JP4556693B2 - Two-room disposable warmer packaging material and method for producing the same - Google Patents
Two-room disposable warmer packaging material and method for producing the same Download PDFInfo
- Publication number
- JP4556693B2 JP4556693B2 JP2005030174A JP2005030174A JP4556693B2 JP 4556693 B2 JP4556693 B2 JP 4556693B2 JP 2005030174 A JP2005030174 A JP 2005030174A JP 2005030174 A JP2005030174 A JP 2005030174A JP 4556693 B2 JP4556693 B2 JP 4556693B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- storage chamber
- packaging material
- chamber
- surface film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、二重に包装された従来の使い捨てカイロに対して、特に、一重包装とするため、発熱材を充填する部屋と発熱させる部屋とに分けた２室式の使い捨てカイロ包装材に関するものである。 The present invention relates to a two-room disposable body warmer packaging material divided into a room for heating material and a room for heat generation, in particular, in order to make a single-layer packaging, in contrast to the conventional disposable body warmer packaged twice. It is.
従来の使い捨てカイロは、紙や樹脂繊維或いは孔あき加工されたフィルム等で作成したカイロ包装袋に、炭、鉄粉、吸水性素材等の内容物を充填したカイロ本体と、それを外気から遮断して、発熱を防ぐための外袋との構成になっている。すなわち、内容物を充填したカイロ本体をバリア性を有する外袋にいれた二重包装形式で流通していることが知られている。 The conventional disposable body warmer is a body warmer made of paper, resin fiber, or perforated film, filled with contents such as charcoal, iron powder, water-absorbing material, etc., and shields it from the outside air. And it is the structure with the outer bag for preventing heat generation. That is, it is known that the body of the warmer filled with the contents is distributed in a double packaging form in an outer bag having a barrier property.
この二重に包装された使い捨てカイロの使用方法は、外袋からカイロ本体をとりだすことにより、空気中の酸素と内容物が反応して発熱するようになっている。また、発熱を促進させるためにカイロ本体を手で揉む等をすることにより、内容物がよく混合されて薄く形成された本体の袋の繊維間等を通じての外気により一段と早く発熱するものである。 In the method of using the double-packed disposable body warmer, the body body is taken out from the outer bag so that oxygen in the air reacts with the contents to generate heat. Further, by manually holding the body of the warmer in order to promote heat generation, the contents are mixed well and heat is generated more quickly by the outside air between the fibers of the main body bag formed thinly.
しかしながら、従来の使い捨てカイロは本体の発熱を防ぐためのバリア性を有する外袋が必要である。しかし使用時にはこの外袋が不必要となり、ゴミとなってしまう。さらに、内袋（カイロ本体）と外袋と二重に包まれていることも包装材コストを上げる原因になっていた。 However, the conventional disposable body warmer requires an outer bag having a barrier property to prevent heat generation of the main body. However, this outer bag becomes unnecessary and becomes garbage when used. Furthermore, the double wrapping of the inner bag (the body of the warmer) and the outer bag has also caused the packaging material cost to increase.
そこで本発明は、上記の問題点を解決するためになされたもので、使い捨てカイロの包装形態を二重包装から一重包装にしても内容物が発熱しない形態とし、特に、表裏の樹脂フィルムにより内容物を充填する収納部とその片側或いは両側端部に空収納部を設け、この空収納部の裏面フィルムには内容物が漏れない程度の大きさの多数の微細孔を設けた２室式の使い捨てカイロ包装材を提供するものである。 Therefore, the present invention has been made to solve the above-described problems, and even if the packaging form of the disposable body warmer is changed from double packaging to single packaging, the contents do not generate heat. A two-chamber type in which a storage portion for filling an object and an empty storage portion are provided at one or both ends thereof, and a back film of the empty storage portion is provided with a large number of fine holes of a size that does not leak contents. A disposable warmer packaging material is provided.
本発明の請求項１は、表面フィルムにトレイ形状又は袋形状の収納室が形成され、前記収納室に発熱体を充填した後、裏側を裏面フィルムで密封してなる使い捨てカイロ包装材であって、前記表面フィルムは、バリア性フィルムの内面に融点が７０℃から１６０℃のイージーピールシーラントが積層された積層フィルムであり、前記収納室が、前記発熱体を充填する中央収納室とその両側の空収納室に隔絶区分けされ、前記裏面フィルムは、バリア性フィルムに、前記イージーピールシーラントとシール可能、かつ、イージーピール可能なシーラントフィルムが積層された積層フィルムであり、前記裏面フィルムは、前記表面フィルムより一回り大きく、かつ前記表面フィルムの周囲に余白部が設けられ、前記中央収納室に前記発熱体を充填した後に、前記裏面フィルムの前記余白部を前記表面フィルムの周囲に強シールして前記空収納室底部と前記中央収納室底部を密封し、前記中央収納室と前記空収納室の間の隔絶部分を前記裏面フィルムに容易に剥離可能に弱シールして隔絶区分けした構成からなり、前記空収納室を覆う前記裏面フィルムの部分には多数の外気取り入れ用の通気孔が設けられていることを特徴とする２室式の使い捨てカイロ包装材である。 Claim 1 of the present invention is a disposable warmer packaging material in which a tray-shaped or bag-shaped storage chamber is formed on a surface film, the heating chamber is filled with a heating element , and the back side is sealed with a back film. the surface film is a laminated film easy peel sealant is laminated with a melting point on the inner surface of the barrier film 160 ° C. from 70 ° C., the storage chamber, the central storage chamber and on both sides of filling the heating element The back film is a laminated film in which a sealant film that can be sealed with an easy peel sealant and can be peeled easily is laminated on a barrier film. slightly larger than the film, and the margin portion is provided around the surface film, filled with the heating element to the central storage chamber After the, said margin and strong seal around the surface film to seal the central storage chamber bottom and the air storage chamber bottom, isolated portion between the air receiving chamber and the central storage chamber of the back film The back film has a structure in which the back film is easily peelably weakly sealed and separated from each other, and a portion of the back film covering the empty storage chamber is provided with a number of ventilation holes for taking in outside air. Is a two-room disposable warmer packaging material.
本発明の請求項２は、上記表面フィルムの前記イージーピールシーラントがポリエチレン系イージーピール材であることを特徴とする上記の２室式の使い捨てカイロ包装材である。 A second aspect of the present invention is the above-described two-chamber disposable warmer packaging material , wherein the easy peel sealant of the surface film is a polyethylene easy peel material .
本発明の請求項３は、上記の２室式の使い捨てカイロ包装材の製造方法であって、前記表面フィルムの前記中央収納室に前記発熱体を充填する工程と、前記表面フィルムの周囲を温度と圧力を高く設定した強シールにより密封する工程と、前記中央収納室と前記空収納室の間の前記隔絶部分を、温度と圧力を低く設定した弱シールにより隔絶区分けする工程を有することを特徴とする２室式の使い捨てカイロ包装材の製造方法である。 Claim 3 of the present invention is a method for producing the above-described two-chamber disposable warmer packaging material, the step of filling the central storage chamber of the surface film with the heating element, and the temperature around the surface film. And a step of sealing with a strong seal with a high pressure set, and a step of isolating the isolated portion between the central storage chamber and the empty storage chamber with a weak seal with a low temperature and pressure. It is a manufacturing method of the two-chamber type disposable body packaging material .
本発明の請求項４は、上記の２室式の使い捨てカイロ包装材の製造方法であって、前記表面フィルムの前記中央収納室に前記発熱体を充填する工程と、前記表面フィルムの周囲
の強シール部はシールバーを高くして、前記中央収納室と前記空収納室の間の前記隔絶部分はシールバーを低く設定して弱シールする構成で同時シールする工程を有することを特徴とする２室式の使い捨てカイロ包装材の製造方法である。
Claim 4 of the present invention is a method for producing the above-described two-chamber disposable warmer packaging material, comprising the step of filling the central storage chamber of the surface film with the heating element, and the periphery of the surface film
The strong seal portion has a step of simultaneously sealing with a configuration in which the seal bar is raised and the isolated portion between the central storage chamber and the empty storage chamber is set to be low and the seal bar is weakly sealed. It is a manufacturing method of the two-chamber type disposable warmer packaging material .
本発明における２室式の使い捨てカイロ包装材は、表裏のフィルムにより発熱体等の内容物が包まれており、かつ裏面フィルムの一部に内容物が出ない（漏れない）程度の多数の通気孔が設けられており、この通気孔部分は内容物充填部分とイージーピール材シール部分で隔絶されており、使用時にその弱シール部分（隔絶部分）を剥がして発熱体である内容物の一部を移動させて、空収納室裏面の通気孔より外気を取り入れ発熱させる構造となっている。すなわち、外気中の酸素等を取り入れ内容物を発熱させると共に、熱がカイロ全体に放出される特徴を有するものである。さらに、従来における内袋と外袋との二重包装が改善され包装材のコストダウンになる等の優れた効果を奏する。 In the two-room type disposable warmer packaging material of the present invention, the contents such as the heating element are wrapped by the front and back films, and the contents are not exposed to a part of the back film (does not leak). There are air holes, and this air vent part is isolated by the contents filling part and the easy peel material seal part, and during use, the weak seal part (isolation part) is peeled off and a part of the content that is a heating element Is moved to generate heat by taking in outside air from the vents on the back of the empty storage chamber. That is, it has the characteristics that it takes in oxygen or the like in the outside air to heat the contents and releases the heat to the whole body. Furthermore, the conventional double wrapping of the inner bag and the outer bag is improved, and excellent effects such as a reduction in the cost of the packaging material are exhibited.
図に基づき実施するための最良の形態を詳細に説明する。 The best mode for carrying out the invention will be described in detail with reference to the drawings.
図１は、本発明の一実施例を示す２室式の使い捨てカイロ包装材の断面説明図である。図２は、本発明における２室式の使い捨てカイロ包装材を示すもので、（Ａ）は上面から見た平面図であり、（Ｂ）は、裏面側から見た平面図である。また、図３は、本発明の一実施例を示す２室式の使い捨てカイロ包装材における隔絶部分（弱シール部分）を剥がし、内容物を一部移動させ発熱させる状態を示す断面説明図である。 FIG. 1 is a cross-sectional explanatory view of a two-chamber disposable warmer packaging material showing an embodiment of the present invention. 2A and 2B show a two-chamber disposable warmer packaging material according to the present invention, in which FIG. 2A is a plan view seen from the top surface, and FIG. 2B is a plan view seen from the back surface side. FIG. 3 is an explanatory cross-sectional view showing a state in which the isolated portion (weakly sealed portion) in the two-chamber disposable warmer packaging material showing an embodiment of the present invention is peeled off and the contents are partially moved to generate heat. .
図１に示すように、本発明における２室式の使い捨てカイロ包装材の構成は、適宜トレイ形状や袋形状等に形成された表面フィルムに炭、鉄粉、吸水性素材等の発熱体である内容物を充填した後、裏側を裏面フィルムで密封した２室式の使い捨てカイロ包装材であって、前記トレイ形状等の表面フィルム（１１）を複数の収納室に隔絶区分けし、このいずれか一つの収納室（１１ａ）に内容物（３０）を充填し、この片側或いは両側に区分けされた空収納室（１１ａ，１１ａ）を設けたものである。また、裏面フィルム（１４）は、表面フィルム（１１）及び空収納室（１１ａ，１１ａ）より一回り大きく、かつ表面フィルムの周囲に余白部（１４ａ，１４ａ）を設けた構成である。次に、このいずれか一つの表面フィルム（１１）による収納室（１１ａ）に内容物（３０）を充填した後、裏面フィルムで収納室底部や空収納室を密封して、しかも前記空収納室（１１ａ，１１ａ）部分の表面フィルム（１１）、裏面フィルム（１４）或いはこの両面には多数の外気取り入れ用の通気孔（１５）が設けられていることを特徴とするものである。 As shown in FIG. 1, the configuration of the two-chamber disposable warmer packaging material in the present invention is a heating element such as charcoal, iron powder, and a water-absorbing material on a surface film appropriately formed in a tray shape, a bag shape, or the like. After filling the contents, a two-room disposable warmer wrapping material whose back side is sealed with a back film, wherein the tray-shaped surface film (11) is separated into a plurality of storage chambers, The two storage chambers (11a) are filled with the contents (30), and the empty storage chambers (11a, 11a) divided on one side or both sides are provided. The back film (14) is larger than the front film (11) and the empty storage chambers (11a, 11a), and is provided with blank portions (14a, 14a) around the front film. Next, after the storage chamber (11a) of any one of the surface films (11) is filled with the contents (30), the bottom of the storage chamber or the empty storage chamber is sealed with the back film, and the empty storage chamber The surface film (11), the back film (14) or both surfaces of the (11a, 11a) portion are provided with a large number of vent holes (15) for taking in outside air.
また、図２（Ａ）に示すように、前記表面フィルム（１１）の片側或いは両側に設けた空収納室（１１ａ，１１ａ）は、裏面フィルム（１４）と容易に剥離可能な二箇所の弱シール部分（１２，１２）により隔絶区分けされているもので、これにより表面フィルムを複数の収納室、空収納室に区分けしたものである。 Further, as shown in FIG. 2A, the empty storage chambers (11a, 11a) provided on one side or both sides of the surface film (11) have two weak spots that can be easily peeled off from the back film (14). These are separated from each other by the seal portions (12, 12), whereby the surface film is divided into a plurality of storage chambers and empty storage chambers.
また、前記裏面フィルム（１４）は、表面フィルム（１１）による収納室（１１ａ）及
び空収納室（１１ａ，１１ａ）より一回り大きく、かつ表面フィルムの周囲に余白部（１４ａ，１４ａ）を設けた構成である。この余白部（１４ａ，１４ａ）に、前記表面フィルム（１１）の周囲を強シールにより密封したものである。さらに、図２（Ｂ）に示すように、裏面フィルムで収納室底部や空収納室底部を密封して、しかも前記空収納室（１１ａ，１１ａ）部分の裏面フィルム（１４）には多数の外気取り入れ用の通気孔（１５）が設けられている。
Further, the back film (14) is slightly larger than the storage chamber (11a) and the empty storage chamber (11a, 11a) of the front film (11), and a blank portion (14a, 14a) is provided around the front film. It is a configuration. The margins (14a, 14a) are sealed around the surface film (11) with a strong seal. Further, as shown in FIG. 2B, the bottom of the storage chamber or the bottom of the empty storage chamber is sealed with a back film, and a large amount of outside air is applied to the back film (14) in the empty storage chamber (11a, 11a). An intake vent (15) is provided.
次に、本発明の２室式の使い捨てカイロ包装材の使用時は、図３に示すように、複数室に隔絶された表面フィルムと裏面フィルムとによる弱シール部分（１２，１２）を剥離して収納室、空収納室を一体にして、この何れか一つの収納室（１１ａ）に充填した内容物（３０）の一部を空収納室（１１ａ，１１ａ）内に移動させる（振り分ける）ことにより、元の空収納室底部の裏面フィルムの多数の外気取り入れ用の通気孔（１５）から外気が入り内容物全体が発熱するものである。さらに裏面フィルムだけでなく、空収納室の表面フィルム、裏面フィルム或いはこの両面に通気孔を設けることも可能である。 Next, when the two-chamber disposable warmer packaging material of the present invention is used, as shown in FIG. 3, the weakly sealed portions (12, 12) formed by the surface film and the back film separated from each other are peeled off. The storage chamber and the empty storage chamber are integrated, and a part of the contents (30) filled in any one of the storage chambers (11a) is moved (sorted) into the empty storage chambers (11a, 11a). As a result, outside air enters through the large number of outside air intake holes (15) in the back film at the bottom of the original empty storage chamber, and the entire contents generate heat. Furthermore, not only the back film, but also air holes can be provided on the surface film, the back film, or both surfaces of the empty storage chamber.
本発明に使用する表面フィルム（１１）の詳細は、バリア性フィルムを基本として、内面にイージーピールシーラントを貼ったものが良い。シーラントとしてはカイロの発熱温度考慮して、発熱温度よりも融点の高いものが望ましいが、ある程度低温シール性が無いと充填機スピードに制約がでるので、融点が７０℃から１６０℃程度のものが望ましい。材料としては、ポリエチレン系イージーピールフィルム、ポリプロピレン系イージーピールフィルム等を用いて、シール圧力やシール温度で開封強度をコントロールできるタイプのものが望ましい。また、バリアフィルムとしては、アルミ箔、透明蒸着フィルム、ポリ塩化ビニリデンコートフィルムを使用することができる。また、シーラント層の外側に内容物（中身）が見えないように、印刷等による隠蔽層やアルミ蒸着フィルムを用いることでも構わない。 As for the details of the surface film (11) used in the present invention, it is preferable that an easy peel sealant is pasted on the inner surface based on a barrier film. In consideration of the heat generation temperature of the warmer, a sealant having a melting point higher than the heat generation temperature is desirable. desirable. The material is preferably of a type in which the opening strength can be controlled by the sealing pressure or the sealing temperature using a polyethylene-based easy peel film, a polypropylene-based easy peel film, or the like. Moreover, an aluminum foil, a transparent vapor deposition film, and a polyvinylidene chloride coating film can be used as a barrier film. Further, a concealing layer by printing or the like or an aluminum vapor deposition film may be used so that the contents (contents) cannot be seen outside the sealant layer.
次に、裏面フィルム（１４）は、基本的に表面フィルムと同様の構成であるが表面フィルムと異なる点は、
・発熱開始時に空気中の酸素を取り入れるための通気孔（１５）を一部に設けておく
ことが必要である。
Next, the back film (14) is basically the same structure as the surface film, but the difference from the surface film is that
-It is necessary to provide a part of the ventilation hole (15) for taking in oxygen in the air at the start of heat generation.
また、表面フィルムのイージーピールフィルムとシール可能、かつイージーピール可能なフィルムであれば通常のシーラントフィルムでも構わない。但し、表裏の両方のフィルムをイージーピールフィルムにする必要はない。 Moreover, a normal sealant film may be used as long as it can be sealed with an easy peel film as a surface film and can be easily peeled. However, it is not necessary for both the front and back films to be easy peel films.
さらに、発熱体（内容物）充填時の「強シール部」と「容易に剥離させる弱シール部」の強度コントロールの方法としては、
・強シール部シール時は温度と圧力を高く設定し、弱シール部シール時は温度と圧力
を低く設定して、それぞれ別々にシールする（２回シール）。
Furthermore, as a method of strength control of "strong seal part" and "weak seal part that can be easily peeled off" when heating element (contents) is filled,
・ Set the temperature and pressure high when sealing a strong seal, and set the temperature and pressure low when sealing a weak seal, and seal each separately (twice sealing).
・強シール部はシールバーを高くして、弱シール部を低く設定したシールバーを用い
て、同時シールをする。
・ Use a seal bar with a high seal bar for the strong seal and a low seal for the weak seal.
等が考えられるが、上記方法を組み合わせたり、他の方法で実施しても良い。さらに、弱シール部のみに、イージーピールフィルムのリボンを挟み込んでシールし、使用時に剥離できるようにしておく方法も可能である。 However, the above methods may be combined or implemented by other methods. Furthermore, it is possible to use a method in which an easy peel film ribbon is sandwiched and sealed only in the weak seal portion so that it can be peeled off during use.
なお、空気中の酸素を取り入れるための通気孔の孔空け加工は発熱体である炭、鉄粉、吸水性素材等の内容物より小さい孔を、微小な針り等で物理的に空けたり、放電やレーザー等で焼き空けたりする方法を使用することができる。 In addition, the hole drilling process for taking in oxygen in the air is to make a hole smaller than the contents of charcoal, iron powder, water absorbent material etc. as a heating element physically with a fine needle or the like, A method of baking with a discharge or a laser can be used.
以下に具体的な実施例を詳細に説明する。 Specific examples will be described in detail below.
（実施例１）
表面フィルムとして、厚み２０μｍ塩化ビニリデンコートナイロン（ＫＮｙ）と厚み２０μｍの蒸着リニア低密度ポリエチレン（ＶＭＬＬＤＰＥ）をドライラミネートし、蒸着リニア低密度ポリエチレンのポリエチレン（ＰＥ）面にＰＥ系イージーピール材（ジェイフィルム社製「ＰＹ２０００」を１５μｍＳＰＥ加工した。次に、裏面フィルムとしては、表面フィルムと同一の構成で作成し、全面でなく一部に内容物が漏れない程度のピンホール（通気孔）を設けて裏面フィルムとした。
Example 1
As a surface film, dry laminate of 20 μm thick vinylidene chloride coated nylon (KNy) and 20 μm thick vapor-deposited linear low density polyethylene (VMLLDPE), and PE-based easy peel material (J film) on the polyethylene (PE) surface of the vapor-deposited linear low density polyethylene. “PY2000” made by the company was processed with 15 μm SPE, and then the back film was made with the same structure as the front film, and a pinhole (vent hole) was provided to the extent that the contents did not leak but not the entire surface. It was set as the back film.
この表面フィルムと裏面フィルムを用いて、「炭、鉄粉、吸水性材料」等のカイロ内容物（発熱体）を裏面フィルムの通気孔の空いていない部分の表面フィルム内に充填して四隅を裏面フィルムの余白部に強くシールし、後で剥離する弱シール部は弱くシールする（サイズ：５０×８０ｍｍ角）。このシールのコントロールの仕方としては、２回シールで行った。 Using this surface film and the back film, fill the inside of the surface film of the back film with no air holes with the contents of the body (heating elements) such as “charcoal, iron powder, water-absorbing material”. It seals strongly in the blank part of a back film, and the weak seal part peeled off later seals weakly (size: 50x80 mm square). As a method of controlling this seal, sealing was performed twice.
（実施例２）
表面フィルムとして、厚み２０μｍ塩化ビニリデンコートナイロン（ＫＮｙ）と厚み２０μｍの蒸着リニア低密度ポリエチレン（ＶＭＬＬＤＰＥ）をドライラミネートし、蒸着リニア低密度ポリエチレンのポリエチレン（ＰＥ）面にＰＥ系イージーピール材（ジェイフィルム社製「ＰＹ２０００」を１５μｍＳＰＥ加工した。次に、裏面フィルムとして、厚み２０μｍ塩化ビニリデンコートナイロン（ＫＮｙ）と厚み２０μｍの蒸着リニア低密度ポリエチレン（ＶＭＬＬＤＰＥ）をドライラミネートし、蒸着リニア低密度ポリエチレンのポリエチレン（ＰＥ）面にリニア低密度ポリエチレン（ＬＬＤＰＥ）を３０μｍエキストルーダー加工を施した。さらに、全面ではなく一部に内容物が零れない程度のピンホール（通気孔）を空けて裏面フィルムとする。
(Example 2)
As a surface film, dry laminate of 20 μm thick vinylidene chloride coated nylon (KNy) and 20 μm thick vapor-deposited linear low density polyethylene (VMLLDPE), and PE-based easy peel material (J film) on the polyethylene (PE) surface of the vapor-deposited linear low density polyethylene. “PY2000” manufactured by the company was processed by 15 μm SPE, and then the back film was dry laminated with 20 μm thick vinylidene chloride coated nylon (KNy) and 20 μm thick evaporated linear low density polyethylene (VMLDDPE), and the evaporated linear low density polyethylene polyethylene The (PE) surface was treated with a linear low-density polyethylene (LLDPE) 30 μm extruder, and the back surface was filled with a pinhole (vent hole) that would not spill the contents on the entire surface. To.
この表面フィルムと裏面フィルムを用いて、「炭、鉄粉、吸水性材料」等のカイロ内容物（発熱体）を裏面フィルムの通気孔の空いていない部分の表面フィルム内に充填して四隅を裏面フィルムの余白部に強くシールし、後で剥離する弱シール部は弱くシールする（サイズ：５０×８０ｍｍ角）。このシールのコントロールの仕方としては、２回シールで行った。 Using this surface film and the back film, fill the inside of the surface film of the back film with no air holes with the contents of the body (heating elements) such as “charcoal, iron powder, water-absorbing material”. It seals strongly in the blank part of a back film, and the weak seal part peeled off later seals weakly (size: 50x80 mm square). As a method of controlling this seal, sealing was performed twice.
（実施例３）
内袋用の表面フィルムとして、厚み１５μｍのナイロン（Ｎｙ）と厚み２０μｍの蒸着リニア低密度ポリエチレン（ＶＭＬＬＤＰＥ）をドライラミネートし、蒸着リニア低密度ポリエチレンのポリエチレン（ＰＥ）面にリニア低密度ポリエチレン（ＬＬＤＰＥ）を３０μｍエキストルーダーラミを施した。また、内袋用の裏面フィルムとして、上記内袋用の表面フィルムと同一構成品のものに、実施例１と同様に内容物が零れない程度のピンホールを空けて裏面フィルムとする。さらに、剥離用リボンとして、内面のポリエチレン（ＰＥ）に対して剥離可能な厚み３０μｍのＰＥ系イージーピール材（ジェイフィルム社製「ＰＹ２０００」を５ｍｍ幅にスリットしておく。製袋する際は弱シール部分にする位置に、前記剥離用リボンを挟み込んで製袋する。その際、内容物は実施例１と同様に通気孔の内部分に充填する。
(Example 3)
As a surface film for the inner bag, nylon (Ny) with a thickness of 15 μm and vapor-deposited linear low density polyethylene (VMLLDPE) with a thickness of 20 μm are dry laminated, and the linear low density polyethylene (LLDPE) is deposited on the polyethylene (PE) surface of the vapor-deposited linear low density polyethylene. ) Was subjected to 30 μm extruder lami. Further, as the back film for the inner bag, a pin film having the same configuration as the above-described surface film for the inner bag is provided with a pinhole that does not spill the contents in the same manner as in Example 1 to obtain a back film. Furthermore, as a peeling ribbon, a 30 μm thick PE-based easy peel material (“PY2000” manufactured by J-Film Co., Ltd.) is slit to a width of 5 mm, which is weak when making bags. The peeling ribbon is sandwiched at a position where the sealing portion is to be formed, and the contents are filled in the inner portion of the vent hole in the same manner as in Example 1.
（比較例１）
比較例１として従来と同様のカイロ袋を製造して比較品とした。先ず、内袋用の表面フィルムとして、厚み１５μｍのナイロン（Ｎｙ）と厚み２０μｍの蒸着リニア低密度ポリ
エチレン（ＶＭＬＬＤＰＥ）をドライラミネートし、蒸着リニア低密度ポリエチレンのポリエチレン（ＰＥ）面にリニア低密度ポリエチレン（ＬＬＤＰＥ）を３０μｍエキストルーダーラミを施した。また、内袋用の裏面フィルムとして、上記内袋用の表面フィルムと同一構成品のものに、実施例１と同様に内容物が零れない程度のピンホールを空けて裏面フィルムとする。この表面フィルムと裏面フィルムを用いて、「炭、鉄粉、吸水性材料」等のカイロ内容物を充填して四隅をシールした（サイズ：５０×８０ｍｍ角）。さらに、この外袋として構成が、塩化ビニリデンコート延伸ポリプロピレン（ＫＯＰ）／「ＶＡ含有量１０％のエチレン酢酸ビニル共重合体（ＥＶＡ）」３０μｍのもので外袋を作成し、さらに包装する。
(Comparative Example 1)
As Comparative Example 1, a warmer bag similar to the conventional one was manufactured and used as a comparative product. First, as a surface film for the inner bag, nylon (Ny) having a thickness of 15 μm and vapor-deposited linear low density polyethylene (VMLLDPE) having a thickness of 20 μm are dry-laminated, and the linear low-density polyethylene is deposited on the polyethylene (PE) surface of the vapor-deposited linear low-density polyethylene. (LLDPE) was subjected to 30 μm extruder lami. Further, as the back film for the inner bag, a pin film having the same configuration as the above-described surface film for the inner bag is provided with a pinhole that does not spill the contents in the same manner as in Example 1 to obtain a back film. Using this surface film and the back film, the contents of the body such as “charcoal, iron powder, water-absorbing material” were filled and the four corners were sealed (size: 50 × 80 mm square). Further, the outer bag is made of vinylidene chloride coated polypropylene (KOP) / “ethylene vinyl acetate copolymer (EVA) with 10% VA content” 30 μm, and further packaged.
以上の実施例１から実施例３及び比較例１の製品の比較評価を行った。この結果は表１に示す。 The comparative evaluation of the products of Examples 1 to 3 and Comparative Example 1 was performed. The results are shown in Table 1.
本発明のカイロ包装材は二重包装になっている使い捨てカイロの全てに使用することが可能である。また、冷却及び温める湿布材等の包装材に利用することが可能である。 The warmer packaging material of the present invention can be used for all disposable warmers that are double-wrapped. Further, it can be used for packaging materials such as a poultice material for cooling and heating.
１０……２室式の使い捨てカイロ
１１……中央部の表面フィルム
１１ａ……空収納室
１２……弱シール部
１４……裏面フィルム
１４ａ…裏面フィルムの 余白部
１５……通気孔
３０……発熱体等の内容物
10 …… Two-room type disposable warmer 11 ……
Claims (4)