JP4683536B2 - Sunscreen emulsified cosmetics - Google Patents
Sunscreen emulsified cosmetics Download PDFInfo
- Publication number
- JP4683536B2 JP4683536B2 JP2005068306A JP2005068306A JP4683536B2 JP 4683536 B2 JP4683536 B2 JP 4683536B2 JP 2005068306 A JP2005068306 A JP 2005068306A JP 2005068306 A JP2005068306 A JP 2005068306A JP 4683536 B2 JP4683536 B2 JP 4683536B2
- Authority
- JP
- Japan
- Prior art keywords
- zinc oxide
- mass
- oxide powder
- powder
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、疎水化処理酸化亜鉛粉末を配合した日焼け止め乳化化粧料に関する。さらに詳しくは、洗浄性を改良した乳化日焼け止め乳化化粧料に関する。 The present invention relates to a sunscreen emulsified cosmetic containing a hydrophobized zinc oxide powder. More specifically, the present invention relates to an emulsified sunscreen emulsified cosmetic with improved detergency.
太陽光線の紫外線のうち、中波長紫外部の波長２８０〜３２０ｎｍは、皮膚にサンバーンと呼ばれる紅斑を引き起こし、ひどい場合は、火傷と同様の水泡を起こす。また、長波長紫外部の波長３２０〜４００ｎｍは、皮膚の黒化をもたらし、いずれの波長も長期に渡って繰り返し作用すると皮膚の老化を促進することが知られている。 Among the ultraviolet rays of sunlight, the wavelength of 280 to 320 nm in the middle wavelength ultraviolet region causes erythema called sunburn on the skin, and in severe cases, causes water bubbles similar to burns. Further, it is known that the wavelength of 320 to 400 nm in the long-wavelength ultraviolet part causes skin darkening, and when any wavelength repeatedly acts for a long time, it promotes skin aging.
紫外線による肌への悪影響を防御するためには、紫外線吸収剤や紫外線防御粉体を配合した日焼け止め化粧料が使用されている。 In order to prevent the harmful effects of ultraviolet rays on the skin, sunscreen cosmetics containing ultraviolet absorbers and ultraviolet protective powders are used.
このうち、長波長紫外部領域を効果的に防御し、かつ可視部の透明性が高い素材として微粒子酸化亜鉛粉末が使用されている。また、耐汗性の点で、Ｗ／Ｏ型乳化組成物が良好であることが知られている。 Among these, fine zinc oxide powder is used as a material that effectively protects the long wavelength ultraviolet region and has high transparency in the visible region. In addition, it is known that the W / O type emulsion composition is good in terms of sweat resistance.
Ｗ／Ｏ型乳化組成物に、微粒子酸化亜鉛を配合する場合、製剤の安定性の観点から表面処理が必要である。しかしながら、表面処理が不均一であると亜鉛イオンが溶出して系の安定性を害することがあり、微粒子酸化亜鉛は、表面処理方法及びＷ／Ｏ型乳化組成物への安定配合が極めて困難な粉末であった。 When blending fine particle zinc oxide with the W / O emulsion composition, surface treatment is necessary from the viewpoint of the stability of the preparation. However, if the surface treatment is not uniform, zinc ions may elute and harm the stability of the system, and the finely divided zinc oxide is extremely difficult to be stably incorporated into the surface treatment method and W / O type emulsion composition. It was a powder.
一方、サンスクリーン等の日焼け止め化粧料はプールや海水浴で使用されることから、撥水性や撥油性が要求され、何度も塗り直す必要がないように、化粧持ち（撥水性・撥油性）の優れたものが要求されている。そのため、疎水性粉末を配合した油中水型乳化化粧料が日焼け止め化粧料として利用されている。疎水性粉末を配合した油中水型乳化化粧料は、例えば特許文献５〜８に記載されている。化粧持ちを向上させる技術としては通常の油分よりもさっぱりした使用性で、撥水効果が高いオイルや樹脂成分を配合することが常套手段として用いられている。
しかしながら、使用後にはこれらの成分が残存してしまいシャワー等で洗浄し難くなってしまうといった課題があった。
On the other hand, sunscreen cosmetics such as sunscreens are used in swimming pools and sea bathing, so they are required to have water and oil repellency and do not need to be repainted many times (water and oil repellency). An excellent one is required. For this reason, water-in-oil emulsified cosmetics containing hydrophobic powder are used as sunscreen cosmetics. For example,
However, there is a problem that these components remain after use and are difficult to wash with a shower or the like.
また、特許文献９においても、シリコン処理した酸化亜鉛粉末を配合した日焼け止め化粧料が開示されている。この日焼け止め化粧料は、イソノナン酸エステルとシリコーン系界面活性剤を配合するものであり、のびがよく使用感触に優れるものの、上記特許文献５〜８の乳化化粧料と同じく、使用後の洗浄性が好ましくなく、落とし難いといった課題があった。
Patent Document 9 also discloses sunscreen cosmetics containing silicon-treated zinc oxide powder. This sunscreen cosmetic contains an isononanoic acid ester and a silicone-based surfactant and has a good spread and excellent touch feeling. However, as with the above-described emulsified cosmetics of
発明者らは上述の観点に鑑み、透明性の高い紫外線散乱剤として有用な微粒子酸化亜鉛粉末を配合した日焼け止め化粧料において、特定の油分を、シリコーン系界面活性剤でなく特定の非イオン性界面活性剤で乳化すると、化粧もちが良くてかつ使用後に極めて洗い流し易い日焼け止め乳化化粧料が得られることを見出し、本発明を完成するに至った。 In view of the above-mentioned viewpoints, the inventors of the sunscreen cosmetic blended with fine zinc oxide powder useful as a highly transparent ultraviolet light scattering agent have a specific oil content, not a silicone surfactant, a specific nonionic property. When emulsified with a surfactant, it has been found that a sunscreen emulsified cosmetic with good makeup and easy to wash off after use can be obtained, and the present invention has been completed.
本発明の目的は、使用後の洗浄性に極めて優れた日焼け止め乳化化粧料を提供することである。 An object of the present invention is to provide a sunscreen emulsified cosmetic that is extremely excellent in cleanability after use.
すなわち、本発明は、
（ａ）１次粒子径１μｍ以下の微粒子酸化亜鉛粉末を表面処理することにより製造される疎水化処理酸化亜鉛粉末を１〜４０質量％と、（ｂ）揮発性シリコーンを１０〜４０質量％と、（ｃ）イソノナン酸イソノニルを３〜１０質量％と、（ｄ）シリコーン系界面活性剤以外のHLBが7以下の親油性界面活性剤である非イオン性界面活性剤を１〜４質量％と、（ｅ）水とを含有し、前記（ｄ）非イオン性界面活性剤がジイソステアリン酸ポリグリセリル又はトリイソステアリン酸PEG-20グリセリルであることを特徴とする日焼け止め油中水型乳化化粧料を提供するものである。
さらに、本発明は、
（ａ）１次粒子径１μｍ以下の微粒子酸化亜鉛粉末を表面処理することにより製造される疎水化処理酸化亜鉛粉末を１〜４０質量％と、（ｂ）揮発性シリコーンを１０〜４０質量％と、（ｃ）流動パラフィン及びイソノナン酸イソノニルを１〜１０質量％と、（ｄ）シリコーン系界面活性剤以外のHLBが7以下の親油性界面活性剤である非イオン性界面活性剤を１〜４質量％と、（ｅ）水とを含有し、前記（ｄ）非イオン性界面活性剤がジイソステアリン酸ポリグリセリル又はトリイソステアリン酸PEG-20グリセリルであることを特徴とする日焼け止め油中水型乳化化粧料を提供するものである。
That is, the present invention
(A) 1 to 40% by mass of hydrophobized zinc oxide powder produced by surface-treating fine particle zinc oxide powder having a primary particle diameter of 1 μm or less, and (b) 10 to 40% by mass of volatile silicone. (C) 3 to 10% by mass of isononyl isononanoate and (d) 1 to 4% by mass of a nonionic surfactant which is a lipophilic surfactant having an HLB of 7 or less other than the silicone surfactant. And (e) water, and (d) a nonionic surfactant is polyglyceryl diisostearate or PEG-20 glyceryl triisostearate, and provides a water-in-sun emulsion oil-based cosmetic. To do.
Furthermore, the present invention provides
(A) 1 to 40% by mass of hydrophobized zinc oxide powder produced by surface-treating fine particle zinc oxide powder having a primary particle diameter of 1 μm or less, and (b) 10 to 40% by mass of volatile silicone. (C) 1 to 10% by mass of liquid paraffin and isonononyl isononanoate, and (d) 1 to 4 nonionic surfactants which are lipophilic surfactants having an HLB of 7 or less other than silicone surfactants. A sunscreen oil-in-water emulsified cosmetic, comprising: (e) water, and (d) the nonionic surfactant is polyglyceryl diisostearate or PEG-20 glyceryl triisostearate A fee is provided.
また、本発明は、シリコーン系界面活性剤を実質的に使用しないことを特徴とする上記の日焼け止め油中水型乳化化粧料を提供するものである。
The present invention also provides the water-in-oil-in-sun emulsified cosmetic described above, characterized by substantially not using a silicone-based surfactant .
本発明の日焼け止め乳化化粧料は、化粧持ち（撥水性・撥油性）に優れながら、使用後に容易に洗い流せるという顕著な効果を発揮する。即ち、日焼け止め化粧料やメーキャップ化粧料専用のクレンジング洗浄料を使う必要がなく、石鹸、ボディーソープで簡単に洗い落とすことが出来るので、極めて便利である。また、塗布し易く、塗布時の使用感にも優れている。 The sunscreen emulsified cosmetic of the present invention exhibits a remarkable effect that it can be easily washed off after use, while having excellent makeup (water and oil repellency). In other words, it is not necessary to use a cleansing cleansing agent dedicated to sunscreen cosmetics or makeup cosmetics, and can be easily washed off with soap and body soap, which is extremely convenient. Moreover, it is easy to apply and excellent in the feeling of use during application.
以下、本発明について詳述する。 Hereinafter, the present invention will be described in detail.
（ａ）疎水化処理酸化亜鉛粉末
使用できる疎水化処理酸化亜鉛としては、ステアリン酸アルミニウム等で処理された金属石鹸処理酸化亜鉛、シクロデキストリン−脂肪酸エステル等で処理された脂肪酸−デキストリン処理粉体（ＷＳＸ−トランスパロンTM等）、Ｎ−ラウロイル−Ｌ−リジン等で処理されたアミノ酸処理粉体（ＬＬ５−ＳＴ（ＨＳ）TM等）、メチルハイドロジェンポリシロキサン、メチルハイドロジェンポリシロキサン・ジメチルポリシロキサン共重合体、ジメチルポリシロキサン、シリカ＋ジメチルポリシロキサン等で処理されたシリコーン処理粉体（ＳＳ−Ａｃｔｉｖｏｘ８０TM等）、パーフルオロアルキルリン酸等で処理されたフッ素処理粉体（ＰＦTM等）、オクチルトリエトキシシラン等で処理されたシランカップリング剤処理粉体（ＯＴＳTM等）が挙げられる。この中で、特に好ましい処理粉体として、オクチルトリエトキシシラン等で処理されたシランカップリング剤処理粉体等が挙げられる。
本発明に使用する疎水化処理酸化亜鉛粉末は特に限定されない。
但し、酸化亜鉛粉末を溶媒中に分散させて、一般式（１）で示されるパーフルオロアルキルを有するリン酸エステルと、一般式（２）で示される、分子量が３０，０００〜３００，０００のアクリル酸２-エチルヘキシル、メタクリル酸、メタクリル酸メチル、メタクリル酸ブチルの共重合体とメチルポリシロキサンのメチル基の一部をヒドロキシプロピル基で置換したものとのエステルとにより表面処理を行って疎水化処理酸化亜鉛粉末を製造する方法において、１次粒子径１μm以下の微粒子酸化亜鉛粉末を使用し、溶媒の使用量を該酸化亜鉛粉末に対して５０〜９０質量％の範囲の範囲で行うことにより製造される疎水化処理酸化亜鉛粉末を使用することが好ましい。なぜなら、一般的なＷ／Ｏ型製剤の連続相に配合しても製剤として低粘度のものが得られやすく、また、比表面積が維持されていることから、肌に塗布した時のシェアでほぐれて白浮きせずに効果的に長波長紫外部を防御することが可能となるからである。
The hydrophobized zinc oxide powder used in the present invention is not particularly limited.
However, the zinc oxide powder is dispersed in a solvent, the phosphoric acid ester having perfluoroalkyl represented by the general formula (1), and the molecular weight represented by the general formula (2) is 30,000 to 300,000. Hydrophobized by surface treatment with 2-ethylhexyl acrylate, methacrylic acid, methyl methacrylate, butyl methacrylate copolymer and ester of methylpolysiloxane partially substituted with hydroxypropyl group In the method for producing a treated zinc oxide powder, by using a fine particle zinc oxide powder having a primary particle diameter of 1 μm or less and using a solvent in an amount in the range of 50 to 90 mass% with respect to the zinc oxide powder. It is preferable to use the hydrophobized zinc oxide powder produced. Because it is easy to obtain a low-viscosity formulation even when blended into a continuous phase of a general W / O type formulation, and since the specific surface area is maintained, the share when applied to the skin is loosened. This is because it is possible to effectively protect the long-wavelength ultraviolet part without causing white floating.
この疎水化処理酸化亜鉛粉末は、特開２００１−３０２４５５号公報に記載された方法において、表面処理される化粧料顔料の代りに、１次粒子径１μm以下の微粒子酸化亜鉛粉末を表面処理することにより製造される。好ましくは０.１μｍ以下の微粒子酸化亜鉛粉末が使用される。なお、１次粒子径とは１次粒子の平均粒子径のことである。 This hydrophobized zinc oxide powder is obtained by surface-treating fine zinc oxide powder having a primary particle diameter of 1 μm or less in place of the cosmetic pigment to be surface-treated in the method described in JP-A-2001-302455. Manufactured by. Preferably, a fine particle zinc oxide powder of 0.1 μm or less is used. The primary particle size is the average particle size of primary particles.
１次粒子径１μｍ以下の微粒子酸化亜鉛としては、例えば堺化学（株）製のＦＩＮＥＸ−５０、住友大阪セメント（株）製のＺｎＯ−３５０、石原産業（株）製の酸化亜鉛ＦＺＯ−５０、あるいはテイカ（株）製の微粒子酸化亜鉛ＭＺ−５００等を使用できる。また、ＷＯ９９／２５６５４号公報（特願平１１−５２５９８４号）記載の微粒子酸化亜鉛粉末（カーネーションの花びら状の外観を有するもの）を使用できる。 Examples of the fine particle zinc oxide having a primary particle diameter of 1 μm or less include FINEX-50 manufactured by Sakai Chemical Co., Ltd., ZnO-350 manufactured by Sumitomo Osaka Cement Co., Ltd., and zinc oxide FZO-50 manufactured by Ishihara Sangyo Co., Ltd. Alternatively, fine zinc oxide MZ-500 manufactured by Teika Co., Ltd. can be used. In addition, fine zinc oxide powder (having a carnation petal-like appearance) described in WO99 / 25654 (Japanese Patent Application No. 11-525984) can be used.
一般式（１）で示されるパーフルオロアルキル基を有するリン酸エステルとしては、例えば、旭硝子（株）からＡＧ−５３０の名称で市販されている水分散エマルジョンの固形分であるパーフルオロアルキルリン酸エステルジエタノールアミン塩、またはこれと同じ分子構造を持つが塩の形が異なるパーフルオロアルキルリン酸エステルナトリウム塩、パーフルオロアルキルリン酸エステルカリウム塩、パーフルオロアルキルリン酸アンモニウム塩等を酸を用いてアミン塩、アンモニウム塩、アルカリ金属塩を除去したものを用いることができる。 As the phosphoric acid ester having a perfluoroalkyl group represented by the general formula (1), for example, perfluoroalkyl phosphoric acid which is a solid content of an aqueous dispersion emulsion commercially available under the name AG-530 from Asahi Glass Co., Ltd. Ester diethanolamine salt or perfluoroalkyl phosphate sodium salt, perfluoroalkyl phosphate potassium salt, perfluoroalkyl phosphate ammonium salt, etc. having the same molecular structure but different salt form using amine What removed salt, ammonium salt, and alkali metal salt can be used.
一般式（２）で示されるエステル（以下「アクリルシリコーン共重合物」と称する場合がある）としては、例えば、信越化学工業（株）からＫＰ−５４１、ＫＰ−５４３、ＫＰ−５４５の名称で市販されているイソプロピルアルコール、酢酸ブチル、揮発性シリコーンに溶解された共重合物、あるいはＫＰ−５４４と称するアクリルシリコーン共重合物をその他の有機溶媒に溶解したものが挙げられる。 Examples of the ester represented by the general formula (2) (hereinafter sometimes referred to as “acrylic silicone copolymer”) include the names KP-541, KP-543 and KP-545 from Shin-Etsu Chemical Co., Ltd. Examples include commercially available isopropyl alcohol, butyl acetate, a copolymer dissolved in volatile silicone, or an acrylic silicone copolymer called KP-544 dissolved in another organic solvent.
一般式（１）及び（２）にて示されるパーフルオロアルキルリン酸エステルとアクリルシリコーン共重合物の総被覆量は、微粒子酸化亜鉛粉末の比表面積をＸｍ2/ｇとすると、Ｘ／５〜Ｘ／１０重量％に調整することにより、十分な撥水性と撥油性が得られる。この範囲外の量で被覆すると、一般式（１）のリン酸エステルが粉体表面以外で自らが粉末状に析出し粉末中に共存するようになり、また粉末同士の過剰な凝集が無視できなくなって長波長紫外部の防御能が低下する恐れがあり、あるいは撥水性・撥油性が不足する可能性がある。
したがって、表面処理される微粒子酸化亜鉛粉末の比表面積がＸ(m2/g)の場合、一般式（１）のリン酸エステルと一般式（２）のエステルとの使用量の和は、該酸化亜鉛粉末に対してＸ／１０〜Ｘ／５質量％の範囲で行われることが好ましい。
The total coating amount of the perfluoroalkyl phosphate ester and acrylic silicone copolymer represented by the general formulas (1) and (2) is X / 5 to 5 when the specific surface area of the fine zinc oxide powder is Xm 2 / g. By adjusting to X / 10% by weight, sufficient water repellency and oil repellency can be obtained. If the coating amount is outside this range, the phosphoric acid ester of the general formula (1) is deposited in a powder form other than the powder surface and coexists in the powder, and excessive aggregation of the powder can be ignored. There is a possibility that the defensive ability of the long-wavelength ultraviolet part may be reduced and the water repellency and oil repellency may be insufficient.
Therefore, when the specific surface area of the finely divided zinc oxide powder to be surface-treated is X (m 2 / g), the sum of the amounts used of the phosphate ester of the general formula (1) and the ester of the general formula (2) is It is preferable to carry out in the range of X / 10 to X / 5% by mass with respect to the zinc oxide powder.
また、一般式（１）のリン酸エステルと前記一般式（２）のエステルとの使用量の質量比が、一般式（１）のリン酸エステル／一般式（２）のエステル＝１〜５で行うことが好ましく、さらに好ましくは、２〜４である。この範囲外であると、得られる粉末は、一般的に用いられる化粧料油分との親和性が低下したり、あるいは製剤として肌に塗布した時の耐水性（撥油性）が不足したりする場合がある。 Moreover, the mass ratio of the usage-amount of the phosphate ester of General formula (1) and the ester of the said General formula (2) is the ester of General formula (1) / ester of General formula (2) = 1-5. It is preferable to carry out with 2-4. If the content is outside this range, the resulting powder may have poor affinity with commonly used cosmetic oils, or water resistance (oil repellency) may be insufficient when applied to the skin as a formulation. There is.
この製造方法では、溶媒の量が酸化亜鉛粉末に対して５０〜９０質量％の範囲であることを特徴とする。表面処理剤の一般式（１）のリン酸エステルと一般式（２）のエステルを用いて、常法に従って表面処理を行うと、驚くべきことに、低吸油量、見掛けの比容積が低く撥水性・撥油性に優れた疎水化処理微粒子酸化亜鉛粉末が製造される。この溶媒の量は、粉末が分散する系内に存在するすべての溶媒の量であり、一般式（１）と（２）の化合物を除いたすべての溶液のことである。なお、粉末は予め溶媒に分散させて処理容器内に添加する必要はない。処理容器に、最初に粉末を添加し、次に一般式（１）と（２）の処理剤溶液（溶液）を添加し、最後に溶媒を添加して攪拌処理する方法が好ましい。 This production method is characterized in that the amount of the solvent is in the range of 50 to 90% by mass with respect to the zinc oxide powder. Surprisingly, when the surface treatment is carried out according to a conventional method using the phosphoric acid ester of the general formula (1) and the ester of the general formula (2), the low oil absorption and the apparent specific volume are low. Hydrophobized finely divided zinc oxide powder with excellent water and oil repellency is produced. The amount of the solvent is the amount of all the solvents present in the system in which the powder is dispersed, and is all the solutions excluding the compounds of the general formulas (1) and (2). The powder need not be dispersed in a solvent in advance and added to the processing container. A method is preferred in which the powder is first added to the processing container, then the processing agent solutions (solutions) of the general formulas (1) and (2) are added, and finally the solvent is added and stirred.
溶媒は、メチルアルコール、エチルアルコール、イソプロピルアルコール等の低級アルコール類、酢酸エチル、酢酸ブチル等のエステル溶媒、揮発性シリコーン、アセトン等の有機溶媒である。イソプロピルアルコール（以下、ＩＰＡと記載）が好ましく用いられる。なお、本発明において、酸化亜鉛粉末に対して５０〜９０質量％用いる溶媒は、表面処理剤を予め溶解させる場合に用いる溶媒を含む、全溶媒量である。 The solvent is a lower alcohol such as methyl alcohol, ethyl alcohol or isopropyl alcohol, an ester solvent such as ethyl acetate or butyl acetate, or an organic solvent such as volatile silicone or acetone. Isopropyl alcohol (hereinafter referred to as IPA) is preferably used. In addition, in this invention, the solvent used 50 to 90 mass% with respect to zinc oxide powder is the total amount of solvent containing the solvent used when dissolving a surface treating agent previously.
上記製造方法のフローシートを「図１」に示す。
（１）まず、処理容器に、１次粒子径１μm以下の微粒子酸化亜鉛粉末、表面処理剤の一般式（１）のリン酸エステルと一般式（２）のエステル、溶媒とを添加する。添加の順は特に問われないが、粉末、処理剤（溶液）、溶媒の順で添加することが好ましい。
表面処理剤は、そのまま添加しても、予め溶媒に溶かした状態で添加しても良いが、製造効率上、予め溶媒に溶かした状態で添加することが好ましい。
表面処理剤を溶解する溶媒は制限されない。通常はイソプロピルアルコールなどの溶媒に３０〜７０％程度に溶解させた状態で添加するのが扱いやすい。
さらに加える溶媒量としては、処理剤を予め溶かすための溶媒との合計量が、被処理粉末量に対して５０〜９０質量％であることが好ましく、さらに好ましくは６０〜８０質量％である。５０質量％未満では溶媒中に粉末が十分に分散しきれず凝集したまま被覆される（不完全な表面処理の）割合が高くなる。一方、９０質量％より多い量では粉末は十分に分散されるものの、見掛けの比容積が下がりにくく、また被覆そのものは溶媒がほとんど除去されるタイミングで行われるため、その領域に達するまでの溶媒除去時間が長くなる。即ち溶媒が過剰で、かつ非効率的でもあるので好ましくない。
粉末を混合（分散）させる方法は特に限定されないが、通常は適当な混合(分散)機、例えば回転ボールミル、振動式ボールミル、遊星型ボールミル、サンドミル、アトライター、バグミル、ポニミキサー、プラネタリーミキサー、らいかい機、ヘンシェルミキサー、スーパーミキサー、ニーダー、媒体撹拌ミル（ビーズミル）等を用いて行う。
混合時間は制限されないが、通常0.1〜2hで行なう。
（２）次に溶媒除去を行う。溶媒除去は分散液を撹拌及び場合により適当に加熱をしながら行う。さらに効率的にはトラップを備えた真空ポンプで減圧状態を保つことで行うことができる。
（３）次に粉砕を行う。粉砕方法は特に限定されないが、高速回転粉砕機（ハンマーミル、ケージミル、ピンミル、ディスインテグレータ、スクリーンミル、ターボ型ミル、遠心分級ミル等）、ボールミル（転動ミル、振動ボールミル、遊星ミル）、撹拌ミル（タワーミル、撹拌槽型ミル、流通管型ミル、アニュラーミル）、ラボミル、ジェットミル、剪断ミル、圧縮摩粋型粉砕機、コロイドミル等により行う。
（４）最後に乾燥する。
乾燥は電熱式タイプの加熱乾燥機、あるいは加熱した気体を供給して行う乾燥機等を用いて行う。
乾燥時間は、特に限定されないが、１ｈ〜２５０ｈ、乾燥温度は５０〜１５０℃の範囲で行うことが望ましい。これ以外で行うと、十分な乾燥が行われないか、あるいは処理剤の劣化が起こる恐れがある。
A flow sheet of the above manufacturing method is shown in FIG.
(1) First, a fine particle zinc oxide powder having a primary particle diameter of 1 μm or less, a phosphate ester of the general formula (1), an ester of the general formula (2), and a solvent are added to the processing container. The order of addition is not particularly limited, but it is preferable to add in the order of powder, treating agent (solution), and solvent.
The surface treatment agent may be added as it is, or may be added in a state dissolved in a solvent in advance, but it is preferably added in a state dissolved in a solvent in advance for production efficiency.
The solvent that dissolves the surface treatment agent is not limited. Usually, it is easy to handle by adding it in a state of about 30 to 70% dissolved in a solvent such as isopropyl alcohol.
Further, as the amount of the solvent to be added, the total amount with the solvent for dissolving the treating agent in advance is preferably 50 to 90% by mass, more preferably 60 to 80% by mass with respect to the amount of powder to be treated. If it is less than 50% by mass, the ratio of the powder that cannot be sufficiently dispersed in the solvent and is agglomerated and coated (incomplete surface treatment) becomes high. On the other hand, if the amount exceeds 90% by mass, the powder is sufficiently dispersed, but the apparent specific volume is unlikely to decrease, and the coating itself is performed at the timing when the solvent is almost removed. The time will be longer. That is, it is not preferable because the solvent is excessive and inefficient.
The method of mixing (dispersing) the powder is not particularly limited, but usually a suitable mixing (dispersing) machine, such as a rotating ball mill, vibratory ball mill, planetary ball mill, sand mill, attritor, bag mill, poni mixer, planetary mixer, lei It is carried out using a paddle machine, a Henschel mixer, a super mixer, a kneader, a medium stirring mill (bead mill) or the like.
The mixing time is not limited, but is usually 0.1 to 2 hours.
(2) Next, the solvent is removed. Solvent removal is carried out with stirring and optionally heating the dispersion. More efficiently, it can be carried out by maintaining a reduced pressure state with a vacuum pump provided with a trap.
(3) Next, pulverization is performed. The grinding method is not particularly limited, but a high-speed rotary grinding machine (hammer mill, cage mill, pin mill, disintegrator, screen mill, turbo mill, centrifugal classification mill, etc.), ball mill (rolling mill, vibrating ball mill, planetary mill), stirring Milling (tower mill, stirring tank mill, flow pipe mill, annular mill), lab mill, jet mill, shear mill, compression-type mill, colloid mill, etc.
(4) Finally, dry.
Drying is performed using an electric heating type heat dryer or a dryer which is supplied with heated gas.
Although drying time is not specifically limited, It is desirable to perform in 1-250h and drying temperature in the range of 50-150 degreeC. Otherwise, sufficient drying may not be performed or the processing agent may be deteriorated.
上記により得られる微粒子酸化亜鉛粉末は、低吸油量、見掛けの比容積が低いという顕著な効果を有する。
この微粒子酸化亜鉛粉末の好ましい吸油量は１５〜４０mL/１００gである。
この吸油量は、ＪＩＳＫ５１０１ ２１.に準じた方法、あるいは市販の吸油量測定機器を用いて測定される数値である。
また、本発明に用いる微粒子酸化亜鉛粉末の好ましい見掛けの比容積は０.５〜０.９mL/gである。
この見掛けの比容積は、ＪＩＳＫ５１０１ ２０.２記載のタップ法に準じて測定される１ｇ当たりの容積（mL）を表す数値（mL/g）である。
The finely divided zinc oxide powder obtained as described above has a remarkable effect of low oil absorption and low apparent specific volume.
The preferred oil absorption of the fine zinc oxide powder is 15 to 40 mL / 100 g.
This oil absorption is a numerical value measured using a method according to JISK5101 21. or using a commercially available oil absorption measuring instrument.
The preferred specific volume of the fine zinc oxide powder used in the present invention is 0.5 to 0.9 mL / g.
This apparent specific volume is a numerical value (mL / g) representing a volume (mL) per gram measured according to the tap method described in JISK5101 20.2.
本発明において好ましく使用される（ａ）疎水化処理酸化亜鉛粉末は、上述の通りである。この微粒子酸化亜鉛粉末は、低吸油量、見掛けの比容積が低いという優れた効果を有すると同時に、撥水性・撥油性に優れ、かつ製剤に安定配合可能なものであり、紫外線散乱効果にも優れている。 The (a) hydrophobized zinc oxide powder preferably used in the present invention is as described above. This fine zinc oxide powder has the excellent effects of low oil absorption and low apparent specific volume, and at the same time, it is excellent in water and oil repellency, and can be stably blended into the preparation, and also has an ultraviolet scattering effect. Are better.
＜配合量の説明＞
本発明の日焼け止め化粧において、（ａ）成分の疎水化処理酸化亜鉛粉末は、好ましくは０.１〜６０質量％、より好ましくは１〜４０質量％程度配合される。０．１質量％未満では、紫外線防御効果を十分に得ることができず、逆に６０質量％を越えて配合すると、塗布部が白浮きしてしまう場合がある。また、粉っぽい使用性になることがある。
油中水型乳化化粧料の場合には１〜４０質量％配合されることが好ましい。
<Description of blending amount>
In the sunscreen makeup of the present invention, the hydrophobized zinc oxide powder (a) is preferably blended in an amount of 0.1 to 60% by mass, more preferably about 1 to 40% by mass. If the amount is less than 0.1% by mass, a sufficient ultraviolet protective effect cannot be obtained. Conversely, if the amount exceeds 60% by mass, the coated part may whiten. Moreover, it may become powdery usability.
In the case of a water-in-oil emulsified cosmetic, 1 to 40% by mass is preferably blended.
（ｂ）揮発性シリコーン
本発明に使用する（ｂ）成分の揮発性シリコーンは、デカメチルシクロペンタシロキサン、オクタメチルシクロテトラシロキサン、ドデカメチルシクロヘキサシロキサン、メチルトリメチコン、デカメチルテトラシロキサンであり、単独または２種以上が目的に応じて組み合わせて配合される。
(B) Volatile silicone The volatile silicone of component (b) used in the present invention is decamethylcyclopentasiloxane, octamethylcyclotetrasiloxane, dodecamethylcyclohexasiloxane, methyltrimethicone, decamethyltetrasiloxane, A single compound or a combination of two or more compounds is blended depending on the purpose.
＜配合量の説明＞
配合量は適宜決定されるが、１０〜４０質量％配合することが好ましい。１０質量％未満の場合安定な油中水型乳化組成物を得るためには必然的に他の油分の配合量が多くなるためさっぱりした使用感触といった揮発性シリコーン配合のメリットが得られにくくなる。４０質量％を越えると塗布中のなじみが遅くなり、使用感触が油っぽくなるため好ましくない。
<Description of blending amount>
Although a compounding quantity is determined suitably, it is preferable to mix | blend 10-40 mass%. When the amount is less than 10% by mass, in order to obtain a stable water-in-oil emulsion composition, the blending amount of other oils inevitably increases, so that it is difficult to obtain the merit of volatile silicone blending such as a refreshing feel. If it exceeds 40% by mass, the familiarity during application becomes slow and the feeling of use becomes oily, which is not preferable.
（ｃ）流動パラフィン及び／又はイソノナン酸イソノニル
（１）使用性の観点（のび、なじみ、べたつきのなさ）、（２）他のシリコーン油やシリコーン活性剤（基本的に洗浄性が悪い）との相溶性の高さ、（３）相溶性の高さゆえの安定性の向上、（４）紫外線吸収剤の溶解性の高さという観点からは、イソノナン酸イソノニルが好ましい。しかし、流動パラフィンも、従来通常配合していた不揮発性シリコーン油に換えて配合すると、格段に洗浄性が向上する。
流動パラフィンとイソノナン酸イソノニルとを併用しても好ましい。
イソノナン酸イソノニルの市販品としては、Ｃｅｔｉｏｌ ＩＮＩＮ（ヘンケル社）が挙げられる。
(C) Liquid paraffin and / or isononyl isononanoate (1) Usability point of view (free, familiar, non-sticky), (2) Other silicone oils and silicone activators (basically poor cleanability) From the viewpoints of high compatibility, (3) improvement in stability due to high compatibility, and (4) high solubility of the ultraviolet absorber, isononyl isononanoate is preferred. However, when liquid paraffin is blended in place of the conventional non-volatile silicone oil, detergency is greatly improved.
It is also preferable to use liquid paraffin and isononyl isononanoate in combination.
A commercially available product of isononyl isononanoate is Cetiol ININ (Henkel).
＜流動パラフィンの配合量の説明＞
配合量は日焼け止め乳化化粧料全量に対して１〜１０質量％であることが好ましい。１．０質量％未満の場合、洗浄性の向上効果が得られにくくなる。１０質量％を越えるとべたつきが感じられ、のびも重くなるため好ましくない。
<Description of blending amount of liquid paraffin>
The blending amount is preferably 1 to 10% by mass relative to the total amount of the sunscreen emulsified cosmetic. When the amount is less than 1.0% by mass, it is difficult to obtain the effect of improving the cleaning property. If it exceeds 10% by mass, stickiness is felt and the spread becomes heavy.
＜イソノナン酸イソノニルの配合量の説明＞
配合量は日焼け止め乳化化粧料全量に対して１〜１０質量％であることが好ましい。１．０質量％未満の場合、洗浄性の向上効果が得られにくくなる。１０質量％を越えるとべたつきが感じられ、のびも重くなるため好ましくない。
<Description of blending amount of isononyl isononanoate>
The blending amount is preferably 1 to 10% by mass relative to the total amount of the sunscreen emulsified cosmetic. When the amount is less than 1.0% by mass, it is difficult to obtain the effect of improving the cleaning property. If it exceeds 10% by mass, stickiness is felt and the spread becomes heavy.
本発明の日焼け止め乳化化粧料は、（ｄ）非イオン性界面活性剤を配合して、油中水型乳化日焼け止め化粧料とすることにより、洗浄性に優れたものとなる。また、伸びが良く、さっぱりとした使用性を発揮することができる。
本発明では、シリコーン系界面活性剤｛例えば親油性活性剤として周知なポリオキシアルキレン変性オルガノポリシロキサンであるシリコーンＫＦ−６０１７、シリコーンＫＦ−６０２８（信越化学工業社製）等｝は実質的に使用しない。シリコーン系界面活性剤を配合すると、使用後の洗浄性が落ちてしまう。
好ましい非イオン性界面活性剤は、シリコーン系界面活性剤以外のHLBが7以下の親油性界面活性剤であり、例えば、ジイソステアリン酸ポリグリセリル、トリイソステアリン酸PEG-20グリセリルが挙げられる。市販品としては、WOGEL18DV（松本製薬工業株式会社製）、エマレックスGWIS320（日本エマルジョン社製）、エステモール182V（日清製油株式会社製）などが挙げられる。
The sunscreen emulsified cosmetic of the present invention has excellent detergency by blending (d) a nonionic surfactant into a water-in-oil emulsified sunscreen cosmetic. In addition, it has good elongation and can exhibit a refreshing usability.
In the present invention, a silicone-based surfactant {for example, silicone KF-6017 and silicone KF-6028 (manufactured by Shin-Etsu Chemical Co., Ltd.), which are polyoxyalkylene-modified organopolysiloxanes well-known as lipophilic surfactants) is substantially used. do not do. When a silicone-based surfactant is blended, the washability after use is lowered.
Preferred nonionic surfactants are lipophilic surfactants having an HLB of 7 or less other than silicone surfactants, and examples thereof include polyglyceryl diisostearate and PEG-20 glyceryl triisostearate . Examples of commercially available products include WOGEL18DV (manufactured by Matsumoto Pharmaceutical Co., Ltd.), Emarex GWIS320 (manufactured by Nippon Emulsion Co., Ltd.), and Este Mall 182V (manufactured by Nisshin Oil Co., Ltd.).
＜配合量の説明＞
配合量は日焼け止め乳化化粧料全量に対して１〜４質量％が好ましい。１質量％以下では、油中水型乳化化粧料とした場合に乳化安定性が悪くなる場合がある。また、４質量％以上配合しても乳化安定性のさらなる向上は得られず、かえって皮膚への刺激やべたつきが生じる原因となる。
<Description of blending amount>
The blending amount is preferably 1 to 4% by mass with respect to the total amount of the sunscreen emulsified cosmetic. If it is 1% by mass or less, the emulsion stability may be deteriorated when a water-in-oil emulsion cosmetic is used. Further, even when blended in an amount of 4% by mass or more, further improvement in emulsification stability cannot be obtained, which may cause skin irritation and stickiness.
（ｅ）水
本発明の日焼け止め化粧料を、油中水型乳化日焼け止め化粧料して用いる場合には、水が１〜６０質量％範囲で適宜配合される。
(E) Water When the sunscreen cosmetic of the present invention is used as a water-in-oil emulsified sunscreen cosmetic, water is appropriately blended in the range of 1 to 60% by mass.
本発明の油中水型乳化日焼け止め化粧料は、さらに（ｆ）有機変性粘土鉱物を配合することにより、安定性を向上させ、塗布の時の伸びがよく、みずみずしい使用感を付与することができる。
本発明に配合される（ｆ）有機変性粘土鉱物は、乳化助剤として用いられものである。この有機変性粘土鉱物は、三層構造を有するコロイド性含水ケイ酸アルミニウムの一種で、一般に下記一般式（３）で表される粘土鉱物を第四級アンモニウム塩型カチオン界面活性剤で変性したものである。
具体的にはモンモリロナイト、サポナイト、ヘクトライト等の天然または合成（この場合、式中の（ＯＨ）基がフッ素で置換されたもの）のモンモリロナイト群（市販品ではビーガム、クニピア、ラポナイト等がある。）およびナトリウムシリシックマイカやナトリウムまたはリチウムテニオライトの名で知られる合成雲母（市販品ではダイモナイト：トピー工業（株）等がある。）等の粘土鉱物を第四級アンモニウム塩型カチオン界面活性剤で処理して得られる。
ここで用いられる第四級アンモニウム塩型カチオン界面活性剤は、下記一般式（４）で表されるものである。
かかる第四級アンモニウム塩型カチオン界面活性剤としては、例えばドデシルトリメチルアンモニウムクロリド、ミリスチルトリメチルアンモニウムクロリド、セチルトリメチルアンモニウムクロリド、ステアリルトリメチルアンモニウムクロリド、アラキルトリメチルアンモニウムクロリド、ベヘニルトリメチルアンモニウムクロリド、ミリスチルジメチルエチルアンモニウムクロリド、セチルジメチルエチルアンモニウムクロリド、ステアリルジメチルエチルアンモニウムクロリド、アラキルジメチルエチルアンモニウムクロリド、ベヘニルジメチルエチルアンモニウムクロリド、ミリスチルジエチルメチルアンモニウムクロリド、セチルジエチルメチルアンモニウムクロリド、ステアリルジエチルメチルアンモニウムクロリド、アラキルジエチルメチルアンモニウムクロリド、ベヘニルジエチルメチルアンモニウムクロリド、ベンジルジメチルミリスチルアンモニウムクロリド、ベンジルジメチルセチルアンモニウムクロリド、ベンジルジメチルステアリルアンモニウムクロリド、ベンジルジメチルベヘニルアンモニウムクロリド、ベンジルメチルエチルセチルアンモニウムクロリド、ベンジルメチルエチルステアリルアンモニウムクロリド、ジベヘニルジヒドロキシエチルアンモニウムクロリド、および相当するブロミド等、更にはジパルミチルプロピルエチルアンモニウムメチルサルフェート等が挙げられる。本発明の実施にあたっては、これらのうち一種または二種以上が任意に選択される。
有機変性粘土鉱物の代表的なものとしては、ジメチルアルキルアンモニウムヘクトライト、ベンジルジメチルステアリルアンモニウムヘクトライト、塩化ジステアリルジメチルアンモニウム処理ケイ酸アルミニウムマグネシウム等が挙げられる。市販品としては、ベントン２７（ベンジルジメチルステアリルアンモニウムクロライド処理ヘクトライト：ナショナルレッド社製）およびベントン３８（ジステアリルジメチルアンモニウムクロライド処理ヘクトライト：ナショナルレッド社製）が好ましい。
The water-in-oil emulsified sunscreen cosmetic of the present invention can further improve stability by adding (f) an organically modified clay mineral, has good elongation at the time of application, and can give a fresh feeling of use. it can.
The (f) organically modified clay mineral blended in the present invention is used as an emulsification aid. This organically modified clay mineral is a kind of colloidal hydrous aluminum silicate having a three-layer structure, and is generally a clay mineral represented by the following general formula (3) modified with a quaternary ammonium salt type cationic surfactant. It is.
Specifically, there are montmorillonite groups of natural or synthetic (in this case, the (OH) group in the formula is substituted with fluorine) such as montmorillonite, saponite, hectorite (commercially available products include bee gum, kunipia, laponite). ) And synthetic mineral mica known as sodium silicic mica and sodium or lithium teniolite (commercially available products include Dimonite: Topy Industries, Ltd.). Quaternary ammonium salt type cationic surfactants Is obtained by processing.
The quaternary ammonium salt type cationic surfactant used here is represented by the following general formula (4).
Examples of the quaternary ammonium salt type cationic surfactant include dodecyltrimethylammonium chloride, myristyltrimethylammonium chloride, cetyltrimethylammonium chloride, stearyltrimethylammonium chloride, aralkyltrimethylammonium chloride, behenyltrimethylammonium chloride, myristyldimethylethylammonium. Chloride, cetyldimethylethylammonium chloride, stearyldimethylethylammonium chloride, aralkyldimethylethylammonium chloride, behenyldimethylethylammonium chloride, myristyldiethylmethylammonium chloride, cetyldiethylmethylammonium chloride, stearyldiethylmethylammonium chloride, arachi Diethylmethylammonium chloride, behenyldiethylmethylammonium chloride, benzyldimethylmyristylammonium chloride, benzyldimethylcetylammonium chloride, benzyldimethylstearylammonium chloride, benzyldimethylbehenylammonium chloride, benzylmethylethylcetylammonium chloride, benzylmethylethylstearylammonium chloride, di Examples include behenyl dihydroxyethylammonium chloride and the corresponding bromide, and further dipalmitylpropylethylammonium methyl sulfate. In carrying out the present invention, one or more of these are arbitrarily selected.
Representative examples of the organically modified clay mineral include dimethylalkylammonium hectorite, benzyldimethylstearylammonium hectorite, distearyldimethylammonium chloride-treated aluminum magnesium silicate, and the like. Benton 27 (benzyldimethylstearyl ammonium chloride-treated hectorite: National Red) and Benton 38 (distearyldimethylammonium chloride-treated hectorite: National Red) are preferable as commercial products.
本願発明の日焼け止め乳化化粧料には、オクチルメトキシシンナメート等の紫外線吸収剤を上記油分に溶解して配合することが好ましい。紫外線吸収剤の配合量は油分の配合量に応じて適宜決定されるが、好ましくは、日焼け止め乳化化粧料全量に対して１〜１０質量％である。
本発明の日焼け止め乳化化粧料は、化粧料に通常配合される成分を本発明の効果を損なわない範囲で適宜配合して、商品形態に応じて常法により製造される。
In the sunscreen emulsified cosmetic of the present invention, an ultraviolet absorber such as octyl methoxycinnamate is preferably dissolved in the oil. Although the compounding quantity of a ultraviolet absorber is suitably determined according to the compounding quantity of an oil component, Preferably it is 1-10 mass% with respect to the total amount of sunscreen emulsified cosmetics.
The sunscreen emulsified cosmetic of the present invention is produced by a conventional method according to the form of the product by appropriately blending the components usually blended into the cosmetic within a range not impairing the effects of the present invention.
本発明を実施例により具体的に説明する。本発明の技術範囲はこれら実施例によってなんら限定されるものではない。なお、配合量については特記しない限り、質量％で示す。 The present invention will be specifically described with reference to examples. The technical scope of the present invention is not limited by these examples. In addition, unless otherwise indicated about a compounding quantity, it shows with the mass%.
（ａ）疎水化処理酸化亜鉛粉末
「製造例１」
炭素数１２の一般式（１）のパーフルオロアルキルリン酸エステル（Rf：炭素数１０，ｎ＝２，１≦y≦２）を３００g、及び一般式（２）のエステル（アクリルシリコーン共重合体：信越化学工業社製KP-544：一般式（２）で示される、分子量が３０，０００〜３００，０００のアクリル酸２−エチルヘキシル、メタクリル酸、メタクリル酸メチル、メタクリル酸ブチルの共重合体とメチルポリシロキサンのメチル基の一部をヒドロキシプロピル基で置換したものとのエステル）１００g、ＩＰＡ（溶媒）を３．５ｋｇ用意した。これらを用い、上記一般式（１）のリン酸エステルの５０質量％溶液と上記一般式（２）のエステルの６０質量％溶液を調製した。
20Lの高速撹拌混合機に、ＷＯ９９／２５６５４号公報（特願平１１−５２５９８４号）記載の微粒子酸化亜鉛粉末（カーネーションの花びら状の外観を有するもの，比表面積（Ｘ）＝６０m2/g）５kgを入れ、上記一般式（１）のリン酸エステルの溶液と、上記一般式（２）のエステルの溶液入れた。さらに残りのＩＰＡを入れ、全溶媒量となるトータルのＩＰＡ量を３．５ｋｇとした。その後、６０℃で１時間撹拌した後、１２０℃に加温し高速撹拌混合機内を減圧にして約２時間保ち、溶媒であるＩＰＡを完全に除去した。
(A) Hydrophobized zinc oxide powder “Production Example 1”
300 g of perfluoroalkyl phosphate ester of general formula (1) having 12 carbon atoms (Rf:
Fine particle zinc oxide powder described in WO 99/25654 (Japanese Patent Application No. 11-525984) (with carnation petal-like appearance, specific surface area (X) = 60 m 2 / g) in a 20 L high-
次に、混合機内から払い出した後、２ｍｍスクリーンを備えたハンマーミルで粉砕し、４５１３０℃で２４ｈ加熱することにより、炭素数が１２のパーフルオロアルキルリン酸エステル６％と、アクリルシリコーン共重合体２％で表面被覆した微粒子酸化亜鉛を得た。 Next, after discharging from the inside of the mixer, the mixture was pulverized with a hammer mill equipped with a 2 mm screen and heated at 45130 ° C. for 24 hours to obtain 6% perfluoroalkyl phosphate ester having 12 carbon atoms and an acrylic silicone copolymer. Particulate zinc oxide surface-coated with 2% was obtained.
粉末の吸油量は、ＪＩＳＫ５１０１の方法に準じ、油分としてシリコーン油を用いて測定した結果、３０.８mL／１００gであった。粉末の見掛けの比容積は、ＪＩＳＫ５１０１ ２０.２記載のタップ法に準じて測定した結果、０.７１mL／gであった。粉末の接触角は、粉末を錠剤成型機等を用いてペレットを作製し、この上に流動パラフィンを滴下して形成される接触角を測定した結果、５２°であった。
製造例１の製造方法における溶媒の使用量は該酸化亜鉛粉末に対して７０質量％である。
また、一般式（１）のリン酸エステルと一般式（２）のエステルとの使用量の和は、８％であり、一般式（１）のリン酸エステル／一般式（２）のエステル＝３である。
The amount of oil absorption of the powder was 30.8 mL / 100 g as a result of measurement using silicone oil as the oil content according to the method of JISK5101. The apparent specific volume of the powder was 0.71 mL / g as a result of measurement according to the tap method described in JISK5101 20.2. The contact angle of the powder was 52 ° as a result of measuring the contact angle formed by preparing pellets of the powder using a tablet molding machine or the like and dropping liquid paraffin thereon.
The amount of the solvent used in the production method of Production Example 1 is 70% by mass with respect to the zinc oxide powder.
Moreover, the sum of the usage-amount of the phosphate ester of General formula (1) and the ester of General formula (2) is 8%, and the ester of General formula (1) / ester of General formula (2) = 3.
「製造例２〜１０、比較製造例１〜３」
製造例１と同様にして製造した。すなわち、後述の製造処方の「表１」に従い、微粒子酸化亜鉛粉末、炭素数１２の一般式（１）のパーフルオロアルキルリン酸エステル（Rf：炭素数１０，ｎ＝２，１≦y≦２）、及び一般式（２）のエステル（アクリルシリコーン共重合体：信越化学工業社製KP-544：一般式（２）で示される、分子量が３０，０００〜３００，０００のアクリル酸２−エチルヘキシル、メタクリル酸、メタクリル酸メチル、メタクリル酸ブチルの共重合体とメチルポリシロキサンのメチル基の一部をヒドロキシプロピル基で置換したものとのエステル）、及びＩＰＡ（溶媒）を用意した。
20Lの高速撹拌混合機に、微粒子酸化亜鉛粉末５kgを入れ、次に予めＩＰＡに溶解させた上記一般式（１）のリン酸エステルの５０質量％溶液と上記一般式（２）のエステルの６０質量％溶液を入れた。さらに全溶媒量となるトータルのＩＰＡ量を調整するためＩＰＡを加えた。その後、６０℃で１時間撹拌した後、１２０℃に加温し高速撹拌混合機内を減圧にして約２時間保ち、溶媒であるＩＰＡを完全に除去し、表面被覆微粒子酸化亜鉛を得た。
また、製造例１と同様にして、得られた粉末の吸油量、見掛けの比容積、流動パラフィンに対する接触角を測定した。
"Production Examples 2 to 10, Comparative Production Examples 1 to 3"
Manufactured in the same manner as in Production Example 1. That is, in accordance with “Table 1” of the production recipe described later, fine zinc oxide powder, perfluoroalkyl phosphate ester of general formula (1) having 12 carbon atoms (Rf:
Into a 20 L high-speed stirring mixer, 5 kg of fine zinc oxide powder was added, and then a 50 mass% solution of the phosphoric acid ester of the above general formula (1) and 60 of the ester of the above general formula (2) dissolved in IPA in advance. A mass% solution was added. Furthermore, IPA was added in order to adjust the total amount of IPA to be the total amount of solvent. Then, after stirring at 60 ° C. for 1 hour, the mixture was heated to 120 ° C. and the inside of the high-speed stirring mixer was reduced in pressure and maintained for about 2 hours to completely remove IPA as a solvent to obtain surface-coated fine particle zinc oxide.
In the same manner as in Production Example 1, the oil absorption, apparent specific volume, and contact angle with liquid paraffin of the obtained powder were measured.
製造例及び比較製造例を「表１」及び「表２」にまとめると次のようになる。
＊２）微粒子酸化亜鉛ＦＩＮＥＸ−５０（堺化学社製、比表面積（Ｘ）＝５０m2/g）
* 2) Fine zinc oxide FINEX-50 (manufactured by Sakai Chemical Co., Ltd., specific surface area (X) = 50 m 2 / g)
また、以上の表面処理条件を、粉末量に対する溶媒使用量と、一般式（１）のリン酸エステル／一般式（２）のエステルの比のパラメータに対する吸油量と見掛けの比容積の値をグラフに示すと、「図２」、「図３」及び「図４」のようになる。 Further, the above surface treatment conditions are graphs of the amount of oil absorption and the apparent specific volume with respect to the parameter of the amount of solvent used relative to the amount of powder and the ratio of phosphate ester of general formula (1) / ester of general formula (2). As shown in FIG. 2, “FIG. 2”, “FIG. 3” and “FIG. 4” are obtained.
これらの図から、粉末量に対する溶媒量をコントロールして見掛けの比容積と吸油量を適度に制御することにより、化粧料、特に油分に分散することを特徴とする化粧料に極めて配合（分散）し易くすることができる。また、処理剤の比率と量は、比容積と吸油量に影響することはもちろん、化粧持ち（撥水性・撥油性）向上に寄与する撥油性とも関連があることから、これらの条件を選択することにより、化粧料調製時の処方幅(特にフッ素化合物で被覆された粉末と既存原料との親和性向上)と化粧品としての機能を両立できる。したがって、本発明に用いる（ａ）疎水化処理酸化亜鉛粉末は、日焼け止め化粧料に極めて有用な疎水化処理粉末であることが分かる。 From these figures, by controlling the amount of solvent with respect to the amount of powder and appropriately controlling the apparent specific volume and oil absorption, it is extremely blended (dispersed) in cosmetics, especially in cosmetics characterized by being dispersed in oil. Can be made easier. In addition, the ratio and amount of the treatment agent not only affects the specific volume and the oil absorption amount, but also has a relation with the oil repellency that contributes to the improvement of makeup durability (water repellency / oil repellency). This makes it possible to satisfy both the prescription width at the time of cosmetic preparation (particularly, the improvement in the affinity between the powder coated with the fluorine compound and the existing raw material) and the function as a cosmetic. Therefore, it can be seen that the (a) hydrophobized zinc oxide powder used in the present invention is a hydrophobized powder that is extremely useful for sunscreen cosmetics.
次に、本発明の日焼け止め化粧料の実施例を説明する。表３および表４の処方の油中水型乳化化粧料を常法により製造し、その効果を下記により評価した。
＜洗浄容易性の評価＞
１０人の専門パネルに実際に使用してもらい、洗浄容易性（落ち易さ）について、以下の基準で判定した。
◎：８〜１０人が洗浄し易いと回答した。
○：５〜7人が洗浄し易いと回答した。
△：２〜４人が洗浄し易いと回答した。
×：０〜１人が洗浄し易いと回答した。
Next, examples of the sunscreen cosmetics of the present invention will be described. Water-in-oil emulsified cosmetics having the formulations shown in Tables 3 and 4 were produced by a conventional method, and the effects were evaluated as follows.
<Evaluation of easy cleaning>
Ten professional panels actually used it, and the ease of cleaning (easy to drop) was determined according to the following criteria.
A: 8 to 10 people answered that it was easy to clean.
○ : 5 to 7 people answered that it was easy to clean.
Δ: 2 to 4 people answered that it was easy to wash.
X: 0 to 1 person answered that it was easy to wash.
「表３及び表４の（ａ）疎水化処理酸化亜鉛粉末」
（ａ）疎水化処理酸化亜鉛粉末＊１：パーフルオロアルキルリン酸エステル処理酸化亜鉛粉末（商品名FSA-ZnO（SF）、大東化成工業株式会社）
（ａ）疎水化処理酸化亜鉛粉末＊２：シランカップリング剤−カチオン界面活性剤処理酸化亜鉛粉末
（ａ）疎水化処理酸化亜鉛粉末＊３：脂肪酸−デキストリン処理酸化亜鉛粉末（商品名WSX-MZ-700、テイカ株式会社）
（ａ）疎水化処理酸化亜鉛粉末＊４：金属石鹸処理酸化亜鉛粉末（商品名MT-Finex25、三好化成株式会社）
（ａ）疎水化処理酸化亜鉛粉末＊５：シリコーン処理酸化亜鉛粉末（商品名SS-ActivoxC80、昭和電工株式会社）
“(A) Hydrophobized zinc oxide powder in Table 3 and Table 4”
(A) Hydrophobized zinc oxide powder * 1: perfluoroalkyl phosphate-treated zinc oxide powder (trade name FSA-ZnO (SF), Daito Kasei Kogyo Co., Ltd.)
(A) Hydrophobized zinc oxide powder * 2: Silane coupling agent-cationic surfactant-treated zinc oxide powder (a) Hydrophobized zinc oxide powder * 3: Fatty acid-dextrin treated zinc oxide powder (trade name WSX-MZ -700, Teika Corporation)
(A) Hydrophobized zinc oxide powder * 4: Metal soap-treated zinc oxide powder (trade name MT-Finex25, Miyoshi Kasei Co., Ltd.)
(A) Hydrophobized zinc oxide powder * 5: Silicone-treated zinc oxide powder (trade name SS-ActivoxC80, Showa Denko KK)
（ａ）疎水化処理酸化亜鉛粉末と（ｂ）揮発性シリコーンとが配合された日焼け止め乳化化粧料に、（ｃ）流動パラフィンまたはイソノナン酸イソノニルと（ｄ）非イオン性界面活性剤とを組み合わせて配合すると洗浄容易性が高くなる。特にイソノナン酸イソノニルを配合した場合は顕著に高い洗浄容易性を示す。
（ｃ）流動パラフィン若しくは（ｃ）イソノナン酸イソノニル、又は、（ｄ）非イオン性界面活性剤の一方のみの配合では本願発明の効果は半減する。しかし、（ｃ）成分と、（ｄ）成分との洗浄容易性に対する寄与は、（ｃ）成分の方が大きい。
A sunscreen emulsified cosmetic containing (a) a hydrophobized zinc oxide powder and (b) a volatile silicone combined with (c) liquid paraffin or isononanoyl isononanoate and (d) a nonionic surfactant. When blended, the ease of cleaning increases. In particular, when isononyl isononanoate is blended, the removability is remarkably high.
When only one of (c) liquid paraffin, (c) isononyl isononanoate, or (d) a nonionic surfactant is blended, the effect of the present invention is halved. However, the contribution of the component (c) and the component (d) to the ease of cleaning is greater in the component (c).
以下にその他の本発明の実施例を挙げる。いずれも、化粧持ち（撥水性・撥油性）と、洗浄容易性に優れた日焼け止め化粧料である。なお、下記実施例においては、製造例１〜１０の任意の疎水化処理酸化亜鉛粉末を配合することが可能である。 Other examples of the present invention are listed below. Both of these are sunscreen cosmetics that have a long-lasting makeup (water and oil repellency) and are easy to clean. In addition, in the following Example, it is possible to mix | blend the arbitrary hydrophobized zinc oxide powder of manufacture examples 1-10.
実施例１１：Ｗ／Ｏ型乳化日焼け止めクリーム
ジメチルポリシロキサン 0.5
デカメチルシクロペンタシロキサン 28
ラウリリルメチコン 6
トリメチルシロキシケイ酸 0.5
ポリエーテル変性シリコーン 1
（信越化学社製ＫＦ−６０１７）
ジプロピレングリコール 5
トリイソステアリン酸PEG-20グリセリル 2
製造例２で得られた酸化亜鉛 18
イソノナン酸イソノニル(または流動パラフィン) 5
パラベン 適量
フェノキシエタノール 適量
エデト酸三ナトリウム 適量
パラメトキシ桂皮酸２−エチルヘキシル 7.5
ジメチルジステアリルアンモニウムヘクトライト 1
球状ＰＭＭＡ粉末 4
精製水 残余
香料 適量
Example 11: W / O type emulsion sunscreen cream dimethylpolysiloxane 0.5
Decamethylcyclopentasiloxane 28
Lauryl Methicone 6
Trimethylsiloxysilicate 0.5
Polyether modified
(Shin-Etsu Chemical KF-6017)
PEG-20 glyceryl triisostearate 2
Zinc oxide obtained in Production Example 2 18
Isononyl isononanoate (or liquid paraffin) 5
Paraben Appropriate amount Phenoxyethanol Appropriate amount Trisodium edetate Appropriate amount 2-methoxyhexyl paramethoxycinnamate 7.5
Dimethyl
Spherical PMMA powder 4
Purified water Residual fragrance
実施例１２：Ｗ／Ｏ型乳化日焼け止めクリーム
ヘキシリルメチコン 5
デカメチルシクロペンタシロキサン 25
メチルトリメチコン 5
１，３−ブチレングリコール 5
微粒子酸化チタン（テイカ社製MT−100TV） 5
セスキイソステアリン酸ソルビタン 2
製造例３で得られた酸化亜鉛 18
イソノナン酸イソノニル(または流動パラフィン) 5
パラベン 適量
フェノキシエタノール 適量
エデト酸三ナトリウム 適量
ジメチルジステアリルアンモニウムヘクトライト 1
球状ポリメチルシルセスキオキサン粉末 5
精製水 残余
香料 適量
Example 12: W / O type emulsifying sunscreen
Decamethylcyclopentasiloxane 25
1,3-
Fine particle titanium oxide (MT-100TV manufactured by Teika) 5
Sorbitan sesquiisostearate 2
Zinc oxide obtained in Production Example 3 18
Isononyl isononanoate (or liquid paraffin) 5
Paraben Appropriate amount Phenoxyethanol Appropriate amount Trisodium edetate Appropriate amount Dimethyl
Purified water Residual fragrance
実施例１３：二層型Ｗ／Ｏ日中用乳液
カプリリルメチコン 7
デカメチルシクロペンタシロキサン 15
デカメチルテトラシロキサン 13
分岐型ポリエーテル変性シリコーン 1.5
（信越化学社製ＫＦ−６０２８）
１，３−ブチレングリコール 5
スクワラン 0.5
タルク 1
グリチルリチン酸ジカリウム 0.1
酢酸トコフェロール 0.1
エデト酸三ナトリウム 0.05
パラメトキシ桂皮酸２−エチルヘキシル 5
ジイソステアリン酸ポリグリセリル 2
製造例３で得られた酸化亜鉛 18
イソノナン酸イソノニル(または流動パラフィン) 5
ジメチルジステアリルアンモニウムヘクトライト 0.5
球状ポリエチレン末 3
フェノキシエタノール 適量
エタノール 5
精製水 残余
香料 適量
Example 13: Two-layer W / O daytime
Decamethylcyclopentasiloxane 15
Decamethyltetrasiloxane 13
Branched polyether-modified silicone 1.5
(Shin-Etsu Chemical KF-6028)
1,3-
Squalane 0.5
Dipotassium glycyrrhizinate 0.1
Tocopherol acetate 0.1
Edetate trisodium 0.05
2-
Polyglyceryl diisostearate 2
Zinc oxide obtained in Production Example 3 18
Isononyl isononanoate (or liquid paraffin) 5
Dimethyl distearyl ammonium hectorite 0.5
Phenoxyethanol Appropriate amount of
Purified water Residual fragrance
本発明によれば、化粧持ち（撥水性・撥油性）と、洗浄容易性に優れた日焼け止め乳化化粧料を提供できる。 According to the present invention, it is possible to provide a sunscreen emulsified cosmetic that has a long lasting makeup (water and oil repellency) and is easy to clean.
Claims (3)