JP6652325B2 - 再剥離性圧着記録用紙の感圧接着剤層用の水性インクジェット用インク組成物 - Google Patents
再剥離性圧着記録用紙の感圧接着剤層用の水性インクジェット用インク組成物 Download PDFInfo
- Publication number
- JP6652325B2 JP6652325B2 JP2015059979A JP2015059979A JP6652325B2 JP 6652325 B2 JP6652325 B2 JP 6652325B2 JP 2015059979 A JP2015059979 A JP 2015059979A JP 2015059979 A JP2015059979 A JP 2015059979A JP 6652325 B2 JP6652325 B2 JP 6652325B2
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- anionic group
- mass
- ink composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
以下、本発明の基紙及び感圧接着剤層を有する再剥離性圧着記録用紙の感圧接着剤層用の水性インクジェット用インク組成物に含まれる各成分について説明する。
本発明のアニオン性基含有樹脂被覆顔料は、アニオン性基含有樹脂に被覆された顔料である。
本発明の顔料としては、特に限定されるものではないが、一般にインクジェット記録液で使用される各種の無機顔料や有機顔料を挙げることができる。無機顔料としては、例えば、カーボンブラック、チタンブラック、チタンホワイト、硫化亜鉛、ベンガラなどが挙げられ、有機顔料としては、例えば、キナクリドン系顔料、ジオキサジン系顔料、フタロシアニン系顔料、アントラピリミジン系顔料、アンサンスロン系顔料、インダンスロン系顔料、フラバンスロン系顔料、ペリレン系顔料、ジケトピロロピロール系顔料、ペリノン系顔料、キノフタロン系顔料、アントラキノン系顔料、チオインジゴ系顔料、ベンツイミダゾロン系顔料、イソインドリノン系顔料、アゾメチン系顔料、アゾ系顔料などを挙げることができる。顔料は、少なくとも1種を用いればよく、2種以上を組み合わせて用いることができる。
本発明のアニオン性基含有樹脂としては、通常のインキや塗料の顔料分散用やバインダーとして利用できるアニオン性基含有樹脂であって、塩基性化合物の存在下で水性媒体中に溶解できるものであれば特に制限はないが、カルボキシル基、スルホン酸基、ホスホノ基(−P(=O)(OH2))などのアニオン性基の1種又は2種以上を含有する樹脂が好ましい。
Woodの式:1/Tg=W1/Tg1+W2/Tg2+W3/Tg3+・・・・・+Wx/Tgx
[式中、Tg1〜Tgxはアニオン性基含有樹脂を構成する単量体1、2、3・・・xのそれぞれの単独重合体のガラス転移温度、W1〜Wxは単量体1、2、3・・・xのそれぞれの重合分率、Tgは理論ガラス転移温度を表す。ただし、woodの式におけるガラス転移温度は絶対温度である。]
前記アニオン性基含有樹脂のガラス転移温度は、アニオン性基含有樹脂がアクリル系共重合体樹脂以外の場合、熱分析により求めた理論ガラス転移温度である。熱分析の方法としては、JIS K7121(プラスチックの転移温度測定方法)に準じ、一例として、パーキンエルマー社製Pyris1 DSCを用いて、昇温速度20℃/分、窒素ガス流速20ミリリットル/分の条件下でガラス転移温度を測定する事ができる。
本発明のアニオン性基含有樹脂被覆顔料は、前記アニオン性基含有樹脂を塩基性化合物存在下に水性媒体中に溶解後、前記顔料を加え、ミル型分散機、高圧分散機などの分散機で顔料分散物(インクベース前駆体ともいう)を得、これを必要に応じて希釈し、酸析法やイオン交換手段などにより、塩基性化合物を除去して得られるものである。
前記塩基性化合物としては、水酸化ナトリウム、水酸化カリウムのような無機塩基性化合物や、アンモニア、メチルアミン、エチルアミン、モノエタノールアミン、N、N−ジメチルエタノールアミン、N、N−ジエチルエタノールアミン、N、N−ジブチルエタノールアミン、ジエタノールアミン、N−メチルジエタノールアミン、トリエタノールアミン、モルホリン、N−メチルモルホリン、N−エチルモルホリンのような有機塩基性化合物などが挙げられる。これら塩基性化合物は、単独または2種以上を混合して用いることができる。中でも、顔料分散の点からモノエタノールアミン、N、N−ジメチルエタノールアミン、N、N−ジエチルエタノールアミン、N、N−ジブチルエタノールアミン、ジエタノールアミン、N−メチルジエタノールアミン、トリエタノールアミンなどのアルカノールアミンが好適である。
前記水性媒体としては、水、又は水と水混和性有機溶剤との混合物が使用できる。水混和性有機溶剤としては、例えば、メチルアルコール、エチルアルコール、イソプロピルアルコール、n−プロピルアルコールなどの低級アルコール類、エチレングリコール、プロピレングリコール、ジエチレングリコール、ジプロピレングリコール、グリセリンなどの多価アルコール類、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテルなどの(ポリ)アルキレングリコールのモノアルキルエーテル類、エチレングリコールモノアセテート、プロピレングリコールモノアセテートなどの(ポリ)アルキレングリコールのモノ脂肪酸エステル類などが挙げられる。水混和性有機溶剤は単独または2種以上を混合して使用できる。
前記酸析法としては、塩酸や酢酸などの酸性化合物を前記顔料分散物に加え、pHを中性又は酸性とすることによって、塩基性化合物を除去し、アニオン性基含有樹脂を顔料表面に析出(被覆)させる方法が挙げられる。
前記イオン交換手段としては、イオン交換体を前記顔料分散物に直接加える方法、又はイオン交換体を充填したイオン交換塔に前記顔料分散物を通過させる方法によって、塩基性化合物のカチオンと水素とのイオン交換を行い、これにより顔料表面にアニオン性基含有樹脂を析出(被覆)させる方法が挙げられる。
前記含水ケーキの状態又は乾燥された状態のアニオン性基含有樹脂被覆顔料は、塩基性化合物存在下で水性媒体中に溶解後、再分散させて、アニオン性基含有樹脂被覆顔料の分散液として、本発明の水性インクジェット用インク組成物の製造に使用できる。
本発明のエマルジョンは、水系エマルジョンである。水系エマルジョンの例としては、アクリル系樹脂エマルジョン、スチレン−アクリル系樹脂エマルジョン、ポリエステル系樹脂エマルジョン、ポリウレタン系樹脂エマルジョン、ポリ酢酸ビニル系樹脂エマルジョン、ポリ塩化ビニル系樹脂エマルジョン、ポリブタジエン系樹脂エマルジョン、ポリエチレン系樹脂エマルジョン等が挙げられる。中でも、得られる印刷物の外観及び耐水性、耐溶剤性、耐擦性、耐熱性などの各種耐性に優れる事から、スチレン−アクリル系樹脂エマルジョンが好ましい。エマルジョンは、少なくとも1種を用いればよく、2種以上を組み合わせて用いることができる。
Woodの式:1/Tg=W1/Tg1+W2/Tg2+W3/Tg3+・・・・・+Wx/Tgx
[式中、Tg1〜Tgxはアニオン性基含有樹脂を構成する単量体1、2、3・・・xのそれぞれの単独重合体のガラス転移温度、W1〜Wxは単量体1、2、3・・・xのそれぞれの重合分率、Tgは理論ガラス転移温度を表す。ただし、woodの式におけるガラス転移温度は絶対温度である。]
エマルジョンの樹脂のガラス転移温度は、アクリル系以外の樹脂については、熱分析により求めた理論ガラス転移温度である。熱分析の方法としては、JIS K7121(プラスチックの転移温度測定方法)に準じ、一例として、パーキンエルマー社製Pyris1 DSCを用いて、昇温速度20℃/分、窒素ガス流速20ミリリットル/分の条件下でガラス転移温度を測定する事ができる。
本発明の水溶性溶剤は、本発明の水性インクジェット用インク組成物の保存安定性、インクの吐出安定性、インクの飛翔性を付与できる効果を有し、例えば、モノアルコール類、多価アルコール類、多価アルコールの低級アルキルエーテル類、窒素含有化合物類等を挙げることができる。これらは単独で用いてもよく、2種以上を併用してもよい。
本発明の水は、前記アニオン性基含有樹脂被覆顔料の分散液中に含有する水性媒体としての水、前記エマルジョンに含有する水、及び本発明の水性インクジェット用インク組成物の濃度調製のために加える水、を含むものである。
本発明の水性インクジェット用インク組成物には、さらに、目的に応じて公知の顔料分散剤、防黴剤、防錆剤、増粘剤、酸化防止剤、紫外線吸収剤、保存性向上剤、消泡剤、pH調整剤等の添加剤も添加することもできる。
本発明の水性インクジェット用インク組成物は、前記アニオン性基含有樹脂被覆顔料の分散液に、前記エマルジョン、前記水溶性溶剤、及び前記水を加えて、製造することができる。本発明の水性インクジェット用インク組成物は、製造後の初期粘度が25℃において1〜15mPa・s、好ましくは3〜10mPa・sの範囲である。粘度は、例えば、E型粘度計(商品名:RE100L型粘度計、東機産業社製)により測定できる。
本発明の水性インクジェット用インク組成物を用いた印刷方法について説明する。
<顔料>
カーボンブラック(商品名プリンテックス90、デグサ社製)
イエロー顔料(商品名ノバパームイエロー4G01、クラリアント社製)
マゼンタ顔料(商品名インクジェットマゼンタE5B02、クラリアント社製)
シアン顔料(商品名ヘリオゲンブルーL7101F、BASF社製)
<アニオン性基含有樹脂>
アクリル酸/n−ブチルアクリレート/ベンジルメタクリレート/スチレン共重合体(重量平均分子量30,000、酸価185mgKOH/g)
<エマルジョン>
ネオクリルA−1092(固形分45%、ガラス転移温度9℃、スチレン−アクリル系エマルジョン、DSM Neoresins社製)
ネオクリルA−1120(固形分45%、ガラス転移温度−9℃、スチレン−アクリル系エマルジョン、DSM Neoresins社製)
ネオクリルA−1091(固形分45%、ガラス転移温度98℃、スチレン−アクリル系エマルジョン、DSM Neoresins社製)
モビニール461(固形分64%、ガラス転移温度−40℃、アクリル系エマルジョン、日本合成化学社製)
<水溶性溶剤>
グリセリン
プロピレングリコール
エチレングリコールモノブチルエーテル
<アニオン性基含有樹脂被覆顔料の製造>
アニオン性基含有樹脂(アクリル酸/n−ブチルアクリレート/ベンジルメタクリレート/スチレン共重合体)20質量部を、塩基性化合物(水酸化カリウム)2.5質量部と水性媒体(水)77.5質量部との混合溶液に溶解させて、アニオン性基含有樹脂固形分が20%の樹脂分散剤ワニスを得た。
次いで、前記樹脂分散剤ワニスの23.7質量部(アニオン性基含有樹脂4.74質量部含む)に水性媒体(水)64.3質量部を加えて混合し、アニオン性基含有樹脂固形分が4.74%の顔料分散用樹脂ワニスを得た。さらに、これに顔料(カーボンブラック)12質量部を加え、攪拌混合後、湿式サーキュレーションミルで練肉を行い、アニオン性基含有樹脂被覆顔料分散物(インクベース前駆体)を調製した。
さらに、前記アニオン性基含有樹脂被覆顔料分散物(インクベース前駆体)を、顔料濃度が5%となるように水で希釈した後、希釈液に対して陽イオン交換樹脂(DOWEX MONOSPHERE (H)650C、ダウケミカル社製)を5%添加し攪拌して、pHが4未満となるまでイオン交換後、イオン交換樹脂をメッシュで濾過して、吸引濾過し、アニオン性基含有樹脂被覆顔料(ブラック)を含有する含水ケーキ(アニオン性基含有樹脂被覆顔料固形分25%)を得た。
このアニオン性基含有樹脂被覆顔料を含有する含水ケーキ22.8質量部(アニオン性基含有樹脂1.6質量部、顔料4.1質量部、水性媒体(水)17.1質量部を含む)に、塩基性化合物(水酸化ナトリウム)0.2質量部(該樹脂被覆顔料に含まれるアニオン性基含有樹脂の酸価の80%の中和量)と、水性媒体(水)11質量部を加え、高圧乳化分散装置:ゴーリンホモジナイザー(A.P.V. GAULIN INK.製)で攪拌し、アニオン性基含有樹脂被覆顔料(ブラック)の分散液を得た。
表1に記載の通り、前記アニオン性基含有樹脂被覆顔料(ブラック)の分散液34.0質量部、エマルジョン(ネオクリルA−1092)3.3質量部、水溶性溶剤(グリセリン)40.0質量部、及び水22.7質量部を攪拌混合し、実施例1の再剥離性圧着記録用紙の感圧接着剤層用の水性インクジェット用インク組成物を得た。
表1に記載の顔料に変更した以外は、実施例1に記載の方法で、実施例2〜9、及び比較例1〜6のアニオン性基含有樹脂被覆顔料を得た。さらに、表1の質量割合となるように、所定のエマルジョン、所定の水溶性溶剤、及び水を攪拌混合し、実施例2〜9、及び比較例1〜6の再剥離性圧着記録用紙の感圧接着剤層用の水性インクジェット用インク組成物を得た。
以下の方法により評価し、それらの結果を表1に示す。
(1)印字の剥離耐性
実施例1〜9、比較例1〜6の水性インクジェット用インク組成物を、0.1mmワイヤーバーを用いて、Wメール(北越紀州製紙社製)に展色した。30分後、展色面と非展色面を重ね合わせ、圧力15MPaで圧着し、再剥離性情報シートを得た。その後、圧着面を剥離し、圧着後の非展色面のΔEと未圧着の非展色面のΔEを測定し、それらの差を算出することで、展色面から非展色面への色移りの程度を評価した。尚、測定機器及び測定条件は以下の通りである。
[測定機器]
SpectroEye(X−rite社製)
[測定条件]
白色基準:絶対白色
光源:D50
観測視野:2°
内臓フィルター:なし
[評価基準]
○:ΔEが0.5以下である
△:ΔEが0.5を超えて1以下である
×:ΔEが1を超える
市販のインクジェットプリンターPM−900C(セイコーエプソン(株)製)を用いて、実施例1〜9、比較例1〜6の水性インクジェット用インク組成物を普通紙に印刷した時の吐出安定性を評価した。吐出安定性は、該水性インクジェット用インク組成物を充填し、キャップをせずに、室温30℃、相対湿度50%の環境下で3日間放置し、印字が可能となる条件によりオリフィスからの吐出安定性を評価した。尚、インクジェットプリンター及び普通紙は以下のものを用いた。
インクジェットプリンター:PM−900C(セイコーエプソン(株)製)
普通紙:Xerox L(富士ゼロックスオフィスサプライ(株)製)
[評価基準]
○:吐出オリフィスのクリーニングなしで印字可能
△:印字可能となるまでに吐出オリフィスのクリーニング回数が1〜4回必要
×:印字可能となるまでに吐出オリフィスのクリーニング回数が5回以上必要
Claims (3)
- アニオン性基含有樹脂被覆顔料、エマルジョン、水溶性溶剤、及び水を含有する水性インクジェット用インク組成物であって、
塩基性化合物を含有し、
前記エマルジョンが、アクリル系樹脂エマルジョン及び/又はスチレン−アクリル系樹脂エマルジョンであり、
前記エマルジョンの樹脂のガラス転移温度が−30℃〜30℃であり、
前記水性インクジェット用インク組成物中の前記エマルジョンの樹脂固形分の割合が0.7〜7質量%であり、前記水溶性溶剤の割合が25〜55質量%である、基紙及び感圧接着剤層を有する再剥離性圧着記録用紙の感圧接着剤層用の水性インクジェット用インク組成物。 - 前記水溶性溶剤が、プロピレングリコール、グリセリン、ジエチレングリコール、エチレングリコールモノブチルエーテル、及びジエチレングリコールモノブチルエーテルからなる群より選ばれた少なくとも1種である請求項1に記載の基紙及び感圧接着剤層を有する再剥離性圧着記録用紙の感圧接着剤層用の水性インクジェット用インク組成物。
- 請求項1または2に記載の水性インクジェット用インク組成物を基紙及び感圧接着剤層を有する再剥離性圧着記録用紙の感圧接着剤層に印刷して得られる再剥離性圧着記録用紙印刷物。