JP5524455B2 - インキ組成物 - Google Patents
インキ組成物 Download PDFInfo
- Publication number
- JP5524455B2 JP5524455B2 JP2008184069A JP2008184069A JP5524455B2 JP 5524455 B2 JP5524455 B2 JP 5524455B2 JP 2008184069 A JP2008184069 A JP 2008184069A JP 2008184069 A JP2008184069 A JP 2008184069A JP 5524455 B2 JP5524455 B2 JP 5524455B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- acrylate
- ink composition
- active energy
- display substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
P1:ハイパーブランチオリゴマーおよび/またはハイパーブランチポリマー
P2:デンドリマー
下記のa成分と、b成分と、光重合開始剤(c)と、有機溶媒とを表1のように配合し均一に混合分散してインキ組成物M1〜M4を調製した。
・a成分:ペンタエリスリトールトリアクリレート
・b成分:(活性エネルギー線重合性ポリエステルアクリレート)
・b1:ハイパーブランチオリゴマー(平均官能基数9のアクリロイル基を有し、ガラス転移温度が80℃、粘度3,500mPa・s、数平均分子量1,377、サトマージャパン(株)製、「CN2301」)
・b2:ハイパーブランチポリマー(平均官能基数16のアクリロイル基を有し、ガラス転移温度が82℃、粘度350mPa・s、数平均分子量1,952、サトマージャパン(株)製、「CN2302」)
・光重合開始剤(c):チバ・ジャパン社製、[IRGACURE907](2−メチル−1−(4−メチルチオフェニル)−2−モルフォリノプロパン−1−オン)
・有機溶媒:(トルエンと、メチルエチルケトンとの1:1(質量比)の混合物)
実施例1においてb成分を配合しない以外は表1のように各々の成分を配合し均一に混合分散してインキ組成物N1を調製した。
実施例1においてa成分を配合しない以外は表1のように各々の成分を配合し均一に混合分散してインキ組成物N2を調製した。
実施例1において、b成分を直鎖状構造のポリエステルアクリレート(東亜合成化学工業製、アロニックスM−8530)に代える以外は表1のように各々の成分を配合し均一に混合分散してインキ組成物N3を調製した。
前記のディスプレイ基板の試料を10cm×10cmにカットした試料片とし、該試料片を水平のガラス基板上に置き、カールが生じた試料端面とガラス基板との隙間の幅を測定した。
前記の各々の有機溶媒を除くインキ組成物の密度d1と該組成物を塗布して紫外線硬化した塗膜の密度dpを測定し、下記の式により収縮率を測定した。
収縮率(%)=100×(dp−d1)/dp
JIS K 5600−5−6に準拠して、碁盤目テープ法により塗膜の碁盤目100目盛り中の剥離状態を測定した。
JIS K 5600−5−4に準拠して、鉛筆硬度試験により塗膜硬度を測定した。
新東科学(株)製、HEIDON TYPE 14DRを使用して、塗膜面を直径20mmの圧子にスチールウール#0000を取り付け、荷重750gで50往復擦り、擦った後の傷の状態を下記の評価法により評価した。
○:塗膜面に傷が、認められない。
△:塗膜面に傷が、わずか認められる(傷の数、1本以上5本未満)。
×:塗膜面に傷が、かなり認められる(傷の数、5本以上)。
Claims (8)
- トリアセチルセルロース(セルローストリアセテート)、セルロースジアセテート、セルロースアセテートブチレート、ポリエステル、ポリカーボネート、ポリメタアクリル、ポリスチレン、ポリエーテルスルホン、ポリアリレート、ポリスルフォン、ポリエーテルケトン、ポリプロピレン、ポリビニルアセタール、スチレンアクリル共重合体、ポリイミド又はポリ塩化ビニルのいずれかである、厚さ10μm〜300μmのディスプレイ基板用基材の表面に、活性エネルギー線を用いて塗膜を硬化させてハードコート層を形成する際に使用されるインキ組成物であって、
分子中に3個以上の(メタ)アクリロイル基を有する活性エネルギー線重合性モノマー(a成分)と、下記の多分岐構造を有するP1およびP2から選ばれる少なくとも1種の多官能基を有する活性エネルギー線重合性ポリエステル(メタ)アクリレート(b成分)とを含有し(但し、無機微粒子を含む場合、透光性粒子を含む場合、ポリ(グリシジルメタクリレート)を含む場合を除く)、
前記活性エネルギー線重合性モノマー(a)が、ペンタエリスリトールトリ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、ジトリメチロールプロパントリ(メタ)アクリレート、ジトリメチロールプロパンテトラ(メタ)アクリレート、ポリペンタエリスリトールポリ(メタ)アクリレート、トリペンタエリスリトールテトラ(メタ)アクリレート、トリペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールトリ(メタ)アクリレート、トリメチロールエタントリ(メタ)アクリレート、グリセリントリ(メタ)アクリレート、ジペンタエリスリトールモノヒドロキシペンタ(メタ)アクリレート、および、そのエチレンオキサイド、プロピレンオキサイド又はカプロラクトンにより変性したもの、からなる群から選択される少なくとも1種であり、
前記活性エネルギー線重合性ポリエステル(メタ)アクリレート(b)のガラス転移温度が、70℃〜110℃、および粘度が、200mPa・s〜5,000mPa・s(25℃)であり、
前記活性エネルギー線重合性モノマー(a)と、活性エネルギー線重合性ポリエステル(メタ)アクリレート(b)との配合割合が、a/b=4/6〜7/3(質量比)であることを特徴とするディスプレイ基板用インキ組成物。
P1:ハイパーブランチオリゴマーおよび/またはハイパーブランチポリマー
P2:デンドリマー - 前記P1が、ハイパーブランチオリゴマー、或いは、ハイパーブランチオリゴマーおよびハイパーブランチポリマーである請求項1に記載のディスプレイ基板用インキ組成物。
- 前記ディスプレイ基板用基材が、トリアセチルセルロースである請求項1又は2に記載のインキ組成物。
- 前記活性エネルギー線重合性ポリエステル(メタ)アクリレート(b)が、平均官能基数6〜18の(メタ)アクリロイル基を有する多分岐ポリエステル(メタ)アクリレートである請求項1〜3のいずれか1項に記載のインキ組成物。
- 前記活性エネルギー線重合性ポリエステル(メタ)アクリレート(b)が、平均官能基数9の(メタ)アクリロイル基を有するハイパーブランチオリゴマーである請求項1〜4のいずれか1項に記載のインキ組成物。
- 前記活性エネルギー線重合性ポリエステル(メタ)アクリレート(b)の数平均分子量が、1,000〜3,000である請求項1〜5のいずれか1項に記載のインキ組成物。
- 請求項1〜6のいずれか1項に記載のインキ組成物を、トリアセチルセルロース(セルローストリアセテート)、セルロースジアセテート、セルロースアセテートブチレート、ポリエステル、ポリカーボネート、ポリメタアクリル、ポリスチレン、ポリエーテルスルホン、ポリアリレート、ポリスルフォン、ポリエーテルケトン、ポリプロピレン、ポリビニルアセタール、スチレンアクリル共重合体、ポリイミド又はポリ塩化ビニルのいずれかである、厚さ10μm〜300μmのディスプレイ基板用基材に塗布し、紫外線硬化した塗膜を有することを特徴とするディスプレイ基板。
- 前記ディスプレイ基板用基材が、トリアセチルセルロースである請求項7に記載のディスプレイ基板。