JP5192774B2 - Nanocarbon-coated refractory raw material and production method thereof, and refractory using the same and production method thereof - Google Patents
Nanocarbon-coated refractory raw material and production method thereof, and refractory using the same and production method thereof Download PDFInfo
- Publication number
- JP5192774B2 JP5192774B2 JP2007277550A JP2007277550A JP5192774B2 JP 5192774 B2 JP5192774 B2 JP 5192774B2 JP 2007277550 A JP2007277550 A JP 2007277550A JP 2007277550 A JP2007277550 A JP 2007277550A JP 5192774 B2 JP5192774 B2 JP 5192774B2
- Authority
- JP
- Japan
- Prior art keywords
- refractory
- raw material
- carbon
- refractory raw
- nanocarbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、溶融金属用、主として鉄鋼用の耐火物に使用される耐火原料とそれを使用した耐火物に関する。 The present invention relates to a refractory material used for a refractory for molten metal, mainly steel, and a refractory using the same.
黒鉛、ピッチ、カーボンブラック、またはフェノールレジン等の炭素原料を含有するカーボン含有耐火物は、耐熱衝撃性および耐スラグ性に優れており、例えば、転炉、取鍋、混銑車、もしくは真空脱ガス炉等の内張材としてのれんが、不定形耐火物、浸漬ノズル等の連続鋳造用ノズル、または焼付け材等の補修材として広く使用されている。 Carbon-containing refractories containing carbon raw materials such as graphite, pitch, carbon black, or phenol resin are excellent in thermal shock resistance and slag resistance. For example, converters, ladle, kneading cars, or vacuum degassing. Brick as a lining material for furnaces is widely used as an irregular refractory material, a continuous casting nozzle such as an immersion nozzle, or a repair material such as a baking material.
ところで、近年、製綱工程においてより一層の鋼製品の高品質化と、より厳しい組成コントロールが求められるようになってきている。そのため、カーボン含有耐火物の内部に含有されるカーボンが溶鋼中へ溶解する現象（以下「カーボンピックアップ」という。）による溶鋼の汚染の問題が顕在化してきている。なかでも、転炉、真空脱ガス装置、取鍋等で使用されているマグネシア−カーボンれんがにおいては、もともと１０〜３０質量％もの黒鉛を含有しており、この黒鉛を低減するユーザーの要求は非常に強い。かかるカーボンピックアップを抑えるためには、カーボン含有耐火物の低カーボン化を図る必要がある。 By the way, in recent years, higher quality of steel products and stricter composition control have been required in the steelmaking process. Therefore, the problem of contamination of molten steel due to the phenomenon that carbon contained in the refractory containing carbon dissolves into molten steel (hereinafter referred to as “carbon pickup”) has become apparent. In particular, magnesia-carbon bricks used in converters, vacuum degassing equipment, ladles, etc. originally contain 10 to 30% by mass of graphite, and there is a great demand from users to reduce this graphite. Strong. In order to suppress such a carbon pickup, it is necessary to reduce the carbon of the carbon-containing refractory.
さらには、カーボンが高熱伝導率であるため溶鋼温度低下などの熱ロス、容器の鉄皮変形、さらには、カーボンの燃焼にともなうＣＯガスの放出などの諸問題からも耐火物の低カーボン化が要求されている。 Furthermore, because carbon has a high thermal conductivity, heat loss such as a drop in molten steel temperature, deformation of the iron core of the container, and problems such as the release of CO gas accompanying the combustion of carbon can reduce the refractory's carbon content. It is requested.
しかしながら、低カーボン化すると耐熱衝撃性が低下する問題があり、これを改善する方法が過去に種々検討されている。 However, there is a problem that the thermal shock resistance decreases when the carbon content is lowered, and various methods for improving this have been studied in the past.
例えば、特許文献１には空隙ならびにピッチからなる厚さ５〜１００μｍの層を周囲に形成したマグネシア粒子を１０〜５０容量％含むＭｇＯ−Ｃ質不焼成れんがが開示されている。この不焼成れんがにおいては、組織中、マグネシア粒子の周囲に存在する空隙ならびに結晶度が低い黒鉛が、熱衝撃により発生した亀裂の伝播を阻止する。この阻止作用により、れんがが剥落するほどの大きな亀裂には発達しないとされている。 For example, Patent Document 1 discloses an MgO—C non-fired brick containing 10 to 50% by volume of magnesia particles around which a layer having a thickness of 5 to 100 μm composed of voids and pitches is formed. In this unfired brick, voids existing around the magnesia particles in the structure and graphite having low crystallinity prevent the propagation of cracks generated by thermal shock. It is said that this blocking action does not develop into a crack large enough for the brick to peel off.
また、特許文献２では、フラーレン類を原料として使用することで、組織中にカーボンナノファイバーが生成し、強度と耐熱衝撃性が飛躍的に向上するため、カーボン含有耐火物においてカーボン量を減らすことができると記載されている。とくに、黒鉛使用量が１０質量％以下のカーボン含有耐火物において顕著な効果が得られるとされている。 Moreover, in patent document 2, since carbon nanofiber produces | generates in a structure | tissue by using fullerenes as a raw material, and an intensity | strength and a thermal shock resistance improve dramatically, it reduces carbon amount in a carbon containing refractory. It is stated that you can. In particular, it is said that a remarkable effect is obtained in a carbon-containing refractory having an amount of graphite used of 10% by mass or less.
さらに、特許文献３では、メソフェーズピッチと熱硬化性樹脂を使用した耐火物にはカーボンナノファイバーが生成し、その結果、優れた耐熱衝撃性が得られると記載されている。 Furthermore, Patent Document 3 describes that carbon nanofibers are generated in a refractory using a mesophase pitch and a thermosetting resin, and as a result, excellent thermal shock resistance is obtained.
さらには、近年、カーボンナノチューブまたはカーボンナノファイバーを合成する方法が、種々研究されている。例えば特許文献４では、触媒金属の有機金属塩または無機金属塩を溶媒に分散または溶解した溶液を基板表面に塗布し、還元することで触媒金属微粒子を形成し、その後、ＣＶＤ等によってカーボンナノチューブを合成することが開示されている。
しかしながら、耐熱衝撃性を低下させることなく低カーボン化するために、過去に検討された上記改善方法には種々の問題がある。 However, in order to reduce the carbon without lowering the thermal shock resistance, there are various problems with the above-described improvement methods studied in the past.
例えば、特許文献１に記載の耐火物粒子の周囲に空隙ならびにピッチを形成する方法は、使用中、マグネシア粒子の周囲の空隙にスラグが浸入しやすくなり、スラグに対する耐食性が低下する。 For example, in the method of forming voids and pitches around the refractory particles described in Patent Document 1, slag is likely to enter the voids around the magnesia particles during use, and the corrosion resistance to the slag is reduced.
また、特許文献２に記載のフラーレン類を原料として使用する方法は、ナノサイズと極めて小さいフラーレン類を耐火物中に凝集することなく均一に分散するためには非常に手間を要し、高コストになる。 In addition, the method of using fullerenes described in Patent Document 2 as a raw material is extremely laborious and expensive in order to uniformly disperse nano-sized and extremely small fullerenes in a refractory material without agglomeration. become.
また、特許文献２や特許文献３の方法では、確かにカーボンナノファイバーの効果により耐熱衝撃性が向上するため黒鉛含有量の少ない低カーボン含有耐火物を得ることができるが、耐火原料粒子の周囲からスラグが浸入して組織が溶融し損耗しているため耐食性がネックとなった。 Moreover, in the methods of Patent Document 2 and Patent Document 3, the thermal shock resistance is improved by the effect of carbon nanofibers, so that a low carbon-containing refractory with a low graphite content can be obtained. Since the slag penetrated and the structure melted and was worn out, corrosion resistance became a bottleneck.
本発明が解決しようとする課題は、カーボンナノチューブまたはカーボンナノファイバーを耐火物中に比較的簡単に均一分散させることができ、しかも耐熱衝撃性に優れると共に耐スラグ性にも優れた耐火物を得ることができる耐火原料とその製造方法、およびその耐火原料を使用した耐火物とその製造方法を提供することにある。 The problem to be solved by the present invention is that carbon nanotubes or carbon nanofibers can be dispersed relatively easily and uniformly in a refractory, and a refractory excellent in thermal shock resistance and slag resistance is obtained. An object of the present invention is to provide a refractory raw material that can be used and a method for producing the same, and a refractory using the refractory raw material and a method for producing the same.
本発明は、耐火原料粒子の表面をカーボンナノチューブまたはカーボンナノファイバーで被覆した溶融金属用のナノカーボン被覆耐火原料である。以下カーボンナノチューブをＣＮＴ、カーボンナノファイバーをＣＮＦと称す。 The present invention is a nanocarbon-coated refractory material for molten metal in which the surface of refractory material particles is coated with carbon nanotubes or carbon nanofibers. Hereinafter, the carbon nanotube is referred to as CNT, and the carbon nanofiber is referred to as CNF.
耐火原料粒子の表面をＣＮＴまたはＣＮＦが被覆した状態とは、保管中や運搬などで剥がれることなく密着して付着している状態を言う。また耐火原料の表面を密な状態で全て被覆しても良いが、粗な状態でも構わないし、部分的でも良い。 The state where the surface of the refractory raw material particles is coated with CNT or CNF refers to a state where the refractory raw material particles are adhered and adhered without being peeled off during storage or transportation. Further, the entire surface of the refractory raw material may be covered in a dense state, but it may be in a rough state or a partial state.
この耐火原料粒子の表面を被覆するＣＮＴまたはＣＮＦのうちＣＮＴは、直径が数ｎｍ〜数十ｎｍのシングルウォール及びダブルウォールカーボンナノチューブ、あるいは２層以上の炭素面積層を持ったいわゆる多層（マルチウォール）カーボンナノチューブから主に構成される。一方、ＣＮＦは、直径が数ｎｍ〜数１００ｎｍ、長さが数μｍで、炭素網面が繊維軸に対して平行なplatelet型、炭素網面が繊維軸に対して傾斜したherring-bone（ヘリンボーン）型、炭素網面が繊維軸に平行なtubular（チューブラー）型などから主に構成される。 Among the CNTs or CNFs covering the surface of the refractory raw material particles, CNTs are single-wall and double-wall carbon nanotubes having a diameter of several to several tens of nm, or so-called multi-walls (multi-walls) having two or more carbon area layers. ) Consists mainly of carbon nanotubes. CNF, on the other hand, has a diameter of several nanometers to several hundreds of nanometers, a length of several μm, a carbon network surface parallel to the fiber axis, and a herring-bone whose carbon network surface is inclined with respect to the fiber axis. ) Type and tubular type whose carbon mesh surface is parallel to the fiber axis.
ＣＮＴまたはＣＮＦを被覆させる耐火原料粒子の粒子径としてはとくに限定しないが、耐火物中に均一に分散させる目的からは、平均粒径が１００μｍ以下であることが好ましく、より好ましくは平均粒径が５０μｍ以下１μｍ以上である。平均粒径が１００μｍを超えると、ＣＮＴまたはＣＮＦの耐火物中への均一分散効果が少なくなり、耐熱衝撃性の向上効果が制限される。また、平均粒径が５０μｍ以下の方がよりＣＮＴまたはＣＮＦの耐火物中への均一分散効果が高まるため耐熱衝撃性に優れ、平均粒径が１μｍ未満ではＣＮＴまたはＣＮＦの被覆工程で凝集しやすくなる。ここで平均粒径とはメジアン径であり、被覆する前の耐火原料粒子の粒径分布を測定した粒径（範囲）と重量割合をグラフにプロットし、積算割合が５０％の場合の粒径を平均粒径とする。粒径分布の測定方法としては、レーザー回折式粒度分布測定装置等などがある。 The particle diameter of the refractory raw material particles to be coated with CNT or CNF is not particularly limited, but for the purpose of uniformly dispersing in the refractory, the average particle diameter is preferably 100 μm or less, more preferably the average particle diameter is 50 μm or less and 1 μm or more. When the average particle diameter exceeds 100 μm, the effect of uniformly dispersing CNT or CNF in the refractory decreases, and the effect of improving the thermal shock resistance is limited. Also, when the average particle size is 50 μm or less, the effect of uniform dispersion of CNT or CNF in the refractory is enhanced, so that the thermal shock resistance is excellent. Become. Here, the average particle diameter is the median diameter, and the particle diameter (range) and weight ratio obtained by measuring the particle diameter distribution of the refractory raw material particles before coating are plotted on a graph, and the particle diameter when the integrated ratio is 50%. Is the average particle size. Examples of the particle size distribution measuring method include a laser diffraction particle size distribution measuring apparatus.
ＣＮＴまたはＣＮＦの被覆量は、ナノカーボン被覆耐火原料に対し、３〜４０質量％とする。ＣＮＴまたはＣＮＦの被覆量が３質量％未満では膨張吸収効果（耐熱衝撃性向上効果）が得られにくく、４０質量％を超えると被覆された耐火原料粒子の混合割合を低くせざるを得ないのでＣＮＴまたはＣＮＦを耐火物中に均一に分散できなくなる。 The coating amount of CNT or CNF is 3 to 40 % by mass relative to the nanocarbon-coated refractory raw material. If the coating amount of CNT or CNF is less than 3% by mass, it is difficult to obtain an expansion absorption effect (improvement effect of thermal shock resistance), and if it exceeds 40 % by mass, the mixing ratio of coated refractory raw material particles must be lowered. CNT or CNF cannot be uniformly dispersed in the refractory.
ＣＮＴまたはＣＮＦが被覆される耐火原料粒子としては、マグネシア、アルミナ、スピネル、カルシア、ドロマイト、シリカ、クロミア、ジルコニア、チタニアおよびムライトからなる群のうち１種または２種以上が、耐火物として耐用性に優れた金属酸化物である点から好ましい。これらの耐火原料粒子は、耐火物の原料として一般的に使用されている。なお、これらの耐火原料は、使用中の熱によって耐火原料粒子どうしが焼結するために使用を重ねるに従い耐熱衝撃性が低下してくる傾向があるが、本発明においては表面のＣＮＴまたはＣＮＦによって焼結を抑制する効果が得られる。これに対して非酸化物原料である炭化珪素や鱗状黒鉛等の表面に触媒を被覆してＣＮＴまたはＣＮＦを形成することも考えられるが、これらの非酸化物原料は通常の使用温度領域では互いに焼結することがないため、過焼結防止による耐熱衝撃性の向上効果は期待できない。 As the refractory raw material particles coated with CNT or CNF, one or more of the group consisting of magnesia, alumina, spinel, calcia, dolomite, silica, chromia, zirconia, titania and mullite are used as refractories. It is preferable from the viewpoint of excellent metal oxide. These refractory raw material particles are generally used as a refractory raw material. These refractory raw materials have a tendency to deteriorate in thermal shock resistance as they are repeatedly used because the refractory raw material particles sinter due to heat during use, but in the present invention, the surface CNT or CNF An effect of suppressing sintering is obtained. On the other hand, it is conceivable to form a CNT or CNF by coating a catalyst on the surface of non-oxide raw materials such as silicon carbide and scaly graphite. Since sintering does not occur, the effect of improving thermal shock resistance by preventing oversintering cannot be expected.
耐火原料粒子の表面にＣＮＴまたはＣＮＦを被覆するにあたっては、あらかじめ例えば平均粒径が１００μｍ以下に粒度調整された耐火原料粒子を使用し、これらの表面にＣＮＴまたはＣＮＦを被覆する。ＣＮＴまたはＣＮＦを被覆した後に、耐火原料粒子を粉砕すると粉砕中にＣＮＴまたはＣＮＦが剥がれるためである。 When coating the surface of the refractory raw material particles with CNT or CNF, for example, refractory raw material particles whose average particle size is adjusted to 100 μm or less in advance are used, and these surfaces are coated with CNT or CNF. This is because if the refractory raw material particles are pulverized after being coated with CNT or CNF, the CNTs or CNF are peeled off during the pulverization.
具体的に、耐火原料粒子の表面にＣＮＴまたはＣＮＦを被覆する方法としては、ＣＮＴまたはＣＮＦを分散させた溶液を耐火原料粒子表面に塗布後乾燥する方法などＣＮＴまたはＣＮＦを塗布あるいは塗す方法、または耐火原料粒子の表面に直接ＣＮＴまたはＣＮＦを成長させる方法等が考えられる。 Specifically, as a method of coating CNT or CNF on the surface of the refractory raw material particles, a method of applying or applying CNT or CNF, such as a method of applying a solution in which CNT or CNF is dispersed to the surface of the refractory raw material particles and then drying, Alternatively, a method of directly growing CNT or CNF on the surface of the refractory raw material particles can be considered.
このうち、耐火原料粒子の表面にＣＮＴまたはＣＮＦを成長させる方法が、ＣＮＴまたはＣＮＦが耐火物原料粒子表面に均一にしかも強固に付着することから好適である。つまり、耐火物組織中でカーボンボンドと耐火原料粒子との結合をより強固なものとすることができる。 Among these, the method of growing CNT or CNF on the surface of the refractory raw material particles is preferable because CNT or CNF uniformly and firmly adheres to the surface of the refractory raw material particles. That is, the bond between the carbon bond and the refractory raw material particles can be made stronger in the refractory structure.
具体的には、まず、触媒を液体に分散または触媒前駆体を溶解した液体中に耐火原料粒子を浸漬し、液体を除去することで、耐火原料粒子の表面に触媒を担持させる。次に、このＣＮＴまたはＣＮＦを成長させるための触媒を担持した耐火原料粒子を、炭素化合物と接触下で熱処理することにより表面にＣＮＴまたはＣＮＦを合成することができる。例えばＣＶＤ法により、８５０℃のメタン気流中で熱処理を行うことでシングルウォール及びダブルウォールＣＮＴが得られる。耐火原料粒子へのＣＮＴまたはＣＮＦの被覆量は、例えばＣＶＤ法の諸条件を変えることでコントロールすることができる。またこのとき、７００℃のエチレン／水素あるいは９００℃のメタン気流中で熱処理を行うと、主として多層（マルチウォール）ＣＮＴが得られる。さらに、４５０℃のメタン、エチレン/水素あるいは一酸化炭素／水素気流中で熱処理を行うとＣＮＦが得られる。 Specifically, first, the catalyst is supported on the surface of the refractory raw material particles by immersing the refractory raw material particles in a liquid in which the catalyst is dispersed in the liquid or the catalyst precursor is dissolved, and the liquid is removed. Next, the refractory raw material particles carrying a catalyst for growing CNT or CNF are heat-treated in contact with a carbon compound to synthesize CNT or CNF on the surface. For example, single wall and double wall CNTs can be obtained by performing heat treatment in a methane stream at 850 ° C. by CVD. The coating amount of CNT or CNF on the refractory raw material particles can be controlled, for example, by changing various conditions of the CVD method. At this time, when heat treatment is performed in a 700 ° C. ethylene / hydrogen or 900 ° C. methane stream, multilayer (multi-wall) CNTs are mainly obtained. Furthermore, CNF can be obtained by heat treatment in 450 ° C. methane, ethylene / hydrogen or carbon monoxide / hydrogen stream.
触媒を担持した耐火原料粒子と接触させる炭素化合物は、とくに限定されず通常ＣＮＴまたはＣＮＦの合成に使用されている炭素化合物を使用することができる。好ましくは炭化水素または一酸化炭素を使うと良い。 The carbon compound to be brought into contact with the refractory raw material particles supporting the catalyst is not particularly limited, and a carbon compound usually used for the synthesis of CNT or CNF can be used. Preferably, hydrocarbon or carbon monoxide is used.
触媒は、一般的にＣＮＴまたはＣＮＦの合成に使用されるものであればとくに問題なく使用することができるが、なかでもＶ、Ｆｅ、Ｃｏ、Ｎｉ、Ｃｕ、Ｍｏ、Ｐｄ、Ｒｈ、ＷおよびＰｔからなる群のうち１種または２種以上の金属、その金属の酸化物または金属塩が、耐火物に悪影響を与えない点から好ましい。本発明では、触媒が金属酸化物や金属塩でも、その後、還元性ガスの存在下で加熱されるため金属酸化物は還元されるため、その触媒としての機能は十分得られる。 The catalyst can be used without any problem as long as it is generally used for the synthesis of CNT or CNF. Among them, V, Fe, Co, Ni, Cu, Mo, Pd, Rh, W and Pt can be used. One or two or more metals, oxides or metal salts of the metals in the group consisting of these are preferred from the point of not adversely affecting the refractory. In the present invention, even if the catalyst is a metal oxide or metal salt, the metal oxide is reduced because it is subsequently heated in the presence of a reducing gas, so that the function as the catalyst is sufficiently obtained.
以上のように本発明では、耐火原料粒子の表面にＣＮＴまたはＣＮＦが存在するため、その可撓性により耐火材料の膨張を吸収ししかも耐火原料どうしの焼結を抑制するため耐熱衝撃性が向上すると考えられる。さらに、ＣＮＴまたはＣＮＦは有機バインダーとの馴染みが良いため熱処理によって生成するカーボンボンドと耐火原料粒子との間に隙間を生じることなく強固なボンドが形成されているとも考えられる。このため、耐スラグ性も向上すると推定される。そして、ＣＮＴまたはＣＮＦが被覆された耐火原料粒子が微粉として耐火物中に均一に分散されているため、ＣＮＴまたはＣＮＦも耐火物中に均一に分散して存在することになる。その結果、前記効果をより高めることができると考えられる。一方、揮発分の多いピッチや黒鉛層間が膨張した膨張黒鉛などの材料は骨材の周囲に大きな空隙ができ耐熱衝撃性は得られるものの耐食性が低下する。これに対して、本発明ではこの空隙を減少できるため耐食性の低下は小さい。 As described above, in the present invention, since CNT or CNF is present on the surface of the refractory raw material particles, the thermal shock resistance is improved by absorbing the expansion of the refractory material and suppressing the sintering of the refractory raw materials by its flexibility. I think that. Furthermore, since CNT or CNF is familiar with the organic binder, it is considered that a strong bond is formed without generating a gap between the carbon bond generated by the heat treatment and the refractory raw material particles. For this reason, it is estimated that slag resistance is also improved. And since the refractory raw material particle | grains coat | covered with CNT or CNF are uniformly disperse | distributed in a refractory as a fine powder, CNT or CNF will also be disperse | distributed uniformly in a refractory. As a result, it is considered that the effect can be further enhanced. On the other hand, materials such as pitch with a large amount of volatile matter and expanded graphite in which the graphite layer expands can form large voids around the aggregate, resulting in thermal shock resistance but reduced corrosion resistance. On the other hand, in this invention, since this space | gap can be reduced, the fall of corrosion resistance is small.
本発明のナノカーボン被覆耐火原料は、従来の耐火物を製造するときの耐火原料配合物の一部として使用することで、ＣＮＴまたはＣＮＦを耐火物中に均一に分散させることができる。したがって、あらゆるカーボン含有耐火物に使用することができる。例えば、鉄鋼用として広く使用されているカーボンボンドを有する耐火物に使用することができる。具体的には、アルミナ−カーボン系、アルミナ−炭化珪素−カーボン系、アルミナ−スピネル−カーボン系、ジルコニア−カーボン系、マグネシア−カーボン系、マグネシア−スピネル−カーボン系、炭化珪素−カーボン系、窒化珪素−カーボン系、マグネシア−カルシア−カーボン系等である。カーボン含有量としては、固定炭素として１〜３０質量％を含有していることが好ましい。固定炭素の含有率が１質量％未満では耐スラグ性の向上効果が少なく、３０質量％を超えると耐熱衝撃性の向上効果が少なくなる。ここで固定炭素量は、ＪＩＳ−Ｍ８８１２に準拠して測定される。 The nanocarbon-coated refractory raw material of the present invention can be used as a part of a refractory raw material composition when producing a conventional refractory, whereby CNT or CNF can be uniformly dispersed in the refractory. Therefore, it can be used for any carbon-containing refractory. For example, it can be used for refractories having carbon bonds that are widely used for steel. Specifically, alumina-carbon, alumina-silicon carbide-carbon, alumina-spinel-carbon, zirconia-carbon, magnesia-carbon, magnesia-spinel-carbon, silicon carbide-carbon, silicon nitride -Carbon type, magnesia-calcia-carbon type and the like. As carbon content, it is preferable to contain 1-30 mass% as fixed carbon. If the content of fixed carbon is less than 1% by mass, the effect of improving the slag resistance is small, and if it exceeds 30% by mass, the effect of improving the thermal shock resistance is small. Here, the amount of fixed carbon is measured in accordance with JIS-M8812.
さらに、本発明は不定形耐火物よりも耐熱衝撃性と耐スラグ性の要求レベルがより高い定形耐火物に適用するとより効果的である。定形耐火物は、不定形耐火物よりも低気孔率で緻密になっており（高弾性）、ＣＮＴまたはＣＮＦを含有することで前述の作用によってより低弾性化になるため、より低カーボン化とすることができる。定形耐火物とは、混練物をプレス機等で加圧成形することによって得られるいわゆるれんがであって、溶融金属容器の内張り用れんがや連続鋳造用ノズル等である。 Furthermore, the present invention is more effective when applied to a fixed refractory having higher required levels of thermal shock resistance and slag resistance than an irregular refractory. The regular refractory is denser with a lower porosity than the amorphous refractory (high elasticity), and by containing CNT or CNF, it becomes less elastic due to the above-described action, so the carbonization is further reduced. can do. The fixed refractory is a so-called brick obtained by press-molding the kneaded material with a press or the like, such as a brick for lining a molten metal container, a nozzle for continuous casting, or the like.
とくに、ナノカーボン被覆耐火原料を１〜３０質量％含有する耐火原料配合物に有機バインダーを添加して混練、成形、熱処理することで耐熱衝撃性および耐食性に優れたナノカーボン含有耐火物を得ることができる。ナノカーボン被覆耐火原料の含有量が１質量％未満では、耐熱衝撃性および耐食性の向上効果が不足し、３０質量％を超えるとカーボン量が多くなりすぎる。有機バインダーはカーボンボンドを生成するために使用し、ＣＮＴまたはＣＮＦと組み合わせて使用することで、低弾性でしかも高強度なボンドを形成することができる。有機バインダーとしては、具体的には、フェノール樹脂、フラン樹脂、ピッチ、フェノール類、フルフリルアルコール類およびフルフリルアルデヒド類からなる群のうち１種以上が、強いカーボンボンドを形成する点から好ましい。 In particular, to obtain a nanocarbon-containing refractory excellent in thermal shock resistance and corrosion resistance by adding an organic binder to a refractory raw material composition containing 1-30% by mass of a nanocarbon-coated refractory raw material, kneading, molding, and heat treating Can do. If the content of the nanocarbon-coated refractory raw material is less than 1% by mass, the effect of improving thermal shock resistance and corrosion resistance is insufficient, and if it exceeds 30% by mass, the amount of carbon is excessive. The organic binder is used to generate a carbon bond, and when used in combination with CNT or CNF, a bond having low elasticity and high strength can be formed. Specifically, as the organic binder, one or more members selected from the group consisting of phenol resins, furan resins, pitches, phenols, furfuryl alcohols and furfuryl aldehydes are preferable from the viewpoint of forming a strong carbon bond.
さらに、適用する耐火物の中でもとくに、マグネシア−カーボンれんがに適用した場合には黒鉛量を少なくしても耐熱衝撃性の低下を抑制することができ、高耐用性の低カーボンのマグネシア−カーボンれんがを得ることができる。 Furthermore, especially when applied to magnesia-carbon bricks among the refractories to be applied, even if the amount of graphite is reduced, it is possible to suppress a decrease in thermal shock resistance, and a high durability low carbon magnesia-carbon brick. Can be obtained.
具体的には、マグネシア原料６０〜９９質量％と本発明のナノカーボン被覆耐火原料１〜３０質量％を含む耐火原料配合物に対して、有機バインダーを添加して、混練、成形後熱処理することで得ることができる。そしてこのときに使用されるナノカーボン被覆耐火原料としては、マグネシアであることが好ましい。また鱗状黒鉛は使用しなくても良いが、使用する場合には１５質量％未満、より好ましくは１０質量％未満で使用することで、従来の転炉用、または二次精錬用のマグネシア−カーボンれんがと同様に使用することができる。 Specifically, an organic binder is added to the refractory raw material composition containing 60 to 99% by mass of the magnesia raw material and 1 to 30% by mass of the nanocarbon-coated refractory raw material of the present invention, followed by heat treatment after kneading and molding. Can be obtained at The nanocarbon-coated refractory raw material used at this time is preferably magnesia. Scalar graphite does not have to be used, but when used, it is less than 15% by mass, more preferably less than 10% by mass, so that it can be used for conventional converter or secondary refining magnesia-carbon. Can be used in the same way as brick.
なお、本発明のナノカーボン含有耐火物は、不焼成耐火物であっても焼成耐火物であってもよい。不焼成耐火物とする場合には、熱処理は、カーボン含有耐火物原料の成形体を１００℃以上８００℃未満で加熱する。また、焼成耐火物とする場合には、カーボン含有耐火物原料の成形体を８００℃以上１６００℃未満で加熱する。 The nanocarbon-containing refractory of the present invention may be an unfired refractory or a fired refractory. When the non-fired refractory is used, the heat treatment is performed by heating the carbon-containing refractory raw material at 100 ° C. or higher and lower than 800 ° C. Moreover, when setting it as a fired refractory, the molded object of a carbon containing refractory raw material is heated at 800 degreeC or more and less than 1600 degreeC.
本発明のナノカーボン被覆耐火原料を、カーボン含有耐火物の耐火原料配合物の一部として使用することで、ＣＮＴまたはＣＮＦを耐火物中に均一に分散することができる。このためＣＮＴまたはＣＮＦによって耐火原料の焼結が抑制され、耐火物の応力を吸収することができ、カーボンボンドが強化される。 By using the nanocarbon-coated refractory raw material of the present invention as a part of a refractory raw material composition of a carbon-containing refractory, CNT or CNF can be uniformly dispersed in the refractory. For this reason, sintering of a refractory raw material is suppressed by CNT or CNF, the stress of a refractory can be absorbed, and a carbon bond is strengthened.
その結果、耐熱衝撃性と耐スラグ性が向上し、耐火物の寿命が大幅に向上する。また、カーボン含有耐火物のカーボン量を減らすことができるので、使用時のカーボンピックアップを抑制することができる。 As a result, the thermal shock resistance and slag resistance are improved, and the life of the refractory is greatly improved. Moreover, since the amount of carbon of the carbon-containing refractory can be reduced, carbon pickup during use can be suppressed.
さらに、耐火物の熱伝導性を最適化することで炉の保温性を高めることもできる。 Furthermore, the thermal insulation of the furnace can be improved by optimizing the thermal conductivity of the refractory.
以下、本発明の実施の形態を実施例に基づいて説明する。 Hereinafter, embodiments of the present invention will be described based on examples.
表１は、本発明の実施例に使用したナノカーボン被覆耐火原料および比較例に使用した耐火原料の組成を示す。 Table 1 shows the composition of the nanocarbon-coated refractory material used in the examples of the present invention and the refractory material used in the comparative examples.
表１において、ナノカーボン被覆耐火原料ＡからＨは、担体としてあらかじめ所定の平均粒径に調整したマグネシア（電融マグネシアで純度９７質量％）またはアルミナ（電融アルミナで純度９９質量％）を、硝酸鉄およびモリブデン酸アンモニウムを溶解した水溶液に浸漬し、ろ過、乾燥することにより触媒を担持させた後、ＣＶＤ処理を行った。 In Table 1, the nanocarbon-coated refractory raw materials A to H are magnesia (purity of 97 mass% for electrofused magnesia) or alumina (purity of 99 mass% for electrofused alumina) previously adjusted to a predetermined average particle size as a carrier. After immersing in an aqueous solution in which iron nitrate and ammonium molybdate were dissolved, filtering and drying, the catalyst was supported, and then CVD treatment was performed.
ＣＶＤ処理において、８５０℃のメタン気流中で熱処理を行うと、シングルウォール及びダブルウォールＣＮＴが生成し、耐火原料を被覆することができた（ナノカーボン被覆耐火原料Ａ〜Ｆ）。また、ＣＶＤ処理において、７００℃のエチレン／水素あるいは９００℃のメタン／水素で熱処理を行うことにより多層（マルチウォール）ＣＮＴを被覆したものが得られた（ナノカーボン被覆耐火原料Ｇ）。さらに、ＣＶＤ処理において、４５０℃のエチレン／水素気流中で熱処理を行うことによりＣＮＦを被覆したものが得られた（ナノカーボン被覆耐火原料Ｈ）。 In the CVD process, when heat treatment was performed in a methane gas stream at 850 ° C., single-wall and double-wall CNTs were generated, and the refractory material could be coated (nanocarbon-coated refractory materials A to F). In addition, in the CVD process, heat treatment was performed with 700 ° C. ethylene / hydrogen or 900 ° C. methane / hydrogen to obtain a multilayer (multi-wall) CNT coated (nanocarbon coated refractory raw material G). Further, in the CVD process, a CNF-coated product was obtained by performing a heat treatment in an ethylene / hydrogen stream at 450 ° C. (nanocarbon-coated refractory raw material H).
使用したマグネシアおよびアルミナの平均粒径はそれぞれ表１に示した。粒径の測定は、レーザー回折式粒度分布測定装置で行った。ＣＮＴまたはＣＮＦの被覆量は、得られたナノカーボン被覆耐火原料を酸化雰囲気下１２００℃で２時間加熱し、その前後の質量を測定することで算出した。 The average particle diameters of magnesia and alumina used are shown in Table 1, respectively. The particle size was measured with a laser diffraction particle size distribution analyzer. The coating amount of CNT or CNF was calculated by heating the obtained nanocarbon-coated refractory raw material at 1200 ° C. for 2 hours in an oxidizing atmosphere and measuring the mass before and after that.
図１は表１のナノカーボン被覆耐火原料ＡをＴＥＭにより観察した結果を示す。シングルウォール、ダブルウォールのＣＮＴ２がマグネシア粒子１の表面に隙間なく生成していることが観察される。 FIG. 1 shows the result of observing the nanocarbon-coated refractory material A in Table 1 with a TEM. It is observed that single-wall and double-wall CNTs 2 are formed on the surface of the magnesia particles 1 without any gaps.
図２及び図３は表１のナノカーボン被覆耐火原料ＧをＴＥＭにより観察した結果を示す。マグネシア粒子３が多層（マルチウォール）ＣＮＴ４で被覆された構造を呈していることが観察される。 2 and 3 show the results of observing the nanocarbon-coated refractory raw material G in Table 1 with a TEM. It is observed that the magnesia particles 3 have a structure covered with multilayer (multiwall) CNT4.
図４及び図５は表１のナノカーボン被覆耐火原料ＨをＴＥＭにより観察した結果を示す。マグネシア粒子５がherring-bone（ヘリンボーン）型のＣＮＦ６で被覆された構造を呈していることが観察される。 4 and 5 show the results obtained by observing the nanocarbon-coated refractory raw material H in Table 1 with a TEM. It is observed that the magnesia particles 5 have a structure covered with a herring-bone type CNF6.
一方、表１において、ピッチ被覆原料は、軟化点１２０℃のピッチと耐火原料粒子を容器に入れてピッチが流動する状態になるまで加熱しながら混合することで耐火原料粒子の表面にピッチを被覆したものである。また、カーボンブラック被覆耐火原料は、粒度１０μｍ以下のカーボンブラックを少量の有機バインダーを含有するメタノール中に分散し、耐火原料粒子を入れて混合しながらエタノールを揮発させることで耐火原料粒子の表面にカーボンブラックを被覆したものである。それぞれの被覆量は、前記ナノカーボン被覆耐火原料の場合と同様の方法で測定した。 On the other hand, in Table 1, the pitch-coated raw material is coated with pitch on the surface of the refractory raw material particles by mixing the pitch with a softening point of 120 ° C. and the refractory raw material particles in a container while heating until the pitch flows. It is a thing. The carbon black-coated refractory raw material is prepared by dispersing carbon black having a particle size of 10 μm or less in methanol containing a small amount of an organic binder, and volatilizing ethanol while mixing and mixing the refractory raw material particles on the surface of the refractory raw material particles. Carbon black is coated. Each coating amount was measured by the same method as in the case of the nanocarbon-coated refractory raw material.
表２および表３は各例の耐火原料配合物の組成とその試験結果を示す。各例においては、表２および表３に示す耐火原料配合物に有機バインダーとしてフェノール樹脂を添加して混練し、フリクションプレスにて並形に加圧形後、２５０℃で２４時間加熱した。フェノール樹脂は、エチレングリコールを主成分とする溶媒で希釈し粘性を調整したものを使用した。表中の耐火原料配合物は、最大粒径を３ｍｍとし一般的な耐火れんが（並形形状）に適した粒度構成とした。こうして得られた供試耐火物について、耐熱衝撃性と耐食性を測定した。耐熱衝撃性は１５００℃の溶銑中に３分間浸漬し、その後空冷を１５分間行い、この操作を１０回繰り返した後の亀裂の大きさを目視で測定した。耐食性は回転侵食法により、転炉スラグを用いて１７００℃で５時間の方法で行った。溶損寸法を測定し、表２では実施例１を１００、表３では実施例５を１００として指数で示した。また、実機試験として転炉の内張りに使用した。なお、実施例１の耐火物は、かさ比重３．１５、見掛け気孔率３．０、１４００℃での熱間曲げ強度１５ＭＰａ、固定炭素４．７質量％であった。 Tables 2 and 3 show the compositions of the refractory raw material blends in each example and the test results. In each example, a phenol resin was added as an organic binder to the refractory raw material blends shown in Tables 2 and 3 and kneaded. After pressing in parallel with a friction press, the mixture was heated at 250 ° C. for 24 hours. The phenol resin used was diluted with a solvent containing ethylene glycol as a main component and adjusted in viscosity. The refractory raw material composition in the table had a maximum particle size of 3 mm and a particle size configuration suitable for general refractory bricks (parallel shape). The test refractories thus obtained were measured for thermal shock resistance and corrosion resistance. The thermal shock resistance was immersed for 3 minutes in hot metal at 1500 ° C., then air-cooled for 15 minutes, and the size of the crack was visually measured after repeating this operation 10 times. Corrosion resistance was measured by a rotary erosion method using a converter slag at 1700 ° C. for 5 hours. The erosion dimension was measured, and in Table 2, Example 1 was 100, and in Table 3, Example 5 was 100. Moreover, it used for the lining of the converter as an actual machine test. In addition, the refractory of Example 1 had a bulk specific gravity of 3.15, an apparent porosity of 3.0, a hot bending strength of 15 MPa at 1400 ° C., and fixed carbon of 4.7 mass%.
表２および表３から明らかなように、本発明実施例により得られる耐火物は、いずれも耐熱衝撃性が格段に向上し、耐食性も従来品に相当する比較例に比べて同等以上の数値が得られた。その結果、実機試験においては、実施例２は比較例３に比べて約１．２倍の耐用寿命が得られた。 As is apparent from Tables 2 and 3, the refractories obtained by the examples of the present invention have significantly improved thermal shock resistance, and the corrosion resistance has a numerical value equal to or higher than that of the comparative example corresponding to the conventional product. Obtained. As a result, in the actual machine test, the useful life of Example 2 was about 1.2 times that of Comparative Example 3.
実施例１〜実施例４は、ＣＮＴを被覆する前の耐火原料粒子の平均粒径のみが異なっており、平均粒径が小さいほど耐熱衝撃性に優れる傾向になっている。また、実施例２と実施例３との比較では、実施例３は大きく耐熱衝撃性のレベルが低くなっていることもわかる。 Examples 1 to 4 differ only in the average particle diameter of the refractory raw material particles before coating the CNTs, and the smaller the average particle diameter, the better the thermal shock resistance. Further, in comparison between Example 2 and Example 3, it can be seen that Example 3 has a large thermal shock resistance level.
比較例１は、ピッチを耐火原料粒子に被覆した例、また比較例２はカーボンブラックを耐火原料粒子に被覆した例であるが、実施例と比較すると耐食性および耐熱衝撃性がかなり劣っていることがわかる。また比較例３はメソフェーズピッチを添加した例であるが、やはり耐食性、耐熱衝撃性ともに劣っていることがわかる。比較例４は、従来のアルミナ−カーボン系の耐火物であるが、同じアルミナ−カーボン系の実施例７および実施例８に比べ耐食性、耐熱衝撃性ともに劣っている。 Comparative Example 1 is an example in which pitch is coated with refractory raw material particles, and Comparative Example 2 is an example in which carbon black is coated with refractory raw material particles, but the corrosion resistance and thermal shock resistance are considerably inferior to those of Examples. I understand. Moreover, although the comparative example 3 is an example which added the mesophase pitch, it turns out that both corrosion resistance and thermal shock resistance are also inferior. Comparative Example 4 is a conventional alumina-carbon refractory, but is inferior in both corrosion resistance and thermal shock resistance to Examples 7 and 8 of the same alumina-carbon refractory.
１ マグネシア粒子
２ シングルウォール及びダブルウォールＣＮＴ
３ 多層ＣＮＴで被覆されたマグネシア粒子
４ マグネシア粒子を被覆している多層ＣＮＴ
５ ＣＮＦで被覆されたマグネシア粒子
６ マグネシア粒子を被覆しているherring-bone型ＣＮＦ
1 magnesia particles 2 single wall and double wall CNT
3 Magnesia particles coated with multi-walled CNTs 4 Multi-walled CNTs coated with magnesia particles
5 magnesia particles coated with CNF 6 herring-bone type CNF coated with magnesia particles
Claims (5)