JP3155103B2 - Exterior sheet and resin molded article using the exterior sheet - Google Patents
Exterior sheet and resin molded article using the exterior sheetInfo
- Publication number
- JP3155103B2 JP3155103B2 JP35525392A JP35525392A JP3155103B2 JP 3155103 B2 JP3155103 B2 JP 3155103B2 JP 35525392 A JP35525392 A JP 35525392A JP 35525392 A JP35525392 A JP 35525392A JP 3155103 B2 JP3155103 B2 JP 3155103B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- sheet
- exterior sheet
- molded article
- exterior
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、例えば樹脂成形体の成
形と同時に該樹脂成形体の表面に熱融着によって積層さ
れる等の方法で利用される外装用シート、及び該外装用
シートを利用した樹脂成形体に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an exterior sheet used by, for example, laminating the surface of a resin molded article by heat fusion at the same time as molding the resin molded article, and a method for producing the same. The present invention relates to a resin molding used.
【０００２】[0002]
【従来の技術】樹脂成形体の表面に意匠特性を付与する
ために塗料による着色塗装を行なっていたが、この塗料
による着色塗装では塗料むらの発生のために高意匠性が
得られなく、また樹脂成形体の成形工程と別工程での塗
装工程を実施するものであることから、塗装のための設
備を余分に必要とし、さらに塗装後の乾燥，硬化工程が
煩雑である等の欠点を有する。2. Description of the Related Art In order to impart design characteristics to the surface of a resin molded article, a colored coating with a paint has been performed. However, in the colored coating with this paint, a high design property cannot be obtained due to unevenness of the paint. Since the coating process is performed as a separate process from the molding process of the resin molded body, extra equipment for coating is required, and the drying and curing process after coating is complicated. .
【０００３】このため樹脂成形体の表面に熱融着によっ
て外装用シートを積層することによって樹脂成形体の意
匠特性を高める方法が実施されるようになっており、外
装用シートとして樹脂製の基材シートに金属蒸着層を形
成したものや、ポリオレフィン系樹脂シート等が利用さ
れている。For this reason, a method of improving the design characteristics of the resin molded article by laminating an exterior sheet by heat fusion on the surface of the resin molded article has been implemented. Materials in which a metal vapor-deposited layer is formed on a material sheet, a polyolefin-based resin sheet, and the like are used.
【０００４】[0004]
【発明が解決しようとする課題】前記従来の外装用シー
トのうちの金属蒸着層を有するものは、外装用シートを
樹脂成形体の表面に熱融着する工程で、この外装用シー
トに発生する伸びによって金属蒸着層にクラックが生ず
るという欠点を有する。Among the above-mentioned conventional exterior sheets, those having a metal-deposited layer are generated on the exterior sheet in the step of heat-sealing the exterior sheet to the surface of the resin molded article. There is a disadvantage that cracks occur in the metal deposition layer due to elongation.
【０００５】また、ポリオレフィン系樹脂シートからな
る外装用シートはその表面物性が十分でなく、外装用シ
ートに要求される諸物性を満足し得ない。Further, the exterior sheet made of a polyolefin-based resin sheet has insufficient surface properties, and cannot satisfy various physical properties required for the exterior sheet.
【０００６】従って本発明が解決しようとする課題は、
表面物性が極めて良好であり、しかも樹脂成形体との間
に強固な接着力を形成することができ、さらには十分な
可撓性を有することから、樹脂成形体の表面形状が立体
的であっても該表面形状に沿って整然とした状態で積層
し得る外装用シート、及び該外装用シートを利用した樹
脂成形体を提供することにある。Therefore, the problem to be solved by the present invention is as follows:
Since the surface properties are extremely good, a strong adhesive force can be formed between the resin molded body and the resin molded body, and the resin molded article has sufficient flexibility, the surface shape of the resin molded article is three-dimensional. It is still another object of the present invention to provide an exterior sheet that can be laminated in an orderly manner along the surface shape, and a resin molded article using the exterior sheet.
【０００７】[0007]
【課題を解決するための手段】前記課題は、下記の構成
による本発明の外装用シート及び該外装用シートを利用
した樹脂成形体によって解決される。すなわち本発明の
外装用シートは、弗素樹脂層とアクリル樹脂層との共押
し出し複合フィルムのアクリル樹脂層面に、トリ−２−
エチルヘキシルトリメリテートからなる可塑剤を含有す
る塩化ビニル樹脂による着色樹脂シートが加熱融着され
ており、しかも該着色樹脂シート面に熱可塑性樹脂によ
る基材シートが、イソシアネート系硬化剤を用いてある
ウレタン系樹脂による接着剤を介して積層されている積
層シートからなるものである。The above object can be attained by the exterior sheet of the present invention having the following constitution and a resin molded article using the exterior sheet. That is, the exterior sheet of the present invention has a tri-2-layer on the surface of the acrylic resin layer of the co-extruded composite film of the fluorine resin layer and the acrylic resin layer.
A colored resin sheet made of a vinyl chloride resin containing a plasticizer made of ethylhexyl trimellitate is heat-sealed, and a base sheet made of a thermoplastic resin is used on the surface of the colored resin sheet, using an isocyanate-based curing agent. It is composed of a laminated sheet laminated via an adhesive made of a urethane-based resin.
【０００８】又本発明の外装用シートを利用した樹脂成
形体は、前記の構成による本発明の外装用シートと熱可
塑性樹脂成形体とが、外装用シートの基材シート面と熱
可塑性樹脂成形体の表面とで熱融着によって積層されて
なるものである。[0008] The resin molded article using the exterior sheet of the present invention is characterized in that the exterior sheet of the present invention and the thermoplastic resin molded article having the above-mentioned structure are combined with the base sheet surface of the exterior sheet and the thermoplastic resin molded article. It is formed by laminating with the surface of the body by thermal fusion.
【０００９】前記構成による本発明の外装用シートにお
いて、弗素樹脂層とアクリル樹脂層との共押し出し複合
フィルムにおける弗素樹脂層には、ポリ弗化ビニル，ポ
リ弗化ビニリデン，ポリ４弗化エチレン，エチレン−４
弗化エチレン共重合体等のポリ弗化エチレン系樹脂を利
用し得るが、得られる複合フィルムの剛性や外装用シー
トの成形性等の点から、ポリ弗化ビニリデン（ＰＶＤ
Ｆ）が好適である。In the exterior sheet of the present invention having the above structure, the fluorine resin layer in the coextruded composite film of the fluorine resin layer and the acrylic resin layer includes polyvinyl fluoride, polyvinylidene fluoride, polytetrafluoroethylene, Ethylene-4
Although a polyfluoroethylene resin such as a fluoroethylene copolymer can be used, polyvinylidene fluoride (PVD) is used in view of the rigidity of the obtained composite film and the moldability of an exterior sheet.
F) is preferred.
【００１０】また、前記複合フィルムにおけるアクリル
樹脂層には、ポリメタクリル酸メチル，ポリメタクリル
酸エチル，ポリアクリル酸エチル，ポリアクリル酸ブチ
ル等のアクリル系樹脂を利用し得る。The acrylic resin layer in the composite film may be made of an acrylic resin such as polymethyl methacrylate, polyethyl methacrylate, polyethyl acrylate, and polybutyl acrylate.
【００１１】この弗素樹脂層とアクリル樹脂層との共押
し出し複合フィルムは、ダイスからの２層溶融共押し出
しによる熱融着がなされているものであり、両層の層間
接着強度の極めて高いものである。[0011] The co-extruded composite film of the fluorine resin layer and the acrylic resin layer is heat-sealed by two-layer melting and co-extrusion from a die, and has extremely high interlayer adhesion strength between both layers. is there.
【００１２】弗素樹脂層とアクリル樹脂層との共押し出
し複合フィルムにおける弗素樹脂層やアクリル樹脂層に
は、共押し出し複合フィルム自体の耐候性を向上させ、
また下地層である着色樹脂シートの耐候性を向上させる
ために、必要に応じて紫外線吸収剤を含有させることが
できる。The fluororesin layer and the acrylic resin layer in the coextruded composite film of the fluororesin layer and the acrylic resin layer are provided with an improved weather resistance of the coextruded composite film itself,
Further, in order to improve the weather resistance of the colored resin sheet as the underlayer, an ultraviolet absorber can be contained as necessary.
【００１３】複合フィルムのアクリル樹脂層面に加熱融
着させてある塩化ビニル樹脂による着色樹脂シートは、
顔料，光輝性顔料等の着色剤によって着色されている５
０〜２００μ程度のシートであって、トリ−２−エチル
ヘキシルトリメリテートからなる可塑剤を含有するもの
である。この塩化ビニル樹脂による着色樹脂シートの可
塑剤の含有量は塩化ビニル樹脂１００重量部に対して５
〜５０重量部程度である。A colored resin sheet made of a vinyl chloride resin, which is heated and fused to the acrylic resin layer surface of the composite film,
Colored with a colorant such as a pigment or a bright pigment 5
A sheet having a size of about 0 to 200 µ and containing a plasticizer made of tri-2-ethylhexyl trimellitate. The content of the plasticizer in the colored resin sheet made of the vinyl chloride resin is 5 with respect to 100 parts by weight of the vinyl chloride resin.
It is about 50 parts by weight.
【００１４】塩化ビニル樹脂による着色樹脂シート面に
イソシアネート系硬化剤を用いてあるウレタン系樹脂に
よる接着剤によって積層されている熱可塑性樹脂による
基材シートは、該外装用シートが適用される樹脂成形体
と接する側になる樹脂シートであり、成形面樹脂シート
として作用するものである。A base sheet made of a thermoplastic resin laminated on a surface of a colored resin sheet made of a vinyl chloride resin with an adhesive made of a urethane-based resin using an isocyanate-based curing agent is formed by resin molding to which the exterior sheet is applied. It is a resin sheet on the side that comes into contact with the body, and acts as a molded surface resin sheet.
【００１５】熱可塑性樹脂による基材シートとしては、
例えばポリ塩化ビニル，ポリ塩化ビニリデン，酢酸ビニ
ル−塩化ビニル共重合体，ポリ弗化ビニル，ポリビニル
ブチラール，ポリ弗化ビニリデン等のビニル系樹脂、ポ
リスチレン，ポリアクリルスチレン，ＡＢＳ樹脂等のス
チレン系樹脂、ポリメタクリル酸メチル，ポリメタクリ
ル酸エチル，ポリアクリロニトリル等のアクリル系樹
脂、ポリエチレン，ポリプロピレン，ポリメチルペンテ
ン等のポリオレフィン系樹脂、酢酸セルロース，ニトロ
セルロース等のセルロース誘導体、ナイロン−６，ナイ
ロン−６６などのポリアミド系樹脂、ポリエチレンテレ
フタレート，ポリエチレンテレフタレート−イソフタレ
ート共重合体，ポリブチレンテレフタレート等のポリエ
ステル系樹脂、ブタジエンゴム，クロロプレンゴム，シ
リコンゴム等のゴム系樹脂、さらにはポリカーボネート
等による樹脂シートを利用することができ、特にポリオ
レフィン系樹脂シートが好ましい。As a base sheet made of a thermoplastic resin,
For example, vinyl resins such as polyvinyl chloride, polyvinylidene chloride, vinyl acetate-vinyl chloride copolymer, polyvinyl fluoride, polyvinyl butyral, and polyvinylidene fluoride; styrene resins such as polystyrene, polyacrylstyrene, and ABS resin; Acrylic resins such as polymethyl methacrylate, polyethyl methacrylate, and polyacrylonitrile; polyolefin resins such as polyethylene, polypropylene, and polymethylpentene; cellulose derivatives such as cellulose acetate and nitrocellulose; nylon-6, nylon-66; Polyester resin such as polyamide resin, polyethylene terephthalate, polyethylene terephthalate-isophthalate copolymer, polybutylene terephthalate, rubber such as butadiene rubber, chloroprene rubber, and silicone rubber Resin, more can be used a resin sheet by polycarbonate, polyolefin-based resin sheet is particularly preferred.
【００１６】なお基材シートには、該基材シートと塩化
ビニル樹脂による着色樹脂シートとの接着性を高めるた
めに、接着面をコロナ放電処理しておくことが好まし
い。The base sheet is preferably subjected to a corona discharge treatment on the bonding surface thereof in order to enhance the adhesion between the base sheet and the colored resin sheet made of vinyl chloride resin.
【００１７】基材シートを塩化ビニル樹脂による着色樹
脂シート面に接着させるための接着剤には、イソシアネ
ート系硬化剤を用いてあるウレタン系樹脂からなる硬化
性樹脂を使用する。該樹脂による接着剤層は、例えばグ
ラビアコート，グラビアリバースコート，グラビアオフ
セットコート，スピナーコート等により、５〜１０ｇ／
ｍ2 程度の塗工層として形成する。As an adhesive for adhering the base sheet to the surface of the colored resin sheet made of a vinyl chloride resin, a curable resin made of a urethane-based resin using an isocyanate-based curing agent is used. An adhesive layer made of the resin is coated with a gravure coat, a gravure reverse coat, a gravure offset coat, a spinner coat, or the like, for example, at a rate of 5 to 10 g / g.
It is formed as a coating layer of about m 2 .
【００１８】さらに本発明の外装用シートの任意の層間
には、必要に応じて模様印刷や金属膜蒸着等による装飾
層を設けることができる。Further, between any layers of the exterior sheet of the present invention, a decoration layer may be provided by pattern printing, metal film deposition or the like, if necessary.
【００１９】本発明の外装用シートを積層させる熱可塑
性樹脂成形体としては、ポリ塩化ビニル，ポリ塩化ビニ
リデン，酢酸ビニル−塩化ビニル共重合体，ポリ弗化ビ
ニル，ポリビニルブチラール，ポリ弗化ビニリデン等の
ビニル系樹脂、ポリスチレン，アクリルスチレン，ＡＢ
Ｓ樹脂等のスチレン系樹脂、ポリメタクリル酸メチル，
ポリメタクリル酸エチル，ポリアクリロニトリル等のア
クリル系樹脂、ポリエチレン，ポリプロピレン，ポリメ
チルペンテン等のポリオレフィン系樹脂、酢酸セルロー
ス，ニトロセルロースとのセルロース誘導体、ナイロン
−６，ナイロン−６６などのポリアミド系樹脂、ポリエ
チレンテレフタレート，ポリエチレンテレフタレート−
イソフタレート共重合体，ポリブチレンテレフタレート
等のポリエステル系樹脂、ブタジエンゴム，クロロプレ
ンゴム，シリコンゴム等のゴム系樹脂、ポリカーボネー
ト等による成形体を利用し得る。Examples of the thermoplastic resin molded article on which the exterior sheet of the present invention is laminated include polyvinyl chloride, polyvinylidene chloride, vinyl acetate-vinyl chloride copolymer, polyvinyl fluoride, polyvinyl butyral, polyvinylidene fluoride and the like. Vinyl resin, polystyrene, acrylic styrene, AB
Styrene resins such as S resin, polymethyl methacrylate,
Acrylic resins such as polyethyl methacrylate and polyacrylonitrile; polyolefin resins such as polyethylene, polypropylene and polymethylpentene; cellulose derivatives with cellulose acetate and nitrocellulose; polyamide resins such as nylon-6, nylon-66; Terephthalate, polyethylene terephthalate
A molded product made of a polyester resin such as an isophthalate copolymer or polybutylene terephthalate, a rubber resin such as a butadiene rubber, a chloroprene rubber, or a silicone rubber, or a polycarbonate may be used.
【００２０】なおこの熱可塑性樹脂成形体の樹脂の種類
は、外装用シートにおける基材シートの樹脂と同一であ
ることが好ましく、熱可塑性樹脂成形体と外装用シート
における基材シートとが共にポリオレフィン系樹脂から
なるものが最も好ましい。It is preferable that the type of the resin of the thermoplastic resin molded article is the same as the resin of the base sheet in the exterior sheet, and both the thermoplastic resin molded article and the base sheet in the exterior sheet are polyolefin. Those composed of a series resin are most preferred.
【００２１】外装用シートと熱可塑性樹脂成形体との積
層は、例えば熱可塑性樹脂成形体の射出成形を行なう際
に外装用シートを予め金型内にインサートしておき、熱
可塑性樹脂成形体の成形と同時に外装用シートを積層す
る方法（特公昭３３−３１８０号公報，特公昭５０−１
９１３２号公報等）、外装用シートを真空または圧空成
形すると同時に熱可塑性樹脂成形体に積層する方法（特
公昭３２−９７８５号公報，特公昭５６−４５７６８号
公報）、熱可塑性樹脂成形体の溶融押し出し成形と同時
に外装用シートを積層する方法、ブロー成形用金型内に
外装用シートを、該外装用シートの基材シート面がキャ
ビティー側に乗るようにして予めインサートしておき、
該金型内で熱可塑性樹脂のパリソンをブロー成形すると
共に、ブロー成形された成形体の外周面に外装用シート
を積層させる方法、さらにはシート状の熱可塑性樹脂成
形体と外装用シートとの積層方法として、予備熱処理ロ
ールと１対の熱ラミネートロールとの組み合わせロール
を利用し、両者を熱処理しながら積層する方法（特公平
２−６１３７８号公報）等によって行なうことができ
る。The lamination of the exterior sheet and the thermoplastic resin molded body is performed, for example, by inserting the exterior sheet into a mold before injection molding of the thermoplastic resin molded body, and A method of laminating an exterior sheet simultaneously with molding (Japanese Patent Publication No. 33-3180, Japanese Patent Publication No. 50-1)
No. 9132), a method in which an exterior sheet is vacuum- or pressure-formed and laminated on a thermoplastic resin molded article at the same time (Japanese Patent Publication No. 32-9785 and Japanese Patent Publication No. 56-45768), melting of the thermoplastic resin molded article. A method of laminating an exterior sheet at the same time as extrusion molding, an exterior sheet in a blow molding die, and a base sheet surface of the exterior sheet is inserted in advance so as to ride on the cavity side,
A method in which the parison of the thermoplastic resin is blow-molded in the mold, and a method for laminating an exterior sheet on the outer peripheral surface of the blow-molded molded article. As a laminating method, it is possible to use a combination roll of a preliminary heat treatment roll and a pair of heat laminating rolls, and to laminate them while heat-treating both (Japanese Patent Publication No. 2-61378).
【００２２】本発明の外装用シートを積層した熱可塑性
樹脂成形体の用途は、例えば、窓枠（サッシ）、外壁用
の化粧板、羽目板、扉、自動車のモール等の車輌外装
材、広告用看板等である。The thermoplastic resin molded article laminated with the exterior sheet of the present invention can be used for, for example, window frames (sashes), decorative panels for exterior walls, siding panels, doors, vehicle exterior materials such as automobile malls, and advertisements. It is a signboard.
【００２３】[0023]
【作用】本発明の外装用シートは、弗素樹脂層が外側表
面層となるようにして利用されるもので、耐熱性及び耐
候性等に優れた作用を奏する。The exterior sheet of the present invention is used in such a manner that the fluororesin layer serves as the outer surface layer, and has excellent heat resistance and weather resistance.
【００２４】また本発明の外装用シートは、熱可塑性樹
脂による基材シートが成形面樹脂シートとして作用する
ことから、成形性能においても優れた作用を奏する。In addition, the exterior sheet of the present invention has an excellent effect on the molding performance since the base sheet made of the thermoplastic resin acts as the molding surface resin sheet.
【００２５】さらに本発明の外装用シートは、弗素樹脂
層とアクリル樹脂層との共押し出し複合フィルムのアク
リル樹脂層面に積層する着色樹脂シートとして、トリ−
２−エチルヘキシルトリメリテートからなる可塑剤を含
有する塩化ビニル樹脂による着色樹脂シートを使用して
いるので、該着色樹脂シートの耐熱性，加工性，耐候性
がよく、しかもアクリル樹脂層との間の接着性も良好で
あり、更に可塑剤の耐移行性がよくアクリル樹脂層に対
する着色樹脂シートからの可塑剤のブリードアウトによ
る経時剥離が起こり難く、屋外での使用中における熱，
光の下での経時の層間接着力の劣化も起こり難い。Further, the exterior sheet according to the present invention is a colored resin sheet laminated on the acrylic resin layer surface of a coextruded composite film of a fluorine resin layer and an acrylic resin layer, as a tri-color resin sheet.
Since a colored resin sheet made of a vinyl chloride resin containing a plasticizer made of 2-ethylhexyl trimellitate is used, the colored resin sheet has good heat resistance, workability, and weather resistance, and can be used between the acrylic resin layer and the resin sheet. Has good adhesiveness, the migration resistance of the plasticizer is good, the plasticizer does not easily peel off from the colored resin sheet over time due to bleed-out, and the heat and
Deterioration of the interlayer adhesive strength over time under light is unlikely to occur.
【００２６】さらに本発明の外装用シートを利用した樹
脂成形体は、その表面層が前記外装用シートの表面特性
をそのまま具備するものであり、耐熱性及び耐候性等に
おいて優れた作用を奏する。Further, in the resin molded article using the exterior sheet of the present invention, the surface layer has the surface characteristics of the exterior sheet as it is, and exhibits excellent effects in heat resistance, weather resistance and the like.
【００２７】[0027]
【実施例】以下、本発明の外装用シート及び該外装用シ
ートを利用した樹脂成形体の具体的な構成を、製造実施
例に基づいて説明する。EXAMPLES Specific examples of the exterior sheet of the present invention and a resin molded article using the exterior sheet will be described based on production examples.
【００２８】実施例１ 「外装用シートの製造」 ポリ弗化ビニリデン樹脂層（１０μ）とポリメタクリル
酸メチル樹脂層（５０μ）との厚さ６０μの共押し出し
複合フィルム「カイナーフィルム ＨＷ−６０：サンエ
ー化学 (株) 」のポリメタクリル酸メチル樹脂層面と、
可塑剤としてトリ−２−エチルヘキシルトリメリテート
１０重量％を含有する厚さ１５０μの着色塩化ビニル樹
脂シートとを、１６０℃にて加熱融着させた。Example 1 "Production of an exterior sheet" A co-extruded composite film of a polyvinylidene fluoride resin layer (10 .mu.) And a polymethyl methacrylate resin layer (50 .mu.) Having a thickness of 60 .mu. Chemical Co., Ltd.'s polymethyl methacrylate resin layer surface,
A 150 μm thick colored vinyl chloride resin sheet containing 10% by weight of tri-2-ethylhexyl trimellitate as a plasticizer was heated and fused at 160 ° C.
【００２９】続いて、片面にコロナ放電処理を付してあ
る厚さ１００μのポリプロピレンシートからなる基材シ
ートのコロナ放電処理面に、１０重量％のイソシアネー
ト系硬化剤を含有するウレタン系樹脂からなる接着剤を
グラビアコート法により１０ｇ（ｄｒｙ）／ｍ2 の割合
で塗布し、８０℃，１分間の予備加熱を行なった後、こ
のポリプロピレンシートからなる基材シートの接着剤面
と先の着色塩化ビニル樹脂シート面とを、加熱温度１０
０℃にて接着し、本発明の１実施例品である外装用シー
トを得た。Subsequently, a corona discharge treated surface of a base sheet made of a 100 μm thick polypropylene sheet having a corona discharge treatment on one surface is made of a urethane resin containing 10% by weight of an isocyanate curing agent. The adhesive was applied by a gravure coating method at a rate of 10 g (dry) / m 2 , and was preheated at 80 ° C. for 1 minute. Heat the vinyl resin sheet surface to a heating temperature of 10
The sheet was adhered at 0 ° C. to obtain an exterior sheet which was a product of one example of the present invention.
【００３０】実施例２ 「外装用シートを利用した樹脂成形体の製造」 実施例１で得られた外装用シートを該外装用シートにお
ける基材シートたるポリプロピレンシート面がキャビテ
ィー側に乗るようにして、予めブロー成形用の金型内に
インサートしておき、該金型内でポリプロピレン樹脂製
のパリソンを１５０℃でブロー成形することにより、外
装用シートが外周面に積層されている本発明の１実施例
品であるポリプロピレン樹脂製のブロー成形体を得た。Example 2 "Production of a resin molded article using an exterior sheet" The exterior sheet obtained in Example 1 was placed so that the polypropylene sheet surface serving as a base sheet in the exterior sheet was placed on the cavity side. In the present invention, the exterior sheet is laminated on the outer peripheral surface by inserting in advance in a mold for blow molding, and performing blow molding of a polypropylene resin parison at 150 ° C. in the mold. A blow-molded article made of polypropylene resin, which was a product of Example 1, was obtained.
【００３１】[0031]
【発明の効果】本発明の外装用シートによれば、耐熱性
及び耐候性等に優れた性質を有し、しかも、熱可塑性樹
脂成形体との間の接着強度の高い積層体が得られる。According to the exterior sheet of the present invention, it is possible to obtain a laminate having excellent properties such as heat resistance and weather resistance and high adhesive strength with a thermoplastic resin molded article.
【００３２】また、本発明の外装用シートを利用した樹
脂成形体は、その表面層に前記外装用シートの特性がそ
のまま具備されており、耐熱性及び耐候性等に優れた性
質を有し、外装用シートと熱可塑性樹脂成形体との間の
接着強度の高い積層構造の樹脂成形体になる。Further, the resin molded article using the exterior sheet of the present invention has the properties of the exterior sheet as it is on its surface layer, and has excellent properties such as heat resistance and weather resistance. A resin molded article having a laminated structure with high adhesive strength between the exterior sheet and the thermoplastic resin molded article is obtained.
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) B32B 1/00 - 35/00 ──────────────────────────────────────────────────続 き Continued on front page (58) Field surveyed (Int. Cl. 7 , DB name) B32B 1/00-35/00
Claims (2)
出し複合フィルムのアクリル樹脂層面に、トリ−２−エ
チルヘキシルトリメリテートからなる可塑剤を含有する
塩化ビニル樹脂による着色樹脂シートが加熱融着されて
おり、しかも該着色樹脂シート面に熱可塑性樹脂による
基材シートが、イソシアネート系硬化剤を用いてあるウ
レタン系樹脂による接着剤を介して積層されている積層
シートからなることを特徴とする外装用シート。1. A colored resin sheet of a vinyl chloride resin containing a plasticizer made of tri-2-ethylhexyl trimellitate is heat-sealed on the acrylic resin layer surface of a coextruded composite film of a fluorine resin layer and an acrylic resin layer. And a laminate sheet in which a base sheet made of a thermoplastic resin is laminated on the surface of the colored resin sheet via an adhesive made of a urethane-based resin using an isocyanate-based curing agent. Exterior sheet.
ート面と熱可塑性樹脂成形体の表面とが熱融着によって
積層されていることを特徴とする外装用シートを利用し
た樹脂成形体。2. A resin molding using an exterior sheet, wherein the surface of the base sheet of the exterior sheet according to claim 1 and the surface of the thermoplastic resin molded body are laminated by heat fusion. body.