JP5738295B2 - 吸水性ポリマー粒子 - Google Patents
吸水性ポリマー粒子 Download PDFInfo
- Publication number
- JP5738295B2 JP5738295B2 JP2012527311A JP2012527311A JP5738295B2 JP 5738295 B2 JP5738295 B2 JP 5738295B2 JP 2012527311 A JP2012527311 A JP 2012527311A JP 2012527311 A JP2012527311 A JP 2012527311A JP 5738295 B2 JP5738295 B2 JP 5738295B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- polymer particles
- liquid
- layer
- absorbing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
A.定義
本明細書に使用されているように、「吸液性組成物」という用語は、主として、体液の取得、輸送、分配および貯蔵を含む吸液性物体の液体処理を担う吸液性物体の構成要素を指す。
吸水性ポリマー粒子は、
a)酸基を保持し、少なくとも部分的に中和されていてもよい少なくとも1つのエチレン不飽和モノマーと、
b)少なくとも1つの架橋剤と、
c)少なくとも1つの開始剤と、
d)場合により、a)に挙げられているモノマーと共重合可能な1つまたは複数のエチレン不飽和モノマーと、
e)場合により1つまたは複数の水溶性ポリマーと、
f)水と
を含むモノマー溶液の液滴を周囲の加熱気相にて重合し、ガスを重合チャンバに並流で流し、重合チャンバを出るガスの温度を130℃以下とし、重合チャンバ内のガス速度を少なくとも0.5m/sとし、多数の穴を有する液滴プレートを使用することによって液滴を生成することによって製造される。
すなわちWO2008/069639A1およびWO2008/086976A1に記載されているシステムを使用して、モノマー溶液を気相に計量導入して液滴を形成する。液滴は、液滴プレートを用いて生成される。
液滴重合によって得られる吸水性ポリマー粒子における残留モノマーを気流の存在下で熱後熱処理することによって除去することができる。温度が比較的高く、残留時間が比較的長いほど残留モノマーを良好に除去することができる。ここで重要なことは、吸水性ポリマー粒子が乾燥しすぎてないことである。過剰に乾燥した粒子の場合は、残留モノマーがわずかしか減少しない。水分含有量が多すぎると、吸水性ポリマー粒子の粘結傾向が増大する。吸水性ポリマー粒子熱後処理時に急速に乾燥しないようにするために、流入するガスが既に水蒸気を含むべきである。
本発明の好適な実施形態において、ポリマー粒子は、特性のさらなる向上のために後架橋される。
特性を向上させるために、吸水性ポリマー粒子を被覆および/または場合により加湿することができる。熱後処理に使用される内部流動床、外部流動床および/または外部ミキサー、および/または独立コーター(ミキサー)を吸水性ポリマー粒子の被覆に使用することができる。さらに、冷却器および/または独立コーター(ミキサー)を後架橋吸水性ポリマー粒子の被覆/加湿に使用することができる。取得挙動を制御し、透過性(SFCまたはGBP)を向上させるための好適な被覆剤は、例えば、水不溶性金属塩等の無機不活性物質、有機ポリマー、カチオン性ポリマーおよび多価金属カチオンである。色安定性を向上させるための好適な被覆剤は、例えば、還元剤および抗酸化剤である。塵埃吸着のための好適な被覆剤は、例えばポリオールである。ポリマー粒子の望ましくない粘結傾向に対する好適な被覆剤は、例えば、Aerosil(登録商標)200などのヒュームドシリカおよびSpan(登録商標)20などの界面活性剤である。好適な被覆剤は、一酢酸アルミニウム、硫酸アルミニウム、乳酸アルミニウム、Brueggolite(登録商標)FF7およびSpan(登録商標)20である。
吸水性ポリマー粒子をさらに選択的に凝集させることができる。凝集を重合後、熱後処理後、後架橋後または被覆後に行うことができる。
本発明の好適な実施形態において、熱後処理および後架橋の工程が1つの処理工程で組み合わされる。当該組合せは、完成品に残留後架橋剤が存在する危険性をもたらさずに非常に反応性の強い後架橋剤を使用することを可能にする。それは、また、低コスト装置の使用を可能にし、さらにはコスト効率が良く、熱劣化による完成品の変色および性能特性の低下を回避する低温で処理を実施することができる。
図2:処理スキーム(外部流動床を用いない)
図3:T_出口測定の構造
図4:液滴化装置ユニットの構造
図5:液滴化装置ユニット(長手方向切断面)
図6:液滴化装置ユニット(断面図)
図7:処理スキーム(外部熱後処理および後架橋)
図8:処理スキーム(外部熱後処理、後架橋および被覆)
1 乾燥ガス導入管
2 乾燥ガス量測定値
3 ガス分配器
4 液滴化装置ユニット
5 並行噴霧乾燥機、円筒部
6 円錐体
7 T_出口測定値
8 塔排ガス管
9 バグハウスフィルタ
10 通風装置
11 急冷ノズル
12 コンデンサカラム、向流冷却
13 熱交換器
14 ポンプ
15 ポンプ
16 水出口
17 通風装置
18 排ガス出口
19 窒素入口
20 熱交換器
21 通風装置
22 熱交換器
23 ノズルによる水蒸気射出
24 水負荷測定値
25 調和内部流動床ガス
26 内部流動床生成物温度測定値
27 内部流動床
28 外部流動床への生成物排出、回転弁
29 外部流動床
30 通風装置
31 バグハウスフィルタへの外部流動床排ガス出口
32 回転弁
33 篩
34 最終生成物
35 濾過空気入口
36 通風装置
37 熱交換器
38 ノズルによる水蒸気射出
39 水負荷測定値
40 調和外部流動床ガス
41 固定ミキサー
42 固定ミキサー
43 開始剤供給物
44 開始剤供給物
45 モノマー供給物
46 微粒子分の再処理への出口
47 T_出口測定値(塔周囲の3つの測定値の平均温度)
48 液滴化装置ユニット
49 開始剤供給物予備混合モノマー
50 噴霧乾燥機塔壁
51 液滴化装置ユニット外管
52 液滴化装置ユニット内管
53 液滴化装置カセット
54 テフロンブロック
55 弁
56 開始剤供給物予備混合モノマー導入管コネクタ
57 液滴プレート
58 計数プレート
59 温度制御水用流路
60 モノマー溶液用死容積自由流路
61 液滴化カセットステンレス鋼ブロック
62 外部熱後処理
63 任意の被覆剤供給物
64 後架橋剤供給物
65 熱乾燥機(後架橋)
66 冷却器
67 任意の被覆剤/水供給物
68 コーター
69 被覆剤/水供給物
本発明は、2つ以上の空洞を有する吸水性ポリマー粒子であって、空洞が、好ましくは1から50μm、より好ましくは2から30μm、さらにより好ましくは5から20μm、最も好ましくは7から15μmの内径を有し、残りの粒子が内部に可視の空洞を有さない吸水性ポリマー粒子を提供する。1μm未満の径を有する空洞は、不可視の空洞と見なされる。
SPHT=4πA/U2
[式中、
Aは断面積であり、
Uはポリマー粒子の断面円周である]で定義される。平均球形度は、体積平均球形度である。
流体吸収性物体は、
(A)上部液体透過層と、
(B)下部液体不透過層と、
(C)5から90質量%の繊維状材料および10から95質量%の吸水性ポリマー粒子、
好ましくは20から80質量%の繊維状材料および20から80質量%の吸水性ポリマー粒子、
より好ましくは30から75質量%の繊維状材料および25から70質量%の吸水性ポリマー粒子、
最も好ましくは40から70質量%の繊維状材料および30から60質量%の吸水性ポリマー粒子を含む、(A)と(B)の間の吸液性コアと、
(D)80から100質量%の繊維状材料および0から20質量%の吸水性ポリマー粒子、
好ましくは85から99.9質量%の繊維状材料および0.01から15質量%の吸水性ポリマー粒子、
より好ましくは90から99.5質量%の繊維状材料および0.5から10質量%の吸水性ポリマー粒子、
最も好ましくは95から99質量%の繊維状材料および1から5質量%の吸水性ポリマー粒子を含む、(A)と(B)の間の任意の取得−分配層と、
(E)(C)の真上および/または真下に配置された任意の組織層と、
(F)他の任意の構成要素と
を含む。
液体透過層(A)は、皮膚と直接接触する層である。したがって、液体透過層は、好ましくは、温順で、ソフト感があり、消費者の皮膚に刺激を与えない。一般に、「液体透過性」という用語は、液体、すなわち尿、月経および/または膣液などの体液がその肉厚を容易に透過することを可能にするものと理解される。液体透過層の基本的機能は、着用者から吸液性コアへの体液の取得および輸送である。典型的には、液体透過層は、不織布材料、フィルムまたはそれらの組合せなどの当該技術分野で既知の任意の材料から形成される。好適な液体透過層(A)は、従来の合成もしくは半合成繊維、またはポリエステル、ポリオレフィン、レーヨンもしくは天然繊維の複合繊維もしくはフィルム、またはそれらの任意の組合せからなる。不織布材料の場合は、繊維は、一般に、ポリアクリレートなどの結合剤によって結合される。また、液体透過層は、弾性組成物を含むことで、一方向または二方向に伸縮することを可能にする弾性特性を示すことができる。
液体不透過層(B)は、吸液性コアによって吸収および保持された浸出液が、例えばベッドシート、パンツ、パジャマおよび下着のような、吸液性物体と接触する物体を濡らすことを防止する。したがって、液体不透過層(B)は、織布もしくは不織布材料、ポリエチレンもしくはポリプロピレンの熱可塑性フィルムなどのポリマーフィルム、または膜被覆不織布材料などの複合材料を含むことができる。
吸液性コア(C)は、上部液体透過層(A)と下部液体不透過層(B)との間に配置される。蒸気透過性、柔軟性および厚さなどの要件が満たされるのであれば、好適な吸液性コア(C)を当該技術分野で既知の吸液性コアシステムのいずれかから選択することができる。好適な吸液性コアは、その主な機能が、排出体液を取得、輸送、分配、吸収、貯蔵および保持することである任意の吸液性組成物を指す。
2.液体貯蔵層
3.任意の散粉層
吸液性コアの保全性を高めるために、コアにカバーを設ける。このカバーは、吸液性コアの頂部および/または底部に存在してもよい。さらに、このカバーは、吸液性コア全体を一枚の材料で包含することで、ラップとして機能することができる。ラッピングは、完全ラップ、部分ラップまたはC型ラップで可能である。
吸液性コアに含まれる吸液性組成物は、繊維状材料および吸水性ポリマー粒子を含む。
吸収性コアに含められる任意の構成要素は、隣接する散粉層である。散粉層は、繊維層であり、吸収性コアの頂部および/または底部に配置されてもよい。典型的には、散粉層は、貯蔵層の下に位置する。この下位層は、吸液性コアの製造過程を通じて付着吸水性ポリマー粒子に対する担体として機能するため、散粉層と称する。吸水性ポリマー材料がマクロ構造体、フィルムまたはフレークの形であれば、散粉層の挿入は必要ない。液滴重合から誘導された吸水性ポリマー粒子の場合は、粒子は、エッジのない滑らかな表面を有する。この場合も、散粉層を吸液性コアに加える必要はない。一方、大きな利点として、散粉層は、吸上性能などの追加的ないくつかの液体処理特性を提供し、液体不透過層(B)のピンホールまたはポックマークの発生を抑制することができる。
任意の取得−分配層(D)は、上層(A)と吸液性コア(C)との間に位置し、好ましくは、排出体液を効率的に取得し、それらを吸液性組成物の他の領域、または体液が固定および貯蔵される他の層に輸送および分配させるように構成される。したがって、上層は、排出液を、吸液性コアに分配させるための取得−分配層(D)に輸送する。
任意の組織層は、(C)の真上および/または真下に配置される。
1.脚カフ
典型的な脚カフは、繊維および不織布材料を同時に形成する直接押出法、または後の時点で不織布材料に積層することができる前形成繊維の積層法によって形成することができる不織布材料を含む。直接押出法の例としては、スパンボンディング、メルトブローン、溶剤紡糸、電界紡糸およびそれらの組合せが挙げられる。積層法の例としては、湿式積層および乾式積層(例えば空気積層、カーディング)法が挙げられる。上記方法の組合せとしては、スパンボンド−メルトブローン−スパンボンド(sms)、スパンボンド−メルトブローン−メルトブローン−スパンボンド(smms)、スパンボンド−カーディング(sc)、スパンボンド−空気積層(sa)、メルトブローン−空気積層(ma)およびそれらの組合せが挙げられる。直接押出を含む組合せを同じ時点または後の時点で組み合わせることができる。上記例において、1つまたは複数の個々の層をそれぞれの方法によって製造することができる。したがって、「sms」は、三層不織布材料を指し、「smsms」または「ssmms」は、五層不織布材料を指す。通常、小文字(sms)は個々の層を表すのに対して、大文字(SMS)は、同様の隣接層の集合体を表す。
弾性体は、着用者の体、例えばウエストおよび脚付近に吸液性物体をしっかりと保持し、柔軟に密封して包含性および適合性を向上させるために使用される。脚弾性体は、外層と内層または吸液性物体との間、あるいは外カバーとボディーサイドライナーとの間に配置される。好適な弾性体は、熱可塑性ポリウレタンのシート、条体もしくは糸状体、エラストマー材料、ポリ(エーテル−アミド)ブロックコポリマー、熱可塑性ゴム、スチレン−ブタジエンコポリマー、シリコンゴム、天然ゴム、合成ゴム、スチレンイソプレンコポリマー、スチレンエチレンブチレンコポリマー、ナイロンコポリマー、セグメント化ポリウレタンを含むスパンデックス繊維および/またはエチレン−酢酸ビニルコポリマーを含む。弾性体を延伸後に基板に固定するか、または延伸された基板に固定することができる。そうでなければ、弾性体を基板に固定し、次いで例えば加熱によって弾性化または収縮させることができる。
密封システムは、テープタブ、ランディングゾーン、エラストマー、プルアップおよびベルトシステムを含む。
本発明は、さらに、吸液性物体を提供するための以上に挙げた構成要素および層、フィルム、組織または基板の接合に関する。少なくとも2つ、好ましくは全ての層、フィルム、シート、組織または基板を接合する。
以下の実施形態1において、本発明の1つの好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンド層を含む上部液体透過層(三部表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)全吸収性コア質量に基づいて10から50質量%の吸水性ポリマー粒子を含み、
1.全毛羽量の約50%を含む木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均一な上部コア毛羽層、
2.吸水性ポリマー粒子を含む吸液性層であって、当該構造のための好適な吸水性ポリマー粒子が、少なくとも30g/gの遠心保持能力(CRC)を有する吸液性層、
3.全毛羽量の約50%を含み、散粉層として機能する木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均一な下部コア毛羽層
をこの順に含む多層液体貯蔵部を含む(A)と(B)の間の単一吸液性コアと、
(D)30から80gsmの坪量を有する(A)と(C)の間の通気結合取得−分配層であって、取得−分配層が長方形であり、約150から約250cm2のサイズを有する吸液性コアより小さい通気結合取得−分配層とを含む。
吸液性コアは、各層が均一な長方形サイズを有する多層単一コアシステムからなる。(A)と(B)の間の層状吸液性コアは、多層系の親水性繊維(セルロース繊維、毛羽パルプ繊維)を含む。全毛羽パルプ質量は20.45gであり、上部コア(1)と下部コア(3)との間で等分される。吸液性コアの密度は、前部全体平均が0.18g/cm3であり、割込み帯域が0.17g/cm3であり、後部全体平均が0.15g/cm3である。吸液性コアの坪量は、前部全体平均が802.75gsmであり、割込み帯域が825.94gsmであり、後部全体平均が766.14gsmである。
CRC 33.0g/g
SFC 12×10-7cm3s/g
AUHL 24.6g/g
水分含有量 6.0質量%
吸液性コアの寸法:長さ37.5cm;幅:10.0cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:3脚弾性体および1カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および4.6cmの高さを有する合成繊維による脚カフ。
・18.3cm×4.0cmの寸法のランディングゾーンを有する機械的密封システムおよび3.4cm×1.0cmのフレキシバンド密封テープ;3.4cm×1.4cmのフック固定テープに装着。
・14.6cm×4.5cmの寸法を有する、製品の後部に配置される伸縮性ウエストバンドも含められる。
以下の実施形態2において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)熱結合層を含む上部液体透過層(三部表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)全吸収性コア質量に基づいて40から80質量%の吸水性ポリマー粒子を含み、
1.全毛羽量の約50%を含む木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均一な上部コア毛羽層、
2.吸水性ポリマー粒子を含む吸液性層であって、当該構造のための好適な吸水性ポリマー粒子が、少なくとも20×10-7cm3s/gの生理食塩水通液性(SFC)を有する吸液性層、
3.全毛羽量の約50%を含み、散粉層として機能する木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均一な下部コア毛羽層
をこの順に含む多層液体貯蔵部を含む(A)と(B)の間の単一吸液性コアと、
(D)40から80gsmの坪量を有する(A)と(C)の間の通気結合取得−分配層であって、取得−分配層が長方形であり、約150から約250cm2のサイズを有する吸液性コアより小さい通気結合取得−分配層とを含む。
吸液性コアは、各層が均一な長方形サイズを有する多層単一コアシステムからなる。(A)と(B)の間の層状吸液性コアは、多層系の親水性繊維(セルロース繊維、毛羽パルプ繊維)を含む。全毛羽パルプ質量は12gであり、上部コア(1)と下部コア(3)との間で等分される。吸液性コアの密度は、前部全体平均が0.19g/cm3であり、割込み帯域が0.20g/cm3であり、後部全体平均が0.18g/cm3である。吸液性コアの坪量は、前部全体平均が989gsmであり、割込み帯域が1101gsmであり、後部全体平均が664gsmである。吸液性コアの厚さは、4.5mmの平均値を有する。
CRC 29.2g/g
SFC 40×10-7cm3s/g
AUHL 19.6g/g
水分含有量 12.6質量%
渦時間 56秒
GBP 34ダルシー
吸液性コアの寸法:長さ38cm;幅:10cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:3脚弾性体および1カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および4.6cmの高さを有する合成繊維による脚カフ。
・18.3cm×4.0cmの寸法のランディングゾーンを有する機械的密封システムおよび3.4cm×1.0cmのフレキシバンド密封テープ;3.4cm×1.4cmのフック固定テープに装着。
・14.6cm×4.5cmの寸法を有する製品の後部に配置される伸縮性ウエストバンドも含められる。
以下の実施形態3において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンドウェブを含む上部液体透過層(三部表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)木材パルプ繊維(セルロース繊維)と10から50質量%の均一に分配された吸水性ポリマー粒子との混合物を吸液性コア(C)内に含む(A)と(B)の間の単一吸液性コアであって、当該構造のための好適な吸水性ポリマー粒子が少なくとも30g/gの遠心保持能力(CRC)を有し、吸液性コアが、液体不透過層(B)に隣接し、上記吸液性コアの下に位置する散粉層をさらに含み、散粉層が毛羽(セルロース繊維)のみを含む単一吸液性コアと、
(D)30から80gsmの坪量を有する(A)と(C)の間の通気結合取得−分配層であって、取得−分配層が長方形であり、約150から約250cm2のサイズを有する吸液性コアより小さい通気結合取得−分配層とを含む。
吸液性コアは、木材パルプ繊維(セルロース繊維)と37.11質量%の均一に分配された吸水性ポリマー粒子との混合物を、均一な長方形サイズを有する吸液性コア(C)内に含む(A)と(B)の間の単一吸液性コアからなる。吸液性コア内の吸水性ポリマー粒子の量は11.38gである。全毛羽パルプ質量は19.25gである。吸液性コアの密度は、前部全体平均が0.22g/cm3であり、割込み帯域が0.18g/cm3であり、後部全体平均が0.18g/cm3である。吸液性コアの坪量は、前部全体平均が914.18gsmであり、割込み帯域が925.47gsmであり、後部全体平均が886.32gsmである。
CRC 32.0g/g
SFC 20×10-7cm3s/g
AUHL 24.0g/g
抽出分 1.7質量%
残留モノマー 866ppm
水分含有量 5.8質量%
ESR 0.31g/gs
吸液性コアの寸法:長さ39.2cm;幅:10.0cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:3脚弾性体および1カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および3.0cmの高さを有する合成繊維による脚カフ。
・18.9cm×3.8cmの寸法のランディングゾーンを有する機械的密封システムおよび1.6cm×3.4cmのフレキシバンド密封テープ;1.3cm×3.4cmのフック固定テープに装着。
・10.8cm×2.8cmの寸法を有する、製品の後部に配置される伸縮性ウエストバンドも含められる。
以下の実施形態4において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンドウェブを含む上部液体透過層(三部表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)木材パルプ繊維(セルロース繊維)と40から80質量%の均一に分配された吸水性ポリマー粒子との混合物を吸液性コア内に含む(A)と(B)の間の単一吸液性コアであって、当該構造のための好適な吸水性ポリマー粒子が少なくとも20×10-7cm3s/gの生理食塩水通液性(SFC)を有する単一吸液性コアと、
(D)40から80gsmの坪量を有する上部樹脂結合層を含む(A)と(C)の間の2つの取得−分配層の系であって、上部取得−分配層が、約150から約250cm2のサイズを有する長方形であり、下部取得−分配層が、40から80gsmの坪量および約100から約300cm2のサイズを有する(例えばBuckeye Technologies Inc.の)変性セルロース繊維を含み、両取得−分配層が、吸液性コアより小さい系とを含む。
吸液性コアは、木材パルプ繊維(セルロース繊維)と67.12質量%の均一に分配された吸水性ポリマー粒子との混合物を、均一な長方形サイズを有する吸液性コア(C)内に含む(A)と(B)の間の単一吸液性コアからなる。吸液性コアは、10gsmの坪量を有するスパンボンド材料でラップすることによって封入される。吸液性コア内の吸水性ポリマー粒子の量は12.18gである。全毛羽パルプ質量は5.95gである。吸液性コアの密度は、前部全体平均が0.19g/cm3であり、割込み帯域が0.18g/cm3であり、後部全体平均が0.18g/cm3である。吸液性コアの坪量は、前部全体平均が965.79gsmであり、割込み帯域が913.38gsmであり、後部全体平均が658.85gsmである。
CRC 31.5g/g
SFC 49×10-7cm3s/g
AUHL 24.0g/g
水分含有量 6.2質量%
渦時間 65秒
吸液性コアの寸法:長さ40.0cm;幅:10.0cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:3脚弾性体および2カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および3.3cmの高さを有する合成繊維による脚カフ。
・19.8cm×5.0cmの寸法のランディングゾーンを有する機械的密封システム、ならびに3.5cm×1.5cmの感圧接着帯域および3.5cm×1.2cmの機械的フックからなる3.5cm×2.7cmのフレキシバンド密封テープ。
実施形態5
以下の実施形態5において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンド層を含む上部液体透過層(三部表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)一次コアとしての木材パルプ繊維(セルロース繊維)と吸水性ポリマー粒子との均一混合物、および層状二次吸液性コアを含む(A)と(B)の間の二重吸液性コアであって、全二重吸液性コアが、
1.一次吸収性コア質量に基づいて10から50質量%の吸水性ポリマー粒子を含む木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均質一次コアであって、一次コアが全毛羽量の約30%を含み、当該構造のための好適な吸水性ポリマー粒子が、少なくとも30g/gの遠心保持能力(CRC)を有する均質一次コア、
2.木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの二次コア上部毛羽層であって、二次コア上部層が全毛羽量の約35%を含む二次コア上部毛羽層、
3.二次吸収性コア質量に基づいて10から50質量%の吸水性ポリマー粒子を含む吸液性層であって、当該構造のための好適な吸水性ポリマー粒子が、少なくとも30g/gの遠心保持能力(CRC)を有する吸液性層、
4.散粉層として作用する木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの二次コア下部毛羽層であって、下部コアが全毛羽量の約35%を含む二次コア下部毛羽層
をこの順に含む二重吸液性コアと、
(D)30から80gsmの坪量を有する(A)と(C)の間の通気結合取得−分配層であって、取得−分配層が長方形であり、約150から約250cm2のサイズを有する一次吸液性コアより小さい通気結合取得−分配層とを含む。
全吸液性コアは、それぞれがほぼ均一な長方形サイズを有する一次コアおよび二次コアの二重コアシステムを含む。一次コアは二次コアより小さく、二次コアの前部遠端から6cmの位置および二次コアの後部遠端から10cmの位置に配置され、幅が9cmである。(A)と(B)の間の一次吸液性コアは、木材パルプ繊維の親水性繊維状マトリックスと25質量%の吸水性ポリマー粒子との均一混合物を含む。一次コアは、8gの全質量を有する。二次コアは、木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスおよび30質量%の吸水性ポリマー粒子の多層系である。二次吸液性コア内の吸水性ポリマー粒子の量は6.0gである。吸液性コアの密度は、前部全体平均が0.15g/cm3であり、割込み帯域が0.19g/cm3であり、後部全体平均が0.18g/cm3である。吸液性コアの坪量は、前部全体平均が790.63gsmであり、割込み帯域が1121.38gsmであり、後部全体平均が976.83gsmである。
CRC 35.5g/g
SFC 16×10-7cm3s/g
AUHL 26.2g/g
水分含有量 1.8質量%
二次吸液性コアの寸法:長さ:40.8cm;前部幅:10.5cm;股幅:9.3cm;後部幅:10.3cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:3脚弾性体および2カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および3.8cmの高さを有する合成繊維による脚カフ。
・22.0cm×4.0cmの寸法のランディングゾーンを有する機械的密封システムおよび3.4cm×1.5cmのフレキシバンド密封テープ;3.4cm×1.4cmフック固定テープに装着。
以下の実施形態6において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンド層を含む上部液体透過層(三部表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)一次コアとしての木材パルプ繊維(セルロース繊維)と吸水性ポリマー粒子との均一混合物、および層状二次吸液性コアを含む(A)と(B)の間の二重吸液性コアであって、全二重吸液性コアが、
1.一次吸収性コア質量に基づいて40から80質量%の吸水性ポリマー粒子を含む木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均質一次コアであって、一次コアが全毛羽量の約50%を含み、当該構造のための好適な吸水性ポリマー粒子が、少なくとも20×10-7cm3s/gの生理食塩水通液性(SFC)を有する均質一次コア、
2.木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの二次コア上部毛羽層であって、二次コア上部層が全毛羽量の約25%を含む二次コア上部毛羽層、
3.二次吸収性コア質量に基づいて40から80質量%の吸水性ポリマー粒子を含む吸液性層であって、当該構造のための好適な吸水性ポリマー粒子が、少なくとも20×10-7cm3s/gの生理食塩水通液性(SFC)を有する吸液性層、
4.散粉層として作用する木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの二次コア下部毛羽層であって、下部コアが全毛羽量の約25%を含む二次コア下部毛羽層
をこの順に含む二重吸液性コアと、
(D)40から80gsmの坪量を有する(A)と(C)の間の通気結合取得−分配層であって、取得−分配層が長方形であり、約150から約250cm2のサイズを有する一次吸液性コアより小さい通気結合取得−分配層とを含む。
全吸液性コアは、それぞれがほぼ均一な長方形サイズを有する一次コアおよび二次コアの二重コアシステムを含む。一次コアは二次コアより小さく、二次コアの前部遠端から6cmの位置および二次コアの後部遠端から10cmの位置に配置され、幅が9cmである。(A)と(B)の間の一次吸液性コアは、木材パルプ繊維の親水性繊維状マトリックスと50質量%の吸水性ポリマー粒子との均一混合物を含む。一次コアは、8gの全質量を有する。二次コアは、木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスおよび50質量%の吸水性ポリマー粒子の多層系である。二次吸液性コア内の吸水性ポリマー粒子の量は10.0gである。吸液性コアの密度は、前部全体平均が0.19g/cm3であり、割込み帯域が0.19g/cm3であり、後部全体平均が0.18g/cm3である。吸液性コアの坪量は、前部全体平均が813.46gsmであり、割込み帯域が1209.15gsmであり、後部全体平均が986.27gsmである。
CRC 33.6g/g
SFC 45×10-7cm3s/g
AUHL 18.7g/g
水分含有量 5.5質量%
渦時間 57秒
GBP 33ダルシー
二次吸液性コアの寸法:長さ:40.8cm;前部幅:10.0cm;股幅:9.0cm;後部幅:10.0cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:3脚弾性体および2カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および3.8cmの高さを有する合成繊維による脚カフ。
・22.0cm×4.0cmの寸法のランディングゾーンを有する機械的密封システムおよび3.4cm×1.5cmのフレキシバンド密封テープ;3.4cm×1.4cmフック固定テープに装着。
以下の実施形態7において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンド層を含む上部液体透過層(三部表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)一次コアおよび二次吸液性コアのそれぞれについて木材パルプ繊維(セルロース繊維)とポリマー粒子との均一混合物を含む(A)と(B)の間の二重吸液性コアであって、全二重吸液性コアが、
1.一次吸収性コア質量に基づいて10から50質量%の吸水性ポリマー粒子を含む木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均質一次コアであって、一次コアが全毛羽量の約30%を含み、当該構造のための好適な吸水性ポリマー粒子が、少なくとも30g/gの遠心保持能力(CRC)を有する均質一次コア、
2.二次吸収性コア質量に基づいて10から50質量%の吸水性ポリマー粒子を含む木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均質二次コアであって、二次コアが全毛羽量の約70%を含み、当該構造のための好適な吸水性ポリマー粒子が、少なくとも30g/gの遠心保持能力(CRC)を有する均質二次コア
を含む二重吸液性コアと、
(D)30から80gsmの坪量を有する通気結合取得−分配層であって、取得−分配層が長方形であり、約150から約250cm2のサイズを有する一次吸液性コアより小さい通気結合取得−分配層とを含む。
全吸液性コアは、それぞれがほぼ均一な長方形サイズを有する一次コアおよび二次コアの二重コアシステムを含む。一次コアは二次コアより小さく、二次コアの前部遠端から6cmの位置および二次コアの後部遠端から10cmの位置に配置され、幅が9cmである。(A)と二次吸液性コアの間の一次吸液性コアは、木材パルプ繊維の親水性繊維状マトリックスと25質量%の吸水性ポリマー粒子との均一混合物を含む。一次コアは、8gの全質量を有する。一次コアと(B)の間の二次コアは、木材パルプ繊維の親水性繊維状マトリックスと30質量%の吸水性ポリマー粒子との均一混合物を含む。二次吸液性コア内の吸水性ポリマー粒子の量は6.0gである。二次コアは、20gの全質量を有する。吸液性コアの密度は、前部全体平均が0.15g/cm3であり、割込み帯域が0.19g/cm3であり、後部全体平均が0.18g/cm3である。吸液性コアの坪量は、前部全体平均が790.63gsmであり、割込み帯域が1121.38gsmであり、後部全体平均が976.83gsmである。
CRC 31.5g/g
SFC 35×10-7cm3s/g
AUHL 22.9g/g
水分含有量 7.9質量%
渦時間 63秒
GBP 34ダルシー
二次吸液性コアの寸法:長さ:40.8cm;前部幅:10.5cm;股幅:9.3cm;後部幅:10.3cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:3脚弾性体および2カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および3.8cmの高さを有する合成繊維による脚カフ。
・22.0cm×4.0cmの寸法のランディングゾーンを有する機械的密封システムおよび3.4cm×1.5cmのフレキシバンド密封テープ;3.4cm×1.4cmフック固定テープに装着。
以下の実施形態8において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンド層を含む上部液体透過層(三部表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)一次コアおよび二次吸液性コアのそれぞれについて木材パルプ繊維(セルロース繊維)とポリマー粒子との均一混合物を含む(A)と(B)の間の二重吸液性コアであって、全二重吸液性コアが、
1.一次吸収性コア質量に基づいて40から80質量%の吸水性ポリマー粒子を含む木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均質一次コアであって、一次コアが全毛羽量の約50%を含み、当該構造のための好適な吸水性ポリマー粒子が、少なくとも20×10-7cm3s/gの生理食塩水通液性(SFC)を有する均質一次コア、
2.二次吸収性コア質量に基づいて40から70質量%の吸水性ポリマー粒子を含む木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均質二次コアであって、二次コアが全毛羽量の約50%を含み、当該構造のための好適な吸水性ポリマー粒子が、少なくとも20×10-7cm3s/gの生理食塩水通液性(SFC)を有する均質二次コア
を含む全二重吸液性コアと、
(D)40から80gsmの坪量を有する(A)と(C)の間の通気結合取得−分配層であって、取得−分配層が長方形であり、約150から約250cm2のサイズを有する一次吸液性コアより小さい通気結合取得−分配層とを含む。
全吸液性コアは、それぞれがほぼ均一な長方形サイズを有する一次コアおよび二次コアの二重コアシステムを含む。一次コアは二次コアより小さく、二次コアの前部遠端から6cmの位置および二次コアの後部遠端から10cmの位置に配置され、幅が9cmである。(A)と二次吸液性コアの間の一次吸液性コアは、木材パルプ繊維の親水性繊維状マトリックスと28.6質量%の吸水性ポリマー粒子との均一混合物を含む。一次コアは、8gの全質量を有する。一次コアと(B)の間の二次コアは、木材パルプ繊維の親水性繊維状マトリックスと71.4質量%の吸水性ポリマー粒子との均一混合物を含む。二次吸液性コア内の吸水性ポリマー粒子の量は10.0gである。二次コアは、20gの全質量を有する。吸液性コアの密度は、前部全体平均が0.15g/cm3であり、割込み帯域が0.19g/cm3であり、後部全体平均が0.18g/cm3である。吸液性コアの坪量は、前部全体平均が790.63gsmであり、割込み帯域が1121.38gsmであり、後部全体平均が976.83gsmである。
CRC 31.5g/g
SFC 70×10-7cm3s/g
AUHL 20.4g/g
水分含有量 7.6質量%
渦時間 59秒
GBP 42ダルシー
吸液性コアの寸法:長さ:40.8cm;前部幅:10.5cm;股幅:9.3cm;後部幅:10.3cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:3脚弾性体および2カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および3.8cmの高さを有する合成繊維による脚カフ。
・22.0cm×4.0cmの寸法のランディングゾーンを有する機械的密封システムおよび3.4cm×1.5cmのフレキシバンド密封テープ;3.4cm×1.4cmフック固定テープに装着。
以下の実施形態9(パンティーライナー)において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンド層を含む上部液体透過層(三部表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)全吸収性コア質量に基づいて10から50質量%の吸水性ポリマー粒子を含み、
1.全毛羽量の約50%を含む木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均一な上部コア毛羽層、
2.吸水性ポリマー粒子を含む吸液性層であって、当該構造のための好適な吸水性ポリマー粒子が、少なくとも30g/gの遠心保持能力(CRC)を有する吸液性層
をこの順に含む多層液体貯蔵部を含む(A)と(B)の間の単一吸液性コアと、
(D)40から80gsmの坪量を有する(A)と(C)の間の通気結合取得−分配層であって、取得−分配層が長方形であり、約150から約250cm2のサイズを有する一次吸液性コアより小さい通気結合取得−分配層とを含む。
吸液性コアは、各層が均一な長方形サイズを有する二層単一コアシステムからなる。(A)と(B)の間の層状吸液性コアは、各層がほぼ均一な長方形サイズを有する二層系の親水性繊維(セルロース繊維、毛羽パルプ繊維)を含む。吸液性コアは、10gsmの坪量を有するスパンボンド材料でラップすることによって封入される。吸液性コアの密度は、前部全体平均が0.16g/cm3であり、割込み帯域が0.14g/cm3であり、後部全体平均が0.16g/cm3である。吸液性コアの坪量は、前部全体平均が598.16gsmであり、割込み帯域が596.94gsmであり、後部全体平均が626.23gsmである。吸液性コアの厚さは、3.8mmの平均値を有する。
CRC 34.0g/g
SFC 22×10-7cm3s/g
AUHL 20.4g/g
水分含有量 5.8質量%
渦時間 62秒
GBP 20ダルシー
吸液性コアの寸法:長さ40.8cm;前部幅:14.2cm;股幅:14.5cm;後部幅:14.1cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:5カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および4.7cmの高さを有する合成繊維による脚カフ。
以下の実施形態10(パンティーライナー)において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンド層を含む上部液体透過層(三部表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)全吸収性コア質量に基づいて40から80質量%の吸水性ポリマー粒子を含み、
1.全毛羽量の約50%を含む木材パルプ繊維(セルロース繊維)の親水性繊維状マトリックスの均一な上部コア毛羽層、
2.吸水性ポリマー粒子を含む吸液性層であって、当該構造のための好適な吸水性ポリマー粒子が、少なくとも20×10-7cm3s/gの生理食塩水通液性(SFC)を有する吸液性層
をこの順に含む多層液体貯蔵部を含む(A)と(B)の間の単一吸液性コアと、
(D)40から80gsmの坪量を有する(A)と(C)の間の通気結合取得−分配層であって、取得−分配層が長方形であり、約150から約250cm2のサイズを有する一次吸液性コアより小さい通気結合取得−分配層とを含む。
吸液性コアは、各層が均一な長方形サイズを有する二層単一コアシステムからなる。(A)と(B)の間の層状吸液性コアは、各層がほぼ均一な長方形サイズを有する二層系の親水性繊維(セルロース繊維、毛羽パルプ繊維)を含む。吸液性コアは、10gsmの坪量を有するスパンボンド材料でラップすることによって封入される。吸液性コアの密度は、前部全体平均が0.16g/cm3であり、割込み帯域が0.14g/cm3であり、後部全体平均が0.16g/cm3である。吸液性コアの坪量は、前部全体平均が598.16gsmであり、割込み帯域が596.94gsmであり、後部全体平均が626.23gsmである。吸液性コアの厚さは、3.8mmの平均値を有する。
CRC 33.6g/g
SFC 46×10-7cm3s/g
AUHL 18.3g/g
水分含有量 5.5質量%
渦時間 58秒
GBP 33ダルシー
吸液性コアの寸法:長さ40.8cm;前部幅:14.2cm;股幅:14.5cm;後部幅:14.1cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:5カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および4.7cmの高さを有する合成繊維による脚カフ。
以下の実施形態11(パンティーライナー)において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンド層を含む上部液体透過層(三部表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)全吸収性コア質量に基づいて55から95質量%の吸水性ポリマー粒子を含み、
1.全毛羽量の約95%を含む親水性合成繊維(繊維状マトリックス)の均一上部コア層、
2.吸水性ポリマー粒子を含む高負荷吸液性層であって、当該構造のための好適な吸水性ポリマー粒子が、少なくとも80×10-7cm3s/gの生理食塩水通液性(SFC)を有する高負荷吸液性層
をこの順に含む多層液体貯蔵部を含む(A)と(B)の間の高負荷単一吸液性コアと、
(D)40から80gsmの坪量を有する通気結合取得−分配層であって、取得−分配層が長方形であり、約150から約250cm2のサイズを有する一次吸液性コアより小さい通気結合取得−分配層とを含む。
吸液性コアは、各層が均一な長方形サイズを有する二層高負荷単一コアシステムからなる。(A)と(B)の間の層状吸液性コアは、各層が長方形サイズを有する二層系の親水性繊維(合成繊維)を含む。吸液性コアは、10gsmの坪量を有するスパンボンド材料でラップすることによって封入される。吸液性コアの密度は、前部全体平均が0.20g/cm3であり、割込み帯域が0.20g/cm3であり、後部全体平均が0.21g/cm3である。吸液性コアの坪量は、前部全体平均が551.51gsmであり、割込み帯域が585.71gsmであり、後部全体平均が569.63gsmである。吸液性コアの厚さは、2.9mmの平均値を有する。
CRC 25.5g/g
SFC 60×10-7cm3s/g
AUHL 22.3g/g
水分含有量 0.2質量%
GBP 120ダルシー
吸液性コアの寸法:長さ40.8cm;前部幅:14.2cm;股幅:14.5cm;後部幅:14.1cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:5カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および4.7cmの高さを有する合成繊維による脚カフ。
・液体不透過層(B)の下側の湿潤度指示薬。
以下の実施形態12(パンティーライナー)において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)熱結合層を含む上部液体透過層(表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)全吸収性コア質量に基づいて55から95質量%の吸水性ポリマー粒子を含み、親水性合成繊維の均一層でラップされた高負荷混合吸液性層を含む液体貯蔵部を含む(A)と(B)の間の高負荷単一吸液性コアであって、前記高負荷吸液性層が吸水性ポリマー粒子を含み、当該構造のための好適な吸水性ポリマー粒子が、少なくとも80×10-7cm3s/gの生理食塩水通液性(SFC)を有し、親水性合成繊維の前記均一ラップが全毛羽量の約95%を含む高負荷単一吸液性コアと、
(D)40から80gsmの坪量を有する(A)と(B)の間の通気結合取得−分配層であって、取得−分配層が長方形であり、約150から約250cm2のサイズを有する一次吸液性コアより小さい通気結合取得−分配層とを含む。
吸液性コアは、均一な長方形サイズを有する高負荷単一コアシステムからなる。(A)と(B)の間の吸液性コアは、親水性合成繊維の均一層にラップされた高負荷吸液性層を含む液体貯蔵部を含む。吸液性コアは、10gsmの坪量を有するスパンボンド材料でC型ラップおよび完全ラップ構成でラップすることによって封入される。吸液性コアの密度は、前部全体平均が0.16g/cm3であり、割込み帯域が0.25g/cm3であり、後部全体平均が0.19g/cm3である。吸液性コアの坪量は、前部全体平均が436.86gsmであり、割込み帯域が707.74gsmであり、後部全体平均が555.73gsmである。吸液性コアの厚さは、3.0mmの平均値を有する。
CRC 27.5g/g
SFC 129×10-7cm3s/g
AUHL 20.3g/g
水分含有量 7.7質量%
渦時間 78秒
GBP 98ダルシー
吸液性コアの寸法:長さ40.8cm;前部幅:14.2cm;股幅:14.5cm;後部幅:14.1cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:5カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および4.7cmの高さを有する合成繊維による脚カフ。
以下の実施形態13において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンド層を含む上部液体透過層(表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)スパンボンド材料でラップされた高負荷吸液性層を含む液体貯蔵部を含む、全吸収性コア質量に基づいて55から95質量%の吸水性ポリマー粒子を含む(A)と(B)の間の高負荷単一吸液性コアであって、前記高負荷吸液性層が吸水性ポリマー粒子を含み、当該構造のための好適な吸水性ポリマー粒子が、少なくとも80×10-7cm3s/gの生理食塩水通液性(SFC)を有し、スパンボンド材料の均一ラップが全毛羽量の約100%を含む高負荷単一吸液性コアと、
(D)40から80gsmの坪量を有する上部樹脂結合層を含む(A)と(C)の間の2つの取得−分配層の系であって、上部取得−分配層が、約150から約250cm2のサイズを有する長方形であり、下部取得−分布層が、40から80gsmの坪量および約100から約300cm2のサイズを有する合成繊維を含み、上部取得−分配層が下部取得−分配層より小さく、両取得−分配層が吸液性コアより小さい系とを含む。
吸液性コアは、ほぼ均一な長方形サイズを有する高負荷混合単一コアシステムからなる。(A)と(B)の間の吸液性コアは、坪量が10gsmである親水性スパンボンド繊維の均一層にラップされた高負荷吸液性層を含む液体貯蔵部を含む。吸液性コアの密度は、前部全体平均が0.20g/cm3であり、割込み帯域が0.19g/cm3であり、後部全体平均が0.19g/cm3である。吸液性コアの坪量は、前部全体平均が1114gsmであり、割込み帯域が1007gsmであり、後部全体平均が658gsmである。吸液性コアの厚さは、4.5mmの平均値を有する。
CRC 28.6g/g
SFC 98×10-7cm3s/g
AUHL 21.6g/g
水分含有量 6.3質量%
渦時間 75秒
GBP 62ダルシー
吸液性コアの寸法:長さ43.0cm;前部幅:11.5cm;股幅:7.2cm;後部幅:12.1cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:3脚弾性体および2カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および3.4cmの高さを有する合成繊維による脚カフ。
・14.9cm×3.8cmの寸法のランディングゾーンを有する機械的密封システムおよび3.0cm×1.3cmの接着性密封テープ;3.0cm×1.3cmフック固定テープに装着。
以下の実施形態14において、本発明のさらなる好適な実施形態を説明する。したがって、好適な吸液性物体は、
(A)スパンボンド層を含む上部液体透過層(表層)と、
(B)通気性ポリエチレンフィルムおよびスパンボンド不織布の複合体を含む下部液体不透過層と、
(C)スパンボンド材料でラップされた高負荷吸液性層を含む液体貯蔵部を含む、全吸収性コア質量に基づいて55から95質量%の吸水性ポリマー粒子を含む(A)と(B)の間の高負荷単一吸液性コアであって、前記高負荷吸液性層が吸水性ポリマー粒子を含み、当該構造のための好適な吸水性ポリマー粒子が、少なくとも80×10-7cm3s/gの生理食塩水通液性(SFC)を有し、スパンボンド材料の均一ラップが全毛羽量の約100%を含む高負荷単一吸液性コアと、
(D)40から80gsmの坪量を有する上部樹脂結合層を含む(A)と(C)の間の2つの取得−分配層の系であって、上部取得−分配層が、約150から約250cm2のサイズを有する長方形であり、下部取得−分配層が、40から80gsmの坪量および約100から約300cm2のサイズを有する合成繊維を含み、上部取得−分配層が下部取得−分配層より小さく、両取得−分配層が吸液性コアより小さい系とを含む。
吸液性コアは、ほぼ均一な長方形サイズを有する高負荷混合単一コアシステムからなる。(A)と(B)の間の吸液性コアは、坪量が10gsmである親水性スパンボンド繊維の均一層にラップされた高負荷吸液性層を含む液体貯蔵部を含む。吸液性コアの密度は、前部全体平均が0.25g/cm3であり、割込み帯域が0.25g/cm3であり、後部全体平均が0.26g/cm3である。吸液性コアの坪量は、前部全体平均が878.70gsmであり、割込み帯域が1237.56gsmであり、後部全体平均が495.60gsmである。吸液性コアの厚さは、3.1mmの平均値を有する。
CRC 30.2g/g
SFC 118×10-7cm3s/g
AUHL 19.7g/g
水分含有量 8.4質量%
渦時間 58秒
GBP 54ダルシー
吸液性コアの寸法:長さ42.4cm;前部幅:10.6cm;股幅:10.2cm;後部幅:10.5cm。
・平坦ゴム弾性体;スパンデックス型繊維による弾性体:2脚弾性体および2カフ弾性体。
・層組合せSMSを示し、13から17gsmの坪量および4.4cmの高さを有する合成繊維による脚カフ。
・ウエストバンド:前部:13.7cm×2.1cm;後部:14.8cm×2.2cm
吸液性物体の寸法:長さ:46.7cm;前部幅:33.5cm;股幅:16.0cm;後部幅:33.5cm。
他に指定する場合を除いて、23±2℃の周囲温度および50±10%の相対雰囲気湿度で測定を実施する。吸水性ポリマーは測定前に十分に混合する。
生理食塩水通液性を、EP0640330A1に記載されているように、吸水性ポリマー粒子の膨潤ゲル層のゲル層透過度として測定するが、前記特許出願の19頁および図8に記載されている装置を、ガラスフリット(40)が使用されず、プランジャー(39)がシリンダー(37)と同じポリマー材料からなり、さらにそれぞれが接触面全体に均一に分布した直径が9.65mmの21個の穴を含むように改造した。測定の手順および評価は、EP0640330A1と変わらない。流量を自動的に記録する。
ただし、Fg(t=0)は、t=0への外挿による流量測定値のFg(t)データの線形回帰解析によって得られるg/s単位のNaCl溶液の流量であり、L0は、cm単位のゲル層の厚さであり、dは、g/cm3単位のNaCl溶液の密度であり、Aは、cm2単位のゲル層の表面積であり、WPはdyn/cm2単位のゲル層に対する静水圧である。
1.00g(=W1)の乾燥吸水性ポリマー粒子を25mlのガラスビーカーに秤取し、ガラスビーカーの基部に均一に分配させる。次いで、20mlの0.9質量%の塩化ナトリウム溶液を第2のガラスビーカーに計量分配し、このビーカーの内容物を第1のビーカーに迅速に加え、ストップウォッチを開始させる。液面への反射の消失によって確認される塩溶液の最後の液滴の吸収と同時に、ストップウォッチを停止させる。第2のビーカーに投入され、第1のビーカー内のポリマーによって吸収された液体の正確な量を、第2のビーカーを再度秤量することによって性格に測定する(=W2)。ストップウォッチで測定した吸収に要する時間をtとする。表面上の最後の液滴の消失を時間tと定義する。
しかし、ヒドロゲル形成ポリマーの水分含有量が3質量%を超える場合は、質量W1をこの水分含有量に応じて補正しなければならない。
50.0±1.0mlの0.9%NaCl溶液を100mlビーカーに加える。円筒状撹拌棒(30×6mm)を加え、塩溶液を撹拌プレート上にて60rpmで撹拌する。2.000±0.010gの吸水性ポリマー粒子をできるだけ迅速にビーカーに加え、添加が開始するとストップウォッチを開始させる。混合物の表面が、表面が乱流を有さないことを意味する「静止状態」になったときにストップウォッチを停止し、混合物がまだ旋回する間に粒子の表面全体が一体として旋回する。ストップウォッチの表示時間を渦時間として記録する。
プラスチックカップ(外高が50mmであり、内高(深さ)が38.1mmであり、外径が76.2mmであり、内径が50.8mmである)に、直径が50.75mmで厚さが3.18mmの鋼ディスクを入れる。10.0±0.05gの吸水性ポリマー粒子をカップに入れ、均一に分配させる。次いで、鋼シリンダー(ピストンサイズが、直径=50.75mmおよび高さ=44.45mmであり、ピストンの質量が712.2gである)を吸水性ポリマー粒子上に配置する。次いで、集成装置をカーバープレス型式Auto Series 4425.4D10A01(Carver Inc.;Wabash;アメリカ)に入れる。プレスへの設定力を目標値+200lbsに設定する。圧縮を開始し、デジタル読取値が所望の目標値を示すと、圧縮を手動で停止する。次いで、損傷した吸水性ポリマー粒子を、全量が開始量の0.5質量%以内で除去されるように、ブラシを利用して除去する。
5カップガラス混合瓶を備えたオステライザーブレンダー型式6749−12速、450ワットモーター(Sunbeam Product Inc.;Boca Raton;USA)をバリアックコントローラーなどの可変電圧電源に接続する。ブレンダーの動作速度が10,500rpmになるように電圧コントローラーを調整する。ブレンダー瓶を帯電防止剤(VWRから入手可能なStaticideなど)で処理する。次いで、25.0±0.05gの吸水性ポリマー粒子をブレンダーに入れ、ブレンダー瓶の蓋を瓶の上に配置する。可変電圧電源を通じて装置をオンにし、目標時間にわたって動作させる。混合後、粉塵を3分間にわたって瓶に沈降させる。次いで、蓋を取り除き、次いで損傷した吸水性ポリマー粒子を、全量が開始量の0.5質量%以内で除去されるようにブラシを利用して分離する。
吸水性ポリマー粒子の粒子形態を、顕微鏡解析によって膨潤状態で調べた。約100mgの吸水性ポリマー粒子をガラス製顕微鏡スライドに配置した。シリンジを用いて、0.9%のNaCl水溶液を吸水性ポリマー粒子に塗布して、それらを膨潤させた。溶液を粒子に吸収させながら絶えず補充した。吸水性ポリマー粒子が乾燥しないように注意すべきである。30分間の膨潤時間の後、スライドを顕微鏡(Leica Macroscope Z16 APO、倍率20x、Schott KL2500 LCD低温光源による背面照明、カメラ:Leica DFC 420(いずれもLeica Microsysteme Vertrieb GmbH;Wetzlar;ドイツによる)の下に置き、サンプルの異なる部分の3枚の写真を撮った。
自由膨張ゲル床透過度を測定するための方法は、US2005/0256757のパラグラフ[0061]から[0075]に記載されている。
吸水性ポリマー粒子における残留モノマーの量を、EDANA推奨試験法第WSP410.2−05「残留モノマー」によって測定する。
粒径分布をCamziser(登録商標)画像解析システム(Retsch Technology GmbH;Haan;ドイツ)によって測定する。
ただし、x1は、90質量%の累積率をもたらすメッシュサイズの値であり、x2は、10質量%の累積率をもたらすメッシュサイズの値である。
100から1,000μmの粒径フラクションを使用して、Camziser(登録商標)画像解析システム(Retsch Technology GmbH;Haan;ドイツ)によって平均球形度を測定する。
吸水性ポリマー粒子の水分含有量をEDANA推奨試験法第WSP430.2−05「水分含有量」によって測定する。
吸水性ポリマー粒子の遠心保持能力をEDANA推奨試験法第WSP441.2−05「遠心保持能力」によって測定し、より大きな値の遠心保持能力に対してはラガーティーバッグを使用しなければならない。
21.0g/cm2の質量の代わりに49.2g/cm2の質量を用いることを除いてはEDANA推奨試験法第WSP442.2−05「加圧下吸収度」と同様にして、吸水性ポリマー粒子の高負荷下吸収度を測定する。
吸水性ポリマー粒子の嵩密度をEDANA推奨試験法第WSP460.2−05「密度」によって測定する。
吸水性ポリマー粒子の抽出可能構成成分の量をEDANA推奨試験法第WSP470.2−05「抽出物」によって測定する。
基材ポリマーの製造
実施例1
図1に示されるように集積流動床(27)および外部流動床(29)を備えた並行噴霧乾燥装置にて処理を行った。噴霧乾燥機(5)の円筒部は、22mの高さおよび3.4mの径を有していた。内部流動床(IFB)は、2.0mの径および0.4mの堰高さを有していた。外部流動床(EFB)は、3.0mの長さ、0.65mの幅および0.5mの堰高さを有していた。
噴霧乾燥機出口温度を138℃に調整し、噴霧乾燥機(5)の円筒部における乾燥ガスのガス速度を0.29m/sとし、穴の間隔を5mmとした点を除いては実施例1を繰り返した。モノマー溶液を噴霧乾燥機の頂部に供給するために、200μmの径を有する360個の穴を有する1つの液滴化装置ユニットを使用した。
噴霧乾燥機出口温度を133℃に調整し、噴霧乾燥機(5)の円筒部における乾燥ガスのガス速度を0.45m/sとし、穴の間隔を5mmとした点を除いては実施例1を繰り返した。モノマー溶液を噴霧乾燥機の頂部に供給するために、200μmの径を有する360個の穴を有する1つの液滴化装置ユニットを使用した。
噴霧乾燥機出口温度を130℃に調整し、噴霧乾燥機(5)の円筒部における乾燥ガスのガス速度を0.70m/sとした点を除いては実施例1を繰り返した。モノマー溶液を噴霧乾燥機の頂部に供給するために、200μmの径を有する200個の穴を有する3つの液滴化装置ユニットを使用した。
CRC 26.5g/g
SFC 36×10-7cm3s/g
AUHL 21.6g/g
抽出物 2.0質量%
残留モノマー 735ppm
水分含有量 11.1質量%
FSR 0.35g/gs
得られたポリマー粒子は、59.3g/100mlの嵩密度、440μmの平均粒径、0.63の粒径分布および0.90の平均球形度を有していた。
噴霧乾燥機(5)の円筒部における乾燥ガスのガス速度を0.59m/sとした点を除いては実施例1を繰り返した。モノマー溶液を噴霧乾燥機の頂部に供給するために、200μmの径を有する200個の穴を有する3つの液滴化装置ユニットを使用した。
CRC 28.9g/g
SFC 27×10-7cm3s/g
AUHL 23.0g/g
残留モノマー 384ppm
水分含有量 9.5質量%
FSR 0.3g/gs
得られたポリマー粒子は、69.9g/100mlの嵩密度、421μmの平均粒径を有していた。
噴霧乾燥機(5)の円筒部における乾燥ガスのガス速度を0.59m/sとした点を除いては実施例1を繰り返した。モノマー溶液を噴霧乾燥機の頂部に供給するために、200μmの径を有する200個の穴を有する3つの液滴化装置ユニットを使用した。
CRC 26.0g/g
SFC 54×10-7cm3s/g
AUHL 21.8g/g
抽出物 1.0質量%
残留モノマー 382ppm
水分含有量 9.0質量%
FSR 0.25g/gs
得られたポリマー粒子は、72.6g/100mlの嵩密度および417μmの平均粒径を有していた。
噴霧乾燥機(5)の円筒部における乾燥ガスのガス速度を0.59m/sとした点を除いては実施例1を繰り返した。モノマー溶液を噴霧乾燥機の頂部に供給するために、200μmの径を有する200個の穴を有する3つの液滴化装置ユニットを使用した。
CRC 32.0g/g
SFC 20×10-7cm3s/g
AUHL 24.0g/g
抽出物 1.7質量%
残留モノマー 866ppm
水分含有量 5.8質量%
FSR 0.31g/gs
得られたポリマー粒子は、71.9g/100mlの嵩密度および409μmの平均粒径を有していた。
噴霧乾燥機(5)の円筒部における乾燥ガスのガス速度を0.59m/sとし、穴の間隔を11mmとした点を除いては実施例1を繰り返した。モノマー溶液を噴霧乾燥機の頂部に供給するために、200μmの径を有する267個の穴を有する3つの液滴化装置ユニットを使用した。
CRC 35.0g/g
SFC 8×10-7cm3s/g
AUHL 21.6g/g
抽出物 2.1質量%
残留モノマー 616ppm
水分含有量 9.4質量%
FSR 0.28g/gs
得られたポリマー粒子は、70.7g/100mlの嵩密度および426μmの平均粒径を有していた。
噴霧乾燥機(5)の円筒部における乾燥ガスのガス速度を0.59m/sとし、穴の間隔を11mmとした点を除いては実施例1を繰り返した。モノマー溶液を噴霧乾燥機の頂部に供給するために、200μmの径を有する267個の穴を有する3つの液滴化装置ユニットを使用した。
CRC 40.5g/g
AUHL 12.3g/g
抽出物 3.9質量%
残留モノマー 818ppm
水分含有量 9.0質量%
FSR 0.14g/gs
得られたポリマー粒子は67.9g/100mlの嵩密度および452μmの平均粒径を有していた。
実施例10
実施例8で製造した1kgの吸水性ポリマー粒子を、加熱ジャケットを備えた実験用プラウシェアミキサー(型式M5;Gebrueder Loedige Maschinenbau GmbH(Paderborn、ドイツ)製)に入れた。0.60gのDenacol(登録商標)EX810(エチレングリコールジグリシジルエーテル;ナガセケムテックス株式会社(大阪、日本)より入手)と、20gのプロピレングリコールと、20gの脱イオン水とをビーカーに混入することによって後架橋剤溶液を調製した。450rpmのミキサー速度において、シリンジを使用して、室温で3分間にわたって後架橋剤溶液を吸水性ポリマー粒子に滴加した。次いで、ミキサーを停止し、混合容器の壁に粘着した生成物を掻き取り(バルクと再統合し)、混合を450rpmでさらに2分間継続した。次いで、バッチを2つのステンレス鋼パンに排出させ、1時間にわたって140℃のオーブンに仕込んだ。次いで、パンをオーブンから取り出し、デシケータ中で冷却させた。次いで、冷却生成物を150から710μmで篩い分け、以下のように特徴づけた。
CRC 35.5g/g
SFC 16×10-7cm3s/g
AUHL 26.2g/g
水分含有量 1.8質量%
実施例9で製造した1kgの吸水性ポリマー粒子を、加熱ジャケットを備えた実験用プラウシェアミキサー(型式M5;Gebrueder Loedige Maschinenbau GmbH(Paderborn、ドイツ)製)に入れた。10gの1,4−ブタンジオールと、11.5gのi−プロパノールと、20gの脱イオン水とをビーカーに混入することによって後架橋剤溶液を調製した。450rpmのミキサー速度において、室温で3分間にわたって後架橋剤溶液を噴霧ノズルによってポリマー粉末に添加した。次いで、ミキサーを停止し、混合容器の壁に粘着した生成物を掻き取り(バルクと再統合し)、混合を450rpmでさらに2分間継続した。次いで、ミキサーのジャケットを加熱することによって生成物の温度を190℃まで上昇させた。生成物を80rpmのミキサー速度においてこの温度に45分間維持した。ミキサーを冷却した後、生成物を排出し、150から710μmで篩い分け、以下のように特徴づけた。
CRC 36.2g/g
SFC 9×10-7cm3s/g
AUHL 25.7g/g
水分含有量 0.3質量%
実施例8で製造した1kgの吸水性ポリマー粒子を、加熱ジャケットを備えた実験用プラウシェアミキサー(型式M5;Gebrueder Loedige Maschinenbau GmbH(Paderborn、ドイツ)製)に入れた。300rpmのミキサー速度において、300gのAerosil(登録商標)130(Evonik Degussa GmbH(Frankfurt am Main、ドイツ)のヒュームドシリカ)を添加し、室温で3分間混合した。0.75gのN−(2−ヒドロキシエチル)−2−オキサゾリジノンと、0.75gの1,3−プロパンジオールと、10gのi−プロパノールと、20gの硫酸アルミニウム水溶液(26.8質量%濃度)と、10gの脱イオン水とをビーカーに混入することによって後架橋溶液を調製した。450rpmのミキサー速度において、室温で3分間にわたって後架橋剤溶液を噴霧ノズルによってポリマー粉末に添加した。次いで、ミキサーを停止し、混合容器の壁に粘着した生成物を掻き取り(バルクと再統合し)、混合を450rpmでさらに2分間継続した。次いで、ミキサーのジャケットを加熱することによって生成物の温度を188℃まで上昇させた。生成物を80rpmのミキサー速度においてこの温度に60分間維持した。ミキサーを冷却した後、生成物を排出し、150から710μmで篩い分け、以下のように特徴づけた。
CRC 25.5g/g
SFC 160×10-7cm3s/g
GBP 120ダルシー
AUHL 22.3g/g
水分含有量 0.2質量%
加熱ジャケットを備えた実験用プラウシェアミキサー(型式M5;Gebrueder Loedige Maschinenbau GmbH(Paderborn、ドイツ)製)において、実施例8で製造した800gの吸水性ポリマー粒子を325rpmの速度で混合しながら、0.8gのDenacol(登録商標)EX512(ポリグリセロールポリグリシジルエーテル;ナガセケムテックス株式会社(大阪、日本)より入手)、6gの1,2−プロパンジオールおよび12gの水を含む溶液を滴加した。次いで、16gの乳酸アルミニウム水溶液(25質量%濃度)を滴加した。次いで、吸水性ポリマー粒子と添加溶液を325rpmで60秒間混合させた。
加熱ジャケットを備えた実験用プラウシェアミキサー(型式M5;Gebrueder Loedige Maschinenbau GmbH(Paderborn、ドイツ)製)において、実施例8で製造した800gの吸水性ポリマー粒子を325rpmの速度で混合しながら、0.8gのDenacol(登録商標)EX512(ポリグリセロールポリグリシジルエーテル;ナガセケムテックス株式会社(大阪、日本)より入手)、6gの1,2−プロパンジオールおよび12gの水を含む溶液を滴加した。次いで、20gの硫酸アルミニウム水溶液(27.5質量%濃度)を滴加した。次いで、吸水性ポリマー粒子と添加溶液を325rpmで60秒間混合させた。
加熱ジャケットを備えた実験用プラウシェアミキサー(型式M5;Gebrueder Loedige Maschinenbau GmbH(Paderborn、ドイツ)製)において、実施例9で製造した800gの吸水性ポリマー粒子を325rpmの速度で混合しながら、0.8gのDenacol(登録商標)EX512(ポリグリセロールポリグリシジルエーテル;ナガセケムテックス株式会社(大阪、日本)より入手)、6gの1,2−プロパンジオールおよび12gの水を含む溶液を滴加した。次いで、吸水性ポリマー粒子と添加溶液を325rpmで60秒間混合させた。
実施例16
800gの吸水性ポリマー粒子を室温で機械的プラウシェアミキサー(Pflugschar(登録商標)Mischer Typ M5;Gebr.Loedige Maschinenbau GmbH(Paderborn、ドイツ)に加えた。200rpmの撹拌速度において、吸水性ポリマー粒子を4分以内で硫酸アルミニウムの26.8質量%水溶液で被覆した。吸水性ポリマー粒子に対する固体硫酸アルミニウムの質量%として計算された硫酸アルミニウムの量を以下の表に示す。ミキサーの速度を被覆後に60rpmまで低下させ、これらの条件で生成物をさらに5分間混合した。生成物をミキサーから除去した後、それを850μmスクリーンで篩い分けて潜在的な凝集物を除去した。
硫酸アルミニウム水溶液の代わりに22.0質量%の乳酸アルミニウムコーティング水溶液を用いたこと以外は実施例16を繰り返した。吸水性ポリマー粒子に対する固体乳酸アルミニウムの質量%として計算された、吸水性ポリマー粒子上に塗布した乳酸アルミニウムの量を表11に示す。
硫酸アルミニウム水溶液の代わりにリン酸カルシウムの30質量%水性分散体(Tricalciumphosphat C53−80;Chemische Fabrik Budenheim KG(Budenheim、ドイツ)を用いたこと以外は実施例16を繰り返した。吸水性ポリマー粒子に対する固体リン酸カルシウムの質量%として計算された、吸水性ポリマー粒子上に塗布したリン酸カルシウムの水性分散体量を表10に示す。
硫酸アルミニウム水溶液の代わりに(15質量%水溶液として噴霧される)Lutensol(登録商標)AT80を用いたこと以外は実施例16を繰り返した。吸水性ポリマー粒子に対するLutensol(登録商標)AT80の質量%として計算された、ポリマー粒子上に塗布したLutensol(登録商標)AT80の量を表11に示す。
硫酸アルミニウム水溶液の代わりにシリカ分散体を用いたこと以外は実施例16を繰り返した。ポリマー粒子上に塗布したシリカ分散体の種類および固形分を第14表に示す。吸水性ポリマー粒子に対する固体シリカの質量%として計算されたシリカの量を第14表に示す。
100gの吸水性ポリマー粒子をポリエチレンサンプルボトル(容積500ml)に充填し、無機固体材料を添加した。無機材料の種類を第16表に示す。無機材料の量を第17表に示す。ボトルの内容物を、三次元シェーカー・ミキサー(タイプT2C;Willy A.Bachofen AG Maschinenfabrik(Basel、スイス)を用いて15分間激しく混合した。
100gの吸水性ポリマー粒子を、実施例16または17に従って金属塩水溶液で被覆した。被覆後、生成物をポリエチレンサンプルボトル(容積500ml)に充填し、無機固体材料を添加した。無機材料の種類および量を第18表に示す。ボトルの内容物を、三次元シェーカー・ミキサー(タイプT2F;Willy A.Bachofen AG Maschinenfabrik(Basel、スイス))を用いて15分間激しく混合した。
1kgの吸水性ポリマー粒子を円錐形流動床コーター(Aeromatic Verfahrenstechnische Anlagen AG(Bubendorf、スイス))に充填し、予熱空気(40℃)で流体化した。二相ノズルを用いて、ポリビニルアミン溶液(Lupamin(登録商標)9095およびLupamin(登録商標)4595、BASF SE(Ludwigshafen、ドイツ))を6分間以内で下から吸水性ポリマー粒子上に噴霧した。溶液の量を計算して、吸水性ポリマー粒子に基づいて0.25質量%とした。吸水性ポリマー粒子をコーターから除去し、850μm篩を通して篩い分けて、形成された可能性のある凝集物を除去した。
100gの吸水性ポリマー粒子をポリエチレンサンプルボトル(容積500ml)に充填し、無機固体材料を添加した。無機材料の種類と量を第20表に示す。また、ポリエチレングリコール(PEG400、分子量400g/モル)をダスティング防止剤としてボトルに添加した。ポリマー粒子に基づいてppm(百万分率)単位で計算されたポリエチレングリコールの量を第17表に示す。ボトルの内容物を、三次元シェーカー・ミキサー(タイプT2C;Willy A.Bachofen AG Maschinenfabrik(Basel、スイス))を用いて15分間激しく混合した。
実施例8で製造した吸水性ポリマー粒子と、溶液重合で製造した吸水性ポリマー粒子(Hysorb(登録商標)M7055;BASF SE(Ludwigshafen、ドイツ))とを混合した。Hysorb(登録商標)M7055は、31.6g/gの遠心保持能力(CRC)、23.3g/gの高負荷下吸収度(AUHL)および16×10-7cm3s/gの生理食塩水通液性を有する。
Claims (19)
- a)酸基を保持し、少なくとも部分的に中和されていてもよい少なくとも1つのエチレン不飽和モノマーと、
b)少なくとも1つの架橋剤と、
c)少なくとも1つの開始剤と、
f)水と
を含むモノマー溶液の液滴を周囲の加熱気相にて重合し、ガスを重合チャンバに並流で流し、重合チャンバを出るガスの温度を100℃〜130℃とし、重合チャンバ内のガス速度を少なくとも0.5m/sとし、少なくとも5個の穴を有する液滴プレートを使用することによって液滴を生成することによって、0.86から0.99の平均球形度を有する吸水性ポリマー粒子を製造するための方法。 - 前記モノマー溶液がさらに、
d)a)に挙げられているモノマーと共重合可能な1つまたは複数のエチレン不飽和モノマー
を含む、請求項1に記載の方法。 - 前記モノマー溶液がさらに、
e)1つまたは複数の水溶性ポリマー
を含む、請求項1又は2に記載の方法。 - 重合チャンバを出るガスの温度が、115から125℃である請求項1から3のいずれか1項に記載の方法。
- 重合チャンバ内のガス速度が、0.7から0.9m/sである請求項1から4のいずれか1項に記載の方法。
- 穴の間隔が15から30mmである請求項1から5のいずれか1項に記載の方法。
- 穴の径が150から200μmである請求項1から6のいずれか1項に記載の方法。
- 吸水性ポリマー粒子を、前記ポリマー粒子のカルボキシレート基と少なくとも2つの共有結合を形成することができる基を含む化合物で後架橋する請求項1から7のいずれか1項に記載の方法。
- 吸水性ポリマー粒子を無機不活性物質、有機ポリマー、カチオン性ポリマー、多価金属カチオン、還元剤、抗酸化剤、ポリオール、ヒュームドシリカおよび/または界面活性剤で被覆する請求項1から8のいずれか1項に記載の方法。
- 2つ以上の空洞を有する吸水性ポリマー粒子であって、該空洞は1から50μmの内径を有し、前記吸水性ポリマー粒子が、0.86から0.99の平均球形度、少なくとも0.58g/cm3の嵩密度および250から550μmの平均粒径を有し、粒径分布が0.7未満であり、2つ以上の空洞を有する粒子に対する1つの空洞を有する粒子の比が1.0未満である、前記吸水性ポリマー粒子。
- 請求項1から9のいずれか1項に記載の方法に従って得られる吸水性ポリマー粒子であって、前記ポリマー粒子が、0.86から0.99の平均球形度、少なくとも0.58g/cm3の嵩密度および250から550μmの平均粒径を有し、粒径分布が0.7未満であり、2つ以上の空洞を有する粒子に対する1つの空洞を有する粒子の比が1.0未満である吸水性ポリマー粒子。
- ポリマー粒子が0.7から1g/cm3の嵩密度を有する請求項10または11に記載のポリマー粒子。
- 粒径分布が0.6未満である請求項10から12のいずれか1項に記載のポリマー粒子。
- 粒子の膨潤状態において、空洞が少なくとも1μmの内径を有する請求項10から13のいずれか1項に記載のポリマー粒子。
- ポリマー粒子が少なくとも30g/gの遠心保持能力、少なくとも20g/gの高負荷下吸収度および少なくとも10×10-7cm3s/gの生理食塩水通液性を有する請求項10から14のいずれか1項に記載のポリマー粒子。
- ポリマー粒子が少なくとも20g/gの遠心保持能力、少なくとも15g/gの高負荷下吸収度および少なくとも80×10-7cm3s/gの生理食塩水通液性を有する請求項10から14のいずれか1項に記載のポリマー粒子。
- ポリマー粒子が少なくとも30g/gの遠心保持能力、少なくとも16g/gの高負荷下吸収度および少なくとも20×10-7cm3s/gの生理食塩水通液性を有する請求項10から14のいずれか1項に記載のポリマー粒子。
- 請求項10から17のいずれか1項に記載の吸水性ポリマー粒子に基づく凝集吸水性ポリマー粒子。
- (A)上部液体透過層と、
(B)下部液体不透過層と、
(C)5から90質量%の繊維状材料および10から95質量%の請求項10から16のいずれか1項に記載の吸水性ポリマー粒子を含む層(A)と層(B)の間の吸液性コアと、
(D)80から100質量%の繊維状材料および0から20質量%の請求項10から16のいずれか1項に記載の吸水性ポリマー粒子を含む(A)と(C)の間の任意の取得−分配層と、
(E)(C)の真上および/または真下に配置された任意の組織層と、
(F)他の任意の構成要素と
を含む吸液性物体。