JP6339861B2 - 中綿、ならびに該中綿を含有する布団および衣類 - Google Patents
中綿、ならびに該中綿を含有する布団および衣類 Download PDFInfo
- Publication number
- JP6339861B2 JP6339861B2 JP2014110855A JP2014110855A JP6339861B2 JP 6339861 B2 JP6339861 B2 JP 6339861B2 JP 2014110855 A JP2014110855 A JP 2014110855A JP 2014110855 A JP2014110855 A JP 2014110855A JP 6339861 B2 JP6339861 B2 JP 6339861B2
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- ratio
- batting
- treatment
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)羽毛および架橋アクリレート系繊維を含有する中綿であって、中綿に含まれるねじれ綿の割合が5重量%以下であり、かつ、中綿1gあたりに含まれるねじれ綿の個数が8個以下であること、及び架橋アクリレート系繊維のけん縮率/けん縮数の比が0.60%・インチ/個以下であることを特徴とする中綿。
(2)架橋アクリレート系繊維が塩型カルボキシル基を4.5〜8mmol/g含有するものであることを特徴とする(1)に記載の中綿。
(3)架橋アクリレート系繊維が、トウ状態のアクリロニトリル系繊維に対して、1分子中に2個以上の窒素原子を有する窒素含有化合物による架橋処理と加水分解処理を施すことによって得られたものであることを特徴とする(1)または(2)に記載の中綿。
(4)(1)〜(3)のいずれかに記載の中綿を含有することを特徴とする寝具。
(5)(1)〜(3)のいずれかに記載の中綿を含有することを特徴とする衣類。
JIS−L1015に従って測定し、求める。求められたけん縮率[%]およびけん縮数[個/インチ]からけん縮率/けん縮数の比を算出する。
繊維試料約1gを、50mlの1mol/l塩酸水溶液に30分間浸漬する。次いで、繊維試料を、浴比1:500で水に浸漬する。15分後、浴pHが4以上であることを確認したら、乾燥させる(浴pHが4未満の場合は、再度水洗する)。次に、十分乾燥させた繊維試料約0.2gを精秤し(W1[g])、100mlの水を加え、さらに、15mlの0.1mol/l水酸化ナトリウム水溶液、0.4gの塩化ナトリウムおよびフェノールフタレインを添加して撹拌する。15分後、濾過によって試料繊維と濾液に分離し、引き続き試料繊維を、フェノールフタレインの呈色がなくなるまで水洗する。このときの水洗水と濾液をあわせたものを、フェノールフタレインの呈色がなくなるまで0.1mol/l塩酸水溶液で滴定し、塩酸水溶液消費量(V1[ml])を求める。得られた測定値から、次式によって全カルボキシル基量を算出する。
カルボキシル基量[mmol/g]=(0.1×15−0.1×V1)/W1
繊維試料約2.5gを、熱風乾燥器で105℃、16時間乾燥して重量を測定する(W2[g])。次に、該繊維試料を、温度20℃、65%RHに調節した恒温恒湿器に24時間入れる。このようにして吸湿した繊維試料の重量を測定する(W3[g])。これらの測定結果から、次式によって20℃×65%RH吸湿率を算出する。
20℃×65%RH吸湿率[%]=(W3−W2)/W2×100
試料中綿から測定用サンプルを約5gを採取し、重量(W4[g])を測定する。採取した中綿を目視で観察し、繊維試料が絡んで塊となっている部分、すなわち分散不良部分を取り分ける。また、取り分けた繊維試料の個数(N1[個])と重量(W5[g])を測定し、次式によって分散不良部分の1gあたりの個数と重量割合を算出する。
分散不良部分の1gあたりの個数[個/g]=N1/W4
分散不良部分の重量割合[%]=W5/W4×100
上記の手順を3回繰り返し、分散不要部分の個数と重量の平均値を求め、中綿の分散性を評価する。
また、手に触れたときの異物感を以下の基準に従って評価した。
○:異物感がない
△:異物感がほとんどない
×:異物感が明らかにある
アクリロニトリル90重量%、アクリル酸メチルエステル10重量%のアクリロニトリル系重合体Ap(30℃ジメチルホルムアミド中での極限粘度[η]=1.5)を48%のロダンソーダ水溶液で溶解して、紡糸原液を調製した。該紡糸原液を用いて、常法に従って紡糸を行い、切断することなく、トウ状態で、単繊維繊度0.9dtexのアクリロニトリル系繊維を得た。なお、紡糸におけるけん縮付与工程の条件を調整することによって、アクリロニトリル系繊維のけん縮率/けん縮数の比を0.71%・インチ/個とした。
製造例1で得られたトウ状態のアクリロニトリル系繊維に、水加ヒドラジンの20%水溶液中で、98℃×5時間架橋導入処理を行い、洗浄した。架橋導入された繊維を、3%硝酸水溶液中に浸漬し、90℃×2時間酸処理を行った。続いて3%水酸化ナトリウム水溶液中で90℃×2時間の加水分解処理を行い、3.5%硝酸水溶液で処理し、水洗した。得られた繊維を水に浸漬し、水酸化ナトリウムを添加してpH11に調整した後、繊維に含まれるカルボキシル基量の2倍に相当する硝酸マグネシウムを溶解させた水溶液に50℃×1時間浸漬することによりイオン交換処理を実施し、脱水した。次いで、短繊維状に切断し乾燥することにより、Mg塩型カルボキシル基を有する製造例2の繊維を得た。得られた繊維の評価結果を表1に示す。
アクリロニトリル90重量%、アクリル酸メチルエステル10重量%のアクリロニトリル系重合体Ap(30℃ジメチルホルムアミド中での極限粘度[η]=1.5)を48%のロダンソーダ水溶液で溶解して、紡糸原液を調製した。該紡糸原液を用いて、常法に従って紡糸を行い、切断することなく、トウ状態で、単繊維繊度0.9dtexのアクリロニトリル系繊維を得た。なお、紡糸におけるけん縮付与工程の条件を調整することによって、アクリロニトリル系繊維のけん縮率/けん縮数の比を0.62%・インチ/個とした。
アクリロニトリル90重量%、アクリル酸メチルエステル10重量%のアクリロニトリル系重合体Ap(30℃ジメチルホルムアミド中での極限粘度[η]=1.5)を48%のロダンソーダ水溶液で溶解して、紡糸原液を調製した。該紡糸原液を用いて、常法に従って紡糸を行い、短繊維状に切断し、単繊維繊度0.9dtex、けん縮率/けん縮数の比が0.91%・インチ/個のアクリロニトリル系繊維を得た。
比較例1の繊維を水に浸漬し、水酸化ナトリウムを添加してpH11に調整した後、繊維に含まれるカルボキシル基量の2倍に相当する硝酸マグネシウムを溶解させた水溶液に50℃×1時間浸漬することによりイオン交換処理を実施し、脱水し、乾燥することにより、Mg塩型カルボキシル基を有する製造例5の繊維を得た。得られた繊維の評価結果を表1に示す。
洗浄した羽毛(ホワイトダックダウン85%、フェザー15%)4部と水400部からなる水分散液を準備する。該水分散液を撹拌しつつ、ここに繊維長6mmに切断した各製造例の繊維1部と水100部からなる水分散液を添加する。添加後10分撹拌した後、脱水、乾燥を行い、羽毛と各製造例の繊維からなる中綿を得る。得られた中綿の評価結果を表2に示す。
Claims (5)
- 羽毛および架橋アクリレート系繊維を含有する中綿であって、中綿に含まれるねじれ綿の割合が5重量%以下であり、かつ、中綿1gあたりに含まれるねじれ綿の個数が8個以下であること、及び架橋アクリレート系繊維のけん縮率/けん縮数の比が0.60%・インチ/個以下であることを特徴とする中綿。
- 架橋アクリレート系繊維が塩型カルボキシル基を4.5〜8mmol/g含有するものであることを特徴とする請求項1に記載の中綿。
- 架橋アクリレート系繊維が、トウ状態のアクリロニトリル系繊維に対して、1分子中に2個以上の窒素原子を有する窒素含有化合物による架橋処理と加水分解処理を施すことによって得られたものであることを特徴とする請求項1または2に記載の中綿。
- 請求項1〜3のいずれかに記載の中綿を含有することを特徴とする寝具。
- 請求項1〜3のいずれかに記載の中綿を含有することを特徴とする衣類。