JP6301571B1 - 研摩液及び研摩物の製造方法 - Google Patents
研摩液及び研摩物の製造方法 Download PDFInfo
- Publication number
- JP6301571B1 JP6301571B1 JP2017553430A JP2017553430A JP6301571B1 JP 6301571 B1 JP6301571 B1 JP 6301571B1 JP 2017553430 A JP2017553430 A JP 2017553430A JP 2017553430 A JP2017553430 A JP 2017553430A JP 6301571 B1 JP6301571 B1 JP 6301571B1
- Authority
- JP
- Japan
- Prior art keywords
- polishing
- polishing liquid
- acid
- weak acid
- permanganate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
例えば特許文献1には、約0.1〜5重量パーセントの範囲の濃度で存在する粒子状シリカ研磨剤と約2〜7の範囲のpHを提供する酸性緩衝剤とを含有する水性CMP組成物が記載されている。特許文献1には、砥粒と酸性緩衝液からなる水性CMP組成物により二酸化ケイ素に対する炭化ケイ素の研摩速度の比(選択比)を高くすることができるとされている。
また特許文献2の方法では、設備や研摩液の管理の手間及びコストが大きいことが課題となっている。
本発明の課題は、前述した従来技術が有する種々の欠点を解消し得る研摩液及びそれを用いた研摩物の製造方法を提供することにある。
研摩液が過マンガン酸イオンに加えて弱酸及びその可溶性塩を含有していると研摩液中では以下の解離反応が起こる。なお、これらの式中、HAは弱酸、H+は水素イオン、A―は弱酸の陰イオン、BAは弱酸の可溶性塩、B+は可溶性塩のカチオンを表す。
一方、本実施形態の研摩液では、弱酸及びその可溶性塩を含まない場合に比べて、例えば、仮に初期pHが6以下である場合は、時間経過に対するpH7〜8までのpH上昇の傾きが緩やかであり、且つ研摩時間が更に経過する場合も、その傾きの変化が起こりにくい。従って、本実施形態の研摩液では、pH7〜8までの前記の傾きが弱酸及びその可溶性塩を含まない場合よりも緩やかで、且つ研摩時間が更に経過する場合も、前記の傾きの変化が少ないため、pH変化のグラフが直線に近いものとなる。このようにpHの上昇を緩やかにした場合に、研摩速度の低下が効果的に抑制できることは、本発明において初めて明らかにされたものである。
研摩液中の弱酸及びその可溶性塩の合計の含有量は例えば弱酸をすべて可溶性塩に変換した後、電位差滴定法等を用いて弱酸の濃度を求めることで測定できる。
研摩液中の可溶性塩の含有量は例えば電位差滴定法等を用いて測定できる。
なお、前記緩衝能測定時の研摩液のpHの調整は、例えば、研摩液のpHが3.0より低い場合には濃度0.1mol/Lの水酸化ナトリウムの水溶液を添加することで、4.0より高い場合には濃度0.05mol/Lの希硫酸を添加することで行うことができる。前記の緩衝能が前記の範囲内であることは、前記pH3.0以上4.0以下の範囲のいずれか1のpHにおいて満たされれば、当該範囲の他のpHにおいて満たされていなくてもよい。
特に、本実施形態においては、シリカ、二酸化マンガン、アルミナを用いることが、弱酸及びその可溶性塩を用いることによる研摩速度の低下防止の効果が効果的に奏されるために好ましい。
純水、過マンガン酸カリウム(KMnO4)、酢酸、及び酢酸ナトリウムを、過マンガン酸イオン、酢酸及び酢酸ナトリウムが下記表1の濃度となるように混合し、研摩液を調製した。得られた研摩液の研摩開始前のpH(25℃)を測定した。これを初期pHとして表1に示す。また、緩衝能として25℃において、pHを3.0以上4.0以下に調整した研摩液100mLに、濃度0.1mol/Lの水酸化ナトリウムの水溶液を添加したときのpHが0.5上昇するまでに要する水酸化ナトリウムの水溶液の添加量(mL)を測定した。この時、研摩液のpHの調整は、研摩液のpHが3.0より低い場合には濃度0.1mol/Lの水酸化ナトリウムの水溶液を添加することで、4.0より高い場合には濃度0.05mol/Lの希硫酸を添加することで行った。調整後のpH及び得られた緩衝能の結果を下記表1に示す。なおpHは堀場製作所製pH電極9615S−10Dを用いて測定した(以下、他の実施例及び比較例でも同様)。
前記研摩液を用いて、以下の手順で研摩を行った。研摩対象としては直径3インチ、オフ角が4°のラッピングされた4H−SiC基板を用いた。研摩は基板のSi面に対して行った。研摩装置として、エム・エー・ティー社製片面研摩機BC−15を用いた。定盤に取り付ける研摩パッドには、ニッタ・ハース社製SUBA#600を用いた。定盤の回転数は60rpm、外周部速度は7163cm/minに設定した。またキャリア回転数は60rpm、外周部速度は961cm/minに設定した。また、研摩圧力は210g/cm2とした。研摩液の供給量は200mL/minとした。この条件で研摩液1.0Lを前記のように繰り返し使用して用いた。研摩速度(μm/h)は、研摩前後の基板の質量差とSiCの密度(3.10g/cm3)とから測定した。
また、研摩開始から24時間経過した後の総研摩量(厚さ)についても上記と同様の計算方法で測定した。
純水、過マンガン酸カリウム(KMnO4)、硝酸セリウム(IV)アンモニウム((NH4)2[Ce(NO3)6]、以下CANとも記載する)、酢酸、及び酢酸ナトリウムを、過マンガン酸イオン、酢酸、酢酸ナトリウム及びCANが下記表2の濃度となるように混合し、研摩液を調製した。得られた研摩液の研摩開始前のpH(25℃)を測定した。その結果を初期pHとして下記表2に示す。また得られた研摩液の前記の緩衝能を測定した。その結果を、調整後のpHとともに下記表2に示す。なお過マンガン酸塩の1.0%水溶液にCANを、1.0%濃度となるように添加して得られる溶液の酸化還元電位は25℃で1291mVであり、CANを添加前の過マンガン酸塩の1.0%水溶液の酸化還元電位は25℃で770mVであった。酸化還元電位は、堀場製作所製ORP電極9300−10Dを25℃のこれらの液に浸漬して測定した。
純水、過マンガン酸カリウム(KMnO4)、シリカ粒子(平均粒径d500.34μm)、酢酸、及び酢酸ナトリウムを過マンガン酸イオン、酢酸、酢酸ナトリウム及びシリカ粒子が下記表3の濃度となるように混合し、研摩液を調製した。得られた研摩液の研摩開始前のpH(25℃)を測定した。その結果を初期pHとして下記表3に示す。また得られた研摩液の前記の緩衝能を測定した。その結果を、調整後のpHとともに下記表3に示す。なお前記平均粒径d50の測定は、測定前に酸化物粒子の分散を行うために超音波分散処理(30W)を3分間実施し、レーザー回折・散乱法粒子径分布測定装置(マイクロトラック・ベル(株)製:マイクロトラックMT3300EXII)を使用して、粒子透過性:屈折、真球/非球形:非球形、粒子屈折率:1.46、溶媒屈折率:1.333の条件で測定した。
Claims (8)
- 過マンガン酸イオンと、弱酸と、その可溶性塩とを含み、研摩液中の弱酸及びその可溶性塩の合計の含有量が、弱酸の陰イオンのモル数として0.001mol/L以上1mol/L以下であり、砥粒を含まない研摩液。
- 研摩開始前におけるpHが25℃で0.5以上6以下である、請求項1に記載の研摩液。
- 前記研摩液は、25℃においてpHを3.0以上4.0以下に調整した該研摩液100mLに、濃度0.1mol/Lの水酸化ナトリウムの水溶液を添加したときに、該研摩液のpHを0.5上昇させるのに要する水酸化ナトリウムの水溶液の添加量が、0.1mL以上100mL以下である緩衝能を有する、請求項1又は2に記載の研摩液。
- 弱酸が酢酸である、請求項1〜3のいずれか1項に記載の研摩液。
- 前記弱酸可溶塩がナトリウム塩及び/又はカリウム塩である、請求項1〜4のいずれか1項に記載の研摩液。
- 研摩液中、弱酸の可溶性塩の含有量は、弱酸1モルに対して、0.05モル以上20モル以下である、請求項1〜5のいずれか1項に記載の研摩液。
- 炭化ケイ素の研摩に用いられる請求項1〜6のいずれか1項に記載の研摩液。
- 請求項1〜7のいずれか1項に記載の研摩液を研摩に用いる研摩物の製造方法。