JP5693826B2 - Mortar wall structure, reinforcing sheet adhered to mortar wall surface, and method for manufacturing mortar wall structure - Google Patents
Mortar wall structure, reinforcing sheet adhered to mortar wall surface, and method for manufacturing mortar wall structure Download PDFInfo
- Publication number
- JP5693826B2 JP5693826B2 JP2009117073A JP2009117073A JP5693826B2 JP 5693826 B2 JP5693826 B2 JP 5693826B2 JP 2009117073 A JP2009117073 A JP 2009117073A JP 2009117073 A JP2009117073 A JP 2009117073A JP 5693826 B2 JP5693826 B2 JP 5693826B2
- Authority
- JP
- Japan
- Prior art keywords
- mortar wall
- opening
- reinforcing sheet
- lightweight mortar
- lightweight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、例えば軽量モルタル壁構造に関する。 The present invention relates to a lightweight mortar wall structure, for example.
モルタル(コンクリート)製の壁は、その開口部における隅角部に、ひび割れが入り易い。この為、前記開口部の隅角部の壁内に補強用の金物や繊維ネットを埋設することが提案されている。 A wall made of mortar (concrete) is easily cracked at the corner of the opening. For this reason, it has been proposed to embed reinforcing hardware or fiber nets in the walls of the corners of the openings.
ところで、前記特許文献1,2の技術は、未だ、満足できるものでは無かった。
例えば、木造モルタル造の家に用いられている軽量モルタルは、一般的なモルタルやコンクリートに比べて、軽量で耐火性に優れているものの、強度が低い。この為、開口部における隅角部周辺の軽量モルタルに補強用金物や繊維ネットを埋設しても、前記隅角部周辺のモルタルにひび割れが入ることが多かった。
又、埋設を必須要件としたものであることから、作業性が劣る。すなわち、作業コストが高いものとなっている。
By the way, the techniques of Patent Documents 1 and 2 have not yet been satisfactory.
For example, lightweight mortars used in wooden mortar houses are lighter and have better fire resistance than ordinary mortars and concretes, but have low strength. For this reason, even if a reinforcing metal or fiber net is embedded in a lightweight mortar around the corner of the opening, cracks often occur in the mortar around the corner.
In addition, workability is inferior because embedding is an essential requirement. That is, the work cost is high.
従って、本発明が解決しようとする課題は、モルタルが軽量モルタルであっても、モルタル壁の開口部における隅角部周辺にひび割れが入り難く、かつ、簡単に実施できるモルタル壁構造を提供することである。 Therefore, the problem to be solved by the present invention is to provide a mortar wall structure that is difficult to crack around the corner of the opening of the mortar wall and can be easily implemented even if the mortar is a lightweight mortar. It is.
前記の課題は、
開口部を有するモルタル壁の構造であって、
前記開口部における隅角部周辺のモルタル壁表面に補強シートが貼着されてなる
ことを特徴とするモルタル壁構造によって解決される。
The above issues are
A mortar wall structure having an opening,
The problem is solved by a mortar wall structure in which a reinforcing sheet is attached to the surface of the mortar wall around the corner of the opening.
特に、上記のモルタル壁構造であって、補強シートが光硬化型樹脂を用いて構成されてなることを特徴とするモルタル壁構造によって解決される。 In particular, the above-described mortar wall structure is solved by a mortar wall structure characterized in that the reinforcing sheet is formed using a photocurable resin.
又、上記のモルタル壁構造であって、補強シートが光透過可能に構成されてなることを特徴とするモルタル壁構造によって解決される。 Moreover, it is said mortar wall structure, Comprising: The mortar wall structure characterized by the reinforcing sheet being comprised so that light transmission is possible.
又、上記のモルタル壁構造であって、補強シートが光硬化型接着剤により貼着されてなることを特徴とするモルタル壁構造によって解決される。 Moreover, it is said mortar wall structure, Comprising: It solves by the mortar wall structure characterized by the reinforcing sheet being stuck by the photocurable adhesive agent.
又、前記の課題は、
モルタル壁の開口部における隅角部周辺のモルタル壁表面に貼着される
ことを特徴とする補強シートによって解決される。
In addition, the above problem is
The problem is solved by a reinforcing sheet that is attached to the surface of the mortar wall around the corner of the opening of the mortar wall.
特に、上記の補強シートであって、該補強シートが光硬化型樹脂を用いて構成されてなることを特徴とする補強シートによって解決される。 In particular, the above-described reinforcing sheet is solved by a reinforcing sheet characterized in that the reinforcing sheet is configured using a photocurable resin.
特に、上記の補強シートであって、該補強シートが光透過可能に構成されてなることを特徴とする補強シートによって解決される。 In particular, the above-described reinforcing sheet is solved by the reinforcing sheet characterized in that the reinforcing sheet is configured to transmit light.
又、前記の課題は、
モルタル壁の開口部における隅角部周辺のモルタル壁表面に、上記の補強シートを貼着する
ことを特徴とするモルタル壁構造の製造方法によって解決される。
In addition, the above problem is
The problem is solved by a method for producing a mortar wall structure, characterized in that the reinforcing sheet is adhered to the surface of a mortar wall around the corner of the opening of the mortar wall.
特に、モルタル壁の開口部における隅角部周辺のモルタル壁表面に、接着剤を用いて、上記の補強シートを貼着する
ことを特徴とするモルタル壁構造の製造方法によって解決される。
In particular, the problem is solved by a method for manufacturing a mortar wall structure, characterized in that the reinforcing sheet is adhered to the surface of the mortar wall around the corner of the opening of the mortar wall using an adhesive.
ひび割れが起き難いモルタル壁が、モルタル壁の表面にシートを貼るのみの簡単な作業、かつ、低廉なコストで得られる。
その結果、耐久性が高い建物が低廉なコストで得られる。
A mortar wall that does not easily crack can be obtained by a simple operation of simply attaching a sheet to the surface of the mortar wall and at a low cost.
As a result, a highly durable building can be obtained at a low cost.
第1の本発明はモルタル壁構造(中でも、軽量モルタル壁構造)である。特に、開口部を有するモルタル壁(中でも、軽量モルタル壁)の構造である。そして、前記開口部における隅角部周辺のモルタル壁表面に補強シートが貼着されたものである。前記補強シートは、好ましくは、光硬化型樹脂を用いて構成されたものである。又、好ましくは、光透過可能に構成されたものである。例えば、透過光/入射光が約10%以上の透明材で構成されたシートであるとか、或いは透過光/入射光が約10%以上の透明部を部分的に有するシートで構成されたものである。前記補強シートの貼着は接着剤を用いて行われる。好ましい接着剤として光硬化型接着剤が挙げられる。 The first aspect of the present invention is a mortar wall structure (in particular, a lightweight mortar wall structure). In particular, the structure is a mortar wall (in particular, a lightweight mortar wall) having an opening. And the reinforcement sheet | seat is affixed on the mortar wall surface around the corner | angular part in the said opening part. The reinforcing sheet is preferably configured using a photocurable resin. Further, it is preferably configured so as to be able to transmit light. For example, it is a sheet composed of a transparent material with a transmitted light / incident light of about 10% or more, or a sheet partially having a transparent portion with a transmitted light / incident light of about 10% or more. is there. The reinforcing sheet is attached using an adhesive. A photocurable adhesive is mentioned as a preferable adhesive.
第2の本発明は補強シートである。特に、モルタル壁(中でも、軽量モルタル壁)の開口部における隅角部周辺のモルタル壁表面に貼着される補強シートである。この補強シートは、好ましくは、光硬化型樹脂を用いて構成されたものである。又、好ましくは、光透過可能に構成されたものである。例えば、透過光/入射光が約10%以上の透明材で構成されたシートであるとか、或いは透過光/入射光が約10%以上の透明部を部分的に有するシートで構成されたものである。 The second aspect of the present invention is a reinforcing sheet. In particular, the reinforcing sheet is affixed to the surface of the mortar wall around the corner portion in the opening of the mortar wall (in particular, the lightweight mortar wall). This reinforcing sheet is preferably configured using a photocurable resin. Further, it is preferably configured so as to be able to transmit light. For example, it is a sheet composed of a transparent material with a transmitted light / incident light of about 10% or more, or a sheet partially having a transparent portion with a transmitted light / incident light of about 10% or more. is there.
第3の本発明はモルタル壁構造の製造方法(モルタル壁構築方法)である。そして、モルタル壁(中でも、軽量モルタル壁)の開口部における隅角部周辺のモルタル壁表面に、上記の補強シートを貼着する工程を具備する。特に、モルタル壁(中でも、軽量モルタル壁)の開口部における隅角部周辺のモルタル壁表面に、接着剤を用いて、上記の補強シートを貼着する工程を具備する。 3rd this invention is a manufacturing method (mortar wall construction method) of a mortar wall structure. And the process of sticking said reinforcement sheet on the mortar wall surface of the corner part periphery in the opening part of a mortar wall (especially lightweight mortar wall) is comprised. In particular, it includes a step of adhering the above reinforcing sheet to the surface of the mortar wall around the corner of the opening of the mortar wall (in particular, the lightweight mortar wall) using an adhesive.
以下、更に詳しく説明する。 This will be described in more detail below.
本発明に用いられる補強シートは、樹脂、炭素、ガラス、金属、植物性繊維、動物性繊維等を、適宜、用いて構成できる。尚、軽量性と強度との観点から、樹脂製、炭素製又はガラス製のシートが好ましい。例えば、繊維強化樹脂シートは好ましいものである。特に、短時間に強固な補強シートを得ることが出来ることから、光硬化型樹脂を用いて補強シートを構成したものが好ましい。例えば、可視光や紫外線により硬化する光硬化型樹脂の層と繊維シート層(又は繊維メッシュ層)とが積層されてなる補強シートは好ましいものとして挙げられる。或いは、補強用の繊維の間(例えば、繊維シートにおける繊維間とか繊維メッシュにおけるメッシュ間)に光硬化型樹脂が含浸してなる補強シートも好ましいものとして挙げられる。すなわち、斯かる補強シートは軽量モルタルのひび割れ抑制効果が大きい。上記繊維シート(又は繊維メッシュ)を構成する繊維としては、例えばガラス繊維、炭素繊維、高密度ポリエチレン繊維やアラミド繊維などの有機繊維を用いることが出来る。又、Al等の軽金属の繊維を用いることも出来る。上記光硬化型樹脂は、一般的には、硬化性樹脂成分と光重合開始剤とを含む樹脂組成物で構成される。前記硬化性樹脂成分は、光重合開始剤が吸光により活性化されるに伴い、これによって重合・硬化する樹脂成分である。このような樹脂成分としては、例えば不飽和ポリエステル型、アクリル型、チオール・エン型、エポキシ型などの各種のものが知られている。例えば、光硬化型ビニルエステル樹脂、光硬化開始剤とエポキシアクリレート樹脂との混合物などが挙げられる。この他にも、テトラメチルキシリレンジイソシアネートを含むポリイソシアネートと、ポリオキシアルキレングリコールを含むポリオールと、活性水素及び(メタ)アクリロイル基を有するモノマーとを反応させて得られる末端に(メタ)アクリロイル基を有するウレタン(メタ)アクリレートオリゴマーと、このオリゴマーと相溶性のある(メタ)アクリレートモノマーと、光重合開始剤とを含む組成物からなる樹脂も挙げられる。尚、耐候性の点からはアクリル型のものは好ましいものである。 The reinforcing sheet used in the present invention can be configured using resin, carbon, glass, metal, vegetable fiber, animal fiber, or the like as appropriate. In addition, from the viewpoint of lightness and strength, a resin, carbon, or glass sheet is preferable. For example, a fiber reinforced resin sheet is preferable. In particular, since a strong reinforcing sheet can be obtained in a short time, it is preferable to use a photocurable resin to constitute the reinforcing sheet. For example, a reinforcing sheet formed by laminating a layer of a photocurable resin that is cured by visible light or ultraviolet light and a fiber sheet layer (or a fiber mesh layer) is preferable. Alternatively, a reinforcing sheet formed by impregnating a photocurable resin between reinforcing fibers (for example, between fibers in a fiber sheet or between meshes in a fiber mesh) is also preferable. That is, such a reinforcing sheet has a large effect of suppressing cracking of lightweight mortar. As a fiber which comprises the said fiber sheet (or fiber mesh), organic fiber, such as glass fiber, carbon fiber, a high density polyethylene fiber, and an aramid fiber, can be used, for example. Also, light metal fibers such as Al can be used. The photocurable resin is generally composed of a resin composition containing a curable resin component and a photopolymerization initiator. The curable resin component is a resin component that is polymerized and cured as the photopolymerization initiator is activated by light absorption. As such a resin component, for example, various types such as an unsaturated polyester type, an acrylic type, a thiol / ene type, and an epoxy type are known. Examples thereof include a photocurable vinyl ester resin and a mixture of a photocuring initiator and an epoxy acrylate resin. In addition, a (meth) acryloyl group is obtained at the terminal obtained by reacting a polyisocyanate containing tetramethylxylylene diisocyanate, a polyol containing polyoxyalkylene glycol, and a monomer having active hydrogen and a (meth) acryloyl group. Also included is a resin comprising a composition comprising a urethane (meth) acrylate oligomer having, a (meth) acrylate monomer compatible with this oligomer, and a photopolymerization initiator. From the viewpoint of weather resistance, an acrylic type is preferable.
本発明における補強シートは、好ましくは、開口部の隅角部の形状に略合わせた形状のものである。すなわち、斯かる形状の補強シートは、目的箇所に効率よく貼り付けることが出来る。特に、開口部における隅角部の周辺にのみ、補強シートを効率良く貼り付けることが出来る。この結果、施工効率が良い。 The reinforcing sheet in the present invention preferably has a shape substantially matching the shape of the corner portion of the opening. That is, the reinforcing sheet having such a shape can be efficiently attached to the target location. In particular, the reinforcing sheet can be efficiently attached only around the corners of the opening. As a result, construction efficiency is good.
本発明の補強シートは約10cm2以上の大きさのものであることが好ましい。より好ましくは、20cm2以上の大きさのものである。なぜならば、小さ過ぎると、ひび割れ抑制効果が小さいからである。上限値に格別な制約は無い。しかしながら、大きくなり過ぎると、貼着し難く、かつ、コストも高いものとなる。従って、2000cm2以下の大きさのものが好ましい。 The reinforcing sheet of the present invention preferably has a size of about 10 cm 2 or more. More preferably, the size is 20 cm 2 or more. This is because if it is too small, the effect of suppressing cracking is small. There is no particular restriction on the upper limit. However, if it becomes too large, sticking will be difficult and the cost will be high. Therefore, the thing of the magnitude | size of 2000 cm < 2 > or less is preferable.
補強シートの貼着に用いられる接着剤は、好ましくは、光硬化型樹脂からなる接着剤(光硬化型接着剤)である。なぜならば、光照射で迅速に硬化することから、施工効率が良く、かつ、接着剤の硬化後に直ちにひび割れの発生を抑制できるからである。すなわち、上記補強シートを軽量モルタルに貼り付けるに際して、光硬化型接着剤を用いると、紫外線(又は可視光)の照射により、例えば10〜40分程度の短時間で貼り付けることができる。特に、光硬化型樹脂を用いて補強シートを構成すると共に、補強シートを軽量モルタルに貼り付けるに際しても光硬化型接着剤を用いた場合、紫外線(又は可視光)の照射により、例えば10〜40分程度の短時間で、補強シート(光硬化型樹脂シート)の硬化と貼着が同時に行えるので、より好ましい。尚、この場合、補強シートは、光透過可能に構成されていることを前提とする。すなわち、補強シートが遮光性のものになっていると、光硬化型接着剤に光照射が出来ないからである。尚、光硬化型接着剤以外の接着剤(即ち、非光硬化型接着剤)を用いることも出来る。例えば、2液型のエポキシ樹脂からなる接着剤、2液型ポリエステル樹脂からなる接着剤などが挙げられる。又、光硬化型接着剤と非光硬化型接着剤とを併用することも出来る。尚、補強シートが遮光性に構成されている場合には、熱硬化型接着剤と言った非光硬化型接着剤を用いる。 The adhesive used for sticking the reinforcing sheet is preferably an adhesive made of a photocurable resin (photocurable adhesive). This is because it cures quickly by light irradiation, so that the construction efficiency is good and the occurrence of cracks can be suppressed immediately after the adhesive is cured. That is, when the above-mentioned reinforcing sheet is attached to a lightweight mortar, if a photo-curing adhesive is used, it can be attached in a short time of, for example, about 10 to 40 minutes by irradiation with ultraviolet rays (or visible light). In particular, when a reinforcing sheet is formed using a photocurable resin and a photocurable adhesive is used even when the reinforcing sheet is attached to a lightweight mortar, for example, 10-40 by irradiation with ultraviolet rays (or visible light). It is more preferable because the reinforcing sheet (photocurable resin sheet) can be cured and adhered simultaneously in a short time of about minutes. In this case, it is assumed that the reinforcing sheet is configured to transmit light. That is, if the reinforcing sheet is light-shielding, the light curable adhesive cannot be irradiated with light. Note that an adhesive other than the photocurable adhesive (that is, a non-photocurable adhesive) can also be used. For example, an adhesive made of a two-pack type epoxy resin and an adhesive made of a two-pack type polyester resin can be mentioned. Moreover, a photocurable adhesive and a non-photocurable adhesive can be used in combination. In addition, when the reinforcing sheet is configured to be light-shielding, a non-light curable adhesive called a thermosetting adhesive is used.
接着剤は貼着に際しては流動性を多少なりとも有する。例えば、粘度(以下、特に断らない限り25℃の値)が3000mPa・sの場合よりも高い流動性を有する接着剤は好ましい。なぜならば、斯かる特性の接着剤を軽量モルタルの表面に塗布した場合、軽量モルタルのポア(空孔)に接着剤が含浸し易い。そして、軽量モルタルの空孔に接着剤が含浸すると、軽量モルタルの強度が増し、モルタルにひび割れが起き難いものとなる。かつ、モルタル表面の平坦性が高まり、接着剤による補強シートの貼着性(接着性:一体性)が高まり、モルタルにひび割れが起き難いものとなる。尚、接着剤の流動性が高すぎると、塗布した際に、接着剤が垂れ落ち易いものとなる。従って、好ましくは、粘度が1000mPa・sの場合よりも低い流動性を有する接着剤である。すなわち、粘度が1000〜3000mPa・sの接着剤は好ましい。尚、粘度が3000mPa・sより小さな接着剤を、先ず、補強シートの貼着箇所の軽量モルタル表面に塗布・含浸させた後、この接着剤塗布表面上に粘度が1000mPa・sより大きな接着剤を塗布し、そして補強シートを貼り付けるようにしても良い。このような場合には、最初に塗布する接着剤としては、接着剤が内部に入り込み、光照射が困難な為、非光硬化型接着剤を用いることが好ましい。そして、後から塗布する接着剤として、光硬化型接着剤を用いるのは好ましいことである。 The adhesive has a certain degree of fluidity upon sticking. For example, an adhesive having a higher fluidity than the case where the viscosity (hereinafter, 25 ° C. unless otherwise specified) is 3000 mPa · s is preferable. This is because when an adhesive having such characteristics is applied to the surface of a lightweight mortar, the pores (holes) of the lightweight mortar are easily impregnated with the adhesive. When the adhesive is impregnated into the pores of the lightweight mortar, the strength of the lightweight mortar is increased and the mortar is hardly cracked. And the flatness of the mortar surface increases, the sticking property (adhesiveness: integrity) of the reinforcement sheet by an adhesive increases, and it becomes difficult to cause a crack in the mortar. In addition, when the fluidity | liquidity of an adhesive agent is too high, when apply | coating, an adhesive agent will fall easily. Therefore, an adhesive having a lower fluidity than the case where the viscosity is 1000 mPa · s is preferable. That is, an adhesive having a viscosity of 1000 to 3000 mPa · s is preferable. An adhesive having a viscosity of less than 3000 mPa · s is first applied and impregnated on the surface of the light weight mortar where the reinforcing sheet is applied, and then an adhesive having a viscosity of more than 1000 mPa · s is applied on the adhesive-coated surface. You may make it apply | coat and affix a reinforcement sheet. In such a case, as the adhesive to be applied first, it is preferable to use a non-photocurable adhesive because the adhesive enters the inside and light irradiation is difficult. And it is preferable to use a photocurable adhesive as an adhesive applied later.
本発明の開口部を有する軽量モルタル壁は、セメント、細骨材及び水が含まれる組成物を用いて構成される。 The lightweight mortar wall having an opening according to the present invention is formed using a composition containing cement, fine aggregate and water.
上記軽量モルタルに含有されるセメントは、例えば普通、早強、超早強、中庸熱、低熱ポルトランドセメント等のポルトランドセメント、高炉セメントやフライアッシュセメント等の混合セメント、アルミナセメント、急硬性セメント、超速硬セメント、或いは都市ゴミ焼却灰や下水汚泥焼却灰等の廃棄物を原料として利用したエコセメント等が挙げられる。これらの中の一種のセメントを用いることが出来る。勿論、二種以上のセメントを用いても良い。 The cement contained in the light weight mortar is, for example, normal, early strength, very early strength, moderate heat, low-heat Portland cement such as Portland cement, mixed cement such as blast furnace cement and fly ash cement, alumina cement, rapid hardening cement, super-fast Examples include hard cement or eco-cement using waste such as municipal waste incineration ash and sewage sludge incineration ash as raw materials. Among these, one kind of cement can be used. Of course, two or more types of cement may be used.
上記軽量モルタルに含有される細骨材は、モルタルに使用可能な細骨材であれば限定されない。如何なるものでも良い。例えば、珪砂、石灰石砂、寒水石砂、砕砂、海砂、スラグ細骨材、人工軽量細骨材やパーライト等の無機質軽量細骨材、ポリエチレン粒やエチレン酢酸ビニル粒等の有機質軽量細骨材などを適宜用いることが出来る。 The fine aggregate contained in the said lightweight mortar will not be limited if it is a fine aggregate which can be used for mortar. It can be anything. For example, silica sand, limestone sand, cold water stone sand, crushed sand, sea sand, slag fine aggregates, inorganic lightweight fine aggregates such as artificial lightweight fine aggregates and perlite, and organic lightweight fine aggregates such as polyethylene grains and ethylene vinyl acetate grains Etc. can be used as appropriate.
上記軽量モルタルには、セメント、細骨材及び水に加えて、本発明の効果を損なわない範囲で、モルタルやコンクリートに使用できる混和材料の1種又は2種以上を添加することができる。この混和材料としては、例えば高性能減水剤、高性能AE減水剤、AE減水剤、減水剤、流動化剤を含むセメント分散剤、セメント用ポリマー、膨張材(剤)、急結剤(材)、急硬剤(材)、収縮低減剤、顔料、撥水剤、防水材、表面硬化剤、保水剤、粘度調整剤、起泡剤、発泡剤、消泡剤、遅延剤、硬化促進剤、潜在性水硬性物質、石炭灰やシリカヒューム等のポゾラン反応性物質等が挙げられる。 In addition to cement, fine aggregate, and water, one or more admixtures that can be used for mortar and concrete can be added to the lightweight mortar as long as the effects of the present invention are not impaired. Examples of the admixture include high-performance water-reducing agent, high-performance AE water-reducing agent, AE water-reducing agent, water-reducing agent, cement dispersant containing fluidizing agent, cement polymer, expansion material (agent), and quick setting agent (material). , Rapid hardening agent (material), shrinkage reducing agent, pigment, water repellent, waterproofing material, surface curing agent, water retention agent, viscosity modifier, foaming agent, foaming agent, antifoaming agent, retarder, curing accelerator, Examples include latent hydraulic substances, pozzolanic reactive substances such as coal ash and silica fume.
上記軽量モルタルは、既往(公知)な製造方法を用いて製造できる。例えば、ミキサで混練することによって製造できる。尚、ミキサ混練になるものは、軽量モルタルの成分や物性が均一になるので好ましい。使用するミキサとしては、例えば左官ミキサ、強制練りコンクリートミキサ、万能ミキサ等が挙げられる。混練時に軽量モルタルに含まれる各材料を一度にミキサで混合しても良いし、事前に材料の一部をミキサで混合しても良い。尚、固形の材料は予め乾式混合されていると、混練時に短時間で均質に混合するので好ましい。 The lightweight mortar can be manufactured using a conventional (known) manufacturing method. For example, it can be manufactured by kneading with a mixer. A mixer kneading is preferable because the components and physical properties of the lightweight mortar become uniform. Examples of the mixer to be used include a plastering mixer, a forced kneaded concrete mixer, and a universal mixer. At the time of kneading, each material contained in the lightweight mortar may be mixed at once with a mixer, or a part of the material may be mixed with a mixer in advance. In addition, it is preferable that the solid material is dry-mixed in advance because it is homogeneously mixed in a short time during kneading.
製造された軽量モルタルを壁面に適用する方法は常法によることが出来る。例えば、壁面の合板に防水シートをラス網と共にステイブルにより止め、その表面に軽量モルタルを鏝により塗り付ける方法は好適である。 A method of applying the manufactured lightweight mortar to the wall surface can be a conventional method. For example, a method in which a waterproof sheet is fixed to a plywood on a wall surface together with a lath net by a stable, and a lightweight mortar is applied to the surface with scissors is suitable.
尚、軽量モルタルと接着した補強シートの表面に、塗装や仕上げ材等の化粧層を設けることは美観の点から好ましい。又、セメントペーストやモルタル等を塗り付けることにより、軽量モルタル表面と接着した補強シート表面との段差を無くすことは美観の点から好ましい。 In addition, it is preferable from the viewpoint of aesthetics to provide a decorative layer such as a coating or finishing material on the surface of the reinforcing sheet bonded to the lightweight mortar. Moreover, it is preferable from the viewpoint of aesthetics to apply a cement paste or mortar to eliminate the step between the light weight mortar surface and the bonded reinforcing sheet surface.
以下、具体的な実施例を挙げて本発明を説明する。 Hereinafter, the present invention will be described with specific examples.
図1は本発明になる第1実施形態の軽量モルタル壁構造の概略図、図2は本発明になる第2実施形態の軽量モルタル壁構造の概略図、図3は本発明になる第3実施形態の軽量モルタル壁構造の概略図である。 FIG. 1 is a schematic diagram of a lightweight mortar wall structure according to a first embodiment of the present invention, FIG. 2 is a schematic diagram of a lightweight mortar wall structure of a second embodiment according to the present invention, and FIG. 3 is a third embodiment according to the present invention. 1 is a schematic diagram of a form of lightweight mortar wall structure. FIG.
各図中、1は軽量モルタル壁である。この軽量モルタル壁1には開口部2が設けられている。この開口部2は、適宜な形状のものであり、隅角部2aを有する。尚、軽量モルタル壁1は、上記した軽量モルタル3で構成されている。 In each figure, 1 is a lightweight mortar wall. The lightweight mortar wall 1 is provided with an opening 2. The opening 2 has an appropriate shape and has a corner 2a. The light weight mortar wall 1 is composed of the light weight mortar 3 described above.
4は補強シートである。この補強シート4は上記した如きのものである。例えば、ガラス繊維シート中に光硬化型樹脂を含浸せしめて構成されたものである。そして、透光性を有する。大きさは20〜2000cm2程度のものである。形状は図1〜図3に示される通り、隅角部2aの形状に沿った形状部4aを有する。従って、隅角部2aに沿って軽量モルタル表面に補強シート4を簡単に貼着できるようになっている。尚、隅角部2aの形状に沿った形状部4a以外の箇所での形状は適宜なものである。例えば、円弧状であるとか、「状であるとか、矢羽根状であるとか、種々の形状である。 4 is a reinforcing sheet. The reinforcing sheet 4 is as described above. For example, it is configured by impregnating a photocurable resin in a glass fiber sheet. And it has translucency. The size is about 20 to 2000 cm 2 . As shown in FIGS. 1 to 3, the shape has a shape portion 4 a that follows the shape of the corner portion 2 a. Therefore, the reinforcing sheet 4 can be easily attached to the light mortar surface along the corner 2a. In addition, the shape in places other than the shape part 4a along the shape of the corner part 2a is appropriate. For example, it has an arc shape, “a shape, an arrow blade shape, or various shapes.
補強シート4は、上記した手法で軽量モルタル表面に貼着される。例えば、光硬化型接着剤を軽量モルタル表面に塗布し、そしてこの塗布箇所に補強シート4を貼り、この後で光照射することで、補強シート4が軽量モルタル表面に強く固着された。 The reinforcing sheet 4 is attached to the surface of the lightweight mortar by the method described above. For example, the photocurable adhesive was applied to the surface of the light weight mortar, and the reinforcing sheet 4 was pasted on the applied portion, followed by light irradiation, whereby the reinforcing sheet 4 was strongly fixed to the surface of the light weight mortar.
1 軽量モルタル壁
2 開口部
3 軽量モルタル
4 光硬化型樹脂シート(補強シート)
DESCRIPTION OF SYMBOLS 1 Lightweight mortar wall 2 Opening part 3 Lightweight mortar 4 Photocurable resin sheet (reinforcement sheet)
Claims (8)
前記開口部における隅角部周辺の軽量モルタル壁表面に前記軽量モルタル壁の開口部の隅角部の形状に略合わせた形状部を一枚で有する補強シートが貼着されてなり、
前記補強シートの軽量モルタル壁の開口部の隅角部の形状に略合わせた形状部が略直角の欠損形状であり、
前記開口部の隅角部に合わせて貼着されている前記補強シートは他の隅角部にまでは対応しておらず、かつ、互いに隣接する隅角部に合わせて各々貼着されている前記補強シートは一つには繋がっておらず、前記貼着されている前記補強シートによって前記開口部の全周囲は囲まれていない
ことを特徴とする軽量モルタル壁構造。 A lightweight mortar wall structure with an opening,
A reinforcing sheet having a single shape portion that is substantially matched to the shape of the corner portion of the opening of the lightweight mortar wall is adhered to the surface of the lightweight mortar wall around the corner portion of the opening,
Said shaped portion to fit substantially to the shape of the corner portion of the opening portion of the light mortar wall reinforcement sheet Ri deficiency shape der substantially right angle,
The reinforcing sheets attached to the corners of the opening do not correspond to other corners, and are attached to the corners adjacent to each other. The lightweight mortar wall structure, wherein the reinforcing sheets are not connected to each other, and the entire periphery of the opening is not surrounded by the adhered reinforcing sheet .
ことを特徴とする請求項1の軽量モルタル壁構造。 A photo-curing adhesive having a fluidity with a viscosity (value at 25 ° C.) higher than 3000 mPa · s is applied to the surface of the light mortar wall around the corner of the opening of the light mortar wall. A light-transmitting reinforcing sheet is provided on the surface of the mold adhesive using a light curable resin and has a single shape portion substantially matching the shape of the corner of the opening of the lightweight mortar wall. The lightweight mortar wall structure according to claim 1, wherein the reinforcing sheet is bonded to the surface of the lightweight mortar wall by being cured by light irradiation.
ことを特徴とする請求項1又は請求項2の軽量モルタル壁構造。 The lightweight mortar wall structure according to claim 1 or 2, wherein the reinforcing sheet is formed by impregnating a glass fiber with a photocurable resin.
軽量モルタル壁の開口部の隅角部の形状に略合わせた前記形状部が、略直角の欠損形状であり、
前記開口部の隅角部に合わせて貼着されている前記補強シートは他の隅角部にまでは対応しておらず、かつ、互いに隣接する隅角部に合わせて各々貼着されている前記補強シートは一つには繋がっておらず、前記貼着されている前記補強シートによって前記開口部の全周囲は囲まれていない
ことを特徴とする軽量モルタル壁の補強シート。 Used by sticking to the surface of the mortar wall around the corner in the opening of the lightweight mortar wall, and having a single shape part that roughly matches the shape of the corner of the opening of the lightweight mortar wall,
Said shaped portion to fit substantially to the shape of the corner portion of the opening portion of the light mortar walls, Ri deficiency shape der substantially right angle,
The reinforcing sheets attached to the corners of the opening do not correspond to other corners, and are attached to the corners adjacent to each other. The reinforcing sheet for lightweight mortar wall, wherein the reinforcing sheet is not connected to one, and the entire periphery of the opening is not surrounded by the adhered reinforcing sheet.
ことを特徴とする請求項4の軽量モルタル壁の補強シート。 5. The lightweight mortar wall reinforcing sheet according to claim 4, wherein the glass fiber is impregnated with a photocurable resin.
ことを特徴とする軽量モルタル壁構造の製造方法。 The manufacturing method of the lightweight mortar wall structure characterized by sticking the reinforcement sheet | seat of Claim 4 or Claim 5 on the lightweight mortar wall surface around the corner | angular part in the opening part of a lightweight mortar wall.
前記塗布された光硬化型接着剤の表面に、光硬化型樹脂を用いて構成され、かつ、前記軽量モルタル壁の開口部の隅角部の形状に略合わせた形状部を一枚で有し、前記開口部の隅角部に合わせて貼着されている補強シートは他の隅角部にまでは対応しておらず、かつ、互いに隣接する隅角部に合わせて各々貼着されている補強シートは一つには繋がっておらず、前記貼着されている前記補強シートによって前記開口部の全周囲は囲まれていない光透過可能な補強シートを配し、
この後、光照射して硬化せしめることにより、前記補強シートを前記軽量モルタル壁表面に貼着する
ことを特徴とする軽量モルタル壁構造の製造方法。 After applying a photocurable adhesive having a viscosity (value at 25 ° C.) higher than 3000 mPa · s to the surface of the lightweight mortar wall around the corner of the opening of the lightweight mortar wall,
On the surface of the coated photosetting adhesive, it is configured by using a photocurable resin, and a shaped portion that matches substantially the shape of the corner portion of the opening portion of the light mortar wall possess a piece The reinforcing sheets attached to the corners of the opening do not correspond to the other corners, and are attached to the corners adjacent to each other. The reinforcing sheet is not connected to one, and a reinforcing sheet capable of transmitting light that is not surrounded by the attached reinforcing sheet is surrounded by the reinforcing sheet,
Then, the said reinforcement sheet | seat is stuck on the said lightweight mortar wall surface by irradiating light and making it harden | cure, The manufacturing method of the lightweight mortar wall structure characterized by the above-mentioned.
ことを特徴とする請求項6又は請求項7の軽量モルタル壁構造の製造方法。 The method for producing a lightweight mortar wall structure according to claim 6 or 7, wherein the reinforcing sheet is formed by impregnating a glass fiber with a photocurable resin.