JP5898417B2 - Manufacturing method for sheet-like cosmetics - Google Patents
Manufacturing method for sheet-like cosmetics Download PDFInfo
- Publication number
- JP5898417B2 JP5898417B2 JP2011126207A JP2011126207A JP5898417B2 JP 5898417 B2 JP5898417 B2 JP 5898417B2 JP 2011126207 A JP2011126207 A JP 2011126207A JP 2011126207 A JP2011126207 A JP 2011126207A JP 5898417 B2 JP5898417 B2 JP 5898417B2
- Authority
- JP
- Japan
- Prior art keywords
- cosmetic
- sheet
- cosmetics
- binder
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、ファンデーション，アイシャドウ，頬紅等の粉体含有化粧料の化粧料サンプルや、旅行用の小分けした化粧料等として使用することができるシート状化粧料及びその製造方法に関するものである。 The present invention relates to a cosmetic sample of powder-containing cosmetics such as foundation, eye shadow, blusher, etc., a sheet-like cosmetic that can be used as a small-sized cosmetic for travel, and a method for producing the same.
従来から、ファンデーション，アイシャドウ，頬紅等の粉体含有化粧料のサンプルを収容するものとして、各種のサンプルケースが出回っている。ところが、これらはいずれも立体的な形状であり、このため、嵩張って運搬等の取り扱い性が悪いという問題がある。 Conventionally, various sample cases have been available for containing powder-containing cosmetic samples such as foundations, eye shadows, and blushers. However, these are all three-dimensional shapes, and therefore have a problem that they are bulky and have poor handling properties such as transportation.
このような問題を改善するため、シート状の化粧料が開発されている。このようなシート状化粧料は、通常、シート状基材上にスクリーン印刷方式によって化粧料層を形成することによって製造されるものである。
一方、通常の商品として販売される化粧料としては、特許文献１に記載されたもののように、含水揮発性溶剤を含む組成物を容器充填して、その後乾燥することによる湿式製法によって得られる化粧料が公知である。これらの製造方法とスクリーン印刷方式とは製造方法として根本的に相違するものである。
In order to improve such problems, sheet-like cosmetics have been developed. Such a sheet-like cosmetic is usually produced by forming a cosmetic layer on a sheet-like substrate by a screen printing method.
On the other hand, as a cosmetic sold as a normal product, a cosmetic obtained by a wet manufacturing method in which a composition containing a hydrous volatile solvent is filled in a container and then dried, as described in Patent Document 1. Fees are known. These manufacturing methods and screen printing systems are fundamentally different as manufacturing methods.
このように、実際の商品とシート状化粧料とでは、製造方法が異なるために、その使用時の感触が相違してしまうという問題があった。特に、スクリーン印刷方式によって製造されたシート状化粧料においては、印刷ができるように有機溶剤を添加することが行われるため、溶媒の揮発速度が速くなってしまい、これによって得られた化粧料の色調、光沢、感触等が実際の製品と相違するものとなってしまう。特に、揮発性溶剤を使用して成形する湿式の製造方法によって得られる化粧料においては、揮発の速度が相違することによって、性能に差が生じてしまいやすい。 Thus, since the actual product and the sheet-like cosmetic have different manufacturing methods, there has been a problem that the touch at the time of use is different. In particular, in a sheet-like cosmetic manufactured by a screen printing method, since an organic solvent is added so that printing can be performed, the volatilization rate of the solvent is increased, and the resulting cosmetic is Color tone, gloss, feel, etc. will be different from the actual product. In particular, in a cosmetic obtained by a wet manufacturing method in which molding is performed using a volatile solvent, a difference in performance tends to occur due to a difference in volatilization speed.
シート状化粧料を化粧品サンプルとして使用する場合には、製品としての化粧料との性能の差が大きいことは、サンプルの目的を達することができず、大きな問題となってしまう。 When a sheet-shaped cosmetic is used as a cosmetic sample, a large difference in performance from the cosmetic as a product cannot achieve the purpose of the sample, which is a big problem.
その他のシート状化粧料の製造方法としては、特許文献２に記載されたものが知られている。これは、粉状化粧料をメッシュ上でブラシ毛でかき落とし、その後プレスを行うことによって製造する方法である。このような方法は、複雑な装置を有するため、サンプルのように無料配布する製品に使用するには、コスト高になるという問題がある。 As another method for producing a sheet-shaped cosmetic, one described in Patent Document 2 is known. This is a method for producing a powdery cosmetic material by brushing it off with a brush on a mesh and then pressing it. Since such a method has a complicated apparatus, there is a problem in that it is expensive to use for a product distributed free of charge such as a sample.
また、特許文献３に記載したように水溶性高分子を配合した組成物を基材上に塗布することによってシート状化粧料を得る方法も知られている。しかし、特許文献３の発明は光輝性顔料による光輝感を皮膚に付与するためのものであり、本発明において使用されるような通常のメイクアップ化粧料とは異なり、油性成分を含有しないものである。更に、水溶性高分子は単に光輝性顔料のシートへの付着能を高くするために使用されているものである。 Further, as described in Patent Document 3, a method of obtaining a sheet-shaped cosmetic by applying a composition containing a water-soluble polymer on a substrate is also known. However, the invention of Patent Document 3 is for imparting a radiant feeling to the skin by the brilliant pigment, and does not contain an oily component unlike ordinary makeup cosmetics used in the present invention. is there. Further, the water-soluble polymer is merely used to increase the ability of the glitter pigment to adhere to the sheet.
本発明は、上記問題点を解決するためになされたものであり、販売される本製品と同様の感触を有するために、サンプルとして好適に使用することができ、かつ、簡便な方法によって安価で製造することができるシート状化粧料を得ることを目的とするものである。 The present invention has been made to solve the above problems, and since it has the same feel as the product sold, it can be suitably used as a sample and is inexpensive by a simple method. It aims at obtaining the sheet-like cosmetics which can be manufactured.
本発明は、化粧品原料、粘結剤（Ｂ）及び揮発性溶剤（Ｃ）を混合しスラリー状とする工程（１）、上記工程（１）によって得られたスラリー状組成物をシート状基材上に噴霧する工程（２）、及び、上記工程（２）によって得られた化粧料層を有するシートを乾燥させる工程（３）を有し、化粧料原料は、少なくとも一部が粉体成分（Ａ）及び油性成分（Ｄ）であり、粘結剤（Ｂ）は、ポリビニルピロリドンであり、
粘結剤（Ｂ）は、化粧品原料１００質量部に対して５質量部以下であり、
揮発性溶剤（Ｃ）は、軽質流動イソパラフィン及び／又は水であり、
化粧料層形成面１ｃｍ２に対して０．００２〜０．０８ｇで化粧料層が形成されたものであることを特徴とするシート状化粧料の製造方法でもある。
In the present invention, a cosmetic raw material, a binder (B) and a volatile solvent (C) are mixed to form a slurry (1), and the slurry composition obtained by the above step (1) is used as a sheet-like substrate. The step (2) of spraying on and the step (3) of drying the sheet having the cosmetic layer obtained by the above step (2), wherein the cosmetic raw material is at least partly a powder component ( A) and the oil component (D), the binder (B) is polyvinylpyrrolidone,
The binder (B) is 5 parts by mass or less with respect to 100 parts by mass of the cosmetic raw material,
Volatile solvent (C) is light liquid isoparaffin and / or water,
It is also a method for producing a sheet-like cosmetic, wherein the cosmetic layer is formed at 0.002 to 0.08 g with respect to 1 cm 2 of the cosmetic layer forming surface.
上記工程（１）は、粘結剤（Ｂ）及び揮発性溶剤（Ｃ）を予め混合溶解する工程を行った後に、その他の成分を混合するものであることが好ましい。
本発明のシート状化粧料の製造方法においては、上記工程（２）の後、工程（３）を行う前の段階においてプレスを行わないことが好ましい。
It is preferable that the said process (1) mixes another component, after performing the process which mix-dissolves a binder (B) and a volatile solvent (C) previously .
In the manufacturing method of the sheet-like cosmetics of this invention, it is preferable not to perform a press in the step after performing the said process (2) and before performing a process (3).
本発明により、商品として販売される化粧料と同様の感触を有し、サンプルとして好適に使用することができ、かつ、簡便な方法によって安価で製造することができるシート状化粧料を得ることができる。このようなシート状化粧料は、サンプルだけではなく、小分けした状態の化粧料（例えば、旅行用等の使い切りタイプ）においても使用することができる。 According to the present invention, it is possible to obtain a sheet-like cosmetic that has the same feel as a cosmetic sold as a product, can be suitably used as a sample, and can be manufactured at a low cost by a simple method. it can. Such sheet-shaped cosmetics can be used not only in samples but also in cosmetics in a divided state (for example, a single-use type for travel).
以下、本発明を詳細に説明する。
本発明は、主に粉体成分を含有する化粧料のサンプルとして使用することができるシート状化粧料に関するものである。なお、本発明の化粧料をサンプルとして使用する場合は、商品と同一の組成であってもよいし、感触を調整するために、原料の配合割合を若干変更したものであってもよい。
より具体的には、化粧下地、コンシーラ、ファンデーション、アイカラー、アイブロウ、アイライナー、アイシャドウ等の粉体成分を含有する各種の形態の化粧料において使用することができる。
Hereinafter, the present invention will be described in detail.
The present invention relates to a sheet-like cosmetic that can be used mainly as a cosmetic sample containing a powder component. In addition, when using the cosmetics of this invention as a sample, the same composition as goods may be sufficient, and in order to adjust a touch, the thing which changed the mixture ratio of the raw material slightly may be sufficient.
More specifically, it can be used in various forms of cosmetics containing powder components such as a makeup base, concealer, foundation, eye color, eyebrow, eyeliner, eyeshadow and the like.
本発明の化粧料は、化粧品原料、粘結剤（Ｂ）及び揮発性溶剤（Ｃ）とを使用して得られるものである。上記化粧品原料は、少なくとも一部が粉体成分（Ａ）及び油性成分（Ｄ）である。なお、本明細書において、「化粧品原料」とは上記スラリー状組成物を構成する原料のうち、粘結剤（Ｂ）及び揮発性溶剤（Ｃ）に該当しない成分の総称である。 The cosmetic of the present invention is obtained using a cosmetic raw material, a binder (B), and a volatile solvent (C). The cosmetic raw material is at least partially a powder component (A) and an oil component (D). In the present specification, “cosmetic raw material” is a general term for components that do not correspond to the binder (B) and the volatile solvent (C) among the raw materials constituting the slurry composition.
上記粉体成分（Ａ）としては特に限定されず、例えば、ベンガラ、黄酸化鉄、黒酸化鉄等の無機着色顔料、雲母チタン、ベンガラ被覆雲母チタン、酸化チタン被覆ガラスフレーク等の光輝性着色顔料、マイカ、タルク、カオリン、セリサイト、二酸化チタン、酸化亜鉛等の無機粒子、ポリエチレン末、ナイロン末、架橋ポリスチレン、セルロースパウダー等の有機粒子等の化粧品において汎用される材料を使用することができる。更に、赤色２０１号、赤色２０２号、赤色２２０号、赤色２２６号、赤色１０４号の（１）もしくはその金属レーキ、青色４０４号、青色１号もしくはその金属レーキ、黄色４号もしくはその金属レーキ等の有機色素も上記粉体成分（Ａ）に包含されるものである。 The powder component (A) is not particularly limited, and examples thereof include inorganic colored pigments such as Bengala, yellow iron oxide, black iron oxide, and bright colored pigments such as mica titanium, Bengala-coated mica titanium, and titanium oxide-coated glass flakes. Materials generally used in cosmetics such as inorganic particles such as mica, talc, kaolin, sericite, titanium dioxide, and zinc oxide, and organic particles such as polyethylene powder, nylon powder, cross-linked polystyrene, and cellulose powder can be used. Further, Red 201, Red 202, Red 220, Red 226, Red 104 (1) or its metal rake, Blue 404, Blue 1 or its metal rake, Yellow 4 or its metal rake, etc. These organic dyes are also included in the powder component (A).
これらの成分は必要に応じて表面処理を施したものであってもよい。表面処理としては、シリコーン類、フッ素化合物、金属石鹸、油剤、アシルグルタミン酸塩等の物質による、公知の疎水化処理；シリカやアルミナによる無機系の表面処理等を挙げることができる。
上記粉体成分（Ａ）は、２種以上を併用して使用するものであってもよい。
These components may be subjected to surface treatment as necessary. Examples of the surface treatment include known hydrophobizing treatments with substances such as silicones, fluorine compounds, metal soaps, oil agents, and acyl glutamates; and inorganic surface treatments with silica and alumina.
The powder component (A) may be used in combination of two or more.
本発明の化粧料は、粘結剤（Ｂ）を含有するものである。これによって、噴霧した際に粒子同士が結着しやすくなり、好適な化粧料層を形成することが容易であるという点で好ましいものである。上記粘結剤（Ｂ）は、本発明の工程（２）において、噴霧された化粧料粒子同士を結着させる作用を有する化合物であれば特に限定されず、例えば、水溶性高分子、水分散性高分子、水膨潤性物質等を挙げることができる。これらの２種以上を併用して使用するものであってもよい。 The cosmetic of the present invention contains a binder (B). This is preferable in that the particles are easily bound to each other when sprayed and it is easy to form a suitable cosmetic layer. The binder (B) is not particularly limited as long as it is a compound having an action of binding the sprayed cosmetic particles in the step (2) of the present invention. And water-swellable substances. Two or more of these may be used in combination.
本発明において使用することができる粘結剤（Ｂ）のうち、水溶性高分子としては特に限定されず、例えば、カルボキシビニルポリマー、アルキル変性カルボキシビニルポリマー、アラビアガム、アルギン酸又はその塩、カラギーナン、寒天、グアーガム、クインスシード、タマリンドガム、デキストリン、デキストラン、デンプン、ローカストビーンガム、カラヤガム、トルガカントガム、ペクチン、マルメロ、キトサン、キサンタンガム、ジェランガム、ヒアルロン酸又はその塩、プルラン、メチルセルロース、エチルセルロース、ヒドロキシエチルセルロース、ヒドロキシプロピルメチルセルロース、カルボキシメチルセルロース、カチオン化セルロース、ポリビニルピロリドン、ポリビニルアルコール等からなる群より選択される１種以上であることが好ましい。 Of the binder (B) that can be used in the present invention, the water-soluble polymer is not particularly limited. For example, carboxyvinyl polymer, alkyl-modified carboxyvinyl polymer, gum arabic, alginic acid or a salt thereof, carrageenan, Agar, guar gum, quince seed, tamarind gum, dextrin, dextran, starch, locust bean gum, karaya gum, tolgacant gum, pectin, quince, chitosan, xanthan gum, gellan gum, hyaluronic acid or its salt, pullulan, methylcellulose, ethylcellulose, hydroxyethylcellulose, hydroxy 1 selected from the group consisting of propylmethylcellulose, carboxymethylcellulose, cationized cellulose, polyvinylpyrrolidone, polyvinyl alcohol and the like Or more at a wavelength of 550 nm.
本発明において使用することができる粘結剤（Ｂ）のうち、水分散性高分子としては特に限定されず、例えば、アクリル酸アルキル共重合体エマルジョン、ポリ酢酸ビニルエマルジョン、ポリアクリル酸エステルエマルジョン、ポリ塩化ビニルエマルジョン、（メタ）アクリル酸アルキル・スチレン共重合体エマルション、（メタ）アクリル酸アルキル・酢酸ビニル共重合体エマルション、ビニルピロリドン・スチレン共重合体エマルション、シリコーン系ポリマーエマルション等からなる群より選択される１種以上であることが好ましい。 Of the binder (B) that can be used in the present invention, the water-dispersible polymer is not particularly limited. For example, an alkyl acrylate copolymer emulsion, a polyvinyl acetate emulsion, a polyacrylate emulsion, From the group consisting of polyvinyl chloride emulsion, alkyl (meth) acrylate / styrene copolymer emulsion, alkyl (meth) acrylate / vinyl acetate copolymer emulsion, vinylpyrrolidone / styrene copolymer emulsion, silicone polymer emulsion, etc. It is preferable that it is 1 or more types selected.
本発明において使用することができる粘結剤（Ｂ）のうち、水膨潤性物質としては特に限定されず、例えば、マグネシウムアルミニウムシリケート、ナトリウムマグネシウムシリケート等を挙げることができる。 Of the binder (B) that can be used in the present invention, the water-swellable substance is not particularly limited, and examples thereof include magnesium aluminum silicate and sodium magnesium silicate.
更に、本発明の工程（１）においては、揮発性溶剤（Ｃ）を使用するものである。揮発性溶剤（Ｃ）を含有することで、スラリー状組成物の噴霧によって化粧料層を形成することができる。
上記揮発性溶剤（Ｃ）としては、水、軽質流動イソパラフィン、エチルアルコール、イソプロピルアルコール、アセトン、酢酸エチル、ヘキサン等の低沸点溶剤等を挙げることができる。これらのうち、２種以上を併用して使用するものであってもよい。
Furthermore, in the step (1) of the present invention, a volatile solvent (C) is used. By containing the volatile solvent (C), the cosmetic layer can be formed by spraying the slurry-like composition.
Examples of the volatile solvent (C) include low boiling solvents such as water, light liquid isoparaffin, ethyl alcohol, isopropyl alcohol, acetone, ethyl acetate, and hexane. Of these, two or more may be used in combination.
上記油性成分（Ｄ）としては、化粧品において汎用される油脂類、ロウ類、硬化油類、炭化水素類、エステル油類、脂肪酸類、高級アルコール類、シリコーン油類等を挙げることができる。これらの２種以上を併用して使用することがより好ましい。 Examples of the oil component (D) include fats and oils, waxes, hardened oils, hydrocarbons, ester oils, fatty acids, higher alcohols, silicone oils and the like commonly used in cosmetics. It is more preferable to use two or more of these in combination.
上記油性成分（Ｄ）としてより具体的には、例えば、流動パラフィン、スクワラン等の炭化水素油；ヒマシ油、オリーブ油、ホホバ油、マカデミアナッツ油、ミンク油、タートル油、アーモンド油、サフラワー油、アボガド油、ラノリン等の動植物油；ステアリン酸、オレイン酸、ラウリン酸、ミリスチン酸等の脂肪酸；グリセリルジイソステアレート、グリセリルトリイソステアレート、トリメチロールプロパン−２−エチルイソステアレート、グリセリル−トリ−２−エチルヘキサノエート、イソプロピルミリステート、セチル−２−エチルヘキサノエート、ジイソステアリルマレート、２−ヘプチルウンデシルパルミテート等の合成エステル油；セタノール、ステアリルアルコール、オレイルアルコール、ラウリルアルコール等の高級アルコール；固形パラフィンワックス、セレシンワックス、マイクロクリスタリンワックス、モクロウ、ミツロウ、キャンデリラワックス、カルナウバワックス、ポリエチレンワックス等のワックス類；アルキル変性シリコーンワックス等のシリコーン系油剤；パーフルオロポリエーテル、フッ素変性シリコーン等のフッ素系油剤等が挙げられる。 More specific examples of the oil component (D) include hydrocarbon oils such as liquid paraffin and squalane; castor oil, olive oil, jojoba oil, macadamia nut oil, mink oil, turtle oil, almond oil, safflower oil, avocado Animal and vegetable oils such as oil, lanolin; fatty acids such as stearic acid, oleic acid, lauric acid, myristic acid; glyceryl diisostearate, glyceryl triisostearate, trimethylolpropane-2-ethylisostearate, glyceryl-tri- Synthetic ester oils such as 2-ethylhexanoate, isopropyl myristate, cetyl-2-ethylhexanoate, diisostearyl malate, 2-heptylundecyl palmitate; cetanol, stearyl alcohol, oleyl alcohol, lauryl alcohol, etc. Luxury Solids paraffin wax, ceresin wax, microcrystalline wax, wax, beeswax, candelilla wax, carnauba wax, polyethylene wax, etc .; silicone oils such as alkyl-modified silicone wax; perfluoropolyether, fluorine-modified silicone Fluorine-based oils such as
本発明の化粧料においては、更にその他の成分（Ｅ）を含有するものであってもよい。その他の成分（Ｅ）としては、化粧品において汎用される任意の成分を挙げることができ、例えば、多価アルコール、界面活性剤、薬効成分、着香剤、清涼剤、紫外線吸収剤、紫外線散乱剤、懸濁剤、安定化剤、湿潤剤、抗酸化剤、ｐＨ調整剤、粘度調整剤、着色剤、防腐剤等を挙げることができる。 The cosmetic of the present invention may further contain other component (E). Examples of the other component (E) include any components commonly used in cosmetics, for example, polyhydric alcohols, surfactants, medicinal ingredients, flavoring agents, refreshing agents, ultraviolet absorbers, ultraviolet scattering agents. Suspending agents, stabilizers, wetting agents, antioxidants, pH adjusting agents, viscosity adjusting agents, coloring agents, preservatives and the like.
上記多価アルコールとしては、化粧料分野において一般的に使用される公知のものを使用することができ、例えば、ジプロピレングリコール、１，３‐ブチレングリコール、イソペンチルジオール、１，２−ペンタンジオール、１，２−ヘキサンジオール、ポリエチレングリコール、グリセリン、ジグリセリン、ソルビトール、マルチトール、ラフィノース等を挙げることができる。これらは市販品として容易に入手することができる。上記多価アルコールは、必要に応じて、１種又は２種以上を用いることができる。 As the polyhydric alcohol, known ones commonly used in the cosmetics field can be used. For example, dipropylene glycol, 1,3-butylene glycol, isopentyldiol, 1,2-pentanediol 1,2-hexanediol, polyethylene glycol, glycerin, diglycerin, sorbitol, maltitol, raffinose and the like. These can be easily obtained as commercial products. The said polyhydric alcohol can use 1 type (s) or 2 or more types as needed.
本発明の化粧料を製造する際の工程（１）は、化粧品原料、上記成分（Ｂ）及び成分（Ｃ）を混合することによってスラリー状として、スラリー状組成物を調製する工程である。上記化粧品原料において、化粧料原料は少なくとも上記成分（Ａ）及び成分（Ｄ）を配合するものである。上記成分（Ａ）は、化粧品原料に対して、５０〜９９．５質量％であることが好ましい。５０質量％より少ないと、粉体成分の少ない処方となるので、シート状の化粧料とすることに適さないものとなるおそれがある。９９．５質量％を超えると、粉体比が多すぎて噴霧するノズルが詰まるおそれがある。上記（Ａ）の配合量は、６０〜９５質量％であることがより好ましい。 Step (1) in producing the cosmetic of the present invention is a step of preparing a slurry-like composition as a slurry by mixing the cosmetic raw material, the component (B) and the component (C). In the cosmetic raw material, the cosmetic raw material contains at least the component (A) and the component (D). It is preferable that the said component (A) is 50-99.5 mass% with respect to cosmetic raw materials. If the amount is less than 50% by mass, the formulation has a small amount of powder components, which may make it unsuitable for use as a sheet-like cosmetic. If it exceeds 99.5% by mass, the powder ratio is too high and the spraying nozzle may be clogged. The blending amount of (A) is more preferably 60 to 95% by mass.
上記成分（Ｂ）は、化粧品原料１００質量部に対して、５質量部以下である。５質量部を超えると乾燥後硬くなりすぎて感触が悪くなるおそれがある。上記成分（Ｂ）は化粧品原料１００質量部に対して、３質量部以下であることがより好ましい。上記成分（Ｂ）の配合量の下限は特に限定されるものではないが、０．０５質量部であることが好ましい。 The said component (B) is 5 mass parts or less with respect to 100 mass parts of cosmetic raw materials. If it exceeds 5 parts by mass, it may become too hard after drying, resulting in a poor feel. The component (B) is more preferably 3 parts by mass or less with respect to 100 parts by mass of the cosmetic raw material. Although the minimum of the compounding quantity of the said component (B) is not specifically limited, It is preferable that it is 0.05 mass part.
上記成分（Ｃ）は、化粧品原料１００質量部に対して、３０〜１５００質量部であることが好ましい。
３０質量部より少ないと、粉体比が多すぎて噴霧するノズルが詰まるおそれがある。１５００質量部を超えると、溶剤比が多すぎて生産効率が悪くなるおそれがある。上記成分（Ｃ）の配合量は、化粧品原料１００質量部に対して、５０〜８００質量部であることがより好ましい。
It is preferable that the said component (C) is 30-1500 mass parts with respect to 100 mass parts of cosmetic raw materials.
If it is less than 30 parts by mass, the powder ratio is too high and the spraying nozzle may be clogged. If it exceeds 1500 parts by mass, the solvent ratio is too high and the production efficiency may deteriorate. As for the compounding quantity of the said component (C), it is more preferable that it is 50-800 mass parts with respect to 100 mass parts of cosmetic raw materials.
上記成分（Ｄ）は、化粧品原料全量に対して、０．４〜２０質量％であることが好ましい。上記範囲内とすることで、感触(滑らかさ)と付着性という点で好ましい化粧料を得ることができる。上記成分（Ｄ）は、化粧品原料全量に対して、１〜１５質量％であることがより好ましい。 It is preferable that the said component (D) is 0.4-20 mass% with respect to cosmetics raw material whole quantity. By setting it within the above range, a cosmetic material preferable in terms of feel (smoothness) and adhesion can be obtained. As for the said component (D), it is more preferable that it is 1-15 mass% with respect to cosmetic raw material whole quantity.
上記工程（１）は、化粧品の通常の製造方法における混合と同様に行うことができる。例えば、モーター攪拌、手での攪拌等を挙げることができる。 The said process (1) can be performed similarly to the mixing in the normal manufacturing method of cosmetics. For example, motor agitation, hand agitation and the like can be mentioned.
本発明の工程（１）においては、スラリーを調製する際の混合の順序や方法は特に限定されるものではないが、粘結剤（Ｂ）及び揮発性溶剤（Ｃ）を混合して溶解させた後に、化粧品原料（粉体成分（Ａ）、油性成分（Ｄ）及び必要に応じて使用するその他の成分（Ｅ））を混合することが好ましい。このようにすることで、水溶性高分子が均一に溶解し、粉体成分も液体媒体中に均一に分散するため、優れた性能の化粧料とすることができる。 In the step (1) of the present invention, the order and method of mixing when preparing the slurry are not particularly limited, but the binder (B) and the volatile solvent (C) are mixed and dissolved. After that, it is preferable to mix cosmetic raw materials (powder component (A), oil component (D) and other components (E) used as necessary). By doing so, the water-soluble polymer is uniformly dissolved, and the powder component is also uniformly dispersed in the liquid medium, so that a cosmetic with excellent performance can be obtained.
本発明の化粧料は、上記工程（１）によって得られたスラリー状組成物をシート状基材上に噴霧する工程（２）を有する製造方法によって得られたものである。すなわち、公知の製造方法のように、シルクスクリーンによって化粧料層を形成するのではなく、スラリー状組成物を噴霧することによって化粧料層を形成するものである。これにより、スクリーン印刷で形成した場合のように、凝結した固い状態になるという問題を生じない。また、本発明においては、粘結剤（Ｂ）及び揮発性溶剤（Ｃ）の配合量を調整することによって、得られたシート状化粧料の感触を調整することができる。よって、これらの量を必要に応じて調整することで、製品の感触と近いサンプルとすることができるものである。 The cosmetic of the present invention is obtained by a production method having a step (2) of spraying the slurry-like composition obtained in the step (1) onto a sheet-like substrate. That is, the cosmetic layer is formed by spraying the slurry-like composition instead of forming the cosmetic layer by a silk screen as in a known production method. As a result, there is no problem of a solidified state as in the case of screen printing. Moreover, in this invention, the touch of the obtained sheet-like cosmetics can be adjusted by adjusting the compounding quantity of a binder (B) and a volatile solvent (C). Therefore, by adjusting these amounts as necessary, a sample close to the feel of the product can be obtained.
本発明において使用されるシート状基材としては特に限定されず、紙、樹脂製シート、金属製シート等の任意のものを使用することができる。シート状基材は、化粧料層形成面に凹部を形成して、凹部に化粧料を充填するものであってもよい。 It does not specifically limit as a sheet-like base material used in this invention, Arbitrary things, such as paper, a resin-made sheet | seat, a metal sheet | seat, can be used. The sheet-like base material may be formed by forming a recess on the cosmetic layer forming surface and filling the recess with the cosmetic.
上記工程（２）における噴霧方法は特に限定されず、エアースプレー、エアレススプレー等の公知の任意の噴霧方法によって行うことができる。また、シート状基材の全面に化粧料層を形成するものでない場合には、化粧料層を形成しない部分にマスクフィルムを貼付し、噴霧後に上記マスクフィルムを剥離してもよい。 The spraying method in the said process (2) is not specifically limited, It can carry out by well-known arbitrary spraying methods, such as an air spray and an airless spray. Moreover, when not forming a cosmetics layer on the whole surface of a sheet-like base material, a mask film may be stuck to the part which does not form a cosmetics layer, and the said mask film may be peeled after spraying.
上記工程（２）においては、その噴霧量は特に限定されるものではないが、例えば化粧料層形成面１ｃｍ２に対して０．００２〜０．０８ｇで化粧料層を形成することが好ましい。このような範囲で形成することによって、工程（３）において簡便に乾燥させることができ、また、塗布量が少な過ぎて使用時に化粧料をうまく取ることができない等の問題を生じることもない点で好ましい。
また、原料の配合が異なる複数種類のスラリー状組成物の噴霧を繰り返して行うことによって、多色のサンプルとすることもできる。
In the step (2), the spray amount is not particularly limited, but it is preferable to form the cosmetic layer with 0.002 to 0.08 g with respect to 1 cm 2 of the cosmetic layer forming surface, for example. By forming in such a range, it can be easily dried in the step (3), and there is no problem that the amount of coating is too small to take off the cosmetics when used. Is preferable.
Moreover, it can also be set as a multicolor sample by repeating and spraying several types of slurry-like compositions from which the mixing | blending of a raw material differs.
上記工程（２）によって化粧料層を形成した後に、工程（３）によって乾燥を行うことにより、本発明のシート状化粧料は完成する。上記工程（３）における乾燥によって、揮発性溶剤（Ｃ）は揮発する。
上記工程（３）の乾燥条件等は特に限定されず、例えば、一昼夜の自然乾燥や４０〜８０℃の乾燥機中での３〜１０時間での乾燥という条件等を挙げることができる。
After forming the cosmetic layer by the step (2), the sheet-like cosmetic of the present invention is completed by drying by the step (3). The volatile solvent (C) is volatilized by drying in the step (3).
The drying conditions and the like in the above step (3) are not particularly limited, and examples thereof include conditions such as natural drying all day and night and drying in a dryer at 40 to 80 ° C. for 3 to 10 hours.
本発明においては、上記工程（２）を行った後、工程（３）を行うまでの間にはプレスを行わないことが好ましい。プレスを行うことなく乾燥させることによって、水溶性高分子によって得られた感触を変化させることがない、ひび割れや剥がれを生じない、工程が減ることによってコストダウンを得ることができる等の利点を有するものである。
本発明は、上述したような化粧料の製造方法でもある。
In the present invention, it is preferable not to perform pressing after performing the above step (2) until performing the step (3). By drying without pressing, there is an advantage that the touch obtained by the water-soluble polymer is not changed, cracking or peeling does not occur, and the cost can be reduced by reducing the number of processes. Is.
The present invention is also a method for producing a cosmetic as described above.
次に、本発明を実施例及び比較例を挙げてさらに詳しく説明するが、本発明はこれら実施例に限定されるものではない。尚、配合量はすべて質量％である。 EXAMPLES Next, although an Example and a comparative example are given and this invention is demonstrated in more detail, this invention is not limited to these Examples. In addition, all compounding quantities are the mass%.
（実施例１〜５、比較例１〜２）
表１に示すアイシャドウを下記の方法により製造した。
(Examples 1-5, Comparative Examples 1-2)
Eye shadows shown in Table 1 were produced by the following method.
（アイシャドウの製造方法）
（１）粘結剤（Ｂ）と揮発性溶剤（Ｃ）とを混合し、粘結剤（Ｂ）を完全に溶解させた。
（２）上記（１）にＡ成分、Ｄ成分を混合し、よく攪拌しスラリー状とする。
（３）得られたスラリー状組成物を、表面加工した厚手の紙上に通常の噴霧装置によって噴霧して、化粧料層を形成した。
（４）室温で一昼夜放置することで、乾燥を行った。
(Eye shadow manufacturing method)
(1) The binder (B) and the volatile solvent (C) were mixed to completely dissolve the binder (B).
(2) A component and D component are mixed with said (1), and it stirs well and makes it a slurry form.
(3) The obtained slurry-like composition was sprayed onto a thick surface-treated thick paper with a normal spraying device to form a cosmetic layer.
(4) Drying was performed by leaving it to stand overnight at room temperature.
得られた化粧料について、以下の基準に基づいて評価を行った。
（感触）
化粧品評価専門パネル２０名に実施例及び比較例の化粧料を使用してもらい、以下の基準に従って５段階評価した。なお、評価において対比の対象となる本製品は、各実施例それぞれについて、同様の組成を用いて通常の化粧品容器にスラリーを充填する湿式製法によって得たアイシャドウである。
（評価基準）
評価結果 ： 評点
本製品と全く同じ：５点
本製品とかなり近い：４点
本製品と近い：３点
本製品と異なる：２点
本製品と大きく異なる：１点
The obtained cosmetic was evaluated based on the following criteria.
(Feel)
20 cosmetic cosmetic evaluation panels were asked to use the cosmetics of the examples and comparative examples, and five levels were evaluated according to the following criteria. The product to be compared in the evaluation is an eye shadow obtained by a wet manufacturing method in which a normal cosmetic container is filled with slurry using the same composition for each example.
(Evaluation criteria)
Evaluation results: Scores Same as this product: 5 points Very close to this product: 4 points Close to this product: 3 points Different from this product: 2 points
（付着性）
化粧料毎に評点を付し、更に全パネルの評点の平均点を以下の４段階の判断基準に従って判定した。
（評価基準）
評価結果 ： 評点
非常に良好 ： ５点
良好 ： ４点
普通 ：３点
やや不良 ： ２点
不良 ： １点
（判定基準）
評点の平均点 ： 判定
４．５以上 ： ◎
３．５以上〜４．５未満 ： ○
１．５以上〜３．５未満 ： △
１．５未満 ：×
(Adhesiveness)
A score was assigned to each cosmetic, and the average score of all panels was determined according to the following four criteria.
(Evaluation criteria)
Evaluation result: Score very good: 5 points good: 4 points Normal: 3 points Somewhat bad: 2 points bad: 1 point (Criteria)
Average score: Judgment 4.5 or higher: ◎
3.5 or more and less than 4.5: ○
1.5 or more and less than 3.5: △
Less than 1.5: ×
（外観）
実施例及び比較例の化粧料をそれぞれ１０個用意し、シート状に収容した状態で、ひび割れの状態および３０ｃｍの高さから塩ビ板上に垂直落下させ、落下後の中味表面状態を目視にて以下の４段階の判定基準に従って判定した。
（判定基準）
１０個全てひび割れ、剥がれがない ： ◎
１０個中９個ひび割れ、剥がれがない ： ○
１０個中２〜５個のひび割れ、剥がれがある : △
１０個中６〜１０個のひび割れ、剥がれがある ： ×
(appearance)
10 cosmetics of each of the examples and comparative examples were prepared, and in the state of being accommodated in a sheet shape, dropped vertically on a PVC plate from a cracked state and a height of 30 cm, and the contents surface state after dropping was visually observed. The determination was made according to the following four criteria.
(Criteria)
All 10 pieces are not cracked or peeled: ◎
9 out of 10 cracks, no peeling: ○
There are 2-5 cracks / peeling out of 10: △
There are 6 to 10 of 10 cracks and peeling: ×
（生産性）
実施例及び比較例の化粧品原料、粘結剤（Ｂ）及び揮発性溶剤（Ｃ）を混合、噴霧を行った際の生産性について、以下の４段階の判断基準に従って判定した。
（判定基準）
特に問題なし ： ◎
細かな設定を行えば問題なし ： ○
混合・噴霧は可能だが効率が悪い : △
混合もしくは噴霧が不可 ： ×
(productivity)
The productivity when the cosmetic raw materials, the binder (B), and the volatile solvent (C) of Examples and Comparative Examples were mixed and sprayed was determined according to the following four criteria.
(Criteria)
No problem: ◎
No problem if detailed settings are made: ○
Mixing / spraying is possible but inefficient: △
Cannot be mixed or sprayed: ×
表１の結果から、本発明の化粧料は、感触、付着性、外観、生産性のすべてにおいて優れた性能を有する化粧料であることが明らかである。 From the results of Table 1, it is clear that the cosmetic of the present invention is a cosmetic having excellent performance in all of touch, adhesion, appearance, and productivity.
本発明の化粧料は、柔らかな感触を有することから、粉末含有化粧料についてのサンプルや使い切りタイプとしてのシート状化粧料等として使用することができる。 Since the cosmetic of the present invention has a soft touch, it can be used as a sample for a powder-containing cosmetic, a sheet-like cosmetic as a single-use type, and the like.
Claims (3)
化粧料原料は、少なくとも一部が粉体成分（Ａ）及び油性成分（Ｄ）であり、
粘結剤（Ｂ）は、ポリビニルピロリドンであり、
粘結剤（Ｂ）は、化粧品原料１００質量部に対して５質量部以下であり、
揮発性溶剤（Ｃ）は、軽質流動イソパラフィン及び／又は水であり、
化粧料層形成面１ｃｍ２に対して０．００２〜０．０８ｇで化粧料層が形成されたものであることを特徴とするシート状化粧料の製造方法。 A step (1) of mixing a cosmetic raw material, a binder (B) and a volatile solvent (C) to form a slurry, and spraying the slurry-like composition obtained by the step (1) onto the sheet-like substrate. Step (2), and a step (3) for drying the sheet having the cosmetic layer obtained by the step (2),
The cosmetic raw material is at least partly a powder component (A) and an oil component (D),
The binder (B) is polyvinylpyrrolidone,
The binder (B) is 5 parts by mass or less with respect to 100 parts by mass of the cosmetic raw material,
Volatile solvent (C) is light liquid isoparaffin and / or water,
A method for producing a sheet-like cosmetic, wherein the cosmetic layer is formed at 0.002 to 0.08 g with respect to 1 cm 2 of the cosmetic layer-forming surface.