JP4593383B2 - 防食性複合体およびその製法 - Google Patents
防食性複合体およびその製法 Download PDFInfo
- Publication number
- JP4593383B2 JP4593383B2 JP2005183174A JP2005183174A JP4593383B2 JP 4593383 B2 JP4593383 B2 JP 4593383B2 JP 2005183174 A JP2005183174 A JP 2005183174A JP 2005183174 A JP2005183174 A JP 2005183174A JP 4593383 B2 JP4593383 B2 JP 4593383B2
- Authority
- JP
- Japan
- Prior art keywords
- parts
- pozzolanic
- reducing agent
- concrete
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
耐酸モルタルとして、ポルトランドセメントとともに、高炉スラグやフライアッシュ、シリカフュームなどを多量に混和したモルタルが提案されている(特許文献1)。
また、ひび割れを防止するために収縮低減剤が開発されている。収縮低減剤の使用方法としては、セメントに混和する方法やセメントコンクリートの硬化後塗布する方法が知られており、水硬性組成物、水、および収縮低減剤を混練したものを、硬化したコンクリート表面に施工し、その後、蒸発抑制被覆層を形成する方法も提案されている(非特許文献1、特許文献2)。さらに、コンクリート表面に散布や塗布し、コンクリート表面を被覆する、エチレン−酢ビ共重合エマルジョンを含有する養生用封緘剤も提案されている(特許文献3)。
ポルトランドセメントの粒度は、特に限定されるものではないが、通常、ブレーン比表面積で3000〜6000cm2/gの範囲にある。3000cm2/g未満では強度発現性が充分でない場合があり、6000cm2/gを超えると取り扱いが困難な場合がある。
高炉水砕スラグ微粉末の粉末度は、特に限定されるものではないが、通常、ブレーン比表面積で3000〜9000cm2/g程度の範囲にある。
ポゾラン物質は特に限定されるものではなく、その具体例としては、例えば、フライアッシュ、シリカフューム、パルプスラッジ焼却灰、下水汚泥焼却灰、廃ガラス粉末などが挙げられる。中でも、フライアッシュやシリカフュームの使用が好ましい。
フライアッシュおよびシリカフュームの粉末度は、特に限定されるものではないが、通常、フライアッシュについては、ブレーン比表面積で3000〜9000cm2/g程度の範囲にあり、シリカフュームについては、BET比表面積で2〜20m2/g程度の範囲にある。
セメント組成物における各材料の配合割合は、特に限定されるものではないが、通常、ポルトランドセメント、潜在水硬性物質、およびポゾラン物質の合計100部中、ポルトランドセメント20〜40部が好ましく、25〜35部がより好ましい。潜在水硬性物質は20〜40部が好ましく、25〜35部がより好ましい。ポゾラン物質は30〜50部が好ましく、35部〜45部がより好ましい。ポルトランドセメントが20部未満では、初期の強度発現性が乏しい場合があり、逆に、40部を超えると耐酸性が充分でない場合がある。潜在水硬性物質が20部未満であると、耐酸性が充分でない場合がり、逆に40部を超えると初期の強度発現性が悪くなり、寸法安定性が悪くなる場合がある。ポゾラン物質が30部未満であると耐酸性が十分でない場合があり、50部を超えると、初期の強度発現性が悪くなる場合がある。
具体的には、ポリプロピレングリコール、エチレンオキシドメタノール付加物エチレンオキシド・プロピレンオキシドブロック重合物、エチレンオキシド・プロピレンオキシドランダム重合物、グリコールのシクロアルキル基付加物、グリコールの両端にメチル基を付加した付加物、グリコールのフェニル基付加物、グリコールにメチルフェニル基を付加したブロック重合物、グリコールの両端にエチレンオキサイドメタノールを付加した付加物、およびグリコールにジメチルアミンを付加した付加物などが使用可能である。
収縮低減剤の水の希釈倍率は10倍以下が好ましく、10倍を超えるとひび割れ防止効果が得られない場合がある。
収縮低減剤のコーティング方法は、モルタルやコンクリート表面に均一に分散する方法であれば特に限定されるものではなく、撒布したり、塗布したり、吹付けたりすることが可能であり、施工面積により、噴霧器、噴霧機、およびじょうろなどを用いる方法がある。
本発明で言うポリマーとは、特に限定されるものではない。ポリマーは大別すると、水性ポリマーディスパージョン、水溶性ポリマー、液状ポリマー、再乳化型粉末樹脂の4種類となる。その具体例としては、例えば、水性ポリマーディスパージョンとしては、天然ゴムラテックス、合成ゴムラテックス、樹脂エマルジョン、混合ディスパージョンが分類される。この中には、スチレンブタジエンゴム、クロロプレンゴム、メタクリル酸メチルブタジエンゴム、アクリロニトリル・ブタジエンゴム、ポリアクリル酸エステル、エチレン酢酸ビニル、スチレンアクリル酸エステル、ポリプロピオン酸ビニル、ポリプロピレン、エポキシ樹脂、アスファルト、パラフィン、混合ラテックス、混合エマルジョンなどが挙げられる。水溶性ポリマーとしては、例えば、メチルセルロース、ヒドロキシプロピルメチルセルロース、ポリビニルアルコール、アクリル酸カルシウム、アクリル酸マグネシウムなどが挙げられる。液状ポリマーとしては、例えば、不飽和ポリエステル樹脂やエポキシ樹脂などが挙げられる。再乳化型粉末樹脂としては、例えば、スチレンブタジエンゴム、エチレン酢酸ビニル、酢酸ビニルビニルバーサテート、スチレンアクリル酸エステル、ポリアクリル酸エステルなどが挙げられる。
本発明で言う繊維質物質とは、特に限定されるものではないが、その具体例としては、例えば、ビニロン繊維、セルロース繊維、アクリル繊維などの有機系繊維、炭素繊維、スチールファイバー、ワラストナイト繊維、ガラス繊維などの無機系繊維などが挙げられる。本発明ではこれらのうちの1種または2種以上が使用可能である。
ポルトランドセメント:市販の普通ポルトランドセメント、ブレーン比表面積3000cm2/g
潜在水硬性物質:市販の高炉水砕スラグ微粉末、ブレーン比表面積4000cm2/g
ポゾラン物質A:市販のフライアッシュ、ブレーン比表面積4000cm2/g
ポゾラン物質B:市販のシリカフューム、BET比表面積15m2/g
ポゾラン物質C:市販のパルプスラッジ焼却灰、ブレーン比表面積4000cm2/g
ポゾラン物質D:市販の下水汚泥焼却灰、ブレーン比表面積9000cm2/g
ポゾラン物質E:市販の廃ガラス粉末、ブレーン比表面積4000cm2/g
ポゾラン物質F:ポゾラン物質A75部とポゾラン物質B25部の混合物、ブレーン比表面積9000cm2/g
収縮低減剤イ:低分子量エチレンオキサイドとプロピレンオキサイドの共重合物を成分とする市販品
乾燥収縮低減剤ロ:低級アルコールのアルキレン付加物を成分とする市販品
水:水道水
細骨材:JIS R 5201で使用する標準砂
ひび割れ抵抗性試験:50cm×50cmのコンクリート板にモルタルを10mmの厚さで塗りつけ、温度20℃、相対湿度40%の環境で1日間放置し、ひび割れの発生具合を観察した。◎はひび割れが全くなし。○はひび割れ幅0.05mm以下のひび割れが1本のみ発生。−はひび割れが1本であるがひび割れ幅が0.05mmを超えた場合、△はひび割れが2本発生。×はひび割れが3本以上発生。
耐酸性:7%濃度の硫酸溶液に供試体を3ヶ月間浸漬し、供試体の外観の変化や質量減少から耐酸性を評価した。×は外観の変化が著しく、かつ、質量変化率が±5%以上の場合、△は外観の変化が著しいか、あるいは、質量変化率が±5%以上のいずれか一方を満たす場合、○は外観の変化と質量変化ともに上記条件に該当しない場合とした。
腫れ・剥れの観察:上記耐酸性試験後において、目に見えて腫れが認められ、かつ、硬化体表面に剥れが発生した場合は×、腫れまたは剥れのいずれかが認められた場合は△、いずれも認められず健全な状態であった場合を○とした。
ポリマーα:市販のスチレンブタジエンゴム系
ポリマーβ:市販のポリアクリル酸エステル系
ポリマーγ:市販のエチレン酢酸ビニル系
ポリマーΔ:市販の酢酸ビニルビニルバーサテート系
付着試験:JIS A 1171に準じて、材齢28日の付着強度を測定した。
繊維質物質(1):市販のビニロン繊維、長さ6mm、径200μm
繊維質物質(2):市販のアクリル繊維、長さ6mm、径200μm
繊維質物質(3):市販のセルロース繊維、長さ200μm、径30μm
繊維質物質(4):市販のカーボン繊維、長さ6mm、径200μm
繊維質物質(5):市販のワラストナイト繊維、長さ600μm、径40μm
Claims (2)
- ポルトランドセメント、高炉水砕スラグ微粉末である潜在水硬性物質、およびフライアッシュ、シリカフュームのうちの少なくとも1種であるポゾラン物質からなるセメント組成物において、ポルトランドセメント、潜在水硬性物質、およびポゾラン物質の合計100部中、ポルトランドセメントが20〜40部、潜在水硬性物質が20〜40部、ポゾラン物質が30〜50部であるモルタルまたはコンクリートの表面に収縮低減剤を200〜500g/m 2 コーティングした防食性複合体。
- モルタルまたはコンクリートの硬化前の表面に収縮低減剤をコーティングすることを特徴とする請求項1に記載の防食性複合体の製法。