系樹脂９９．５〜９０重量％とポリエチレンテレフタレート系樹脂０．５〜１０重量％とからなる樹脂組成物から形成されており、前記基材層の厚さが未延伸フィルム全体の厚さの１／２以上であることを特徴とする製缶のための金属板へのラミネート用フィルムが提供され、
前記基材層の、前記接着層を備える面と反対側の面に、外層を備えることを特徴とする前記製缶のための金属板へのラミネート用フィルムが提供され、
厚さが２５μｍ以下であることを特徴とする前記製缶のための金属板へのラミネート用フィルムが提供され
前記ポリエチレンテレフタレート系樹脂が、ポリエチレンテレフタレートのホモポリマーであることを特徴とする前記製缶のための金属板へのラミネート用フィルムが提供される。
That is, according to the present invention, as a means for solving the above problems, it is an unstretched film comprising an adhesive layer and a base material layer, wherein the adhesive layer comprises 85 to 55% by weight of polybutylene terephthalate resin and polyethylene terephthalate resin. A resin composition formed from a resin composition containing 15 to 45% by weight of a resin, wherein the base material layer comprises 99.5 to 90% by weight of a polybutylene terephthalate resin and 0.5 to 10% by weight of a polyethylene terephthalate resin. A film for laminating to a metal plate for can making, wherein the film is formed from a material, and the thickness of the substrate layer is ½ or more of the thickness of the entire unstretched film,
Provided is a film for laminating to a metal plate for the can, which is characterized in that an outer layer is provided on the surface of the base material layer opposite to the surface having the adhesive layer,
Provided is a film for laminating a metal plate for the can, having a thickness of 25 μm or less, wherein the polyethylene terephthalate-based resin is a homopolymer of polyethylene terephthalate. There is provided a film for laminating to a metal plate.
更に本発明によると、前記製缶のための金属板へのラミネート用フィルムの製造方法であって、共押出キャスティング法によることを特徴とする製缶のための金属板へのラミネート用フィルムの製造方法が提供される。 Furthermore, according to the present invention, there is provided a method for producing a film for laminating on a metal plate for can making, which is characterized by a coextrusion casting method, for producing a film for laminating on a metal plate for can making. A method is provided.
本発明の金属板へのラミネート用フィルムは、金属板との一次密着性に優れるだけでなく、二次密着性、成形後密着性にも優れ、更にレトルト処理を行ってもほとんど白化することがない。
よって、本発明のラミネート用フィルムを貼合した金属板は、レトルト処理適性、絞り加工性、しごき加工性に優れる。
The film for laminating on a metal plate of the present invention is not only excellent in primary adhesion to the metal plate, but also excellent in secondary adhesion and adhesion after molding, and can be almost whitened even after retort treatment. Absent.
Therefore, the metal plate to which the laminating film of the present invention is attached is excellent in retort treatment suitability, drawing workability, and ironing workability.
以下、本発明を詳細に説明する。尚、本発明のラミネート用フィルムは、接着層および基材層、更には外層を備えるが、他の樹脂層を備えることを除外するものではない。 Hereinafter, the present invention will be described in detail. The laminating film of the present invention includes an adhesive layer, a base material layer, and an outer layer, but does not exclude the provision of another resin layer.
［ラミネート用フィルム］
本発明のラミネート用フィルムは、少なくとも接着層及び基材層を備え、必要に応じて更に外層を備える。図１は本発明のラミネート用フィルムの模式断面図で、図１（α）は接着層Ａと基材層Ｂのみからなるラミネート用フィルム１０αであり、図１（β）は更に外層Ｃを備えるラミネート用フィルム１０βである。該外層Ｃは、基材層Ｂの接着層Ａを有する面と反対側の面に位置する。よって、本発明のラミネート用フィルムを金属板に貼合した際には、金属板側から順に、接着層Ａ、基材層Ｂ、外層Ｃとなる。
また本発明のラミネート用フィルムは、未延伸フィルムである。延伸処理されたフィルムは引張破断伸度が小さく、絞り加工等を行う際に拡張し難く、破れやすい。
本発明のラミネート用フィルムの膜厚は、３０μｍ以下であることが望ましく、特に２５μｍ以下であることが望ましい。膜厚が増加すると、金属板へのラミネート速度が遅くなる為、生産性が低下する。また膜厚が増加するとレトルト処理時にフィルム内部に蓄積される水蒸気量も増加する恐れがある。レトルト処理時にフィルム内部に蓄積された水蒸気が、そのままフィルム内部で気泡となるとレトルト白化の原因となる。
[Film for laminating]
The laminating film of the present invention includes at least an adhesive layer and a base material layer, and further includes an outer layer as necessary. FIG. 1 is a schematic cross-sectional view of a laminating film of the present invention. FIG. 1(α) is a laminating film 10α composed only of an adhesive layer A and a base material layer B, and FIG. 1(β) further includes an outer layer C. It is a film for lamination 10β. The outer layer C is located on the surface of the base material layer B opposite to the surface having the adhesive layer A. Therefore, when the laminating film of the present invention is attached to a metal plate, the adhesive layer A, the base material layer B, and the outer layer C are formed in order from the metal plate side.
The laminating film of the present invention is an unstretched film. The stretched film has a small tensile elongation at break, is difficult to expand when drawn and is easily broken.
The film thickness of the laminating film of the present invention is preferably 30 μm or less, and particularly preferably 25 μm or less. When the film thickness is increased, the laminating speed on the metal plate becomes slower, which lowers the productivity. Further, as the film thickness increases, the amount of water vapor accumulated inside the film during the retort treatment may increase. If the water vapor accumulated inside the film during the retort treatment becomes bubbles inside the film as it is, it causes the retort whitening.
［接着層］
本発明の接着層は、金属板と接する樹脂層であり、ＰＢＴ系樹脂とＰＥＴ系樹脂とからなる樹脂組成物から形成される。
ＰＢＴ系樹脂とは、テレフタル酸成分と１，４−ブタンジオール成分とを主成分として溶融重縮合反応、あるいは引き続いて固相重合されたＰＢＴのホモポリマー、テレフタル酸成分と１，４−ブタンジオール成分とを主成分とし、本発明の効果が損なわれない範囲で適宜他の成分を共重合した共重合タイプのＰＢＴであるが、レトルト白化の問題を考慮するとＰＢＴのホモポリマーであることを望ましい。またＰＥＴ系樹脂とは、テレフタル酸成分とエチレングリコール成分とを主成分として溶融重縮合反応、あるいは引き続いて固相重合されたＰＥＴのホモポリマー、テレフタル酸成分とエチレングリコール成分とを主成分とし、本発明の効果が損なわれない範囲で適宜他の成分を共重合した共重合体タイプのＰＥＴであるが、レトルト白化の観点からＰＥＴのホモポリマーが特に適する。ＰＥＴのホモポリマーがレトルト白化を抑制する理由は定かではないが、共重合タイプのＰＥＴよりも高い結晶性を持つためと推察される。
接着層におけるＰＢＴ系樹脂とＰＥＴ系樹脂との配合割合は、ＰＢＴ系樹脂：ＰＥＴ系樹脂＝８５〜５５重量％：１５〜４５重量％が好ましく、特に６３〜５２重量％：３７〜４８重量％が好ましい。ＰＥＴ系樹脂の配合割合が上記範囲よりも小さいと、ラミネート用フィルムと金属板の二次密着性、成形後密着性が不足する。逆にＰＥＴ系樹脂の配合割合が上記範囲よりも大きくなると、レトルト白化の恐れが生じる。
[Adhesive layer]
The adhesive layer of the present invention is a resin layer that is in contact with the metal plate, and is formed from a resin composition including a PBT resin and a PET resin.
The PBT-based resin is a homopolymer of PBT that is a terephthalic acid component and a 1,4-butanediol component as main components, or is a solid polymerized PBT homopolymer, a terephthalic acid component and 1,4-butanediol component. The PBT is a copolymer type PBT in which the other components are appropriately copolymerized within a range in which the effects of the present invention are not impaired, but a homopolymer of PBT is desirable in view of the problem of retort whitening. .. In addition, the PET resin is a melt polycondensation reaction mainly composed of a terephthalic acid component and an ethylene glycol component, or a homopolymer of PET which is subsequently solid-phase polymerized, and a main component is a terephthalic acid component and an ethylene glycol component, Although it is a copolymer type PET in which other components are appropriately copolymerized within the range where the effect of the present invention is not impaired, a homopolymer of PET is particularly suitable from the viewpoint of retort whitening. The reason why the PET homopolymer suppresses retort whitening is not clear, but it is presumed that it is because it has higher crystallinity than the copolymer type PET.
The blending ratio of the PBT resin and the PET resin in the adhesive layer is preferably PBT resin:PET resin=85 to 55% by weight:15 to 45% by weight, and particularly 63 to 52% by weight:37 to 48% by weight. Is preferred. If the mixing ratio of the PET resin is smaller than the above range, the secondary adhesion between the laminating film and the metal plate and the adhesion after molding will be insufficient. On the other hand, if the blending ratio of the PET resin is larger than the above range, retort whitening may occur.
該接着層の膜厚は、基材層の厚さがラミネートフィルム全体の厚さの１／２以上になることを妨げなければ特に限定されないが、０．５〜１０μｍ程度が好ましく、１〜５μｍがより好ましく、２〜４μｍが特に好ましい。接着層の膜厚が０．５μｍ未満では密着性の改善効果に乏しく、１０μｍを超えるとレトルト白化抑制効果が低下する。また接着層の厚さが２〜４μｍであると、レトルト白化抑制効果、成形後密着性が共に優れる。 The thickness of the adhesive layer is not particularly limited as long as it does not prevent the thickness of the base material layer from becoming more than half the thickness of the entire laminate film, but is preferably about 0.5 to 10 μm, and 1 to 5 μm. Are more preferable, and 2-4 micrometers is especially preferable. When the film thickness of the adhesive layer is less than 0.5 μm, the effect of improving the adhesion is poor, and when it exceeds 10 μm, the retort whitening suppression effect is reduced. Further, when the thickness of the adhesive layer is 2 to 4 μm, both the retort whitening suppressing effect and the adhesion after molding are excellent.
［基材層］
本発明の基材層は、ラミネート用フィルムにおける主たる層であり、ＰＢＴ系樹脂が９０重量％以上である樹脂組成物から形成される。
基材層におけるＰＢＴ系樹脂も、接着層におけるＰＢＴ系樹脂と同様、ＰＢＴのホモポリマー、或いは該樹脂を主成分とし、本発明の効果が損なわれない範囲で適宜他の成分を共重合した共重合タイプのＰＢＴである。また接着層と同様に、レトルト白化を抑えるためにはＰＢＴのホモポリマーが特に適する。
基材層には、ＰＢＴ系樹脂の耐レトルト白化性を阻害しない範囲で他の樹脂成分を配することができる。そして、接着層との密着性を考慮すると若干のＰＥＴ系樹脂を配することが望ましい。該ＰＥＴ系樹脂を配合する場合、配合量は０．５〜１０重量％が適する。配合量が０．５重量％未満であると接着層との密着性改善の効果が期待できず、１０重量％を超えるとＰＢＴ系樹脂の耐レトルト白化性能を低下させる恐れがある。基材層におけるＰＥＴ系樹脂は、外層におけるＰＥＴ系樹脂と同様に、ＰＥＴのホモポリマー、或いは共重合体タイプのＰＥＴから選ばれる。外層におけるＰＥＴ系樹脂と、基材層におけるＰＥＴ系樹脂が同じタイプの樹脂であると、層間の密着性が特に良好となり、成形後密着性に優れる。
[Base material layer]
The base material layer of the present invention is the main layer in the laminating film, and is formed from a resin composition containing 90% by weight or more of PBT resin.
Similarly to the PBT-based resin in the adhesive layer, the PBT-based resin in the base material layer is a homopolymer of PBT or a copolymer containing the resin as a main component and other components as appropriate as long as the effects of the present invention are not impaired. It is a polymerization type PBT. Also, as with the adhesive layer, a homopolymer of PBT is particularly suitable for suppressing retort whitening.
Other resin components can be arranged in the base material layer in a range that does not impair the retort whitening resistance of the PBT resin. Considering the adhesiveness with the adhesive layer, it is desirable to dispose a small amount of PET resin. When the PET resin is blended, the blending amount is preferably 0.5 to 10% by weight. If the amount is less than 0.5% by weight, the effect of improving the adhesion to the adhesive layer cannot be expected, and if it exceeds 10% by weight, the retort whitening resistance of the PBT resin may be deteriorated. The PET resin in the base material layer is selected from PET homopolymer or copolymer type PET, like the PET resin in the outer layer. When the PET resin in the outer layer and the PET resin in the base material layer are of the same type, the adhesion between the layers becomes particularly good, and the adhesion after molding is excellent.
［外層］
外層（Ｃ）を成す樹脂組成は特に限定されず、飲料用缶に充填される内容物、飲料用缶を製缶する際の加工条件等に応じ適宜決定すればよいが、レトルト白化を抑えるために、ＰＥＴ系樹脂の配合割合が４５重量％以下であることが望ましい。また、該外層（Ｃ）を接着層（Ａ）と同じ樹脂組成物とすれば、ラミネート用フィルムを金属板に積層する際に、ラミネート用フィルムの表裏を区別する必要がなくなる為、作業性が向上する。尚、この場合、外層（Ｃ）の厚さも接着層（Ａ）の厚さと同じであることが望ましい。
[Outer layer]
The resin composition forming the outer layer (C) is not particularly limited, and may be appropriately determined according to the contents to be filled in the beverage can, the processing conditions for producing the beverage can, and the like, in order to suppress retort whitening. In addition, it is desirable that the proportion of the PET resin be 45% by weight or less. Further, when the outer layer (C) is made of the same resin composition as the adhesive layer (A), it is not necessary to distinguish the front and back of the laminating film when laminating the laminating film on the metal plate, and thus workability is improved. improves. In this case, it is desirable that the outer layer (C) also has the same thickness as the adhesive layer (A).
上述した接着層、基材層、外層の各層には滑剤、ブロッキング防止剤、帯電防止剤、防曇剤、酸化防止剤、熱安定剤、光安定剤、紫外線吸収剤、着色剤、顔料剤、帯電防止剤、結晶核剤等の添加剤を適宜添加することができる。尚、ＰＥＴ系樹脂はＰＢＴ系樹脂に比べて結晶化速度が遅い為、ＰＥＴ系樹脂を添加する層には結晶核剤を添加することが好ましい。フィルムを着色する場合は、例えば０．１〜１０重量％の顔料を結晶核剤に代えて用いることができる。 Lubricants, antiblocking agents, antistatic agents, antifogging agents, antioxidants, heat stabilizers, light stabilizers, ultraviolet absorbers, coloring agents, pigment agents, and Additives such as an antistatic agent and a crystal nucleating agent can be appropriately added. Since the PET resin has a slower crystallization rate than the PBT resin, it is preferable to add a crystal nucleating agent to the layer to which the PET resin is added. When the film is colored, for example, 0.1 to 10% by weight of pigment can be used instead of the crystal nucleating agent.
［ラミネート用金属板の製造方法］
本発明のラミネート用フィルムの製造方法は特に限定されないが、品質の良好なフィルムを連続して製造するためには、共押出キャスティング法を採用することが望ましい。具体的には、接着層用樹脂組成物、基材層用樹脂組成物、必要に応じて外層用樹脂組成物を、別々の押出機から一つのフラットダイへ供給し、該フラットダイからフィルム状に溶融押出し、キャスティングロールにて冷却し、これを延伸処理することなく製膜することが望ましい。延伸処理を施さないフィルムは、鋼板へラミネートする際に、ラミネート可能な温度領域が広い。
[Method of manufacturing metal plate for lamination]
The method for producing the laminating film of the present invention is not particularly limited, but it is desirable to adopt the coextrusion casting method in order to continuously produce a good quality film. Specifically, the resin composition for the adhesive layer, the resin composition for the base layer and, if necessary, the resin composition for the outer layer are supplied to one flat die from different extruders, and the flat die is formed into a film. It is desirable that the film is melt extruded, cooled by a casting roll, and formed into a film without stretching. A film that has not been stretched has a wide temperature range in which it can be laminated when laminated on a steel sheet.
［ラミネート金属板］
本発明のラミネート用フィルムをラミネートする金属板は特に限定されるものではないが、安価で且つ密着性に優れるティンフリースチール、ブリキなどの表面処理鋼板、アルミニウム板を用いることができる。また金属板に本発明のラミネート用フィルムを貼合する方法としては、熱圧着法を例示することができる。具体的には、金属板を予め所定温度まで予熱しておき、これとラミネート用フィルムとを温度制御可能なロールによって圧接して熱圧着させた後、室温まで冷却するとよい。
本発明のラミネート用フィルムが積層されたラミネート金属板は、２ピース缶の上蓋、缶胴材、３ピース缶の上蓋、底蓋、缶胴材として用いることができるが、優れた密着性を考慮すると、２ピース缶の缶胴材として特に適している。またレトルト白化の問題もない為、レトルト処理を行う食品の包装に特に適し、特にレトルト白化の目立つ缶の外側にラミネートするフィルムとして適する。
[Laminated metal plate]
The metal plate for laminating the laminating film of the present invention is not particularly limited, but tin-free steel, a surface-treated steel plate such as tin plate, or an aluminum plate which is inexpensive and has excellent adhesion can be used. As a method for laminating the laminating film of the present invention on a metal plate, a thermocompression bonding method can be exemplified. Specifically, the metal plate may be preheated to a predetermined temperature in advance, and the film and the laminating film may be pressure-contacted by a temperature-controllable roll to thermocompression-bond them, and then cooled to room temperature.
The laminated metal plate laminated with the laminating film of the present invention can be used as an upper lid of a two-piece can, a can body, a three-piece can upper lid, a bottom lid, and a can body, in consideration of excellent adhesion. Then, it is particularly suitable as a can body for a two-piece can. Further, since there is no problem of retort whitening, it is particularly suitable for packaging of foods to be subjected to retort treatment, and particularly suitable as a film to be laminated on the outside of a can where retort whitening is conspicuous.
以下、実施例に基づき本発明の効果を詳細に説明する。尚、本発明のフィルムの評価は以下の方法にて行う。
（１）耐レトルト白化性
初めに金属板にラミネート用フィルムを熱圧着してラミネート金属板を得る。次いで、該ラミネート金属板を底蓋形状に打ち抜き、これを試験片とする。該試験片を缶銅に巻き締めた後、１２５℃で９０分間、レトルト処理を行う。処理後、試験片における白化部分の面積率を求め、耐レトルト白化性を評価する。
Hereinafter, the effects of the present invention will be described in detail based on examples. The film of the present invention is evaluated by the following methods.
(1) Retort whitening resistance A laminated film is first thermocompression bonded to a metal plate to obtain a laminated metal plate. Next, the laminated metal plate is punched into a bottom lid shape, and this is used as a test piece. After the test piece is wound around the copper can, the retort treatment is performed at 125° C. for 90 minutes. After the treatment, the area ratio of the whitened portion in the test piece is obtained and the retort whitening resistance is evaluated.
（２）一次密着性
初めに金属板にラミネート用フィルムを熱圧着してラミネート金属板を得る。次いで、該ラミネート金属板の端部において、ラミネート用フィルムの一部を剥離し、該剥離部分を１８０°開いた状態でオートグラフに装着し、ラミネート用フィルムを剥離するために必要な力を測定する。該力が大きいほど、一次密着性は高く、６Ｎ／１５ｍｍ以上であれば、実用上問題はない。
(2) Primary Adhesion First, a laminating film is thermocompression bonded to a metal plate to obtain a laminated metal plate. Next, at the end of the laminated metal plate, a part of the laminating film was peeled off, and the peeled part was mounted on an autograph with the 180° open state, and the force required to peel off the laminating film was measured. To do. The larger the force is, the higher the primary adhesion is. If it is 6 N/15 mm or more, there is no practical problem.
（３）二次密着性
耐レトルト白化性の試験と同様にして、底蓋形状の試験片を作成し、該試験片を缶銅に巻き締めた後、１２５℃９０分間、レトルト処理を行う。処理後、ラミネート用フィルムが金属板から剥離している部分の長さを測定し、二次密着性を評価する。
(3) Secondary Adhesion In the same manner as the retort whitening resistance test, a bottom lid-shaped test piece is prepared, and the test piece is wound around a copper can and then retort-treated at 125° C. for 90 minutes. After the treatment, the length of the portion where the laminating film is peeled off from the metal plate is measured to evaluate the secondary adhesion.
（４）成形後密着性
初めに金属板にラミネート用フィルムを熱圧着してラミネート金属板を得る。次いで、該ラミネート金属板を絞りしごき加工にてＤＩ缶に成形する。得られるＤＩ缶を１２５℃９０分間レトルト処理し、処理後、缶上端から剥離したラミネート用フィルムの長さを測定し、成形後密着性を評価する。
(4) Adhesion after molding First, a laminating film is thermocompression-bonded to a metal plate to obtain a laminated metal plate. Next, the laminated metal plate is squeezed and ironed to form a DI can. The resulting DI can is subjected to retort treatment at 125° C. for 90 minutes, after the treatment, the length of the laminating film peeled from the upper end of the can is measured, and the adhesion after molding is evaluated.
［実施例１］
接着層及び外層用の樹脂組成物として、ＰＢＴのホモポリマーを６０重量％とＰＥＴのホモポリマーを４０重量％混合したものを、基材層用の樹脂組成物として、ＰＢＴのホモポリマーを９７重量％、ＰＥＴのホモポリマーを３重量％混合したものを用い、共押出キャスティング法にて、厚み１８μｍのラミネート用フィルムを製造した。各層の厚さ構成比は、接着層：基材層：外層＝２：６：２である。得られたラミネート用フィルムを用いて（１）（２）（３）の評価を行った。結果を表１に記す。
[Example 1]
As a resin composition for the adhesive layer and the outer layer, a mixture of 60% by weight of PBT homopolymer and 40% by weight of PET homopolymer was used, and as a resin composition for the base layer, 97% by weight of PBT homopolymer. %, and a homopolymer of PET of 3% by weight were mixed, and a film for lamination having a thickness of 18 μm was manufactured by a coextrusion casting method. The thickness composition ratio of each layer is adhesive layer:base material layer:outer layer=2:6:2. The obtained films for laminating were used to evaluate (1), (2) and (3). The results are shown in Table 1.
［実施例２］
各層の厚さ構成比を、接着層：基材層：外層＝１：８：１とした以外は実施例１と同様にして、ラミネート用フィルムを得た。得られたラミネート用フィルムを用いて（１）（２）（３）の評価を行った。結果を表１に記す。
［実施例３、４］
ＰＥＴのホモポリマーに代えて、ポリエチレンテレフタレート−ポリエチレンイソフタレート共重合体（イソフタレート８ｍｏｌ％）を用い、接着層及び外層における該樹脂の配合割合を表１に記すように変化した以外は実施例１と同様にしてラミネート用フィルムを得た。尚、表１においてポリエチレンテレフタレート−ポリエチレンイソフタレート共重合体（イソフタレート８ｍｏｌ％）は、ＰＥＴ−ｉと表記する。得られたフィルムを用いたラミネート金属板の評価を表１に記す。
[Example 2]
A laminating film was obtained in the same manner as in Example 1 except that the thickness composition ratio of each layer was adhesive layer:base material layer:outer layer=1:8:1. The obtained films for laminating were used to evaluate (1), (2) and (3). The results are shown in Table 1.
[Examples 3 and 4]
Example 1 except that a polyethylene terephthalate-polyethylene isophthalate copolymer (isophthalate 8 mol%) was used instead of the PET homopolymer, and the blending ratio of the resin in the adhesive layer and the outer layer was changed as shown in Table 1. A film for lamination was obtained in the same manner as in. In Table 1, a polyethylene terephthalate-polyethylene isophthalate copolymer (isophthalate 8 mol%) is referred to as PET-i. Table 1 shows the evaluation of the laminated metal plate using the obtained film.
［比較例１］
ＰＢＴのホモポリマーを用い、１８μｍの単層のラミネート用フィルムを得た。得られたラミネート用フィルムを用いて（１）（２）（３）の評価を行った。結果を表１に記す。
［比較例２乃至５］
接着層、基材層、外層を形成する樹脂組成物、各層の厚さ構成比を表１に記すように変化した以外は、実施例１と同様にしてラミネート用フィルムを得た。尚、表中のＰＢＴはポリブチレンテレフタレートのホモポリマー、ＰＥＴはポリエチレンテレフタレートのホモポリマー、ＰＥＴ−ｉはポリエチレンテレフタレート−ポリエチレンイソフタレート共重合体（イソフタレート８ｍｏｌ％）を表す。得られたラミネート用フィルムを用いて（１）（２）（３）の評価を行った。結果を表１に記す。
[Comparative Example 1]
Using a homopolymer of PBT, a 18 μm single-layer laminating film was obtained. The obtained films for laminating were used to evaluate (1), (2) and (3). The results are shown in Table 1.
[Comparative Examples 2 to 5]
A laminating film was obtained in the same manner as in Example 1 except that the adhesive composition, the base material layer, the resin composition forming the outer layer, and the thickness composition ratio of each layer were changed as shown in Table 1. In the table, PBT represents a homopolymer of polybutylene terephthalate, PET represents a homopolymer of polyethylene terephthalate, and PET-i represents a polyethylene terephthalate-polyethylene isophthalate copolymer (isophthalate 8 mol%). The obtained films for laminating were used to evaluate (1), (2) and (3). The results are shown in Table 1.
接着層及び外層におけるＰＥＴ系樹脂の割合が４５重量％以下である実施例１乃至４のフィルムを用いたラミネート金属板は、耐レトルト白化試験によってほとんど変色が見られなかった。特に、ＰＥＴ系樹脂としてＰＥＴのホモポリマーを用いた実施例１及び２のフィルムは、レトルト白化が全く見られなかった。一方、ＰＥＴ系樹脂の配合割合が４５重量％を超える比較例２乃至５のフィルムを用いると、耐レトルト白化試験において、大きな面積が白化していた。また比較例１のフィルムを用いた金属板は、レトルト白化は見られなかったが、二次密着性試験において大きな剥離（５ｍｍを超える剥離）が見られた。 The laminated metal plates using the films of Examples 1 to 4 in which the proportion of the PET resin in the adhesive layer and the outer layer was 45% by weight or less showed almost no discoloration by the retort whitening resistance test. In particular, the retort whitening was not observed at all in the films of Examples 1 and 2 in which a PET homopolymer was used as the PET resin. On the other hand, when the films of Comparative Examples 2 to 5 in which the mixing ratio of the PET resin exceeded 45% by weight were used, a large area was whitened in the retort whitening resistance test. The metal plate using the film of Comparative Example 1 did not show retort whitening, but large peeling (peeling exceeding 5 mm) was seen in the secondary adhesion test.
次に、実施例１乃至４、比較例１、比較例３のフィルムをラミネートしたラミネート金属板を用いて、ＤＩ缶を成形し、成形後密着性を確認した。結果を表１に合せて記す。実施例１乃至４のフィルムを用いたものは、剥離がほとんど見られず、成形後密着性が良好であることが確認できた。特に実施例１のフィルムは、剥離が全く見られず、成形後密着性に優れるものであった。一方、ＰＥＴ系樹脂が添加されていない比較例１のフィルムはラミネート用フィルムが大きく剥離していた。また接着性樹脂層にＰＥＴ系樹脂が４５重量％を超えて配合されている比較例３も、成形後密着性は不良であった。 Next, using the laminated metal plate laminated with the films of Examples 1 to 4, Comparative Example 1 and Comparative Example 3, a DI can was molded, and the adhesion after molding was confirmed. The results are also shown in Table 1. With the films using Examples 1 to 4, peeling was hardly seen, and it was confirmed that the adhesiveness after molding was good. In particular, the film of Example 1 showed no peeling at all and was excellent in adhesion after molding. On the other hand, in the film of Comparative Example 1 to which the PET resin was not added, the laminating film was largely peeled off. Also, in Comparative Example 3 in which the PET resin was blended in the adhesive resin layer in an amount of more than 45% by weight, the adhesion after molding was poor.
１０、１０α、１０β：金属板へのラミネート用フィルム
Ａ：接着層
Ｂ：基材層
Ｃ：外層
10, 10α, 10β: Film for laminating on a metal plate A: adhesive layer B: base material layer C: outer layer
Claims (5)
前記接着層はポリブチレンテレフタレート系樹脂８５〜５５重量％とポリエチレンテレフタレート系樹脂１５〜４５重量％とからなる樹脂組成物から形成され、前記基材層がポリブチレンテレフタレート系樹脂９９．５〜９０重量％とポリエチレンテレフタレート系樹脂０．５〜１０重量％とからなる樹脂組成物から形成されており、
厚さが３０μｍ以下、且つ前記基材層の厚さが未延伸フィルム全体の厚さの１／２以上であることを特徴とする製缶のための金属板へのラミネート用フィルム。 An unstretched film comprising an adhesive layer and a base material layer,
The adhesive layer is formed of a resin composition of 85 to 55% by weight of polybutylene terephthalate resin and 15 to 45% by weight of polyethylene terephthalate resin, and the base material layer is 99.5 to 90% by weight of polybutylene terephthalate resin. % And a polyethylene terephthalate-based resin of 0.5 to 10% by weight,
A film for laminating to a metal plate for a can, wherein the thickness of the substrate layer is 30 μm or less, and the thickness of the base layer is ½ or more of the total thickness of the unstretched film.