JP5398236B2 - セメントクリンカの製造方法 - Google Patents
セメントクリンカの製造方法 Download PDFInfo
- Publication number
- JP5398236B2 JP5398236B2 JP2008298548A JP2008298548A JP5398236B2 JP 5398236 B2 JP5398236 B2 JP 5398236B2 JP 2008298548 A JP2008298548 A JP 2008298548A JP 2008298548 A JP2008298548 A JP 2008298548A JP 5398236 B2 JP5398236 B2 JP 5398236B2
- Authority
- JP
- Japan
- Prior art keywords
- portland cement
- raw material
- clinker
- cement clinker
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)原料及びセメントクリンカの化学組成の測定:JIS R 5204に準拠する蛍光X線分析法により測定した。
(2)モルタル圧縮強度の測定:JIS R 5201規格に準拠する強さ試験により測定した。
(3)空隙率の測定:アルコール溶媒を用いたアルキメデス法でおこなった。
表1に分析結果を示す組成から計算し、クリンカ中のTi含有量が、TiO2換算で0.35質量%となるように各原料の配合比を調整し、これを焼成してセメントクリンカを得た。得られたセメントクリンカの化学組成及びボーグ式により算出される鉱物組成を表2に、空隙率を表3に示す。
最終的な組成に占めるTi含有量が異なるように、各原料の配合比を変化させてセメントクリンカを製造した。なおこのとき、Ti含有量以外の組成等が物性に与える影響を排除するため、HM、SM及びIMが実施例1で得たセメントクリンカと実質的に同一となるように計算し他の原料の配合割合も調整している。
Claims (5)
- 複数種の原料を調合、これを焼成して普通ポルトランドセメント、早強ポルトランドセメント又は中庸熱ポルトランドセメントクリンカを製造するに際し、用いる各原料の成分分析を行い、該分析結果に基づいて、焼成後に得られる前記ポルトランドセメントクリンカ中のTi含有量がTiO2換算で0.5〜1.0質量%以下となるように各原料の配合比率を調整する普通ポルトランドセメント、早強ポルトランドセメント又は中庸熱ポルトランドセメントクリンカの製造方法。
- 原料の少なくとも一部として廃棄物を用いる請求項1記載の製造方法。
- 請求項1又は2記載の方法で普通ポルトランドセメント、早強ポルトランドセメント又は中庸熱ポルトランドセメントクリンカを製造し、ついで該ポルトランドセメントクリンカに石膏を混合する普通ポルトランドセメント、早強ポルトランドセメント又は中庸熱ポルトランドセメントの製造方法。
- 複数種の原料を調合、これを焼成して得られた普通ポルトランドセメント、早強ポルトランドセメント又は中庸熱ポルトランドセメントクリンカであって、該ポルトランドセメントクリンカ中のTi含有量がTiO2換算で0.5〜1.0質量%以下であることを特徴とする普通ポルトランドセメント、早強ポルトランドセメント又は中庸熱ポルトランドセメントクリンカ。
- 請求項4記載のポルトランドセメントクリンカに対して、石膏が加えられた普通ポルトランドセメント、早強ポルトランドセメント又は中庸熱ポルトランドセメント。