JP5201792B2 - 液状硬化性樹脂組成物 - Google Patents
液状硬化性樹脂組成物 Download PDFInfo
- Publication number
- JP5201792B2 JP5201792B2 JP2005354760A JP2005354760A JP5201792B2 JP 5201792 B2 JP5201792 B2 JP 5201792B2 JP 2005354760 A JP2005354760 A JP 2005354760A JP 2005354760 A JP2005354760 A JP 2005354760A JP 5201792 B2 JP5201792 B2 JP 5201792B2
- Authority
- JP
- Japan
- Prior art keywords
- acrylate
- meth
- resin composition
- curable resin
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
硬化速度は、ラジカル重合性モノマーや光重合開始剤の選択等により、ある程度高くすることが可能であることが知られている。例えば、高速硬化性に有効な代表的なラジカル重合性モノマーであるN−ビニルカプロラクタムやN−ビニルピロリドン等の環状構造を有するN−ビニル化合物を採用すると共に、光増感剤としてジエチルアミン等の塩基性化合物を併用する等の技術が用いられることがある(特許文献1〜3)。
(A)ポリエーテルポリオール由来の構造を有するウレタン(メタ)アクリレート 35〜85質量%、
(B)(A)以外のエチレン性不飽和基含有化合物 1〜60質量%、
(C)アミン系光増感剤 0.01〜1質量%、及び
(D)光重合開始剤 0.01〜10質量%
を含有する液状硬化性樹脂組成物であって、高周波プラズマ発光・質量分析法(ICP−MS)により求めた組成物中の亜鉛及びコバルト元素の合計含有量が0.5〜10ppmである、液状硬化性樹脂組成物を提供するものである。
また、本発明は、当該液状硬化性樹脂組成物を、放射線により硬化せしめることにより得られる光ファイバ被覆層及び当該被覆層を有する光ファイバを提供するものである。
これらの水酸基含有(メタ)アクリレート化合物は1種単独で、あるいは2種以上組み合わせて使用できる。
また、(A)ウレタン(メタ)アクリレートとしては、ポリプロピレングリコールに由来する構造を有するウレタン(メタ)アクリレートが好ましい。
(C)成分の好ましい具体例としては、トリエチルアミン、ジエチルアミン、ジプロピルアミン、ジブチルアミン、N−メチルジエタノールアミン、エタノールアミン、4−ジメチルアミノ安息香酸、4−ジメチルアミノ安息香酸メチル、4−ジメチルアミノ安息香酸エチル、4−ジメチルアミノ安息香酸イソアミル等を挙げることができる。これらは、1種単独で用いることもできるし、2種以上を併用することもできる。市販品としては、ユベクリルP102、103、104、105(以上、UCB社製)等が挙げられる。
撹拌機を備えた反応容器に、亜鉛及びコバルト化合物を6〜8ppm含んだ数平均分子量が2000のポリプロピレングリコール50.968部、イソホロンジイソシアネート7.920部、2,6−ジ−t−ブチル−p−クレゾール0.015部、フェノチアジン0.005部を仕込み、これらを撹拌しながら液温度が15℃となるまで冷却した。ジブチル錫ジラウレート0.49部を添加した後、攪拌しながら液温度を1時間かけて35℃まで徐々に上げた。その後、液温度を50℃に上げて反応させた。残留イソシアネート基濃度が1.45質量%(仕込量に対する割合)以下となった後、2−ヒドロキシエチルアクリレート2.365部を添加し、液温度約60℃にて撹拌し、反応させた。残留イソシアネート基濃度が0.1質量%以下になった時を反応終了とした。得られたウレタンアクリレートオリゴマーをオリゴマーAとする。
撹拌機を備えた反応容器に、亜鉛及びコバルト化合物を6〜8ppm含んだ数平均分子量が2000のポリプロピレングリコール66.78部、2,4−トリレンジイソシアネート8.141部、2,6−ジ−t−ブチル−p−クレゾール0.019部、フェノチアジン0.005部を仕込み、これらを撹拌しながら液温度が15℃となるまで冷却した。ジブチル錫ジラウレート0.62部を添加した後、攪拌しながら液温度を1時間かけて35℃まで徐々に上げた。その後、液温度を50℃に上げて反応させた。残留イソシアネート基濃度が1.52質量%(仕込量に対する割合)以下となった後、2−ヒドロキシエチルアクリレート3.102部を添加し、液温度約60℃にて撹拌し、反応させた。残留イソシアネート基濃度が0.1質量%以下になった時を反応終了とした。得られたウレタンアクリレートオリゴマーをオリゴマーDとする。
亜鉛及びコバルト化合物を6〜8ppm含んだ数平均分子量が2000のポリプロピレングリコールに替えて、亜鉛及びコバルト化合物を1〜2ppm含んだ数平均分子量が2000のポリプロピレングリコールを用いた以外は、合成例1と同様にして、ウレタンアクリレートオリゴマーを合成した。得られたウレタンアクリレートオリゴマーをオリゴマーBとする。
亜鉛及びコバルト化合物を6〜8ppm含んだ数平均分子量が2000のポリプロピレングリコールに替えて、亜鉛及びコバルト化合物を15〜25ppm含んだ数平均分子量が2000のポリプロピレングリコールを用いた以外は、合成例1と同様にして、ウレタンアクリレートオリゴマーを合成した。得られたウレタンアクリレートオリゴマーをオリゴマーCとする。
撹拌機を備えた反応容器に、イソホロンジイソシアネート15.4部、2,6−ジ−t−ブチル−p−クレゾール0.013部、ジブチル錫ジラウレート0.047部を仕込み、これらを撹拌しながら液温度が10℃以下になるまで氷冷した。ヒドロキシエチルアクリレートを液温度が20℃以下になるように制御しながら11.32g滴下した後、さらに、1時間撹拌し、反応させた。次に数平均分子量1,000のポリテトラメチレングリコール25.4gおよび数平均分子量400のビスフェノールAのアルキレンオキサイド付加ジオール9.36gを加え、液温度70〜75℃にて3時間撹拌を継続させ、残留イソシアネートが0.1質量%以下になった時を反応終了とした。液温度50〜60℃に冷却し、イソボニルアクリレート9.7g、SA−1002(三菱化学社製)14.55g、N−ビニルカプロラクタム9.7g、Irgacure184(チバスペシャリティーケミカルズ社製)2.91gおよびスミライザー GA−80(住友化学社製)0.3gを加え、均一になるまで撹拌して、液状硬化性樹脂組成物を得た。
攪拌機を備えた反応容器に、数平均分子量1000のポリプロピレングリコール180.88g、数平均分子量10000のポリプロピレングリコール9.02g、2,6−ジ−t−ブチル−p−クレゾール0.182g、トリレンジイソシアネート257.22g、2−エチルヘキシルアクリレート95.80gを仕込み、これらを攪拌しながら、液温度が15℃となるまで冷却した。ジブチル錫ジラウレート0.605gを添加した後、温度が40℃以上にならないように注意しながら、1時間ほど攪拌した。室温になるまで攪拌した後、2−ヒドロキシプロピルアクリレート88.89gを、液温度が30℃を越えないように調節しながら滴下した。滴下終了後、液温度40℃で1時間撹拌した。次に、2−ヒドロキシエチルアクリレート220.77gを、液温度が60℃を越えないように調節しながら滴下した。滴下終了後、液温度60℃で撹拌した。残留イソシアネート基濃度が0.1重量%以下になった時を反応終了とし、ウレタン(メタ)アクリレートオリゴマーを得た(これを重合性オリゴマーとする)。液温度を50〜60℃に冷却し、2−エチルへキシルアクリレート114.95g、Irganox245(チバスペシャリティーケミカルズ社製)2.90g、Irgacure184(チバスペシャリティーケミカルズ社製)29.03gを加え、均一な樹脂液になるまで撹拌して、液状硬化性樹脂組成物を得た。
撹拌機を備えた反応容器に表1に示す配合比(質量部)で化合物を仕込み、均一な溶液になるまで液温度50℃で攪拌し、実施例及び比較例の液状硬化性樹脂組成物を得た。
光ファイバ線引き装置(吉田工業製)を使用して、石英ガラスファイバ上に一次被覆材として、実施例又は比較例の組成物を塗布硬化させた後、二次被覆材を塗布し硬化させた。光ファイバの製造条件は以下のように行った。
光ファイバの線径は、ガラスファイバは直径125μmであったが、これに実施例又は比較例で得られた一次被覆材を塗布硬化させ、直径が200μmになるように調整した。さらに形成された一次被覆層の上に、合成例3で得られた二次被覆材を塗布し、硬化した時点で245μmになるように調節して塗布した。紫外線照射装置はORC社製UVランプ(SMX3.5kw)を使用した。光ファイバの線引き速度は200m/minとした。
合成例2で得られた液状硬化性樹脂組成物を一次被覆材とし、合成例4で得られた液状硬化性樹脂組成物を二次被覆材として、それぞれ用いた他は製造例1と同様にして、光ファイバ素線を製造した。
(1)硬化性:
実施例および比較例で得られた液状硬化性樹脂組成物の硬化性を測定した。200μm厚のアプリケーターバーを用いてガラス板上に液状硬化性樹脂組成物を塗布し、これを空気中で20mJ/cm2および500mJ/cm2のエネルギーの紫外線を照射して硬化させ、試験用フィルム二種類を得た。この硬化フィルム二種類からそれぞれ延伸部が幅6mm、長さ25mmとなるよう、短冊状サンプルを作成した。温度23℃、湿度50%下で引張り試験機AGS−1KND(島津製作所社製)を用い、JIS K7127に準拠して引張試験を行った。引張速度は1mm/minで2.5%歪みでの抗張力からヤング率を求めた。20mJ/cm2で硬化させた試験用フィルムのヤング率と500mJ/cm2で硬化させた試験用フィルムのヤング率の比を式(1)より算出して、組成物の硬化速度を評価した。
硬化性 =(20mJ/cm2時のヤング率)/(500mJ/cm2時のヤング率)(1)
実施例および比較例で得られた液状硬化性樹脂組成物の温水浸漬試験を行った。70μm厚のアプリケーターバーを用いてガラス板上に合成例3で調製した二次被覆材を塗布し、これを空気中で100mJ/cm2の紫外線を照射し硬化させた。次に、作製した硬化フィルム上に130μm厚のアプリケーターバーを用いて実施例及び比較例で調製した一次被覆材を塗布し、これを窒素中で500mJ/cm2の紫外線を照射して硬化させた。さらに、200μm厚のアプリケーターバーを用いてガラス板上に合成例3で調製した二次被覆材を塗布し、これを窒素中で500mJ/cm2の紫外線を照射して硬化させ、試験用フィルムを得た。この硬化フィルムからそれぞれ幅10mm、長さ30mmとなるよう、短冊状サンプルを作成した。短冊サンプルを温度60℃の温水に浸漬させ、光学顕微鏡で観察した。720時間温水に浸漬した後に、10μm以上の発泡が認められない場合を「○」、10μm以上の発泡が認められる場合を「×」と評価した。
実施例および比較例で得られた液状硬化性樹脂組成物の濾過性試験を行った。組成物100gをメチルエチルケトン100gに溶解させ、PTFEメンブレンフィルター(1.0μm、47mm:ADVANTEC社製)を使用し濾過した。30分の濾過で得られた濾液量を測定した。
硬化性が0.80以上で、耐温水浸漬試験が「○」評価であり、濾過性試験で100g以上の場合を合格と判定した。
アロニックスM−113:ノニルフェノールエチレンオキサイド変性アクリレート、東亞合成社製
Irganox1035:チオジエチレンビス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート](チバ・スペシャルティ・ケミカルズ社製)SEESORB101:2−ヒドロキシ−4−メトキシベンゾフェノン(シプロ化成社製)
SH6062:γ−メルカプトキシプロピルトリメトキシシラン(東レ・ダウコーニング・シリコーン社製)
Claims (4)
- 組成物全量を100質量%として、
(A)ポリプロピレングリコール由来の構造を有するウレタン(メタ)アクリレート 35〜85質量%、
(B)(A)以外のエチレン性不飽和基含有化合物 1〜60質量%、
(C)アミン系光増感剤 0.01〜1質量%、及び
(D)光重合開始剤 0.01〜10質量%
を含有する液状硬化性樹脂組成物であって、高周波プラズマ発光・質量分析法(ICP−MS)により求めた組成物中の亜鉛及びコバルト元素の合計含有量が0.5〜10ppmである、液状硬化性樹脂組成物。 - (C)アミン系光増感剤が、トリエチルアミン、ジエチルアミン、ジプロピルアミン、ジブチルアミン、N−メチルジエタノールアミン、エタノールアミン、4−ジメチルアミノ安息香酸、4−ジメチルアミノ安息香酸メチル、4−ジメチルアミノ安息香酸エチル、および4−ジメチルアミノ安息香酸イソアミルからなる群から選択される一種以上の化合物である請求項1記載の液状硬化性樹脂組成物。
- 請求項1又は2記載の液状硬化性樹脂組成物を、放射線により硬化せしめることにより得られる光ファイバ被覆層。
- 請求項3記載の被覆層を有する光ファイバ。