JP6685108B2 - 耐火性物品およびその製造方法 - Google Patents
耐火性物品およびその製造方法 Download PDFInfo
- Publication number
- JP6685108B2 JP6685108B2 JP2015219390A JP2015219390A JP6685108B2 JP 6685108 B2 JP6685108 B2 JP 6685108B2 JP 2015219390 A JP2015219390 A JP 2015219390A JP 2015219390 A JP2015219390 A JP 2015219390A JP 6685108 B2 JP6685108 B2 JP 6685108B2
- Authority
- JP
- Japan
- Prior art keywords
- polyisocyanurate
- refractory
- polyisocyanate
- weight
- core material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
また、自由な断面形状(例えば、円形の断面)を有している耐火性物品を得るための、簡便な製造方法を提供することである。
(1)芯材、および
(2)ポリイソシアヌレート樹脂からなる耐火層
を有する耐火性物品を提供する。
(i)芯材と枠の間に空間をとるように芯材の外側周囲に枠を配置する工程、
(ii)芯材と枠の間の空間にポリイソシアヌレート原料液を流し込む工程、および
(iii)ポリイソシアヌレート原料液を反応させて固体のポリイソシアヌレート樹脂の層を得る工程
を有する、耐火性物品を製造する方法をも提供する。
<1>
(1)芯材、および
(2)ポリイソシアヌレート樹脂からなる耐火層
を有する耐火性物品であって、
前記ポリイソシアヌレート樹脂がポリイソシアネートと活性水素含有化合物を含有する原料から製造され、活性水素含有化合物は、水酸基価120〜2000mgKOH/g、官能度2〜4、分子量50〜2000、2つ以上の水酸基を有するポリオールであり、活性水素含有化合物の量は、ポリイソシアネート100重量部に対し、5〜30重量部である耐火性物品。
<2>
前記ポリイソシアヌレート樹脂が、さらに難燃性付与剤を含有する、<1>に記載の耐火性物品。
<3>
前記ポリイソシアヌレート樹脂が、イソシアヌレート化触媒の存在下で製造される、<1>または<2>に記載の耐火性物品。
<4>
前記難燃性付与剤が、水酸化アルミニウムおよび赤燐を含有し、ポリイソシアヌレート樹脂の原料ポリイソシアネート100重量部に対し、水酸化アルミニウムの量が10〜20重量部であり、赤燐の量が5〜10重量部であり、水酸化アルミニウムと赤燐の重量比が1〜4:1である<1>〜<3>のいずれかに記載の耐火性物品。
<5>
芯材(1)が集成材である<1>〜<4>のいずれかに記載の耐火性物品。
<6>
ポリイソシアネートが、芳香族ポリイソシアネート、脂肪族ポリイソシアネート、脂環式ポリイソシアネート、およびこれらの変性物からなる群から選択された少なくとも1種である<1>〜<5>のいずれかに記載の耐火性物品。
<7>
ポリイソシアヌレート樹脂からなる耐火層(2)の外側に、(3)表面層
を有する<1>〜<6>のいずれかに記載の耐火性物品。
<8>
物品が柱、梁、壁、床、桁、筋かいおよび土台からなる群から選択された構造部材である
<1>〜<7>のいずれかに記載の耐火性物品。
<9>
(i)芯材と枠の間に空間をとるように芯材の外側周囲に枠を配置する工程、
(ii)芯材と枠の間の空間にポリイソシアヌレート原料液を流し込む工程、および
(iii)ポリイソシアヌレート原料液を反応させて固体のポリイソシアヌレート樹脂の層
を得る工程
を有する、<1>〜<8>のいずれかに記載の耐火性物品を製造する方法。
また、自由な断面形状(例えば、円形の断面)を有している耐火性物品も、簡単な工程で容易に製造できる。
本発明の耐火性物品は、優れた耐火性、耐熱性、防火性、断熱性を有する。耐火層に使用しているポリイソシアヌレート樹脂の比重(約1.2)は、石膏やモルタルの比重に比較して小さいので、本発明の耐火性物品は、軽量である。
図1および図2は、耐火性物品が正方形の断面を有する態様を表しているが、耐火性物品の断面は、正方形以外の形状であってよい。他の断面形状として、例えば、長方形(例えば、板状)、四角形以外の多角形、円形、楕円形が挙げられる。
本発明において、ポリイソシアネートの一部分は、イソシアネート反応性活性水素を有する化合物と反応する(ウレタン反応)。ウレタン化とイソシアヌレート化は、前後して(別個に)行ってよく、あるいは同時に行ってよい。イソシアヌレート化するイソシアネート基とウレタン化するイソシアネート基のモル比は、1.0:0.018〜0.59、好ましくは 1.0:0.02〜0.50 であってよい。
脂環式ポリイソシアネートとしては、炭素数4〜16の脂環式ジイソシアネートなどが挙げられる。具体例としては、イソホロンジイソシアネート(IPDI)、4,4’−ジシクロヘキシルメタンジイソシアネート、ノルボルナンジイソシアネートなどが挙げられる。
また炭化水素の水素原子を水酸基またはアミノ基によって置換した化合物、あるいはこの置換化合物にポリオキシアルキレン基が付加している化合物、すなわちポリエーテルポリオールであってもよい。オキシアルキレンの炭素数は2〜5であることが好ましく、プロピレンオキシドやエチレンオキシドなどがあげられる。
本発明においては、ポリオールの特性がこの範囲内であると、耐火性物品の耐火性(難燃性)が満足される。
ポリオールの使用量は、ポリイソシアネート100重量部に対し、5〜30重量部、好ましくは6〜25重量部である。ポリオールの使用量が30重量部以下である場合に、生成される樹脂中のウレタン結合基率が低いので、耐熱性が高くなる。
添加剤は、ポリイソシアネートのイソシアネート基と反応してもよいが、イソシアネート基と反応しないことが好ましい。したがって、添加剤は、イソシアネート基と反応する活性水素を有しないことが好ましい。
本発明では、前述のポリオールとこれら難燃性付与剤を合わせて使用することにより難燃性をさらに向上できる。その際の難燃性付与剤の選択については、特に、水酸化アルミニウムと赤リンの組合せが効果的である。
本発明では、特に難燃性能向上に効果的な、水酸化アルミニウムと赤リンの組合せの詳細は以下の通りである。すなわち、難燃性付与剤が、水酸化アルミニウムおよび赤燐を含有し、ポリイソシアヌレート樹脂の原料ポリイソシアネート100重量部に対し、水酸化アルミニウムの量が10〜20重量部であり、赤燐の量が5〜10重量部であり、水酸化アルミニウムと赤燐の重量比が1〜4:1である場合に、難燃性付与剤がこの範囲内であれば、難燃性の向上が顕著である。
本発明に使用する赤燐に限定はなく、各種市販品を選択して使用することができる。
市販品とは例えば、燐化学工業社製のノーバレッド120、120UF、120UFA、ノーバエクセル140、140Fである。本発明に使用する水酸化アルミニウムに限定はなく、各種市販品を選択して使用することができる。市販品とは例えば、住友化学社製のC−12、C−31、C−F−1である。ただし難燃性付与剤の選択においては、ポリオールやポリイソシアネートと撹拌混合の必要性を考慮し、混合を阻害するような形状(例えば固形ペレット状)や粘度を上昇させるような形状(例えば繊維状)の難燃性付与剤は好ましくない。これらの選択は使用実態にあわせて適宜なされるべきである。難燃性付与剤の形状は、例えば、粉末、液体などであってよい。
添加剤の量は、ポリイソシアネート100重量部に対して0〜100重量部、例えば1〜50重量部であってよい。
本発明においてはポリオール化合物とポリイソシアネートが反応するが、その際のイソシアネートインデックス(NCO Index)は、170〜5600、特に200〜5000であることが好ましい。
(i)芯材と枠の間に空間をとるように芯材の外側周囲に枠を配置する工程、
(ii)芯材と枠の間の空間にポリイソシアヌレート原料液を流し込む工程、および
(iii)ポリイソシアヌレート原料液を反応させて固体のポリイソシアヌレート樹脂の層を得る工程
を有する製造方法によって製造できる。
工程(ii)において、ポリイソシアヌレート原料液は、ポリイソシアネートおよびイソシアヌレート化触媒を混合した液であり、芯材と枠の間の空間を埋める。ポリイソシアヌレート原料液は、イソシアネート反応性活性水素を有する化合物(例えば、ポリオールおよび必要によりモノオール)を含む。さらに、ポリイソシアヌレート原料液は、添加剤などを含んでよい。
工程(iii)において、イソシアヌレート化反応およびウレタン反応を生じさせる。工程(iii)における反応温度は、常温(20℃)、あるいは加温(30〜100℃)であってよい。反応に要する時間は、反応温度に依存するが、一般に5分〜24時間である。
耐火層の厚み(製造方法の工程における芯材と枠の距離)は、一つの耐火性物品においては、ほぼ一定とすることが好ましい。これは本発明においては、耐火性能は耐火層の厚みに比例するからであり、部分的に耐火層の厚みに違いがあると、耐火性能にも違いが生じてしまうため好ましくない。
あるいは、上記製造方法によって表面層を有しない物品を製造した後に、表面層を貼り合わせてもよい。
特に指定しない限り、温度は摂氏であり、百分率は重量%である。
イソシアネート1:ポリメリックMDI、(NCO含有率31.5% 粘度180mPa・s/25℃)住化コベストロウレタン(株)製
ポリオール1:住化コベストロウレタン(株)製のプロピレンオキシド付加タイプ、水酸基価500mgKOH/g、官能基数2、分子量220、粘度500mPa・s/25℃のポリエーテルポリオール
ポリオール2:三菱化学(株)製のエチレングルコール(水酸基価1810mgKOH/g、官能基数2、分子量62)
難燃性付与剤1:住友化学社製の水酸化アルミニウムC−31:
難燃性付与剤2:燐化学工業社製のノーバレッド120UFA(赤燐)
難燃性付与剤3:大八化学工業(株)製のTCPP トリス(β-クロロプロピル)ホスフェート(リン酸エステル)
難燃性付与剤4:クラリアント社製のエクソリットOP1230(有機リン酸金属塩)
難燃性付与剤5:日産化学社製のメラミンイソシアヌレートMC4000
触媒1: N,N',N''-トリス(3-ジメチルアミノプロピル)ヘキサヒドロ-s-トリアジン (イソシアヌレート化触媒)
ポリオール1を10重量部、触媒1を1重量部、およびイソシアネート1を100重量部で混合することによってポリイソシアヌレート原料液を調製した。ポリイソシアヌレート原料液を金型(200mmx200mmx厚さ50mm)に流し入れ、20℃で3時間反応させて、固形の非発泡ポリイソシアヌレート樹脂の板(200mmx200mmx厚さ15mm)を得た。これを常温下で1週間静置した後、加熱試験用の試料とした。
表面Bの温度観察の指標として、150℃を芯材に影響を与えないと考えられる上限温度として設定した。試料の表面Bが150℃に達するのに要する時間は、32分であった。結果を表1に示す。また加熱試験中、試料が大きく変形することはなく、ほぼ初期の形状を保っていた。
表1の原料配合に従い各試料を用意し、参考例1と同様な方法で加熱試験を行った。そ
の結果を表1に示す。
表2の原料配合に従い、樹脂組成の試料を用意した。参考例1と同様な方法で加熱試験を行った。その結果を表2に示す。
参考例1〜10、実施例11〜15に比較して、かなりの短時間で試料の表面Bが150℃に達した。
表2の原料配合に従い試料を用意した。参考例1と同様な方法で加熱試験を行ったが、試料の変形が大きく、評価ができなかった。その結果を表2に示す。
芯材に、150mmx150mmx1000mmの集成角材を準備し、その長さ方向の外側に幅25mmの隙間を取るよう離型剤を塗布した木製の外枠を設け、垂直方向に設置した。その隙間に実施例13で使用するポリイソシアヌレート原料液を流し込み、20℃の室温下で3時間静置して反応を完了させた。その後、外枠を外すと、集成角材がポリイソシアヌレート樹脂で被覆された柱状物を得ることができた。ポリイソシアヌレート樹脂と集成材はしっかりと接着しており、接着剤等を使用する必要性はなかった。
このポリイソシアヌレート樹脂で被覆された柱状物は、(糸)鋸で切断を試みると、切り口に亀裂を生じることなく、容易に切断することができた。
参考例1〜3(ポリオール使用)では、比較例1〜3との比較から、これら特定のポリオール成分とその配合量が耐火性(難燃性)向上に有効であることが分かる。
参考例4〜10(ポリオールと難燃化付与剤(単独)の使用)では、参考例1〜3に比較しさらに耐火性(難燃性)が向上されていることが分かる。
実施例11〜15(ポリオールと難燃化付与剤(複数併用)の使用)では、難燃性付与剤が、水酸化アルミニウムおよび赤燐の成分を含有し、ポリイソシアネート100重量部に対し、水酸化アルミニウムの量が10〜20重量部、赤燐の量が5〜10重量部であり、水酸化アルミニウムと赤燐の重量比が水酸化アルミニウム:赤燐=1〜4:1である場合に、非常に優れた耐火性(難燃性)を示すことが分かる。
芯材に必要強度を有する材料を選択すれば、構造部材として使用できる。構造部材の例は、建物の構造部材、例えば、柱、梁、壁、床、桁、筋かい、土台である。
11,21 芯材
12,22 耐火層
13,23 表面層
Claims (8)
- (1)芯材、および
(2)非発泡性材料であるポリイソシアヌレート樹脂からなる耐火層
を有する耐火性物品であって、
前記ポリイソシアヌレート樹脂がポリイソシアネートと活性水素含有化合物を含有する原料から製造され、活性水素含有化合物は、水酸基価120〜2000mgKOH/g、官能度2〜4、分子量50〜2000、2つ以上の水酸基を有するポリオールであり、活性水素含有化合物の量は、ポリイソシアネート100重量部に対し、5〜30重量部であり、 前記ポリイソシアヌレート樹脂が、さらに難燃性付与剤を含有し、
前記難燃性付与剤が、水酸化アルミニウムおよび赤燐を含有し、ポリイソシアヌレート樹脂の原料ポリイソシアネート100重量部に対し、水酸化アルミニウムの量が10〜20重量部であり、赤燐の量が5〜10重量部であり、水酸化アルミニウムと赤燐の重量比が1〜4:1である、耐火性物品。 - 前記ポリイソシアヌレート樹脂が、イソシアヌレート化触媒の存在下で製造されたものである、請求項1に記載の耐火性物品。
- 前記ポリイソシアヌレート樹脂が、ポリイソシアヌレート原料液を反応させることにより得られたものであり、前記ポリイソシアヌレート原料液が、前記ポリイソシアネート、前記イソシアヌレート化触媒、前記活性水素含有化合物、および、前記難燃性付与剤を含み、任意で、可塑剤、無機充填材、強化材、界面活性剤、有機顔料、無機顔料、着色剤、UV安定剤、熱安定剤、および、制カビもしくは制菌効果をもつ物質からなる群から選択される添加剤を含む、請求項1または2に記載の耐火性物品。
- 芯材(1)が集成材である請求項1〜3のいずれかに記載の耐火性物品。
- ポリイソシアネートが、芳香族ポリイソシアネート、脂肪族ポリイソシアネート、脂環式ポリイソシアネート、およびこれらの変性物からなる群から選択された少なくとも1種である請求項1〜4のいずれかに記載の耐火性物品。
- ポリイソシアヌレート樹脂からなる耐火層(2)の外側に、(3)表面層
を有する請求項1〜5のいずれかに記載の耐火性物品。 - 物品が柱、梁、壁、床、桁、筋かいおよび土台からなる群から選択された構造部材である請求項1〜6のいずれかに記載の耐火性物品。
- (i)芯材と枠の間に空間をとるように芯材の外側周囲に枠を配置する工程、
(ii)芯材と枠の間の空間にポリイソシアヌレート原料液を流し込む工程、および
(iii)ポリイソシアヌレート原料液を反応させて固体のポリイソシアヌレート樹脂の層を得る工程
を有する、請求項1〜7のいずれかに記載の耐火性物品を製造する方法。