JP6267869B2 - 発泡成形体 - Google Patents
発泡成形体 Download PDFInfo
- Publication number
- JP6267869B2 JP6267869B2 JP2013070169A JP2013070169A JP6267869B2 JP 6267869 B2 JP6267869 B2 JP 6267869B2 JP 2013070169 A JP2013070169 A JP 2013070169A JP 2013070169 A JP2013070169 A JP 2013070169A JP 6267869 B2 JP6267869 B2 JP 6267869B2
- Authority
- JP
- Japan
- Prior art keywords
- boron
- molded product
- foam
- foamed molded
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
特許文献1では、特定炭素数の脂肪酸のグリセリンエステルと特定炭素数の脂肪族アルコールを用いたポリオレフィン系樹脂の予備発泡粒子を発泡させた発泡体成形が開示されている。しかしながら、表面固有抵抗を下げる効果は不十分であった。
発泡成形体を100mm×100mm×10mm(t)の大きさのサンプルに切り出し、ホウ素系化合物が存在している切断していない面で表面固有抵抗値を測定した。35℃の乾燥室で12時間乾燥させた後、LH40−15P型 恒温恒湿槽(株式会社ナガノサイエンス製)内で24時間置くことでサンプルの温度を35℃、相対湿度を12%に調整した。
表面固有抵抗値の測定に用いる発泡成形体と同様に切り出して同様に状態調節した発泡成形体を、恒温恒湿槽から取り出した後直ちにポリエチレン製の袋(OK袋No.15、大倉工業株式会社製)を用いて成形体表面全体を素早く5往復擦り、直後1秒以内の成形体表面の表面電荷量を測定した。測定はElectrostatic Meter YC−102 (アズワン株式会社製)を使用し、測定距離30mmで実施した(擦り処理、電荷量測定は23℃、相対湿度50%の雰囲気下で行った)。
ポリスチレン発泡性樹脂粒子(カネパール「SBS」、株式会社カネカ製)を通常の方法で予備発泡、型内で発泡成形して、成形体密度20g/Lのポリスチレン系発泡成形体(300mm×400mm×25mm(t))を作製した。測定に使用する面に、成形体表面積に対しホウ素系化合物溶液「アンチスタH(ボロン研究所、ホウ素系帯電防止剤濃度1%の水溶液)」をホウ素系化合物が30g/m2となるように、霧吹きでまんべんなく噴霧した。表面固有抵抗値と表面電荷量の結果を表1に示す。
ホウ素系化合物を10g/m2となるように噴霧した以外は実施例1と同様にして試料を作成した。
ポリエチレン発泡粒子(エペラン「XL38」、株式会社カネカ製)を通常の方法で成形し、成形体密度25g/Lのポリエチレン系発泡成形体(300mm×400mm×25mm(t))を作製した。実施例1と同様に霧吹きでホウ素系化合物溶液を噴霧し、成形体表面に対しホウ素系化合物量が30g/m2とした。
ポリポリプロピレン発泡粒子(エペラン「LBS30」、株式会社カネカ製)を通常の方法で成形し、成形体密度30g/Lのポリプロピレン系発泡成形体(300mm×400mm×25mm(t))を作製した。実施例1と同様に霧吹きでホウ素系化合物溶液を噴霧し、成形体表面に対しホウ素系化合物量が30g/m2とした。
特開WO2009/157374の実施例を参考に、(エペラン「LBS30」、カネカ製)を通常の方法で成形し、成形体密度30g/Lのポリプロピレン系発泡成形体(300mm×400mm×25mm(t))を作製した。実施例1と同様に霧吹きでホウ素系化合物溶液を噴霧し、成形体表面に対しホウ素系化合物量が30g/m2とした。
ホウ素系化合物を使用しなかった以外は実施例1と同様に発泡成形体を作製した。
ホウ素系化合物を使用しなかった以外は実施例2と同様に発泡成形体を作製した。
ホウ素系化合物を使用しなかった以外は実施例3と同様に発泡成形体を作製した。
ホウ素系化合物を使用しなかった以外は実施例4と同様に発泡成形体を作製した。
ホウ素系化合物を4g/m2となるようにホウ素系化合物溶液を噴霧した以外は実施例1と同様にして試料を作成した。
ホウ素系化合物を2g/m2となるようにホウ素系化合物溶液を噴霧した以外は実施例1と同様にして試料を作成した。
ホウ素系化合物の変わりに界面活性剤「EC-4(北広ケミカル株式会社製、ヒドロキシアルキルアミンとイソプロピルアルコールの水溶液)」を使用し、成形体表面の量が30g/m2となるように界面活性剤溶液を噴霧した以外は実施例1と同様にした。
Claims (7)
- ポリスチレン系樹脂、ポリオレフィン系樹脂、スチレン改質ポリオレフィン系樹脂のいずれかからなる樹脂を基材樹脂とし、
ホウ素系化合物が成形体表面に5g/m 2 以上100g/m 2 以下の量で存在し、温度35℃、湿度12%における表面固有抵抗値が1.0×1010Ω以下であることを特徴とする発泡成形体。 - ホウ素系化合物がアルコール化合物とのドナー・アクセプター構造を有することを特徴とする請求項1記載の発泡成形体。
- 発泡成形体の密度が15g/L〜200g/Lであることを特徴とする請求項1または2に記載の発泡成形体。
- 発泡成形体が予備発泡樹脂粒子を型内成形させてなることを特徴とする請求項1〜3のいずれかに記載の発泡成形体。
- 発泡成形体の粒子間のくぼみにホウ素系化合物が存在している請求項1〜4のいずれかに記載の発泡成形体。
- 発泡成形体の表面にホウ素系化合物の水溶液を塗布、または噴霧することにより得られる請求項1〜5のいずれかに記載の発泡成形体。
- 発泡成形体の表面にホウ素系化合物の溶液を塗布、または噴霧することを特徴とする請求項1〜5のいずれかに記載の発泡成形体の製造方法。