JP2985684B2 - Artificial turf with sand - Google Patents
Artificial turf with sandInfo
- Publication number
- JP2985684B2 JP2985684B2 JP6243747A JP24374794A JP2985684B2 JP 2985684 B2 JP2985684 B2 JP 2985684B2 JP 6243747 A JP6243747 A JP 6243747A JP 24374794 A JP24374794 A JP 24374794A JP 2985684 B2 JP2985684 B2 JP 2985684B2
- Authority
- JP
- Japan
- Prior art keywords
- pile
- artificial turf
- sand
- yarn
- monofilament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、各種のスポ−ツが行わ
れるグランドに用いられる人工芝に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an artificial turf used as a ground on which various sports are performed.
【０００２】[0002]
【従来の技術】近年、スポーツ人口の増大とともにスポ
ーツ施設の充実が図られている。従来、グランド等のス
ポーツ施設の表面材はクレーやアンツカーや天然芝等が
主流であった。しかしそうした天然の表面材はメンテナ
ンスが大変であること、また天然芝の場合プレーによる
痛みがひどく頻度の高い利用にはそれに見合ったメンテ
ナンスが必要であった。そこで数多くの人工の全天候型
表面材が開発されてきた。それらはメンテナンスフリー
で快適なスポーツ空間を提供している。しかし、人工表
面材はコストの制約からクレーやアンツカーや天然芝の
ような人体に優しい特性が必ずしも十分に発揮されてい
ないのが実情である。人工表面材の中で特に天然に近い
外観、特性を有するのが人工芝である。従来、天然芝グ
ランドで行われていたサッカーなどのスポーツではボー
ルの転がり特性やスライディング等のプレー性から人工
芝が好適な表面材であると言える。しかし従来のスポー
ツ用人工芝は耐久性を重視するあまり人工芝のパイルの
繊度を大きくし、厚くし、そのため表面タッチが大変硬
いものになる傾向があった。そのためテニスなどプレー
ヤーの肌に直接触れるチャンスの少ないスポーツでは問
題なかったがサッカーのようなスライディングや転倒の
多いスポーツでは肌触りが硬く、またスライディング時
にプレーヤーにすり傷や火傷などの負傷を起こし易いも
のであった。一方、手触りや火傷防止のためにパイル品
種を選ばず、単にパイルの繊度を小さくした場合すなわ
ち厚さが薄く柔らかな場合、パイルに腰がないためパイ
ルがしっかりと立毛せず貧弱な外観になり、耐摩耗性も
大変悪化するものであった。また異種モノフィラメント
の利用による優位特性の利用が考えられてきた。2. Description of the Related Art In recent years, sports facilities have been enhanced with the increase in the sports population. Conventionally, clay, antz car, natural turf, and the like have been mainly used as surface materials for sports facilities such as grounds. However, such natural surface materials are difficult to maintain, and the natural turf is so painful to play that frequent use requires maintenance corresponding to it. A number of artificial all-weather surfacing materials have been developed. They provide a maintenance-free and comfortable sports space. However, due to cost constraints, artificial surface materials do not always fully exhibit human-friendly characteristics such as clay, antzers, and natural turf. Among artificial surface materials, artificial turf has an appearance and characteristics that are particularly close to nature. Conventionally, artificial turf is a suitable surface material for sports such as soccer, which has been played on a natural turf ground, in view of ball rolling characteristics and playability such as sliding. However, conventional artificial grass for sports has tended to increase the fineness and thickness of the pile of the artificial grass so much as to emphasize durability, so that the surface touch became very hard. For this reason, there was no problem in sports such as tennis that have little chance to directly touch the player's skin, but in sports such as soccer such as sliding and many falls, the touch is hard and it is easy for the player to be injured such as scratches or burns when sliding. there were. On the other hand, if the pile size is simply reduced without choosing a pile type to prevent touch and burns, that is, if the pile is thin and soft, the pile will not have firm backs and will have poor appearance without standing up. Also, the abrasion resistance was very poor. In addition, utilization of superior characteristics by using heterogeneous monofilaments has been considered.
【０００３】実公昭６１−１１２８４号公報では天然芝
に著しく類似して耐摩擦性、剛性及び人体接触摩擦によ
る火傷防止効果が良好な、かつ気候条件及び過酷な損耗
に暴露されても悪い影響を受けない人工芝を提供するこ
とを目的に、ポリエステルまたはポリアミド系直立状フ
ィラメントと塩化ビニリデン系カールフィラメントとを
基布の幅方向に交互に植毛されてなり、該直立状フィラ
メントとカールフィラメントとはほぼ同じ太さを有する
モノフィラメントで、かつカールフィラメントに対し直
立状フィラメントの頂部が８〜１ｍｍ突出している人工
芝を提案している。この方法では直立状フィラメントと
カールフィラメントの利用により、二重の表面構造を形
成し、剛性、耐摩耗性の改善などを試みている。それぞ
れのフィラメントの特性の有効利用については耐久性の
あるナイロンを表層に出し、耐久性の劣る塩化ビニリデ
ンを地糸として使う考えで、耐久性を向上した人工芝を
提供せんとしたものであると考えられる。しかし、この
人工芝は直立状フィラメントとカールフィラメントが基
布の幅方向に交互に植毛されているため筋状の畝が現
れ、したがって等方性に欠け、スポーツ用サーフェスと
して大変好ましくない特性を有している。また直毛状フ
ィラメントに何等の規制もなく、耐摩擦性、剛性に関す
る配慮はあるがソフトさに対する配慮はなく、ソフトで
なければスポーツ選手、特にサッカー選手に受け入れら
れないと言う認識がないのが実情である。 本発明は上
述した人工芝の硬い表面タッチを改善しソフトな感触を
与え、しかもスポーツに必要な十分な弾性を与え、さら
に耐久性があるサッカー等に好適な人工芝を提供するこ
とを目的とするものである。[0003] Japanese Utility Model Publication No. 61-112284 discloses that, similar to natural turf, the rub resistance, the rigidity and the effect of preventing burns due to human body contact friction are good, and the bad influences even when exposed to climatic conditions and severe wear. For the purpose of providing an artificial turf that does not receive the same, polyester or polyamide-based upright filaments and vinylidene chloride-based curl filaments are alternately implanted in the width direction of the base fabric, and the upright filaments and the curl filaments are almost An artificial turf has been proposed which is a monofilament having the same thickness and in which the top of the upright filament protrudes 8 to 1 mm from the curl filament. In this method, an upright filament and a curl filament are used to form a double surface structure and to improve rigidity and abrasion resistance. Regarding the effective use of the properties of each filament, the idea is to provide durable nylon on the surface layer and use vinylidene chloride, which has poor durability, as ground yarn, and to provide artificial turf with improved durability. Conceivable. However, this artificial turf has streaky ridges because the upright filaments and the curl filaments are alternately planted in the width direction of the base fabric, and therefore lacks isotropy and has a very unfavorable characteristic as a sports surface. doing. In addition, there are no restrictions on straight-haired filaments, and there are considerations regarding friction resistance and rigidity, but there is no consideration for softness, and there is no recognition that if it is not soft, it will not be accepted by sports players, especially soccer players. It is a fact. It is an object of the present invention to provide an artificial turf that improves the hard surface touch of the above-described artificial turf, gives a soft feel, and yet provides sufficient elasticity required for sports, and is more suitable for durable soccer and the like. Is what you do.
【０００４】[0004]
【課題を解決するための手段】本発明は、かかる目的を
達成するために次の手段を採用するものである。すなわ
ち、本発明の砂入り人工芝は、ナイロンモノフィラメン
トパイルからなる砂入り人工芝であって、該モノフィラ
メントが１００デニール以上３５０デニール以下で、か
つ砂からの突出した部分の該パイルの平均長さが８ｍｍ
以上であり、しかも、下式で表される該パイルの断面積
の該人工芝平面における占有率（空間占有率）が４％以
上８％以下であることを特徴とするものである。The present invention employs the following means to achieve the above object. That is, the artificial turf containing sand of the present invention is an artificial turf containing sand composed of a nylon monofilament pile, wherein the monofilament is 100 denier or more and 350 denier or less, and the average length of the pile at a portion protruding from the sand is 8mm
In addition, the occupancy (space occupancy) of the cross-sectional area of the pile in the artificial turf plane represented by the following formula is 4% or more and 8% or less.
【０００５】空間占有率（％）＝Ｗ／（１０・Ｈ・ρ） ［ 式中、Ｗ：１ｍ2 あたりのパイル重量（ g／ｍ 2 ）、
Ｈ：パイル長さ（mm）、ρ：パイル密度（ g／cm 3 ）］ [0005] space occupancy (%) = W / (10 · H · ρ) [ wherein, W: Pile weight per 1m 2 (g / m 2) ,
H: pile length (mm) , ρ: pile density (g / cm 3 )]
【０００６】[0006]
【作用】本発明の特徴は砂入り人工芝であって、ナイロ
ンパイルモノフィラメントの繊度が３５０デニール以下
の比較的細繊度糸であり、しかも柔らかさを与えるに十
分なパイルの密度を規定したことにある。細繊度糸のた
め、パイルは捲縮糸であっても、直毛糸であっても、砂
の上に寝た状態を形成し、そのため砂入り人工芝であっ
てもプレーヤーが砂に直接接しないようにしたので、表
面の手触りが極めてソフトに感ずる上に、擦り傷も起こ
りにくいという特徴を有するものである。かかる人工芝
のパイル素材としては、一般にポリプロピレン、ポリエ
チレン、ナイロン６、６６、塩化ビニリデン、ナイロン
共重合物、ポリエステル等が利用できるが、耐久性の点
からナイロン系ポリマーからなるモノフィラメントを使
用するのが好ましい。本発明の目的には、ポリプロピレ
ン、ポリエチレン、塩化ビニリデン、ポリエステル等の
パイルは耐久性の点から好ましくない。またナイロン系
パイルの場合でも、砂なし人工芝では耐久性の点から問
題がある。すなわち砂なしの場合、ランニングやスライ
ディングの衝撃や荷重が直接基布やバッキング材に伝わ
り、したがってダメージが起きやすく、耐久性は良くな
い。砂入りの場合は、砂が緩衝材になり、またベアリン
グ効果があり、パイルの耐久性を向上する効果がある。The feature of the present invention is that the artificial grass containing sand is a relatively fine yarn having a nylon pile monofilament fineness of 350 denier or less, and that the density of the pile is sufficient to give softness. is there. Due to the fineness of the yarn, the pile, whether it is crimped or straight wool, forms a state of lying on the sand, so that even if the artificial turf contains sand, the player does not directly touch the sand As a result, the feel of the surface is extremely soft, and the abrasion is unlikely to occur. As the pile material for such artificial turf, polypropylene, polyethylene, nylon 6, 66, vinylidene chloride, nylon copolymer, polyester and the like can be generally used, but from the viewpoint of durability, monofilament made of nylon-based polymer is used. preferable. For the purpose of the present invention, piles of polypropylene, polyethylene, vinylidene chloride, polyester and the like are not preferred in terms of durability. Even in the case of nylon piles, there is a problem in terms of durability with sandless artificial turf. That is, when there is no sand, the impact or load of running or sliding is directly transmitted to the base fabric or the backing material, so that damage is likely to occur and durability is not good. In the case of sand, the sand serves as a cushioning material, has a bearing effect, and has an effect of improving the durability of the pile.
【０００７】本発明の人工芝で形状の効果は極めて大き
い。一般に砂入り人工芝に使用されるパイルの繊度は４
００デニール以上である。しかし４００デニール以上で
は本発明の狙いのソフトな感触、外観を形成することが
困難であることが判った。そこで細繊度化の検討を行っ
た結果、３５０デニール以下、好ましくは３００デニー
ル以下が良好な風合の人工芝を与えることが判った。し
かし、１００デニール未満ではハリ、腰に欠けること、
砂入れ性に問題があるなどの欠点があり、また断面形状
については丸断面の場合は、剛直な風合になり好ましく
ない。鋭意検討の結果、偏平な断面が良く、かつ断面の
最大幅と最小幅の比が３以上、好ましくは５以上である
モノフィラメントがソフトな風合を与えるのでよい。上
記の条件を満たせば、フィラメントは捲縮糸であっても
直毛糸であってもよい。捲縮糸には乾熱、湿熱のスタッ
フィング加工や、特殊な賦形加工、あるいはニットデニ
ット、仮撚り、撚りをいれて熱セットした糸等があり、
いずれも使用することができる。直毛糸は捲縮を付けて
いないパイル糸である。したがってパイルの砂からの突
出長さが８ｍｍ以上とは、本発明の思想から直線的なパ
イルの高さを言うのでは無く、砂の上にパイルが横たわ
っている状態でもよく、砂から出ている部分の長さが８
ｍｍ以上であると言うことである。本発明の効果は細繊
度のパイルを使用することによって得られるもので、こ
のようなパイルでは直毛糸であってもほとんど直線的に
立つことはなく、砂の上に自然に倒れ込んだ状態を示す
ものである。例えばブラシをかけることにより、そのブ
ラシの進行方向にパイルは倒れ、したがってグランド上
にブラシ掛け模様を形成することもできる。パイルの長
さが短いとパイルが細繊度であっても砂の露出度が高く
なり、パイルのソフトさが生きてこない。本発明者らの
鋭意研究した結果、パイルの長さが８ｍｍ未満ではパイ
ルのソフトさが生かされず、８ｍｍ以上で、初めて外
観、感触ともソフトな人工芝を与えることがわかった。The effect of the shape of the artificial turf of the present invention is extremely large. The fineness of the pile generally used for artificial turf with sand is 4
It is more than 00 denier. However, at 400 denier or more, it was found that it was difficult to form the soft feel and appearance aimed at by the present invention. Then, as a result of studying fineness, it was found that 350 denier or less, preferably 300 denier or less gives an artificial turf with a good feeling. However, if it is less than 100 denier, it will be tight,
There are drawbacks such as a problem in sand-filling properties, and the cross-sectional shape is not preferable in the case of a round cross-section because it has a rigid feel. As a result of intensive studies, a monofilament having a flat cross section and a ratio of the maximum width to the minimum width of the cross section of 3 or more, preferably 5 or more gives a soft feeling. If the above conditions are satisfied, the filament may be a crimped yarn or a straight wool yarn. Crimped yarns include dry heat, wet heat stuffing, special shaping, knit denit, false twist, twisted and heat set yarn, etc.
Either can be used. Straight yarn is a pile yarn without crimps. Therefore, the protruding length of the pile from the sand of 8 mm or more does not mean the height of the straight pile from the idea of the present invention, but may be a state in which the pile is lying on the sand. The length of the part that is
mm or more. The effect of the present invention is obtained by using a fine-fiber pile. In such a pile, even a straight wool thread does not stand almost linearly and shows a state of naturally falling on sand. Things. For example, by applying a brush, the pile falls down in the direction of travel of the brush, so that a brushed pattern can be formed on the ground. If the pile length is short, even if the pile is fine, the exposure of the sand will be high, and the softness of the pile will not survive. As a result of extensive studies by the present inventors, it has been found that if the pile length is less than 8 mm, the softness of the pile cannot be utilized, and if the pile length is 8 mm or more, an artificial turf having a soft appearance and feel is provided for the first time.
【０００８】本発明では人工芝についてパイルの表面被
覆度であるパイルのカバーリング性について次のように
考えている。すなわち、スポーツ用サーフェスを考えて
いるため単にソフトさのみでなく、スライディング時の
擦り傷の問題があるためその長さが限定される。スライ
ディング時の擦り傷をなくすような構造にするためにパ
イルのカバーリング性が重要である。そのため鋭意研究
の結果、砂の表面露出度を極力抑えることにより本発明
の目的を達成することができることが判った。砂の露出
度の測定はスポーツの実用性を考えた測定方法による必
要がある。そこで本発明では砂の露出度をパイルのカバ
ーリング性により測定することを提案する。すなわち、
平方メートルあたり１００ｇの荷重で人工芝パイルを平
板で押さえ付けた時のパイルのカバーリング性である。
実際のカバーリング性の決定は平板としてガラスあるい
はアクリル等の透明板を用い、１００ｇ／cm2 で押さえ
付けた時の表面状態を観察しパイルの被覆面積を測定す
る。また簡易には平板に粘着テープを張付け、その粘着
テープ面をパイル面に押さえ付けた時に粘着テープに付
着した砂の範囲から砂の露出面積を測定し、パイルのカ
バーリング性を算出することもできる。このようにして
測定したパイルの表面カバーリング性が大きい程、スポ
ーツ時の擦り傷減少やソフトさに対する効果が大きく、
少なくとも７０％以上であることが本発明の効果の上か
ら好ましいことがわかった。すなわち７０％以下では表
面が砂っぽく見え、プレーヤーの心理的な反応として、
視覚的にハードな印象を与えたり、実際にスライディン
グした時に擦り傷を起こしやすい傾向を示す。７０％を
越え、１００％になると本発明のパイルの構成により感
触や視覚的にも十分なソフトさを与え、快適なプレーを
約束するので好ましい。細繊度のパイルで長さが８ｍｍ
以上であってもパイル密度が高すぎると細繊度パイルの
特徴のソフトさが生かされず固い感触の人工芝が形成さ
れる。また密度が高すぎた場合、砂の詰込みができなく
なり、砂によるプレーヤーの足元をしっかりと支える効
果が得られなくなる。更にパイル先端部が表面を覆うこ
とになり感触は固くなる。パイルの密度が適当に低いと
スライディング時にパイルの動く範囲が大きくなること
により、快適な感触のスライディング性が得られる。In the present invention, the following is considered regarding the covering property of the pile, which is the degree of surface coverage of the pile with respect to the artificial turf. That is, since the sports surface is considered, not only the softness but also the length of the surface is limited due to the problem of abrasion at the time of sliding. The covering property of the pile is important in order to have a structure that eliminates abrasion during sliding. Therefore, as a result of earnest research, it has been found that the object of the present invention can be achieved by minimizing the degree of surface exposure of sand. It is necessary to measure the degree of exposure of sand by a measuring method that considers the practicality of sports. Therefore, the present invention proposes to measure the degree of exposure of the sand by the covering property of the pile. That is,
The covering property of the pile when the artificial turf pile is pressed with a flat plate under a load of 100 g per square meter.
The actual covering property is determined by using a transparent plate such as glass or acrylic as a flat plate, observing the surface state when pressed at 100 g / cm 2 , and measuring the covering area of the pile. It is also possible to simply attach an adhesive tape to a flat plate, measure the exposed area of the sand from the range of sand that adhered to the adhesive tape when pressing the adhesive tape surface on the pile surface, and calculate the covering property of the pile. it can. The greater the surface covering properties of the pile measured in this way, the greater the effect on abrasion reduction and softness during sports,
It has been found that at least 70% or more is preferable from the viewpoint of the effect of the present invention. In other words, below 70%, the surface looks sandy,
It tends to give a visually hard impression or to be easily scratched when actually sliding. When it exceeds 70% and becomes 100%, the pile structure of the present invention provides sufficient softness in feel and visual, and promises comfortable play, which is preferable. 8mm length of fine fine pile
Even with the above, if the pile density is too high, the softness of the characteristics of the fine fineness pile is not utilized, and an artificial turf having a hard feel is formed. On the other hand, if the density is too high, the sand cannot be packed, and the effect of the sand to firmly support the player's feet cannot be obtained. Further, the tip of the pile covers the surface, and the feel becomes hard. If the density of the pile is appropriately low, the range of movement of the pile during sliding is increased, so that a sliding feeling with a comfortable feel is obtained.
【０００９】このパイル密度は、下記式で表されるパイ
ルの断面積の該人工芝平面における占有率、空間占有率
で表すことができる。The pile density can be represented by the occupancy and the space occupancy of the cross-sectional area of the pile expressed by the following equation on the artificial turf plane.
【００１０】空間占有率（％）＝Ｗ／（１０・Ｈ・ρ） ［ 式中、Ｗ：１ｍ2 あたりのパイル重量（ g／ｍ 2 ）、
Ｈ：パイル長さ（mm）、ρ：パイル密度（ g／cm 3 ）］ かかるパイルの断面積の空間占有率の変更は植毛時のト
ータル繊度、タフトのスティッチ等のタフト機の条件変
更により行うことができる。またパイル密度は植込まれ
たパイルの断面積を計算して求めることができる。これ
によりの断面積の空間占有率を決め、本発明の目的のソ
フトな感触や外観が得られるパイル密度を検討した。４
％未満ではパイルが少なく、美観に欠けまたパイルのク
ッション性が無く、本発明の目的が達成できない。８％
を越えると密度が高すぎ、パイル先端が表面を覆う状態
になり、感触が固くなる。つまり、空間占有率が４〜８
％の範囲にある場合に、最適な状態を与える人工芝を形
成することができることがわかった。Space occupancy (%) = W / (10 · H · ρ) [ where W is the pile weight per 1 m 2 (g / m 2 ) ,
H: pile length (mm) , ρ: pile density (g / cm 3 )] The change in the space occupancy of the cross-sectional area of the pile is performed by changing the conditions of the tuft machine such as the total fineness at the time of flocking and the stitch of the tuft. be able to. Further, the pile density can be obtained by calculating the cross-sectional area of the implanted pile. The space occupancy of the cross-sectional area was determined thereby, and the pile density at which the soft feel and appearance of the present invention were obtained was examined. 4
%, The pile is small, lacks aesthetic appearance, and has no cushioning property of the pile, and the object of the present invention cannot be achieved. 8%
Exceeding the density causes the density to be too high and the pile tip to cover the surface, resulting in a hard feel. That is, the space occupancy is 4 to 8
%, It was found that an artificial turf giving optimum conditions could be formed.
【００１１】パイルの全体の長さはスポーツでの実用性
から２０〜５０ｍｍ程度の範囲にあるのが好ましい。本
発明では砂をパイルが８ｍｍ以上突出すように入れるの
でそのときの砂の厚みは１２から４２ｍｍになる。野球
やサッカーのスパイクの長さを考えると最低でも１０ｍ
ｍは必要である。砂の厚みが増すと緩衝性が向上する。
もちろん人工芝の下に合成樹脂性の発泡体のアンダーパ
ッドを敷設するが、ボールのバウンド性の兼合いがあ
り、砂の厚みが厚い方が天然のクレーや天然芝の感触に
近くなる。またあまりパイルが長すぎると製造コストが
高くなりすぎるが、人工芝は摩耗するのでそれを予想し
て長さを設定する必要がある。その点からパイルの長さ
は２５〜４０ｍｍが好ましい範囲である。例えばナイロ
ンで３０ｍｍのパイル長さの場合、パイルの植付け重量
が平方メートルあたり２ｋｇでパイルの断面積の空間占
有率は５．８％となる。The overall length of the pile is preferably in the range of about 20 to 50 mm for practical use in sports. In the present invention, the sand is inserted so that the pile protrudes by 8 mm or more, so that the thickness of the sand at that time becomes 12 to 42 mm. At least 10m considering the length of baseball and soccer spikes
m is required. As the thickness of the sand increases, the buffering property improves.
Of course, an underpad made of synthetic resin foam is laid under the artificial turf, but the ball has a combination of bouncing properties, and the thicker the sand, the closer to the feel of natural clay and natural turf. If the pile is too long, the production cost becomes too high. However, since artificial turf wears, it is necessary to set the length in anticipation of the wear. From that point, the preferred length of the pile is 25 to 40 mm. For example, in the case of a pile length of 30 mm made of nylon, the planting weight of the pile is 2 kg per square meter, and the space occupancy of the cross-sectional area of the pile is 5.8%.
【００１２】本発明により、初めて細繊度糸のソフトさ
を充分に活かすことができ、スライディングや転倒など
のある激しいスポーツに好適な砂入り人工芝を提供する
ことができたものである。According to the present invention, for the first time, it is possible to provide an artificial turf containing sand, which can make full use of the softness of the fineness yarn and is suitable for severe sports such as sliding and falling.
【００１３】[0013]
【実施例】次に実施例により、本発明をさらに詳しく説
明する。Next, the present invention will be described in more detail by way of examples.
【００１４】実施例１、２、３、比較例１、２、３ ナイロン６６のモノフィラメントの直毛糸で単糸の繊度
が２５０、３００、３５０、４００、５００デニールの
５種類の糸を用い、パイル長さ２６ｍｍとし、パイルの
断面積の空間占有率をおおよそ５％として人工芝を作成
した。この５種の人工芝に砂が１６ｍｍの高さになるよ
うに充填した。本発明で定義したパイルの被覆度はいず
れも１００％であった。このような人工芝について感
触、外観、スライディング性がよいか等について官能表
かを実施した。その結果を下表に示す。下表に示すよう
に本発明の人工芝はソフトな触感、外観を示し、スライ
ディング性も大変良い特徴を示している。Examples 1, 2, and 3 and Comparative Examples 1, 2, and 3 A pile of monofilament straight yarn of nylon 66 having a fineness of 250, 300, 350, 400, and 500 deniers. Artificial turf was prepared with a length of 26 mm and a space occupancy of the cross-sectional area of the pile of about 5%. The five types of artificial turf were filled with sand so as to have a height of 16 mm. The coverage of the pile defined in the present invention was 100%. With respect to such artificial turf, whether it is good in feel, appearance, sliding property, etc., it was determined whether it was a functional table. The results are shown in the table below. As shown in the table below, the artificial turf of the present invention has a soft touch and appearance, and also has a very good sliding property.
【００１５】[0015]
【表１】 実施例 ４、５、比較例４、５ ナイロン６６のモノフィラメント、３００デニールの直
毛糸を用い、３０ｍｍのパイル長さにし、パイルの断面
積の空間占有率を５．５％として植込み、人工芝を作成
した。この人工芝を用い、砂の充填量をかえてパイルの
突出し長さを変えて特性を評価した。その結果、下表の
ように、８ｍｍ以上のパイル突出し長さで良好な感触、
外観、スライディング性などの特性が得られることがわ
かった。[Table 1] Examples 4 and 5 and Comparative Examples 4 and 5 A monofilament of nylon 66 and a straight yarn of 300 denier were used, the pile length was set to 30 mm, and the space occupation ratio of the cross-sectional area of the pile was set to 5.5%. Created. Using this artificial turf, the characteristics were evaluated by changing the length of the pile protrusion by changing the amount of sand filling. As a result, as shown in the table below, a good feel with a pile protrusion length of 8 mm or more,
It was found that characteristics such as appearance and sliding properties were obtained.
【表２】 実施例 ６、７、比較例６、７ ナイロン６６のモノフィラメント、２５０デニールの直
毛糸を用い、２８ｍｍのパイル長さにし、パイルの断面
積の空間占有率を３．５％，４．５％，７％，８．５％
にして、人工芝を作成した。これらの人工芝にパイルが
約１０ｍｍ突出すように砂を充填した。これらの砂入り
人工芝の特性を評価した。その結果、パイル密度が低い
人工芝は感触、外観とも貧弱で、耐久性の点でも不安の
あるものであった。高い密度の人工芝は密度が高いため
パイルの倒れる余裕が無く、そのためパイルの先端が手
に触れるため感触が粗硬になった。４．５、７．０％の
人工芝は感触、外観とも良好で、パイルが適度に動ける
余裕があるため、スライディングも快適に行うことがで
きた。[Table 2] Examples 6, 7 and Comparative Examples 6, 7 Using a nylon 66 monofilament and a 250 denier straight yarn, the pile length was set to 28 mm, and the space occupancy of the cross-sectional area of the pile was 3.5%, 4.5%, 7%, 8.5%
Then, artificial turf was created. Sand was filled into these artificial grass so that the pile protruded by about 10 mm. The properties of these artificial turf with sand were evaluated. As a result, the artificial turf having a low pile density was poor in feel and appearance, and was uneasy in terms of durability. Due to the high density of artificial turf, there was no room for the pile to fall over, so the tip of the pile touched the hand and the feel became coarse and hard. The artificial turf of 4.5% and 7.0% had a good feel and appearance, and the pile was able to move moderately, so that the sliding could be performed comfortably.
【００１６】[0016]
【表３】 実施例 ８ ナイロン６６の３００ｄのモノフィラメントについて湿
熱のスタッフィング加工により、かなり強い捲縮加工を
行った。またもう一つは製糸過程で仮撚り加工を行い、
弱い捲縮加工を行った。これらの糸を用い、パイル長３
２ｍｍでパイルの断面積の空間占有率を４．６％で植毛
し、人工芝を作成した。この人工芝に砂を充填し、パイ
ルの突出し長が１０ｍｍ程度にした。捲縮加工糸の場合
はパイルによる表面のカバーリング性が良いためパイル
密度は低めの方がソフト感がでるがいずれの場合も感
触、外観、スライディング性とも良好であった。[Table 3] Example 8 A 300d monofilament of nylon 66 was considerably crimped by wet heat stuffing. Another is to perform false twisting in the process of spinning,
Weak crimping was performed. Using these yarns, pile length 3
The artificial turf was prepared by implanting the hair at a space occupation ratio of 4.6% of the pile cross section at 2 mm. The artificial turf was filled with sand, and the protruding length of the pile was set to about 10 mm. In the case of the crimped yarn, the lower the pile density, the better the softness due to the good covering properties of the surface by the pile, but in all cases, the feel, appearance, and sliding properties were also good.
【００１７】実施例９、比較例８ ナイロン６６の３００デニールのモノフィラメントで円
形断面のものと、幅と厚みの比が５の断面を持つモノフ
ィラメントの生糸を用い、パイル長３０mmの人工芝を作
製した。この人工芝のパイル密度は１４００ gで、断面
積の空間占有率は４％であった。円形断面のものは、剛
直になり、風合が硬く、外観も人工的で今ひとつであっ
た。断面が平面的な幅と厚みの比が５程度のものでは風
合がソフトで外観も良く、適度なヘタリが天然芝の外観
を呈していた。Example 9 and Comparative Example 8 An artificial turf having a pile length of 30 mm was prepared using a 300 denier monofilament of nylon 66 having a circular cross section and a monofilament raw yarn having a cross section having a width-to-thickness ratio of 5. . The pile density of this artificial turf was 1400 g, and the space occupancy of the cross-sectional area was 4%. Those with a circular cross section were rigid, had a hard feel, and had an unnatural appearance. When the ratio of the width to the thickness of the cross section was about 5, the feel was soft and the appearance was good, and a moderate stiffness exhibited the appearance of natural grass.
【００１８】[0018]
【発明の効果】本発明の砂入り人工芝によれば、細繊度
のモノフィラメントが砂の表層部のほとんどを覆うよう
に形成するので、また、植込み密度が適度に低いので、
手触りが極めてソフトな感触を与え、スライディング時
の擦り傷や火傷防止等の効果を発揮し、さらに、砂の層
が適度に厚いので、スポーツ用サーフェスとして必要な
弾性と耐久性を有し、スポーツに好適な、安全な砂入り
人工芝を提供することができる。特に、転倒やスライデ
ィングなどが伴うハードなスポーツに好適なグランドを
提供することができる。According to the artificial turf containing sand of the present invention, the fine filaments are formed so as to cover most of the surface layer of the sand, and the planting density is appropriately low.
Gives an extremely soft touch and has the effect of preventing scratches and burns when sliding.In addition, since the sand layer is moderately thick, it has the elasticity and durability required for sports surfaces, A suitable and safe artificial turf containing sand can be provided. In particular, it is possible to provide a ground suitable for a hard sport involving falling or sliding.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平６−101209（ＪＰ，Ａ) 特開 平６−128903（ＪＰ，Ａ) 特開 平５−171614（ＪＰ，Ａ) 特開 平４−185803（ＪＰ，Ａ) 特開 平４−106203（ＪＰ，Ａ) 特開 平６−158609（ＪＰ，Ａ) 特開 平４−347203（ＪＰ，Ａ) 特開 平１−131628（ＪＰ，Ａ) 特開 平４−131412（ＪＰ，Ａ) (58)調査した分野(Int.Cl.6，ＤＢ名) E01C 13/08 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-6-101209 (JP, A) JP-A-6-128903 (JP, A) JP-A-5-171614 (JP, A) 185803 (JP, A) JP-A-4-106203 (JP, A) JP-A-6-158609 (JP, A) JP-A-4-347203 (JP, A) JP-A-1-131628 (JP, A) JP-A-4-131412 (JP, A) (58) Fields investigated (Int. Cl. 6 , DB name) E01C 13/08
Claims (5)
砂入り人工芝であって、該モノフィラメントが１００デ
ニール以上３５０デニール以下で、かつ砂からの突出し
た部分の該パイルの平均長さが８ｍｍ以上であり、しか
も、下式で表される該パイルの断面積の該人工芝平面に
おける占有率（空間占有率）が４％以上８％以下である
砂入り人工芝。 空間占有率（％）＝Ｗ／（１０・Ｈ・ρ） ［ 式中、Ｗ：１ｍ2 あたりのパイル重量（ g／ｍ 2 ）、
Ｈ：パイル長さ（mm）、ρ：パイル密度（ g／cm 3 ）］ 1. An artificial turf containing sand made of a nylon monofilament pile, wherein the monofilament is 100 denier or more and 350 denier or less, and the average length of the pile at a portion protruding from the sand is 8 mm or more, and An artificial turf containing sand, wherein an occupancy (space occupancy) of the cross-sectional area of the pile in the artificial turf plane represented by the following formula is 4% or more and 8% or less. Space occupancy (%) = W / (10 · H · ρ) [ where, W: pile weight per 1 m 2 (g / m 2 ) ,
H: pile length (mm) , ρ: pile density (g / cm 3 )]
芝を上方から平板で押さえ付けた時のパイルの表面カバ
ーリング性が７０％以上であることを特徴とする請求項
１記載の砂入り人工芝。2. A surface covering of the pile when the addition of artificial turf load was pressed with a flat plate from above the square cm per 100g is equal to or less than 70% according to claim 1 containing sand Artificial turf.
幅の比が３以上であることを特徴とする請求項１または
２記載の人工芝。人工芝。3. A process according to claim 1, wherein the ratio of the maximum and minimum widths of the cross-section of the monofilaments is greater than or equal to three or
2. The artificial turf according to 2 . Artificial turf.
を特徴とする請求項１〜３のいずれかに記載の人工芝。4. A synthetic turf according to any one of claims 1 to 3 in which the monofilament yarn is characterized in that it is a crimped yarn.
を特徴とする請求項１〜４のいずれかに記載の人工芝。5. The artificial turf of any one of claims 1-4 for, characterized in that said monofilament yarn is straight yarn.