JP2963976B2 - Method and structure for attaching surface finishing material to cement-based molded plate - Google Patents
Method and structure for attaching surface finishing material to cement-based molded plateInfo
- Publication number
- JP2963976B2 JP2963976B2 JP7233993A JP23399395A JP2963976B2 JP 2963976 B2 JP2963976 B2 JP 2963976B2 JP 7233993 A JP7233993 A JP 7233993A JP 23399395 A JP23399395 A JP 23399395A JP 2963976 B2 JP2963976 B2 JP 2963976B2
- Authority
- JP
- Japan
- Prior art keywords
- plate
- finishing material
- surface finishing
- cement
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、プレキャストコン
クリート（ＰＣ）板や気泡コンクリート（ＡＬＣ）板等
のセメント系成形板に石材やセラミックやガラスなどに
よるパネル状の表面仕上材を取り付ける方法及びその取
付構造に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of attaching a panel-like surface finishing material made of stone, ceramic, glass or the like to a cement-based molded plate such as a precast concrete (PC) plate or an aerated concrete (ALC) plate. It is about structure.
【０００２】[0002]
【従来の技術】石材、セラミック、ガラス等を材質とす
るパネル状部材を建物の外装として使用する場合、その
取り付け方法の一例として従来は、現場において外壁を
構成する部材の表面に順次個別に張設していたが、近
年、この従来の現場施工方法にかわって、工期の短縮や
施工の容易性を求めて外壁を構成するセメント系成形板
の表面に石材などのパネル状部材を工場で予め張設する
方法が採用されている。2. Description of the Related Art When a panel-shaped member made of stone, ceramic, glass, or the like is used as an exterior of a building, as an example of a method of attaching the panel-shaped member, conventionally, an individual member is sequentially and sequentially stretched on the surface of a member constituting an outer wall at a site. In recent years, in place of this conventional on-site construction method, panel-like members such as stones have been pre-installed at the factory on the surface of a cement-based molded plate that constitutes the outer wall in order to shorten the construction period and ease of construction. The method of stretching is adopted.
【０００３】図５はかかる方法の一例を示し、石打込プ
レキャストコンクリート（ＰＣ）板20の場合で、裏面に
シアコネクタ21を突出させて取り付け裏面処理剤22を塗
布した石材23を型枠にそって予め配列・固定した後、配
筋し、型枠にコンクリート19を打設し、養生硬化させる
もので、硬化時にシアコネクタ21の突出部分が打設した
コンクリート内に埋設されこれにより石材23がコンクリ
ート板に結合されるものである。FIG. 5 shows an example of such a method. In the case of a stone-cast precast concrete (PC) plate 20, a stone material 23 having a shear connector 21 protruded from the back surface and attached to the back surface treatment agent 22 is drawn along a formwork. After arranging and fixing in advance, reinforcing bars are laid, concrete 19 is poured into the formwork, and cured and cured, and the protruding portion of the shear connector 21 is buried in the poured concrete at the time of curing, whereby the stone material 23 is It is connected to a concrete board.
【０００４】図６は一型枠で一枚が製造される大型気泡
コンクリート（ＡＬＣ）板にタイルを後張り工法で取り
付けた例で、工場で大型ＡＬＣ板24に下地処理を施し、
タイルの取付面に接着モルタル25を塗布し、振動工具を
使用してタイル26を密着張りし、目地詰め27したもので
ある。FIG. 6 shows an example in which tiles are attached to a large-sized cellular concrete (ALC) plate, one of which is manufactured in one mold frame, by a backing method.
The adhesive mortar 25 is applied to the mounting surface of the tile, the tile 26 is closely adhered using a vibration tool, and the joint 27 is filled.
【０００５】図７は一型枠で複数枚を製造するＡＬＣ板
に大型陶板を後張りする例で、ＡＬＣ板の製造時に、該
ＡＬＣ板28の内部にステンレス製の板29を予め埋設し、
他方、大型陶板30の裏面に取付金物31を予め取り付けて
おき、この取付金物31を介してタッピングビス32で大型
陶板30をＡＬＣ板28の表面に結合するもので、補助的な
取付手段として構造的接着強度を有する構造接着剤33を
大型陶板30とＡＬＣ板28との間の隙間に充填する。[0005] Fig. 7 shows an example in which a large porcelain plate is backed on an ALC plate for manufacturing a plurality of sheets in a single mold. In manufacturing the ALC plate, a stainless steel plate 29 is buried in advance inside the ALC plate 28,
On the other hand, a mounting hardware 31 is attached to the back of the large ceramic plate 30 in advance, and the large ceramic plate 30 is connected to the surface of the ALC plate 28 with a tapping screw 32 via the mounting hardware 31. A gap between the large porcelain plate 30 and the ALC plate 28 is filled with a structural adhesive 33 having a proper adhesive strength.
【０００６】[0006]
【発明が解決しようとする課題】図５に示した石打込Ｐ
Ｃ板は、意匠上の差異を設けるために厚みの異なる表面
仕上材を用いて表面に凹凸を設ける場合、型枠として内
面に凹凸が形成してある特別のものを用意する必要があ
り、また、表面仕上材を型枠内に配設した状態で粗骨材
を含むコンクリートを型枠に打設するものであるため、
表面仕上材にガラス板などを使用すると、これが割れる
おそれがある。The stone driving P shown in FIG.
When providing irregularities on the surface using surface finishing materials having different thicknesses in order to provide a difference in design, it is necessary to prepare a special form having irregularities on the inner surface as a mold, In order to cast concrete containing coarse aggregate into the form while the surface finishing material is arranged in the form,
When a glass plate or the like is used as a surface finishing material, it may be broken.
【０００７】図６に示したタイル張り大型ＡＬＣ板の場
合は、ＡＬＣ板の製造工程に高温高圧蒸気養生が含まれ
ているため、図６に示したような方法ではタイルを打ち
込むことができず、前記のような接着モルタルを用いた
後張り工法を採用しているが、ＡＬＣ板は表面強度が小
さいために、小型のタイルしか取り付けられず、使用で
きる表面仕上材が限定されてしまう。In the case of the large-sized ALC board with a tile shown in FIG. 6, since the high-temperature and high-pressure steam curing is included in the manufacturing process of the ALC board, the tile cannot be driven by the method as shown in FIG. Although the backing method using the adhesive mortar as described above is employed, the ALC plate has a small surface strength, so that only small tiles can be attached, and usable surface finishing materials are limited.
【０００８】図７に示した大型陶板張りＡＬＣ板の場合
は、内部にステンレス板を埋設するものであるため、長
尺のタッピングビスを使用すれば機械的に固定できる
が、構造接着剤は表面強度の小さいＡＬＣ板に直接接着
されるものであるため、表面仕上材が剥離する危険性が
あり、取り付けの信頼性が十分とはいえなかった。[0008] In the case of a large ceramic-plated ALC plate shown in Fig. 7, a stainless steel plate is buried inside. Therefore, if a long tapping screw is used, it can be mechanically fixed. Since it is directly bonded to the low strength ALC plate, there is a danger that the surface finishing material will peel off, and the reliability of the installation is not sufficient.
【０００９】本発明の目的は前記従来例の不都合を解消
し、ＰＣ板やＡＬＣ板等のセメント系成形板に、これを
製造した後に表面仕上材を取り付ける後張り工法におい
て、取付の信頼性と施工性が向上し、使用可能な表面仕
上材の選択幅も拡大するセメント系成形板への表面仕上
材取付方法及び取付構造を提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to solve the above-mentioned disadvantages of the prior art, and to improve the reliability and reliability of the installation in a post-stretching method in which a surface finishing material is attached to a cement-based molded plate such as a PC plate or an ALC plate after the production. It is an object of the present invention to provide a method and an attachment structure for a surface finishing material to a cement-based formed plate in which workability is improved and a selection range of usable surface finishing materials is expanded.
【００１０】[0010]
【課題を解決するための手段】本発明は前記目的を達成
するため、プレキャストコンクリート（ＰＣ）板や気泡
コンクリート（ＡＬＣ）板等のセメント系成形板に石材
やセラミックやガラスなどによるパネル状の表面仕上材
を取り付ける場合、セメント系成形板の成形時に、鉄や
ステンレスなどによる金属製で、底部が上面開口部より
幅広の細長中空部材で構成する取付金物を、上面開口部
が成形板の表面に位置するように打ち込み、成形後、前
記取付金物内にグラウト材や接着剤を充填し、表面仕上
材の裏面に取り付けたボルトなどの金物を取付金物内に
挿入し、グラウト材や接着剤を硬化させることで表面仕
上材を成形板の表面に固定すること、および、鉄やステ
ンレスなどによる金属製で、底部が上面開口部より幅広
の細長中空部材で構成する取付金物を、上面開口部が成
形板の表面に位置するように取り付け、表面仕上材の裏
面に取り付けたボルトなどの金物を、前記取付金物内に
充填したグラウト材や接着剤内に挿入し、表面仕上材を
成形板の表面に固定することを要旨とするものである。In order to achieve the above object, the present invention provides a panel-like surface made of stone, ceramic, glass or the like on a cement-based molded plate such as a precast concrete (PC) plate or an aerated concrete (ALC) plate. When attaching a finishing material, a metal fitting made of metal such as iron or stainless steel, with a bottom made of an elongated hollow member wider than the top opening, is attached to the surface of the molding plate when forming the cement-based molding plate. After filling, grouting material and adhesive are filled in the mounting hardware, metal fittings such as bolts attached to the back of the surface finishing material are inserted into the mounting hardware, and the grout material and adhesive are cured. By fixing the surface finishing material to the surface of the molded plate by making it, and by using an elongated hollow member made of metal such as iron or stainless steel, the bottom of which is wider than the top opening The mounting hardware to be formed is mounted so that the upper surface opening is positioned on the surface of the molded plate, and the hardware such as a bolt mounted on the back surface of the surface finishing material is inserted into a grout material or an adhesive filled in the mounting hardware. The gist is to fix the surface finishing material to the surface of the formed plate.
【００１１】請求項１、請求項２記載の本発明によれ
ば、セメント系成形板の成形時に打ち込んだ取付金物内
に充填したグラウト材や接着剤内に、表面仕上材の裏面
に取り付けたボルトなどの金物を挿入し、グラウト材や
接着剤を硬化させることで、ボルトと取付金物とが一体
化し、アンカー効果を発揮して表面仕上材が成形板の表
面に強固に取り付けられる。これにより、表面強度の小
さなＡＬＣ板のようなセメント系成形板に対しても重量
や寸法の大きい表面仕上材の取り付けが可能となる。According to the first and second aspects of the present invention, a bolt attached to the back surface of the surface finishing material is provided in a grout material or an adhesive filled in a metal fitting which is driven in forming a cement-based formed plate. By inserting a metal material such as the above and hardening the grout material or the adhesive, the bolt and the mounting metal material are integrated, and an anchor effect is exhibited so that the surface finishing material is firmly attached to the surface of the molded plate. This makes it possible to attach a surface finishing material having a large weight and size to a cement-based formed plate such as an ALC plate having a small surface strength.
【００１２】さらに接着剤は取付金物の上面開口部に露
出し、表面仕上材の裏面と帯状に面接触で接着するか
ら、表面仕上材が剥離しにくく、万一これが破損しても
飛散脱落することを防止でき信頼性が向上する。Further, since the adhesive is exposed at the opening on the upper surface of the mounting hardware and adheres to the back surface of the surface finishing material in a belt-like surface contact, the surface finishing material is hardly peeled off and scatters and drops even if it is broken. Can be prevented and reliability is improved.
【００１３】そして、表面仕上材は成形板の成形後に取
り付けるから、ＰＣ板のように粗骨材を含むコンクリー
トを打設して成形板を成形するものに対しても、ガラス
のような割れやすい表面仕上材の使用が可能となるとと
もに、隣接する表面仕上材に厚みの異なるものを使用で
きるから、表面に凹凸を設けることも可能となる。Since the surface finishing material is attached after the forming plate is formed, the surface finishing material is easily broken, such as glass, even when the forming plate is formed by casting concrete containing coarse aggregate, such as a PC plate. Since the surface finishing material can be used and the adjacent surface finishing materials having different thicknesses can be used, it is also possible to provide unevenness on the surface.
【００１４】[0014]
【発明の実施の形態】以下、図面について本発明の実施
形態を詳細に説明する。図１は本発明のセメント系成形
板への表面仕上材取付構造の実施形態を示す要部の縦断
側面図、図２は同上縦断正面図で、セメント系成形板と
してプレキャストコンクリート（ＰＣ）板１を用い、表
面仕上材として石板２を使用する場合を示し、石板２は
ＰＣ板１に後張り工法によって取り付けられる。Embodiments of the present invention will be described below in detail with reference to the drawings. FIG. 1 is a longitudinal sectional side view of an essential part showing an embodiment of a structure for attaching a surface finishing material to a cement-based molded plate of the present invention, and FIG. 2 is a longitudinal sectional front view of the same, showing a precast concrete (PC) plate 1 as a cement-based molded plate. Is used, and the case where the stone board 2 is used as a surface finishing material is shown. The stone board 2 is attached to the PC board 1 by a backing method.
【００１５】ＰＣ板１は、型枠内にコンクリートを打設
して成形するものであるが、図１〜図３に示すように打
設時に、鉄やステンレスなどによる金属製で、底部３ａ
が上面開口部３ｂより幅広の、図示の例では断面台形状
の細長中空部材で構成する取付金物３を、上面開口部３
ｂが成形板１ａの表面と同一面上に位置するように打ち
込み、成形後、前記取付金物３内にグラウト材や接着剤
等の充填材４を充填する。The PC board 1 is formed by casting concrete in a mold, and is formed of metal such as iron or stainless steel at the time of casting as shown in FIGS.
In the example shown in the figure, the mounting hardware 3 which is wider than the upper surface opening 3b and which is formed of an elongated hollow member having a trapezoidal cross section,
b is driven so as to be positioned on the same plane as the surface of the forming plate 1a, and after forming, the mounting metal 3 is filled with a filler 4 such as a grout material or an adhesive.
【００１６】一方、表面仕上材としての石板２の裏面に
ボルト５などの金物を予め取り付けておき、このボルト
５を取付金物３内に挿入し、石材２の裏面を成形板１ａ
の表面に密着させた状態にしてグラウト材や接着剤等の
充填材４を硬化させる。On the other hand, a metal member such as a bolt 5 is previously attached to the back surface of the stone plate 2 as a surface finishing material, and the bolt 5 is inserted into the mounting member 3 so that the back surface of the stone member 2 is formed into a forming plate 1a.
The filler 4 such as a grout material or an adhesive is cured while being in close contact with the surface of the substrate.
【００１７】これによりボルト５が充填材４を介して取
付金物３と一体化しアンカー効果を発揮して表面仕上材
である石板２が成形板１ａに固定される。この場合、取
付金物３の底部３ａの断面積は上面開口部３ｂよりも幅
広に形成してあるから、ボルト５と充填材４との結合強
度は大きい。As a result, the bolts 5 are integrated with the metal fittings 3 via the filler 4 to exert an anchor effect, and the stone plate 2 as a surface finishing material is fixed to the formed plate 1a. In this case, since the cross-sectional area of the bottom 3a of the mounting hardware 3 is formed wider than the upper opening 3b, the bonding strength between the bolt 5 and the filler 4 is large.
【００１８】また、取付金物３の上面開口部３ｂには成
形板１ａと同一面に充填材４が露出し、これが石材２の
裏面と帯状に直接面接触するから、石板２が剥離しにく
く、万一これが破損しても飛散脱落することを防止でき
る。さらに、図示は省略するが、補助的取付手段として
石材２と成形板１ａの界面に構造的な強度を有する構造
用シールを併用すれば、より大きな取付強度が得られ
る。The filler 4 is exposed on the upper surface opening 3b of the mounting member 3 on the same surface as the molding plate 1a, and the filler 4 is in direct surface contact with the back surface of the stone material 2 in a strip shape. Even if it breaks, it can be prevented from falling off. Further, although not shown, if a structural seal having structural strength is used in combination with the interface between the stone 2 and the molded plate 1a as an auxiliary mounting means, a higher mounting strength can be obtained.
【００１９】なお、成形板１ａの基材や表面仕上材の素
材、形状などは前記した実施形態に限定されるものでは
なく、種々の形態が考えられ、成形時に粗骨材を含む成
形材料を型枠内に打設するＰＣ板に対しても、表面仕上
材は後張りとしたから表面仕上材としてガラス板のよう
な割れやすい材質のものも使用可能となる。The material and shape of the base material and surface finishing material of the molded plate 1a are not limited to the above-described embodiment, and various forms are conceivable. Since the surface finishing material is also a backing for the PC board to be cast in the formwork, a material that is easily broken such as a glass plate can be used as the surface finishing material.
【００２０】また、図１に示すように隣接する石板２に
厚みの異なるものを使用すれば、表面に凹凸を簡単に設
けられる。Further, as shown in FIG. 1, if adjacent stone plates 2 having different thicknesses are used, unevenness can be easily provided on the surface.
【００２１】[0021]
【発明の効果】以上述べたように本発明のセメント系成
形板への表面仕上材取付方法及び取付構造は、表面仕上
材は、セメント系成形板に成形時に打ち込んだ取付金物
に固定されるから、表面強度の小さなＡＬＣ板のような
セメント系成形板に対しても重量や寸法の大きい表面仕
上材の取り付けが可能となる。As described above, according to the method and structure for mounting a surface finishing material on a cement-based molded plate of the present invention, the surface finishing material is fixed to the mounting hardware that is driven into the cement-based molded plate during molding. Also, it is possible to attach a surface finishing material having a large weight and size to a cement-based formed plate such as an ALC plate having a small surface strength.
【００２２】さらに接着剤は取付金物の上面開口部に露
出し、表面仕上材の裏面と帯状に面接触で接着するか
ら、表面仕上材が剥離しにくく、万一これが破損しても
飛散脱落することを防止でき信頼性が向上する。また、
成形板製造後に表面仕上材を取り付ける後張り工法であ
るので、表面仕上材を成形板の界面に構造用シールの併
用が可能となり、より大きな取付強度を得ることができ
る。Further, the adhesive is exposed at the opening on the upper surface of the mounting hardware and adheres to the back surface of the surface finishing material in a belt-like surface contact, so that the surface finishing material is hardly peeled off and scatters and drops even if it is broken. Can be prevented and reliability is improved. Also,
Since this is a post-stretching method of attaching a surface finishing material after manufacturing a molded plate, the surface finishing material can be used together with a structural seal at the interface of the molded plate, and greater mounting strength can be obtained.
【００２３】そして、表面仕上材は成形板の成形後に取
り付けるから、ＰＣ板のように粗骨材を含むコンクリー
トを打設して成形板を成形するものに対しても、ガラス
のような割れやすい表面仕上材の使用が可能となるとと
もに、隣接する表面仕上材に厚みの異なるものを使用で
きるから、表面に凹凸を設けることも可能となるもので
ある。Since the surface finishing material is attached after the forming plate is formed, the surface finishing material is easily broken like glass even when the forming plate is formed by casting concrete containing coarse aggregate such as a PC plate. Since the surface finishing material can be used, and the adjacent surface finishing materials having different thicknesses can be used, it is also possible to provide irregularities on the surface.
【図１】本発明のセメント系成形板への表面仕上材取付
構造の実施形態を示す要部の縦断側面図である。FIG. 1 is a longitudinal sectional side view of a main part showing an embodiment of a structure for attaching a surface finishing material to a cement-based formed plate of the present invention.
【図２】本発明のセメント系成形板への表面仕上材取付
構造の実施形態を示す要部の縦断正面図である。FIG. 2 is a longitudinal sectional front view of a main part showing an embodiment of a structure for attaching a surface finishing material to a cement-based formed plate of the present invention.
【図３】本発明のセメント系成形板への表面仕上材取付
構造の実施形態を示す成形板の平面図である。FIG. 3 is a plan view of a molded plate showing an embodiment of a structure for attaching a surface finishing material to a cement-based molded plate of the present invention.
【図４】本発明のセメント系成形板への表面仕上材取付
構造の実施形態を示す成形板の縦断側面図である。FIG. 4 is a longitudinal sectional side view of a molded plate showing an embodiment of a structure for attaching a surface finishing material to a cement-based molded plate of the present invention.
【図５】従来のセメント系成形板への表面仕上材取付構
造の第１例を示す縦断側面図である。FIG. 5 is a vertical sectional side view showing a first example of a conventional structure for attaching a surface finishing material to a cement-based formed plate.
【図６】従来のセメント系成形板への表面仕上材取付構
造の第２例を示す縦断側面図である。FIG. 6 is a vertical sectional side view showing a second example of a conventional structure for attaching a surface finishing material to a cement-based formed plate.
【図７】従来のセメント系成形板への表面仕上材取付構
造の第３例を示す縦断正面図である。FIG. 7 is a longitudinal sectional front view showing a third example of a conventional structure for attaching a surface finishing material to a cement-based formed plate.
１…ＰＣ板 １ａ…成形板 ２…石板 ３…取付金物 ３ａ…底部 ３ｂ…開口部 ４…充填材 ５…ボルト 19…コンクリート 20…石打込プレキャストコンクリート（ＰＣ）板 21…シアコネクタ 22…裏面処理剤 23…石材 24…大型ＡＬＣ板 25…モルタル 26…タイル 27…目地詰め 28…ＡＬＣ板 29…ステンレス製の
板 30…大型陶板 31…取付金物 32…タッピングビス 33…構造接着剤DESCRIPTION OF SYMBOLS 1 ... PC board 1a ... Forming board 2 ... Stone board 3 ... Mounting hardware 3a ... Bottom 3b ... Opening 4 ... Filler 5 ... Bolt 19 ... Concrete 20 ... Stone cast precast concrete (PC) board 21 ... Shear connector 22 ... Backside treatment 23 ... Stone material 24 ... Large ALC plate 25 ... Mortar 26 ... Tile 27 ... Seal filling 28 ... ALC plate 29 ... Stainless steel plate 30 ... Large ceramic plate 31 ... Mounting hardware 32 ... Tapping screw 33 ... Structural adhesive
フロントページの続き (58)調査した分野(Int.Cl.6，ＤＢ名) B32B 7/08 B32B 31/04 E04C 2/04 E04C 2/46 E04B 2/94 E04F 13/08 102 E04F 13/08 101 E04F 13/14 Continuation of the front page (58) Field surveyed (Int.Cl. 6 , DB name) B32B 7/08 B32B 31/04 E04C 2/04 E04C 2/46 E04B 2/94 E04F 13/08 102 E04F 13/08 101 E04F 13/14
Claims (2)
気泡コンクリート（ＡＬＣ）板等のセメント系成形板に
石材やセラミックやガラスなどによるパネル状の表面仕
上材を取り付ける場合、セメント系成形板の成形時に、
鉄やステンレスなどによる金属製で、底部が上面開口部
より幅広の細長中空部材で構成する取付金物を、上面開
口部が成形板の表面に位置するように打ち込み、成形
後、前記取付金物内にグラウト材や接着剤を充填し、表
面仕上材の裏面に取り付けたボルトなどの金物を取付金
物内に挿入し、グラウト材や接着剤を硬化させることで
表面仕上材を成形板の表面に固定することを特徴とした
セメント系成形板への表面仕上材取付方法。When a panel-like surface finishing material such as stone, ceramic or glass is attached to a cement-based formed plate such as a precast concrete (PC) plate or an aerated concrete (ALC) plate,
It is made of metal such as iron or stainless steel, and a metal fitting whose bottom is formed of an elongated hollow member wider than the upper surface opening is driven in such a manner that the upper surface opening is located on the surface of the molding plate, and after molding, the mounting metal is inserted into the metal fitting. Fill the grout material or adhesive, insert the metal such as bolts attached to the back of the surface finishing material into the mounting hardware, and cure the grout material or adhesive to fix the surface finishing material to the surface of the molded plate A method of attaching a surface finishing material to a cement-based formed plate, characterized in that:
気泡コンクリート（ＡＬＣ）板等のセメント系成形板に
石材やセラミックやガラスなどによるパネル状の表面仕
上材を取り付ける場合、鉄やステンレスなどによる金属
製で、底部が上面開口部より幅広の細長中空部材で構成
する取付金物を、上面開口部が成形板の表面に位置する
ように取り付け、表面仕上材の裏面に取り付けたボルト
などの金物を、前記取付金物内に充填したグラウト材や
接着剤内に挿入し、表面仕上材を成形板の表面に固定す
ることを特徴としたセメント系成形板への表面仕上材取
付構造。2. When a panel-like surface finishing material such as stone, ceramic, or glass is attached to a cement-based molded plate such as a precast concrete (PC) plate or an aerated concrete (ALC) plate, it is made of metal such as iron or stainless steel. A metal fitting having a bottom portion formed of an elongated hollow member wider than the upper surface opening is attached so that the upper surface opening is located on the surface of the forming plate, and a metal member such as a bolt attached to the back surface of the surface finishing material is attached. A surface finishing material attaching structure to a cement-based molded plate, wherein the surface finishing material is fixed to a surface of a molded plate by inserting the material into a grout material or an adhesive filled in a metal object and fixing the surface finishing material to the surface of the molded plate.