JP3305414B2 - How to use demolition concrete waste - Google Patents
How to use demolition concrete wasteInfo
- Publication number
- JP3305414B2 JP3305414B2 JP12543493A JP12543493A JP3305414B2 JP 3305414 B2 JP3305414 B2 JP 3305414B2 JP 12543493 A JP12543493 A JP 12543493A JP 12543493 A JP12543493 A JP 12543493A JP 3305414 B2 JP3305414 B2 JP 3305414B2
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- aggregate
- limestone
- cement
- crushed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、コンクリート構造物を
解体した際に発生するコンクルートガラと称されている
解体コンクリート廃材の利用方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of using demolition concrete waste called "concrete glass" generated when a concrete structure is demolished.
【０００２】[0002]
【従来の技術】コンクリートガラと称されている解体コ
ンクリート廃材は、大部分は廃棄物として埋立処分され
ているが、最近は建設副産物として再利用する必要性の
認識が高まってきているが、この種解体コンクリート廃
材の利用方法としては、簡易な敷き砂利用にまたは埋立
用に一部使用されるにとどまり、効果的な利用法が実現
されていない。そこで、近時は、解体コンクリート廃材
を骨材とセメント硬化物とに分けて骨材を再度骨材とし
て利用し、セメント硬化物は乾燥微粉砕して再生セメン
トとなす提案がなされている。2. Description of the Related Art Demolition concrete waste, which is called concrete waste, is mostly disposed of as landfill waste. Recently, however, it has been recognized that it is necessary to reuse it as a construction by-product. As the method of using the seed dismantled concrete waste material, it is only used for simple spread sand or partially used for landfill, and an effective use method has not been realized. Therefore, recently, a proposal has been made to separate the dismantled concrete waste into aggregate and hardened cement, reuse the aggregate as aggregate, and dry and finely pulverize the hardened cement into recycled cement.
【０００３】[0003]
【発明が解決使用とする課題】しかし、上記従来の骨材
を分離して再利用する方法は、骨材とセメント硬化物と
の分離に手数と費用がかかり高価となる課題を有すると
ともに、分離したセメント硬化物による再生セメント
は、水和反応が完了したものを多く含んでいること、年
月を経過しているので無活性物質となっていることから
強度の低い低品質のコンクリートしか得られないという
課題を有している。However, the above-mentioned conventional method for separating and reusing aggregates has the problem that the separation of the aggregates from the hardened cement is troublesome, expensive and expensive. Recycled cement made from hardened cement contains a lot of materials that have completed the hydration reaction, and since it has passed the years, it is an inactive substance, so only low-quality, low-strength concrete can be obtained. There is a problem that there is no.
【０００４】そこで本発明は上記課題を解決すべくなさ
れたもので、再利用をし易いように、予め、源コンクリ
ートの製造時に細粗骨材にセメント原料と同系列の石灰
岩を使用することで再生し易く、かつ強度低下も有効に
防げる解体コンクリート廃材の利用方法を提供すること
を目的としたものである。Accordingly, the present invention has been made to solve the above-mentioned problems. In order to facilitate reuse, limestone of the same series as the cement raw material is used in advance in the production of the source concrete for fine coarse aggregate. An object of the present invention is to provide a method of using demolition concrete waste material that is easy to regenerate and that can effectively prevent a decrease in strength.
【０００５】[0005]
【課題を解決するための手段】上記の目的に沿い、先述
特許請求の範囲を要旨とする本発明の構成は前述課題を
解決するために、石灰岩骨材を使用した高強度コンクリ
ートの廃材を、破砕機で破砕し、上記破砕物を１１０〜
２００℃程度で含水率１０％以下に乾燥した後、粉砕機
で粉砕して粒子径１０５μｍ以下に篩分して、コンクリ
ートのバインダー材やセメント代替品として使用するす
ることを特徴とした技術的手段を講じたものである。In order to solve the above-mentioned problems, according to the present invention, in order to solve the above-mentioned problems, a waste material of high-strength concrete using limestone aggregate is provided. Crushed by a crusher, and the crushed
A technical means characterized in that it is dried at about 200 ° C. to a water content of 10% or less, then pulverized by a pulverizer, sieved to a particle diameter of 105 μm or less, and used as a concrete binder or a cement substitute. It was taken.
【０００６】[0006]
【作用】最近のコンクリートは高性能ＡＥ減水剤の利用
によって水分量（Ｗ／Ｃ）を少なくして施工性と高強度
が達成できるようになってきた。この種のコンクリート
はセメント粒子の表面のみが水和反応してゲル化して膜
をつくる性質を有し、セメント粒子中心部には未水和物
が残存している。したがって、これを微粉砕することで
表面を水和膜で覆われた未水和物が再度水和可能な状態
となる作用を呈する。The use of a high performance AE water reducing agent has recently reduced the amount of water (W / C) in concrete and has made it possible to achieve workability and high strength. This type of concrete has the property that only the surface of the cement particles undergoes a hydration reaction to gel and form a film, and unhydrated remains in the center of the cement particles. Therefore, the unhydrated material whose surface is covered with the hydrated film can be rehydrated by pulverizing the powder.
【０００７】もっとも、上記作用は水和完了物が混入す
ることから、新しいコンクリートに比べては低品質化の
原因となり、新しいコンクリートの補充のもとに使用し
て所期の強度を得るようになすことが望ましいが、本発
明では、セメントと同系列の酸化カルシューム（Ｃａ
Ｏ），二酸化珪素（ＳｉＯ2）を多量に含む石灰岩を骨
材に使用しているため、これらが微粉砕に伴ってセメン
トと混入し、セメントの活性化低減を抑止する作用を呈
する。すなわち、上記酸化カルシューム（ＣａＯ）が無
機のセメント活性化材として作用し、初期強度を高くす
るものである。However, since the above-mentioned action involves the incorporation of the completed hydration product, it causes lower quality compared to new concrete. In the present invention, it is desirable to use calcium oxide (Ca
Since limestone containing a large amount of O) and silicon dioxide (SiO 2 ) is used as an aggregate, these limestones are mixed with cement along with the fine pulverization, and exhibit an effect of suppressing reduction in activation of cement. That is, the calcium oxide (CaO) acts as an inorganic cement activator to increase the initial strength.
【０００８】[0008]
【実施例】次に、本発明の実施例を添附図面にを参照に
説明すれば以下の通りである。まず、本発明法は石灰岩
骨材を使用した高強度コンクリートの廃材を、破砕機で
破砕する。DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments of the present invention will be described below with reference to the accompanying drawings. First, in the method of the present invention, waste material of high-strength concrete using limestone aggregate is crushed by a crusher.
【０００９】すなわち、従来骨材は代表的には川砂を使
用しているが、川砂も不足気味で海砂を洗浄したり、岩
石を砂状に粉砕したものも使用されるに至っている。そ
こで、本発明に使用するコンクリートの廃材には、再利
用の便宜性を予め考慮して、コンクリート構造物を構築
する際に骨材に石灰岩を使用しておく。この石灰岩は砂
状に破砕し、従来法でセメントと混入して使用すればよ
いが、高性能減水剤を添加（実施例としては、高性能減
水剤の添加のもとに、水分量（Ｗ／Ｃ）を５０％以下と
する。）し、ワーカビリチー、強度の確保をおこなう。That is, the conventional aggregate typically uses river sand. However, river sand has been used to wash sea sand or to crush rock into sand because the river sand tends to be insufficient. Therefore, limestone is used as an aggregate when constructing a concrete structure in consideration of the convenience of reuse of the concrete waste used in the present invention. This limestone may be crushed into sand and used by mixing it with cement by a conventional method. However, a high-performance water reducing agent is added (as an example, the water content (W / C) to 50% or less.) To secure workability and strength.
【００１０】そして、上記石灰岩の骨材を使用した高強
度コンクリートの構築物が不要になったり、耐久年数が
経過して解体する必要性が生じたら、これを従来法で解
体してコンクリートの廃材を得る。そして、このコンク
リートの廃材は、必要に応じては次工程での取扱の便宜
のために予め適宜の大きさに破砕機等で破砕しておく。
なお、ここでの破砕はコンクリート構築物を常法で解体
すると、解体現場では騒音や粉塵発生の問題もあって、
最低限運搬に支障を生じない程度に比較的大きい塊状
に、例えば、長径１〜２ｍ程度の大きさに解体されるこ
ともあるので、このように大きいコンクリートの廃材は
そのままではハンドリング等に非常に大型の装置を必要
とするので、通常のハンドリング装置によって連続的に
搬送可能な程度の大きさに破砕しておく。[0010] When a high-strength concrete structure using the limestone aggregate becomes unnecessary, or when it becomes necessary to disassemble it after the end of its durability, this is dismantled by a conventional method to remove concrete waste material. obtain. Then, if necessary, the waste material of the concrete is crushed in advance by a crusher or the like to an appropriate size for convenience of handling in the next step.
In addition, the crushing here is when the concrete structure is dismantled by the ordinary method, there is a problem of noise and dust generation at the dismantling site,
At a minimum, it may be dismantled into a relatively large lump that does not impede transportation, for example, to a length of about 1 to 2 m. Since a large device is required, the material is crushed to a size that can be continuously transported by a normal handling device.
【００１１】そして、上記破砕物を１１０〜２００℃程
度で乾燥した後、粉砕機で粉砕して粒子径１０５μｍ以
下に篩分して、コンクリートのバインダー材やセメント
代替品として使用するする。The crushed product is dried at about 110 to 200 ° C., crushed by a crusher and sieved to a particle diameter of 105 μm or less, and used as a concrete binder or a cement substitute.
【００１２】ここで乾燥するのは、水分を含んでいる
と、この水分が物理的力の伝達を阻害して粉砕の支障と
なるのと、粉砕によって新たに暴露した未水和物を水和
するおそれを有するからである。特に、石灰岩粒子は含
水し易い性質を有し、廃材として搬入されるコンクリー
トは解体時の粉塵防止のために注水してある場合がが多
いので付着水もしくは侵入水も相当に存在している。し
たがって、１００〜２００℃で含水量１０％以下となし
ておく。What is dried here is that, if water is contained, the water impedes the transmission of physical force and hinders the pulverization. This is because there is a risk of doing so. In particular, limestone particles have a property of being easily hydrated, and concrete carried in as waste material is often injected with water in order to prevent dust at the time of dismantling, so that considerable amount of attached water or intrusion water also exists. Therefore, the water content is set to 10% or less at 100 to 200 ° C.
【００１３】なお、乾燥には従来加熱トオネル等の従来
公知の装置が利用でき、乾燥に先だって効率的な乾燥を
行う目的で、コンクリートの廃材を一定の大きさ以下に
さらに破砕しておくことも無論差し支えなく、本実施例
では最大径２０ｃｍ程度のコンクリート塊を乾燥装置に
投入したが、ジョウクラッシャー等で予め最大径が数ｃ
ｍとなしてから乾燥工程を施すことが乾燥用の熱エネル
ギーを有効に利用できるものである。なお、前記した、
粉砕に際して水分が物理的力の伝達を阻害するとしたの
は微粉砕段階のことで、この程度の粗い破砕段階では水
分量の影響は無視できるものである。A conventionally known apparatus such as a conventionally heated tonel can be used for drying. For the purpose of efficient drying prior to drying, waste concrete may be further crushed to a certain size or less. Needless to say, in this embodiment, concrete mass having a maximum diameter of about 20 cm was put into the drying device, but the maximum diameter was several c in advance with a jaw crusher or the like.
Performing the drying step after setting m allows the thermal energy for drying to be effectively used. In addition, as described above,
It is in the pulverization stage that water impedes the transmission of physical force during pulverization, and the effect of water content can be neglected in such a coarse pulverization stage.
【００１４】そして、乾燥したコンクリート廃材は粉砕
機で粉砕するが、粉砕の効率を考慮して複数の粉砕機を
利用することが望ましく、本実施例では先ず、ジョウク
ラッシャーで粗く砕き（乾燥前にジョウクラッシャーで
破砕した場合はこの工程を省略してもよい。）、次い
で、トップグラインダーと称する粉砕機で２０ｍｍ以下
に粗粉砕し、さらにミルで微粉砕する。なお、ここでの
微粉砕は粒径をできるだけ小さくする目的でなされるも
ので、その粉砕機の方式は上記に限られるのものでない
ことは無論である。The dried concrete waste is pulverized by a pulverizer. It is preferable to use a plurality of pulverizers in consideration of the pulverization efficiency. In this embodiment, first, the pulverizer is coarsely pulverized by a jaw crusher (before drying). If crushed by a jaw crusher, this step may be omitted.) Then, the material is coarsely pulverized to 20 mm or less by a pulverizer called a top grinder, and further finely pulverized by a mill. Here, the pulverization is performed for the purpose of reducing the particle size as much as possible, and it goes without saying that the method of the pulverizer is not limited to the above.
【００１５】そして微粉砕したものは１０５μｍの篩い
装置で篩分する。この篩い装置も従来巧緻なものが使用
でき、篩い装置の上に残留した大径のコンクリートの廃
材は前の粉砕工程に再度戻すようになせばよい。The finely pulverized product is sieved with a 105 μm sieving apparatus. As the sieving apparatus, conventionally sophisticated ones can be used, and large-diameter concrete waste remaining on the sieving apparatus may be returned to the previous pulverizing step.
【００１６】比較のため、上記と同じ条件で軟質砂岩を
骨材としたコンクリートの廃材を粉砕したところ平均粒
径は２５〜２７μｍであるが、石灰岩を骨材に使用する
と平均粒径は２０〜２３μｍと小さくなり、１０５μｍ
の篩い装置に残存する割合は軟質砂岩を骨材とした場合
は約６０％であったが、石灰岩を骨材に使用すると約３
０〜３５％の残存率で石灰岩自体が軟質の岩石であるこ
とから省エネルギーで容易にセメントの廃材をを微細化
できるものであることが確認できた。For comparison, when the waste material of concrete using soft sandstone as an aggregate was pulverized under the same conditions as described above, the average particle size was 25 to 27 μm, but when limestone was used as the aggregate, the average particle size was 20 to 27 μm. 23 μm and 105 μm
The ratio remaining in the sieving apparatus was about 60% when soft sandstone was used as aggregate, but about 3% when limestone was used as aggregate.
Since the limestone itself is a soft rock with a residual rate of 0 to 35%, it was confirmed that the waste material of cement can be easily miniaturized with energy saving.
【００１７】そして、以上の様にして得られたものを再
生混合材としてコンクリート骨材として利用して、コン
クリートを作成して強度を比較したところ「図１」のよ
うになった。なお、同図ではコンクリート廃材は以下の
配合の物を使用している。 ＮＬ：普通セメントに骨材として石灰岩を使用 ＮＨ：普通セメントに骨材として硬質砂岩を使用 ＢＬ：高炉Ｂ種セメントに骨材として石灰岩を使用 ＢＨ：高炉Ｂ種セメントに骨材として硬質砂岩を使用 ＦＬ：ブライアッシュＢ種セメントに骨材として石灰岩
を使用 ＦＨ：ブライアッシュＢ種セメントに骨材として硬質砂
岩を使用 ＨＣ：普通コンクリートに減水剤を添加し骨材として石
灰岩を使用 また、試験に使用したものは全て材令２８日のものであ
る。The concrete obtained by using the thus obtained material as a recycled aggregate as a concrete aggregate and comparing the strength was as shown in FIG. 1. In the figure, the concrete waste materials used have the following composition. NL: Use limestone as aggregate for ordinary cement NH: Use hard sandstone as aggregate for ordinary cement BL: Use limestone as aggregate for blast furnace type B cement BH: Use hard sandstone as aggregate for blast furnace type B cement FL: Use limestone as an aggregate for Briash B cement. FH: Use hard sandstone as an aggregate for Briash B cement. HC: Add a water reducing agent to ordinary concrete and use limestone as aggregate. Also used for testing All that was done is 28 days old.
【００１８】したがって、「図１」の試験結果から、石
灰岩の骨材の使用が強度向上に貢献していることは明白
あり、石灰岩がバインダー機能を有するものである。Therefore, from the test results shown in FIG. 1, it is clear that the use of limestone aggregate contributes to the improvement in strength, and limestone has a binder function.
【００１９】[0019]
【発明の効果】本発明は上記のごときで、石灰岩を骨材
に使用することで、石灰岩自体が比較的軟質であるので
微粉砕が容易で、再利用し易い解体コンクリート廃材の
利用方法を提供できるものである。As described above, the present invention provides a method of using demolition concrete waste which is easy to pulverize because limestone itself is relatively soft and easy to reuse by using limestone as an aggregate. You can do it.
【００２０】また、石灰岩を骨材に使用することで、こ
の石灰岩を微粉砕することで石灰岩がバインダー機能を
発揮し、強度低下も有効に防げる解体コンクリート廃材
の利用方法を提供することができるものである。Further, by using limestone as an aggregate, it is possible to provide a method of using demolition concrete waste material in which the limestone exhibits a binder function by finely pulverizing the limestone, thereby effectively preventing a decrease in strength. It is.
【００２１】また、本発明により得られた微細粉体は土
壌の改良材、泥水のフィルター、泥水等の中和剤として
も利用できるもので、建設副産物としてのコンクリート
の廃材を多目的に利用することができる解体コンクリー
ト廃材の利用方法を提供することができるものである。The fine powder obtained by the present invention can also be used as a soil improving material, a filter for muddy water, and a neutralizing agent for muddy water. The present invention can provide a method of using demolition concrete waste material that can be used.
【図１】本発明によって得られる微細粉体をコンクリー
トに混入利用した際の比較圧縮強度試験結果を示すグラ
フである。FIG. 1 is a graph showing a comparative compressive strength test result when a fine powder obtained by the present invention is mixed and used in concrete.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 新井 光興 神奈川県大和市下鶴間2570−４ 西松建 設株式会社技術研究所内 (72)発明者 中田 善久 神奈川県大和市下鶴間2570−４ 西松建 設株式会社技術研究所内 (56)参考文献 特開 平５−238790（ＪＰ，Ａ) 特開 平３−54137（ＪＰ，Ａ) 特開 平５−170498（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) C04B 7/24 C04B 18/16 ──────────────────────────────────────────────────続 き Continuing from the front page (72) Inventor Mitsuko Arai 2570-4 Nishimatsu Construction, Shimotsuruma, Yamato-shi, Kanagawa Prefecture Inside the Technical Research Institute (72) Inventor Yoshihisa Nakata 2570-4 Shimotsurumama, Yamato-shi, Kanagawa Pref. (56) References JP-A-5-238790 (JP, A) JP-A-3-54137 (JP, A) JP-A-5-170498 (JP, A) (58) Fields surveyed ( Int.Cl. 7 , DB name) C04B 7/24 C04B 18/16
Claims (1)
ートの廃材を、破砕機で破砕し、 上記破砕物を１１０〜２００℃程度で含水率１０％以下
に乾燥した後、粉砕機で粉砕して粒子径１０５μｍ以下
に篩分して、コンクリートのバインダー材やセメント代
替品として使用するすることを特徴とした解体コンクリ
ート廃材の利用方法。1. A high-strength concrete waste material using limestone aggregate is crushed by a crusher, and the crushed material is dried at about 110 to 200 ° C. to a water content of 10% or less, and then crushed by a crusher. A method of using demolition concrete waste material, which is sieved to a particle diameter of 105 μm or less and used as a binder material for concrete or a cement substitute.