JP5556942B2 - Precast block refractory and ladle lay structure using this precast block refractory - Google Patents
Precast block refractory and ladle lay structure using this precast block refractory Download PDFInfo
- Publication number
- JP5556942B2 JP5556942B2 JP2013161396A JP2013161396A JP5556942B2 JP 5556942 B2 JP5556942 B2 JP 5556942B2 JP 2013161396 A JP2013161396 A JP 2013161396A JP 2013161396 A JP2013161396 A JP 2013161396A JP 5556942 B2 JP5556942 B2 JP 5556942B2
- Authority
- JP
- Japan
- Prior art keywords
- block
- refractory
- ladle
- precast block
- outer peripheral
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、例えば製鋼用取鍋の敷き部に施工するプレキャストブロック耐火物と、このプレキャストブロック耐火物を用いた製鋼用取鍋の敷き部構造に関するものである。 The present invention relates to, for example, a precast block refractory applied to a laying part of a steel ladle and a laying part structure of a steelmaking ladle using the precast block refractory.
前記プレキャストブロック耐火物としては、羽口ブロック及び湯当りブロックが例示され、例えば取鍋の敷き部において周りに不定形キャスタブル耐火物を流し込んで施工される。 Examples of the precast block refractory include a tuyere block and a hot water block. For example, an amorphous castable refractory is poured around a ladle laying portion.
例えば取鍋の敷き部は、１６５０〜１７５０℃などの高温の溶鋼を受鋼して保持し、場合によっては受鋼した溶鋼をガスバブリングするなど過酷な条件に曝される。しかも、溶解炉から受鋼する際には、溶鋼と共に流出する高侵食性の溶融スラグにも曝される。 For example, the ladle laying part receives and holds high-temperature molten steel such as 1650 to 1750 ° C. and is exposed to severe conditions such as gas bubbling of the received molten steel in some cases. Moreover, when receiving steel from the melting furnace, it is also exposed to highly erodible molten slag flowing out together with the molten steel.
従って、取鍋の敷き部では、不定形キャスタブル耐火物に比べて強度や熱間衝撃に強く優れているプレキャストブロックを、羽口部や取鍋内へ溶鋼流が落下して当たる湯当り部に施工している。 Therefore, in the ladle laying section, a precast block that is stronger and more resistant to hot shock than an indeterminate castable refractory is applied to the hot water contact area where the molten steel flow falls into the tuyere and ladle. We are constructing.
つまり、取鍋の敷き部は、図６に示すように、所定位置にＳＮ羽口プレキャストブロック１、ポーラス羽口プレキャストブロック２、及び湯当りプレキャストブロック３を施工し、その周辺の一般敷き部は、不定形キャスタブル耐火物４をライニング施工している。
That is, as shown in FIG. 6, the ladle laying section is constructed with SN tuyere precast block 1, porous
しかしながら、不定形キャスタブル耐火物とプレキャストブロックを組み合わせた施工の場合、プレキャストブロックの使用中の浮き上がりや、鋳込み終了後、残湯排滓時に落下が発生する場合がある。また、プレキャストブロックと不定形キャスタブル耐火物間の目地開きによる地金差し等の問題が発生する場合もある。 However, in the case of construction in which an indeterminate castable refractory and a precast block are combined, the precast block may be lifted during use, or may fall when the remaining hot water is drained after casting. In addition, there may be a problem such as a metal insertion due to a joint opening between the precast block and the indeterminate castable refractory.
そこで、溶融金属容器を構成する鉄皮と接する側の端部の外周に張り出し部を設けた羽口ブロックが特許文献１で提案されている。 Therefore, Patent Document 1 proposes a tuyere block in which an overhanging portion is provided on the outer periphery of the end portion on the side in contact with the iron skin constituting the molten metal container.
一方、湯当りブロックとして、プレキャストブロックの全面及び周囲の不定形キャスタブル耐火物を目地緩和焼結層で覆う技術が特許文献２で、前記プレキャストブロックとして焼成プレキャストブロックを使用する技術が特許文献３で提案されている。
On the other hand, as a hot water block,
しかしながら、特許文献１で開示された技術は、羽口ブロックの周囲は煉瓦を施工しているので、残湯排滓時の落下や浮上は防止できるものの、煉瓦の目地部では従来と同様、地金差しが発生する場合がある。また、羽口ブロックの外周面がストレートな形状であるため、羽口ブロックの外周部においても地金差しを効果的に抑制することは難しい。 However, since the technique disclosed in Patent Document 1 is constructed with brick around the tuyere block, it can prevent falling and rising when the remaining hot water is drained, but the brick joints are similar to conventional ones. There may be money. In addition, since the outer peripheral surface of the tuyere block has a straight shape, it is difficult to effectively suppress the bare metal insertion even at the outer peripheral part of the tuyere block.
一方、特許文献２で提案された技術の場合、湯当りブロックと不定形キャスタブル耐火物間の目地を目地緩和焼結層で覆うので、残湯排滓時の落下や浮上、地金差しを効果的に防止できる。しかしながら、目地緩和焼結層が溶損や亀裂した場合には、地金差しの効果的な抑制は期待し難い。
On the other hand, in the case of the technique proposed in
また、特許文献３で提案された焼成湯当りブロックの場合は、外周形状は従来と同じストレートであるため、残湯排滓時の落下や浮上、地金差しを効果的に防止することが難しい。
Moreover, in the case of the block per baking hot water proposed by
また、湯当りブロックは、重量物のため施工時、吊手が必要となるが、受鋼中の衝撃により吊手を外した部分が損傷する場合がある。 Moreover, the hot water block is heavy and requires a hand during construction. However, the part from which the hand is removed may be damaged due to an impact during receiving steel.
本発明が解決しようとする問題点は、従来技術の場合、プレキャストブロック耐火物と不定形キャスタブル耐火物間の地金差しを効果的に抑制することが難しいという点である。また、湯当りブロックの場合には、施工時には吊手が必要となるので、受鋼中の衝撃により吊手を外した部分が損傷する場合があり、使用中の浮き上がりや残湯排滓時に落下する場合もあるという点である。 The problem to be solved by the present invention is that, in the case of the prior art, it is difficult to effectively suppress the metal insert between the precast block refractory and the indeterminate castable refractory. In addition, in the case of a block against hot water, a suspension hand is required at the time of construction. Therefore, the part where the suspension is removed may be damaged due to an impact in the steel receiving part. It is a point that there is also a case.
本発明は、プレキャストブロック耐火物と不定形キャスタブル耐火物間の地金差しを効果的に抑制するとともに、湯当りブロックの場合には、施工の際の吊手を不要とし、かつ湯当りブロックの使用中の浮き上がりや残湯排滓時の落下を効果的に防止するために、以下のような構成を採用した。 The present invention effectively suppresses ingots between a precast block refractory and an indeterminate castable refractory, and in the case of a hot water block, it eliminates the need for a hanging hand during construction and In order to effectively prevent floating during use and dropping when draining remaining hot water, the following configuration was adopted.
本発明は、不定形キャスタブル耐火物とプレキャストブロック耐火物を用いて製鋼用取鍋の敷き部を施工する際に湯当りとして用いるプレキャストブロック耐火物であって、
前記プレキャストブロック耐火物の、前記敷き部を構成するパーマ煉瓦と接する側の端部の外周面全域に、外周面からの引っ込み幅が５０mm以上、１００mm以下であって、かつ、高さが５０mm以上、１００mm以下の凹部を形成し、この凹部を除く前記外周面部分を、当該プレキャストブロック耐火物の底面に対して７０°以上、８５°以下の角度をなして形成したことを最も主要な特徴としている。
The present invention is a precast block refractory used as hot water when constructing a ladle for a steel ladle using an indeterminate castable refractory and a precast block refractory,
The retracted width from the outer peripheral surface is 50 mm or more and 100 mm or less and the height is 50 mm or more in the entire outer peripheral surface of the end portion of the precast block refractory that is in contact with the permanent brick constituting the laying portion. The most important feature is that a concave portion of 100 mm or less is formed and the outer peripheral surface portion excluding the concave portion is formed at an angle of 70 ° to 85 ° with respect to the bottom surface of the precast block refractory. Yes.
また、本発明は、
プレキャストブロック耐火物の周りに不定形キャスタブル耐火物を流し込んだ製鋼用取鍋の敷き部構造であって、
羽口ブロックとして、前記敷き部を構成する鉄皮と接する側の端部の外周面全域に凸部を形成したプレキャストブロック耐火物を使用する一方、
湯当りブロックとして、上記に記載のプレキャストブロック耐火物を使用することを最も主要な特徴としている。
The present invention also provides:
A ladle structure for a steel ladle in which an amorphous castable refractory is poured around a precast block refractory,
As a tuyere block, while using a precast block refractory formed with a convex portion in the entire outer peripheral surface of the end portion on the side in contact with the iron skin constituting the laying portion,
The main feature is to use the above-mentioned precast block refractory as a hot water block.
本発明の製鋼用取鍋の敷き部構造では、
前記羽口ブロックとして使用するプレキャストブロック耐火物の、前記敷き部を構成する鉄皮と接する側の端部の外周面全域に形成した凸部は、
前記外周面からの張出し幅が５０mm以上、１００mm以下であって、かつ、高さが５０mm以上、１００mm以下であることが望ましい。
In the ladle structure of the ladle for steel making of the present invention,
The precast block refractory used as the tuyere block, the convex part formed in the entire outer peripheral surface of the end part on the side in contact with the iron skin constituting the laying part,
It is desirable that the overhang width from the outer peripheral surface is 50 mm or more and 100 mm or less and the height is 50 mm or more and 100 mm or less.
また、前記羽口ブロックとして使用するプレキャストブロック耐火物の外周部分の前記凸部を除く部分は、当該プレキャストブロック耐火物の底面に対して７０°以上、８５°以下の角度をなしていることが望ましい。 Moreover, the part except the said convex part of the outer peripheral part of the precast block refractory used as the said tuyere block may form an angle of 70 ° or more and 85 ° or less with respect to the bottom surface of the precast block refractory. desirable.
本発明では、湯当りとして使用するプレキャストブロック耐火物の、製鋼用取鍋の敷き部を構成するパーマ煉瓦と接する側の端部の外周面全域に凹部を有する形状とするので、不定形キャスタブルとの境界部からの地金差しを効果的に抑制することができる。また、施工時における作業時間を短縮できる。さらに、使用中の浮き上がりや、残湯排出時の落下を防止することができる。 In the present invention, since the precast block refractory used as hot water perforation has a concave portion in the entire outer peripheral surface of the end portion on the side in contact with the perm brick constituting the laying portion of the steelmaking ladle, the castable castable and It is possible to effectively suppress the ingot from the boundary portion. Moreover, the work time at the time of construction can be shortened. Furthermore, it is possible to prevent floating during use and dropping when the remaining hot water is discharged.
本発明では、プレキャストブロック耐火物と不定形キャスタブル耐火物間の地金差しを効果的に抑制するとともに、施工に際して湯当りブロックの吊手を不要とし、かつ湯当りブロックの使用中の浮き上がりや残湯排滓時の落下を防止するという目的を、プレキャストブロック耐火物の形状を変更することで実現した。 The present invention effectively suppresses the ingot between the precast block refractory and the irregular castable refractory, eliminates the need for a hot water block block during construction, and lifts and remains during use of the hot water block. The purpose of preventing falling when the hot water is drained is realized by changing the shape of the precast block refractory.
発明者は、プレキャストブロック耐火物の形状・敷き部構造等について 種々検討し、試験を重ねた結果、次のような知見を得た。 The inventor conducted various studies on the shape and laying structure of the precast block refractory, and as a result of repeated tests, the following knowledge was obtained.
（羽口ブロックについて）
従来、取鍋等の敷き部を敷き煉瓦で施工していた時は、敷き煉瓦としてストレート煉瓦を採用していた。また、羽口ブロックも平面視矩形状のストレート煉瓦を使用していたが、不定形キャスタブル耐火物の採用により平面視円状の羽口ブロックを使用するようになった。
(About tuyere block)
Conventionally, when a laying part such as a ladle was laid with a brick, a straight brick was used as the laying brick. Also, the tuyere block used a straight brick with a rectangular shape in plan view, but the use of an indeterminate castable refractory has led to the use of a tuyere block with a plan view circular shape.
しかしながら、平面視円状の羽口ブロック１１を使用することで、図７に示すように、羽口ブロック１１と不定形キャスタブル耐火物１２間の目地１３が鉄皮１４まで通り、通し目地となって地金差しが発生することになった。なお、図７中の１５は大床キャスタブル耐火物、１６はパーマ煉瓦を示す。
However, by using the tuyere block 11 having a circular shape in plan view, as shown in FIG. 7, the
そこで、図１に示すように、羽口ブロック２１の、前記敷き部を構成する鉄皮１４と接する側の端部（以下、鉄皮側端部という。）の外周面全域に凸部２２を形成することで、地金の浸入をパーマ煉瓦１６か凸部２２の位置で制止できることが分かった。
Therefore, as shown in FIG. 1, the protrusions 22 are provided on the entire outer peripheral surface of the end portion of the tuyere block 21 on the side in contact with the
この羽口ブロック２１は、当該羽口ブロック２１の底面に対して７０〜８５°角度の傾斜を設ければ、目地１３の長さが長くなって不定形キャスタブル耐火物１２との接触面積が大きくなるので、溶鋼の垂直力も緩和され、地金の浸入も抑制される。また、不定形キャスタブル耐火物１２が羽口ブロック２１を覆い被さる状態になるので、使用中の浮き上がりや、受鋼終了後の残湯排出時における落下が防止できる。
If the tuyere block 21 is inclined at an angle of 70 to 85 ° with respect to the bottom surface of the tuyere block 21, the length of the
また、羽口ブロック２１は、前記凸部２２の前記外周面からの張出し幅と高さを、それぞれ５０mm以上、１００mm以下とすれば、凸部２２の亀裂発生を抑制でき、また、使用中の浮き上がりや残湯排出時の落下を防止することができる。 Further, the tuyere block 21 can suppress the occurrence of cracks in the convex portion 22 if the protruding width and height of the convex portion 22 from the outer peripheral surface are 50 mm or more and 100 mm or less, respectively. It is possible to prevent floating and falling when discharging remaining hot water.
（湯当りブロックについて）
従来の湯当りブロック３１と不定形キャスタブル耐火物１２との境界部３２は、図８に示すように垂直であるため、稼動中に地金の浸入が発生しやすかった。従って、使用中に湯当りブロック３１が浮き上がり、また受鋼終了後の残湯排出時には、湯当りブロック３１が落下する問題が生じていた。
(About the block per hot water)
Since the
また、湯当りブロック３１は重量物のため、施工時は吊手３３をつけてセットし、施工後、吊手を３３外して受鋼しているが、受鋼中の衝撃により吊手を外した部分に損傷が発生するという問題が生じていた。
In addition, the
そこで、図２に示すように、湯当りブロック４１の、取鍋等の敷き部を構成するパーマ煉瓦１６と接する側の端部の外周面全域に、外周面からの引っ込み幅と高さが、それぞれ５０mm以上、１００mm以下の凹部４２を形成し、この凹部４２を除く前記外周面部分を、当該湯当りブロック４１の底面に対して７０°以上、８５°以下の角度をなして形成することで、目地長さが長くなり、地金の浸入が抑制され、地金がパーマ煉瓦１６まで進行せず、凹部４２の位置で停止することが分かった。
Therefore, as shown in FIG. 2, the retracted width and height from the outer peripheral surface of the block 41 of hot water is in the entire outer peripheral surface of the end portion on the side in contact with the
また、湯当りブロック４１は不定形キャスタブル耐火物１２で覆い被さる状態になり、湯当りブロック４１の落下・浮き上がりも無くなることが分かった。さらに、床面に凹部４２を設けて吊手をなくしたので、吊手を外した部分のブロック損傷が無くなり、また、施工時、玉掛けワイヤーがパーマ煉瓦１６と湯当りブロック４１に挟まれること無く、凹部４２に玉掛けワイヤーを掛けるだけでよくなって、作業時間が短縮できる。
Further, it has been found that the hot water block 41 is covered with the irregular castable refractory 12, and the hot water block 41 does not fall or rise. Further, since the recess 42 is provided on the floor surface and the suspension is eliminated, the block damage of the portion where the suspension is removed is eliminated, and the slinging wire is not sandwiched between the
本発明は、以上の知見に基づいてなされたものであり、
不定形キャスタブル耐火物とプレキャストブロック耐火物を用いて製鋼用取鍋の敷き部を施工する際に羽口として用いるプレキャストブロック耐火物の場合は、鉄皮側端部の外周面全域に凸部を形成したことを最も主要な特徴としている。
The present invention has been made based on the above findings,
In the case of a precast block refractory used as a tuyere when laying a ladle for a steelmaking ladle using an indeterminate castable refractory and a precast block refractory, a convex portion is provided on the entire outer peripheral surface of the iron skin side end. The most important feature is the formation.
この場合、前記羽口ブロックの鉄皮側端部の外周面全域に形成した凸部は、前記外周面からの張出し幅が５０mm以上、１００mm以下であって、かつ、高さが５０mm以上、１００mm以下であることが望ましい。 In this case, the protrusion formed on the entire outer peripheral surface of the iron skin side end of the tuyere block has a protruding width from the outer peripheral surface of 50 mm or more and 100 mm or less and a height of 50 mm or more and 100 mm. The following is desirable.
また、前記羽口ブロックの外周部分の前記凸部を除く部分は、当該羽口ブロックの底面に対して７０°以上、８５°以下の角度をなしていることが望ましい。 In addition, it is desirable that a portion of the outer peripheral portion of the tuyere block excluding the convex portion has an angle of 70 ° to 85 ° with respect to the bottom surface of the tuyere block.
本発明において、羽口ブロックの凸部の外周面からの張出し幅と高さが、それぞれ５０〜１００ｍｍが望ましい理由は、５０mm未満の場合は、使用中の浮き上がり防止や残湯排出時の落下防止の効果が低くなるからである。一方、１００mmより大きくすると、凸部の根元に応力がかかり亀裂の原因となるからである。 In the present invention, the reason why the overhang width and height from the outer peripheral surface of the convex portion of the tuyere block are preferably 50 to 100 mm, respectively, is to prevent lifting during use and prevention of falling when discharging remaining hot water when it is less than 50 mm. This is because the effect of. On the other hand, if it is larger than 100 mm, stress is applied to the base of the convex portion, causing cracks.
また、本発明において、羽口ブロックの外周部分の前記凸部を除く部分は、当該羽口ブロックの底面に対して７０°以上、８５°以下の角度とすることが望ましい理由は次の通りである。 In addition, in the present invention, the reason why it is desirable that the portion of the outer peripheral portion of the tuyere block excluding the convex portion is set to an angle of 70 ° or more and 85 ° or less with respect to the bottom surface of the tuyere block is as follows. is there.
前記角度が８５°より大きくなると、溶鋼の垂直力が大きくなって地金の浸入が発生しやすくなり、残湯排出時に落下しやすくなるのと共に、凸部の付け根に応力がかかって凸部に亀裂が発生して落下する場合があるからである。一方、７０°未満の場合は周辺の不定形キャスタブル耐火物の厚みが稼動面側で薄くなり、稼動面側から不定形キャスタブル耐火物の損耗が進行するからである。 When the angle is larger than 85 °, the vertical force of the molten steel is increased and the intrusion of the metal becomes easy to occur, and it is easy to fall when the remaining hot water is discharged, and stress is applied to the base of the convex portion to the convex portion. This is because cracks may occur and fall. On the other hand, when the angle is less than 70 °, the thickness of the surrounding amorphous castable refractory is reduced on the operating surface side, and the wear of the amorphous castable refractory progresses from the operating surface side.
また、不定形キャスタブル耐火物とプレキャストブロック耐火物を用いて製鋼用取鍋の敷き部を施工する際に湯当りとして用いるブロック耐火物の場合は、
前記敷き部を構成するパーマ煉瓦１６と接する側の端部の外周面全域に、外周面からの引っ込み幅が５０mm以上、１００mm以下であって、かつ、高さが５０mm以上、１００mm以下の凹部を形成し、この凹部を除く前記外周面部分を、当該プレキャストブロック耐火物の底面に対して７０°以上、８５°以下の角度をなして形成したことを最も主要な特徴としている。
In addition, in the case of block refractories used as hot water per unit when constructing the laying part of a ladle for steel making using irregular castable refractories and precast block refractories,
A recess having a retraction width of 50 mm or more and 100 mm or less and a height of 50 mm or more and 100 mm or less from the outer peripheral surface over the entire outer peripheral surface of the end portion in contact with the
本発明において、湯当りブロックの前記パーマ煉瓦と接する側の端部の外周面全域に形成した凹部の、外周面からの引っ込み幅と高さを、それぞれ５０mm以上、１００mm以下としたのは以下の理由による。 In the present invention, the recesses formed in the entire outer peripheral surface of the end portion of the hot water contact block on the side in contact with the perm brick have a retraction width and height from the outer peripheral surface of 50 mm or more and 100 mm or less, respectively. Depending on the reason.
前記引っ込み幅及び高さが５０mm未満の場合は、凹部に入る不定形キャスタブル耐火物の厚みが薄くなって不定形キャスタブル耐火物の強度が低下すると共に、施工時、玉掛けワイヤーの出し入れ作業性が悪くなるからである。一方、前記引っ込み幅及び高さが１００mmを超える場合は、縦方向の強度が低下し、湯当りブロックの効能が低下するからである。 When the retracted width and height are less than 50 mm, the thickness of the amorphous castable refractory entering the recess is reduced, and the strength of the amorphous castable refractory is reduced. Because it becomes. On the other hand, when the retraction width and height exceed 100 mm, the strength in the longitudinal direction is lowered, and the effectiveness of the hot water block is lowered.
また、本発明において、前記凹部を除く前記外周面部分を、当該湯当りブロックの底面に対して７０°以上、８５°以下の角度をなして形成したのは以下の理由による。すなわち、７０°未満の場合は、稼動面側の湯当りブロックと不定形キャスタブル耐火物の境界部が鋭角になって、不定形キャスタブル耐火物の損耗が早くなるからである。一方、８５°を超えると、外周面が垂直傾向になって目地に対して垂直力が加わり、目地に地金の浸入が発生し易くなるからである。また、使用中の浮き上がりや、残湯排出時の落下が発生し易くなるからである。 In the present invention, the outer peripheral surface portion excluding the concave portion is formed at an angle of 70 ° to 85 ° with respect to the bottom surface of the hot water block for the following reason. That is, when the angle is less than 70 °, the boundary between the hot water contact block on the operating surface side and the irregular castable refractory becomes an acute angle, and the wear of the irregular castable refractory is accelerated. On the other hand, if the angle exceeds 85 °, the outer peripheral surface tends to be vertical and a vertical force is applied to the joint, so that the entry of the metal into the joint is likely to occur. Moreover, it is easy to occur during use and to drop when the remaining hot water is discharged.
製鋼用取鍋の敷き部を施工するに際し、図３に示すように、前記の羽口ブロック２１及び湯当りブロック４１を使用すれば、不定形キャスタブル耐火物１２との境界部からの地金差しを効果的に抑制することができる。また、湯当りブロック４１のセット時における作業時間を短縮できる。さらに、湯当りブロック４１の使用中の浮き上がりや、残湯排出時の落下を防止することができる。これが本発明の製鋼用取鍋の敷き部構造である。 When constructing the laying part of the ladle for steel making, as shown in FIG. 3, if the tuyere block 21 and the hot water block 41 are used as described above, the bullion insert from the boundary with the irregular castable refractory 12 is used. Can be effectively suppressed. Moreover, the work time at the time of setting the block 41 per hot water can be shortened. Furthermore, it is possible to prevent the hot water block 41 from being lifted during use and falling when the remaining hot water is discharged. This is the laying part structure of the ladle for steel making according to the present invention.
ちなみに、図１に示した本発明の敷き部構造に使用する羽口ブロックと図２に示した本発明の湯当りブロックを使用し、図３に示すように施工したＶＯＤ取鍋を使用した場合の、地金差し件数と湯当りブロックのセットに要する作業時間を調査した結果を図４及び図５に示す。 By the way, when using the tuyere block used in the laying part structure of the present invention shown in FIG. 1 and the hot water contact block of the present invention shown in FIG. 2 and using a VOD ladle constructed as shown in FIG. 4 and 5 show the results of investigating the number of bullion feeds and the work time required to set the blocks per hot water.
前記ＶＯＤ取鍋に出鋼した溶鋼は、その温度が１７００〜１７５０℃のＮｉ系、Ｃｒ系のステンレス鋼の溶鋼で、１ヒート当たり７５トンずつ２７回出鋼した。比較として、図７に示した従来の羽口ブロックと図８に示した湯当りブロックを用いて施工したＶＯＤ取鍋を使用した場合の結果も図４及び図５に併せて示す。 The molten steel delivered to the VOD ladle was Ni-based and Cr-based stainless steel having a temperature of 1700 to 1750 ° C., and was discharged 27 times by 75 tons per heat. As a comparison, the results when using a VOD ladle constructed using the conventional tuyere block shown in FIG. 7 and the hot water block shown in FIG. 8 are also shown in FIGS.
本発明では、羽口ブロック、湯当りブロックとも、地金差しが皆無になった（図４参照）。また、湯当りブロックをセットする際の作業時間の従来は３０分かかっていたものが５分で行えるようになった（図５参照）。 In the present invention, there are no metal bars for both the tuyere block and the hot water block (see FIG. 4). In addition, the work time for setting a block per hot water, which conventionally took 30 minutes, can be performed in 5 minutes (see FIG. 5).
本発明は上記の例に限らず、各請求項に記載された技術的思想の範疇であれば、適宜実施の形態を変更しても良いことは言うまでもない。 The present invention is not limited to the above example, and it goes without saying that the embodiments may be changed as appropriate within the scope of the technical idea described in each claim.
以上の本発明は、取鍋に限らず転炉などの溶融金属容器であっても適用できる。 The present invention as described above can be applied not only to a ladle but also to a molten metal container such as a converter.
１２ 不定形キャスタブル耐火物
１６ パーマ煉瓦
２１ 羽口ブロック
２２ 凸部
４１ 湯当りブロック
４２ 凹部
12 Indeterminate castable refractory 16 Perm brick 21 Tuyere block 22 Convex part 41 Hot water block 42 Concave part
Claims (4)
前記プレキャストブロック耐火物の、前記敷き部を構成するパーマ煉瓦と接する側の端部の外周面全域に、外周面からの引っ込み幅が５０mm以上、１００mm以下であって、かつ、高さが５０mm以上、１００mm以下の凹部を形成し、この凹部を除く前記外周面部分を、当該プレキャストブロック耐火物の底面に対して７０°以上、８５°以下の角度をなして形成したことを特徴とするプレキャストブロック耐火物。 A precast block refractory used as hot water when constructing a ladle for a steel ladle using an indeterminate castable refractory and a precast block refractory,
The retracted width from the outer peripheral surface is 50 mm or more and 100 mm or less and the height is 50 mm or more in the entire outer peripheral surface of the end portion of the precast block refractory that is in contact with the permanent brick constituting the laying portion. A precast block having a recess of 100 mm or less and the outer peripheral surface portion excluding the recess formed at an angle of 70 ° to 85 ° with respect to the bottom surface of the precast block refractory Refractory.
羽口ブロックとして、前記敷き部を構成する鉄皮と接する側の端部の外周面全域に凸部を形成したプレキャストブロック耐火物を使用する一方、
湯当りブロックとして、請求項１に記載のプレキャストブロック耐火物を使用することを特徴とする製鋼用取鍋の敷き部構造。 A ladle structure for a steel ladle in which an amorphous castable refractory is poured around a precast block refractory,
As a tuyere block, while using a precast block refractory formed with a convex portion in the entire outer peripheral surface of the end portion on the side in contact with the iron skin constituting the laying portion,
A ladle structure for a ladle for steel making, wherein the precast block refractory according to claim 1 is used as a hot water block.
前記外周面からの張出し幅が５０mm以上、１００mm以下であって、かつ、高さが５０mm以上、１００mm以下であることを特徴とする請求項２に記載の製鋼用取鍋の敷き部構造。 The precast block refractory used as the tuyere block, the convex part formed in the entire outer peripheral surface of the end part on the side in contact with the iron skin constituting the laying part,
The ladle structure for a steel ladle according to claim 2, wherein the overhang width from the outer peripheral surface is 50 mm or more and 100 mm or less and the height is 50 mm or more and 100 mm or less.
当該プレキャストブロック耐火物の底面に対して７０°以上、８５°以下の角度をなしていることを特徴とする請求項２又は請求項３に記載の製鋼用取鍋の敷き部構造。 The part excluding the convex part of the outer peripheral part of the precast block refractory used as the tuyere block,
The ladle laying structure for a steel ladle according to claim 2 or 3, wherein the ladle has an angle of 70 ° to 85 ° with respect to the bottom surface of the precast block refractory.