JP4529481B2 - 表面保護フィルム - Google Patents
表面保護フィルム Download PDFInfo
- Publication number
- JP4529481B2 JP4529481B2 JP2004055174A JP2004055174A JP4529481B2 JP 4529481 B2 JP4529481 B2 JP 4529481B2 JP 2004055174 A JP2004055174 A JP 2004055174A JP 2004055174 A JP2004055174 A JP 2004055174A JP 4529481 B2 JP4529481 B2 JP 4529481B2
- Authority
- JP
- Japan
- Prior art keywords
- protective film
- polymer
- surface protective
- acid
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
1.ジエン系ブロック重合体の水素添加物、及び、液状材料を含むエラストマー組成物からなる表面保護フィルムであって、
上記ジエン系ブロック重合体の水素添加物は、ビニル結合含量が25%未満であるブタジエン重合体ブロック(I)と、ビニル結合含量が25〜95%であるブタジエン重合体ブロック(II)とからなるジエン系ブロック重合体が水素添加されたものであり、
上記液状材料は、軟化剤であり、
上記液状材料の含有量は、重合体成分の合計100質量部に対して、400〜800質量部であり、
上記表面保護フィルムを厚さ0.5mmとした場合、そのヘイズは5%未満であり、且つ全光線透過率は90%以上であることを特徴とする表面保護フィルム。
2.上記軟化剤が鉱物油系軟化剤である上記1に記載の表面保護フィルム。
3.上記エラストマー組成物の少なくとも一部が架橋されている上記1又は2に記載の表面保護フィルム。
4.上記エラストマー組成物は、着色剤を含む上記1乃至3のいずれかに記載の表面保護フィルム。
5.本表面保護フィルムの一面に粘着層が更に形成された上記1乃至4のいずれかに記載の表面保護フィルム。
6.携帯電話、携帯情報端末、デスクトップ型コンピュータ用ディスプレイ、ノート型コンピュータ、車載用コンピュータ、タッチパネル、テレビジョン及び時計用である上記1乃至5のいずれかに記載の表面保護フィルム。
また、エラストマー組成物が着色剤を含む場合には、着色された表面保護フィルムが配設された材料がどの工程で用いられるものであるかを判別しやすくなる。更には、着色された表面保護フィルムが配設された製品の種類を容易に判別することが可能となる。
本発明の表面保護フィルムは、ジエン系ブロック重合体の水素添加物、及び、液状材料を含むエラストマー組成物からなることを特徴とするものである。
上記ジエン系ブロック重合体の水素添加物は、ビニル結合含量が25%未満であるブタジエン重合体ブロック(I)と、ビニル結合含量が25〜95%であるブタジエン重合体ブロック(II)とからなるジエン系ブロック重合体が水素添加されたものである。上記ジエン系ブロック重合体のブロック構造としては、(A−B)mA、(B−A)mB、(A−B−A)m、(B−A−B)m等が挙げられ、更に、(A−B)mX、(B−A)mX、(A−B−A)mX、(B−A−B)mX等のように、カップリング剤残基Xを介して重合体分子鎖が延長又は分岐されたものでもよい。各一般式において、「A」はブタジエン重合体ブロック(I)、「B」はブタジエン重合体ブロック(II)、mは1以上の整数である。
尚、上記重合体ブロック(II)において、ビニル結合(1,2−ビニル結合及び3,4−ビニル結合)の含量は、25〜95%であり、より好ましくは25〜90%、更に好ましくは30〜85%である。
また、上記重合体(P)は、トリブロック以上のブロックを有する共重合体であれば、水素添加物とした場合に形状保持性及び力学的性質により優れる成形体を得ることができる。従って、上記一般式において、m1は、2以上の整数であることが好ましい。
上記カップリング剤としては、1,2−ジブロモエタン、メチルジクロロシラン、トリクロロシラン、メチルトリクロロシラン、テトラクロロシラン、テトラメトキシシラン、ジビニルベンゼン、アジピン酸ジエチル、アジピン酸ジオクチル、ベンゼン−1,2,4−トリイソシアネート、トリレンジイソシアネート、エポキシ化1,2−ポリブタジエン、エポキシ化アマニ油、テトラクロロゲルマニウム、テトラクロロスズ、ブチルトリクロロスズ、ブチルトリクロロシラン、ジメチルクロロシラン、1,4−クロロメチルベンゼン、ビス(トリクロロシリル)エタン等が挙げられる。
また、上記部分架橋共重合体は、これらの極性基含有化合物に多官能性不飽和結合を有する化合物を共重合することにより得られるが、この化合物としては、多価アリル化合物、多価(メタ)アクリレート化合物、ジビニル化合物、ビスマレイミド化合物、ジオキシム化合物等が挙げられる。
上記アクリル酸アルキルエステルとしては、メチルアクリレート、エチルアクリレート、n−プロピルアクリレート、n−ブチルアクリレート、イソブチルアクリレート、n−ペンチルアクリレート、イソアミルアクリレート、n−ヘキシルアクリレート、2−メチルペンチルアクリレート、n−オクチルアクリレート、2−エチルヘキシルアクリレート、n−デシルアクリレート、n−ドデシルアクリレート、n−オクタデシルアクリレート、シアノメチルアクリレート、1−シアノエチルアクリレート、2−シアノエチルアクリレート、1−シアノプロピルアクリレート、2−シアノプロピルアクリレート、3−シアノプロピルアクリレート、4−シアノブチルアクリレート、6−シアノヘキシルアクリレート、2−エチル−6−シアノヘキシルアクリレート、8−シアノオクチルアクリレート等が挙げられる。これらは、1種単独であるいは2種以上を組み合わせて用いることができる。
上記アクリル酸アルコキシアルキルエステルとしては、2−メトキシエチルアクリレート、2−エトキシエチルアクリレート、2−(n−プロポキシ)エチルアクリレート、2−(n−ブトキシ)エチルアクリレート、3−メトキシプロピルアクリレート、3−エトキシプロピルアクリレート、2−(n−プロポキシ)プロピルアクリレート、2−(n−ブトキシ)プロピルアクリレート等が挙げられる。
上記有機ジイソシアネートとしては、4,4’−ジフェニルメタンジイソシアネート、トリレンジイソシアネート、1,5−ナフチレンジイソシアネート、キシリレンジイソシアネート、フェニレンジイソシアネート、3,3’−ジクロロ−4,4’−ジフェニルメタンジイソシアネート等の芳香族ジイソシアネート類;ヘキサメチレンジイソシアネート、イソホロンジイソシアネート、4,4’−ジシクロヘキシルメタンジイソシアネート、水添キシリレンジイソシアネート等の脂肪族又は脂環式ジイソシアネート類等が挙げられる。これらの有機ジイソシアネートは、1種単独であるいは2種以上を組み合わせて用いることができる。
これらのうち、ポリエステルジオールとしては、脂肪族ジオールと脂肪族ジカルボン酸又はこれらのエステル形成性誘導体の反応により得られた脂肪族ポリエステルジオール、脂肪族ジオールと芳香族ジカルボン酸又はそれらのエステル形成性誘導体の反応により得られた芳香族ポリエステルジオール等が挙げられる。また、ポリエーテルジオールとしては、ポリエチレングリコール、ポリプロピレングリコール、ポリテトラメチレングリコール又はそれらのブロック共重合体等が挙げられる。更に、ポリカーボネートジオールとしては、脂肪族ジオールとカーボネート化合物との反応により得られたポリカーボネートジオール、ビスフェノールA等の芳香族ジオールとカーボネート化合物との反応により得られたポリカーボネートジオール等が挙げられる。これらの高分子ジオールは、1種単独であるいは2種以上を組み合わせて用いることができる。
上記以外に、エチレン・酢酸ビニル共重合体、スチレン系重合体、ポリカーボネート、ポリアセタール、エポキシ系重合体等の重合体を用いることもできる。
上記有機過酸化物としては、t−ブチルハイドロパーオキサイド、1,1,3,3−テトラメチルブチルハイドロパーオキサイド、p−メンタンハイドロパーオキサイド、クメンハイドロパーオキサイド、ジイソプロピルベンゼンハイドロパーオキサイド、2,5−ジメチルヘキサン−2,5−ジハイドロパーオキサイド、1,1−ジ−t−ブチルパーオキシ−3,3,5−トリメチルシクロヘキサン、ジ−t−ブチルパーオキサイド、t−ブチルクミルパーオキサイド、ジクミルパーオキサイド、1,1−ビス(t−ブチルパーオキシ)シクロドデカン、2,2−ビス(t−ブチルパーオキシ)オクタン、1,1−ジ−t−ブチルパーオキシシクロヘキサン、2,5−ジメチル−2,5−ジ−(t−ブチルパーオキシ)ヘキサン、2,5−ジメチル−2,5−ジ−(t−ブチルパーオキシ)ヘキシン、1,3−ビス(t−ブチルパーオキシ−イソプロピル)ベンゼン、2,5−ジメチル−2,5−ジ−(ベンゾイルパーオキシ)ヘキサン、1,1−ビス(t−ブチルパーオキシ)−3,3,5−トリメチルシクロヘキサン、n−ブチル−4,4−ビス(t−ブチルパーオキシ)バレレート、ベイゾイルパーオキサイド、m−トルイルパーオキサイド、p−クロロベンゾイルパーオキサイド、2,4−ジクロロベンゾイルパーオキサイド、t−ブチルパーオキシイソブチレート、t−ブチルパーオキシ−2−エチルヘキサノエート、t−ブチルパーオキシベンゾエート、t−ブチルパーオキシ−イソプロピルカーボナート、t−ブチルパーオキシアリルカーボナート等が挙げられる。これらは、1種単独であるいは2種以上を組み合わせて用いることができる。
この液状材料としては特に限定されないが、40℃における動粘度が500mm2/s(1mm2/s=1cSt)以下であるものが好ましい。より好ましい動粘度は400mm2/s以下、更に好ましくは0.1〜100mm2/sである。このような液状材料としては、軟化剤が用いられる。また、本発明以外の液状材料としては、可塑剤、滑剤、液状重合体が挙げられる。
可塑剤としては、フタル酸誘導体、イソフタル酸誘導体、テトラヒドロフタル酸誘導体、アジピン酸誘導体、セバシン酸誘導体、フマル酸誘導体、クエン酸誘導体、アゼライン酸誘導体、リン酸誘導体、マレイン酸誘導体等の各種脂肪酸の誘導体等が挙げられる。
滑剤としては、パラフィン系滑剤、炭化水素系滑剤、金属セッケン等が挙げられる。
また、液状重合体としては、室温において液状である各種重合体が挙げられ、例としては、液状ポリブタジエン、液状スチレン・ブタジエンゴム等の液状ゴム、ポリイソブチレン、シリコーンオイル等が挙げられる。
上記例示した液状材料は、1種単独であるいは2種以上を組み合わせて用いることができる。
この着色剤としては、公知の顔料、染料を用いることができる。これらは、それぞれ1種単独であるいは2種以上を組み合わせて用いることができる。
顔料としては、有機顔料、無機顔料を用いることができる。有機顔料としては、モノアゾ系、クロモフタールレッド等の縮合アゾ系、アンスラキノン系、イソインドリノン系、複素環系、ペリノン系、キナクリドン系、ペリレン系、チオインジゴ系、ジオキサジン系、フタロシアニン系、ニトロソ系、有機蛍光顔料等が挙げられる。また、無機顔料としては、酸化チタン、カーボンブラック、チタンイエロー、酸化鉄、群青、コバルトブルー、焼成顔料、メタリック顔料、マイカ、パール顔料、亜鉛華、沈降性シリカ、カドミウム赤等が挙げられる。
また、染料としては、アンスラキノン系、複素環系、ペリノン系、塩基性染料、酸性染料、媒染染料等が挙げられる。更に、トリフェニルメタン系、フルオラン系、フェノチアジン系、オーラミン系、スピロピラン系のロイコ染料等の、放射線照射により着色する化合物を用いることもできる。尚、放射線によって着色する化合物を着色剤として使用する場合は、フェノールホルマリン樹脂の初期重合体、芳香族カルボン酸誘導体、活性白土等の電子受容体等を顕色剤として併用することが好ましい。
この添加剤としては、軟化剤、可塑剤、滑剤、酸化防止剤、老化防止剤、熱安定剤、難燃剤、防菌・防かび剤、耐候剤、紫外線吸収剤、粘着付与剤、造核剤、有機フィラー、無機フィラー、シランカップリング剤、チタンカップリング剤等が挙げられる。
得られる表面保護フィルムの厚さは、用途等の必要に応じて種々の範囲とすることができ特に限定されないが、10〜3000μmであることが好ましく、より好ましくは10〜2000μmである。
また、本発明の表面保護フィルムは、耐熱性にも優れており、好ましくは−80〜100℃、より好ましくは−50〜70℃において、粘弾性及び形状保持性を併せ持つ。
従って、本発明の表面保護フィルムは、常温のみならず、0℃以下の低温時における使用にも好適である。
この粘着層の厚さについては特に限定はなく、用途等の必要に応じて種々の範囲とすることができる。通常、粘着層の厚さは0.5〜500μm、好ましくは1〜300μm、更に好ましくは1〜100μmである。
また、この粘着層は剥離又は再剥離する際に、被着面に粘着剤の移行がないことが好ましい。粘着層を構成する粘着剤成分としては、例えば、アクリル系、ゴム系及びウレタン系等の粘着剤を用いることができる。また、これらの粘着剤の硬化機構は、熱硬化型、UV硬化型、EB硬化型、ホットメルト型等のいずれであってもよい。
この粘着層を形成する方法としては、T−ダイ押出法、コーター法、T−ダイコーター法、キャスト法、積層(貼り合わせ)法及びロール法等が挙げられる。
上記剥離フィルムは、単一層でも多層でもよい。また、この支持フィルムの厚さは、通常、10〜3000μm、好ましくは10〜2000μmである。
また、本発明の表面保護フィルムは、製品の表面保護だけでなく、製造段階のものにも好適に使用することができる。この場合、種類の判別等が容易となる。また、従来のものよりも透明性に優れるため、欠陥検査等の精度を向上させることができる。
1.エラストマー組成物の調製
以下に示す重合体、液状材料、架橋剤及び着色剤を用いて表1に記載の割合で混合し、エラストマー組成物(i)〜(ix)を調製した。
1−1.重合体
(1)ジエン系ブロック共重合体の水素添加物(A1)
窒素置換された内容積50リットルの反応容器に、シクロヘキサン25kg、テトラヒドロフラン1g、1,3−ブタジエン1500g及びn−ブチルリチウム3.9gを投入し、70℃で重合を開始した。反応完結後、反応溶液の温度を40℃とし、テトラヒドロフラン100gを、次いで、1,3−ブタジエン3500gを添加して更に断熱重合した。30分後、メチルジクロロシラン2.7gを添加し、15分間反応を行い、反応を完結させた。
次に、水素ガスを0.4MPa−Gの圧力で供給し、反応溶液を撹拌しながら、リビングアニオンとして生きているポリマー末端リチウムと20分間反応させ、水素添加リチウムとした。その後、反応溶液を80℃とし、水添触媒であるチタノセンジクロリドを加え、水素ガスの圧力を1.0MPaで維持しながら2時間反応させた。反応後、反応溶液を常温、常圧に戻して反応容器より抜き出した。次いで、反応溶液を水中に撹拌投入して溶媒を水蒸気蒸留により除去することによって、目的とするジエン系ブロック共重合体の水素添加物A1を得た。得られたジエン系ブロック共重合体の水素添加物A1の水素添加率は99%、GPCによる重量平均分子量は34万、水素添加前ポリマーの1段目のブタジエン重合体ブロックのビニル結合含量は14%、水素添加前ポリマーの2段目のブタジエン重合体ブロックのビニル結合含量は49%であった。
窒素置換された内容積50リットルの反応容器に、シクロヘキサン25kg、テトラヒドロフラン1g、1,3−ブタジエン1500g及びn−ブチルリチウム4.1gを投入し、70℃で重合を開始した。反応完結後、反応溶液の温度を35℃とし、テトラヒドロフラン27gを、次いで、1,3−ブタジエン3500gを添加して更に断熱重合した。30分後、メチルジクロロシラン2.9gを添加し、15分間反応を行い、反応を完結させた。
次に、水素ガスを0.4MPa−Gの圧力で供給し、反応溶液を撹拌しながら、リビングアニオンとして生きているポリマー末端リチウムと20分間反応させ、水素添加リチウムとした。その後、反応溶液を80℃とし、水添触媒であるチタノセンジクロリドを加え、水素ガスの圧力を1.0MPaで維持しながら2時間反応させた。反応後、反応溶液を常温、常圧に戻して反応容器より抜き出した。次いで、反応溶液を水中に撹拌投入して溶媒を水蒸気蒸留により除去することによって、目的とするジエン系ブロック共重合体の水素添加物A2を得た。得られたジエン系ブロック共重合体の水素添加物A2の水素添加率は98%、GPCによる重量平均分子量は29万、水素添加前ポリマーの1段目のブタジエン重合体ブロックのビニル結合含量は14%、水素添加前ポリマーの2段目のブタジエン重合体ブロックのビニル結合含量は35%であった。
窒素置換された内容積50リットルの反応容器に、シクロヘキサン25kg、テトラヒドロフラン1g、1,3−ブタジエン1500g及びn−ブチルリチウム4.1gを加え、70℃で重合を開始した。反応完結後、反応溶液の温度を35℃とし、テトラヒドロフラン350gを、次いで、1,3−ブタジエン3500gを添加して更に断熱重合した。30分後、メチルジクロロシラン2.9gを添加し、15分間反応を行い、反応を完結させた。
次に、水素ガスを0.4MPa−Gの圧力で供給し、反応溶液を撹拌しながら、リビングアニオンとして生きているポリマー末端リチウムと20分間反応させ、水素添加リチウムとした。その後、反応溶液を80℃とし、水添触媒であるチタノセンジクロリドを加え、水素ガスの圧力を1.0MPaで維持しながら2時間反応させた。反応後、反応溶液を常温、常圧に戻して反応容器より抜き出した。次いで、反応溶液を水中に撹拌投入して溶媒を水蒸気蒸留により除去することによって、目的とするジエン系ブロック共重合体の水素添加物A3を得た。得られたジエン系ブロック共重合体の水素添加物A3の水素添加率は99%、GPCによる重量平均分子量は30万、水素添加前ポリマーの1段目のブタジエン重合体ブロックのビニル結合含量は14%、水素添加前ポリマーの2段目のブタジエン重合体ブロックのビニル結合含量は78%であった。
エチレンに由来する構造単位を75.1モル%、プロピレンに由来する構造単位を22.8モル%、5−エチリデン−2−ノルボルネンに由来する構造単位を1.8モル%、及び8−メチル−8−カルボキシテトラシクロ[4.4.0.12,5.17,10]−3−ドデセンに由来する構造単位を0.3モル%含み、重量平均分子量(Mw)が16.0×104である官能基含有オレフィン系共重合体100部をトルエン1000部に溶解した後、官能基含有オレフィン系共重合体中の官能基1モル%に対して、0.25モル%のジルコニウム(IV)ブトキシド(85%の1−ブタノール溶液(和光純薬工業社製)を使用)を用いて架橋し、トルエンを乾燥除去して、極性基変性オレフィン系重合体A4を得た。
(5)熱可塑性ポリウレタンエラストマー(A5)
比較用として、熱可塑性ポリウレタンエラストマー(クラレ社製、商品名「クラミロンU1190」)を用いた。
「B1」;40℃における動粘度が30.85mm2/sである鉱物油系軟化剤(出光興産社製、商品名「PW−32」)である。
「B2」;40℃における動粘度が95.54mm2/sである鉱物油系軟化剤(出光興産社製、商品名「PW−90」)である。
「B3」;40℃における動粘度が381.6mm2/sである鉱物油系軟化剤(出光興産社製、商品名「PW−380」)である。
「C1」;有機過酸化物(日本油脂社製、商品名「パーヘキサ3M」)。
1−4.着色剤
「D1」;コバルトブルー(大日精化工業社製、商品名「コバルトブルー」)。
実施例1〜6、参考例7〜8及び比較例1
上記エラストマー組成物(i)〜(ix)を用い、コーター成形によりフィルムを作製し、これを表面保護フィルムとした。この表面保護フィルムを以下の方法で評価した。その結果を表2に示す。
(1)全光線透過率及びヘイズ
厚さ0.7mmの溶融成形アルミノケイ酸薄板ガラス(コーニング社製、商品名「Corning 1737」)2枚の間に、厚さ0.5mmの薄肉体をはさみ、25℃における全光線透過率(%)及びヘイズ(%)を、全光線透過率ヘイズ測定装置(BYK−Gardner社製、商品名「Haze−gard plus4725」)により測定した。尚、透明度は、ヘイズが5%未満である場合を「○」、5%以上である場合を「×」とした。
(2)粘弾性
剪断貯蔵弾性率(G’)及びtanδを、動的粘弾性測定装置(レオロジー社製「MR−500」)により、温度30℃、1Hzの条件で測定した。尚、G’は、70℃、1Hzの条件でも測定した。
(3)耐熱性
上記動的粘弾性測定装置を用い、温度70℃及び周波数1Hzの条件でフィルム(厚さ500μm)の剪断貯蔵弾性率(G70’)を測定した。そして、測定温度30℃及び70℃におけるG’の変化量δG’〔log(30℃におけるG’30/70℃におけるG’70)〕を計算した。このδG’が小さいほど耐熱性に優れる。表2において、「○」は、δG’が3.0以下であったことを示し、「×」は、δG’が3.0より大きかったことを示す。
(4)機械的強度
JIS K−7127に準拠して、引張速度500mm/分で各表面保護フィルムの引張強度及び引張伸びを測定した。
(5)耐衝撃性
図1に示すように、大理石等からなる基台3の上に、厚さ0.7mmの溶融成形アルミノケイ酸薄板ガラスである基層2(コーニング社製、商品名「Corning 1737」)を載せた。そして、該基層2の上に、厚さ0.5mmの表面保護フィルム1を載置し、その上に、厚さ0.5mmのアクリル板4(日東樹脂工業株式会社製、商品名「クラレックス」)を載せた。次いで、鋼球5(直径50.8mm、質量550g)を、所定高さから表面保護フィルム上に自由落下させ、衝突させた。その後、基層2にひびや割れが起きていないか目視で確認した。そして、基層2が破損したときの高さを落球高度(m)として求め、この落球高度から、以下の式により衝撃破壊エネルギー(J)を算出することにより、耐衝撃性を評価した。
衝撃破壊エネルギー(J)=A×B×9.8
A;落球高度(m) B;鋼球の質量(kg)
(6)着色性
各エラストマー組成物70g及び着色剤3.5mg(重合体100部あたり0.005部)を2インチロールを用いてロール成形し、1.9mm厚の着色フィルムを作製して、その両面を50μm厚の無着色の透明PETフィルムで挟み、2mm厚のフィルムを作製し、着色の状態を目視で確認することにより着色性を調べた。表2において、「○」は、着色性が良好であったことを示し、「×」は、着色性にムラがあったことを示す。
(7)剥離性
各表面保護フィルム(厚さ500μm)を厚さ0.7mmのガラス板(コーニング社製、商品名「Corning 1737」)に圧着ロールで貼り付けた後、ガラス板から剥離し、ガラス板表面における糊残りの有無を目視で観察し、剥離性を評価した。表2において、「○」は、表面保護フィルム剥離後のガラス板表面に糊残りが観察されなかったことを示し、「×」は、表面保護フィルム剥離後のガラス板表面に糊残りが観察されたことを示す。
(8)耐傷付き性
親指の爪で各表面保護フィルムの表面を擦り、傷付きの度合いを目視にて判定した。表2において、「○」は、表面保護フィルムに傷が付かなかったことを示し、「△」は、表面保護フィルムにうっすらと傷が入ることを示し、「×」は、表面保護フィルムに深い傷が入ることを示す。
表2によれば、重合体として熱可塑性ポリウレタンエラストマーを含むエラストマー組成物を用いて形成された比較例1では、ヘイズの値が29.9%と高く、透明度に劣っており、且つ全光線透過率も89%と低かった。また、30℃及び70℃における剪断貯蔵弾性率並びにtanδ(30℃)の値が大きく、粘弾性に劣っていた。更に、δG’[log(G’30/G’70)]の値が3.10であり、耐熱性の評価は「×」であった。また、引張伸びが410%と低く、衝撃破壊エネルギーも0.9Jと低かった。更に、着色性、剥離性及び耐傷付き性の評価も「×」であった。
これに対して、実施例1〜6は、ヘイズの値が2.5〜4.5%と低く、透明性に優れており、且つ全光線透過率も93〜94%と高かった。また、30℃及び70℃における剪断貯蔵弾性率並びにtanδ(30℃)の値が小さく、粘弾性に優れていた。更に、δG’[log(G’30/G’70)]の値が0.37〜0.48と小さく、耐熱性の評価は「○」であった。また、引張強度が0.3〜1.7MPaであり、且つ引張伸びが2010〜2700%と機械的強度にも優れていた。更に、衝撃破壊エネルギーも2.5〜8.1Jと高かった。また、着色性、剥離性及び耐傷付き性の評価も「○」であった。
上記のことから、本実施例の表面保護フィルムは、透明性、粘弾性、耐衝撃性、耐熱性、着色性、耐傷付き性及び剥離性に優れていることが確認できた。
また、本発明の表面保護フィルムは、上記特性を生かして、携帯電話、携帯情報端末、デスクトップ型コンピュータ用、ノート型コンピュータ用、又は車載用コンピュータ(カーナビゲーション等)用ディスプレイ、タッチパネル、テレビジョン、及び時計等のディスプレイ用パネル等に好適に使用することができる。
Claims (6)
- ジエン系ブロック重合体の水素添加物、及び、液状材料を含むエラストマー組成物からなる表面保護フィルムであって、
上記ジエン系ブロック重合体の水素添加物は、ビニル結合含量が25%未満であるブタジエン重合体ブロック(I)と、ビニル結合含量が25〜95%であるブタジエン重合体ブロック(II)とからなるジエン系ブロック重合体が水素添加されたものであり、
上記液状材料は、軟化剤であり、
上記液状材料の含有量は、重合体成分の合計100質量部に対して、400〜800質量部であり、
上記表面保護フィルムを厚さ0.5mmとした場合、そのヘイズは5%未満であり、且つ全光線透過率は90%以上であることを特徴とする表面保護フィルム。 - 上記軟化剤が鉱物油系軟化剤である請求項1に記載の表面保護フィルム。
- 上記エラストマー組成物の少なくとも一部が架橋されている請求項1又は2に記載の表面保護フィルム。
- 上記エラストマー組成物は、着色剤を含む請求項1乃至3のいずれかに記載の表面保護フィルム。
- 本表面保護フィルムの一面に粘着層が更に形成された請求項1乃至4のいずれかに記載の表面保護フィルム。
- 携帯電話、携帯情報端末、デスクトップ型コンピュータ用ディスプレイ、ノート型コンピュータ、車載用コンピュータ、タッチパネル、テレビジョン及び時計用である請求項1乃至5のいずれかに記載の表面保護フィルム。