JP3365484B2 - 光学的記録媒体用の樹脂組成物 - Google Patents
光学的記録媒体用の樹脂組成物Info
- Publication number
- JP3365484B2 JP3365484B2 JP11642598A JP11642598A JP3365484B2 JP 3365484 B2 JP3365484 B2 JP 3365484B2 JP 11642598 A JP11642598 A JP 11642598A JP 11642598 A JP11642598 A JP 11642598A JP 3365484 B2 JP3365484 B2 JP 3365484B2
- Authority
- JP
- Japan
- Prior art keywords
- optical recording
- resin
- recording medium
- specific gravity
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
気ディスクに用いられる樹脂膜にかかり、特に、金属膜
と直接接触し、保護層や接着剤層となる樹脂膜の樹脂組
成物に関する。
込み、又は読み込み/書き込みを行う媒体として、光デ
ィスクや光磁気ディスクが用いられている。
に用いられる光ディスクでは、透明な樹脂円盤上にピッ
トを有する金属膜が形成され、ピット配列によって所定
の情報が記憶された後、金属膜表面に保護層が形成され
ており、金属膜に向け、透明な樹脂円盤側からレーザ光
を照射し、反射光を読みとっている。
分が樹脂膜を透過し、金属膜が腐食し、情報が読みとれ
なくなると寿命になることから、保護層の特性が、光デ
ィスクの寿命に大きな影響を与えるため、従来より種々
の材質が研究されている。
では、2枚の透明円盤で金属膜を挟んだ構造の光ディス
クにおいて、保護層又は接着層に用いる樹脂に、高硬度
のものを用いたものが開示されており、その結果、透湿
性が小さく、耐湿性に優れた保護層が得られると記載さ
れている。
は、金属膜の応力腐食に着目し、所定値の引張応力を有
する保護層が開示されており、耐候性に優れた媒体が得
られると記載されている。
に、保護層の特性、材質等が盛んに研究されているが、
例えば高硬度の樹脂を用いた場合、透湿度は低くなるも
のの、硬化収縮率が大きくなり、光ディスク全体が歪
み、応力腐食が発生するという問題があり、逆に、引張
応力に着目した樹脂は熱硬化型であり、紫外線硬化型の
樹脂に比べ、熱による応力が発生するおそれがある。
は、硬化収縮率、透湿度、吸水率、吸湿率を所定範囲に
した保護層が開示されており、金属膜の酸化が防止さ
れ、信頼性の高い媒体が得られると記載されているが、
それらの条件の全てを管理することは、製造工程上困難
である。
の課題を解決するために創作されたものであり、その目
的は金属膜表面に形成される保護層又は接着層に適した
樹脂を提供することにある。
録媒体の金属薄膜の腐食と、保護層や接着層に用いる樹
脂膜の材質の関係について研究したところ、腐食が少な
い樹脂膜が得られる液状オリゴマの比重は、通常用いら
れている液状オリゴマの比重よりも大きいことを見出し
た。
水性が小さいと考えられているが、高比重液状オリゴマ
はかさ高い置換基を多数有しており、それらが重合した
場合、かさ高い置換基が水分の侵入を防ぎ、透水性が小
さい樹脂膜が得られると考えられる。
を用い、樹脂組成物を構成して樹脂膜を作成し、腐食の
程度を調査したところ、1.10以上の平均比重を有す
る高比重液状オリゴマを用いると、腐食が少ない樹脂膜
が得られることを見出した。
であり、請求項1記載の発明は、基体と、前記基体上に
形成された金属膜とを有し、前記金属膜に、読み取り可
能に情報が記録された光学的記録媒体であって、前記金
属膜表面に、光重合反応に関与する光重合性硬化樹脂を
含有する樹脂組成物であって、前記光重合性硬化樹脂
は、比重が1.10以上の高比重液状オリゴマを含有す
る樹脂組成物を用いた樹脂膜が形成されたことを特徴と
する光学的記録媒体である。
マだけではなく、低比重液状オリゴマやモノマーも一緒
に用いられるが、光重合性硬化樹脂中の高比重液状オリ
ゴマの含有率は重要であり、請求項2記載の発明のよう
に、前記光重合性硬化樹脂中には、その35重量%以上
70重量%以下の範囲で前記高比重液状オリゴマを含有
させることが好ましい。含有率が少なすぎると効果がな
く、多すぎると粘度が高くなりすぎ、塗布できなくな
る。
の光学的記録媒体の樹脂組成物に用いられる高比重液状
オリゴマについては、請求項3記載の発明のように、エ
ポキシアクリレートを用いることができる。
組成物は、金属膜表面に樹脂膜を形成し、保護層や接着
層とすることができる。本発明の光学的記録媒体は、コ
ンパクトディスクのようにレーザ光を用いて読みとるも
のの他、磁気的手段を併用するものも含まれる。
共に説明する。先ず、エポキシアクリレートのうち、比
重が1.13以上の高比重の液状オリゴマA〜Dと、比
重が1.04及び1.08の通常の液状オリゴマE、F
を用い、各液状オリゴマA〜Fの50重量部に対し、第
1のモノマー(トリプロピレングリコールジアクリレー
ト)30重量部、第2のモノマー(フェノキシアクリレー
ト)20重量部、開始剤(ダロキュア1173)5重量
部、その他の成分(禁止剤等)5重量部添加し、混合して
4種類の本発明の樹脂組成物1〜4と、比較例としての
樹脂組成物5、6とを作成した。
パッタリング法により、表面にアルミニウム薄膜11
(膜厚500Å)が形成された透明なポリカーボネートか
ら成る基体11(厚さ1.2mm)を用意し、各樹脂組成
物1〜6をアルミニウム薄膜1表面にそれぞれ滴下し、
スピンコート法にて樹脂組成物層を形成した後、紫外線
を照射し(積算光量500mJ/cm2)、光硬化させ、
同図(b)に示すように、アルミニウム薄膜12表面に樹
脂膜13が形成された単盤型の光学的記録媒体10を得
た。
半分の厚さにした基体21(厚さ0.6mm)上にアルミ
ニウム薄膜22を形成し、上記樹脂組成物1〜7をアル
ミニウム薄膜22表面にそれぞれ滴下し、スピンコート
法によって樹脂組成物層を形成した後、その表面に、同
じ厚さ(0.6mm)の基体24を密着させた後、紫外線
を照射し、貼り合わせ型の光学的記録媒体20を得た。
6種類の単盤型の光学的記録媒体10と6種類の貼り合
わせ型の光学的記録媒体20を、温度80℃、相対湿度
85%の雰囲気に置き、1000時間放置した後、ピン
ホール数を測定した。また、液体の比重と硬化物の比重
により硬化収縮率(体積収縮率)を求めた。
各液状オリゴマA〜Gの比重、グレード、メーカー名と
併せて下記表に示す。
組成物1〜4用いた光学的記録媒体が本発明の実施例で
あり、他の2種類の樹脂組成物5〜6を用いた光学的記
録媒体が比較例である。上記表1から、本発明の樹脂組
成物1〜4を用いた場合、単盤型と貼り合わせ型の光学
的記録媒体の両方とも、全てピンホール数は0であり、
優れた保護特性を有する樹脂膜が形成されていることが
分かる。
た欄は、各メーカーの商標名を示しており、CN111は大
豆変成エポキシアクリレート、それ以外のものはビスフ
ェノールA型アクリレートである。メーカー名の欄中、
「サトーマー」はサトーマーカンパニーの略、「UC
B」は「UCBケミカルズコーポレーション」の略であ
り、どちらも外国法人である。
い、その含有量と、上記の第1、第2のモノマーの含有
量を変えて、2種類の本発明の樹脂組成物7、8を作成
した。また、上記高比重液状オリゴマDを用い、同様
に、その含有量と第1、第2のモノマーの含有量を変え
て本発明の樹脂組成物9、10を作成した。
組成物1〜7の場合と同様に、単盤型の光学的記録媒体
と貼り合わせ型の光学的記録媒体を作成した。
で1000時間放置し、ピンホール数を測定した。その
結果を下記表2に示す。
10を用いた場合にはピンホール数は少なく、保護特性
の高い樹脂膜が形成されていることが分かる。樹脂組成
物10を用いた場合には、高比重の液状オリゴマDを用
いているのに、他の樹脂組成物1〜9に比べてピンホー
ル数が多い。その原因は、液状オリゴマDの含有率が小
さい点にある。この樹脂組成物10の測定結果から、本
発明では、高比重液状オリゴマを35%以上含有させる
ことが望ましいことが分かる。
の良好な樹脂膜を形成できるので、長寿命の光学的記録
媒体を得ることができる。
製造工程を説明するための図
めの図
Claims (3)
- 【請求項1】基体と、前記基体上に形成された金属膜と
を有し、前記金属膜に、読み取り可能に情報が記録され
た光学的記録媒体であって、 前記金属膜表面に、光重合反応に関与する光重合性硬化
樹脂を含有する樹脂組成物であって、前記光重合性硬化
樹脂は、比重が1.10以上の高比重液状オリゴマを含
有する樹脂組成物を用いた樹脂膜が形成されたことを特
徴とする光学的記録媒体。 - 【請求項2】前記光重合性硬化樹脂中には、前記高比重
液状オリゴマが、35重量%以上70重量%以下の範囲
で含有された請求項1記載の光学的記録媒体。 - 【請求項3】前記高比重液状オリゴマがエポキシアクリ
レートである請求項1又は請求項2のいずれか1項記載
の光学的記録媒体。