JP2722300B2 - Method for producing functional nonwoven fabric - Google Patents
Method for producing functional nonwoven fabricInfo
- Publication number
- JP2722300B2 JP2722300B2 JP4268475A JP26847592A JP2722300B2 JP 2722300 B2 JP2722300 B2 JP 2722300B2 JP 4268475 A JP4268475 A JP 4268475A JP 26847592 A JP26847592 A JP 26847592A JP 2722300 B2 JP2722300 B2 JP 2722300B2
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- calcium phosphate
- weight
- producing
- functional nonwoven
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【利用分野】本発明は、リン酸カルシウム系化合物を担
持した機能性不織布の製造方法に関する。The present invention relates to a method for producing a functional nonwoven fabric carrying a calcium phosphate compound.
【０００２】[0002]
【従来技術及びその問題点】リン酸カルシウム系化合物
が様々な物質や動植物細胞に対して吸着作用を有するこ
とに着目し、最近、リン酸カルシウム系化合物粒子を含
む機能紙が提案された。しかしながら、この機能紙は、
通気性、柔軟性及び引き裂き強度に欠けるため、その用
途に制限があった。例えば、機能紙をフィルターとして
用いる場合には、通気性に乏しいため、ニードルパンチ
等の二次加工が必要であった。また、柔軟性及び引き裂
き強度の不足により衣料、包帯などの医療用品には不適
当であった。2. Description of the Related Art Focusing on the fact that calcium phosphate compounds have an adsorbing effect on various substances and animal and plant cells, a functional paper containing calcium phosphate compound particles has recently been proposed. However, this functional paper
Lack of breathability, flexibility and tear strength has limited its use. For example, in the case where a functional paper is used as a filter, secondary processing such as needle punching or the like was necessary because of poor air permeability. Moreover, it was unsuitable for medical supplies such as clothing and bandages due to lack of flexibility and tear strength.
【０００３】さらに、抄紙技術によって機能紙を製造す
る際に、リン酸カルシウム系化合物粒子はパルプスラリ
ー中で沈殿しやすく、機能紙に一様にリン酸カルシウム
系化合物を分布させることが困難であった。また、紙パ
ルプに担持させたリン酸カルシウム粒子が取り扱い中に
脱落しやすいという問題点もあった。Further, when producing a functional paper by the papermaking technique, the calcium phosphate compound particles easily precipitate in the pulp slurry, and it is difficult to uniformly distribute the calcium phosphate compound on the functional paper. There is also a problem that the calcium phosphate particles supported on the paper pulp easily fall off during handling.
【０００４】[0004]
【発明の目的】本発明は、前記従来技術の欠点を解消
し、通気性、柔軟性及び引き裂き強度に優れると共にリ
ン酸カルシウム系化合物粒子の分布及び付着性が著しく
改善された機能性不織布を製造する方法を提供すること
を目的とする。SUMMARY OF THE INVENTION The object of the present invention is to solve the above-mentioned disadvantages of the prior art, and to provide a method for producing a functional nonwoven fabric which is excellent in air permeability, flexibility and tear strength, and in which the distribution and adhesion of calcium phosphate compound particles are remarkably improved. The purpose is to provide.
【０００５】[0005]
【発明の概要】本発明は、リン酸カルシウム系化合物粒
子を分散剤によって水中に良好に分散させて不織布に担
持させると共に結合剤によって強固に付着させることに
よって上記目的を達成したものである。SUMMARY OF THE INVENTION The present invention has achieved the above object by dispersing calcium phosphate compound particles in water well with a dispersant, supporting the particles on a nonwoven fabric, and firmly adhering them with a binder.
【０００６】すなわち、本発明による機能性不織布の製
造方法は、二通りあり、Ｃa ／Ｐのモル比が１．０〜
２．０のリン酸カルシウム系化合物粒子、水溶性結合剤
及びポリカルボン酸系高分子分散剤を含む水性分散液で
不織布を含浸又はコーティングすることを特徴とする方
法及び原料繊維、Ｃa ／Ｐのモル比が１．０〜２．０
のリン酸カルシウム系化合物粒子、結合剤及びポリカル
ボン酸系高分子分散剤を含む水性分散液を用いて抄紙技
術により不織布を製造することを特徴とする方法であ
る。That is, there are two methods for producing a functional nonwoven fabric according to the present invention, and the molar ratio of Ca / P is 1.0 to 1.0.
A method comprising impregnating or coating a nonwoven fabric with an aqueous dispersion containing a calcium phosphate compound particle of 2.0, a water-soluble binder and a polycarboxylic acid polymer dispersant, and a raw fiber, Ca / P molar ratio. Is 1.0 to 2.0
Using an aqueous dispersion containing the calcium phosphate compound particles, a binder, and a polycarboxylic acid polymer dispersant according to a papermaking technique.
【０００７】本発明において、上記のの方法は乾式法
又は湿式法で予め製造した不織布を用いる方法であり、
の方法は湿式法で不織布を製造する際に原料繊維のス
ラリーにリン酸カルシウム系化合物粒子、結合剤及び高
分子分散剤を添加する方法である。In the present invention, the above method is a method using a nonwoven fabric previously produced by a dry method or a wet method,
Is a method of adding calcium phosphate compound particles, a binder, and a polymer dispersant to a slurry of raw fibers when a nonwoven fabric is produced by a wet method.
【０００８】いずれの方法においても、不織布に用いる
繊維は、天然繊維、人造繊維、合成繊維及びこれらの混
合物であってよく、特に制限はない。不織布に使用され
る代表的な繊維としては、木綿、羊毛、レーヨン、アセ
テート、ポリアミド、ポリエステル、アクリル繊維など
が挙げられる。また、使用する繊維の繊維長及び繊度並
びに不織布の厚さは、用途などに応じて適宜選択するこ
とができる。In any of the methods, the fibers used for the nonwoven fabric may be natural fibers, artificial fibers, synthetic fibers, and mixtures thereof, and are not particularly limited. Typical fibers used for the nonwoven fabric include cotton, wool, rayon, acetate, polyamide, polyester, acrylic fiber and the like. In addition, the fiber length and fineness of the fibers used and the thickness of the nonwoven fabric can be appropriately selected according to the use and the like.
【０００９】また、本発明に用いるリン酸カルシウム系
化合物としては、Ｃa ／Ｐ比が 1.0〜2.０のものであれ
ば各種のものであってよい。具体的には、ハイドロキシ
アパタイト、フッ素アパタイト等の各種のアパタイト、
リン酸三カルシウム、リン酸四カルシウムなどを使用す
ることができる。これらの化合物は、自体公知の方法で
製造することができ、単独で又は混合物として使用する
ことができる。As the calcium phosphate compound used in the present invention, various compounds may be used as long as the Ca / P ratio is 1.0 to 2.0. Specifically, various apatites such as hydroxyapatite and fluorapatite,
Tricalcium phosphate, tetracalcium phosphate and the like can be used. These compounds can be produced by a method known per se, and can be used alone or as a mixture.
【００１０】本発明においては、これらのリン酸カルシ
ウム系化合物は粉末、顆粒又は多孔質顆粒の形であって
よいが、粒径が 0.0１〜２００μｍで、比表面積が 0.1
ｍ2／ｇ以上の粒子であることが好ましく、1.０ｍ2 ／
ｇ以上がより好ましく、１０ｍ2 ／ｇ以上が最も好まし
い。粒径が 0.0１μｍ未満であると、粒子が凝集しやす
くなり、水中に均一に分散させ難くなる。また、粒径が
２００μｍを超えると、出来上がりの不織布の手触りが
悪い上、吸着能も低下する。また、比表面積が0.１ｍ2
／ｇ未満であると吸着効果が不充分となる。In the present invention, these calcium phosphate compounds may be in the form of powder, granules or porous granules, but have a particle size of 0.01 to 200 μm and a specific surface area of 0.1 to 0.1 μm.
m is preferably 2 / g or more particles, 1.0 m 2 /
g or more, more preferably 10 m 2 / g or more. If the particle size is less than 0.01 μm, the particles are likely to aggregate, making it difficult to uniformly disperse the particles in water. On the other hand, if the particle size exceeds 200 μm, the texture of the finished nonwoven fabric is poor, and the adsorptivity is reduced. The specific surface area is 0.1 m 2
/ G, the adsorption effect becomes insufficient.
【００１１】また、の方法で不織布を製造する場合に
は、粒径１〜３０μｍの二次粒子からなるリン酸カルシ
ウム粉末を用いるのがより好ましい。粒径が１μｍより
小さいと、抄紙の際に抄紙機の網から水と共に落下して
しまい、３０μｍを超えると、重すぎて、均一に分散す
ることが困難となる。When a nonwoven fabric is produced by the above method, it is more preferable to use a calcium phosphate powder composed of secondary particles having a particle size of 1 to 30 μm. If the particle size is smaller than 1 μm, it will fall from the net of the paper machine together with water during papermaking, and if it exceeds 30 μm, it will be too heavy and difficult to disperse uniformly.
【００１２】リン酸カルシウム系化合物の多孔質顆粒
は、公知の方法で湿式合成したリン酸カルシウム系化合
物の結晶粒子を原料として様々な方法で製造することが
できる。例えば、この原料粒子を懸濁したスラリーを直
接噴霧乾燥などにより二次粒子に造粒するかあるいはこ
のスラリーに粘度調整剤、加熱により消失する有機化合
物粒子又は繊維等の添加物を加えて噴霧乾燥などにより
二次粒子に造粒する。この二次粒子自体、多孔質粒子と
なっており、この二次粒子をそのまま原料として用いる
こともでき、さらに高気孔率のものが好ましい場合に
は、次の方法で多孔質顆粒を作製する。この二次粒子を
再びスラリー状に懸濁して湿式成形するか又は加圧によ
る乾式成形等によりブロック体に成形する。その際、焼
成の過程で消散して気孔を形成するための有機化合物を
添加してもよい。無添加でも、焼成温度など、他の条件
を調節することにより気孔径を制御することもできる。
得られたブロック体を５００℃〜１３００℃の温度範囲
で焼成する。焼成温度が５００℃未満では、有機化合物
の熱消失やブロック体の焼結が充分に行われない。ま
た、焼成を１３００℃を超える高温で行うと、焼結体が
緻密化しすぎたり、リン酸カルシウムが分解を起こすお
それがある。このように焼成したブロック体を粉砕後、
分級して必要な粒径の顆粒を得ることができる。この顆
粒の気孔径は、二次粒子造粒用の原料スラリー中の結晶
粒子の大きさ、スラリーの粘度、添加物などを適切に調
節することによって調整することができる。[0012] The porous granules of the calcium phosphate compound can be produced by various methods using crystal particles of the calcium phosphate compound wet-synthesized by a known method as a raw material. For example, the slurry in which the raw material particles are suspended is granulated into secondary particles by direct spray drying or the like, or the slurry is dried by adding an additive such as a viscosity modifier and organic compound particles or fibers which disappear by heating. Granulate into secondary particles by, for example, The secondary particles themselves are porous particles, and the secondary particles can be used as a raw material as they are. If a material having a high porosity is preferable, a porous granule is produced by the following method. The secondary particles are suspended again in a slurry state and wet-molded, or formed into a block by dry molding or the like under pressure. At this time, an organic compound for dissipating and forming pores during the firing may be added. Even without the addition, the pore size can be controlled by adjusting other conditions such as the firing temperature.
The obtained block body is fired in a temperature range of 500C to 1300C. If the firing temperature is lower than 500 ° C., heat disappearance of the organic compound and sintering of the block are not sufficiently performed. Further, if the firing is performed at a high temperature exceeding 1300 ° C., the sintered body may be too dense, or calcium phosphate may be decomposed. After crushing the fired block,
The granules having a required particle size can be obtained by classification. The pore size of the granules can be adjusted by appropriately adjusting the size of the crystal particles in the raw material slurry for the secondary particle granulation, the viscosity of the slurry, the additives, and the like.
【００１３】不織布のリン酸カルシウム系化合物粒子担
持率は、用途などによって変動し、広範囲で適宜選択す
ることができるが、通常、５〜６５重量％であるのが好
ましく、５〜４０重量％であるのがより好ましい。５重
量％未満では、リン酸カルシウム系化合物の効果が発現
せず、６５重量％を超えると、取り扱い時などに飛散す
る粒子が多くなる。なお、本明細書において、担持率と
は、完成品の機能性不織布を基準とする百分率である。The calcium phosphate-based compound particle loading rate of the nonwoven fabric varies depending on the application and can be appropriately selected in a wide range, but is usually preferably 5 to 65% by weight, and more preferably 5 to 40% by weight. Is more preferred. If it is less than 5% by weight, the effect of the calcium phosphate compound will not be exhibited, and if it exceeds 65% by weight, the particles scattered during handling will increase. In addition, in this specification, a loading rate is a percentage based on the functional nonwoven fabric of a finished product.
【００１４】本発明に用いる水溶性結合剤としては、Ｃ
ＭＣ、ポリビニルアルコール、ポリアクリル酸、ポリア
クリル酸ナトリウム、ポリエチレンオキシドなどが挙げ
られる。また、上記のの方法においては、結合剤は冷
水に不溶であっても、熱水に可溶に調製されたポリビニ
ルアルコール繊維、ポリエステルなどのフィブリル化し
たものなどを使用することもできる。The water-soluble binder used in the present invention includes C
MC, polyvinyl alcohol, polyacrylic acid, sodium polyacrylate, polyethylene oxide and the like. In the above-mentioned method, even if the binder is insoluble in cold water, fibrillated polyvinyl alcohol fibers or polyester prepared in a manner soluble in hot water can also be used.
【００１５】また、本発明に用いるポリカルボン酸系高
分子分散剤としては、ポリカルボン酸アンモニウム、ポ
リカルボン酸ナトリウムなどのカルボン酸塩が好まし
い。The polycarboxylic acid polymer dispersant used in the present invention is preferably a carboxylate such as ammonium polycarboxylate and sodium polycarboxylate.
【００１６】本発明方法のうち上記の方法、すなわ
ち、不織布をリン酸カルシウム系化合物粒子の分散液で
含浸するか又はコーティングする方法を実施する場合、
この分散液中のリン酸カルシウム系化合物粒子の濃度
は、不織布への所望の担持率に応じて適宜選定すること
ができるが、分散性や作業性を考慮して通常、５〜７０
重量％、好ましくは１０〜４０重量％とする。含浸及び
コーティングを１回あるいは２回以上行って所望のリン
酸カルシウム担持量とすることもできる。When carrying out the above-mentioned method of the present invention, that is, the method of impregnating or coating a nonwoven fabric with a dispersion of calcium phosphate compound particles,
The concentration of the calcium phosphate-based compound particles in the dispersion can be appropriately selected according to the desired loading rate on the nonwoven fabric, but is usually 5 to 70 in consideration of dispersibility and workability.
% By weight, preferably 10 to 40% by weight. Impregnation and coating may be performed once or twice or more to obtain a desired calcium phosphate loading.
【００１７】また、分散液には、結合剤をリン酸カルシ
ウム系化合物に対して２〜５０重量％、好ましくは４〜
２０重量％、分散剤をリン酸カルシウム系化合物に対し
て0.３〜１５重量％、好ましくは 0.5〜１０重量％の量
で配合する。結合剤の量が２重量％未満の場合、不織布
とリン酸カルシウム粉末との結合が弱く、リン酸カルシ
ウム粉末の落下があり、５０重量％を超えると、リン酸
カルシウム粉末の効果が著しく低下する。また、分散剤
の量が 0.3重量％未満である場合、リン酸カルシウム粉
末の凝集が起こり、製品のムラが生じる。１５重量％を
超えると、リン酸カルシウム粉末の担持が著しく悪化す
る。In the dispersion, a binder is used in an amount of 2 to 50% by weight, preferably 4 to 50% by weight based on the calcium phosphate compound.
The dispersant is added in an amount of 0.3 to 15% by weight, preferably 0.5 to 10% by weight, based on the calcium phosphate compound. When the amount of the binder is less than 2% by weight, the bond between the nonwoven fabric and the calcium phosphate powder is weak, and the calcium phosphate powder drops. When the amount exceeds 50% by weight, the effect of the calcium phosphate powder is significantly reduced. If the amount of the dispersing agent is less than 0.3% by weight, the calcium phosphate powder will agglomerate, resulting in uneven product. If it exceeds 15% by weight, the loading of the calcium phosphate powder will be remarkably deteriorated.
【００１８】本発明方法のうち上記の方法、すなわち
湿式法により不織布を製造する際にリン酸カルシウム系
化合物粉末を添加する方法を実施する場合には、まず、
原料繊維、リン酸カルシウム系化合物粒子、結合剤及び
分散剤を含む分散液を調製する。この分散液中のリン酸
カルシウム系化合物粒子と原料繊維との配合比は、不織
布への所望の担持量に応じて適宜選定することができる
が、通常、原料繊維に対して５〜２００重量％、好まし
くは１０〜１００重量％とする。When the above method of the present invention, that is, the method of adding a calcium phosphate compound powder when producing a nonwoven fabric by a wet method, is carried out, first,
A dispersion containing raw fibers, calcium phosphate-based compound particles, a binder and a dispersant is prepared. The mixing ratio of the calcium phosphate compound particles and the raw fibers in the dispersion can be appropriately selected according to the desired amount of the nonwoven fabric to be supported. Is 10 to 100% by weight.
【００１９】また、上記の方法に用いる分散液には、
結合剤をリン酸カルシウム系化合物に対して２〜５０重
量％、好ましくは４〜２０重量％の量で配合する。結合
剤の量が２重量％未満の場合、繊維を結合させると共に
繊維にリン酸カルシウム粉末を付着させることが充分に
できず、５０重量％を超えると、不織布との分散性が低
下する。Further, the dispersion used in the above method includes:
The binder is blended in an amount of 2 to 50% by weight, preferably 4 to 20% by weight based on the calcium phosphate compound. When the amount of the binder is less than 2% by weight, it is not possible to bond the fibers and to attach the calcium phosphate powder to the fibers sufficiently. If the amount exceeds 50% by weight, the dispersibility with the nonwoven fabric is reduced.
【００２０】さらに、の方法に用いる分散剤は、原料
繊維及びリン酸カルシウム系化合物粉末を分散させるた
め、0.３〜１５重量％、好ましくは 0.5〜１０重量％の
量で配合する。0.３重量％未満である場合、リン酸カル
シウム粉末の凝集が起こり、製品にムラを生じる。ま
た、１５重量％を超えると、リン酸カルシウム粉末の担
持が低下する。Further, the dispersant used in the above method is added in an amount of 0.3 to 15% by weight, preferably 0.5 to 10% by weight in order to disperse the raw material fiber and the calcium phosphate compound powder. If it is less than 0.3% by weight, the calcium phosphate powder agglomerates, causing unevenness in the product. If the content exceeds 15% by weight, the loading of the calcium phosphate powder decreases.
【００２１】本発明方法のいずれの方法においても、分
散液にさらに粘度調整剤、例えば、ポリエチレンオキシ
ド−１８（２５００ｃｐ）、メチルセルロース（Ｍ−１
００００）１６０ｃｐ、カルボキシメチルセルロース
（イナセルＫNo３）５６０ｃｐなどを添加することがで
きる。In any of the methods of the present invention, a viscosity modifier such as polyethylene oxide-18 (2500 cp), methylcellulose (M-1) is added to the dispersion.
0000) 160 cp, carboxymethylcellulose (Inacell KNo3) 560 cp, and the like.
【００２２】[0022]
【実施例】次に、実施例に基づいて本発明をさらに詳述
するが、本発明はこれによって制限されるものではな
い。なお、以下の例中「部」は、特に断らない限り、
「重量部」を意味するものとする。Next, the present invention will be described in more detail with reference to Examples, but the present invention is not limited thereto. In addition, in the following examples, "parts"
It means “parts by weight”.
【００２３】実施例１ 平均粒径 0.0５μｍ、比表面積８０ｍ2 ／ｇ、Ｃa ／Ｐ
比 1.6７の多孔質ハイドロキシアパタイト顆粒８部、ポ
リカルボン酸アンモニウム塩（分散剤、東亜合成株式会
社製、商品名Ａ−Ｇ１１４）0.０８部及びポリビニルア
ルコール（結合剤、日本合成化学株式会社製、商品名ゴ
ーセノールＧＬ−０５）0.８部を蒸留水９1.１２部に加
え、攪拌して分散液を作製した。Example 1 Average particle size 0.05 μm, specific surface area 80 m 2 / g, Ca / P
8 parts of porous hydroxyapatite granules having a ratio of 1.67, 0.08 parts of ammonium polycarboxylate (dispersing agent, manufactured by Toagosei Co., Ltd., trade name: A-G114) and polyvinyl alcohol (binder, manufactured by Nippon Synthetic Chemical Co., Ltd.) 0.8 parts of Gohsenol GL-05) was added to 91.12 parts of distilled water and stirred to prepare a dispersion.
【００２４】この分散液で厚さ 0.3ｍｍのポリエステル
不織布（重量２７ｇ／ｍ2 ）を含浸し、乾燥してハイド
ロキシアパタイトを不織布構成繊維上に固定させた。得
られた不織布のハイドロキシアパタイト担持率は１６重
量％であり、ほぼ一様な担持が認められた。A 0.3-mm-thick polyester non-woven fabric (weight 27 g / m 2 ) was impregnated with this dispersion and dried to fix hydroxyapatite on the non-woven fabric fibers. The hydroxyapatite loading of the obtained nonwoven fabric was 16% by weight, and almost uniform loading was observed.
【００２５】実施例２ 平均粒径１０μｍ、比表面積５ｍ2 ／ｇ、Ｃa ／Ｐ比
1.6７のハイドロキシアパタイト顆粒３０部、ポリカル
ボン酸ナトリウム0.１５部及びポリアクリル酸ナトリウ
ム結合剤 0.6部を蒸留水６9.２５部に加え、攪拌して分
散液を作製した。この分散液で厚さ 0.1ｍｍのレーヨン
製不織布（重量１５ｇ／ｍ2 ）を含浸し、８０℃で熱風
乾燥してハイドロキシアパタイトを不織布構成繊維上に
固定させた。得られた不織布のハイドロキシアパタイト
担持率は１４重量％であり、ほぼ一様な担持が認められ
た。Example 2 Average particle size 10 μm, specific surface area 5 m 2 / g, Ca / P ratio
30 parts of 1.67 hydroxyapatite granules, 0.15 part of sodium polycarboxylate and 0.6 part of sodium polyacrylate binder were added to 69.25 parts of distilled water, and stirred to prepare a dispersion. A 0.1 mm thick rayon nonwoven fabric (weight 15 g / m 2 ) was impregnated with the dispersion and dried with hot air at 80 ° C. to fix hydroxyapatite on the nonwoven fabric fibers. The hydroxyapatite loading ratio of the obtained nonwoven fabric was 14% by weight, and almost uniform loading was observed.
【００２６】実施例３ 平均粒径８０μｍ、比表面積１１ｍ2 ／ｇ、Ｃa ／Ｐ比
1.5のリン酸三カルシウム粒子６０部、ポリカルボン酸
アンモニウム９部及びポリビニルアルコール結合剤６部
を蒸留水２５部に加え、攪拌して分散液を作製した。こ
の分散液で厚さ0.２ｍｍのポリエステル製不織布（重量
１８ｇ／ｍ2 ）を含浸し、乾燥してリン酸三カルシウム
を不織布構成繊維上に固定させた。得られた不織布のリ
ン酸三カルシウムの担持率は２８重量％であり、ほぼ一
様な担持が認められた。Example 3 Average particle size 80 μm, specific surface area 11 m 2 / g, Ca / P ratio
60 parts of 1.5 calcium tricalcium phosphate particles, 9 parts of polyammonium ammonium carboxylate and 6 parts of polyvinyl alcohol binder were added to 25 parts of distilled water and stirred to prepare a dispersion. A 0.2-mm-thick polyester non-woven fabric (weight: 18 g / m 2 ) was impregnated with this dispersion, dried, and tricalcium phosphate was fixed on the non-woven fabric constituent fibers. The loading ratio of tricalcium phosphate in the obtained nonwoven fabric was 28% by weight, and almost uniform loading was observed.
【００２７】実施例４ 平均粒径 3.5μｍ、比表面積６４ｍ2 ／ｇ、Ｃa ／Ｐ比
2.0のリン酸四カルシウム粒子２０部、ポリカルボン酸
ナトリウム0.４部及びポリアクリル酸ナトリウム８部を
蒸留水７1.６部に加え、攪拌して分散液を作製した。こ
の分散液で厚さ0.１ｍｍのレーヨン製不織布（重量１５
ｇ／ｍ2 ）を含浸し、乾燥してリン酸四カルシウムを不
織布構成繊維上に固定させた。得られた不織布のリン酸
四カルシウムの担持率は２１重量％であり、ほぼ一様な
担持が認められた。Example 4 Average particle size 3.5 μm, specific surface area 64 m 2 / g, Ca / P ratio
20 parts of tetracalcium phosphate particles of 2.0, 0.4 parts of sodium polycarboxylate and 8 parts of sodium polyacrylate were added to 71.6 parts of distilled water and stirred to prepare a dispersion. A non-woven fabric of rayon having a thickness of 0.1 mm (weight 15
g / m 2 ) and dried to fix the tetracalcium phosphate on the nonwoven fabric fibers. The loading ratio of tetracalcium phosphate in the obtained nonwoven fabric was 21% by weight, and almost uniform loading was observed.
【００２８】実施例５ 平均粒径 0.0５μｍ、比表面積８０ｍ2 ／ｇ、Ｃa ／Ｐ
比 1.6７のハイドロキシアパタイト顆粒５部、分散剤と
してポリカルボン酸アンモニウム0.０５部、結合剤とし
てポリエチレンオキシド１部、ポリエステル不織布原料
繊維４０部及び蒸留水５4.９５部を混合攪拌した後、抄
紙製造装置により不織布を製造した。９０℃で熱風乾燥
後、得られた不織布のハイドロキシアパタイト担持率は
２３重量％であり、ほぼ一様な担持が認められた。Example 5 Average particle size 0.05 μm, specific surface area 80 m 2 / g, Ca / P
5 parts of hydroxyapatite granules having a ratio of 1.67, 0.05 part of ammonium polycarboxylate as a dispersing agent, 1 part of polyethylene oxide as a binder, 40 parts of a polyester nonwoven fabric fiber and 54.95 parts of distilled water were mixed and stirred. The nonwoven fabric was manufactured by the manufacturing apparatus. After drying with hot air at 90 ° C., the hydroxyapatite loading of the obtained nonwoven fabric was 23% by weight, and almost uniform loading was observed.
【００２９】実施例６ 平均粒径８０μｍ、比表面積１１ｍ2 ／ｇ、Ｃa ／Ｐ比
1.5のリン酸三カルシウム粒子２５部、ポリカルボン酸
アンモニウム2.５部、ポリエチレンオキシド0.５部、ポ
リエステル不織布原料繊維５５部及び蒸留水１７部を混
合攪拌した後、抄紙製造装置により不織布を製造した。
９０℃で熱風乾燥後、得られた不織布のリン酸三カルシ
ウムの担持率は１３重量％であり、ほぼ一様な担持が認
められた。Example 6 Average particle size 80 μm, specific surface area 11 m 2 / g, Ca / P ratio
After mixing and stirring 25 parts of tricalcium phosphate particles of 1.5, 2.5 parts of ammonium polycarboxylate, 0.5 part of polyethylene oxide, 55 parts of polyester nonwoven fabric fiber and 17 parts of distilled water, a nonwoven fabric is manufactured by a papermaking machine. did.
After drying with hot air at 90 ° C., the loading rate of tricalcium phosphate in the obtained nonwoven fabric was 13% by weight, and almost uniform loading was observed.
【００３０】比較例 平均粒径１０μｍ、比表面積５ｍ2 ／ｇ、Ｃa ／Ｐ比
1.6７のハイドロキシアパタイト顆粒２５部、ポリアク
リル酸ナトリウム結合剤２５部及び分散剤としてカチオ
ン界面活性剤である変性アミン塩１部を蒸留水４９部に
加え、攪拌して分散液を作製した。この分散液で厚さ
0.3ｍｍのポリエステル不織布（重量２７ｇ／ｍ2 ）を
含浸し、８０℃で熱風乾燥させた。得られた不織布のハ
イドロキシアパタイト担持率は５重量％であったが、不
織布上にハイドロキシアパタイトの担持ムラが生じた。Comparative Example Average particle size 10 μm, specific surface area 5 m 2 / g, Ca / P ratio
25 parts of 1.67 hydroxyapatite granules, 25 parts of a sodium polyacrylate binder, and 1 part of a modified amine salt as a cationic surfactant as a dispersant were added to 49 parts of distilled water, followed by stirring to prepare a dispersion. Thickness of this dispersion
A 0.3 mm polyester nonwoven fabric (weight: 27 g / m 2 ) was impregnated and dried at 80 ° C. with hot air. The hydroxyapatite loading rate of the obtained nonwoven fabric was 5% by weight, but unevenness of hydroxyapatite loading occurred on the nonwoven fabric.
【００３１】[0031]
【発明の効果】本発明方法によれば、リン酸カルシウム
系化合物粒子が一様に分布し、強固に付着している機能
性不織布を効率よく容易に製造することができる。本発
明により得られる機能性不織布は、不織布を基材とする
ため、通気性、柔軟性及び引き裂き強度に優れており、
また、リン酸カルシウム系化合物粒子を含むため、種々
の物質に対する吸着作用及び脱臭作用を有し、床擦れ防
止シート、脱臭シート、除菌フィルター、オペガウン、
その他のヘルスケア関連製品に好適である。According to the method of the present invention, a functional nonwoven fabric in which calcium phosphate compound particles are uniformly distributed and firmly adhered can be efficiently and easily produced. The functional nonwoven fabric obtained by the present invention has excellent breathability, flexibility and tear strength because the nonwoven fabric is a base material,
In addition, because it contains calcium phosphate compound particles, it has an adsorbing action and a deodorizing action for various substances, and a floor rubbing prevention sheet, a deodorizing sheet, a disinfecting filter, an opegan,
Suitable for other healthcare related products.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 平出 恒男 東京都板橋区前野町２丁目36番９号 旭 光学工業株式会社内 (56)参考文献 特開 平３−51396（ＪＰ，Ａ) 特開 平４−144564（ＪＰ，Ａ) 特開 昭61−136439（ＪＰ，Ａ) ──────────────────────────────────────────────────続 き Continuation of front page (72) Inventor Tsuneo Hiraide 2-36-9 Maenocho, Itabashi-ku, Tokyo Asahi Optical Industry Co., Ltd. (56) References JP-A-3-51396 (JP, A) JP-A-4-144564 (JP, A) JP-A-61-136439 (JP, A)
Claims (10)
ン酸カルシウム系化合物粒子、水溶性結合剤及びポリカ
ルボン酸系高分子分散剤を含む水性分散液で不織布を含
浸又はコーティングすることを特徴とする機能性不織布
の製造方法。A nonwoven fabric is impregnated or coated with an aqueous dispersion containing calcium phosphate compound particles having a Ca / P molar ratio of 1.0 to 2.0, a water-soluble binder and a polycarboxylic acid polymer dispersant. A method for producing a functional nonwoven fabric, comprising:
タイト、リン酸三カルシウム、リン酸四カルシウム又は
これらの混合物の粒径が０．０１〜２００μｍ、比表面
積が０．１ｍ2 ／ｇ以上の粉末、顆粒又は多孔質顆粒で
ある請求項１記載の機能性不織布の製造方法。2. Powders or granules having a particle size of apatite, tricalcium phosphate, tetracalcium phosphate or a mixture thereof of 0.01 to 200 μm and a specific surface area of 0.1 m 2 / g or more. 2. The method for producing a functional nonwoven fabric according to claim 1, wherein the functional nonwoven fabric is a porous granule.
を５〜７０重量％含む請求項１記載の機能性不織布の製
造方法。3. The method according to claim 1, wherein the aqueous dispersion contains a calcium phosphate compound in an amount of 5 to 70% by weight.
散剤をリン酸カルシウム系化合物に対して０．３〜１５
重量％含む請求項１記載の機能性不織布の製造方法。4. The aqueous dispersion contains a polycarboxylic acid-based polymer dispersant in an amount of 0.3 to 15 based on the calcium phosphate-based compound.
The method for producing a functional nonwoven fabric according to claim 1, wherein the content of the functional nonwoven fabric is included by weight.
シウム系化合物に対して２〜５０重量％含む請求項１記
載の機能性不織布の製造方法。5. The method for producing a functional nonwoven fabric according to claim 1, wherein the aqueous dispersion contains a water-soluble binder in an amount of 2 to 50% by weight based on the calcium phosphate compound.
２．０のリン酸カルシウム系化合物粒子、結合剤及びポ
リカルボン酸系高分子分散剤を含む水性分散液を用いて
抄紙技術により不織布を製造することを特徴とする機能
性不織布の製造方法。6. The raw material fiber, wherein the molar ratio of Ca / P is from 1.0 to 1.0.
A method for producing a functional nonwoven fabric, comprising producing a nonwoven fabric by a papermaking technique using an aqueous dispersion containing 2.0 calcium phosphate compound particles, a binder and a polycarboxylic acid polymer dispersant.
タイト、リン酸三カルシウム、リン酸四カルシウム又は
これらの混合物の粒径が０．０１〜２００μｍ、比表面
積が０．１ｍ2 ／ｇ以上の粉末、顆粒又は多孔質顆粒で
ある請求項６記載の機能性不織布の製造方法。7. A powder or granule in which the calcium phosphate compound particles have a particle size of apatite, tricalcium phosphate, tetracalcium phosphate or a mixture thereof of 0.01 to 200 μm and a specific surface area of 0.1 m 2 / g or more. 7. The method for producing a functional nonwoven fabric according to claim 6, wherein the functional nonwoven fabric is a porous granule.
を原料繊維に対して５〜２００重量％含む請求項６記載
の機能性不織布の製造方法。8. The method for producing a functional nonwoven fabric according to claim 6, wherein the aqueous dispersion contains a calcium phosphate compound in an amount of 5 to 200% by weight based on the weight of the raw fibers.
散剤をリン酸カルシウム系化合物に対して 0.3〜１５重
量％含む請求項６記載の機能性不織布の製造方法。9. The method for producing a functional nonwoven fabric according to claim 6, wherein the aqueous dispersion contains a polycarboxylic acid-based polymer dispersant in an amount of 0.3 to 15% by weight based on the calcium phosphate-based compound.
ム系化合物に対して２〜５０重量％含む請求項６記載の
機能性不織布の製造方法。10. The method for producing a functional nonwoven fabric according to claim 6, wherein the aqueous dispersion contains a binder in an amount of 2 to 50% by weight based on the calcium phosphate compound.