JP3774400B2 - Process for producing ethylene-vinyl acetate copolymer resin emulsion - Google Patents
Process for producing ethylene-vinyl acetate copolymer resin emulsion Download PDFInfo
- Publication number
- JP3774400B2 JP3774400B2 JP2001371909A JP2001371909A JP3774400B2 JP 3774400 B2 JP3774400 B2 JP 3774400B2 JP 2001371909 A JP2001371909 A JP 2001371909A JP 2001371909 A JP2001371909 A JP 2001371909A JP 3774400 B2 JP3774400 B2 JP 3774400B2
- Authority
- JP
- Japan
- Prior art keywords
- emulsion
- vinyl acetate
- ethylene
- polymerization
- acetate copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【0001】
【発明の属する技術分野】
本発明は、乳化重合コントロール性に優れ、しかもホルムアルデヒド、アセトアルデヒド等のアルデヒド化合物をほとんどまたはまったく含有しない環境負荷の少ないエチレン−酢酸ビニル共重合体系樹脂エマルジョンの製造方法に関する。
【0002】
【従来の技術】
従来、ポリビニルアルコール(以下、PVAと略記することがある)を保護コロイドとするポリ酢酸ビニル系樹脂エマルジョンは紙用、木工用およびプラスチック用などの各種接着剤、含浸紙用および不織製品用などの各種バインダー、混和剤、打継ぎ材、塗料、紙加工および繊維加工、壁紙などの分野で広く用いられている。
PVAを保護コロイドとするポリ酢酸ビニル系樹脂エマルジョンの一種であるエチレン−酢酸ビニル共重合体系樹脂エマルジョンの重合には、重合安定性、エマルジョンの耐水性などの観点から、過酸化水素が広く用いられ、過酸化水素とのレドックス反応が鋭敏であることから、ソジウムホルムアルデヒドスルホキシレート(通称ロンガリット、以下ロンガリットと記述する)が頻用されてきた。しかし、ロンガリットは分解時にホルムアルデヒドを発生するため、得られるエマルジョン中にホルムアルデヒドが含まれるという重大な問題点を有しており、昨今の環境問題から、ロンガリットの使用が忌避されている。
このような状況下、未反応酢酸ビニルモノマーを低減するためには、重合開始剤、および重合条件を再構築することが不可欠となっている。特開2001−163910公報ではエリソルビン酸類、アスコルビン酸類を還元剤として用いることでノンホルムアルデヒド化しうる旨が報告されているが、酢酸ビニルモノマーの加水分解に由来するアセトアルデヒドは依然として系中に含まれているのが現状であった。
【0003】
【発明が解決しようとする課題】
本発明は、このような事情のもとで乳化重合コントロール性に優れ、しかも環境負荷の少ないエチレン−酢酸ビニル共重合体系樹脂エマルジョンの製造方法を提供することを目的とするものである。
【0004】
【課題を解決するための手段】
本発明者らは、前記の好ましい性質を有するエチレン−酢酸ビニル共重合体系樹脂エマルジョンの製造方法を開発すべく鋭意研究を重ねた結果、けん化度70モル%以上のビニルアルコール系重合体を分散剤として、エチレンおよび酢酸ビニルを乳化重合する際に、過酸化水素と酒石酸、エリソルビン酸、L−アスコルビン酸およびこれらの金属塩から選ばれる少なくとも一種の化合物とからなるレドックス系重合開始剤を用い、鉄化合物を添加して乳化重合し、乳化重合後に無機系還元剤を添加するエチレン−酢酸ビニル共重合体系樹脂エマルジョンの製造方法を提供することによって、上記目的が達成されることを見出した。
また、上記レドックス系重合開始剤として、過酸化水素と酒石酸および/または酒石酸ナトリウムとからなるレドックス系重合開始剤を使用することにより、上記目的がより好適に達成されることを見出した。
【0005】
【発明の実施の形態】
本発明のエチレン−酢酸ビニル共重合体系樹脂エマルジョンの製造方法において、分散剤として使用する、けん化度70モル%以上のビニルアルコール系重合体(以下、PVA系重合体と略記する場合がある)は、常法により、ビニルエステル系重合体をけん化することにより得ることができる。
【0006】
また、該分散剤として使用するPVA系重合体は、本発明の目的を損なわない範囲で共重合可能なエチレン性不飽和単量体を共重合したものでも良い。このようなエチレン性不飽和単量体としては、例えば、エチレン、プロピレン、イソブチレンなどのα−オレフィン、アクリル酸、メタクリル酸、フマル酸、(無水)マレイン酸、イタコン酸、アクリロニトリル、メタクリロニトリル、アクリルアミド、メタクリルアミド、トリメチル−(3−アクリルアミド−3−ジメチルプロピル)−アンモニウムクロリド、アクリルアミド−2−メチルプロパンスルホン酸およびそのナトリウム塩、エチルビニルエーテル、ブチルビニルエーテル、N−ビニルピロリドン、塩化ビニル、臭化ビニル、フッ化ビニル、塩化ビニリデン、フッ化ビニリデン、テトラフルオロエチレン、ビニルスルホン酸ナトリウム、アリルスルホン酸ナトリウムなどが挙げられる。
また、上記分散剤としては、チオール酢酸、メルカプトプロピオン酸などのチオール化合物の存在下で、酢酸ビニルを重合するか、または酢酸ビニルと上記エチレン性不飽和単量体とを共重合し、それをけん化することによって得られる末端変性物を用いることもできる。
【0007】
本発明の水性エマルジョンの分散剤として使用するPVA系重合体は、けん化度が、70モル%以上であることが必要であり、より好ましくは、80モル%以上、さらに好ましくは85モル%以上である。けん化度が70モル%未満の場合には、 PVA系重合体本来の性質である水溶性が低下するため乳化重合コントロール性が低下する場合がある。また本発明の目的を達成するためには該PVA系重合体の重合度は、100〜8000の範囲が好ましく、300〜3000がより好ましい。
【0008】
分散剤として使用するPVA系重合体の使用量については特に制限はないが、分散質(エチレン−酢酸ビニル共重合体系樹脂)100重量部に対して好ましくは2〜15重量部、より好ましくは3〜10重量部の範囲である。該使用量が2重量部未満および15重量部を越える場合には、乳化重合コントロール性が低下することがある。
【0009】
本発明においては、乳化重合時に単量体としてエチレンおよび酢酸ビニルを主に使用するが、本発明の目的を損なわない範囲で、エチレン性不飽和単量体および/またはジエン系単量体を共重合しても構わない。このような単量体としては、プロピレン、イソブチレンなどのα−オレフィン、塩化ビニル、フッ化ビニル、ビニリデンクロリド、ビニリデンフルオリドなどのハロゲン化オレフィン、アクリル酸、アクリル酸メチル、アクリル酸エチル、アクリル酸ブチル、アクリル酸2−エチルヘキシル、アクリル酸ドデシル、アクリル酸2−ヒドロキシエチルなどのアクリル酸およびそのエステル、メタクリル酸、メタクリル酸メチル、メタクリル酸エチル、メタクリル酸ブチル、メタクリル酸2−エチルヘキシル、メタクリル酸ドデシル、メタクリル酸2−ヒドロキシエチルなどのメタクリル酸およびそのエステル、アクリル酸ジメチルアミノエチル、メタクリル酸ジメチルアミノエチルおよびこれらの四級化物、さらには、アクリルアミド、メタクリルアミド、N−メチロールアクリルアミド、N,N−ジメチルアクリルアミド、アクリルアミド−2−メチルプロパンスルホン酸およびそのナトリウム塩などのアクリルアミド系単量体、スチレン、α−メチルスチレン、p−スチレンスルホン酸およびそのナトリウム、カリウム塩などのスチレン系単量体、その他N−ビニルピロリドンなど、また、ブタジエン、イソプレン、クロロプレンなどのジエン系単量体、さらにはトリアリルシアヌレート、トリアリルイソシアヌレート、ジアリルフタレートなどの多官能性単量体が挙げられる。
分散質を構成する重合体におけるエチレンの含有量は、5〜50重量%が好ましく、さらに好ましくは7〜40重量%、最適には10〜30重量%である。
【0010】
本発明の製造方法では、重合開始剤として過酸化水素と酒石酸、エリソルビン酸、アスコルビン酸およびこれらの金属塩から選ばれる少なくとも一種の化合物とからなるレドックス系重合開始剤を用いる。酒石酸としては右旋性のL(+)酒石酸、左旋性のD(−)酒石酸、これらの対掌体のラセミ化合物であるDL酒石酸があり、特に制限されないが、これらの中でもL(+)酒石酸を用いた場合、乳化重合コントロール性が顕著に向上する。また、またこれらの金属塩を用いることも可能であり、金属の種類は特に制限されないが、酒石酸ナトリウム、エリソルビン酸ナトリウム、アスコルビン酸ナトリウムが好適に用いられる。これらの中でもL(+)酒石酸ナトリウムが好ましく用いられる。L(+)酒石酸ナトリウムを用いた場合、上記利点に加えて、乳化重合時にpH調整を行わない場合でも重合コントロール性に優れ、さらには乳化重合後通常行われるアンモニア、苛性ソーダ等のアルカリによるpH調整も不要となる長所がある。
過酸化水素の使用量は、全単量体100重量部に対し0.01〜2重量部であることが好適であり、さらに好適には0.02〜0.15重量部である。
【0011】
過酸化水素と、酒石酸、エリソルビン酸、アスコルビン酸およびこれらの金属塩から選ばれる少なくとも一種の化合物との使用割合は特に制限されないが、通常過酸化水素100重量部に対して、上記化合物を50〜200重量部、好ましくは70〜180重量部、より好ましくは80〜170重量部である。上記化合物をこの範囲で使用することにより、乳化重合コントロール性が良好となる。該レドックス系重合開始剤の量は、未反応酢酸ビニルモノマーが5重量%になるまでに用いる量を示す。
【0012】
本発明の製造方法では、乳化重合系のpHを3〜7に調整することが好適であり、さらに好ましくは4〜6に調整する。pHをこの範囲に調整することにより、乳化重合コントロール性が良好となる。
乳化重合系のpHの調整方法は特に制限されず、任意の緩衝剤を用いることが可能であるが、通常、酢酸ナトリウム、酢酸/酢酸ナトリウム系、水酸化ナトリウム、炭酸ナトリウムなどが好ましく用いられる。本発明において、乳化重合系のpHとは、重合初期から重合終了までのpHを言い、本発明においては重合系のどの時点においてもpHが3〜7にあることが好適である。
【0013】
本発明の製造方法では、乳化重合系に鉄化合物を添加することが必須である。鉄化合物としては特に制限されないが、塩化第一鉄、硫酸第一鉄、塩化第二鉄、硝酸第二鉄、硫酸第二鉄から選ばれる少なくとも1種の鉄化合物が好ましく用いられ、中でも塩化第一鉄、硫酸第一鉄が特に好ましく用いられる。
【0014】
鉄化合物の使用量は特に制限されないが、通常全単量体に対して1〜100ppm、より好ましくは5〜50ppmである。鉄化合物をこの範囲で使用することにより、着色が少なく、乳化重合コントロール性も良好となる。
【0015】
前記レドックス系重合開始剤の添加方法は特に制限されない。過酸化水素は通常の乳化重合で行われる方法、すなわち、重合開始初期にショットで添加する方法、重合中に逐次的に添加する方法などが挙げられる。酒石酸、エリソルビン酸、アスコルビン酸およびこれらの金属塩から選ばれる少なくとも一種の化合物は、乳化重合初期に全量を添加して用いても良いし、乳化重合中に逐次的に添加する方法でも構わないが、酒石酸および/またはその金属塩(とくにナトリウム塩)は全量を乳化重合初期に添加して用い、エリソルビン酸、アスコルビン酸および/またはその金属塩(とくにナトリウム塩)は逐次的に添加して用いるのが好適である。鉄化合物の添加方法も特に制限されないが、通常、乳化重合初期に全量を添加して用いる。
【0016】
本発明の製造方法では、無機系還元剤を乳化重合後に添加することが必須である。ここで乳化重合後とは、重合系において未反応の酢酸ビニルモノマー量が5重量%以下、好ましくは4重量%以下になった時点をいう。好適な無機系還元剤の添加時期は、乳化重合終了後、脱エチレン操作を行う前あるいは後である。
無機系還元剤としては特に制限されないが、亜硫酸塩類が好ましく用いられる。亜硫酸塩類としては、亜硫酸ナトリウム、亜硫酸カリウム、亜硫酸アルミニウム、亜硫酸アンモニウム、亜硫酸亜鉛、亜硫酸カルシウム、亜硫酸マグネシウム、亜硫酸クロム、亜硫酸水素ナトリウム、亜硫酸水素アンモニウム、亜硫酸水素カルシウム、亜硫酸水素カリウム、ピロ亜硫酸アンモニウム、ピロ亜硫酸ナトリウム、ピロ亜硫酸カリウムなどが挙げられる。これらの中でも亜硫酸水素ナトリウム、ピロ亜硫酸ナトリウム、亜硫酸水素アンモニウムなどが好ましく用いられる。
【0017】
無機系還元剤の添加量は特に制限されないが、通常、重合後のエマルジョン固形分100重量部に対して、0.01〜10重量部、好ましくは0.02〜5重量部、より好ましくは0.03〜3重量部である。無機系還元剤をこの範囲で使用することにより、エマルジョン中のアルデヒド化合物の残存量を低減させることができ、また得られるエマルジョンの臭気を低減させることができる。
【0018】
本発明の製造方法では、必要に応じて、重合系中の未反応酢酸ビニルモノマー量を低減する目的でヒドロパーオキサイド類を添加しても構わない。ヒドロパーオキサイド類の添加時期は特に限定されないが、通常、重合後半すなわち残存酢酸ビニルモノマーが10重量%以下、好ましくは5重量%以下になってから添加される。この時点でヒドロパーオキサイド類を添加することにより、着色が少なく、乳化重合コントロール性も良好となる。
ヒドロパーオキサイド類としては、t−ブチルヒドロパーオキサイド、キュメンヒドロパーオキサイド、ジイソプロピルベンゼンヒドロパーオキサイド、p−メンタンヒドロパーオキサイド、1,1,3,3−テトラメチルブチルヒドロパーオキサイド、過酸化水素などが挙げられ、中でもt−ブチルヒドロパーオキサイド、キュメンヒドロパーオキサイドが好ましく用いられる。
【0019】
本発明の乳化重合は、加圧下、好適には20〜70kg/cm2の加圧下に行われるが、乳化重合途中で、たとえば残存酢酸ビニル濃度が10重量%となった時点で、最初の重合圧力より5〜35kg/cm2低い圧力下、好適には10〜30kg/cm2低い圧力下に調整してエチレンの一部を放出することが好適である。
【0020】
本発明の製造方法により得られるエチレン−酢酸ビニル共重合体系樹脂エマルジョンは、エマルジョン中に含まれるホルムアルデヒド濃度が1ppm以下、アセトアルデヒド濃度が1ppm以下である。ここでエマルジョン中のホルムアルデヒド濃度及びアセトアルデヒド濃度の測定は、ガス検知管を用いて行った数値をいう。エマルジョン中に含まれるホルムアルデヒド濃度あるいはアセトアルデヒド濃度が1ppmを超える場合、いわゆるノンアルデヒドエマルジョンということは出来ず、本発明の目的を達成することができない。
【0021】
本発明の製造方法で得られるエチレン−酢酸ビニル共重合体系樹脂エマルジョンは、そのままで各種用途に用いることができるが、必要に応じ、本発明の効果を損なわない範囲で、従来公知の各種エマルジョンを添加して用いることができる。
なお、本発明に用いる分散剤としては、上記のPVA系重合体が用いられるが、必要に応じて、従来公知のアニオン性、ノニオン性あるいはカチオン性の界面活性剤や、ヒドロキシエチルセルロースなどを併用することもできる。
【0022】
本発明の製造方法により得られるエチレン−酢酸ビニル共重合体系樹脂エマルジョンは、エマルジョン中にホルムアルデヒド、アセトアルデヒドなどのアルデヒド化合物を含有せず、また臭気もほとんどないため、環境負荷の極めて少ないものであり、壁紙用ベースエマルジョン、建材特に内装用接着剤、塗料などとして好ましく用いられ、また紙管、製袋、合紙、段ボール用等の紙、パルプなどの紙加工用接着剤、一般木工等の木工用接着剤および各種プラスチック用の接着剤、含浸紙用、不織製品用のバインダー、セメントモルタル用混和剤、セメントモルタル用打継ぎ材、紙加工および繊維加工などの分野でも好適に用いられる。
【0023】
【実施例】
次に、実施例および比較例により本発明をさらに詳細に説明する。なお、以下の実施例および比較例において「部」および「%」は、特に断らない限り重量基準を意味する。また、得られたエマルジョン中のホルムアルデヒド濃度、アセトアルデヒド濃度などのエマルジョン物性、乳化重合のコントロール性などを下記の要領で評価した。
【0024】
(評価方法)
(1)ホルムアルデヒド含有量
10mlガラスバイアルにエマルジョンを0.1g採取し、40℃×1hr加温した後、ガス検知管(No.171SB:光明理化学工業製、100ml吸引)で測定。
(2)アセトアルデヒド含有量
10mlガラスバイアルにエマルジョンを0.1g採取し、40℃×1hr加温した後、ガス検知管(No.133SB:光明理化学工業製、100ml吸引)で測定。
(3)乳化重合のコントロール性
過酸化水素の添加を停止した際、速やかに重合による発熱が停止するか否か、あるいは過酸化水素の添加を開始した際、速やかに重合が進行し発熱がおこるか否かを観察し、下記の基準で評価した。すなわち、過酸化水素の添加、添加停止により、重合温度を調整し、重合温度60℃を中心として温度の振れ幅がどの程度になるかにより評価した。
◎ コントロール性非常に良好(温度の振れ幅が±1℃以内)
○ コントロール性良好(温度の振れ幅が±3℃以内)
△ コントロール性やや不良(温度の振れ幅が±5℃以内)
× コントロール不可(温度の振れ幅が±5℃以上)
(4)臭気
水性エマルジョンの臭気程度を官能試験により調べ下記の基準で評価した。
○:臭気がほとんど感じられない
△:僅かに臭気が感じられる
×:臭気が激しく感じられる
【0025】
実施例1
窒素吹き込み口、温度計、撹拌機を備えた耐圧50リットルオートクレーブにPVA−1{重合度1700、けん化度88モル%、(株)クラレ製PVA−217}を1061g、イオン交換水19440g、L(+)酒石酸8.3g、酢酸ナトリウム10g、塩化第一鉄0.4gを仕込み、95℃で完全に溶解し、その後60℃に冷却し、窒素置換を行った。水溶液のpHを確認したところpH=5.5であった。次に酢酸ビニル22360gを仕込んだ後、エチレンを45kg/cm2まで加圧して導入し、0.4%過酸化水素水溶液1000gを5時間かけて圧入し、60℃で乳化重合を行った。残存酢酸ビニル濃度が10%となったところで、エチレンを放出し、エチレン圧力20kg/cm2とし、3%過酸化水素水溶液50gを圧入し、重合を完結させた。冷却後、pHを確認したところpH=4.1であった。10%水酸化ナトリウム水溶液を230g添加しエマルジョンのpHを5.5に調整し、60メッシュのステンレス製金網を用いてろ過した。その後、エマルジョン100gに対し、亜硫酸水素ナトリウムを1g配合し、固形分濃度54.4%、エチレン含量18重量%のエチレン−酢酸ビニル共重合体系樹脂エマルジョンが得られた。評価を前述の方法により行った。結果を表1に示す。
【0026】
実施例2
実施例1においてL(+)酒石酸8.3gの代わりに、L(+)酒石酸ナトリウムを12.7g用いた他は、実施例1と同様にして乳化重合を行い、固形分濃度54.4%、エチレン含量18重量%のエチレン−酢酸ビニル共重合体系樹脂エマルジョンを得た。得られたエマルジョンの評価を実施例1と同様に行った結果を表1に併せて示す。
【0027】
実施例3
実施例1においてL(+)酒石酸8.3gの代わりに、アスコルビン酸ナトリウムを12.7g用いた他は、実施例1と同様にして乳化重合を行い、固形分濃度54.4%、エチレン含量18重量%のエチレン−酢酸ビニル共重合体系樹脂エマルジョンを得た。得られたエマルジョンの評価を実施例1と同様に行った結果を表1に併せて示す。
【0028】
比較例1
実施例1においてL(+)酒石酸の代わりにロンガリットを用いた他は、実施例1と同様にして乳化重合を行い、固形分濃度54.4%、エチレン含量18重量%のエチレン−酢酸ビニル共重合体系樹脂エマルジョンを得た。得られたエマルジョンの評価を実施例1と同様に行った結果を表1に併せて示す。
【0029】
実施例4
実施例1において亜硫酸水素ナトリウムの代わりにピロ亜硫酸ナトリウムを用いた他は、実施例1と同様にして、固形分濃度54.4%、エチレン含量18重量%のエチレン−酢酸ビニル共重合体系樹脂エマルジョンを得た。得られたエマルジョンの評価を実施例1と同様に行った結果を表1に併せて示す。
【0030】
実施例5
実施例1において亜硫酸水素ナトリウムの代わりに亜硫酸水素アンモニウムを用いた他は、実施例1と同様にして、固形分濃度54.4%、エチレン含量18重量%のエチレン−酢酸ビニル共重合体系樹脂エマルジョンを得た。得られたエマルジョンの評価を実施例1と同様に行った結果を表1に併せて示す。
【0031】
比較例2
実施例1において塩化第一鉄を用いなかった他は、実施例1と同様にして乳化重合を試みたが、重合のコントロール性が乏しく危険であったため途中で中止した。
【0032】
比較例3
実施例1において亜硫酸水素ナトリウムを用いなかった他は、実施例1と同様にして、固形分濃度54.4%、エチレン含量18重量%のエチレン−酢酸ビニル共重合体系樹脂エマルジョンを得た。得られたエマルジョンの評価を実施例1と同様に行った結果を表1に併せて示す。
なお、表1中のEmはエマルジョンを示す。
【0033】
【表1】
【0034】
【発明の効果】
本発明の製造方法は、乳化重合コントロール性に優れ、また得られるエチレン−酢酸ビニル共重合体系樹脂エマルジョンは、エマルジョン中にホルムアルデヒド、アセトアルデヒドなどのアルデヒド化合物をほとんどまたはまったく含有せず、また臭気もほとんどないため、環境負荷が少ない。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a method for producing an ethylene-vinyl acetate copolymer resin emulsion that has excellent emulsion polymerization controllability and contains little or no aldehyde compounds such as formaldehyde and acetaldehyde and has a low environmental impact.
[0002]
[Prior art]
Conventionally, polyvinyl acetate resin emulsions using polyvinyl alcohol (hereinafter sometimes abbreviated as PVA) as a protective colloid are various adhesives for paper, woodwork and plastic, impregnated paper and non-woven products. Are widely used in the fields of various binders, admixtures, jointing materials, paints, paper and fiber processing, wallpaper, and the like.
Hydrogen peroxide is widely used for the polymerization of ethylene-vinyl acetate copolymer resin emulsion, which is a kind of polyvinyl acetate resin emulsion using PVA as protective colloid, from the viewpoint of polymerization stability and water resistance of the emulsion. Sodium formaldehyde sulfoxylate (commonly referred to as Rongalite, hereinafter referred to as Rongalite) has been frequently used because of its sensitive redox reaction with hydrogen peroxide. However, since longgarit generates formaldehyde at the time of decomposition, it has a serious problem that formaldehyde is contained in the resulting emulsion, and the use of longgarit is avoided due to recent environmental problems.
Under such circumstances, in order to reduce the unreacted vinyl acetate monomer, it is essential to reconstruct the polymerization initiator and the polymerization conditions. JP 2001-163910 discloses that erythorbic acids and ascorbic acids can be converted into non-formaldehyde by using as reducing agents, but acetaldehyde derived from hydrolysis of vinyl acetate monomer is still contained in the system. Was the current situation.
[0003]
[Problems to be solved by the invention]
Under the circumstances, an object of the present invention is to provide a method for producing an ethylene-vinyl acetate copolymer resin emulsion having excellent emulsion polymerization controllability and low environmental load.
[0004]
[Means for Solving the Problems]
As a result of intensive studies to develop a method for producing an ethylene-vinyl acetate copolymer resin emulsion having the above-mentioned preferable properties, the present inventors have obtained a vinyl alcohol polymer having a saponification degree of 70 mol% or more as a dispersant. In the emulsion polymerization of ethylene and vinyl acetate, a redox polymerization initiator composed of hydrogen peroxide and at least one compound selected from tartaric acid, erythorbic acid, L-ascorbic acid and metal salts thereof is used. It has been found that the above object can be achieved by providing a method for producing an ethylene-vinyl acetate copolymer resin emulsion in which a compound is added, emulsion polymerization is performed, and an inorganic reducing agent is added after the emulsion polymerization.
Moreover, it discovered that the said objective was achieved more suitably by using the redox type polymerization initiator which consists of hydrogen peroxide and tartaric acid and / or sodium tartrate as said redox type polymerization initiator.
[0005]
DETAILED DESCRIPTION OF THE INVENTION
In the method for producing an ethylene-vinyl acetate copolymer resin emulsion of the present invention, a vinyl alcohol polymer (hereinafter sometimes abbreviated as PVA polymer) having a saponification degree of 70 mol% or more used as a dispersant is used. It can be obtained by saponifying a vinyl ester polymer by a conventional method.
[0006]
The PVA polymer used as the dispersant may be a copolymer of an ethylenically unsaturated monomer that can be copolymerized within a range that does not impair the object of the present invention. Examples of such ethylenically unsaturated monomers include α-olefins such as ethylene, propylene, and isobutylene, acrylic acid, methacrylic acid, fumaric acid, (anhydrous) maleic acid, itaconic acid, acrylonitrile, methacrylonitrile, Acrylamide, methacrylamide, trimethyl- (3-acrylamido-3-dimethylpropyl) -ammonium chloride, acrylamido-2-methylpropanesulfonic acid and its sodium salt, ethyl vinyl ether, butyl vinyl ether, N-vinyl pyrrolidone, vinyl chloride, bromide Examples thereof include vinyl, vinyl fluoride, vinylidene chloride, vinylidene fluoride, tetrafluoroethylene, sodium vinyl sulfonate, and sodium allyl sulfonate.
In addition, as the dispersant, vinyl acetate is polymerized in the presence of a thiol compound such as thiol acetic acid or mercaptopropionic acid, or vinyl acetate and the ethylenically unsaturated monomer are copolymerized, A terminal modified product obtained by saponification can also be used.
[0007]
The PVA polymer used as a dispersant for the aqueous emulsion of the present invention needs to have a saponification degree of 70 mol% or more, more preferably 80 mol% or more, and still more preferably 85 mol% or more. is there. When the degree of saponification is less than 70 mol%, the water-soluble nature which is the original property of the PVA polymer is lowered, so that the emulsion polymerization controllability may be lowered. In order to achieve the object of the present invention, the degree of polymerization of the PVA polymer is preferably in the range of 100 to 8000, more preferably 300 to 3000.
[0008]
Although there is no restriction | limiting in particular about the usage-amount of the PVA type polymer used as a dispersing agent, Preferably it is 2-15 weight part with respect to 100 weight part of dispersoid (ethylene-vinyl acetate copolymer type resin), More preferably, it is 3 It is the range of -10 weight part. When the amount used is less than 2 parts by weight and exceeds 15 parts by weight, emulsion polymerization controllability may be lowered.
[0009]
In the present invention, ethylene and vinyl acetate are mainly used as monomers at the time of emulsion polymerization, but ethylenically unsaturated monomers and / or diene monomers are used as long as the object of the present invention is not impaired. You may superpose | polymerize. Examples of such monomers include α-olefins such as propylene and isobutylene, halogenated olefins such as vinyl chloride, vinyl fluoride, vinylidene chloride, and vinylidene fluoride, acrylic acid, methyl acrylate, ethyl acrylate, and acrylic acid. Acrylic acid and esters thereof such as butyl, 2-ethylhexyl acrylate, dodecyl acrylate, 2-hydroxyethyl acrylate, methacrylic acid, methyl methacrylate, ethyl methacrylate, butyl methacrylate, 2-ethylhexyl methacrylate, dodecyl methacrylate Methacrylic acid and its esters such as 2-hydroxyethyl methacrylate, dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate and quaternized products thereof, acrylamide, Acrylamide monomers such as luamide, N-methylolacrylamide, N, N-dimethylacrylamide, acrylamide-2-methylpropanesulfonic acid and its sodium salt, styrene, α-methylstyrene, p-styrenesulfonic acid and its sodium, Styrene monomers such as potassium salts, other N-vinyl pyrrolidones, etc., diene monomers such as butadiene, isoprene and chloroprene, and polyfunctionals such as triallyl cyanurate, triallyl isocyanurate and diallyl phthalate Ionic monomers.
The ethylene content in the polymer constituting the dispersoid is preferably 5 to 50% by weight, more preferably 7 to 40% by weight, and most preferably 10 to 30% by weight.
[0010]
In the production method of the present invention, a redox polymerization initiator composed of hydrogen peroxide and at least one compound selected from tartaric acid, erythorbic acid, ascorbic acid, and metal salts thereof is used as the polymerization initiator. Tartaric acid includes dextrorotatory L (+) tartaric acid, levorotatory D (-) tartaric acid, and DL tartaric acid which is a racemic compound of these enantiomers, and is not particularly limited, but among these, L (+) tartaric acid When is used, emulsion polymerization controllability is remarkably improved. These metal salts can also be used, and the type of metal is not particularly limited, but sodium tartrate, sodium erythorbate, and sodium ascorbate are preferably used. Among these, L (+) sodium tartrate is preferably used. When L (+) sodium tartrate is used, in addition to the above-mentioned advantages, even when pH adjustment is not performed at the time of emulsion polymerization, it is excellent in polymerization control property, and furthermore, pH adjustment by alkali such as ammonia or caustic soda that is usually performed after emulsion polymerization There is also an advantage that becomes unnecessary.
The amount of hydrogen peroxide used is preferably 0.01 to 2 parts by weight, more preferably 0.02 to 0.15 parts by weight with respect to 100 parts by weight of the total monomers.
[0011]
The use ratio of hydrogen peroxide and at least one compound selected from tartaric acid, erythorbic acid, ascorbic acid and metal salts thereof is not particularly limited, but the above compound is usually added in an amount of 50 to 100 parts by weight per 100 parts by weight of hydrogen peroxide. 200 parts by weight, preferably 70 to 180 parts by weight, more preferably 80 to 170 parts by weight. By using the above compound in this range, the emulsion polymerization controllability is improved. The amount of the redox polymerization initiator indicates the amount used until the unreacted vinyl acetate monomer reaches 5% by weight.
[0012]
In the production method of the present invention, it is suitable to adjust the pH of the emulsion polymerization system to 3 to 7, and more preferably to 4 to 6. By adjusting the pH within this range, the emulsion polymerization controllability is improved.
The method for adjusting the pH of the emulsion polymerization system is not particularly limited, and any buffering agent can be used. Usually, sodium acetate, acetic acid / sodium acetate system, sodium hydroxide, sodium carbonate and the like are preferably used. In the present invention, the pH of the emulsion polymerization system refers to the pH from the initial stage of polymerization to the end of the polymerization. In the present invention, the pH is preferably 3 to 7 at any point in the polymerization system.
[0013]
In the production method of the present invention, it is essential to add an iron compound to the emulsion polymerization system. The iron compound is not particularly limited, but at least one iron compound selected from ferrous chloride, ferrous sulfate, ferric chloride, ferric nitrate, and ferric sulfate is preferably used. Ferrous iron and ferrous sulfate are particularly preferably used.
[0014]
Although the usage-amount of an iron compound is not restrict | limited, Usually, it is 1-100 ppm with respect to all the monomers, More preferably, it is 5-50 ppm. By using an iron compound in this range, there is little coloring and emulsion polymerization controllability becomes good.
[0015]
The method for adding the redox polymerization initiator is not particularly limited. Examples of the hydrogen peroxide include a method that is performed by usual emulsion polymerization, that is, a method that is added in a shot at the beginning of polymerization, a method that is sequentially added during polymerization, and the like. At least one compound selected from tartaric acid, erythorbic acid, ascorbic acid, and metal salts thereof may be used by adding the total amount at the initial stage of emulsion polymerization, or may be a method of sequentially adding during emulsion polymerization. , Tartaric acid and / or metal salts thereof (especially sodium salts) are added in the initial stage of emulsion polymerization, and erythorbic acid, ascorbic acid and / or metal salts thereof (especially sodium salts) are added in sequence. Is preferred. The method for adding the iron compound is not particularly limited, but the total amount is usually added at the initial stage of emulsion polymerization.
[0016]
In the production method of the present invention, it is essential to add an inorganic reducing agent after emulsion polymerization. Here, the term “after emulsion polymerization” refers to a point in time when the amount of unreacted vinyl acetate monomer in the polymerization system is 5% by weight or less, preferably 4% by weight or less. A suitable addition time of the inorganic reducing agent is after the completion of the emulsion polymerization and before or after the de-ethylene removal operation.
The inorganic reducing agent is not particularly limited, but sulfites are preferably used. Sulphites include sodium sulfite, potassium sulfite, aluminum sulfite, ammonium sulfite, zinc sulfite, calcium sulfite, magnesium sulfite, chromium sulfite, sodium hydrogen sulfite, ammonium hydrogen sulfite, calcium hydrogen sulfite, potassium hydrogen sulfite, ammonium pyrosulfite, pyropyro Examples thereof include sodium sulfite and potassium pyrosulfite. Among these, sodium hydrogen sulfite, sodium pyrosulfite, ammonium hydrogen sulfite and the like are preferably used.
[0017]
The addition amount of the inorganic reducing agent is not particularly limited, but is usually 0.01 to 10 parts by weight, preferably 0.02 to 5 parts by weight, and more preferably 0 to 100 parts by weight of the emulsion solid content after polymerization. 0.03 to 3 parts by weight. By using the inorganic reducing agent within this range, the residual amount of the aldehyde compound in the emulsion can be reduced, and the odor of the resulting emulsion can be reduced.
[0018]
In the production method of the present invention, if necessary, hydroperoxides may be added for the purpose of reducing the amount of unreacted vinyl acetate monomer in the polymerization system. The timing of addition of hydroperoxides is not particularly limited, but it is usually added after the latter half of the polymerization, that is, when the residual vinyl acetate monomer is 10% by weight or less, preferably 5% by weight or less. By adding hydroperoxides at this time, there is little coloring and emulsion polymerization controllability is improved.
Hydroperoxides include t-butyl hydroperoxide, cumene hydroperoxide, diisopropylbenzene hydroperoxide, p-menthane hydroperoxide, 1,1,3,3-tetramethylbutyl hydroperoxide, hydrogen peroxide Among them, t-butyl hydroperoxide and cumene hydroperoxide are preferably used.
[0019]
The emulsion polymerization of the present invention is carried out under pressure, preferably 20 to 70 kg / cm 2 , but during the emulsion polymerization, for example, when the residual vinyl acetate concentration becomes 10% by weight, the first polymerization is performed. It is preferable that a part of ethylene is released under a pressure lower than the pressure by 5 to 35 kg / cm 2 , preferably 10 to 30 kg / cm 2 .
[0020]
The ethylene-vinyl acetate copolymer resin emulsion obtained by the production method of the present invention has a formaldehyde concentration contained in the emulsion of 1 ppm or less and an acetaldehyde concentration of 1 ppm or less. Here, the measurement of the formaldehyde concentration and the acetaldehyde concentration in the emulsion refers to numerical values obtained using a gas detector tube. When the formaldehyde concentration or acetaldehyde concentration contained in the emulsion exceeds 1 ppm, it cannot be a so-called non-aldehyde emulsion, and the object of the present invention cannot be achieved.
[0021]
The ethylene-vinyl acetate copolymer resin emulsion obtained by the production method of the present invention can be used for various applications as it is, but if necessary, various conventionally known emulsions can be used as long as the effects of the present invention are not impaired. It can be added and used.
As the dispersant used in the present invention, the above PVA polymer is used. If necessary, a conventionally known anionic, nonionic or cationic surfactant, hydroxyethyl cellulose, or the like is used in combination. You can also.
[0022]
The ethylene-vinyl acetate copolymer resin emulsion obtained by the production method of the present invention does not contain aldehyde compounds such as formaldehyde and acetaldehyde in the emulsion and has almost no odor, and therefore has very little environmental impact. Base emulsion for wallpaper, adhesives for interior materials, especially interior materials, paints, etc., paper tube, bag making, interleaf, paper for cardboard, paper processing adhesive for pulp, woodwork such as general woodwork It is also suitably used in the fields of adhesives and adhesives for various plastics, binders for impregnated paper and non-woven products, admixtures for cement mortar, joint materials for cement mortar, paper processing and fiber processing.
[0023]
【Example】
Next, the present invention will be described in more detail with reference to examples and comparative examples. In the following examples and comparative examples, “parts” and “%” mean weight basis unless otherwise specified. Further, emulsion physical properties such as formaldehyde concentration and acetaldehyde concentration in the obtained emulsion, controllability of emulsion polymerization, and the like were evaluated in the following manner.
[0024]
(Evaluation methods)
(1) Formaldehyde content 0.1 g of the emulsion was collected in a 10 ml glass vial, heated at 40 ° C. × 1 hr, and then measured with a gas detector tube (No. 171SB: manufactured by Komyo Chemical Co., Ltd., 100 ml suction).
(2) Acetaldehyde content 0.1 g of the emulsion was collected in a 10 ml glass vial, heated at 40 ° C. for 1 hr, and then measured with a gas detector tube (No. 133SB: 100 ml suction manufactured by Kokariri Chemical Industry).
(3) Controllability of emulsion polymerization When the addition of hydrogen peroxide is stopped, whether or not the heat generation due to the polymerization stops immediately, or when the addition of hydrogen peroxide is started, the polymerization proceeds rapidly and the heat generation occurs. Whether or not was evaluated according to the following criteria. That is, the polymerization temperature was adjusted by adding and stopping the addition of hydrogen peroxide, and the evaluation was made based on how much the temperature fluctuation centered around the polymerization temperature of 60 ° C.
◎ Very good controllability (temperature fluctuation is within ± 1 ℃)
○ Good controllability (temperature fluctuation range is within ± 3 ℃)
△ Somewhat poor controllability (temperature fluctuation range is within ± 5 ℃)
× Not controllable (temperature fluctuation is ± 5 ° C or more)
(4) Odor The odor level of the aqueous emulsion was examined by a sensory test and evaluated according to the following criteria.
○: Odor is hardly felt Δ: Slight odor is felt ×: Odor is felt intensely [0025]
Example 1
PVA-1 {Polymerization degree 1700, saponification degree 88 mol%, Kuraray Co., Ltd. PVA-217} 1061 g, ion-exchanged water 19440 g, L ( +) 8.3 g of tartaric acid, 10 g of sodium acetate, and 0.4 g of ferrous chloride were charged and completely dissolved at 95 ° C., then cooled to 60 ° C., and purged with nitrogen. When pH of aqueous solution was confirmed, it was pH = 5.5. Next, after charging 22360 g of vinyl acetate, ethylene was pressurized to 45 kg / cm 2 and introduced, 1000 g of 0.4% aqueous hydrogen peroxide solution was injected over 5 hours, and emulsion polymerization was performed at 60 ° C. When the residual vinyl acetate concentration reached 10%, ethylene was released, the ethylene pressure was set to 20 kg / cm 2, and 50 g of 3% hydrogen peroxide aqueous solution was injected to complete the polymerization. After cooling, the pH was confirmed to be pH = 4.1. 230 g of 10% aqueous sodium hydroxide solution was added to adjust the pH of the emulsion to 5.5, followed by filtration using a 60 mesh stainless steel wire mesh. Thereafter, 1 g of sodium hydrogen sulfite was added to 100 g of the emulsion to obtain an ethylene-vinyl acetate copolymer resin emulsion having a solid content concentration of 54.4% and an ethylene content of 18% by weight. Evaluation was carried out by the method described above. The results are shown in Table 1.
[0026]
Example 2
Emulsion polymerization was carried out in the same manner as in Example 1 except that 12.7 g of sodium L (+) tartrate was used instead of 8.3 g of L (+) tartaric acid in Example 1, and the solid content concentration was 54.4%. An ethylene-vinyl acetate copolymer resin emulsion having an ethylene content of 18% by weight was obtained. The results of evaluation of the obtained emulsion in the same manner as in Example 1 are also shown in Table 1.
[0027]
Example 3
Emulsion polymerization was carried out in the same manner as in Example 1 except that 12.7 g of sodium ascorbate was used instead of 8.3 g of L (+) tartaric acid in Example 1, the solid content concentration was 54.4%, and the ethylene content An 18 wt% ethylene-vinyl acetate copolymer resin emulsion was obtained. The results of evaluation of the obtained emulsion in the same manner as in Example 1 are also shown in Table 1.
[0028]
Comparative Example 1
Emulsion polymerization was carried out in the same manner as in Example 1 except that Rongalite was used instead of L (+) tartaric acid in Example 1, and an ethylene-vinyl acetate copolymer having a solid content concentration of 54.4% and an ethylene content of 18% by weight was obtained. A polymer resin emulsion was obtained. The results of evaluation of the obtained emulsion in the same manner as in Example 1 are also shown in Table 1.
[0029]
Example 4
An ethylene-vinyl acetate copolymer resin emulsion having a solid content of 54.4% and an ethylene content of 18% by weight was the same as in Example 1, except that sodium pyrosulfite was used instead of sodium bisulfite in Example 1. Got. The results of evaluation of the obtained emulsion in the same manner as in Example 1 are also shown in Table 1.
[0030]
Example 5
An ethylene-vinyl acetate copolymer resin emulsion having a solid content of 54.4% and an ethylene content of 18% by weight was the same as in Example 1, except that ammonium hydrogen sulfite was used instead of sodium hydrogen sulfite in Example 1. Got. The results of evaluation of the obtained emulsion in the same manner as in Example 1 are also shown in Table 1.
[0031]
Comparative Example 2
Emulsion polymerization was attempted in the same manner as in Example 1 except that ferrous chloride was not used in Example 1. However, since the polymerization control was poor and it was dangerous, it was stopped halfway.
[0032]
Comparative Example 3
An ethylene-vinyl acetate copolymer resin emulsion having a solid content concentration of 54.4% and an ethylene content of 18% by weight was obtained in the same manner as in Example 1 except that sodium bisulfite was not used in Example 1. The results of evaluation of the obtained emulsion in the same manner as in Example 1 are also shown in Table 1.
In Table 1, Em represents an emulsion.
[0033]
[Table 1]
[0034]
【The invention's effect】
The production method of the present invention is excellent in emulsion polymerization controllability, and the resulting ethylene-vinyl acetate copolymer resin emulsion contains little or no aldehyde compounds such as formaldehyde and acetaldehyde in the emulsion, and has almost no odor. Because there is no environmental impact.
Claims (4)