JP6341636B2 - 積層体 - Google Patents
積層体 Download PDFInfo
- Publication number
- JP6341636B2 JP6341636B2 JP2013121204A JP2013121204A JP6341636B2 JP 6341636 B2 JP6341636 B2 JP 6341636B2 JP 2013121204 A JP2013121204 A JP 2013121204A JP 2013121204 A JP2013121204 A JP 2013121204A JP 6341636 B2 JP6341636 B2 JP 6341636B2
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- component
- synthetic
- resin
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
このような建材としては、天然骨材や人工骨材等の着色粒子と結合材を主成分とする成形物が挙げられる。しかし、このような材料を、建築物内外装表面の曲面に対して施工した場合、折り曲げることが容易ではなかったり、また、折り曲げることができたとしても、美観性を損なう不具合を生じたりする場合がある。
1.基材上に、装飾層が積層された積層体であって、
前記装飾層は、合成樹脂(A)、平均粒子径10μm以上1000μm以下の着色粒子(B)、及び平均繊維長0.1mm以上5mm以下の化学繊維(C)を含み(ただし、炭酸カルシウムを結合成分として含有するものを除く)、
前記化学繊維(C)が、半合成繊維及び合成繊維から選ばれる少なくとも1種を含み、
前記半合成繊維が、アセテート繊維、トリアセテート繊維、プロミックス繊維、前記合成繊維が、ビニロン繊維、ナイロン繊維、アラミド繊維、ビニリデン繊維、ポリ塩化ビニル繊維、ポリエステル繊維、アクリル繊維、ポリエチレン繊維、ポリプロピレン繊維、ポリクラール繊維から選ばれる1種または2種以上であり、
前記(A)成分100重量部に対し、前記(B)成分を100〜4000重量部、前記(C)成分を1〜100重量部を含み、
前記基材は、織布または不織布であり、厚み0.05〜1.5mmであることを特徴とする積層体。
2.前記化学繊維が、親水性であることを特徴とする1.に記載の積層体。
3.前記合成樹脂が、合成樹脂エマルションを含むことを特徴とする1.または2.に記載の積層体。
本発明の基材としては、特に限定されないが、例えば、紙、合成紙、不燃紙、樹脂シート、金属シート、組布、織布、不織布等が挙げられる。これらは、必要に応じて表面処理等が施されたものであってもよい。その厚みは、0.05mm以上(より好ましく0.1〜5mm)であることが好ましい。このような範囲内であれば、強度、伸縮性等の点で好適である。
本発明の装飾層は、上記基材上に形成され、積層体に意匠性を付与する層である。この装飾層は、着色粒子による模様を有するものである。
・上記(A)成分と(C)成分の屈折率差が小さいため、装飾層中で(C)成分は略透明な状態となるため意匠性を阻害しないと推察される。
・上記(A)成分と(C)成分の比重差が小さいため、(A)成分中に(C)成分が均一に分散されるため、効果的に可とう性及び強度を付与することができると推察される。
・有機繊維である(C)成分は、ステンレス鋼繊維やロックウール等の無機繊維と比較し伸び率(伸度)が大きいため、効果的に可とう性及び強度を付与することができると推察される。本発明では(C)成分の伸度は、好ましくは5%以上(より好ましくは7%以上)である。
本発明では、上記基材の上に装飾層が積層される限り、その製造方法は特に限定されないが、例えば、以下のような製造方法が挙げられる。
(ア)基材上に、(A)成分、(B)成分、及び(C)成分を含む装飾層用組成物を塗付して装飾層を形成する方法。
(イ)型枠に、(A)成分、(B)成分、及び(C)成分を含む装飾層用組成物を流し込んだ後、基材を積層させる方法。
(I)型枠に装飾層用組成物を流し込み、乾燥、脱型して装飾層を成型し、その後接着剤等で基材を積層する方法、
(II)型枠に装飾層用組成物を流し込み、該装飾層用組成物が乾燥する前に基材を積層し、乾燥、脱型する方法
等が挙げられる。
また、上記(I)(II)において装飾層用組成物を流し込む際には、上記(ア)と同様の塗付方法を採用することができる。
例えば、上記(ア)の方法で製造する場合、凹凸模様の形成や、装飾材料の散布は、装飾層用組成物が硬化する前に行えばよい。凹凸模様の形成は、こて、型押し、ローラー等を用いた方法を採用することができる。装飾材料の散布は、公知または市販の散布機等を用いることができる。また、上記(イ)の方法で製造する場合、型枠側が積層体表面となるため、凹凸模様の形成は型枠内側の形状を調整することで付与することができる。装飾材料を散布する場合、公知または市販の散布機等を用い型枠内の底面に装飾材料を散在させた後に、装飾層用組成物を流し込めばよい。
これらの塗装は、公知の塗装方法によれば良く、スプレー、コーター、ローラー、刷毛等の塗装器具を使用することができる。
また、接着剤には、施工性、仕上り性、接着強度、防火性等の各種性能を付与するために、粉体成分、中空粒子、多孔質粒子、繊維等を添加したり、必要に応じ、着色材料、体質顔料、分散剤、粘性調整剤、消泡剤、防黴剤、防腐剤、防藻剤等の通常使用される添加剤を適宜加えることができる。
表1に示す配合に従い、各原料を常法により混合・攪拌することによって装飾層用組成物1〜9を製造した。なお、原料としては以下のものを使用した。
・着色粒子1:着色珪砂(黒色、平均粒子径90μm)
・着色粒子2:着色珪砂(黒色、平均粒子径160μm)
・着色粒子3:着色珪砂(黒色、平均粒子径300μm)
・化学繊維1:ビニロン繊維(平均繊維長1mm、公定水分率5.0%、伸度12〜26%)
・化学繊維2:ポリエステル繊維(平均繊維長1mm、公定水分率0.4〜0.5%、伸度28〜45%)
・無機繊維1:ステンレス鋼繊維(平均繊維長1mm、公定水分量0%、伸度1〜2%)
基材(ガラス繊維含有不織布、厚み0.3mm)上に、装飾層用組成物1を、乾燥厚みが2mmとなるようにコーターで塗付し、60℃下で60分間乾燥し、積層体1を得た。得られた積層体は、美観性に優れていた。
(評価1)
得られた積層体1を90°折り曲げた後、表面の外観を目視で評価した。その結果を表2に示す。
なお、評価基準は、「異常なし」をA、「異常が認められた」ものをCとし、A>B>Cの3段階で評価した。
装飾層用組成物1を装飾層用組成物2〜9に代えた以外は、試験例1と同様の方法で、それぞれ積層体2〜9を作製した。積層体2〜9はいずれも美観性に優れるものであった。積層体9は無機繊維によりやや意匠性に劣るものであった。
得られた積層体につき、試験例1と同様の試験を行った。結果は表2に示す。
Claims (3)
- 基材上に、装飾層が積層された積層体であって、
前記装飾層は、合成樹脂(A)、平均粒子径10μm以上1000μm以下の着色粒子(B)、及び平均繊維長0.1mm以上5mm以下の化学繊維(C)を含み(ただし、炭酸カルシウムを結合成分として含有するものを除く)、
前記化学繊維(C)が、半合成繊維及び合成繊維から選ばれる少なくとも1種を含み、
前記半合成繊維が、アセテート繊維、トリアセテート繊維、プロミックス繊維、前記合成繊維が、ビニロン繊維、ナイロン繊維、アラミド繊維、ビニリデン繊維、ポリ塩化ビニル繊維、ポリエステル繊維、アクリル繊維、ポリエチレン繊維、ポリプロピレン繊維、ポリクラール繊維から選ばれる1種または2種以上であり、
前記(A)成分100重量部に対し、前記(B)成分を100〜4000重量部、前記(C)成分を1〜100重量部を含み、
前記基材は、織布または不織布であり、厚み0.05〜1.5mmであることを特徴とする積層体。 - 前記化学繊維が、親水性であることを特徴とする請求項1に記載の積層体。
- 前記合成樹脂が、合成樹脂エマルションを含むことを特徴とする請求項1または請求項2に記載の積層体。