JP2004099053A

JP2004099053A - Inner sealant for hermetically sealing container mouth

Info

Publication number: JP2004099053A
Application number: JP2002259749A
Authority: JP
Inventors: Arata Yamada; 山田　新; Taketaka Hamada; 浜田　剛孝
Original assignee: Dai Nippon Printing Co Ltd
Current assignee: Dai Nippon Printing Co Ltd
Priority date: 2002-09-05
Filing date: 2002-09-05
Publication date: 2004-04-02

Abstract

<P>PROBLEM TO BE SOLVED: To provide an inner sealant for hermetically sealing a container mouth wherein heat generated from an aluminum foil by irradiation of high frequency is easily conductive to a heat-bonding resin layer and the sealant is excellent in highfrequency sealability. <P>SOLUTION: The inner sealant for hermetically sealing the container mouth consists of a re-sealable layer including a paper board layer and a polyolefin layer; and a sealable layer including a release layer, a glassine layer, an aluminum foil layer and the heat-bonding resin layer. These layers are laminated peelably at an interface between the polyolefin layer of the re-sealable layer and the release layer of the sealable layer. <P>COPYRIGHT: (C)2004,JPO

Description

【０００１】
【発明の属する技術分野】
本発明は、インナーシール材を装填したキャップを容器口部に取り付けた後に、高周波の照射により容器口部に接着させる容器口部密封用インナーシール材に関する。
【０００２】
【従来の技術】
従来、コーヒー等の吸湿性の高い内容物を収納した容器口部を密封するための容器口部密封用インナーシール材において、アルミニウム箔層を有するシール層の最下層に熱接着性樹脂層を積層し、高周波を照射してアルミニウム箔層を発熱させ熱接着性樹脂層を溶融させて容器口部に接着させる構成のものとしては、例えば、特許第３０５３６０２号公報に記載されているような、キャップの内側に残されるリシール層と、剥離層とアルミニウム箔とポリエチレン層とグラシン紙とホットメルト接着剤層からなるシール層を剥離可能に積層した構成の容器口部密封用インナーシール材が知られている。
【０００３】
しかしながら、上記の容器口部密封用インナーシール材は、高周波の照射によりアルミニウム箔を発熱させ、その熱によりホットメルト接着剤層を溶融させて容器口部に接着させるものであるが、シール層の構成が剥離層とアルミニウム箔とポリエチレン層とグラシン紙とホットメルト接着剤層からなり、アルミニウム箔とホットメルト接着剤層の間にポリエチレン層とグラシン紙が積層されているため、高周波の照射によりアルミニウム箔の発生する熱がポリエチレン層とグラシン紙を通してホットメルト接着剤層に伝わりホットメルト接着剤層を溶融させることになり、アルミニウム箔の発生する熱のホットメルト接着剤層への伝導性がよくないため高周波シールの効率が悪くなるという欠点がある。また、アルミニウム箔とグラシン紙を積層するために使用されているポリエチレン層が、アルミニウム箔から発生する熱により溶融してアルミニウム箔とグラシン紙が剥離するおそれがあるという欠点を有している。
【０００４】
【発明が解決しようとする課題】
本発明の目的は、高周波の照射によりアルミニウム箔から発生する熱が熱接着性樹脂層に伝導しやすく高周波シール性に優れた容器口部密封用インナーシール材を提供することである。
【０００５】
【課題を解決するための手段】
板紙層とポリオレフィン層を有するリシール層と、離型層とグラシン紙層と接着層とアルミニウム箔層と熱接着性樹脂層からなるシール層が、ポリオレフィン層と離型層の界面で剥離可能に積層された構成とすることにより、この容器口部密封用インナーシール材を装填したキャップを容器口部に取り付けキャップの外から高周波を照射して熱接着性樹脂層を溶融させて容器口部に接着する際の高周波シール性に優れたインナーシール材とすることができる。
【０００６】
上記の容器口部密封用インナーシール材において、リシール層が板紙層とポリオレフィン層間に発泡体層が積層された構成とすることにより、嵌合方式のキャップを使用した場合においても、リシール層のクッション性がよいので、容器からキャップを外し容器口部に接着されたシール層を剥がし取って開封した後に、キャップ内に残ったリシール層にて容器口部を確実に密封できる。
【０００７】
板紙層と接着層とプラスチックフィルムと離型層からなるリシール層と、ポリオレフィン層とグラシン紙層と接着層とアルミニウム箔層と熱接着性樹脂層からなるシール層が、ポリオレフィン層と離型層の界面で剥離可能に積層された構成とすることにより、高周波シール性が優れるとともに、容器口部に接着されたシール層を剥がし取って開封した後に、キャップに残ったリシール層により容器口部を密封した際に、リシール層の防湿性が優れるので容器に収納されたインスタントコーヒー等の内容物の吸湿を防止することができる。
【０００８】
上記の容器口部密封用インナーシール材において、離型層面に部分接着剤層が形成されている構成とすることにより、離型層面及び部分接着剤層面とポリオレフィン層面間の接着強度、即ちリシール層とシール層の接着強度を調整するのが容易となるので、容器口部密封用インナーシール材をキャップに装填して容器口部に取り付けるまではリシール層とシール層が剥離してしまうことがなく、且つ容器からキャップを外す際に、弱い力でリシール層とシール層を分離させることが可能となる。
【０００９】
【発明の実施の形態】
以下、図面を引用して本発明の実施の形態を説明する。
図１は本発明の第１実施形態の積層構成を示す断面図、図２は第１実施形態の容器口部密封用インナーシール材を装填したキャップを容器口部に取り付け高周波の照射により容器口部に接着した後キャップを外してリシール層とシール層に分離した状態を示す部分断面図、図３は本発明の第２実施形態の積層構成を示す断面図、図４は本発明の第３実施形態の積層構成を示す断面図、図５は第１実施形態のリシール層とシール層に分離した状態を示す図２に対応する部分断面図であり、１，１’　，１”はリシール層、２，２’はシール層、３は容器口部、４はキャップ、５は熱接着部、１１は板紙、１２は接着層、１３，　２６はポリオレフィン層、１４は発泡体層、１５はプラスチックフィルム層、１６，　２１は離型層、２２はグラシン紙層、２３は接着層、２４はアルミニウム箔層、２５は熱接着性樹脂層、２７は部分接着剤層を表す。
【００１０】
本発明の第１実施形態の積層構成は図１に示すとおりであり、リシール層１とシール層２に分離した状態は図２に示すとおりである。第１実施形態の積層構成は、外面から順に板紙層１１と接着層１２とポリオレフィン層１３が積層されたリシール層１と、部分接着剤層２７と離型層２１とグラシン紙層２２と接着層２３とアルミニウム箔層２４と熱接着性樹脂層２５が積層されたシール層２が、リシール層１のポリオレフィン層１３とシール層２の部分接着剤層２７及び離型層２１の界面で剥離可能に接着された構成である。絵柄層はグラシン紙層２２の内面側ないしは外面側にグラビア印刷等により形成することができる。なお、離型層２１面に形成する部分接着剤層２７はリシール層１とシール層２の接着強度を調整しやすくするためのものであるが、部分接着剤層２７を形成しない構成とすることもできる。
【００１１】
第１実施形態の容器口部密封用インナーシール材をキャップ４内に熱接着性樹脂層２５が外面となるように嵌め込んで装填し、容器口部密封用インナーシール材を装填したキャップ４を内容物を充填した容器口部３に取り付け、キャップ４の上部から高周波を照射することにより、アルミニウム箔層２４が発熱しその熱により熱接着性樹脂層２５が溶融するので、容器口部密封用インナーシール材を容器口部３に接着させて密封することができる。第１実施形態では、アルミニウム箔層２４面に熱接着性樹脂層２５が積層されており、高周波の照射によりアルミニウム箔層２４の発生する熱が熱接着性樹脂層２５へ伝導しやすいので高周波シール性をよくすることができる。
【００１２】
第１実施形態の容器口部密封用インナーシール材を使用して容器口部３を密封した状態からキャップ４を外すことにより、図２に示すように、容器口部密封用インナーシール材はポリオレフィン層１３と離型層２１及び部分接着剤層２７の界面で剥離してリシール層１とシール層２に分離し、リシール層１はキャップ４の内部に装填されたままの状態で残り、シール層２は接着部５にて熱接着性樹脂層２５面が容器口部３に接着して容器口部３を密封した状態となる。容器口部３に接着されたシール層２は、指で突き破って容器口部３から剥がし取ることにより簡単に開封することができる。
【００１３】
本発明の第２実施形態の積層構成は、図３に示すとおり、外面から順に板紙層１１と接着層１２と発泡体層１４とポリオレフィン層１３からなるリシール層１’と、部分接着剤層２７と離型層２１とプラスチックフィルム層２２と接着層２３とアルミニウム箔層２４と熱接着性樹脂層２５からなるシール層２が、ポリオレフィン層１３と部分接着剤層２７及び離型層２１の界面で剥離可能に接着された構成である。第２実施形態では、リシール層１’は発泡体層１４が積層された構成となっておりクッション性に優れるので、嵌合方式のキャップを使用した場合でも、キャップを外し容器口部３に接着されたシール層１’を剥がし取って開封した後に、キャップ内に残ったリシール層１’により容器口部３を確実に密封することができる。
【００１４】
本発明の第３実施形態の積層構成は、図４に示すとおり、外面から順に板紙層１１と接着層１２とプラスチックフィルム層１５と離型層１６と部分接着剤層２７とからなるリシール層１”と、ポリオレフィン層２６とグラシン紙層２２と接着層２３とアルミニウム箔層２４と熱接着性樹脂層２５からなるシール層１’が、離型層１６及び部分接着剤層２７とポリオレフィン層２６の界面で剥離可能に接着された構成である。
【００１５】
第３実施形態の容器口部密封用インナーシール材を装填したキャップ４を容器口部３に取り付けて高周波の照射により容器口部密封用インナーシール材を容器口部３に接着して密封した後に、キャップ４を容器口部３から取り外すことにより、図５に示すように、離型層１６及び部分接着剤層２７とポリオレフィン層２６の界面で剥離して分離し、板紙層１１と接着層１２とプラスチックフィルム層１５と離型層１６と部分接着剤層２７とからなるリシール層１”がキャップ４内に残り、ポリオレフィン層２６とグラシン紙層２２と接着層２３とアルミニウム箔層２４と熱接着性樹脂層２５からなるシール層１’が容器口部３に接着さた状態となる。第３実施形態では、分離してキャップ内に残ったリシール層１”の内面にプラスチックフィルム層１５が積層された構成でありリシール層１”の防湿性が優れるので、シール層２’を剥離した後もキャップを閉めることにより防湿性を保持することができる。
【００１６】
離型層に使用できる樹脂としては、ニトロセルロース系樹脂、ポリアミド系樹脂、アクリル系樹脂、ゴム系樹脂、ポリエステル系樹脂、ポリウレタン系樹脂、塩化ビニル−酢酸ビニル共重合体樹脂等の単体あるいは混合物である。上記樹脂の単体あるいは混合物にシリコーン樹脂を添加した組成としてもよい。離型層は全面ベタ印刷により形成される。上記の樹脂はポリエチレン等からなるポリオレフィン層との親和性が弱く離型性を有するので、離型層面に溶融押出しされたポリオレフィン層を積層することにより、離型層とポリオレフィン層間の接着強度を５〜５０ｇ／３０ｍｍ巾程度に調整することができる。
【００１７】
部分接着剤層に使用できる樹脂としては、塩素化ポリプロピレン、エチレン−酢酸ビニル共重合体等である。これらの樹脂は、ポリエチレン等のポリオレフィン層との親和性がよいのでポリオレフィン層とよく接着する。したがって、これらの樹脂を離型層２１面に点状、碁盤目状、万線状等に所定の面積比となるように部分接着剤層２６を形成することにより、ポリオレフィン層と離型層及び部分接着剤層間の接着強度、即ち、リシール層とシール層間の接着強度を調整するのが容易となり、容器口部密封用インナーシール材をキャップに装填して容器口部に取り付けるまではリシール層とシール層が剥離してしまうことがなく、且つ容器からキャップを外す際に、弱い力でリシール層とシール層を分離させることが可能となる。
【００１８】
板紙層としては、剛性の大きい坪量が４００〜６５０ｇ／ｍ^２程度の板紙が使用される。上記の剛性の大きい板紙を使用することにより、容器口部密封用インナーシール材が装填されたキャップを内容物を充填した容器口部に取り付けて密封した後、キャップを容器口部から取り外した際に、容器口部密封用インナーシール材がキャップから脱落してしまうことなく、シール層がキャップ内に残った状態でシール層とリシール層とに分離させることができる。ポリオレフィン層としては熱溶融押出ししたポリエチレン等が使用される。発泡体層としては厚さが０．６〜１．０ｍｍのポリプロピレン、ポリエチレン等からなるポリオレフィン系発泡体が使用される。プラスチックフィルム層としては防湿性の優れた２軸延伸ポリエチレンテレフタレート、２軸延伸ポリプロピレン等の２軸延伸フィルムが使用できるが、２軸延伸ポリプロピレンは防湿性が優れるので好ましい。熱接着性樹脂層としては、エチレン−酢酸ビニル共重合体を主成分としたホットメルトタイプの熱接着性樹脂が使用される。グラシン紙層とアルミニウム箔層を積層する接着層としては耐熱性のよいウレタン系接着剤を使用するのが好ましい。
【００１９】
【発明の効果】板紙層とポリオレフィン層を有するリシール層と、離型層とグラシン紙層と接着層とアルミニウム箔層と熱接着性樹脂層からなるシール層が、ポリオレフィン層と離型層の界面で剥離可能に積層された構成とすることにより、この容器口部密封用インナーシール材を装填したキャップを容器口部に取り付けキャップの外から高周波を照射して熱接着性樹脂層を溶融させて容器口部に接着する際の高周波シール性に優れたインナーシール材とすることができる。
【００２０】
また、リシール層が板紙層とポリオレフィン層間に発泡体層が積層された構成とすることにより、嵌合方式のキャップを使用した場合においても、リシール層のクッション性がよいので、容器からキャップを外し容器口部に接着されたシール層を剥がし取って開封した後に、キャップ内に残ったリシール層にて容器口部を確実に密封できる。
【００２１】
板紙層と接着層とプラスチックフィルムと離型層からなるリシール層と、ポリオレフィン層とグラシン紙層と接着層とアルミニウム箔層と熱接着性樹脂層からなるシール層が、ポリオレフィン層と離型層の界面で剥離可能に積層された構成とすることにより、高周波シール性が優れるとともに、容器口部に接着されたシール層を剥がし取って開封した後に、キャップに残ったリシール層により容器口部を密封した際に、リシール層の防湿性が優れるので容器に収納されたインスタントコーヒー等の内容物の吸湿を防止することができる。
【図面の簡単な説明】
【図１】本発明の第１実施形態の積層構成を示す断面図。
【図２】第１実施形態の容器口部密封用インナーシール材を装填したキャップを容器口部に取り付け高周波の照射により容器口部に接着した後キャップを外してリシール層とシール層に分離した状態を示す部分断面図。
【図３】本発明の第２実施形態の積層構成を示す断面図。
【図４】本発明の第３実施形態の積層構成を示す断面図。
【図５】第３実施形態のリシール層とシール層に分離した状態を示す図２に対応する部分断面図。
【符号の説明】
１，１’　，１”　リシール層
２，２’　　シール層
３　容器口部
４　キャップ
５　熱接着部
１１　　板紙
１２　　接着層
１３，　２６　　ポリオレフィン層
１４　　発泡体層
１５　プラスチックフィルム層
１６，　２１　　離型層
２２　グラシン紙層
２３　　接着層
２４　アルミニウム箔層
２５　熱接着性樹脂層
２７　部分接着剤層[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to an inner seal material for sealing a container mouth which is attached to the mouth of the container by attaching a cap loaded with the inner seal material to the mouth of the container and then irradiated with high frequency radiation.
[0002]
[Prior art]
Conventionally, a heat-adhesive resin layer is laminated on the lowermost layer of a sealing layer having an aluminum foil layer in an inner sealing material for sealing a container opening for sealing a container opening containing highly hygroscopic contents such as coffee. Then, high-frequency irradiation is performed to cause the aluminum foil layer to generate heat to melt the thermo-adhesive resin layer and adhere to the container mouth, for example, a cap such as described in Japanese Patent No. 3053602. An inner sealing material for sealing a mouth of a container having a configuration in which a reseal layer left on the inside of a container, a peel layer, an aluminum foil, a polyethylene layer, a glass layer, and a seal layer made of a hot melt adhesive layer are releasably laminated. I have.
[0003]
However, the above-mentioned inner sealing material for sealing the mouth of the container heats the aluminum foil by high-frequency irradiation, and the heat melts the hot-melt adhesive layer to adhere to the mouth of the container. The structure consists of a release layer, an aluminum foil, a polyethylene layer, glassine paper and a hot melt adhesive layer, and the polyethylene layer and glassine paper are laminated between the aluminum foil and the hot melt adhesive layer. The heat generated by the foil is transmitted to the hot-melt adhesive layer through the polyethylene layer and glassine paper, causing the hot-melt adhesive layer to melt, resulting in poor conductivity of the heat generated by the aluminum foil to the hot-melt adhesive layer. Therefore, there is a disadvantage that the efficiency of the high-frequency seal is reduced. Further, there is a disadvantage that the polyethylene layer used for laminating the aluminum foil and the glassine paper may be melted by heat generated from the aluminum foil and the aluminum foil and the glassine paper may be peeled off.
[0004]
[Problems to be solved by the invention]
SUMMARY OF THE INVENTION An object of the present invention is to provide an inner sealing material for sealing a mouth of a container, in which heat generated from an aluminum foil by high-frequency irradiation is easily conducted to a heat-adhesive resin layer and has excellent high-frequency sealing properties.
[0005]
[Means for Solving the Problems]
A reseal layer having a paperboard layer and a polyolefin layer, and a seal layer consisting of a release layer, a glassine paper layer, an adhesive layer, an aluminum foil layer, and a thermo-adhesive resin layer, which are releasably laminated at an interface between the polyolefin layer and the release layer. With this configuration, the cap loaded with the inner sealing material for sealing the mouth of the container is attached to the mouth of the container, and high-frequency radiation is applied from outside the cap to melt the heat-adhesive resin layer and adhere to the mouth of the container. In this case, an inner seal material having excellent high-frequency sealing properties can be obtained.
[0006]
In the inner sealing material for sealing the mouth of the container, the reseal layer is formed by laminating the foam layer between the paperboard layer and the polyolefin layer. After removing the cap from the container, peeling off the sealing layer adhered to the container opening, and opening the container, the container opening can be securely sealed with the reseal layer remaining in the cap.
[0007]
A reseal layer consisting of a paperboard layer, an adhesive layer, a plastic film and a release layer, a seal layer consisting of a polyolefin layer, a glassine paper layer, an adhesive layer, an aluminum foil layer, and a thermoadhesive resin layer, and a polyolefin layer and a release layer. The high-frequency sealability is excellent by adopting a configuration that is laminated so that it can be peeled off at the interface, and the container mouth is sealed with the reseal layer remaining on the cap after the seal layer adhered to the container mouth is peeled off and opened. In this case, since the moisture resistance of the resealing layer is excellent, it is possible to prevent moisture absorption of contents such as instant coffee stored in the container.
[0008]
In the above inner seal material for sealing the mouth of the container, the adhesive strength between the release layer surface and the partial adhesive layer surface and the polyolefin layer surface, that is, the reseal layer, is formed by forming the partial adhesive layer on the release layer surface. It is easy to adjust the adhesive strength of the seal layer and the seal layer, so the reseal layer and the seal layer do not peel off until the inner seal material for sealing the container mouth is loaded into the cap and attached to the container mouth. In addition, when the cap is removed from the container, the reseal layer and the seal layer can be separated with a small force.
[0009]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, embodiments of the present invention will be described with reference to the drawings.
FIG. 1 is a cross-sectional view showing a laminated structure according to a first embodiment of the present invention, and FIG. 2 is a diagram showing a first embodiment of the present invention in which a cap loaded with an inner sealing material for sealing the container mouth is attached to the mouth of the container. FIG. 3 is a partial cross-sectional view showing a laminated structure of a second embodiment of the present invention, and FIG. 4 is a third cross-sectional view showing a laminated structure of a second embodiment of the present invention. FIG. 5 is a sectional view corresponding to FIG. 2 showing a state in which a reseal layer and a seal layer of the first embodiment are separated, and FIG. 5 is a partial sectional view corresponding to FIG. , 2, 2 'is a sealing layer, 3 is a container opening, 4 is a cap, 5 is a thermal bonding part, 11 is a paperboard, 12 is an adhesive layer, 13, 26 is a polyolefin layer, 14 is a foam layer, and 15 is plastic. Film layer, 16 and 21 are release layers, 22 is glassine paper layer 23 adhesive layer, 24 is an aluminum foil layer, 25 is heat-adhesive resin layer, 27 represents a partial adhesive layer.
[0010]
The laminated structure of the first embodiment of the present invention is as shown in FIG. 1, and the state of being separated into the reseal layer 1 and the seal layer 2 is as shown in FIG. The laminated structure of the first embodiment includes a reseal layer 1 in which a paperboard layer 11, an adhesive layer 12, and a polyolefin layer 13 are sequentially laminated from an outer surface, a partial adhesive layer 27, a release layer 21, a glassine paper layer 22, and an adhesive layer. The seal layer 2 on which the laminate 23, the aluminum foil layer 24, and the heat-adhesive resin layer 25 are laminated can be peeled off at the interface between the polyolefin layer 13 of the reseal layer 1, the partial adhesive layer 27 of the seal layer 2, and the release layer 21. This is a bonded configuration. The picture layer can be formed on the inner side or the outer side of the glassine paper layer 22 by gravure printing or the like. The partial adhesive layer 27 formed on the surface of the release layer 21 is for facilitating the adjustment of the adhesive strength between the reseal layer 1 and the seal layer 2, but has a configuration in which the partial adhesive layer 27 is not formed. Can also.
[0011]
The inner sealing material for sealing the container mouth portion of the first embodiment is fitted and loaded into the cap 4 so that the thermo-adhesive resin layer 25 becomes the outer surface, and the cap 4 loaded with the inner sealing material for sealing the container mouth portion is mounted. By attaching to the container opening 3 filled with the contents and irradiating high frequency from above the cap 4, the aluminum foil layer 24 generates heat and the heat causes the heat-adhesive resin layer 25 to melt. The inner sealing material can be sealed by adhering to the container opening 3. In the first embodiment, the heat-adhesive resin layer 25 is laminated on the surface of the aluminum foil layer 24, and the heat generated by the aluminum foil layer 24 by high-frequency irradiation is easily conducted to the heat-adhesive resin layer 25. Sex can be improved.
[0012]
By removing the cap 4 from the state where the container mouth 3 is sealed using the container mouth sealing inner seal of the first embodiment, as shown in FIG. 2, the container mouth sealing inner seal is made of polyolefin. At the interface between the layer 13, the release layer 21 and the partial adhesive layer 27, the layer is separated into a reseal layer 1 and a seal layer 2, and the reseal layer 1 remains loaded in the cap 4, Reference numeral 2 denotes a state in which the surface of the heat-adhesive resin layer 25 is bonded to the container opening 3 at the bonding portion 5 to seal the container opening 3. The seal layer 2 adhered to the container opening 3 can be easily opened by piercing with a finger and peeling off from the container opening 3.
[0013]
As shown in FIG. 3, the laminated structure of the second embodiment of the present invention includes, in order from the outer surface, a reseal layer 1 ′ including a paperboard layer 11, an adhesive layer 12, a foam layer 14, and a polyolefin layer 13, and a partial adhesive layer 27. , A release layer 21, a plastic film layer 22, an adhesive layer 23, an aluminum foil layer 24, and a heat-adhesive resin layer 25, and a seal layer 2 is formed at the interface between the polyolefin layer 13, the partial adhesive layer 27, and the release layer 21. This is a configuration in which it is peelably bonded. In the second embodiment, the reseal layer 1 ′ has a configuration in which the foam layer 14 is laminated and has excellent cushioning properties. Therefore, even when a cap of a fitting type is used, the cap is removed and adhered to the container opening 3. After peeling off the opened sealing layer 1 ′ and opening it, the container opening 3 can be securely sealed by the reseal layer 1 ′ remaining in the cap.
[0014]
As shown in FIG. 4, the laminated structure of the third embodiment of the present invention is a resealing layer 1 composed of a paperboard layer 11, an adhesive layer 12, a plastic film layer 15, a release layer 16, and a partial adhesive layer 27 in this order from the outer surface. The sealing layer 1 ′ composed of the polyolefin layer 26, the glassine paper layer 22, the adhesive layer 23, the aluminum foil layer 24, and the heat-adhesive resin layer 25 forms the release layer 16, the partial adhesive layer 27, and the polyolefin layer 26. This is a configuration in which the adhesive is detachably bonded at the interface.
[0015]
After the cap 4 loaded with the inner sealing material for sealing the container opening of the third embodiment is attached to the container opening 3 and the inner sealing material for sealing the container opening is adhered to the container opening 3 by high frequency irradiation, and then sealed. By removing the cap 4 from the container opening 3, the release layer 16 and the adhesive layer 27 are separated and separated at the interface between the polyolefin layer 26 and the paperboard layer 11 and the adhesive layer 12 as shown in FIG. Reseal layer 1 "consisting of a plastic film layer 15, a release layer 16, and a partial adhesive layer 27, remains in the cap 4, and is thermally bonded to the polyolefin layer 26, the glassine paper layer 22, the adhesive layer 23, and the aluminum foil layer 24. The sealing layer 1 'made of the conductive resin layer 25 is adhered to the container opening 3. In the third embodiment, a plastic film is applied to the inner surface of the reseal layer 1 "separated and left in the cap. Since the resealing layer 1 ″ is excellent in moisture-proof property because of the laminated structure of the memory layer 15, the moisture-proof property can be maintained by closing the cap even after the sealing layer 2 ′ is peeled off.
[0016]
As the resin that can be used for the release layer, a nitrocellulose resin, a polyamide resin, an acrylic resin, a rubber resin, a polyester resin, a polyurethane resin, a vinyl chloride-vinyl acetate copolymer resin, or a mixture thereof can be used. is there. A composition in which a silicone resin is added to a simple substance or a mixture of the above resins may be used. The release layer is formed by solid printing on the entire surface. Since the above resin has a weak affinity for a polyolefin layer made of polyethylene or the like and has releasability, by laminating a melt-extruded polyolefin layer on the surface of the release layer, the adhesive strength between the release layer and the polyolefin layer is reduced by 5%. It can be adjusted to about 50 g / 30 mm width.
[0017]
Resins that can be used for the partial adhesive layer include chlorinated polypropylene and ethylene-vinyl acetate copolymer. These resins have good affinity for a polyolefin layer such as polyethylene, and therefore adhere well to the polyolefin layer. Therefore, by forming these resins on the surface of the release layer 21 in the form of dots, grids, lines, or the like to form the partial adhesive layer 26 so as to have a predetermined area ratio, the polyolefin layer and the release layer and It is easy to adjust the adhesive strength between the partial adhesive layers, that is, the adhesive strength between the reseal layer and the seal layer. It is possible to separate the reseal layer and the seal layer with a small force when the cap is removed from the container without peeling off the seal layer.
[0018]
As the paperboard layer, a paperboard having a large rigidity and a basis weight of about 400 to 650 g / m ² is used. By using the above-mentioned rigid paperboard, the cap loaded with the inner sealing material for sealing the container mouth is attached to the container mouth filled with the contents, and the cap is removed from the container mouth. Furthermore, the inner sealing material for sealing the mouth of the container does not fall off the cap, and the sealing layer can be separated into the sealing layer and the resealing layer with the sealing layer remaining in the cap. As the polyolefin layer, hot melt extruded polyethylene or the like is used. As the foam layer, a polyolefin foam having a thickness of 0.6 to 1.0 mm made of polypropylene, polyethylene, or the like is used. As the plastic film layer, a biaxially stretched film such as biaxially stretched polyethylene terephthalate and biaxially stretched polypropylene having excellent moisture resistance can be used, but biaxially stretched polypropylene is preferable because it has excellent moisture resistance. As the heat-adhesive resin layer, a hot-melt type heat-adhesive resin containing an ethylene-vinyl acetate copolymer as a main component is used. As an adhesive layer for laminating the glassine paper layer and the aluminum foil layer, it is preferable to use a urethane-based adhesive having good heat resistance.
[0019]
According to the present invention, a reseal layer having a paperboard layer and a polyolefin layer, a seal layer including a release layer, a glassine paper layer, an adhesive layer, an aluminum foil layer, and a thermoadhesive resin layer are provided at the interface between the polyolefin layer and the release layer. By attaching a cap loaded with the inner sealing material for sealing the container mouth to the container mouth, by applying a high frequency from outside the cap to melt the thermal adhesive resin layer An inner sealing material having excellent high-frequency sealing properties when adhering to the container mouth can be obtained.
[0020]
In addition, since the reseal layer has a structure in which the foam layer is laminated between the paperboard layer and the polyolefin layer, even when a cap of a fitting type is used, the cushion property of the reseal layer is good, so the cap is removed from the container. After peeling off and opening the seal layer adhered to the container mouth, the container mouth can be reliably sealed with the reseal layer remaining in the cap.
[0021]
A reseal layer consisting of a paperboard layer, an adhesive layer, a plastic film and a release layer, a seal layer consisting of a polyolefin layer, a glassine paper layer, an adhesive layer, an aluminum foil layer, and a thermoadhesive resin layer, and a polyolefin layer and a release layer. The high-frequency sealability is excellent by adopting a structure that is laminated so that it can be peeled off at the interface, and the container mouth is sealed with the reseal layer remaining in the cap after the seal layer adhered to the container mouth is peeled off and opened. In this case, since the moisture resistance of the resealing layer is excellent, it is possible to prevent moisture absorption of contents such as instant coffee stored in the container.
[Brief description of the drawings]
FIG. 1 is a cross-sectional view illustrating a stacked configuration according to a first embodiment of the present invention.
FIG. 2 shows a cap loaded with an inner sealing material for sealing a container mouth portion of the first embodiment, attached to the container mouth portion, adhered to the container mouth portion by high-frequency irradiation, and then removed to separate a reseal layer and a seal layer. FIG. 4 is a partial cross-sectional view showing a state.
FIG. 3 is a cross-sectional view illustrating a stacked configuration according to a second embodiment of the present invention.
FIG. 4 is a cross-sectional view illustrating a stacked configuration according to a third embodiment of the present invention.
FIG. 5 is a partial cross-sectional view corresponding to FIG. 2 and showing a state in which a reseal layer and a seal layer of a third embodiment are separated.
[Explanation of symbols]
1, 1 ', 1 "resealing layer 2, 2' sealing layer 3 container mouth 4 cap 5 heat bonding section 11 paperboard 12 bonding layer 13, 26 polyolefin layer 14 foam layer 15 plastic film layer 16, 21 release layer 22 Glassine paper layer 23 Adhesive layer 24 Aluminum foil layer 25 Thermal adhesive resin layer 27 Partial adhesive layer

Claims

板紙層とポリオレフィン層を有するリシール層と、離型層とグラシン紙層と接着層とアルミニウム箔層と熱接着性樹脂層からなるシール層が、前記ポリオレフィン層と前記離型層の界面で剥離可能に積層された構成からなることを特徴とする容器口部密封用インナーシール材。A reseal layer having a paperboard layer and a polyolefin layer, a seal layer composed of a release layer, a glassine paper layer, an adhesive layer, an aluminum foil layer, and a thermoadhesive resin layer can be peeled off at an interface between the polyolefin layer and the release layer. An inner sealing material for sealing a container mouth portion, wherein the inner sealing material has a configuration laminated on the substrate.

前記リシール層が板紙層とポリオレフィン層間に発泡体層が積層された構成からなることを特徴とする請求項１記載の容器口部密封用インナーシール材。2. The inner sealing material for sealing a mouth of a container according to claim 1, wherein the reseal layer has a structure in which a foam layer is laminated between a paperboard layer and a polyolefin layer.

板紙層と接着層とプラスチックフィルムと離型層からなるリシール層と、ポリオレフィン層とグラシン紙層と接着層とアルミニウム箔層と熱接着性樹脂層からなるシール層が、前記離型層と前記ポリオレフィン層の界面で剥離可能に積層された構成からなることを特徴とする容器口部密封用インナーシール材。A resealing layer comprising a paperboard layer, an adhesive layer, a plastic film, and a release layer; a sealing layer comprising a polyolefin layer, a glassine paper layer, an adhesive layer, an aluminum foil layer, and a thermoadhesive resin layer, wherein the release layer and the polyolefin An inner sealing material for sealing a mouth of a container, wherein the inner sealing material has a structure laminated so as to be peelable at an interface between layers.

前記離型層面に部分接着剤層が形成されていることを特徴とする請求項１〜３のいずれかに記載の容器口部密封用インナーシール材。The inner seal material for sealing a container mouth part according to any one of claims 1 to 3, wherein a partial adhesive layer is formed on the surface of the release layer.