JP5391590B2 - アクリル系共重合体の製造方法 - Google Patents
アクリル系共重合体の製造方法 Download PDFInfo
- Publication number
- JP5391590B2 JP5391590B2 JP2008167367A JP2008167367A JP5391590B2 JP 5391590 B2 JP5391590 B2 JP 5391590B2 JP 2008167367 A JP2008167367 A JP 2008167367A JP 2008167367 A JP2008167367 A JP 2008167367A JP 5391590 B2 JP5391590 B2 JP 5391590B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- acrylic
- polymerization
- copolymer
- functional group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
また、本発明は、上記製造方法によって得られた共重合体を含むアクリル系樹脂組成物に関する。
さらに、本発明は、上記製造方法によって得られた共重合体、又は、上記アクリル系樹脂組成物を含むアクリル系接着剤組成物に関する。
本発明の製造方法は、単量体成分全体を100重量%としてアクリル酸アルキルエステル54〜78重量%、アクリロニトリル20〜34重量%、及びカルボキシル基、ヒドロキシル基、酸無水物基、アミノ基、アミド基及びエポキシ基からなる群より選ばれる少なくとも1種の官能基を有する官能基含有メタクリル酸エステル2〜12重量%を重合する共重合体の製造方法である。
撹拌機、温度計、窒素ガス導入管および排出管、加熱ジャケットによって構成された4リットルフラスコを反応器とし、まずフラスコ内を窒素パージし、30mL/minで窒素を流した。次いで、フラスコに、モノマー混合物の反応初期敷液とし水2000g、分散助剤としてポリビニルアルコール0.2gを仕込んだ。
この接着フィルムを、幅10mmに切断し、テスター産業株式会社製90度ピール強度測定機を用いて接着強度を測定した(チャック間距離50mm、引っ張り速度50mm/分)。
また、この接着フィルムを温度85℃、湿度85%に調整した恒温恒湿槽に48時間又は100時間放置した後の接着フィルムについて、上記と同様に接着強度を測定した。
実施例1と同様のモノマー配合と製造方法で、初期に供給するメタクリル酸グリシジルの配合量を40g(総供給量の67重量%)、重合率30%で供給するメタクリル酸グリシジルの配合量を20g(総供給量の33重量%)にし、アクリル系共重合体を製造した。得られたアクリル系共重合体を用いて、実施例1と同様な方法で樹脂ワニス、接着剤組成物、接着剤フィルムを作製し、接着強度を測定した。
実施例1と同様の製造方法で、モノマー混合比をアクリル酸ブチル370g、アクリル酸エチル250g、アクリロニトリル280gとし、初期に供給するメタクリル酸グリシジルの配合量を50g(総供給量の50重量%)、重合率30%で供給するメタクリル酸グリシジルの配合量を50g(総供給量の50重量%)にし、アクリル系共重合体を製造した。得られたアクリル系共重合体を用いて、実施例1と同様な方法で樹脂ワニス、接着剤組成物、接着剤フィルムを作製し、接着強度を測定した。
実施例1と同様のモノマー配合と製造方法で、初期に供給するメタクリル酸グリシジルの配合量を60g(総供給量の100重量%)にし、アクリル系共重合体を製造した。得られたアクリル系共重合体を用いて、実施例1と同様な方法で樹脂ワニス、接着剤組成物、接着剤フィルムを作製し、接着強度を測定した。
実施例1と同様のモノマー配合と製造方法で、初期のメタクリル酸グリシジルの配合量を0g、重合率30%で供給するメタクリル酸グリシジルの配合量を60g(総供給量の100重量%)にし、アクリル系共重合体を製造した。得られたアクリル系共重合体を用いて、実施例1と同様な方法で樹脂ワニス、接着剤組成物、接着剤フィルムを作製し、接着強度を測定した。
実施例1と同様のモノマー配合と製造方法で、初期に供給するメタクリル酸グリシジルの配合量を30g(総供給量の50重量%)、重合率60%で供給するメタクリル酸グリシジルの配合量を30g(総供給量の50重量%)にし、アクリル系共重合体を製造した。得られたアクリル系共重合体を用いて、実施例1と同様な方法で樹脂ワニス、接着剤組成物、接着剤フィルムを作製し、接着強度を測定した。
Claims (3)
- 単量体成分全体を100重量%として、アクリル酸アルキルエステル54〜78重量%、アクリロニトリル20〜34重量%、及びカルボキシル基、ヒドロキシル基、酸無水物基、アミノ基及びエポキシ基からなる群より選ばれる少なくとも1種の官能基を有する官能基含有メタクリル酸エステル2〜12重量%を重合する共重合体の製造方法であって、前記アクリル酸アルキルエステル及び前記アクリロニトリルの全量と、前記官能基含有メタクリル酸エステルの全量の内の30〜70重量%とを混合し、重合率20〜50%まで重合した後、さらに、前記官能基含有メタクリル酸エステルの全量の内の残りの30〜70重量%を混合して重合することを特徴とするアクリル系共重合体の製造方法。
- 請求項1記載の製造方法によって得られた共重合体を含むアクリル系樹脂組成物。
- 請求項1記載の製造方法によって得られた共重合体、又は、請求項2記載のアクリル系樹脂組成物を含むアクリル系接着剤組成物。