JP3253562B2 - Manufacturing method of fat-removing paper - Google Patents
Manufacturing method of fat-removing paperInfo
- Publication number
- JP3253562B2 JP3253562B2 JP14449597A JP14449597A JP3253562B2 JP 3253562 B2 JP3253562 B2 JP 3253562B2 JP 14449597 A JP14449597 A JP 14449597A JP 14449597 A JP14449597 A JP 14449597A JP 3253562 B2 JP3253562 B2 JP 3253562B2
- Authority
- JP
- Japan
- Prior art keywords
- paper
- calendered
- producing
- fat
- base paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、主として女性が化
粧する際などに顔の脂を吸収させて取り除くために用い
るのに適する脂取り紙の製造法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a grease-removing paper suitable for use in absorbing and removing facial fat, mainly when a woman makes up makeup.
【０００２】[0002]
【従来の技術】従来、化粧用の脂取り紙として箔打ち紙
が知られている。この箔打ち紙は金箔を打ち延ばす際に
金箔を挟む。そして、これらの所望枚数を一束として箔
打ち機により束面から万遍なく繰り返して叩く。このと
き、箔打ち紙はその繊維が砕けるほどに叩かれることに
より、柔軟性、平滑性、光沢が与えられる。箔打ち紙は
これら柔軟性、平滑性により脂の吸収性に優れているこ
とがわかり、高品質の化粧用脂取り紙として使用されて
いる。2. Description of the Related Art Foiled paper is conventionally known as a fat removing paper for cosmetics. This foil stamping paper sandwiches the gold leaf when the gold leaf is rolled out. Then, the desired number of sheets is bundled into a bundle and is repeatedly and uniformly beaten from the bundle surface by a foiling machine. At this time, the foiled paper is given flexibility, smoothness, and gloss by being beaten to such an extent that the fibers are broken. Foiled paper has been found to be excellent in fat absorption due to its flexibility and smoothness, and is used as a high-quality cosmetic fat removing paper.
【０００３】しかしながら、このような化粧用脂取り紙
は、箔打ちに使用した箔打ち紙の有効利用に過ぎず、自
ら供給量に限界がある。また、近年、化粧用としてのみ
ならず、清潔感等を得るために顔の脂分を取り除くため
に使用され、性別、年令の高低を問わず、使用者層が拡
がる傾向にあり、多量の脂取り紙の提供が要望されてい
る。[0003] However, such a fat removing paper for cosmetics is only an effective use of the foil stamping paper used for the foil stamping, and there is a limit in the supply amount by itself. In recent years, it has been used not only for cosmetics but also for removing facial oils to obtain a clean feeling, etc., and the gender, regardless of age, tends to expand the user base. There is a demand for the provision of greasy paper.
【０００４】そこで、近年、箔を挟むことなく、原紙の
みを束ねた状態で箔打ち機により叩いた脂取り紙が提供
されている。Therefore, in recent years, there has been provided a grease-absorbing paper obtained by tapping with a foiling machine in a state where only the base paper is bundled without sandwiching the foil.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、このよ
うな脂取り紙は、原紙のみを束状に重ねて箔打ち機によ
り叩いており、同じ種類の原紙同士が接触しているた
め、原紙の繊維が潰れ難く、しかも、光沢も得難い。し
たがって、柔軟性、平滑性を得ることができないため、
脂の吸収性に劣り、しかも、肌触りも劣り、箔打ち紙に
比べて品質において数段劣る。また、箔打ち紙は原紙の
製造時に格子、亀甲等の漉き模様を入れているが、上記
脂取り紙には漉き模様が入っていないため、箔打ち紙の
ような高級感を得ることができない。However, in such a grease-removing paper, only the base papers are piled up in a bundle and are beaten by a foiling machine, and the base papers of the same type are in contact with each other. Is difficult to crush and gloss is hard to obtain. Therefore, flexibility and smoothness cannot be obtained,
It is inferior in absorbability of fats and, furthermore, inferior in feel, and is several steps inferior in quality as compared with foil stamped paper. In addition, the foil stamped paper has a lattice pattern, a turtle shell, etc. made during the production of the base paper, but since the fat-leafed paper does not have a crepe pattern, it cannot obtain a high-grade feel like a foil stamped paper. .
【０００６】本発明は、上記のような従来の問題を解決
するものであり、箔打ち紙と同様の脂分の吸収性、光
沢、肌触り等を得ることができ、したがって、箔打ち紙
と同様の高品質を得ることができ、しかも、作業能率を
向上させることができるようにした脂取り紙の製造法を
提供し、また、上記目的に加え、所望の漉き模様を得る
ことができ、したがって、箔打ち紙と同様の外観を得る
ことができるようにした脂取り紙の製造法を提供するこ
とを目的とするものである。The present invention has been made to solve the above-mentioned conventional problems, and can obtain the same absorptivity, gloss, texture, and the like of a fat stamped paper. The present invention provides a method for producing a grease-removed paper which is capable of obtaining high quality and improving the working efficiency. It is an object of the present invention to provide a method for producing a grease-removed paper capable of obtaining the same appearance as that of a foil stamped paper.
【０００７】[0007]
【課題を解決するための手段】上記課題を解決するため
の本発明の脂取り紙の製造法は、原紙にカレンダー加工
を施した後、このカレンダー加工紙と、このカレンダー
加工紙より堅い補助用シート状物とを交互に重ね合わ
せ、これらカレンダー加工紙および補助用シート状物の
所望枚数を一束として束面から叩くようにしたものであ
る。According to the present invention, there is provided a method for producing a grease-removed paper, which comprises subjecting a base paper to a calendering process, and then applying the calendered paper to an auxiliary material which is harder than the calendered paper. Sheets are alternately overlapped with each other, and the desired number of the calendered paper and the auxiliary sheet are bundled into a bundle to be hit from the bundle surface.
【０００８】上記課題を解決するための本発明の他の脂
取り紙の製造法は、上記製造法において、所望の漉き模
様を有する原紙を用いたものである。Another method for producing a grease-removed paper according to the present invention for solving the above-mentioned problems is to use a base paper having a desired woven pattern in the above-mentioned production method.
【０００９】そして、上記各製造法において、原紙の原
料成分として、植物繊維、動物繊維から選択し、必要に
応じて無機質填料を添加することができ、また、原紙の
原料を所望の漉き模様で漉き、乾燥させて原紙を形成す
ることができる。[0009] In each of the above-mentioned production methods, a raw material component of the base paper can be selected from plant fibers and animal fibers, and an inorganic filler can be added as necessary. It can be made and dried to form base paper.
【００１０】また、原紙をカレンダー加工する際にアロ
エ、絹タンパク、米ぬか、コラーゲンを選択的に含浸さ
せることができる。When the base paper is calendered, aloe, silk protein, rice bran, or collagen can be selectively impregnated.
【００１１】上記本発明の製造法によれば、原紙にカレ
ンダー加工を施して繊維を潰すとともに、密度および平
滑度を高めた後、このカレンダー加工紙と、このカレン
ダー加工紙より堅い補助用シート状物とを交互に重ねて
叩くので、カレンダー加工紙の繊維を砕くようにすると
ともに、繊維の目を比較的簡単に、かつ確実に潰して適
度の柔軟性、平滑性を兼ね備えることができるととも
に、堅い補助用シート状物との摩擦によって磨くように
することができ、箔打ち紙と同様の脂分の吸収性、光
沢、肌触り等を得ることができる。According to the production method of the present invention, the base paper is calendered to crush the fibers, and the density and smoothness are increased. Then, the calendered paper and an auxiliary sheet which is harder than the calendered paper are formed. As the material is alternately layered and hit, the fibers of the calendered paper are crushed, and the eyes of the fibers can be relatively easily and reliably crushed and have appropriate flexibility and smoothness, It can be polished by friction with a rigid auxiliary sheet-like material, and can obtain the same absorptivity, luster, texture, and the like of a fat as with foil-fed paper.
【００１２】また、所望の漉き模様を有する原紙を用い
ることにより、所望の漉き模様を有する脂取り紙を得る
ことができる。Further, by using a base paper having a desired woven pattern, a grease-removed paper having a desired laid pattern can be obtained.
【００１３】[0013]
【発明の実施の形態】以下、本発明の実施形態について
説明する。原紙の原料成分である植物繊維として、例え
ば、ガンピ、サンピ、パルプ、みつまた、マニラ麻等を
用い、動物繊維として、例えば、絹繊維を用い、無機質
填料として、例えば、泥を用いる。そして、従来の製紙
方法と同様に、ガンピ、サンピ、パルプ、みつまた、マ
ニラ麻、絹繊維等を単独で、若しくは所望の配合比で組
み合わせて用い、必要に応じて泥をガンピ等１００部に
対して５部〜５０部の配合比で添加し、紙の層の形成に
おいて異なったワイヤーパートを通し、それぞれについ
て従来の箔打ち紙で用いられている格子、亀甲など、所
望の漉き模様を有するシリンダを通すことにより、異な
った二層の紙を形成し、これをプレスロールにより合紙
する。この二層からなる合紙をドライヤーパートに通過
させることにより製紙する。ここで、ガンピ等に対して
泥を添加することにより紙の平滑性等を高めることがで
きるが、ガンピ等１００部に対して泥が５部未満である
と平滑性等に劣り、５０部を超えると紙の品質を害する
おそれがあり、したがって、５部〜５０部の間で選択す
るのが好ましい。Embodiments of the present invention will be described below. For example, ganpi, sampi, pulp, honey, manila hemp, and the like are used as plant fibers as raw material components of base paper, animal fibers are used, for example, silk fibers, and inorganic filler is, for example, mud. Then, in the same manner as in the conventional paper making method, ganpi, sampi, pulp, honey, manila hemp, silk fiber, etc. are used alone or in combination at a desired blending ratio, and mud is applied to 100 parts of ganpi, etc. as necessary. Cylinders having a desired pattern, such as a grid or a turtle shell, each of which is used in a conventional foil stamping paper, are passed through different wire parts in the formation of a paper layer, and are added in a mixing ratio of 5 to 50 parts. The paper is passed through to form two different layers of paper, which are interleaved by press rolls. The paper is made by passing the two-layered interleaving paper through a dryer part. Here, the smoothness and the like of the paper can be enhanced by adding the mud to the ganpi etc., but if the mud is less than 5 parts per 100 parts of the ganpi etc., the smoothness is inferior. If it exceeds, the quality of the paper may be impaired. Therefore, it is preferable to select between 5 and 50 parts.
【００１４】次に、上記のように所望の漉き模様を有す
る原紙に水分を与えながらカレンダーロールに通すこと
により、繊維を潰すとともに、密度および平滑度を高め
る。上記水分として、純水にアロエ、絹タンパク、米ぬ
か、コラーゲン等のいずれか、若しくはそれらの複数種
を添加し、この水分を含浸法、若しくは加湿法（水蒸
気）により上記原紙に与え、その成分を原紙に含有させ
る。Next, the base paper having the desired pattern is passed through a calender roll while supplying moisture to crush the fibers and increase the density and smoothness. As the water, any one of aloe, silk protein, rice bran, collagen, or the like, or a plurality thereof is added to pure water, and this water is given to the base paper by an impregnation method or a humidification method (steam), and the components are added. Include in base paper.
【００１５】次に、上記カレンダー加工紙と、このカレ
ンダー加工紙より堅い補助用シート状物とを例えば、２
０ｃｍ以上の正方形、若しくは長方形に形成して交互に
重ね合わせ、これらカレンダー加工紙および補助用シー
ト状物の所望枚数、例えば、５００枚〜１０００枚程度
を一束として箔打ち機により束面から万遍なくカレンダ
ー加工紙の繊維が砕けるほど叩く。このとき、熱が発生
するため、冷ましながら叩く作業を繰り返して行う。カ
レンダー加工紙の間にこれより堅い補助用シート状物を
挟んでいるので、カレンダー加工紙の繊維を砕くように
するとともに、繊維の目を簡単に、かつ確実に潰して柔
軟性を得ることができるとともに、堅い補助用シート状
物との摩擦により磨くようにして光沢（艶）を得ること
ができる。この工程を加えることにより、箔打ち紙と同
様の脂の吸収性、光沢、肌触りを有する紙質を作り上げ
ることができる。Next, the calendered paper and an auxiliary sheet material which is harder than the calendered paper are, for example,
It is formed into a square or a rectangle of 0 cm or more and alternately overlapped, and a desired number of these calendered papers and auxiliary sheets, for example, about 500 to 1,000 sheets, is bundled by a foiling machine from the bundle surface to a bundle. Tap so that the fibers of the calendered paper are broken. At this time, since heat is generated, the tapping operation is repeatedly performed while cooling. Since a harder auxiliary sheet is sandwiched between the calendered papers, the fibers of the calendered paper can be crushed and the eyes of the fibers can be easily and reliably crushed to obtain flexibility. As well as being able to polish by friction with a rigid auxiliary sheet material, it is possible to obtain gloss. By adding this step, paper quality having the same fat absorbency, gloss, and texture as that of the foil stamped paper can be produced.
【００１６】[0016]
【実施例】以下、本発明の実施例について説明する。原
紙の原料として、ガンピとマニラ麻３０対７０の割合で
用い、このガンピとマニラ麻１００部に対して泥を約２
５部の配合比で添加した。上記原料成分により従来の箔
打ち紙と同様の格子模様、若しくは亀甲模様となるよう
にそれぞれ上記のように二層漉きを行い、カレンダー加
工を行った。このようにして製造したカレンダー加工紙
と、補助用シート状物として、上記カレンダー加工紙よ
り堅いパルプ１００％のグラシンなどとを２０ｃｍ以上
の正方形、若しくは長方形に形成して交互に重ね合わ
せ、５００枚〜１０００枚を一束として箔打ち機により
大、小重さの異なるハンマーを使い分けて束面から万遍
なく繰り返して叩いて脂取り紙を製造した。Embodiments of the present invention will be described below. As raw materials for the base paper, ganpi and manila hemp were used in a ratio of 30 to 70.
It was added at a mixing ratio of 5 parts. Each of the raw material components was subjected to two-layer making as described above so as to form a lattice pattern or a turtle pattern similar to that of a conventional foil stamped paper, and calendered. The calendered paper manufactured in this manner and, as an auxiliary sheet-like material, glassine or the like with 100% pulp harder than the calendered paper are formed into a square or rectangle of 20 cm or more and alternately overlapped, and 500 sheets Approximately 1000 sheets were bundled into one bundle, and a hammer having different weights, different in weight, was used by a foiling machine.
【００１７】比較例として、上記本発明実施例と同様
で、カレンダー加工を施していない原紙のみを重ね合わ
せ、同様に、５００枚〜１０００枚を一束として上記本
発明実施例と同様に叩いて脂取り紙を製造した。As a comparative example, in the same manner as in the above-described embodiment of the present invention, only the uncalendered base papers are overlapped, and similarly, 500 to 1000 sheets are bundled and beaten in the same manner as in the above-described embodiment of the present invention. A greased paper was produced.
【００１８】上記本発明実施例の脂取り紙と上記比較例
の脂取り紙と従来の箔打ち紙について複数の女性により
顔の脂の吸収テストを行った結果、脂の吸収性、肌触り
において、従来の箔打ち紙が最も優れ、比較例の脂取り
紙が最も劣り、本発明実施例の脂取り紙は比較例の脂取
り紙より優れ、従来の箔打ち紙よりやや劣るものの、こ
れに近い特性を有することがわかった。また、本発明実
施例の脂取り紙は、光沢において、比較例の脂取り紙よ
りも優れ、従来の箔打ち紙と同等であることがわかっ
た。また、本発明実施例の脂取り紙において、アロエ、
絹タンパク、米ぬか、コラーゲン等を含浸、若しくは加
湿により付与することにより、殺菌、美白、日焼け防
止、肌の柔軟性、優れた光沢等の効果を有することも明
らかである。A plurality of women conducted a face fat absorption test on the fat removing paper of the present invention, the fat removing paper of the comparative example, and the conventional foil stamping paper. The conventional foil stamped paper is the best, the comparative example is the worst, and the present example is superior to the comparative example, but slightly inferior to the conventional foil stamped paper, but close to this. It was found to have properties. Further, it was found that the degreased paper of the example of the present invention was superior to the degreased paper of the comparative example in gloss, and was equivalent to the conventional foil stamped paper. Further, in the fat removing paper of the embodiment of the present invention, aloe,
It is also apparent that impregnation with silk protein, rice bran, collagen, or the like, or humidification, has effects such as sterilization, whitening, prevention of sunburn, skin flexibility, and excellent gloss.
【００１９】なお、上記実施例では、ガンピとマニラ麻
を用いた場合について説明したが、このほか、みつま
た、サンピ等を用いても同様の脂の吸収性、光沢、肌触
り等が得られることは明らかである。In the above embodiment, the case where ganpi and manila hemp were used was described. In addition to this, it is apparent that the same fat absorbency, luster, and softness can be obtained by using honey or sampi. It is.
【００２０】[0020]
【発明の効果】以上要するに本発明の製造法によれば、
原紙にカレンダー加工を施して繊維を潰すとともに、密
度および平滑度を高めた後、このカレンダー加工紙と、
このカレンダー加工紙より堅い補助用シート状物とを交
互に重ねて叩くので、カレンダー加工紙の繊維を砕くよ
うにするとともに、繊維の目を比較的簡単に、かつ確実
に潰して適度の柔軟性、平滑性を兼ね備えることができ
るとともに、堅い補助用シート状物との摩擦によって磨
くようにすることができ、箔打ち紙と同様の脂分の吸収
性、光沢、肌触りを得ることができる。したがって、箔
打ち紙と同様の高品質を得ることができ、しかも、作業
能率を向上させることができる。In summary, according to the production method of the present invention,
After calendering the base paper to crush the fibers and increasing the density and smoothness, the calendered paper and
Since the auxiliary sheet material, which is stiffer than this calendered paper, is alternately layered and beaten, the fibers of the calendered paper are crushed, and the eyes of the fibers are relatively easily and reliably crushed to give appropriate flexibility. In addition to being able to have smoothness, it can be polished by friction with a hard auxiliary sheet-like material, and it is possible to obtain the same absorptivity, gloss, and feel of fat as in the case of foil stamped paper. Therefore, the same high quality as that of the foil stamped paper can be obtained, and the work efficiency can be improved.
【００２１】また、所望の漉き模様を有する原紙を用い
ることにより、所望の漉き模様を有する脂取り紙を得る
ことができる。したがって、箔打ち紙と同様の外観を得
ることができる。Further, by using base paper having a desired woven pattern, it is possible to obtain a greased paper having a desired laid pattern. Therefore, the same appearance as that of the foil stamped paper can be obtained.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平５−344913（ＪＰ，Ａ) 特開 平６−319664（ＪＰ，Ａ) 特開 平８−56867（ＪＰ，Ａ) 特公 昭54−18181（ＪＰ，Ｂ１) 堀洸，小ロット製紙工学，日本，株式 会社紙業タイムス社，初版，ｐ．402− 404 紙パルプ技術協会，紙パルプ事典，日 本，金原出版株式会社，第５版，ｐ. 396−397 (58)調査した分野(Int.Cl.7，ＤＢ名) A45D 42/00 - 44/00 A45D 33/38 A47K 7/00 D21H 25/04 ────────────────────────────────────────────────── ─── Continuation of the front page (56) References JP-A-5-344913 (JP, A) JP-A-6-319664 (JP, A) JP-A-8-56867 (JP, A) 18181 (JP, B1) Ko Hori, Small Lot Paper Engineering, Japan, Paper Industry Times, First Edition, p. 402-404 Japan Pulp and Paper Technology Association, Japan Pulp and Paper Encyclopedia, Japan, Kanehara Publishing Co., Ltd., 5th edition, p. 396-397 (58) Fields investigated (Int. Cl. 7 , DB name) A45D 42/00- 44/00 A45D 33/38 A47K 7/00 D21H 25/04
Claims (5)
カレンダ加工紙と、このカレンダー加工紙より堅い補助
用シート状物とを交互に重ね合わせ、これらカレンダー
加工紙および補助用シート状物の所望枚数を一束として
束面から叩く脂取り紙の製造法。After subjecting a base paper to calendering, the calendered paper and an auxiliary sheet material which is harder than the calendered paper are alternately overlapped, and the calendered paper and the auxiliary sheet material are desirably laminated. A method for producing grease-absorbing paper that is beaten from the bundle surface in batches.
記載の脂取り紙の製造法。2. The base paper has a desired pattern.
The method for producing a grease-absorbing paper according to the above.
から選択され、必要に応じて無機質填料が添加される請
求項１または２記載の脂取り紙の製造法。3. The method for producing fat-removed paper according to claim 1, wherein the raw material components of the base paper are selected from plant fibers and animal fibers, and an inorganic filler is added as required.
燥させて原紙を形成する請求項２または３記載の脂取り
紙の製造法。4. The method for producing a grease-removed paper according to claim 2, wherein the raw material of the base paper is made in a desired pattern and dried to form the base paper.
絹タンパク、米ぬか、コラーゲンを選択的に含浸してあ
る請求項１ないし４のいずれかに記載の脂取り紙の製造
法。5. When the base paper is calendered, aloe,
The method for producing a greased paper according to any one of claims 1 to 4, wherein silk protein, rice bran, or collagen is selectively impregnated.