JPH09273107A - Artificial lawn with filler - Google Patents

Abstract

PROBLEM TO BE SOLVED: To improve the function, by planting specified curled threads and straight threads in a base cloth and stuffing a filler among the threads and specifying the characteristics of the threads. SOLUTION: A number of curled threads 14 applied with the split processing and straight threads 15 are planted on a base cloth 13 and filler sand 16 is stuffed among the threads 14, 15 to constitute an artificial lawn 10. In this time, the height of the treads 14 is made lower than that of the threads 15 and the front end of the threads 14 is exposed from the filler sand 16 and the threads 14 are curled at the rate of 0. 5 peaks/2.54cm-5 peaks/ 2. 54 am and the thread 15 is a mono-filament type formed of 20-1000 denier per pierce and made of polyamide polyester or the like. In this way, since the curled threads are mixed with the straight threads, an appearance like natural lawn can be obtained. And since a split processing is applied on the curled threads, solidification of the stuffed layer is suppressed and a good grounding touch can be retained for a long time. And also since the straight threads are used as a monofilament type, the skin touch is made favorable.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は充填材入り人工芝生
に係り、さらに詳しく言えば、良好な接地感を長期間維
持できるとともに、肌触りや外観性を向上できる充填材
入り人工芝生に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an artificial lawn containing a filler, and more particularly, to an artificial lawn containing a filler that can maintain a good ground contact feeling for a long period of time and can improve touch and appearance. .

【０００２】[0002]

【従来の技術】近年、例えばテニスコートを施工するに
あたっては、導入コスト，維持コストが安価であるとと
もに、比較的天然芝生に近い外観性および接地感が得ら
れる砂入り人工芝生を代表とする充填材入り人工芝生が
多用されている。ここで、充填材入り人工芝生とは、面
状の基布にパイルが多数植設され、これらのパイル間に
目砂，ゴムチップ等の充填材が充填されているものを指
し、特に充填材入り人工芝生として広く用いられ、周知
になっているのが、充填材として砂を採用した砂入り人
工芝生である。2. Description of the Related Art In recent years, for example, when constructing a tennis court, the cost of introduction and maintenance is low, and a filling typified by a sand-filled artificial lawn, which is relatively close in appearance and feels like a natural lawn. Artificial grass with wood is often used. Here, the artificial turf with a filler refers to a sheet-like base cloth in which a large number of piles are planted, and fillers such as sand grains and rubber chips are filled between these piles, in particular with a filler. A widely used and well-known artificial grass is a sand-containing artificial grass that uses sand as a filler.

【０００３】このような充填材入り人工芝生は、同一形
態のパイルを均一、かつ、高密度に植設すると、観者に
例えば頭髪用ブラシや歯ブラシ等を連想させ、芝面が実
際以上に硬いという印象を与える。そして、このような
印象を充填材入り人工芝生において競技する競技者に与
えると、競技者が芝面の硬さを考慮して、例えば思い切
ったスライディング等を行えなくなり、競技自体の性格
が変わる虞れがある。したがって、充填材入り人工芝生
においては、観者に軟らかい印象を与えるように、人工
芝生に近似した外観性が求められている。さらに、充填
材入り人工芝生は、競技用スパイク等により充填材が突
き固められると、充填材間の空隙が減少して充填層が次
第に固化し、施工当初に得られた良好な接地感が損なわ
れるという問題があり、各種工夫がなされている。In such an artificial lawn containing a filler, when piles of the same shape are planted uniformly and with high density, the viewer is reminded of, for example, a hair brush or a toothbrush, and the grass surface is harder than it actually is. Gives the impression. When such an impression is given to a competitor who competes in an artificial lawn with a filling material, the competitor may not be able to perform drastic sliding in consideration of the hardness of the turf surface, which may change the character of the competition itself. There is Therefore, the artificial grass with the filler is required to have an appearance similar to that of the artificial grass so as to give the viewer a soft impression. Furthermore, in artificial turf with fillers, when the fillers are tampered with by spikes for competition, the gap between the fillers decreases and the filler layer gradually solidifies, impairing the good grounding feeling obtained at the beginning of construction. There is a problem that it is done, and various ideas have been made.

【０００４】例えば、本願出願人は、ストレート糸と、
スプリット加工が施された捲縮糸とを基布に多数植設し
た砂入り人工芝生を提案した（特願平７−２８４４６７
号：従来例）。この従来例によれば、ストレート糸およ
び捲縮糸が混在しているため、比較的人工芝生に近似し
た外観性が得られる。また、この従来例では、捲縮糸に
施されたスプリット加工により充填層の内部に空隙が形
成されるため、充填層の固化が抑制され、これにより良
好な接地感を長期間維持できる。[0004] For example, the applicant of the present application, straight yarn,
We proposed an artificial lawn containing sand in which a large number of split crimped yarns were planted on a base fabric (Japanese Patent Application No. 7-284467).
No .: Conventional example). According to this conventional example, since the straight yarn and the crimped yarn are mixed, the appearance that is relatively similar to the artificial lawn can be obtained. Further, in this conventional example, since the voids are formed inside the filling layer by the split processing applied to the crimped yarn, the solidification of the filling layer is suppressed, and thereby a good ground feeling can be maintained for a long period of time.

【０００５】[0005]

【発明が解決しようとする課題】しかしながら、近年で
は、充填材入り人工芝生に対して、さらに良好な肌触り
や外観性が求められつつある。本発明は、このような要
望を満たすためになされたもので、その目的は、良好な
接地感を長期間維持できるとともに、肌触りや外観性を
一層向上できる充填材入り人工芝生を提供することにあ
る。However, in recent years, it has been demanded for artificial turf containing a filler to have better touch and appearance. The present invention has been made to satisfy such a demand, and an object thereof is to provide an artificial lawn with a filler capable of maintaining a good ground contact feeling for a long period of time and further improving the touch and the appearance. is there.

【０００６】[0006]

【課題を解決するための手段】前記目的を達成するため
に、本発明の請求項１に記載した発明は、スプリット加
工が施された捲縮糸と、ストレート糸とが基布に多数植
設され、前記捲縮糸および前記ストレート糸間に充填材
が充填された充填材入り人工芝生において、前記ストレ
ート糸がモノフィラメントタイプであることを特徴とし
ている。In order to achieve the above object, the invention described in claim 1 of the present invention is such that a large number of split crimped yarns and straight yarns are planted on a base cloth. In the artificial grass with a filler in which a filler is filled between the crimped yarn and the straight yarn, the straight yarn is a monofilament type.

【０００７】この場合、捲縮糸としては、例えばテープ
状や棒状，あるいは筒状のパイルに捲縮加工を施せばよ
い。そして、捲縮加工としては、例えばテープ状のパイ
ルが略波形状となるように加工したり、あるいは棒状，
筒状のパイルが略蛇腹形状となるように加工すればよ
く、例えばニットデニット製法やジェット製法等により
所望形状に形成すればよい。さらに、スプリット加工と
しては、パイルに直線，曲線等の切り込みを形成してお
けばよく、切り込みに囲まれた部分が捲縮加工に伴って
捲縮糸から突出するようにしておけばよい。そして、ス
トレート糸としては、使用状態に応じて適宜スプリット
加工を施しておいてもよい。In this case, as the crimped yarn, for example, tape-shaped, rod-shaped, or tubular piles may be crimped. As the crimping process, for example, a tape-shaped pile is processed into a substantially corrugated shape, or a bar-shaped pile,
The tubular pile may be processed so as to have a substantially bellows shape, and may be formed into a desired shape by, for example, a knit-denit manufacturing method or a jet manufacturing method. Further, as the split processing, it is sufficient to form a cut such as a straight line or a curved line in the pile, and a portion surrounded by the cut may be projected from the crimped yarn in accordance with the crimp processing. Then, the straight yarn may be appropriately split according to the state of use.

【０００８】また、これらの捲縮糸およびストレート糸
は、基布に形成されたタフト孔に対して一本づつ個別に
植設してもよく、あるいは複数本を束にして個別に植設
してもよい。そして、捲縮糸およびストレート糸は、基
布に設けられた同一タフト孔に混在させた状態で植設し
てもよく、あるいは別個のタフト孔に対して交互に植設
したり、ランダムに植設してもよい。さらに、捲縮糸お
よびストレート糸を複数本づつ束ねた場合には、それぞ
れ同一長さを有していてもよく、あるいは別個の長さを
有していてもよい。また、充填材としては、砂，土，樹
脂粒子，コルク等が採用でき、これらを単体あるいは混
合して充填すればよい。These crimped yarns and straight yarns may be individually planted in the tuft holes formed in the base cloth, or a plurality of tufted yarns may be bundled and individually planted. May be. The crimped yarn and the straight yarn may be mixed in the same tuft hole provided in the base cloth, or may be alternately arranged in separate tuft holes or randomly. You may set it up. Further, when a plurality of crimped yarns and a plurality of straight yarns are bundled, they may have the same length or may have different lengths. Further, as the filler, sand, soil, resin particles, cork, etc. can be adopted, and these may be filled alone or in a mixture.

【０００９】このような本発明の請求項１に記載した発
明においては、捲縮糸およびストレート糸が基布に混植
されているため、これらの捲縮糸およびストレート糸が
露出するように充填材を充填すれば、従来と同様に比較
的人工芝生に近似した外観性が得られることになる。そ
して、請求項１に記載した発明においては、捲縮糸にス
プリット加工が施されているため充填層の固化が抑制さ
れ、従来と同様に良好な接地感を長期間維持できること
になる。一方、この請求項１に記載した発明において
は、ストレート糸がモノフィラメントタイプであるた
め、例えばテープ状のストレート糸を採用した場合に比
較して、良好な肌触りおよび外観性が得られることにな
り、これにより前記目的が達成される。In the invention described in claim 1 of the present invention, since the crimped yarn and the straight yarn are mixedly planted in the base cloth, the filler is so exposed that the crimped yarn and the straight yarn are exposed. By filling with, the appearance similar to that of artificial grass can be obtained as in the conventional case. Further, in the invention described in claim 1, since the crimped yarn is subjected to the split processing, the solidification of the filling layer is suppressed, and a good ground contact feeling can be maintained for a long time as in the conventional case. On the other hand, in the invention described in claim 1, since the straight yarn is a monofilament type, good touch and appearance can be obtained as compared with the case where a tape-shaped straight yarn is adopted, This achieves the above object.

【００１０】また、請求項２に記載した発明において
は、前記捲縮糸が前記ストレート糸よりも低く、かつ、
先端が前記充填材から露出する高さを有していることを
特徴としているため、ストレート糸および捲縮糸が凹凸
状に混在した芝面となり、一層天然芝生に近似した外観
性が得られることになる。そして、請求項３に記載した
発明は、前記捲縮糸の山数が０．５山／２．５４ｃｍな
いし５山／２．５４ｃｍであることを特徴としているた
め、捲縮糸に適度な捲縮形状が得られることになる。し
たがって、請求項３に記載した発明においては、天然芝
生に近似した外観性が得られるとともに、充填材の過度
な充填を効果的に防止できることになる。さらに、請求
項４に記載した発明においては、前記ストレート糸の太
さが２０デニールないし１０００デニールであることを
特徴としているため、適度な細さのストレート糸によ
り、耐久性を維持しながら一層良好な肌触りが得られる
ことになる。In the invention described in claim 2, the crimped yarn is lower than the straight yarn, and
Since the tip has a height exposed from the filler, it becomes a turf surface in which straight yarns and crimped yarns are unevenly mixed, and an appearance more similar to a natural lawn can be obtained. become. The invention according to claim 3 is characterized in that the number of ridges of the crimped yarn is 0.5 ridges / 2.54 cm to 5 ridges / 2.54 cm. A reduced shape will be obtained. Therefore, in the invention described in claim 3, the appearance similar to that of the natural lawn can be obtained, and the excessive filling of the filler can be effectively prevented. Further, in the invention described in claim 4, since the thickness of the straight yarn is 20 denier to 1000 denier, the straight yarn having an appropriate thinness is more preferable while maintaining durability. You will get a nice touch.

【００１１】また、請求項５に記載した発明は、前記充
填材が弾性を有していることを特徴とし、例えば粒状，
棒状のゴムチップや、コルクチップ等が採用できる。そ
して、この充填材は、単独で用いてもよく、あるいは砂
等と混合して用いてもよい。この請求項５に記載した発
明においては、捲縮糸に適度に保持された充填材が常に
充填層に存在するため、弾力性に富んだ良好な接地感が
常時得られることになる。Further, the invention described in claim 5 is characterized in that the filling material has elasticity, for example, granular,
Rod-shaped rubber chips, cork chips, etc. can be used. The filler may be used alone or may be mixed with sand or the like. In the invention described in claim 5, since the filling material appropriately held in the crimped yarn is always present in the filling layer, a good ground contact feeling with rich elasticity can always be obtained.

【００１２】そして、請求項６に記載した発明は、前記
ストレート糸がポリアミドおよびポリエステルのうちの
少なくとも一方により形成された糸を主体としているこ
とを特徴としている。この請求項６に記載した発明にお
いては、ストレート糸が他の材質により形成された場合
に比較して良好な直立性を示すため、経時変化により倒
れることが少ないとともに、良好な水はけを維持できる
ことになる。なお、ポリアミドおよびポリエステルのう
ちの少なくとも一方により形成された糸の比率は、すべ
てのストレート糸に対して２０％以上とすることが好ま
しい。The invention set forth in claim 6 is characterized in that the straight yarn is mainly composed of a yarn formed of at least one of polyamide and polyester. In the invention described in claim 6, since the straight yarn exhibits a good uprightness as compared with the case where the straight yarn is made of another material, it is less likely to collapse due to a change with time, and good drainage can be maintained. Become. The ratio of the yarn formed of at least one of polyamide and polyester is preferably 20% or more with respect to all straight yarns.

【００１３】[0013]

【発明の実施の形態】図１には、本発明に係る一実施例
が示されている。本実施例において、充填材入り人工芝
生である砂入り人工芝生１０は、例えばテニスコート等
の運動競技場を施工するために、基礎地面１１上に打設
された下地材１２の上に敷設されている。なお、本実施
例の砂入り人工芝生１０は、コンクリート等を打設する
ことにより平坦化された下地材１２の上に敷設されてい
るが、例えば基礎地面１１上に並べて敷いた砕石等の粒
体の上に敷設してもよく、あるいは下地材１２を省いて
もよい。さらに、砂入り人工芝生１０は、下地材１２の
上にゴムシート等を敷設することにより、弾性層を設け
てもよい。この砂入り人工芝生１０は、面状の基布１３
に捲縮糸１４およびストレート糸１５が所定の比率で植
設されている。そして、捲縮糸１４およびストレート糸
１５間には、充填材である目砂１６がデッキブラシによ
り充填され、これにより充填層１７が形成されている。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS FIG. 1 shows an embodiment according to the present invention. In this embodiment, a sand-containing artificial lawn 10 which is an artificial lawn containing a filler is laid on a base material 12 cast on a base ground 11 in order to construct an athletic field such as a tennis court. ing. The sand-containing artificial lawn 10 of the present embodiment is laid on a base material 12 that is flattened by pouring concrete or the like, but for example, grains of crushed stone or the like laid side by side on the foundation ground 11 It may be laid on the body or the base material 12 may be omitted. Further, the sand-containing artificial lawn 10 may be provided with an elastic layer by laying a rubber sheet or the like on the base material 12. This sand-containing artificial lawn 10 has a planar base cloth 13
The crimped yarns 14 and the straight yarns 15 are planted in a predetermined ratio. A space between the crimped yarn 14 and the straight yarn 15 is filled with filler sand 16 which is a filler by a deck brush, thereby forming a filler layer 17.

【００１４】なお、本実施例では、充填材として目砂１
６を例示しているが、例えば粒状，棒状のゴムチップ
や、粉砕したコルクチップ等の弾性を有する充填材を採
用してもよい。このような充填材によれば、充填層に弾
力性が得られ、接地感を一層良好にできる。Incidentally, in this embodiment, as a filler, sand 1 is used.
Although 6 is shown as an example, elastic fillers such as granular or rod-shaped rubber chips and crushed cork chips may be used. With such a filling material, elasticity can be obtained in the filling layer, and the ground contact feeling can be further improved.

【００１５】図２に示すように、捲縮糸１４は略テープ
状とされ、スプリット加工および捲縮加工が施されてい
る。この捲縮糸１４は、基布１３に形成されたタフト孔
に複数本を一束として植設されている（図１参照）。一
方、ストレート糸１５は、例えばポリアミドあるいはポ
リエステルにより２０デニール／本〜１０００デニール
／本に形成されたモノフィラメントタイプとされ、基布
１３に形成されたタフト孔に複数本を一束として植設さ
れている。As shown in FIG. 2, the crimped yarn 14 has a substantially tape shape, and is split and crimped. A plurality of the crimped yarns 14 are planted in a tuft hole formed in the base fabric 13 as a bundle (see FIG. 1). On the other hand, the straight yarn 15 is of a monofilament type formed of polyamide or polyester in a denier of 20 to 1000 denier per book, and a plurality of tufts are planted in a tuft hole formed in the base cloth 13 as a bundle. There is.

【００１６】これらの捲縮糸１４およびストレート糸１
５は、比率が１：９ないし９：１となるように、基布１
３に対して５／３２ゲージ，３ステッチで交互にタフト
されていて、ストレート糸１５には必要に応じて適宜ス
プリット加工が施される。なお、捲縮糸１４およびスト
レート糸１５の束は、基布に形成された多数のタフト孔
に対してランダムに植設してもよく、一定面積当たりの
混植比率が１：９ないし９：１となればよい。また、捲
縮糸１４およびストレート糸１５は、タフト孔に対して
それぞれ一本づつ植設してもよく、あるいは互いに混在
させた一束を植設してもよい。These crimped yarns 14 and straight yarns 1
5 is the base cloth 1 so that the ratio becomes 1: 9 to 9: 1.
The tufts are alternately tufted with 3/5/32 gauge and 3 stitches, and the straight yarn 15 is appropriately split-processed as necessary. The bundle of crimped yarns 14 and straight yarns 15 may be randomly planted in a large number of tuft holes formed in the base fabric, and the mixed planting ratio per given area is 1: 9 to 9: 1. It should be In addition, the crimped yarn 14 and the straight yarn 15 may be planted one by one in the tuft holes, or may be planted in a bundle mixed with each other.

【００１７】スプリット加工は、捲縮糸１４の厚み方向
に貫通し、かつ、長手方向に連続する多数の切り込み１
４Ａを不規則に形成する。一方、捲縮加工は、捲縮糸１
４が０．５山／２．５４ｃｍないし５山／２．５４ｃｍ
に捲縮するように、ニットデニット製法あるいはジェッ
ト製法により行われる。したがって、捲縮糸１４は、切
り込み１４Ａに囲まれた（挟まれた）突出部１４Ｂが捲
縮加工に伴って湾曲し、捲縮糸１４から突出した空隙２
０を形成する。この空隙２０は、切り込み１４Ａの形態
および捲縮糸１４の捲縮度を適宜選択することにより、
捲縮糸１４の周囲に充填された目砂１６を侵入させ難
く、かつ、侵入した目砂１６を外部に排出し易くする。The split processing is performed by a number of cuts 1 which penetrate the crimped yarn 14 in the thickness direction and are continuous in the longitudinal direction.
4A is irregularly formed. On the other hand, the crimping process is the crimped yarn 1.
4 is 0.5 crests / 2.54 cm or 5 crests / 2.54 cm
The crimping is performed by a knit denit manufacturing method or a jet manufacturing method. Therefore, in the crimped yarn 14, the protruding portion 14 </ b> B surrounded (sandwiched) by the notch 14 </ b> A is curved along with the crimping process, and the void 2 protruding from the crimped yarn 14 is formed.
Form 0. The void 20 is formed by appropriately selecting the form of the cut 14A and the crimping degree of the crimped yarn 14.
It is difficult for the grain sand 16 filled around the crimped yarn 14 to enter, and the grain sand 16 that has entered is easily discharged to the outside.

【００１８】以上のような本実施例の砂入り人工芝生１
０によれば、捲縮糸１４およびストレート糸１５が基布
１３に混植されているため、従来と同様に比較的天然芝
生に近似した外観性が得られる。また、この砂入り人工
芝生１０によれば、捲縮糸１４にスプリット加工が施さ
れているため、充填層１７の固化が抑制され、従来と同
様に良好な接地感を長期間維持できる。一方、本実施例
の砂入り人工芝生１０よれば、ストレート糸１５がモノ
フィラメントタイプであるため、例えばテープ状のスト
レート糸を採用した場合に比較して、良好な肌触りおよ
び外観性が得られる。The artificial grass with sand 1 of this embodiment as described above
According to 0, since the crimped yarn 14 and the straight yarn 15 are mixedly planted in the base cloth 13, the appearance similar to that of a natural lawn can be obtained as in the conventional case. Further, according to the sand-containing artificial lawn 10, since the crimped yarn 14 is subjected to the split processing, the filling layer 17 is suppressed from being solidified, and a good ground contact feeling can be maintained for a long time as in the conventional case. On the other hand, according to the sand-containing artificial lawn 10 of the present embodiment, the straight yarn 15 is a monofilament type, so that, for example, better feel and appearance can be obtained as compared with the case where a tape-shaped straight yarn is adopted.

【００１９】また、捲縮糸１４がストレート糸１５より
も低く、かつ、先端が充填層１７から露出する高さを有
しているため、砂入り人工芝生１０の芝面が凹凸状とな
り、一層天然芝生に近似した外観性が得られる。特に、
捲縮糸１４は、山数が０．５山／２．５４ｃｍないし５
山／２．５４ｃｍであるため、適度な捲縮形状による天
然芝生に近似した外観性が得られるとともに、充填材の
過度な充填を効果的に防止できる。さらに、ストレート
糸１５は、太さが２０デニールないし１０００デニール
であるため、肌触りが一層良好となる。そして、ストレ
ート糸１５は、ポリアミドあるいはポリエステルにより
形成されているため、ストレート糸が他の材質により形
成された場合に比較して良好な直立性を示す。したがっ
て、砂入り人工芝生１０は、ストレート糸１５が経時変
化により倒れることが少ないため、良好な外観性および
排水性を維持できる。Further, since the crimped yarn 14 is lower than the straight yarn 15 and has a height where the tip is exposed from the filling layer 17, the turf surface of the sand-containing artificial lawn 10 becomes uneven, and Appearance similar to that of natural grass can be obtained. Especially,
The number of peaks of the crimped yarn 14 is 0.5 peaks / 2.54 cm to 5
Since the height is 2.54 cm, an appearance similar to that of a natural lawn with an appropriate crimped shape can be obtained, and excessive filling of the filler can be effectively prevented. Further, since the straight yarn 15 has a thickness of 20 denier to 1000 denier, the touch is further improved. Since the straight yarn 15 is made of polyamide or polyester, it shows good uprightness as compared with the case where the straight yarn is made of another material. Therefore, in the sand-containing artificial lawn 10, the straight yarn 15 is less likely to collapse due to a change with time, and thus good appearance and drainage can be maintained.

【００２０】図３および図４には、本発明に係る他の実
施例が示されている。なお、以下に説明する各実施例に
おいて、既に図１および図２において説明した部材につ
いては、図中に同一符号を付すことにより説明を簡略あ
るいは省略する。図３に示す充填材入り人工芝生３０
は、充填層３１の深部が弾性充填材３２により形成され
ている。すなわち、充填層３１は、粒状，棒状のゴムチ
ップや粉砕したコルクチップ等の弾性充填材３２が捲縮
糸１４およびストレート糸１５間に充填された後、この
弾性充填材３２を覆うように目砂１６が充填されてい
る。このような実施例の充填材入り人工芝生３０によれ
ば、充填層３１の深部が弾性充填材３２により形成され
ているため、充填材として砂，土等を単体で採用した場
合に比較して良好な接地感が得られる。3 and 4 show another embodiment according to the present invention. In each embodiment described below, the members already described with reference to FIGS. 1 and 2 are denoted by the same reference numerals in the drawings to simplify or omit the description. Artificial lawn 30 with filler shown in FIG.
In, the deep portion of the filling layer 31 is formed by the elastic filler 32. That is, the filling layer 31 is filled with an elastic filler 32 such as granular or rod-shaped rubber chips or crushed cork chips between the crimped yarns 14 and the straight yarns 15, and then the sand filler is provided so as to cover the elastic fillers 32. 16 are filled. According to the artificial turf 30 with a filling material of such an embodiment, since the deep part of the filling layer 31 is formed by the elastic filling material 32, compared to the case where sand, soil, etc. are used alone as the filling material. A good touch feeling can be obtained.

【００２１】一方、図４に示す充填材入り人工芝生４０
は、互いに混合された目砂１６および前述した弾性充填
材３２により充填層４１が形成されている。このような
実施例の充填材入り人工芝生４０によれば、前述した充
填材入り人工芝生３０と同様な効果が得られる。そし
て、この充填材入り人工芝生４０によれば、充填層４１
を形成するにあたって、捲縮糸１４およびストレート糸
１５間に目砂１６および弾性充填材３２を個別に充填す
る必要がなく、施工を簡略化できる。On the other hand, the artificial grass 40 containing the filler shown in FIG.
The filling layer 41 is formed of the sand 16 and the elastic filler 32 which are mixed with each other. According to the artificial turf 40 with a filler of such an example, the same effect as the artificial turf 30 with a filler mentioned above is acquired. Then, according to the artificial grass 40 containing the filling material, the filling layer 41
When forming the, it is not necessary to individually fill the sand 16 and the elastic filler 32 between the crimped yarn 14 and the straight yarn 15, and the construction can be simplified.

【００２２】[0022]

【実施例】次に、捲縮糸１４，ストレート糸１５につい
ての捲縮度，高さ，太さ，材質，混植比率と、充填層の
構成を変えて実際に砂入り人工芝生１０を多数施工し、
接地感の変化，外観性および耐久性を評価したので、表
１ないし表３に基づいて比較例とともに説明する。[Examples] Next, a large number of artificial grasses 10 with sand are actually constructed by changing the crimping degree, height, thickness, material, mixed planting ratio of the crimped yarn 14 and the straight yarn 15 and the composition of the filling layer. Then
The change in the feeling of contact with the ground, the appearance and the durability were evaluated, and will be described together with Comparative Examples based on Tables 1 to 3.

【００２３】[0023]

【表１】 [Table 1]

【００２４】[0024]

【表２】 [Table 2]

【００２５】[0025]

【表３】 [Table 3]

【００２６】[0026]

【表４】 [Table 4]

【００２７】なお、捲縮糸１４の捲縮度は、捲縮糸１４
を無作為に１００本抽出して山数／２．５４ｃｍを実測
した平均値である。ここで、山数の数え方としては、例
えばボルトにおけるネジ山の数え方に倣った。また、接
地感の変化は、砂入り人工芝生１０を施工した直後にヘ
ッドモデル落下試験によりＧｍａｘ１を測定しておき、
その後、所定の締め固め機により芝面を１００００回圧
縮したとき後に測定したＧｍａｘ２との差をΔＧｍａｘ
として表示した。すなわち、接地感の変化は、ΔＧｍａ
ｘの値が小さいものほど良好であるとして評価した。The crimp degree of the crimped yarn 14 is
Is an average value obtained by measuring 100 peaks / 2.54 cm at random. Here, as the method of counting the number of threads, for example, the method of counting the screw threads on the bolt is followed. In addition, the change in the feeling of contact with the ground is to measure Gmax1 by a head model drop test immediately after the artificial grass 10 containing sand is constructed,
After that, when the grass surface was compressed 10,000 times by a predetermined compactor, the difference from Gmax2 measured later was calculated as ΔGmax.
Displayed as That is, the change in the feeling of contact is ΔGma
The smaller the value of x, the better.

【００２８】さらに、外観性は、前述したように、砂入
り人工芝生１０の施工後に、所定の締め固め機により１
００００回圧縮したときの芝面の外観性を複数の屋外競
技者が視認し、ストレート糸が直立性を維持することに
より、天然芝生の外観性に近似していることを基準とし
て◎‥極めて良好，○‥良好，△‥可，×‥不良とする
４段階評価の平均とした。次に、肌触りの評価として
は、天然芝生上をスライディングしたときの感触に近似
していることを基準として、複数の屋外競技者が砂入り
人工芝生１０の上をスライディングしたときの感触を◎
‥極めて良好，○‥良好，×‥不可とする３段階評価の
平均とした。Further, as described above, the appearance of the sand-filled artificial lawn 10 is 1 by a predetermined compactor after the construction.
The appearance of the turf surface after being compressed 0000 times is visually recognized by multiple outdoor athletes, and the straight thread maintains the uprightness, which is similar to the appearance of a natural lawn. , ○: good, △: good, ×: bad The average of four grades was used. Next, as the evaluation of the skin feel, the feeling when sliding on the artificial grass with sand 10 by a plurality of outdoor athletes is based on being similar to the feeling when sliding on the natural grass.
・ ・ ・ Extremely good, ○ ・ ・ ・ Good, × ・ ・ ・ Not acceptable

【００２９】また、耐久性の評価としては、締め固め機
により芝面を１００００回圧縮した後に、ストレート糸
１５の倒れ（へたり）を前述した複数の屋外競技者が観
察し、◎‥極めて良好，○‥良好，△‥可，×‥不良と
する４段階に評価の平均とした。そして、これらの実施
例および比較例において、捲縮糸１４およびストレート
糸１５が混在している場合には、基布１３に対して５／
３２ゲージ，３ステッチで交互にタフトし、捲縮糸１４
あるいはストレート糸１５を単独で用いた場合には、基
布１３に対して５／３２ゲージ，３ステッチでタフトし
た。Further, as the evaluation of durability, after the turf surface was compressed 10,000 times by a compaction machine, the above-mentioned plural outdoor athletes observed the collapse (sagging) of the straight yarn 15, and ◎ ... very good ∙∙∙∙∙∙∙∙∙∙∙∙∙∙∙ ∘ ∙ In these examples and comparative examples, when the crimped yarn 14 and the straight yarn 15 are mixed, the ratio of 5 /
Alternately tufted with 32 gauge, 3 stitches, crimped yarn 14
Alternatively, when the straight yarn 15 was used alone, the base fabric 13 was tufted with 5/32 gauge and 3 stitches.

【００３０】（実施例１）モノフィラメントタイプのス
トレート糸１５をポリアミドにより太さ４５０デニール
／本，高さ３０ｍｍに形成するとともに、スプリット加
工が施された捲縮糸１４を捲縮度４．００山／２．５４
ｃｍ，高さ２４．０ｍｍに形成した。そして、これらの
ストレート糸１５および捲縮糸１４を２１：７９の比率
で基布１３に混植し、充填材として砂を２５．５ｍｍ充
填した。この実施例１では、ΔＧｍａｘが２，外観性お
よび肌触りが○評価，耐久性が◎評価となっている。(Example 1) A monofilament type straight yarn 15 was formed of polyamide to a thickness of 450 denier / thread and a height of 30 mm, and the split crimped yarn 14 had a crimp degree of 4.00. /2.54
cm and height 24.0 mm. Then, these straight yarns 15 and crimped yarns 14 were mixed and planted in the base cloth 13 at a ratio of 21:79, and 25.5 mm of sand was filled as a filler. In this Example 1, ΔGmax is 2, appearance and touch are evaluated as ◯, and durability is evaluated as ⊚.

【００３１】（実施例２）モノフィラメントタイプのス
トレート糸１５をポリアミドにより太さ４５０デニール
／本，高さ３０ｍｍに形成するとともに、スプリット加
工が施された捲縮糸１４を捲縮度４．０３山／２．５４
ｃｍ，高さ２４．３ｍｍに形成した。そして、これらの
ストレート糸１５および捲縮糸１４を７９：２１の比率
で基布１３に混植し、充填材として砂を２５．５ｍｍ充
填した。この実施例２では、ΔＧｍａｘが４，外観性が
○評価，肌触りおよび耐久性が◎〜○評価となってい
る。(Example 2) Monofilament type straight yarn 15 was formed of polyamide to a thickness of 450 denier / piece and a height of 30 mm, and split crimped yarn 14 was crimped to have a crimp degree of 4.03. /2.54
cm and height 24.3 mm. Then, these straight yarns 15 and crimped yarns 14 were mixed and planted in the base cloth 13 at a ratio of 79:21, and 25.5 mm of sand was filled as a filler. In this Example 2, ΔGmax is 4, the appearance is evaluated as ◯, and the touch and durability are evaluated as ⊚ to ∘.

【００３２】（実施例３）モノフィラメントタイプのス
トレート糸１５をポリエチレンにより太さ４５０デニー
ル／本，高さ３０ｍｍに形成するとともに、スプリット
加工が施された捲縮糸１４を捲縮度３．９９山／２．５
４ｃｍ，高さ２４．６ｍｍに形成した。そして、これら
のストレート糸１５および捲縮糸１４を５０：５０の比
率で基布１３に混植し、充填材として砂を２５．８ｍｍ
充填した。この実施例３では、ΔＧｍａｘが６，外観性
が○評価，肌触りが◎〜○評価，耐久性が○評価となっ
ている。(Embodiment 3) A straight filament 15 of monofilament type is formed of polyethylene to have a thickness of 450 denier / piece and a height of 30 mm, and the crimped yarn 14 subjected to split processing has a crimp degree of 3.99. /2.5
It was formed to have a height of 4 cm and a height of 24.6 mm. Then, these straight yarns 15 and crimped yarns 14 are mixed and planted in the base cloth 13 at a ratio of 50:50, and sand is used as a filler in an amount of 25.8 mm.
Filled. In this Example 3, ΔGmax is 6, the appearance is evaluated as ◯, the touch is evaluated as ⊚ to ◯, and the durability is evaluated as ◯.

【００３３】（実施例４）モノフィラメントタイプのス
トレート糸１５をポリエチレンにより太さ４５０デニー
ル／本，高さ３０ｍｍに形成するとともに、スプリット
加工が施された捲縮糸１４を捲縮度４．１２山／２．５
４ｃｍ，高さ２４．２ｍｍに形成した。そして、これら
のストレート糸１５および捲縮糸１４を５０：５０の比
率で基布１３に混植し、充填材として砂を２２．５ｍｍ
充填した。この実施例４では、ΔＧｍａｘが２，外観性
および肌触りが◎評価，耐久性が○評価となっている。(Embodiment 4) Monofilament type straight yarn 15 is formed of polyethylene to have a thickness of 450 denier / thread and a height of 30 mm, and the split crimped yarn 14 has a crimp degree of 4.12. /2.5
It was formed to have a height of 4 cm and a height of 24.2 mm. Then, these straight yarns 15 and crimped yarns 14 are mixed and planted in the base cloth 13 at a ratio of 50:50, and sand is used as a filling material for 22.5 mm.
Filled. In Example 4, ΔGmax is 2, appearance and touch are evaluated as ⊚, and durability is evaluated as ∘.

【００３４】（実施例５）モノフィラメントタイプのス
トレート糸１５をポリエチレンにより太さ１９デニール
／本，高さ３０ｍｍに形成するとともに、スプリット加
工が施された捲縮糸１４を捲縮度４．５８山／２．５４
ｃｍ，高さ２３．４ｍｍに形成した。そして、これらの
ストレート糸１５および捲縮糸１４を５０：５０の比率
で基布１３に混植し、充填材として砂を２１．０ｍｍ充
填した。この実施例５では、ΔＧｍａｘが４，外観性お
よび肌触りが◎評価，耐久性が○〜△評価となってい
る。(Embodiment 5) Monofilament type straight yarn 15 is formed of polyethylene to have a thickness of 19 denier / piece and a height of 30 mm, and the split crimped yarn 14 has a crimp degree of 4.58 ridges. /2.54
cm and height 23.4 mm. Then, these straight yarns 15 and crimped yarns 14 were mixed and planted in the base cloth 13 at a ratio of 50:50, and 21.0 mm of sand was filled as a filler. In Example 5, ΔGmax is 4, appearance and touch are evaluated as ⊚, and durability is evaluated as ◯ to Δ.

【００３５】（実施例６）モノフィラメントタイプのス
トレート糸１５をポリエチレンにより太さ１０１０デニ
ール／本，高さ３０ｍｍに形成するとともに、スプリッ
ト加工が施された捲縮糸１４を捲縮度４．９６山／２．
５４ｃｍ，高さ２４．６ｍｍに形成した。そして、これ
らのストレート糸１５および捲縮糸１４を５０：５０の
比率で基布１３に混植し、充填材として砂を２０．７ｍ
ｍ充填した。この実施例６では、ΔＧｍａｘが３，外観
性が◎評価，肌触りおよび耐久性が○評価となってい
る。(Embodiment 6) Monofilament type straight yarn 15 is formed of polyethylene to have a thickness of 1010 denier / piece and a height of 30 mm, and the split crimped yarn 14 is crimped at 4.96 threads. / 2.
It was formed to have a height of 54 cm and a height of 24.6 mm. Then, the straight yarns 15 and the crimped yarns 14 are mixed and planted in the base cloth 13 at a ratio of 50:50, and sand as a filler is 20.7 m.
m. In Example 6, ΔGmax is 3, the appearance is evaluated as ⊚, and the touch and durability are evaluated as ∘.

【００３６】（実施例７）モノフィラメントタイプのス
トレート糸１５をポリエチレンにより太さ２５デニール
／本，高さ３０ｍｍに形成するとともに、スプリット加
工が施された捲縮糸１４を捲縮度４．９０山／２．５４
ｃｍ，高さ２５．２ｍｍに形成した。そして、これらの
ストレート糸１５および捲縮糸１４を５０：５０の比率
で基布１３に混植し、充填材として砂を２２．５ｍｍ充
填した。この実施例７では、ΔＧｍａｘが３，外観性お
よび肌触りが◎評価，耐久性が○評価となっている。(Embodiment 7) A monofilament type straight yarn 15 is formed of polyethylene to have a thickness of 25 denier / thread and a height of 30 mm, and the split crimped yarn 14 is crimped at 4.90 threads. /2.54
cm and height 25.2 mm. Then, these straight yarns 15 and crimped yarns 14 were mixed and planted in the base cloth 13 at a ratio of 50:50, and 22.5 mm of sand was filled as a filler. In Example 7, ΔGmax is 3, appearance and touch are evaluated as ⊚, and durability is evaluated as ∘.

【００３７】（実施例８）モノフィラメントタイプのス
トレート糸１５をポリエチレンにより太さ９９０デニー
ル／本，高さ３０ｍｍに形成するとともに、スプリット
加工が施された捲縮糸１４を捲縮度４．４０山／２．５
４ｃｍ，高さ２５．８ｍｍに形成した。そして、これら
のストレート糸１５および捲縮糸１４を５０：５０の比
率で基布１３に混植し、充填材として砂を２２．８ｍｍ
充填した。この実施例８では、ΔＧｍａｘが３，外観性
が◎評価，肌触りが◎〜○評価，耐久性が○評価となっ
ている。(Embodiment 8) Monofilament type straight yarn 15 is formed from polyethylene to have a thickness of 990 denier / piece and a height of 30 mm, and the split crimped yarn 14 is crimped at 4.40 threads. /2.5
It was formed to have a height of 4 cm and a height of 25.8 mm. Then, these straight yarns 15 and crimped yarns 14 are mixed and planted in the base cloth 13 at a ratio of 50:50, and sand as a filler is 22.8 mm.
Filled. In Example 8, ΔGmax is 3, the appearance is evaluated as ⊚, the touch is evaluated as ⊚ to ○, and the durability is evaluated as ∘.

【００３８】（実施例９）モノフィラメントタイプのス
トレート糸１５をポリアミドにより太さ４５０デニール
／本，高さ３０ｍｍに形成するとともに、スプリット加
工が施された捲縮糸１４を捲縮度３．９６山／２．５４
ｃｍ，高さ２４．６ｍｍに形成した。そして、これらの
ストレート糸１５および捲縮糸１４を５０：５０の比率
で基布１３に混植し、充填材として砂を２３．４ｍｍ充
填した。この実施例９では、ΔＧｍａｘが１，外観性，
肌触りおよび耐久性が◎評価となっている。(Embodiment 9) Monofilament type straight yarn 15 is formed of polyamide to a thickness of 450 denier / piece and a height of 30 mm, and the split crimped yarn 14 has a crimp degree of 3.96. /2.54
cm and height 24.6 mm. Then, these straight yarns 15 and crimped yarns 14 were mixed and planted in the base cloth 13 at a ratio of 50:50, and 23.4 mm of sand was filled as a filler. In this Example 9, ΔGmax is 1, appearance,
The skin feel and durability are rated as ◎.

【００３９】（実施例１０）モノフィラメントタイプの
ストレート糸１５をポリエステルにより太さ４５０デニ
ール／本，高さ３０ｍｍに形成するとともに、スプリッ
ト加工が施された捲縮糸１４を捲縮度３．８８山／２．
５４ｃｍ，高さ２４．３ｍｍに形成した。そして、これ
らのストレート糸１５および捲縮糸１４を５０：５０の
比率で基布１３に混植し、充填材として砂を２２．２ｍ
ｍ充填した。この実施例１０では、ΔＧｍａｘが１，外
観性，肌触りおよび耐久性が◎評価となっている。(Embodiment 10) Straight filament 15 of monofilament type is formed of polyester to have a thickness of 450 denier / piece and a height of 30 mm, and the split crimped yarn 14 has a crimp degree of 3.88. / 2.
It was formed to have a height of 54 cm and a height of 24.3 mm. Then, these straight yarns 15 and crimped yarns 14 are mixed and planted in the base cloth 13 at a ratio of 50:50, and sand as a filler is 22.2 m.
m. In Example 10, ΔGmax is 1, and appearance, touch and durability are evaluated as ⊚.

【００４０】（実施例１１）モノフィラメントタイプの
ストレート糸１５をポリアミドにより太さ４５０デニー
ル／本，高さ３０ｍｍに形成するとともに、スプリット
加工が施された捲縮糸１４を捲縮度０．４６山／２．５
４ｃｍ，高さ２５．５ｍｍに形成した。そして、これら
のストレート糸１５および捲縮糸１４を５０：５０の比
率で基布１３に混植し、充填材として砂を２２．５ｍｍ
充填した。この実施例１１では、ΔＧｍａｘが６，外観
性が○評価，肌触りが◎〜○評価，耐久性が○評価とな
っている。(Embodiment 11) Monofilament type straight yarn 15 is formed of polyamide to have a thickness of 450 denier / piece and a height of 30 mm, and the split crimped yarn 14 has a crimp degree of 0.46. /2.5
It was formed to have a height of 4 cm and a height of 25.5 mm. Then, these straight yarns 15 and crimped yarns 14 are mixed and planted in the base cloth 13 at a ratio of 50:50, and sand is used as a filling material for 22.5 mm.
Filled. In Example 11, ΔGmax is 6, the appearance is evaluated as ◯, the touch is evaluated as ⊚ to ◯, and the durability is evaluated as ◯.

【００４１】（実施例１２）モノフィラメントタイプの
ストレート糸１５をポリアミドにより太さ４５０デニー
ル／本，高さ３０ｍｍに形成するとともに、スプリット
加工が施された捲縮糸１４を捲縮度０．５２山／２．５
４ｃｍ，高さ２４．９ｍｍに形成した。そして、これら
のストレート糸１５および捲縮糸１４を５０：５０の比
率で基布１３に混植し、充填材として砂を２３．１ｍｍ
充填した。この実施例１２では、ΔＧｍａｘが３，外観
性および肌触りが◎評価，耐久性が◎〜○評価となって
いる。(Embodiment 12) Monofilament type straight yarn 15 is formed of polyamide to have a thickness of 450 denier / piece and a height of 30 mm, and the split crimped yarn 14 has a crimp degree of 0.52 crests. /2.5
It was formed to have a height of 4 cm and a height of 24.9 mm. Then, these straight yarns 15 and crimped yarns 14 are mixed and planted in the base cloth 13 at a ratio of 50:50, and sand as a filler is 23.1 mm.
Filled. In this Example 12, ΔGmax is 3, appearance and touch are evaluated as ⊚, and durability is evaluated as ∘ to ∘.

【００４２】（実施例１３）モノフィラメントタイプの
ストレート糸１５をポリアミドにより太さ４５０デニー
ル／本，高さ３０ｍｍに形成するとともに、スプリット
加工が施された捲縮糸１４を捲縮度１．０１山／２．５
４ｃｍ，高さ２４．０ｍｍに形成した。そして、これら
のストレート糸１５および捲縮糸１４を５０：５０の比
率で基布１３に混植し、充填材として砂を２２．８ｍｍ
充填した。この実施例１３では、ΔＧｍａｘが２，外観
性，肌触りおよび耐久性が◎評価となっている。(Example 13) Monofilament type straight yarn 15 was formed of polyamide to have a thickness of 450 denier / piece and a height of 30 mm, and the split crimped yarn 14 was crimped with a crimp degree of 1.01. /2.5
It was formed to have a height of 4 cm and a height of 24.0 mm. Then, these straight yarns 15 and crimped yarns 14 are mixed and planted in the base cloth 13 at a ratio of 50:50, and sand as a filler is 22.8 mm.
Filled. In this Example 13, ΔGmax is 2, and appearance, touch and durability are evaluated as ⊚.

【００４３】（実施例１４）モノフィラメントタイプの
ストレート糸１５をポリフッ化ビニリデンにより太さ４
５０デニール／本，高さ３０ｍｍに形成するとともに、
スプリット加工が施された捲縮糸１４を捲縮度３．０６
山／２．５４ｃｍ，高さ２４．０ｍｍに形成した。そし
て、これらのストレート糸１５および捲縮糸１４を５
０：５０の比率で基布１３に混植し、充填材として砂を
２２．８ｍｍ充填した。この実施例１４では、ΔＧｍａ
ｘが１，外観性および肌触りが◎評価，耐久性が◎〜○
評価となっている。(Embodiment 14) A straight filament 15 of monofilament type was made to have a thickness of 4 with polyvinylidene fluoride.
50 denier / piece, height 30mm, and
The crimped yarn 14 subjected to the split processing has a crimping degree of 3.06.
It was formed to have a height of 2.54 cm and a height of 24.0 mm. Then, these straight yarn 15 and crimped yarn 14 are
The base cloth 13 was mixed and planted at a ratio of 0:50, and 22.8 mm of sand was filled as a filler. In this example 14, ΔGma
x is 1, appearance and feel are ◎, and durability is ◎ to ○
It is evaluated.

【００４４】（実施例１５）モノフィラメントタイプの
ストレート糸１５をポリアミドにより太さ４５０デニー
ル／本，高さ３０ｍｍに形成するとともに、スプリット
加工が施された捲縮糸１４を捲縮度５．１０山／２．５
４ｃｍ，高さ２４．０ｍｍに形成した。そして、これら
のストレート糸１５および捲縮糸１４を５０：５０の比
率で基布１３に混植し、充填材として砂を２２．５ｍｍ
充填した。この実施例１５では、ΔＧｍａｘが３，外観
性が○評価，肌触りが◎〜○評価，耐久性が○評価とな
っている。(Example 15) A monofilament type straight yarn 15 was formed from polyamide to a thickness of 450 denier / piece and a height of 30 mm, and the split crimped yarn 14 was crimped at a degree of 5.10. /2.5
It was formed to have a height of 4 cm and a height of 24.0 mm. Then, these straight yarns 15 and crimped yarns 14 are mixed and planted in the base cloth 13 at a ratio of 50:50, and sand is used as a filling material for 22.5 mm.
Filled. In Example 15, ΔGmax is 3, the appearance is evaluated as ◯, the touch is evaluated as ⊚ to ◯, and the durability is evaluated as ◯.

【００４５】（実施例１６）モノフィラメントタイプの
ストレート糸１５をポリアミドにより太さ４５０デニー
ル／本，高さ３０ｍｍに形成するとともに、スプリット
加工が施された捲縮糸１４を捲縮度４．９５山／２．５
４ｃｍ，高さ２４．０ｍｍに形成した。そして、これら
のストレート糸１５および捲縮糸１４を５０：５０の比
率で基布１３に混植し、充填材として砂を２２．２ｍｍ
充填した。この実施例１６では、ΔＧｍａｘが１，外観
性および肌触りが◎評価，耐久性が◎〜○評価となって
いる。(Example 16) A straight filament 15 of monofilament type was formed from polyamide to a thickness of 450 denier / piece and a height of 30 mm, and the split crimped yarn 14 was crimped at 4.95 threads. /2.5
It was formed to have a height of 4 cm and a height of 24.0 mm. Then, these straight yarns 15 and crimped yarns 14 are mixed and planted in the base cloth 13 at a ratio of 50:50, and sand as a filler is 22.2 mm.
Filled. In this Example 16, ΔGmax is 1, appearance and touch are evaluated as ⊚, and durability is evaluated as ∘ to ∘.

【００４６】（実施例１７）モノフィラメントタイプの
ストレート糸１５をポリアミドにより太さ４５０デニー
ル／本，高さ３０ｍｍに形成するとともに、スプリット
加工が施された捲縮糸１４を捲縮度３．９８山／２．５
４ｃｍ，高さ２４．７ｍｍに形成した。そして、これら
のストレート糸１５および捲縮糸１４を５０：５０の比
率で基布１３に混植し、ゴム粒および砂を混合した充填
材を２３．０ｍｍ充填した。この実施例１７では、ΔＧ
ｍａｘが０，外観性および肌触りが◎〜○評価，耐久性
が◎評価となっている。(Example 17) A straight filament 15 of monofilament type was formed from polyamide to a thickness of 450 denier / piece and a height of 30 mm, and the crimped yarn 14 subjected to the split processing had a crimp degree of 3.98. /2.5
It was formed to have a height of 4 cm and a height of 24.7 mm. Then, these straight yarns 15 and crimped yarns 14 were mixed and planted in the base cloth 13 at a ratio of 50:50, and 23.0 mm of a filler in which rubber particles and sand were mixed was filled. In this example 17, ΔG
Max is 0, appearance and touch are rated ⊚- ○, and durability is rated ⊚.

【００４７】（実施例１８）モノフィラメントタイプの
ストレート糸１５をポリアミドにより太さ４５０デニー
ル／本，高さ３０ｍｍに形成するとともに、スプリット
加工が施された捲縮糸１４を捲縮度３．９０山／２．５
４ｃｍ，高さ２４．３ｍｍに形成した。そして、これら
のストレート糸１５および捲縮糸１４を５０：５０の比
率で基布１３に混植し、ゴム粒を充填した後、砂を充填
して充填層を２３．０ｍｍに形成した。この実施例１８
では、ΔＧｍａｘが０，外観性，肌触りおよび耐久性が
◎評価となっている。(Example 18) Monofilament type straight yarn 15 was formed of polyamide to have a thickness of 450 denier / piece and a height of 30 mm, and the split crimped yarn 14 had a crimp degree of 3.90. /2.5
It was formed to have a height of 4 cm and a height of 24.3 mm. Then, these straight yarns 15 and crimped yarns 14 were mixed and planted in the base cloth 13 at a ratio of 50:50, rubber particles were filled, and then sand was filled to form a filled layer having a thickness of 23.0 mm. This Example 18
In the above, ΔGmax is 0, and appearance, touch and durability are evaluated as ⊚.

【００４８】（実施例１９）モノフィラメントタイプの
ストレート糸１５をポリアミドにより太さ４５０デニー
ル／本，高さ３０ｍｍに形成するとともに、スプリット
加工が施された捲縮糸１４を捲縮度３．９１山／２．５
４ｃｍ，高さ２４．３ｍｍに形成した。そして、これら
のストレート糸１５および捲縮糸１４を５０：５０の比
率で基布１３に混植し、充填材としてゴム粒を２２．６
ｍｍ充填した。この実施例１９では、ΔＧｍａｘが０，
外観性および肌触りが○評価，耐久性が◎評価となって
いる。(Example 19) A straight filament 15 of monofilament type was formed from polyamide to a thickness of 450 denier / piece and a height of 30 mm, and the crimped yarn 14 subjected to split processing had a crimp degree of 3.91. /2.5
It was formed to have a height of 4 cm and a height of 24.3 mm. Then, these straight yarns 15 and crimped yarns 14 are mixed and planted in the base cloth 13 in a ratio of 50:50, and rubber particles are used as a filler in an amount of 22.6.
mm filled. In this Example 19, ΔGmax is 0,
Appearance and touch are rated as ○, and durability is rated as ◎.

【００４９】（実施例２０）モノフィラメントタイプの
ストレート糸１５をポリアミドにより太さ４５０デニー
ル／本，高さ２８．５ｍｍに形成するとともに、スプリ
ット加工が施された捲縮糸１４を捲縮度４．３２山／
２．５４ｃｍ，高さ３０ｍｍに形成した。そして、これ
らのストレート糸１５および捲縮糸１４を５０：５０の
比率で基布１３に混植し、充填材として砂を２６．４ｍ
ｍ充填した。この実施例２０では、ΔＧｍａｘが２，外
観性および肌触りが○〜△評価，耐久性が◎〜○評価と
なっている。(Embodiment 20) Monofilament type straight yarn 15 is formed of polyamide to have a thickness of 450 denier / piece and a height of 28.5 mm, and the split crimped yarn 14 has a crimping degree of 4. 32 mountains /
It was formed to have a height of 2.54 cm and a height of 30 mm. Then, these straight yarns 15 and crimped yarns 14 are mixed and planted in the base cloth 13 at a ratio of 50:50, and sand as a filler is 26.4 m.
m. In this Example 20, ΔGmax is 2, appearance and touch are evaluated as ◯ to Δ, and durability is evaluated as ⊚ to ◯.

【００５０】（比較例１）スプリット加工が施された捲
縮糸１４を捲縮度４．０３山／２．５４ｃｍ，高さ２
５．０ｍｍに形成して基布１３に植設し、充填材として
砂を２２．５ｍｍ充填した。この比較例１では、ΔＧｍ
ａｘが３，外観性および肌触りが×評価，耐久性が○評
価となっている。 （比較例２）モノフィラメントタイプのストレート糸１
５をポリアミドにより太さ４５０デニール／本，高さ３
０ｍｍに形成して基布１３に植設し、充填材として砂を
２７．０ｍｍ充填した。この比較例２では、ΔＧｍａｘ
が９，外観性が○〜△評価，肌触りが○評価，耐久性が
△〜×評価となっている。(Comparative Example 1) The crimped yarn 14 subjected to the split processing was crimped with a crimp degree of 4.03 peaks / 2.54 cm and a height of 2.
It was formed into 5.0 mm and planted in the base cloth 13, and 22.5 mm of sand was filled as a filler. In this comparative example 1, ΔGm
The ax is 3, the appearance and touch are evaluated as x, and the durability is evaluated as o. (Comparative Example 2) Monofilament type straight yarn 1
Polyamide 5 with thickness 450 denier / piece, height 3
It was formed into 0 mm and was planted in the base cloth 13, and was filled with sand as a filling material in an amount of 27.0 mm. In this comparative example 2, ΔGmax
No. 9, the appearance was evaluated as ○ to △, the touch was evaluated as ○, and the durability was evaluated as △ to ×.

【００５１】（比較例３）テープ状でスプリット加工が
施されたストレート糸をポリアミドにより太さ４５０デ
ニール／本，高さ３０ｍｍに形成するとともに、スプリ
ット加工が施された捲縮糸１４を捲縮度４．２０山／
２．５４ｃｍ，高さ２７．０ｍｍに形成した。そして、
これらのストレート糸および捲縮糸１４を５０：５０の
比率で基布１３に混植し、充填材として砂を２５．４ｍ
ｍ充填した。この比較例３では、ΔＧｍａｘが２，外観
性が△評価，肌触りが×評価，耐久性が◎〜○評価とな
っている。(Comparative Example 3) A straight yarn in the form of a tape, which is split, is formed of polyamide to a thickness of 450 denier / piece and a height of 30 mm, and the crimped yarn 14 which is split is crimped. 4.20 degrees /
It was formed to have a height of 2.54 cm and a height of 27.0 mm. And
These straight yarns and crimped yarns 14 were mixed and planted in the base cloth 13 at a ratio of 50:50, and 25.4 m of sand was used as a filler.
m. In Comparative Example 3, ΔGmax is 2, appearance is evaluated as Δ, touch is evaluated as ×, and durability is evaluated as ⊚ to ∘.

【００５２】（比較例４）マルチフィラメントタイプの
ストレート糸をポリアミドにより太さ４５０デニール／
束，高さ３０ｍｍに形成するとともに、スプリット加工
が施された捲縮糸１４を捲縮度４．１９山／２．５４ｃ
ｍ，高さ２６．４ｍｍに形成した。そして、これらのス
トレート糸および捲縮糸１４を５０：５０の比率で基布
１３に混植し、充填材として砂を２２．８ｍｍ充填し
た。この比較例４では、ΔＧｍａｘが３，外観性が×評
価，肌触りが○評価，耐久性が×評価となっている。(Comparative Example 4) A straight filament of multifilament type was made of polyamide and had a thickness of 450 denier /
The crimp yarn 14 formed into a bundle and a height of 30 mm and subjected to a split process has a crimp degree of 4.19 ridges / 2.54c.
m and height 26.4 mm. Then, these straight yarns and crimped yarns 14 were mixed and planted in the base cloth 13 at a ratio of 50:50, and 22.8 mm of sand was filled as a filler. In Comparative Example 4, ΔGmax is 3, the appearance is evaluated as x, the touch is evaluated as o, and the durability is evaluated as x.

【００５３】（比較例５）モノフィラメントタイプのス
トレート糸１５をポリアミドにより太さ４５０デニール
／本，高さ３０ｍｍに形成して基布１３に植設し、充填
材としてゴム粒を２７．０ｍｍ充填した。この比較例５
では、ΔＧｍａｘが２，外観性および肌触りが△評価，
耐久性が△〜×評価となっている。(Comparative Example 5) Monofilament type straight yarn 15 was formed with polyamide to a thickness of 450 denier / piece and a height of 30 mm, and was planted in a base cloth 13, and 27.0 mm of rubber particles were filled as a filler. . This Comparative Example 5
Then, ΔGmax is 2, appearance and touch are evaluated as Δ,
Durability is evaluated as Δ to ×.

【００５４】以上の評価から、各実施例は、ストレート
糸および捲縮糸が混植されているため、比較例１および
比較例２に比較して外観性および肌触りに優れているこ
とが判る。そして、各実施例は、ストレート糸がモノフ
ィラメントタイプであるため、比較例３に比較して外観
性および肌触りが飛躍的に向上することが判る。From the above evaluation, it can be seen that, in each of the examples, since the straight yarn and the crimped yarn are mixed and planted, the appearance and the touch are superior to those of the comparative examples 1 and 2. Further, in each of the examples, since the straight yarn is of the monofilament type, it can be seen that the appearance and the touch are dramatically improved as compared with Comparative Example 3.

【００５５】また、各実施例のうち、実施例４ないし実
施例１６は、捲縮糸１４が充填材１６から露出する高さ
を有しているため、実施例１ないし実施例３に比較して
良好な外観性を得られることが判る。そして、実施例１
ないし実施例１９は、捲縮糸１４がストレート糸１５よ
りも低いため、比較例２０に比較して良好な外観性およ
び肌触りを得られることが判る。In addition, among the respective examples, Examples 4 to 16 have a height at which the crimped yarn 14 is exposed from the filler material 16, and therefore are compared with Examples 1 to 3. It can be seen that excellent appearance can be obtained. And Example 1
It is understood that the crimped yarns 14 in Example 19 are lower than the straight yarns 15 and therefore better appearance and feel can be obtained as compared with Comparative Example 20.

【００５６】また、実施例１２ないし実施例１４および
実施例１６は、捲縮糸１４が０．５山／２．５４ｃｍな
いし５山／２．５４ｃｍという適度な捲縮形状を有して
いるため、実施例１１および実施例１５に比較してΔＧ
ｍａｘの値を小さくできるとともに、外観性，肌触り，
耐久性の各評価が良好であることが判る。さらに、実施
例４ないし実施例１６のうち、実施例４および実施例７
ないし実施例１６は、ストレート糸１５の太さが２０デ
ニールないし１０００デニールであるため、実施例５お
よび実施例６に比較して、外観性，肌触りおよび耐久性
が高次元でバランスすることが判る。In addition, in Examples 12 to 14 and Example 16, the crimped yarn 14 has an appropriate crimped shape of 0.5 crests / 2.54 cm to 5 crests / 2.54 cm. , G compared to Examples 11 and 15
The value of max can be reduced and the appearance, touch,
It can be seen that each evaluation of durability is good. Furthermore, among Examples 4 to 16, Example 4 and Example 7
In Example 16 to Example 16, since the thickness of the straight yarn 15 is 20 denier to 1000 denier, it can be seen that the appearance, touch and durability are highly balanced in comparison with Examples 5 and 6. .

【００５７】そして、実施例１７ないし実施例１９は、
弾性充填材が用いられているため、実施例９に比較して
Ｇｍａｘの絶対値およびΔＧｍａｘの値が良好となるこ
とが判る。これらのことから、充填材入り人工芝生の充
填材として、弾性充填材を採用すれば、芝面の硬度およ
び硬度変化の特性を大幅に良好にできることになる。さ
らに、実施例１９と比較例５とを比較すると、充填材と
して弾性充填材を用いた上に、スプリット加工を施した
捲縮糸とストレート糸とを混在させる必要があることが
判る。また、実施例９および実施例１０は、ストレート
糸１５がそれぞれポリアミドおよびポリエステルにより
形成されているため、実施例３ないし実施例８および実
施例１４に比較して、へたり等が少なく、耐久性が向上
することが判る。Then, Examples 17 to 19 are
It can be seen that since the elastic filler is used, the absolute value of Gmax and the value of ΔGmax are better than those of Example 9. From these facts, if the elastic filler is used as the filler of the artificial grass containing the filler, the hardness of the grass surface and the characteristics of hardness change can be significantly improved. Furthermore, comparing Example 19 with Comparative Example 5, it is found that it is necessary to use the elastic filler as the filler and to mix the crimped yarn and the straight yarn subjected to the split processing. In addition, in Examples 9 and 10, since the straight yarn 15 is formed of polyamide and polyester, respectively, compared to Examples 3 to 8 and 14, the settling is less and the durability is improved. It can be seen that

【００５８】なお、本発明は前述した実施例に限定され
るものではなく、例えば、前記実施例で示した捲縮糸，
ストレート糸，充填材の材質，形状，寸法，形態，数，
配置個所等は本発明を達成できるものであれば任意であ
り、本発明を達成できる範囲での改良，変形等は本発明
に含まれるものである。The present invention is not limited to the above-mentioned embodiments. For example, the crimped yarn shown in the above-mentioned embodiments,
Material, shape, size, form, number of straight yarn and filler,
Arrangement locations and the like are arbitrary as long as the present invention can be achieved, and improvements, modifications and the like within the range in which the present invention can be achieved are included in the present invention.

【００５９】[0059]

【発明の効果】本発明の請求項１に記載した発明によれ
ば、良好な接地感を長期間維持できるとともに、肌触り
や外観性を向上できる。また、請求項２に記載した発明
によれば、芝面を一層天然芝生に近似した凹凸状でき
る。そして、請求項３に記載した発明によれば、適度な
捲縮形状を有する捲縮糸により一層天然芝生に近似した
外観性が得られるとともに、充填材の過度な充填を効果
的に防止できる。According to the invention described in claim 1 of the present invention, it is possible to maintain a good feeling of contact with the ground for a long period of time and to improve the touch and the appearance. Further, according to the invention described in claim 2, the lawn surface can be made to have an uneven shape more similar to a natural lawn. According to the invention described in claim 3, the crimped yarn having an appropriate crimped shape can provide an appearance more similar to that of a natural lawn and can effectively prevent excessive filling of the filler.

【００６０】さらに、請求項４に記載した発明によれ
ば、適度な細さのストレート糸により、一層良好な肌触
りが得られる。また、請求項５に記載した発明よれば、
充填材が弾性を有しているため、よりいっそう弾力性に
富んだ良好な接地感が得られる。そして、請求項６に記
載した発明よれば、ストレート糸が他の材質により形成
された場合に比較して良好な直立性を示すため、良好な
外観性および排水性を長期間維持できる。Further, according to the invention described in claim 4, the straight yarn having an appropriate thinness can provide a better touch. According to the invention described in claim 5,
Since the filling material has elasticity, it is possible to obtain a good feeling of contact with ground that is even more elastic. Further, according to the invention described in claim 6, since the straight yarn exhibits better uprightness as compared with the case where the straight yarn is made of another material, it is possible to maintain good appearance and drainage for a long period of time.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明の一実施例を示す模式断面図である。FIG. 1 is a schematic sectional view showing an embodiment of the present invention.

【図２】捲縮糸を示す正面図および側面図である。FIG. 2 is a front view and a side view showing a crimped yarn.

【図３】本発明の他の実施例を示す模式断面図である。FIG. 3 is a schematic sectional view showing another embodiment of the present invention.

【図４】本発明の他の実施例を示す模式断面図である。FIG. 4 is a schematic cross-sectional view showing another embodiment of the present invention.

【符号の説明】[Explanation of symbols]

１０，３０，４０ 充填材入り人工芝生である砂入り人
工芝生 １４ 捲縮糸 １５ ストレート糸 １６ 充填材である目砂 ３２ 充填材である弾性充填材10, 30, 40 Artificial lawn containing sand which is an artificial lawn containing filler 14 Crimped yarn 15 Straight yarn 16 Grain sand which is a filler 32 Elastic filler which is a filler

───────────────────────────────────────────────────── フロントページの続き (72)発明者 田中 雅和 兵庫県明石市魚住町清水41番地の１ 住友 ゴム魚住寮内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Masakazu Tanaka 1 1 41, Shimizu, Uozumi Town, Akashi City, Hyogo Prefecture

Claims (6)

【特許請求の範囲】[Claims] 【請求項１】 スプリット加工が施された捲縮糸と、ス
トレート糸とが基布に多数植設され、前記捲縮糸および
前記ストレート糸間に充填材が充填された充填材入り人
工芝生において、前記ストレート糸がモノフィラメント
タイプであることを特徴とする充填材入り人工芝生。1. A filler-containing artificial grass in which a large number of split crimped yarns and straight yarns are planted in a base fabric, and a filler is filled between the crimped yarns and the straight yarns. An artificial lawn containing a filler, wherein the straight yarn is a monofilament type. 【請求項２】 前記捲縮糸が前記ストレート糸よりも低
く、かつ、先端が前記充填材から露出する高さを有して
いることを特徴とする請求項１に記載した充填材入り人
工芝生。2. The artificial turf with a filler according to claim 1, wherein the crimped yarn is lower than the straight yarn, and the tip of the crimped yarn has a height exposed from the filler. . 【請求項３】 前記捲縮糸の山数が０．５山／２．５４
ｃｍないし５山／２．５４ｃｍであることを特徴とする
請求項１に記載した充填材入り人工芝生。3. The number of peaks of the crimped yarn is 0.5 peaks / 2.54
Artificial lawn with a filler according to claim 1, characterized in that the height is cm to 5 peaks / 2.54 cm. 【請求項４】 前記ストレート糸の太さが２０デニール
ないし１０００デニールであることを特徴とする請求項
１に記載した充填材入り人工芝生。4. The artificial grass with a filler according to claim 1, wherein the straight yarn has a thickness of 20 denier to 1000 denier. 【請求項５】 前記充填材が弾性を有していることを特
徴とする請求項１に記載した充填材入り人工芝生。5. The artificial turf with a filler according to claim 1, wherein the filler has elasticity. 【請求項６】 前記ストレート糸がポリアミドおよびポ
リエステルのうちの少なくとも一方により形成された糸
を主体としていることを特徴とする請求項１に記載した
充填材入り人工芝生。6. The artificial lawn with a filler according to claim 1, wherein the straight yarn is mainly composed of a yarn formed of at least one of polyamide and polyester.