JP5205870B2 - Aqueous coolant for DI molding of laminated metal sheet - Google Patents
Aqueous coolant for DI molding of laminated metal sheet Download PDFInfo
- Publication number
- JP5205870B2 JP5205870B2 JP2007221042A JP2007221042A JP5205870B2 JP 5205870 B2 JP5205870 B2 JP 5205870B2 JP 2007221042 A JP2007221042 A JP 2007221042A JP 2007221042 A JP2007221042 A JP 2007221042A JP 5205870 B2 JP5205870 B2 JP 5205870B2
- Authority
- JP
- Japan
- Prior art keywords
- molding
- coolant
- laminated metal
- metal plate
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、ラミネートDI缶を製造する際に用いられるクーラント(潤滑・冷却剤)に関し、詳しくはラミネート金属板をしごき成形または再絞り・しごき成形してDI缶を製造する際に用いられる水性しごき成形用クーラントに関するものである。 The present invention relates to a coolant (lubricant / coolant) used in manufacturing a laminated DI can, and more specifically, an aqueous iron used in manufacturing a DI can by ironing or redrawing / ironing a laminated metal plate. The present invention relates to a molding coolant.
DI缶は、その胴と底の部分につなぎ目の無い2ピース缶の一つであり、金属板を絞り成形(カッピング)して作製した絞り缶をしごき成形または再絞り・しごき成形して加工される缶で、ビール、清涼飲料などの飲料用容器やスープ、野菜などの食品用容器として使用されている。
ここで、絞り成形とは、カッピングプレスと称される絞り成形機において、円盤状に切り抜いた金属板をしわ押さえ装置により固定し、ポンチとダイスの組み合わせからなる工具で底付きのカップ状に成形する加工方法である。また、しごき成形とは、絞り成形により得られたカップの側壁を薄く伸ばす加工である。
絞り成形において、円盤状に切り抜かれた金属板の直径がしごきポンチの直径に比べて大きすぎる場合には1回の絞り成形では所要の形状のカップを得ることが困難なことがあり、その場合2回の絞り成形(絞り−再絞り成形)で所要の形状に成形することが一般に行われる。この工程では、カッピングプレスと称される絞り成形機により比較的直径の大きなカップが製造され、次いでボディメーカー(缶体成形機)において先ず再絞り成形が行われ、その後しごき成形を実施することになる。
The DI can is one of two-piece cans that have no joint between the body and the bottom. The can is made by drawing or redrawing and ironing a drawn can made by drawing (copping) a metal plate. It is used as a container for beverages such as beer and soft drinks and as a container for foods such as soup and vegetables.
Here, the drawing is a drawing machine called a cupping press. A metal plate cut out in a disk shape is fixed with a crease presser and formed into a cup shape with a bottom using a tool consisting of a combination of a punch and a die. It is a processing method to do. In addition, ironing is a process of thinly extending the side wall of a cup obtained by drawing.
In drawing, if the diameter of the metal plate cut out in a disk shape is too large compared to the diameter of the ironing punch, it may be difficult to obtain a cup of the required shape by one drawing. In general, forming into a required shape by two times of drawing (drawing-redrawing) is performed. In this process, a cup having a relatively large diameter is manufactured by a drawing machine called a cupping press, then redrawing is first performed in a body maker (can body forming machine), and then ironing is performed. Become.
DI缶の素材としては、これまでは錫めっき鋼板またはアルミ薄板の金属板が一般に用いられてきた。そして、これらの金属板をDI成形により所望の形状に成形にした後に洗浄、表面処理、塗装等の後処理が行われ、製品(DI缶)となる。しかし、最近は、このような洗浄、表面処理、塗装等の後処理を省略または簡略化できるようにと、フィルムをラミネートした金属板(以下、ラミネート金属板と称することもある)を用いてDI成形することで後処理すること無しに容器製品とする方法が検討されている。 As a material of the DI can, a tin-plated steel plate or an aluminum thin metal plate has been generally used so far. Then, after these metal plates are formed into a desired shape by DI molding, post-treatments such as washing, surface treatment, and painting are performed to obtain a product (DI can). However, recently, in order to eliminate or simplify such post-treatments such as cleaning, surface treatment, and painting, DI using a metal plate laminated with a film (hereinafter sometimes referred to as a laminated metal plate). A method of forming a container product without post-processing by molding has been studied.
フィルムがラミネートされた金属板をDI成形する場合と、従来の金属板を素材とする場合とではDI成形方法が大きく異なる。
従来の金属板を素材としたDI缶の製造では、一般には乳化液型クーラントが用いられる。乳化液型クーラントでは水中に油が分散されているため、缶表面に残存した油の洗浄に薬剤を使用する必要があり、ラミネート金属板のDI成形には適さない。また、最近では、特許文献1〜3に記載されるように、脱脂性、洗浄性に優れる水溶性クーラントが開発され一般的になってきた。この水溶性クーラントは、金属板を素材とするため、金属表面と成形工具の間の摩擦を低減し成形性を高める目的でポリアルキレンポリオール(特許文献1)、三価アルコールと炭素数18の脂肪酸とのエステル(特許文献2)、ポリオキシアルキレン(特許文献3)などにより粘度を高くしており、また、成形工具及び金属板の防錆目的でアミン系の防錆剤を加えてアルカリ性に調整されている。しかし、上記水溶性クーラントを、ラミネート金属板を素材とするDI成形に適用しようとすると、例えば、成形性に劣り、フィルムにダメージを与えやすい上、食品安全性にも劣るなど、さまざまな問題があり適用できない。
一方で、クーラント用ではないが、鉄系金属装置の防錆に食品安全性の高いアミノ酸を添加する試みがなされている。特許文献4には、アミノ酸を含むポリマーを添加することが記載されている。しかし、アスパラギン酸等の酸性アミノ酸は必ずしも鉄の腐食防止に有効ではない。
In the production of a conventional DI can made of a metal plate, an emulsion type coolant is generally used. In the emulsion type coolant, since oil is dispersed in water, it is necessary to use a chemical for cleaning the oil remaining on the surface of the can, which is not suitable for DI molding of a laminated metal plate. Recently, as described in Patent Documents 1 to 3, water-soluble coolants having excellent degreasing properties and cleaning properties have been developed and become common. Since this water-soluble coolant is made of a metal plate, a polyalkylene polyol (Patent Document 1), a trihydric alcohol and a fatty acid having 18 carbon atoms are used for the purpose of reducing the friction between the metal surface and the forming tool and improving the formability. Viscosity is increased by ester (Patent Document 2), polyoxyalkylene (Patent Document 3), etc., and it is made alkaline by adding an amine-based rust preventive for the purpose of rust prevention of forming tools and metal plates. Has been. However, when the above water-soluble coolant is applied to DI molding using a laminated metal plate as a raw material, there are various problems such as inferior moldability, easy film damage, and poor food safety. Yes, not applicable.
On the other hand, although not for coolants, attempts have been made to add amino acids with high food safety to rust prevention of iron-based metal devices. Patent Document 4 describes that a polymer containing an amino acid is added. However, acidic amino acids such as aspartic acid are not necessarily effective in preventing iron corrosion.
ラミネート金属板をDI成形する場合は、金属板表面がラミネートフィルムで被覆されているために従来の金属板のDI成形とは成形方法が根本的に異なる。
ラミネートフィルムの表面は金属表面に比べ柔らかくまた潤滑性もあるため、金属板に使用されるような高分子を含んだ高粘性のクーラントを使用すると逆に成形性が低下することになる。
さらに、ラミネート金属板に使用されるポリエステルフィルムは酸性では安定だがアルカリ性ではやや耐久性に劣る。さらに、トリエタノールアミン等のアミン系の防錆剤は必ずしも食品安全性が高いとは言えなかった。
In the case of DI molding of a laminated metal plate, the molding method is fundamentally different from DI molding of a conventional metal plate because the metal plate surface is covered with a laminate film.
Since the surface of the laminate film is softer and more lubricious than the metal surface, if a high-viscosity coolant containing a polymer such as that used for a metal plate is used, the moldability is lowered.
Furthermore, the polyester film used for the laminated metal plate is stable when acidic, but is slightly inferior in durability when alkaline. Furthermore, it cannot be said that amine-based rust preventives such as triethanolamine have high food safety.
本発明は、かかる事情に鑑みなされたもので、ラミネート金属板のDI成形を可能とし、耐久性と食品安全性に優れたラミネートDI缶を得ることが可能なラミネート金属板DI成形用水性クーラントを提供することを目的とする。 SUMMARY OF THE INVENTION The present invention has been made in view of such circumstances. An aqueous coolant for forming a laminated metal plate DI that can form a laminated metal plate DI and obtain a laminated DI can excellent in durability and food safety is provided. The purpose is to provide.
本発明者らは、上記課題を解決するために鋭意研究を行った。その結果、以下の知見を得た。
ラミネート金属板のDI成形に適するクーラントを検討したところ、適切なアミノ酸、ポリペプチドを含有し、かつクーラント溶液としてほぼ中性のpHの水性クーラントを使用することにより、食品安全性を損なわずにラミネート金属板のDI成形性が非常に高まることを見出した。
また、アミノ酸、ポリペプチドとして適切なものは、水溶液中で合計で0.03〜1質量%となるようにアミノ酸および/またはポリペプチドを溶解した時の50℃でのpHが6.5〜12となるもので、分子内にアミノ基を多く含むことにより鉄等の金属表面に吸着しやすく成形装置内および素材の防錆性が高まるとともに、一方でカルボキシル基を分子内に含むためポリエステル樹脂等フィルムの劣化を抑制できる。さらに、DI成形後の缶の洗浄も従来のクーラントに比べ非常に容易になることも見出した。
The inventors of the present invention have intensively studied to solve the above problems. As a result, the following knowledge was obtained.
We have investigated a coolant suitable for DI molding of laminated metal plates. By using an aqueous coolant with an appropriate amino acid and polypeptide and an almost neutral pH as the coolant solution, it is possible to laminate without sacrificing food safety. It has been found that the DI formability of the metal plate is greatly enhanced.
In addition, suitable amino acids and polypeptides have a pH of 6.5 to 12 at 50 ° C. when the amino acids and / or polypeptides are dissolved so that the total amount is 0.03 to 1% by mass in an aqueous solution. Because it contains a lot of amino groups in the molecule, it can be easily adsorbed on the surface of metals such as iron, and the rust resistance of the molding equipment and the material is increased. Deterioration of the film can be suppressed. Furthermore, it has been found that cleaning of the can after DI molding is much easier than conventional coolant.
本発明は、以上の知見に基づきなされたもので、その要旨は以下のとおりである。
[1]pHが6.5〜12である、アミノ酸およびポリペプチドの中から選ばれる1種以上を合計で0.03〜1質量%含み、50℃におけるpHが6〜8であるラミネート金属板DI成形用水性クーラント。
ただし、前記pHが6.5〜12である、アミノ酸およびポリペプチドとは、水溶液中で合計で0.03〜1質量%となるようにアミノ酸およびポリペプチドの中から選ばれる1種以上を溶解した時の50℃でのpHが6.5〜12である。
[2]前記[1]において、前記アミノ酸は、ヒスチジン、アルギニン、リシン、オキシリシン、テアニンから選ばれる1種以上であることを特徴とするラミネート金属板DI成形用水性クーラント。
[3]前記[1]または[2]において、前記ポリペプチドは、ヒスチジン、アルギニン、リシン、オキシリシンから選ばれる1種以上のアミノ酸を40質量%以上含むことを特徴とするラミネート金属板DI成形用水性クーラント。
[4]前記[1]〜[3]のいずれかにおいて、更に、防錆剤、油性剤、界面活性剤、清浄剤、分散剤、酸化防止剤、防腐剤、消泡剤の中から選ばれる1種以上を含有することを特徴とするラミネート金属板DI成形用水性クーラント。
The present invention has been made based on the above findings, and the gist thereof is as follows.
[1] Laminated metal plate having a pH of 6.5 to 12 and containing 0.03 to 1% by mass in total of at least one selected from amino acids and polypeptides and having a pH of 6 to 8 at 50 ° C. Aqueous coolant for DI molding.
However, the amino acid and the polypeptide having the pH of 6.5 to 12 dissolve at least one selected from the amino acid and the polypeptide so that the total amount in the aqueous solution is 0.03 to 1% by mass. The pH at 50 ° C. is 6.5-12.
[2] The water-based coolant for forming a laminated metal sheet DI according to [1], wherein the amino acid is at least one selected from histidine, arginine, lysine, oxylysine, and theanine.
[3] In the above [1] or [2], the polypeptide contains 40% by mass or more of one or more amino acids selected from histidine, arginine, lysine and oxylysine. Aqueous coolant.
[4] In any one of the above [1] to [3], further selected from rust preventives, oily agents, surfactants, detergents, dispersants, antioxidants, preservatives, and antifoaming agents. An aqueous coolant for forming a laminated metal sheet DI, comprising at least one kind.
本発明の水性クーラントをDI成形に用いることにより、ラミネート金属板のDI成形を可能とし、食品安全性と耐久性に優れたラミネートDI缶を得ることが可能となる。また、成形後の洗浄工程も簡略されるため、生産性も非常に高まる。 By using the aqueous coolant of the present invention for DI molding, a laminated metal plate can be DI molded, and a laminated DI can excellent in food safety and durability can be obtained. In addition, since the cleaning process after molding is simplified, productivity is greatly increased.
本発明のラミネート金属板DI成形用水性クーラントは、pHが6.5〜12である、アミノ酸およびポリペプチドの中から選ばれる1種以上を合計で0.03〜1質量%含み、50℃におけるpHが6〜8であることを特徴とする。ただし、前記pHが6.5〜12である、アミノ酸およびポリペプチドとは、水溶液中で合計で0.03〜1質量%となるようにアミノ酸および/またはポリペプチドを溶解した時の50℃でのpHが6.5〜12である。
以下、これについて、詳細に説明する。
The water-based coolant for forming a laminated metal sheet DI of the present invention contains 0.03 to 1% by mass in total of at least one selected from amino acids and polypeptides having a pH of 6.5 to 12, at 50 ° C. The pH is 6-8. However, the amino acid and polypeptide having a pH of 6.5 to 12 are at 50 ° C. when the amino acid and / or polypeptide are dissolved in an aqueous solution so that the total amount is 0.03 to 1% by mass. PH of 6.5-12.
Hereinafter, this will be described in detail.
pHが6.5〜12である、アミノ酸およびポリペプチドの中から選ばれる1種以上を合計で0.03〜1質量%
本発明のアミノ酸およびポリペプチドは、カルボキシル基とアミノ基の両方を分子内に含み、アミノ基の数が多い構造をとることにより、アミノ基により金属表面に吸着し金属の腐食を十分抑制しながら、一方でカルボキシル基を含むことにより、ラミネートフィルムに使用されるポリエステル樹脂の劣化を抑制することが可能とする。そのような効果を得るためには、アミノ酸およびポリペプチドのpHは、6.5以上とする。一方、pHが12超えのアミノ酸やポリペプチドは少ないが、これらはフィルムにダメージを及ぼす可能性がある。なお、この場合のpHが6.5〜12とは、水溶液中で合計で0.03〜1質量%となるようにアミノ酸および/またはポリペプチドを溶解した時の50℃でのpHが6.5〜12である。以降、「水溶液中で合計で0.03〜1質量%となるようにアミノ酸および/またはポリペプチドを溶解した時の50℃でのpHが6.5〜12」を、略して「pHが6.5〜12」と記載することとする。
また、本発明において、ポリペプチドとは、アミノ酸がペプチド結合により2つ以上縮合した高分子化合物とする。ポリペプチドは天然たんぱく質の部分加水分解による生成、またはアミノ酸の脱水縮合により合成される。さらに、pH6.5〜12という条件を満たす限り、天然たんぱく質もポリペプチドに含むこととする。
そして、本発明における、pHが6.5〜12である、アミノ酸およびポリペプチドは、ポリエステルフィルムを劣化させず、またフィルム中にも残留しにくいので簡易の洗浄で十分洗い落とすことができる。さらに、ラミネート金属板および装置両方の腐食を抑制することが十分に可能である。
0.03 to 1% by mass in total of at least one selected from amino acids and polypeptides having a pH of 6.5 to 12
The amino acids and polypeptides of the present invention contain both a carboxyl group and an amino group in the molecule, and have a structure with a large number of amino groups, so that they are adsorbed on the metal surface by the amino group and sufficiently suppress the corrosion of the metal. On the other hand, by including a carboxyl group, it is possible to suppress deterioration of the polyester resin used for the laminate film. In order to obtain such an effect, the pH of amino acids and polypeptides should be 6.5 or higher. On the other hand, although there are few amino acids and polypeptides whose pH exceeds 12, these may cause damage to the film. In addition, pH in this case is 6.5-12. When amino acid and / or polypeptide are melt | dissolved so that it may become 0.03-1 mass% in total in aqueous solution, pH at 50 degreeC is 6. 5-12. Hereinafter, “pH of 6.5 to 12 at 50 ° C. when amino acids and / or polypeptides are dissolved so that the total amount is 0.03 to 1% by mass in an aqueous solution” is abbreviated as “pH is 6”. .5-12 ".
In the present invention, a polypeptide is a polymer compound in which two or more amino acids are condensed by peptide bonds. Polypeptides are synthesized by partial hydrolysis of natural proteins or by dehydration condensation of amino acids. Furthermore, as long as the condition of pH 6.5 to 12 is satisfied, the natural protein is included in the polypeptide.
The amino acids and polypeptides having a pH of 6.5 to 12 in the present invention do not deteriorate the polyester film and hardly remain in the film, so that they can be sufficiently washed out by simple washing. Furthermore, it is possible to suppress corrosion of both the laminated metal plate and the device.
また、本発明では、アミノ酸およびポリペプチド成分の中から選ばれる1種以上を合計で0.03〜1質量%含有することとする。0.03質量%未満では腐食の抑制効果が低い。一方、1質量%超えでも防錆効果にあまり変わりなく、一方で、簡易洗浄では洗い落としにくくなり、コスト面からも不適である。好ましくは、合計で0.05〜0.5質量%である。 Moreover, in this invention, it shall contain 0.03-1 mass% in total of 1 or more types chosen from an amino acid and polypeptide component. If it is less than 0.03% by mass, the effect of inhibiting corrosion is low. On the other hand, even if it exceeds 1% by mass, the rust-preventing effect does not change much. On the other hand, it is difficult to wash off by simple cleaning, which is unsuitable from the viewpoint of cost. Preferably, it is 0.05-0.5 mass% in total.
上記組成のアミノ酸およびポリペプチドを水に溶かし、水性クーラントの基本組成とする。溶媒となる水としては、水道水、イオン交換水、蒸留水などいずれもそのまま使用可能である。 The amino acid and polypeptide having the above composition are dissolved in water to obtain the basic composition of the aqueous coolant. As water used as a solvent, tap water, ion exchange water, distilled water, etc. can be used as they are.
以上のように、本発明では、上記のように、pHが6.5〜12であるアミノ酸および/またはポリペプチドを用いることができる。また、アミノ酸としては、タンパク質構成アミノ酸、タンパク質非構成アミノ酸ともに用いることができる。
食品安全性も高くまた入手も容易な点からは、前記アミノ酸は、ヒスチジン、アルギニン、リシン、オキシリシン、テアニンから選ばれる1種以上であることが好ましい。
As described above, in the present invention, as described above, amino acids and / or polypeptides having a pH of 6.5 to 12 can be used. As amino acids, both protein-constituting amino acids and protein non-constituting amino acids can be used.
From the viewpoint of high food safety and easy availability, the amino acid is preferably at least one selected from histidine, arginine, lysine, oxylysine, and theanine.
前記ポリペプチドは、ヒスチジン、アルギニン、リシン、オキシリシンから選ばれる1種以上のアミノ酸を40質量%以上含むことが好ましい。これら食品安全性の高いアミノ酸を多く含むことにより、pHが6.5〜12で安全性の高いポリペプチドが得られる。例えば、かつお節の抽出成分からは、ヒスチジンを50%以上含むpH7付近のポリペプチドが得られ、またその成分であるアンセリン、カルノシンもヒスチジンを含むジペプチドであり、好適である。
50℃におけるpHが6〜8
ラミネート金属板のDI成形におけるクーラント温度は50℃前後に調節される。そのため、その温度域でのクーラント物性が重要となる。金属板の場合はアミン等を加えてアルカリ性に調節されるのに対し、本発明で用いるラミネート金属板に適当なpHとしては、ほぼ中性の領域のpH6〜8が最適である。なお、この場合の50℃におけるpHが6〜8とは、上記アミノ酸およびポリペプチドの中から選ばれる1種以上を水性クーラント中に添加した場合、および、上記アミノ酸およびポリペプチドの中から選ばれる1種以上に加え、さらにその他の添加剤も水性クーラント中に添加した場合の50℃におけるpHである。pHが6.5〜12のアミノ酸および/またはポリペプチドを添加するため、pHが高すぎる場合は、酢酸やクエン酸等のカルボン酸やアミノ酸の添加によりpHを低下させる。pHが8より高いとフィルムが劣化しやすく、pHが6より低いと下地の金属板が腐食しやすい。
The polypeptide preferably contains 40% by mass or more of one or more amino acids selected from histidine, arginine, lysine and oxylysine. By containing many amino acids having high food safety, a highly safe polypeptide having a pH of 6.5 to 12 can be obtained. For example, from the extract component of bonito, a polypeptide near pH 7 containing 50% or more of histidine is obtained, and its components, anserine and carnosine, are also dipeptides containing histidine.
PH at 50 ° C. is 6-8
The coolant temperature in DI molding of the laminated metal plate is adjusted to around 50 ° C. Therefore, the coolant physical properties in that temperature range are important. In the case of a metal plate, it is adjusted to be alkaline by adding an amine or the like, whereas the pH suitable for the laminated metal plate used in the present invention is optimally pH 6 to 8 in a substantially neutral region. In this case, the pH of 6 to 8 at 50 ° C. is selected from the case where one or more selected from the above amino acids and polypeptides are added to the aqueous coolant, and from the above amino acids and polypeptides. The pH at 50 ° C. when one or more other additives are added to the aqueous coolant. Since amino acids and / or polypeptides having a pH of 6.5 to 12 are added, if the pH is too high, the pH is lowered by adding a carboxylic acid such as acetic acid or citric acid or an amino acid. If the pH is higher than 8, the film tends to deteriorate, and if the pH is lower than 6, the underlying metal plate tends to corrode.
さらに、本発明では、食品安全性を損なわない限り腐食抑制を補助するような他の防錆剤を添加することができる。 Furthermore, in this invention, the other rust preventive agent which assists corrosion suppression can be added unless food safety is impaired.
防錆剤
補助的に添加する防錆成分としては、1)オクタン酸、ナフテン酸、アルケニルコハク酸、セバシン酸、オレイン酸、ラノリン酸、カプリル酸、ペラルゴン酸、ラウリン酸、リシノール酸、(4−ノニルフェノキシ)酢酸等のカルボン酸類、上記カルボン酸類のエステル、または上記カルボン酸類の金属塩(Na、K、Ca、Mg等)の中から選ばれる1種以上、2)石油スルホン酸、ジノニルナフタレンスルホン酸、アルキルベンゼンスルホン酸、アルキルナフタレンスルホン酸等のスルホン酸類、上記スルホン酸類のエステル、または上記スルホン酸類の金属塩(Na、K、Ca、Mg等)の中から選ばれる1種以上、3)ホウ酸、ケイ酸、リン酸等の酸類、ホウ酸、ケイ酸、リン酸等の各々のエステル、またはホウ酸、ケイ酸、リン酸等の各々の金属塩(Na、K、Ca、Mg等)の中から選ばれる1種以上が好適に用いられる。そして、上記1)〜3)を添加するにあたっては、1)〜3)の中から選ばれる1種を単独で添加してもよいし、1)〜3)の中から選ばれる1種以上を複合添加してもよい。
上記成分はポリエステルフィルムを劣化させず、またフィルム中にも残留しにくいので簡易の洗浄で十分洗い落とすことができる。そして、ラミネート金属板および装置両方の腐食を抑制することが十分に可能である。
上記防錆成分の含有量は0.03〜1質量%が好ましい。0.03質量%未満では腐食の抑制効果が低い。一方、1質量%超えでも防錆効果にあまり変わりなく、一方で、簡易洗浄では洗い落としにくくなり、コスト面からも不適である。さらに好ましくは、0.05〜0.5質量%である。
As rust preventive components to be added as a rust preventive auxiliary agent, 1) octanoic acid, naphthenic acid, alkenyl succinic acid, sebacic acid, oleic acid, lanolinic acid, caprylic acid, pelargonic acid, lauric acid, ricinoleic acid, (4- Nonylphenoxy) One or more selected from carboxylic acids such as acetic acid, esters of the above carboxylic acids, or metal salts (Na, K, Ca, Mg, etc.) of the above carboxylic acids, 2) petroleum sulfonic acid, dinonylnaphthalene One or more selected from sulfonic acids such as sulfonic acids, alkylbenzene sulfonic acids, alkylnaphthalene sulfonic acids, esters of the above sulfonic acids, or metal salts of the above sulfonic acids (Na, K, Ca, Mg, etc.) 3) Boric acid, silicic acid, phosphoric acid and other acids, boric acid, silicic acid, phosphoric acid and other esters, boric acid, silicic acid, Each metal salt such as phosphate (Na, K, Ca, Mg, etc.) one or more selected from among is suitably used. And in adding said 1) -3), 1 type chosen from 1) -3) may be added independently, and 1 or more types chosen from 1) -3) are added. Multiple additions may be made.
The above components do not deteriorate the polyester film and do not easily remain in the film, so that they can be sufficiently washed out by simple washing. And it is possible to suppress corrosion of both the laminated metal plate and the apparatus.
The content of the rust preventive component is preferably 0.03 to 1% by mass. If it is less than 0.03% by mass, the effect of inhibiting corrosion is low. On the other hand, even if it exceeds 1% by mass, the rust-preventing effect does not change much. On the other hand, it is difficult to wash off by simple cleaning, which is unsuitable from the viewpoint of cost. More preferably, it is 0.05-0.5 mass%.
さらに、本発明では、上記に加え、所望により他の添加剤、例えば、油性剤、界面活性剤、清浄剤、分散剤、酸化防止剤、防腐剤、消泡剤、金属イオン封止剤等を適宜配合してもよい。添加剤の配合量は、特に限定されず、常法に従って適宜調製すればよい。 Furthermore, in the present invention, in addition to the above, if desired, other additives such as oily agents, surfactants, detergents, dispersants, antioxidants, preservatives, antifoaming agents, metal ion sealing agents and the like are added. You may mix | blend suitably. The compounding amount of the additive is not particularly limited, and may be appropriately prepared according to a conventional method.
油性剤
油性剤としては、脂肪酸、脂肪酸エステル、高級アルコール等があり、脂肪酸としては、例えば、ステアリン酸等の直鎖飽和脂肪酸、オレイン酸等のモノエン不飽和脂肪酸、ポリエン不飽和脂肪酸、脂環式脂肪酸、モノヒドロキシ脂肪酸、ジヒドロキシ脂肪酸等が挙げられ、脂肪酸エステルとしては、例えば、上記脂肪酸のアルキルアルコ−ルとのエステル(メチルエステル、エチルエステル、プロピルエステル、ブチルエステル、ペンチルエステル、ヘキシルエステル、オクチルエステル、ノニルエステル、デカンエステル、ウンデカンエステル、ドデカンエステル、テトラデカンエステル、ヘキサデカンエステル、オクタデカンエステル)やトリメチロ−ルプロパン、ペンタリスリト−ルとのエステル等が挙げられる。また、高級アルコールとしては、ラウリルアルコールやオレイルアルコールが挙げられる。
Examples of oily agents include fatty acids, fatty acid esters, higher alcohols, and the like, for example, linear saturated fatty acids such as stearic acid, monoene unsaturated fatty acids such as oleic acid, polyene unsaturated fatty acids, alicyclic Fatty acid, monohydroxy fatty acid, dihydroxy fatty acid and the like can be mentioned. Examples of fatty acid esters include esters of the above fatty acids with alkyl alcohols (methyl esters, ethyl esters, propyl esters, butyl esters, pentyl esters, hexyl esters, octyls). Ester, nonyl ester, decane ester, undecane ester, dodecane ester, tetradecane ester, hexadecane ester, octadecane ester), ester with trimethylolpropane, pentalithitol, and the like. Further, examples of the higher alcohol include lauryl alcohol and oleyl alcohol.
界面活性剤
界面活性剤としては、ノニオン系、アニオン系、カチオン系または両性系界面活性剤を用いることができ、これらの中でも、特に、ノニオン系界面活性剤が好ましい。ノニオン系界面活性剤としては、具体的には、アルキルポリエチレンオキサイドエーテル、アルキルポリプロピレンオキサイドポリエチレンオキサイドエーテル、プルロニック、テトロニック等のポリエチレンオキサイドエーテル系界面活性剤、ソルビタン脂肪酸エステル、脂肪酸シュガーエステル、グリセリン脂肪酸エステル、ペンタエリスリトール脂肪酸エステル等の多価アルコール脂肪酸エステル系界面活性剤、ポリエチレンオキサイド脂肪酸エステル、ソルビタンポリエチレンオキサイド脂肪酸エステル、ソルビトールポリエチレンオキサイド脂肪酸エステル、ペンタエリスリトールポリエチレンオキサイド脂肪酸エステル、ひまし油ポリエチレンオキサイド等のポリエチレンオキサイドエステル系界面活性剤等が挙げられる。
上記ノニオン系界面活性剤とアニオン系界面活性剤を併用することもできる。さらに公知のカチオン系界面活性剤、両性系界面活性剤を用いることもできる。
As the surfactant surfactant, nonionic, anionic, cationic or amphoteric surfactants can be used, and among these, nonionic surfactants are particularly preferable. Specific examples of nonionic surfactants include polyethylene oxide ether surfactants such as alkyl polyethylene oxide ether, alkyl polypropylene oxide polyethylene oxide ether, pluronic and tetronic, sorbitan fatty acid ester, fatty acid sugar ester, glycerin fatty acid ester. , Polyhydric alcohol fatty acid ester surfactants such as pentaerythritol fatty acid ester, polyethylene oxide fatty acid ester, sorbitan polyethylene oxide fatty acid ester, sorbitol polyethylene oxide fatty acid ester, pentaerythritol polyethylene oxide fatty acid ester, castor oil polyethylene oxide, etc. Surfactant etc. are mentioned.
The nonionic surfactant and the anionic surfactant can be used in combination. Furthermore, known cationic surfactants and amphoteric surfactants can also be used.
清浄剤
清浄剤としては、アルカリ金属またはアルカリ土類金属スルホネート、アルカリ金属またはアルカリ土類金属サルシレート、アルカリ金属またはアルカリ土類金属フェネート、脂肪酸石けん等が挙げられる。
Examples of the detergent cleaner include alkali metal or alkaline earth metal sulfonate, alkali metal or alkaline earth metal salicylate, alkali metal or alkaline earth metal phenate, and fatty acid soap.
分散剤
分散剤としては、アルケニルコハク酸イミド、非イオン系界面活性剤等が挙げられる。
Examples of the dispersant include alkenyl succinimides and nonionic surfactants.
酸化防止剤
酸化防止剤としては、2,6−ジ−tert−ブチル−p−クレゾール(DBPC)等のフェノール化合物、4,4‘メチレンビス(2,6−ジ−tert−ブチルフェノール)等のビスフェノール化合物などが挙げられる。
Antioxidants As antioxidants, phenol compounds such as 2,6-di-tert-butyl-p-cresol (DBPC), bisphenol compounds such as 4,4'methylenebis (2,6-di-tert-butylphenol) Etc.
防腐剤
防腐剤としては、フェノール系、トリアジン系又はイソチアゾリン系等が代表的であるが、具体的には、フェノール系としては、o−フェニルフェノール、Na−o−フェニルフェノール、2,3,4,6−テトラクロロフェノール等が挙げられる。トリアジン系としては、ヘキサヒドロ−1,3,5−トリス(2−ヒドロキシエチル)−1,3,5−トリアジン等が挙げられる。イソチアゾリン系としては、1,2−ベンゾイソチアゾリン−3−オン、5−クロロ−2−メチル−4−イソチアゾリン−3−オン、2−メチル−イソチアゾリン−3−オン等が挙げられる。
Typical examples of the antiseptics include phenolic, triazine-based, and isothiazoline-based compounds. Specific examples of the phenolic-based compounds include o-phenylphenol, Na-o-phenylphenol, 2,3,4. , 6-tetrachlorophenol and the like. Examples of triazines include hexahydro-1,3,5-tris (2-hydroxyethyl) -1,3,5-triazine. Examples of the isothiazoline series include 1,2-benzisothiazoline-3-one, 5-chloro-2-methyl-4-isothiazoline-3-one, and 2-methyl-isothiazoline-3-one.
消泡剤
消泡剤としては、シリコーンのエマルション、高級アルコール、金属石けん、エチレン−プロピレンコポリマー等を挙げることができる。
Examples of antifoaming agents include silicone emulsions, higher alcohols, metal soaps, and ethylene-propylene copolymers.
本発明におけるラミネート金属板の素材としては、鋼板、アルミニウム素材が使用可能であるが、経済性から安価な鋼板が好ましい。ラミネート下地用の鋼板としては、クロムめっき鋼板またはぶりき鋼板が使用可能である。クロムめっき鋼板(ティンフリースチール)としては、表面に付着量50〜200mg/m2の金属クロム層と、金属クロム換算の付着量が3〜30mg/m2のクロム酸化物層を前記金属クロム層の表面に有することが好ましい。ぶりきは、0.5〜15g/m2のめっき量を有するものが好ましい。板厚は、特に限定されないが、例えば、0.15〜0.30mmの範囲のものが好適に使用できる。 As a material of the laminated metal plate in the present invention, a steel plate or an aluminum material can be used, but an inexpensive steel plate is preferable from the viewpoint of economy. As the steel sheet for the laminate base, a chrome-plated steel sheet or a tinted steel sheet can be used. Chromium The plated steel sheet (tin-free steel), a metal layer of chromium coating weight 50-200 mg / m 2 on a surface, said metallic chromium layer of chromium oxide layer of the deposited amount 3 to 30 mg / m 2 of metallic chromium conversion It is preferable to have on the surface. The tinplate preferably has a plating amount of 0.5 to 15 g / m 2 . Although plate | board thickness is not specifically limited, For example, the thing of the range of 0.15-0.30 mm can be used conveniently.
次いで、本発明におけるラミネート金属板を構成する樹脂層について説明する。本発明のラミネート金属板を構成する樹脂層はポリエステル樹脂を基本とする。ポリエステル樹脂フィルムは、機械的強度に優れ、摩擦係数が小さく潤滑性が良好で、ガスや液体に対する遮蔽効果すなわちバリア性に優れ、かつ安価である。従って、DI成形のように、伸び率が300%にもなる加工度の高い成形にも十分に耐えることができ、皮膜は成形後も健全である。
ポリエステル樹脂のジカルボン酸成分はテレフタル酸を主成分とし、ジオール成分は、エチレングリコールを主成分とする。そして、ポリエステル樹脂層の加工性と強度のバランスから、共重合成分として、8mol%以上20mol%以下のイソフタル酸成分を含有することが好ましい。また、結晶化温度は120〜160℃であることが好ましい。
共重合成分比率が低い場合、分子が配向し易く、加工度が高くなると、フィルム剥離が発生したり、缶高さ方向に平行な亀裂(破断)が生じる傾向にある。また、加工後の缶体に熱処理を施した場合も同様に配向が進む。配向のし難さの点からは、共重合成分の比率は高いほど良いが、20mol%を超えるとフィルムコストが高くなるため経済性が劣る他、フィルムが柔軟になり傷付き性や耐薬品性が低下する可能性がある。
結晶化温度については、120℃より低いと非常に結晶化しやすいため高加工度の加工ではフィルム樹脂にクラックやピンホールが発生する場合がある。一方、160℃より高い場合は結晶化スピードが非常に遅いため、150℃以上の熱処理でも十分に結晶化せずフィルムの強度や耐久性が損なわれる場合がある。
さらに、樹脂層中には顔料や滑剤、安定剤などの添加剤を加えて用いても良いし、他の機能を有する樹脂層を上層または下地鋼板との中間層に配置して2層以上の樹脂層にしても良い。樹脂層の厚みについては、5μm以上50μm以下のものが好適に使用できる。
本発明におけるラミネート金属板は、前述した金属板に前述したポリエステル樹脂層を両面に有する。金属板への樹脂のラミネート方法は特に限定されない。2軸延伸フィルム、あるいは無延伸フィルムを熱圧着させる熱圧着法、Tダイなどを用いて金属板上に直接樹脂層を形成させる押し出し法など適宜選択することができる。さらに、ポリエステルウレタン系、飽和ポリエステル系等の接着剤を使用して、ポリエステル樹脂フィルムを下地金属板に貼り合わせることも可能であり、いずれの方法でも十分な効果が得られることが確認されているが、特に熱圧着法が、下地金属との密着性にも優れ、また接着剤を必要としない等の理由で経済的にも有利である。
Subsequently, the resin layer which comprises the laminated metal plate in this invention is demonstrated. The resin layer constituting the laminated metal plate of the present invention is based on a polyester resin. The polyester resin film is excellent in mechanical strength, has a small coefficient of friction and good lubricity, has an excellent shielding effect against gas and liquid, that is, barrier property, and is inexpensive. Therefore, it can sufficiently withstand the forming with a high degree of processing such as the DI forming with an elongation of 300%, and the film is sound after the forming.
The dicarboxylic acid component of the polyester resin has terephthalic acid as the main component, and the diol component has ethylene glycol as the main component. And it is preferable to contain 8 mol% or more and 20 mol% or less of isophthalic acid components as a copolymerization component from the balance of workability and strength of the polyester resin layer. The crystallization temperature is preferably 120 to 160 ° C.
When the copolymer component ratio is low, the molecules are easily oriented, and when the degree of processing increases, film peeling tends to occur or cracks (breaks) parallel to the can height direction tend to occur. Further, when the processed can body is subjected to a heat treatment, the orientation proceeds in the same manner. From the standpoint of difficulty in orientation, the higher the ratio of the copolymer component, the better. However, if it exceeds 20 mol%, the film cost becomes high, resulting in poor economics, and the film becomes flexible, scratching and chemical resistance. May be reduced.
With respect to the crystallization temperature, if it is lower than 120 ° C., it is very easy to crystallize, so that cracking and pinholes may occur in the film resin in processing with a high degree of processing. On the other hand, when the temperature is higher than 160 ° C., the crystallization speed is very slow. Therefore, even when heat treatment at 150 ° C. or higher, the film is not sufficiently crystallized and the strength and durability of the film may be impaired.
Furthermore, in the resin layer, additives such as pigments, lubricants and stabilizers may be added and used, or a resin layer having other functions may be arranged in an upper layer or an intermediate layer with the base steel plate to form two or more layers. It may be a resin layer. With respect to the thickness of the resin layer, a thickness of 5 μm or more and 50 μm or less can be suitably used.
The laminated metal plate in the present invention has the above-described polyester resin layer on both sides of the above-described metal plate. The method for laminating the resin on the metal plate is not particularly limited. A thermocompression bonding method in which a biaxially stretched film or an unstretched film is thermocompression bonded, an extrusion method in which a resin layer is directly formed on a metal plate using a T die, or the like can be appropriately selected. Furthermore, it is possible to bond a polyester resin film to a base metal plate using an adhesive such as polyester urethane or saturated polyester, and it has been confirmed that any method can provide a sufficient effect. However, the thermocompression bonding method is also economically advantageous because it has excellent adhesion to the base metal and does not require an adhesive.
本発明のDI成形では、市販のカッピングプレス、およびDIプレス装置が使用可能であり、その仕様による差はない。本発明のラミネート金属板DI成形用水性クーラントはDIプレス装置でのしごき成形(および再絞り成形)に用いられ、装置内を循環して成形時の冷却を行う。一方、カッピングプレスの絞り加工時の潤滑としては、ラミネート金属板表面にワックスを塗布することが好ましく、融点30〜80℃のパラフィンや脂肪酸エステル系のワックスを10〜500mg/m2塗布したものが良好な成形性を示す。
DIプレス装置での成形後は、洗浄すること無しにそのまま乾燥処理を行って使用することもできるが、洗浄して使用する場合は水による洗浄で十分である。洗浄水に界面活性剤や防錆剤等の添加剤を添加して、洗浄性をさらに高めることや腐食の抑制を行うことも可能である。
また、その後に乾燥とフィルムの密着性向上のために60℃以上樹脂層融点以下での乾燥処理を行うことが好ましく、さらに好ましくは200℃以上で乾燥処理することが好ましい。
In the DI molding of the present invention, a commercially available cupping press and DI press apparatus can be used, and there is no difference depending on the specifications. The water-based coolant for forming a laminated metal sheet DI of the present invention is used for ironing (and redrawing) in a DI press device, and circulates in the device to cool during forming. On the other hand, as the lubrication during the drawing process of the cupping press, it is preferable to apply a wax to the surface of the laminated metal plate, and a coating of 10 to 500 mg / m 2 of paraffin or fatty acid ester wax having a melting point of 30 to 80 ° C. Good moldability.
After molding in the DI press apparatus, it can be used as it is without being washed, but can be used as it is, but when washed and used, washing with water is sufficient. Additives such as surfactants and rust preventives can be added to the cleaning water to further improve cleaning properties and to suppress corrosion.
In order to improve drying and film adhesion, it is preferable to carry out a drying treatment at a temperature not lower than 60 ° C. and not higher than the melting point of the resin layer, more preferably at 200 ° C. or higher.
以下、本発明の実施例について説明する。 Examples of the present invention will be described below.
「ラミネート鋼板の作製」
厚さ0.20mmのテンパー度T3のクロムめっき鋼板(金属Cr層:120mg/m2、Cr酸化物層:金属Cr換算で10mg/m2)を下地原板として用い、この原板に対して、2軸延伸法で作製された厚さ25μmのイソフタル酸10%共重合ポリエチレンテレフタレートフィルムを、240℃に加熱した鋼板上にニップロールを用いて圧着し、その後1秒以内に水冷、乾燥することにより、ラミネートDI缶用ラミネート鋼板を作製した。
"Production of laminated steel sheet"
A chrome-plated steel sheet having a thickness of 0.20 mm and a tempering degree T3 (metal Cr layer: 120 mg / m 2 , Cr oxide layer: 10 mg / m 2 in terms of metal Cr) was used as the base original plate, A 25% thick 10% copolymerized polyethylene terephthalate film of isophthalic acid produced by the axial stretching method is pressure-bonded onto a steel plate heated to 240 ° C. using a nip roll, and then cooled with water and dried within 1 second to laminate. A laminated steel sheet for DI cans was produced.
「缶体成形」
上記により得られたラミネート鋼板を用いて、以下に示す条件によりDI成形して缶を成形した。また、DI成形後に、ストリッピング性、DI成形性(成形後の缶外面フィルム健全性)、耐食性(缶内面の健全性)を、以下に述べる性能試験によって評価した。なお、上記DI成形性、上記耐食性の評価については、DI成形で作られたDI缶に対し、50℃のイオン交換水で2分間スプレーして表面を洗浄し、次いで、200℃の乾燥炉で30秒間乾燥した後に、下記の試験を行った。得られた結果を表1に示す。
"Can body molding"
Using the laminated steel sheet obtained as described above, a can was formed by DI molding under the following conditions. Moreover, stripping property, DI moldability (film outer surface soundness after molding), and corrosion resistance (can inner surface soundness) were evaluated by the performance test described below after DI molding. In addition, about evaluation of the said DI moldability and the said corrosion resistance, it sprays with 50 degreeC ion-exchange water for 2 minutes with respect to DI can made by DI shaping | molding, Then, it is 200 degreeC drying oven. After drying for 30 seconds, the following tests were conducted. The obtained results are shown in Table 1.
「DI成形」
DI成形は、まずラミネート鋼板の両面に融点45℃のパラフィンワックスを50mg/m2塗布した後に、123mmφのブランクを打ち抜き、そのブランクを市販のカッピングプレスで、内径71mmφ、高さ36mmのカップに絞り成形した。次いでこのカップを市販のDIプレス装置に装入して、ポンチスピード200mm/s、ストローク560mmで、再絞り加工及び3段階のアイアニング加工(それぞれのリダクション20%、19%、23%)を行い、最終的に缶内径52mm、缶高さ90mmの缶を成形した。なお、DI成形中には、表1に示す組成のクーラントを50℃の温度で循環させた。また、表1に記載のクーラントは水としての水道水を使用した。
"DI molding"
In DI molding, 50 mg / m 2 of paraffin wax having a melting point of 45 ° C. was applied to both surfaces of a laminated steel sheet, and then a 123 mmφ blank was punched out, and the blank was squeezed into a cup with an inner diameter of 71 mmφ and a height of 36 mm using a commercially available cupping press Molded. Next, this cup was inserted into a commercially available DI press machine, and redrawing and three-stage ironing (reduction 20%, 19%, 23%, respectively) were performed at a punch speed of 200 mm / s and a stroke of 560 mm. Finally, a can having an inner diameter of 52 mm and a height of 90 mm was formed. During DI molding, a coolant having the composition shown in Table 1 was circulated at a temperature of 50 ° C. Moreover, the coolant of Table 1 used the tap water as water.
(1)ストリッピング性
DI成形時に、成形された缶体からポンチが引抜かれる際に、缶体の開口端がストリッパーにひっかかり缶の開口部端が歪む現象を、下記のように評価した。
(評価)
開口端に発生した歪みがトリミング部にまで達する:×
開口端に歪みが発生するが、その歪みがトリミング部にまで達しない:△
開口端に歪みが発生するが、その歪みが開口端の耳の部分に留まる:○
開口端に歪み無し:◎
(2)DI成形性(成形後の缶外面フィルム健全性)
成形後の缶外面フィルムの健全性(フィルム欠陥の少ないものが良好)により評価を行った。洗浄、乾燥後のDI缶について、DI缶の鋼板に通電できるように缶口にやすりで傷をつけた後に、電解液(NaCl1%溶液、温度25℃)を入れた容器(DI缶よりやや大きい)にDI缶を、底を下にして入れて缶の外面だけが電解液に接するようにした。その後缶体と電解液間に6.2Vの電圧を付与した時に測定される電流値に応じて下記のように評価した。
(評価)
5mA超:×
0.5mA超、5mA以下:△
0.05mA超、0.5mA以下:○
0.05mA以下:◎
(3)耐食性(缶内面の健全性)
缶内面フィルムの健全性(フィルム欠陥の少ないものが良好)については、洗浄、乾燥後のDI缶について、DI缶の鋼板に通電できるように、やすりで缶口に傷をつけた後に、缶内に電解液(NaCl1%溶液、温度25℃)を注ぎ缶口まで満たし、その後缶体と電解液間に6.2Vの電圧を付与した。この時測定される電流値に応じて下記のように評価した。
(評価)
1mA超:×
0.1mA超、1mA以下:△
0.01mA超、0.1mA以下:○
0.01mA以下:◎
(1) Stripping property When the punch was pulled out from the molded can body during the DI molding, the phenomenon that the opening end of the can body was caught by the stripper and the opening end of the can was distorted was evaluated as follows.
(Evaluation)
The distortion generated at the open end reaches the trimming part: ×
Although distortion occurs at the opening end, the distortion does not reach the trimming part: Δ
Distortion occurs at the open end, but the distortion remains at the ear at the open end: ○
No distortion at the open end: ◎
(2) DI moldability (can film outer film soundness after molding)
Evaluation was performed based on the soundness of the outer film of the can after molding (those having few film defects are good). After cleaning and drying the DI can, the container can be energized with a file so that the steel plate of the DI can can be energized, and then the container containing the electrolyte (NaCl 1% solution, temperature 25 ° C.) is slightly larger than the DI can The DI can was placed with the bottom facing down so that only the outer surface of the can was in contact with the electrolyte. Thereafter, evaluation was performed as follows according to the current value measured when a voltage of 6.2 V was applied between the can and the electrolyte.
(Evaluation)
Over 5 mA: ×
More than 0.5 mA, 5 mA or less: △
More than 0.05 mA, 0.5 mA or less: ○
0.05 mA or less: ◎
(3) Corrosion resistance (soundness of the inner surface of the can)
Regarding the soundness of the inner film of the can (those with fewer film defects are good), after cleaning and drying the DI can, the can mouth is scratched with a file so that the steel plate of the DI can be energized. An electrolyte solution (NaCl 1% solution, temperature 25 ° C.) was poured into the can and filled up to the can, and then a voltage of 6.2 V was applied between the can and the electrolyte. Evaluation was made as follows according to the current value measured at this time.
(Evaluation)
Over 1 mA: ×
More than 0.1 mA, 1 mA or less: △
More than 0.01 mA, 0.1 mA or less: ○
0.01 mA or less: ◎
表1より、本発明例であるクーラントC1〜C17を用いた場合は、ストリッピング性、DI成形性、耐食性のいずれも良好であった。一方、比較例であるクーラントC18〜C24を用いた場合は、ストリッピング性、DI成形性、耐食性のいずれか1つ以上が劣っていた。 From Table 1, when coolant C1-C17 which is an example of this invention was used, stripping property, DI moldability, and corrosion resistance were all favorable. On the other hand, when the coolants C18 to C24, which are comparative examples, were used, any one or more of stripping properties, DI moldability, and corrosion resistance were inferior.
Claims (4)
前記アミノ酸は、ヒスチジン、アルギニン、リシン、オキシリシン、テアニンから選ばれる1種以上であることを特徴とするラミネート金属板DI成形用水性クーラント。
ただし、前記pHが6.5〜12である、アミノ酸およびポリペプチドとは、水溶液中で合計で0.03〜1質量%となるようにアミノ酸およびポリペプチドの中から選ばれる1種以上を溶解した時の50℃でのpHが6.5〜12である。 pH is 6.5 to 12, comprising 0.03 to 1 wt% of one or more selected from among amino acids and polypeptides in total, Ri pH 6 to 8 der at 50 ° C.,
The water-based coolant for forming a laminated metal sheet DI , wherein the amino acid is at least one selected from histidine, arginine, lysine, oxylysine, and theanine .
However, the amino acid and the polypeptide having the pH of 6.5 to 12 dissolve at least one selected from the amino acid and the polypeptide so that the total amount in the aqueous solution is 0.03 to 1% by mass. The pH at 50 ° C. is 6.5-12.