JP5450863B2 - 導電層形成用分散物及び透明導電体 - Google Patents
導電層形成用分散物及び透明導電体 Download PDFInfo
- Publication number
- JP5450863B2 JP5450863B2 JP2013065637A JP2013065637A JP5450863B2 JP 5450863 B2 JP5450863 B2 JP 5450863B2 JP 2013065637 A JP2013065637 A JP 2013065637A JP 2013065637 A JP2013065637 A JP 2013065637A JP 5450863 B2 JP5450863 B2 JP 5450863B2
- Authority
- JP
- Japan
- Prior art keywords
- metal
- nanowire
- diameter
- less
- aqueous dispersion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、オートクレーブ(120℃、8時間)を用い、水溶媒中で銀アンモニア錯体を還元することにより得られた、長軸長さが数十μm、短軸長さが28nm〜50nmのナノワイヤーが報告されている(非特許文献1参照)。
また、100℃の水溶媒を用い70分かけて作製される長軸長さ数μm、短軸長さが10nmの銀ナノワイヤーが遠心分離で精製することにより観察することができると報告されている(非特許文献2参照)。
また、水溶媒中で塩化銀をグルコースを用いて還元することにより短軸の長さが100nmの単分散なナノワイヤーが報告されている(非特許文献3参照)。
また、銅微粒子を電界析出したガラス基板を硝酸銀水溶液に一晩浸漬することにより得られえられた、短軸長さ90nm〜300nmの銀ナノワイヤーが提案されている(特許文献3参照)。
<1> 直径が50nm以下であり、かつ長さが5μm以上である金属ナノワイヤーが、全金属粒子中に金属量で50質量%以上含まれていることを特徴とする金属ナノワイヤーである。
<2> 金属ナノワイヤーの直径の変動係数が40%以下である前記<1>に記載の金属ナノワイヤーである。
<3> 金属ナノワイヤーの断面形状が、角が丸まった形状である前記<1>から<2>のいずれかに記載の金属ナノワイヤーである。
<4> 金属ナノワイヤーが銀を含有する前記<1>から<3>のいずれかに記載の金属ナノワイヤーである。
<5> 前記<1>から<4>のいずれかに記載の金属ナノワイヤーを製造する方法であって、
少なくともハロゲン化合物及び還元剤を含む水溶媒中に、金属錯体溶液を添加して150℃以下の温度で加熱することを特徴とする金属ナノワイヤーの製造方法である。
<6> 前記<1>から<4>のいずれかに記載の金属ナノワイヤーを含有することを特徴とする水性分散物である。
<7> 前記<1>から<4>のいずれかに記載の金属ナノワイヤーを含有する透明導電層を有することを特徴とする透明導電体である。
<8> 前記<7>に記載の透明導電体を有することを特徴とするタッチパネルである。
<9> 前記<7>に記載の透明導電体を有することを特徴とする太陽電池パネルである。
本発明の金属ナノワイヤーは、直径が50nm以下であり、かつ長さが5μm以上であり、このような直径及び長さを有する金属ナノワイヤーが、全金属粒子中に金属量で50質量%以上含まれているものである。
本発明において、前記金属ナノワイヤーとは、アスペクト比(長さ/直径)が30以上である金属微粒子を意味する。
前記金属ナノワイヤーの長さ(長軸長さ)は、5μm以上であり、10μm以上が好ましく、30μm以上がより好ましい。なお、金属ナノワイヤーの長軸の長さが長すぎると金属ナノワイヤー製造時に絡まるためか、製造過程で凝集物が生じてしまうことがあるため、前記長軸の長さは1mm以下であることが好ましい。前記長軸長さが5μm未満であると、密なネットワークを形成することが難しいためか、十分な導電性を得ることができないことがある。
ここで、前記金属ナノワイヤーの直径及び長軸長さは、例えば、透過型電子顕微鏡(TEM)と光学顕微鏡を用い、TEM像や光学顕微鏡像を観察することにより求めることができ、本発明においては、金属ナノワイヤーの直径及び長軸の長さは、透過型電子顕微鏡(TEM)により300個の金属ナノワイヤーを観察し、その平均値から求めたものである。
前記直径が50nm以下であり、長さが5μm以上である金属ナノワイヤーの割合(以下、「適切ワイヤー化率」と称することもある)が、50質量%未満であると、伝導に寄与する金属量が減少するためか伝導性が低下してしまうことがあり、同時に密なワイヤーネットワークを形成できないために電圧集中が生じるためか、耐久性が低下してしまうことがある。また、ナノワイヤー以外の形状の粒子が球形などのプラズモン吸収が強い場合には透明度を悪化してしまうことがある。
ここで、前記適切ワイヤー化率は、例えば金属ナノワイヤーが銀ナノワイヤーである場合には、銀ナノワイヤー水分散液をろ過して銀ナノワイヤーとそれ以外の粒子を分離し、ICP発光分析装置を用いてろ紙に残っているAg量と、ろ紙を透過したAg量を各々測定することで、適切ワイヤー化率を求めることができる。ろ紙に残っている金属ナノワイヤーをTEMで観察し、300個の金属ナノワイヤーの直径を観察し、その分布を調べることにより、直径が50nm以下であり、かつ長さが5μm以上である金属ナノワイヤーであることを確認する。なお、ろ紙は、TEM像で直径が50nm以下であり、かつ長さが5μm以上である金属ナノワイヤー以外の粒子の最長軸を計測し、その最長軸の5倍以上であり、かつワイヤー長軸の最短長の1/2以下の径のものを用いることが好ましい。
前記変動係数が40%を超えると、直径の細いワイヤーに電圧が集中してしまうためか、耐久性が悪化することがある。
前記金属ナノワイヤーの直径の変動係数は、例えば透過型電子顕微鏡(TEM)像から300個のナノワイヤーの直径を計測し、その標準偏差と平均値を計算することにより、求めることができる。
前記金属ナノワイヤーの断面形状は、基材上に金属ナノワイヤー水分散液を塗布し、断面を透過型電子顕微鏡(TEM)で観察することにより調べることができる。
前記金属ナノワイヤーの断面の角とは、断面の各辺を延長し、隣り合う辺から降ろされた垂線と交わる点の周辺部を意味する。また、「断面の各辺」とはこれらの隣り合う角と角を結んだ直線とする。この場合、前記「断面の各辺」の合計長さに対する前記「断面の外周長さ」との割合を鋭利度とした。鋭利度は、例えば図1に示したような金属ナノワイヤー断面では、実線で示した断面の外周長さと点線で示した五角形の外周長さとの割合で表すことができる。この鋭利度が75%以下の断面形状を角の丸い断面形状と定義する。前記鋭利度は60%以下が好ましく、50%以下であることが更に好ましい。前記鋭利度が75%を超えると、該角に電子が局在し、プラズモン吸収が増加するためか、黄色みが残るなどして透明性が悪化してしまうことがある。
前記金属としては、長周期律表(IUPAC1991)の第4周期、第5周期、及び第6周期からなる群から選ばれる少なくとも1種の金属が好ましく、第2〜14族から選ばれる少なくとも1種の金属がより好ましく、第2族、第8族、第9族、第10族、第11族、第12族、第13族、及び第14族から選ばれる少なくとも1種の金属が更に好ましく、主成分として含むことが特に好ましい。
本発明の金属ナノワイヤーの製造方法は、本発明の前記金属ナノワイヤーを製造する方法であって、少なくともハロゲン化合物、及び還元剤を含む水溶媒中に、金属錯体溶液を添加して150℃以下の温度で加熱する工程を含み、必要に応じて脱塩処理工程を含んでなる。
前記金属錯体の添加は、分散剤とハロゲン化合物の後に添加することが好ましい。ワイヤー核を高い確率で形成できるためか、本発明における適切な径や長さの金属ナノワイヤーの割合を高める効果がある。
前記加熱温度が150℃を超えると、ナノワイヤーの断面の角が急峻になるためか、塗布膜評価での透過率が低くなることがある。また、前記加熱温度が低くなる程、核形成確率が下がり金属ナノワイヤーが長くなりすぎたためか、金属ナノワイヤーが絡みやすく、分散安定性が悪くなることがある。この傾向は20℃以下で顕著となる。
なお、還元剤種によっては機能として分散剤としても働く場合があり、同様に好ましく用いることができる。
前記ハロゲン化合物としては、臭素、塩素、ヨウ素を含有する化合物であれば特に制限はなく、目的に応じて適宜選択することができ、例えば、臭化ナトリウム、塩化ナトリウム、ヨウ化ナトリウム、ヨウ化カリウム、臭化カリウム、塩化カリウムなどのアルカリハライドや下記の分散剤と併用できる物質が好ましい。ハロゲン化合物の添加タイミングは、分散剤の添加前でも添加後でもよく、還元剤の添加前でも添加後でもよい。
なお、ハロゲン化合物種によっては、分散剤として機能するものがありうるが、同様に好ましく用いることができる。
分散剤とハロゲン化合物、又はハロゲン化金属微粒子は同一物質で併用してもよい。分散剤とハロゲン化合物を併用した化合物としては、例えば、アミノ基と臭化物イオンを含むHTAB(ヘキサデシル−トリメチルアンモニウムブロミド)、アミノ基と塩化物イオンを含むHTAC(ヘキサデシル−トリメチルアンモニウムクロライド)が挙げられる。
前記分散剤を添加する段階は、粒子調製する前に添加し、分散ポリマー存在下で添加してもよいし、粒子調整後に分散状態の制御のために添加しても構わない。分散剤の添加を二段階以上に分けるときには、その量は必要とするワイヤーの長さにより変更する必要がある。これは核となる金属粒子量の制御によるワイヤーの長さに起因しているためと考えられる。
前記分散剤として使用可能な構造については、例えば「顔料の事典」(伊藤征司郎編、株式会社朝倉書院発行、2000年)の記載を参照できる。
使用する分散剤の種類によって得られる金属ナノワイヤーの形状を変化させることができる。
本発明の水性分散物は、分散溶媒中に本発明の前記金属ナノワイヤーを含有してなる。
本発明の前記金属ナノワイヤーの前記水性分散物における含有量は、0.1質量%〜99質量%が好ましく、0.3質量%〜95質量%がより好ましい。前記含有量が、0.1質量%未満であると、製造時、乾燥工程における負荷が多大となり、99質量%を超えると、粒子の凝集が起こりやすくなることがある。
前記有機溶媒としては、例えば、沸点が50℃〜250℃、より好ましくは55℃〜200℃のアルコール系化合物が好適に用いられる。このようなアルコール系化合物を併用することにより、塗布工程での塗り付け良化、乾燥負荷の低減をすることができる。
前記アルコール系化合物としては、特に制限はなく、目的に応じて適宜選択することができ、例えばメタノール、エタノール、エチレングリコール、ジエチレングリコール、トリエチレングリコール、ポリエチレングリコール200、ポリエチレングリコール300、グリセリン、プロピレングリコール、ジプロピレングリコール、1,3−プロパンジオール、1,2−ブタンジオール、1,4−ブタンジオール、1,5−ペンタンジオール、1−エトキシ−2−プロパノール、エタノールアミン、ジエタノールアミン、2−(2−アミノエトキシ)エタノール、2−ジメチルアミノイソプロパノール、などが挙げられ、好ましくはエタノール、エチレングリコールである。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記水性分散物の電気伝導度は、1mS/cm以下が好ましく、0.1mS/cm以下がより好ましく、0.05mS/cm以下が更に好ましい。
前記水性分散物の20℃における粘度は、0.5mPa・s〜100mPa・sが好ましく、1mPa・s〜50mPa・sがより好ましい。
インクジェットプリンターによる画像形成用途において、水性分散物を塗設する基板としては、例えば紙、コート紙、表面に親水性ポリマーなどを塗設したPETフィルムなどが挙げられる。
本発明の透明導電体は、本発明の前記水性分散物により形成される透明導電層を有する。
前記透明導電体の製造方法は、本発明の前記水性分散物を、基板上へ塗設し、乾燥する。
以下、前記透明導電体の製造方法の説明を通じて、本発明の透明導電体の詳細についても明らかにする。
(1)石英ガラス、無アルカリガラス、結晶化透明ガラス、パイレックス(登録商標)ガラス、サファイア等のガラス
(2)ポリカーボネート、ポリメチルメタクリレート等のアクリル樹脂、ポリ塩化ビニル、塩化ビニル共重合体等の塩化ビニル系樹脂、ポリアリレート、ポリサルフォン、ポリエーテルサルフォン、ポリイミド、PET、PEN、フッ素樹脂、フェノキシ樹脂、ポリオレフィン系樹脂、ナイロン、スチレン系樹脂、ABS樹脂等の熱可塑性樹脂
(3)エポキシ樹脂等の熱硬化性樹脂
前記基板の形状としては、円盤状、カード状、シート状等のいずれの形状であってもよい。また、三次元的に積層されたものでもよい。更に基板のプリント配線を行う箇所にアスペクト比が1以上の細孔、細溝を有していてもよく、これらの中に、インクジェットプリンター又はディスペンサーにより本発明の水性分散物を吐出することもできる。
前記親水性ポリマー層の層厚(乾燥時)は、0.001μm〜100μmが好ましく、0.01μm〜20μmがより好ましい。
前記親水性ポリマー層には、硬膜剤を添加して膜強度を高めることが好ましい。前記硬膜剤としては、特に制限はなく、目的に応じて適宜選択することができ、例えばホルムアルデヒド、グルタルアルデヒド等のアルデヒド化合物;ジアセチル、シクロペンタンジオン等のケトン化合物;ジビニルスルホン等のビニルスルホン化合物;2−ヒドロキシ−4,6−ジクロロ−1,3,5−トリアジン等のトリアジン化合物;米国特許第3,103,437号明細書等に記載のイソシアネート化合物、などが挙げられる。
更に、基板と上記親水性ポリマー層の間に、密着性の改善を目的として必要により下引き層を形成してもよい。
本発明の透明導電体は、例えばタッチパネル、ディスプレイ用帯電防止、電磁波シールド、有機又は無機ELディスプレイ用電極、電子ペーパー、フレキシブルディスプレイ用電極、フレキシブルディスプレイ用帯電防止、太陽電池用電極、その他の各種デバイスなどに幅広く適用される。
以下の例において、金属ナノワイヤーの直径及び長軸長さ、金属ナノワイヤー直径の変動係数、適切ワイヤー化率、及び金属ナノワイヤーの断面角の鋭利度は、以下のようにして測定した。
透過型電子顕微鏡(TEM;日本電子株式会社製、JEM−2000FX)を用い、300個の金属ナノワイヤーを観察し、その平均値から金属ナノワイヤーの直径及び長軸長さ求めた。
透過型電子顕微鏡(TEM;日本電子株式会社製、JEM−2000FX)を用い、300個の金属ナノワイヤーを観察し、その平均値から金属ナノワイヤーの直径を計測し、その標準偏差と平均値を計算することにより変動係数を求めた。
各銀ナノワイヤー水分散物をろ過して銀ナノワイヤーとそれ以外の粒子を分離し、ICP発光分析装置(株式会社島津製作所製、ICPS−8000)を用いてろ紙に残っているAg量と、ろ紙を透過したAg量を各々測定し、直径が50nm以下であり、かつ長さが5μm以上である銀ナノワイヤー(適切なワイヤー)の全金属粒子中の金属量(質量%)を求めた。
なお、適切ワイヤー比率を求める際の適切な銀ワイヤーの分離は、メンブレンフィルター(Millipore社製、FALP 02500、孔径1.0μm)を用いて行った。
金属ナノワイヤーの断面形状は、基材上に金属ナノワイヤー水分散液を塗布し、断面を透過型電子顕微鏡(TEM;日本電子株式会社製、JEM−2000FX)で観察し、300個の断面について、断面の外周長さと断面の各辺の合計長さを計測し、「断面の各辺」の合計長さに対する前記「断面の外周長さ」との比率である鋭利度を求めた。この鋭利度が75%以下の場合には角の丸い断面形状であるとした。
−添加液Aの調製−
硝酸銀粉末0.51gを純水50mLに溶解した。その後、1Nのアンモニア水を透明になるまで添加した。そして、全量が100mLになるように純水を添加した。
−添加液Gの調製−
グルコース粉末0.5gを140mLの純水で溶解して、添加液Gを調製した。
−添加液Hの調製−
HTAB(ヘキサデシル−トリメチルアンモニウムブロミド)粉末0.5gを27.5mLの純水で溶解して、添加液Hを調製した。
−試料101の銀ナノワイヤー水分散物の作製−
三口フラスコ内に入れ20℃にて攪拌しながら、純水410mL、添加液H 82.5mL、及び添加液G 206mLをロートにて添加した(一段目)。この液に、添加液A 206mLを流量2.0mL/min、攪拌回転数800rpmで添加した(二段目)。その10分後、添加液Hを82.5mL添加した。その後、3℃/分で内温75℃まで昇温した。その後、攪拌回転数を200rpmに落とし、5時間加熱した。
得られた水分散物を冷却した後、限外濾過モジュールSIP1013(旭化成株式会社製、分画分子量6,000)、マグネットポンプ、ステンレスカップをシリコンチューブで接続し、限外濾過装置とした。銀ナノワイヤー分散液(水溶液)をステンレスカップに入れ、ポンプを稼動させて限外濾過を行った。モジュールからの濾液が50mLになった時点で、ステンレスカップに950mLの蒸留水を加え、洗浄を行った。上記の洗浄を10回繰り返した後、母液の量が50mLになるまで濃縮を行った。
得られた試料101の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料102の銀ナノワイヤー水分散物の作製−
実施例1において、一段目の混合溶液の初期温度20℃を25℃に変えた以外は、実施例1と同様にして、試料102の銀ナノワイヤー水分散物を作製した。
得られた試料102の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料103の銀ナノワイヤー水分散物の作製−
実施例1において、一段目の混合溶液の初期温度20℃を30℃に変えた以外は、実施例1と同様にして、試料103の銀ナノワイヤー水分散物を作製した。
得られた試料103の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料104の銀ナノワイヤー水分散物の作製−
実施例1において、一段目で添加する添加液Hの量を82.5mLから70.0mLに変えた以外は、実施例1と同様にして、試料104の銀ナノワイヤー水分散物を作製した。
得られた試料104の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び断面角の鋭利度を表1に示す。
−試料105の銀ナノワイヤー水分散物の作製−
実施例1において、一段目で添加する添加液Hの量を82.5mLから65.0mLに変えた以外は、実施例1と同様にして、試料105の銀ナノワイヤー水分散物を作製した。
得られた試料105の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料106の銀ナノワイヤー水分散物の作製−
実施例1において、添加液Aの添加流量2.0mL/minを4.0mL/minに変えた以外は、実施例1と同様にして、試料106の銀ナノワイヤー水分散物を作製した。
得られた試料106の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料107の銀ナノワイヤー水分散物の作製−
実施例1において、添加液Aの添加流量2.0mL/minを6.0mL/minに変えた以外は、実施例1と同様にして、試料107の銀ナノワイヤー水分散物を作製した。
得られた試料107の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料108の銀ナノワイヤー水分散物の作製−
実施例1において、二段目の温度を75℃から1時間毎に1.5℃ずつ上昇させた以外は、実施例1と同様にして、試料108の銀ナノワイヤー水分散物を作製した。
得られた試料108の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料109の銀ナノワイヤー水分散物の作製−
実施例1において、二段目の温度を75℃から1時間毎に2.5℃ずつ上昇させた以外は、実施例1と同様にして、試料109の銀ナノワイヤー水分散物を作製した。
得られた試料109の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料110の銀ナノワイヤー水分散物の作製−
実施例1において、二段目の温度を80℃に保持した以外は、実施例1と同様にして、試料110の銀ナノワイヤー水分散物を作製した。
得られた試料110の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料111の銀ナノワイヤー水分散物の作製−
実施例1において、二段目の温度を90℃に保持した以外は、実施例1と同様にして、試料111の銀ナノワイヤー水分散物を作製した。
得られた試料111の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料112の銀ナノワイヤー水分散物の作製−
実施例1において、二段目の温度を75℃から1時間毎に3.5℃ずつ上昇させた以外は、実施例1と同様にして、試料112の銀ナノワイヤー水分散物を作製した。
得られた試料112の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料113の銀ナノワイヤー水分散物の作製−
実施例1において、二段目の温度を95℃に保持した以外は、実施例1と同様にして、試料113の銀ナノワイヤー水分散物を作製した。
得られた試料113の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料201の銀ナノワイヤー水分散物の作製−
実施例1において、一段目の混合液の初期温度20℃を40℃に変えた以外は、実施例1と同様にして、試料201の銀ナノワイヤー水分散物を作製した。
得られた試料201の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料202の銀ナノワイヤー水分散物の作製−
実施例1において、一段目で添加する添加液Hの量を82.5mLから50.0mLに変えた以外は、実施例1と同様にして、試料202の銀ナノワイヤー水分散物を作製した。
得られた試料202の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−試料203の銀ナノワイヤー水分散物の作製−
実施例1において、添加液Aの添加流量2.0mL/minを8.0mL/minに変えた以外は、実施例1と同様にして、試料203の銀ナノワイヤー水分散物を作製した。
得られた試料203の銀ナノワイヤーの直径、長軸長さ、適切ワイヤー比率、銀ナノワイヤー直径の変動係数、及び銀ナノワイヤーの断面角の鋭利度を表1に示す。
−下引き層の組成−
ブチルアクリレート(40質量%)、スチレン(20質量%)、グリシジルアクリレート(40質量%)の共重合体ラテックスにヘキサメチレン−1,6−ビス(エチレンウレア)を0.5質量%含有したもの
次に、ドクターコーターを用いて、試料101〜113及び試料201〜203の各塗布用水分散物を親水性ポリマー層上に塗布し、乾燥した。塗布銀量を蛍光X線分析装置(SII社製、SEA1100)にて測定し、0.02g/m2となるように塗布量を調節した。
得られた各塗布物を、島津製作所製UV−2550を用いて、400nm〜800nmの透過率を測定した。
〔評価基準〕
◎:透過率が90%以上で、実用上問題ないレベルである。
○:透過率が80%以上90%未満で、実用上問題ないレベルである。
△:透過率が75%以上80%未満で、実用上問題ないレベルである。
×:透過率が0%以上75%未満で、実用上問題あるレベルである。
得られた各塗布物を、三菱化学株式会社製Loresta−GP MCP−T600を用いて表面抵抗を測定し、下記基準で導電性を評価した。
〔評価基準〕
◎:表面抵抗が100Ω/□未満で、実用上問題ないレベルである。
○:表面抵抗が500Ω/□未満で、実用上問題ないレベルである。
△:表面抵抗が1000Ω/□未満で、実用上問題ないレベルである。
×:表面抵抗が1000Ω/□以上で、実用上問題あるレベルである。
試料101〜113及び試料201〜203の各水分散物を用いて、前述と同様の方法で塗布サンプルを作製した。50℃、湿度60%RHの空気中にて2週間経時し、経時後の表面抵抗測定と透過測定により、塗布物の保存安定性の比較を行った。
Claims (10)
- 直径が50nm以下であり、かつ長さが5μm以上である金属ナノワイヤーが、全金属粒子中に金属量で75質量%以上含まれ、
前記金属ナノワイヤーの平均直径が35nm以下であり、
前記金属ナノワイヤーの直径の変動係数が40%以下である金属ナノワイヤーを含有することを特徴とする導電層形成用分散物。 - 金属ナノワイヤーの平均直径が23.8nm以下である請求項1に記載の導電層形成用分散物。
- 金属ナノワイヤーの断面形状が、角が丸まった形状である請求項1から2のいずれかに記載の導電層形成用分散物。
- 金属ナノワイヤーが銀を含有する請求項1から3のいずれかに記載の導電層形成用分散物。
- 直径が50nm以下であり、かつ長さが5μm以上である金属ナノワイヤーが、全金属粒子中に金属量で75質量%以上含まれ、
前記金属ナノワイヤーの平均直径が35nm以下であり、
前記金属ナノワイヤーの直径の変動係数が40%以下である金属ナノワイヤーを含有する透明導電層を有することを特徴とする透明導電体。 - 金属ナノワイヤーの平均直径が23.8nm以下である請求項5に記載の透明導電体。
- 金属ナノワイヤーの断面形状が、角が丸まった形状である請求項5から6のいずれかに記載の透明導電体。
- 金属ナノワイヤーが銀を含有する請求項5から7のいずれかに記載の透明導電体。
- 請求項1から4のいずれかに記載の導電層形成用分散物から形成された透明導電層、又は請求項5から8のいずれかに記載の透明導電体を有することを特徴とするタッチパネル。
- 請求項1から4のいずれかに記載の導電層形成用分散物から形成された透明導電層、又は請求項5から8のいずれかに記載の透明導電体を有することを特徴とする太陽電池パネル。