JP5926548B2 - 印刷用紙 - Google Patents
印刷用紙 Download PDFInfo
- Publication number
- JP5926548B2 JP5926548B2 JP2011266461A JP2011266461A JP5926548B2 JP 5926548 B2 JP5926548 B2 JP 5926548B2 JP 2011266461 A JP2011266461 A JP 2011266461A JP 2011266461 A JP2011266461 A JP 2011266461A JP 5926548 B2 JP5926548 B2 JP 5926548B2
- Authority
- JP
- Japan
- Prior art keywords
- printing paper
- black pigment
- fluorescent whitening
- paper
- black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
パルプとして、濾水度400mlcsfのLBKPが85部、濾水度450mlcsfのNBKPが15部からなるパルプスラリーに、填料として軽質炭酸カルシウム(商品名:TP−121、奥多摩工業社製)20部、両性澱粉(商品名:Cato3210、日本エヌエスシー社製)1.0部、硫酸バンド1.0部、アルキルケテンダイマー型サイズ剤(商品名:サイズパインK903、荒川化学工業社製)0.3部を添加して、長網抄紙機で抄紙し乾燥した。その後、酸化澱粉(商品名:MS#3800、日本食品化工社製)100部、黒顔料として平均一次粒子径Dが0.2μmのカーボンブラック(商品名:TB−510 BLACK TR、大日精化工業社製)0.05部、蛍光増白染料としてスチルベンジスルホン酸誘導体(商品名:Leucophor AP liq、クラリアント社製)50部からなる糊液を、ゲートロールコーターを用いて乾燥含有量で、印刷用紙の含有量として酸化澱粉が2g/m2、黒顔料が0.001g/m2、蛍光増白染料が1g/m2となるように塗布した。その後、マシンカレンダー処理をして坪量75g/m2、密度0.85g/cm3の実施例1の印刷用紙を作製した。
黒顔料の配合部数を0.25部として印刷用紙の黒顔料含有量を0.005g/m2とした以外は、実施例1と同様にして実施例2の印刷用紙を作製した。
黒顔料の配合部数を0.5部として印刷用紙の黒顔料含有量を0.01g/m2とした以外は、実施例1と同様にして実施例3の印刷用紙を作製した。
蛍光増白染料の配合部数を1.5部として印刷用紙の蛍光増白染料含有量を0.03g/m2とした以外は、実施例2と同様にして実施例4の印刷用紙を作製した。
蛍光増白染料の配合部数を150部として印刷用紙の蛍光増白染料含有量を3g/m2とした以外は、実施例2と同様にして実施例5の印刷用紙を作製した。
黒顔料を平均一次粒子径Dが0.2μmのフタロシアニンブラック(商品名:TB−786 BLACK、大日精化工業社製)とした以外は、実施例2と同様にして実施例6の印刷用紙を作製した。
蛍光増白染料をクマリン系化合物(商品名:Whitex Ws、住化ケムテックス社製)とした以外は、実施例2と同様にして実施例7の印刷用紙を作製した。
蛍光増白染料の配合部数を25部として印刷用紙の蛍光増白染料含有量を0.5g/m2とした以外は、実施例3と同様にして実施例8の印刷用紙を作製した。
蛍光増白染料の配合部数を300部として印刷用紙の蛍光増白染料含有量を6g/m2とした以外は、実施例2と同様にして実施例9の印刷用紙を作製した。
黒顔料を平均一次粒子径Dが0.02μmのカーボンブラックとした以外は、実施例2と同様にして参考例1の印刷用紙を作製した。
黒顔料を平均一次粒子径Dが0.05μmのカーボンブラックとした以外は、実施例2と同様にして実施例10の印刷用紙を作製した。
黒顔料を平均一次粒子径Dが0.5μmのカーボンブラックとした以外は、実施例2と同様にして実施例11の印刷用紙を作製した。
黒顔料を平均一次粒子径Dが0.7μmのカーボンブラックとした以外は、実施例2と同様にして参考例2の印刷用紙を作製した。
黒顔料の配合部数を0.025部として印刷用紙の黒顔料含有量を0.0005g/m2とした以外は、実施例1と同様にして比較例1の印刷用紙を作製した。
黒顔料の配合部数を1部として印刷用紙の黒顔料含有量を0.02g/m2とした以外は、実施例1と同様にして比較例2の印刷用紙を作製した。
蛍光増白染料の配合部数を0.5部として印刷用紙の蛍光増白染料含有量を0.01g/m2とした以外は、実施例2と同様にして比較例3の印刷用紙を作製した。
黒顔料の配合部数を0部として印刷用紙の黒顔料含有量を0g/m2とし、蛍光増白染料の配合部数を0部として印刷用紙の蛍光増白染料含有量を0とした以外は、実施例1と同様にして比較例4の印刷用紙を作製した。
填料として軽質炭酸カルシウム(商品名:TP−121、奥多摩工業社製)の配合部数を30部、酸化チタン(商品名:タイペークW−10、石原産業社製)の配合部数を10部とした以外は、比較例4と同様にして比較例5の印刷用紙を作製した。
JIS−P8148に規定された白色度測定方法を用いて、印刷用紙の白色度を測定した。3以上の評価では、実用上問題ないレベルである。
5:85%以上。
4:82%以上、85%未満。
3:79%以上、82%未満。
2:76%以上、79%未満。
1:76%未満。
JIS−P8149に規定された不透明度測定方法を用いて、印刷用紙の不透明度を測定した。3以上の評価では、実用上問題ないレベルである。
5:89%以上。
4:87%以上、89%未満。
3:85%以上、87%未満。
2:83%以上、85%未満。
1:83%未満。
RI印刷適性機を用いて墨色ベタ印刷を施した。印刷は以下の条件で行った。
インキ:IGT測定用インキ 墨 TV.20(大日本インキ化学工業社製)
インキ量:1.0cc
印刷回転速度:80rpm
その後、印刷面のピッキングの程度を目視で判定した。3以上の評価では、実用上問題ないレベルである。
5:ピッキング全くなし。
4:ほとんどピッキングなし。
3:わずかにピッキングが見られる。
2:少しピッキングが見られる。
1:かなりピッキングが見られる。
Claims (3)
- 坪量が75g/m2以下の印刷用紙であって、印刷用紙が塗布により黒顔料および蛍光増白染料を含有し、含有する黒顔料の含有量X(g/m2)が0.001≦X≦0.01の範囲であり、含有する蛍光増白染料の含有量Y(g/m2)が0.03≦Yの範囲であり、前記黒顔料の平均一次粒子径D(μm)が0.05≦D≦0.5の範囲であることを特徴とする印刷用紙。
- 前記黒顔料がカーボンブラックである請求項1に記載の印刷用紙。
- 前記蛍光増白染料がスチルベンジスルホン酸誘導体である請求項1または2に記載の印刷用紙。