JP6714325B2 - 耐摩耗性、寸法安定性、滑り性及び防汚性を有するモノフィラメント、それを含む編織布及びその使用 - Google Patents
耐摩耗性、寸法安定性、滑り性及び防汚性を有するモノフィラメント、それを含む編織布及びその使用 Download PDFInfo
- Publication number
- JP6714325B2 JP6714325B2 JP2015083189A JP2015083189A JP6714325B2 JP 6714325 B2 JP6714325 B2 JP 6714325B2 JP 2015083189 A JP2015083189 A JP 2015083189A JP 2015083189 A JP2015083189 A JP 2015083189A JP 6714325 B2 JP6714325 B2 JP 6714325B2
- Authority
- JP
- Japan
- Prior art keywords
- monofilament
- polysiloxane
- nylon
- fabric
- monofilaments
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
i)マトリックスポリマーとポリシロキサン粒子、又はマトリックスポリマーと、ポリシロキサン粒子を含むマスターバッチを押出機内で混合する、
ii)工程i)の混合物を紡糸口金ダイから押し出す、
iii)得られたモノフィラメントを抜き取る、
iv)任意にモノフィラメントを延伸及び/又は緩和する、そして
v)モノフィラメントを巻き取る
の手段を含む。
[発明の態様]
[1]
熱可塑性ポリマーのマトリックスと、その中に分散された直径10nm〜200μmのポリシロキサンの粒子とを含むモノフィラメント。
[2]
ポリシロキサンの粒子が球形で、直径0.2〜50μmである、1に記載のモノフィラメント。
[3]
粒子が0.01〜8wt%存在する、1及び2のいずれかに記載のモノフィラメント。
[4]
ポリシロキサンが、反復構造要素−SiR 1 R 2 −O−を含む線状又は架橋ポリシロキサンであるか、又は、式R 1 SiO 3/2 [式中、R 1 はC 1 −C 6 −アルキル、特にメチルであり、R 2 はC 1 −C 6 −アルキル又はフェニル、特にメチル又はフェニルである]のシルセスキオキサンである、1〜3のいずれかに記載のモノフィラメント。
[5]
ポリシロキサンが、線状又は架橋ポリジメチルシロキサン又はポリメチルシルセスキオキサンである、4に記載のモノフィラメント。
[6]
熱可塑性ポリマーが、ポリエステル、ポリアミド、ポリエーテルケトン、ポリフェニレンスルフィド、ポリオレフィン又はこれらの二つ以上の組合せである、1〜5のいずれかに記載のモノフィラメント。
[7]
熱可塑性ポリマーが、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ジカルボン酸変性ポリエチレンテレフタレート、ジカルボン酸変性ポリブチレンテレフタレート、ナイロン−6、ナイロン−6,6、ナイロン−6,10、ナイロン−12、ナイロン−6,12又はこれらの二つ以上の組合せである、6に記載のモノフィラメント。
[8]
カルボジイミド安定剤、好ましくは高分子カルボジイミド安定剤をさらに含む、1〜7のいずれかに記載のモノフィラメント。
[9]
熱可塑性ポリマーの割合が60〜95wt%、ポリシロキサンの割合が0.02〜8wt%、そしてカルボジイミドの割合が0〜10wt%であり、ここで量的詳細はモノフィラメントの全量に基づく、1〜8のいずれかに記載のモノフィラメント。
[10]
0.001〜10wt%の慣用添加剤、特に、酸化剤、UV安定剤、充填剤、顔料、殺生物剤、導電率向上剤、耐摩耗性増強剤、減摩添加剤、スピン仕上げ剤、加工助剤、可塑剤、滑沢剤、艶消剤、粘度調整剤、結晶化促進剤又はこれらの二つ以上の組合せをさらに含む、1〜9の1項又は複数の項に記載のモノフィラメント。
[11]
1〜10の1項又は複数の項に記載のモノフィラメントを含む編織布であって、特に、織布、ループを延伸して編んだ布、ループを形成するように編んだ布、編組布又はノンクリンプ布である編織布。
[12]
1〜10の1項又は複数の項に記載のモノフィラメントの、抄紙機用クロスとしての、コンベヤーベルト及びろ過スクリーンにおける使用法。
[13]
抄紙機用クロスが、抄紙機の形成セクション及び/又は乾燥セクションに使用される、12に記載の方法。
マトリックスポリマーは、市販のポリエチレンテレフタレート:AD01(DuFor Resins B.V.社製、ゼーフェナール(Zevenaar)/オランダ)である。ポリシロキサン分散物を加えるために、2.5wt%の熱可塑性小球−MB 50−010(Dow Corning S.A.社製、セネフ(Seneffe)/ベルギー)を量り取り、次いで2.5wt%のRenol Weiss ATX 406(Clariant Masterbatches社製、ラーンシュタイン(Lahnstein)/ドイツ)を加えた。
DSM社から市販されているAkulon F 136−C1 ナイロンn−6を98.5wt%で使用した。これに1.5wt%の熱可塑性ポリシロキサン小球:Pellet S(Wacker Chemie社製)を加えた。
使用されたマトリックスポリマーが99.0wt%の市販ナイロン−6:Akulon F 136−C1(DSM社製)であった以外は実施例2を繰り返した。使用されたポリシロキサン小球は、1.0wt%のPMSQ E+580(Coating Products社製)あった。ポリシロキサン小球の平均直径は8μmであった。
使用されたマトリックスポリマーが99.0wt%の市販ポリエチレンテレフタレート:RT 52(Invista社製)であった以外は実施例2を繰り返した。使用されたシリコーン小球は、1.0wt%のPMSQ E+580(Coating Products社製)であった。
使用されたマトリックスポリマーが97.5wt%の市販ポリエチレンテレフタレート:RT 52(Invista社製)であった以外は実施例4を繰り返した。使用されたシリコーン小球は、2.5wt%のPMSQ:MB50−010(Dow Corning社製)であった。
使用されたマトリックスポリマーが99.0wt%の市販ポリエチレンテレフタレート:RT 52(Invista社製)であった以外は実施例4を繰り返した。使用されたシリコーン小球は、2.5wt%の熱可塑性シリコーン小球:Pellet S(Wacker Chemie社製)であった。
使用されたマトリックスポリマーが93.3wt%の市販ポリエチレンテレフタレート:RT 12(Invista社製)であった以外は実施例4を繰り返した。使用されたシリコーン小球は、1.0wt%のPMSQ E+580(Coating Products社製)であった。さらに、5.0wt%のPET中芳香族ポリカルボジイミドのマスターバッチ(Stabaxol(登録商標)KE 9428(Rheinchemie社製))及び0.7wt%の置換ジアリールカルボジイミド(Stabaxol(登録商標)I LF(Rheinchemie社製))を使用した。
使用されたマトリックスポリマーが100wt%の市販ナイロン−6:Akulon F 136−C1(DSM社製)であった以外は実施例2を繰り返した。熱可塑性シリコーン小球は添加されなかった。
使用されたマトリックスポリマーが100wt%の市販ポリエチレンテレフタレート:RT 52(Invista社製)であった以外は実施例4を繰り返した。熱可塑性シリコーン小球は添加されなかった。
使用されたマトリックスポリマーが94.3wt%の市販ポリエチレンテレフタレート:RT 12(Invista社製)であった以外は実施例7を繰り返した。熱可塑性シリコーン小球は添加されなかった。カルボジイミド安定剤の種類及び量は実施例7と一致していた。
Claims (9)
- 熱可塑性ポリマーのマトリックスと、その中に分散された直径10nm〜200μmのポリシロキサンの粒子とを含み、
熱可塑性ポリマーが、ナイロン−6、ナイロン−6,6、ナイロン−6,10、ナイロン−12、ナイロン−6,12、ポリフェニレンスルフィド、ポリエーテルケトン又はこれらの二つ以上の組合せであり、
ポリシロキサンが、架橋ポリジメチルシロキサンであるか又はポリメチルシルセスキオキサンである、
モノフィラメント。 - ポリシロキサンの粒子が球形で、直径0.2〜50μmである、請求項1に記載のモノフィラメント。
- 粒子が0.01〜8wt%存在する、請求項1及び2のいずれかに記載のモノフィラメント。
- カルボジイミド安定剤、好ましくは高分子カルボジイミド安定剤をさらに含む、請求項1〜3のいずれかに記載のモノフィラメント。
- 熱可塑性ポリマーの割合が60〜95wt%、ポリシロキサンの割合が0.02〜8wt%、そしてカルボジイミドの割合が0〜10wt%であり、ここで量的詳細はモノフィラメントの全量に基づく、請求項1〜4のいずれかに記載のモノフィラメント。
- 0.001〜10wt%の慣用添加剤、特に、酸化剤、UV安定剤、充填剤、顔料、殺生物剤、導電率向上剤、耐摩耗性増強剤、減摩添加剤、スピン仕上げ剤、加工助剤、可塑剤、滑沢剤、艶消剤、粘度調整剤、結晶化促進剤又はこれらの二つ以上の組合せをさらに含む、請求項1〜5の1項又は複数の項に記載のモノフィラメント。
- 請求項1〜6の1項又は複数の項に記載のモノフィラメントを含む編織布であって、特に、織布、ループを延伸して編んだ布、ループを形成するように編んだ布、編組布又はノンクリンプ布である編織布。
- 請求項1〜6の1項又は複数の項に記載のモノフィラメントの、抄紙機用クロスとしての、コンベヤーベルト及びろ過スクリーンにおける使用法。
- 抄紙機用クロスが、抄紙機の形成セクション及び/又は乾燥セクションに使用される、請求項8に記載の方法。